CN108995331B - 一种基于苎麻纤维粉体的新型装饰革及其制备方法 - Google Patents

一种基于苎麻纤维粉体的新型装饰革及其制备方法 Download PDF

Info

Publication number
CN108995331B
CN108995331B CN201810674788.2A CN201810674788A CN108995331B CN 108995331 B CN108995331 B CN 108995331B CN 201810674788 A CN201810674788 A CN 201810674788A CN 108995331 B CN108995331 B CN 108995331B
Authority
CN
China
Prior art keywords
ramie fiber
fiber powder
butt joint
ring body
joint groove
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201810674788.2A
Other languages
English (en)
Other versions
CN108995331A (zh
Inventor
刘以东
徐广梅
崔庆
何双跃
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongtai Fu'an Synthetic Material Co ltd
Original Assignee
Dongtai Fu'an Synthetic Material Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongtai Fu'an Synthetic Material Co ltd filed Critical Dongtai Fu'an Synthetic Material Co ltd
Priority to CN201810674788.2A priority Critical patent/CN108995331B/zh
Publication of CN108995331A publication Critical patent/CN108995331A/zh
Application granted granted Critical
Publication of CN108995331B publication Critical patent/CN108995331B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种基于苎麻纤维粉体的新型装饰革及其制备方法，包括上贴合面、下贴合面、防腐环体、苎麻纤维粉体；所述的上贴合面和下贴合面通过热压贴合对接；所述的上贴合面下侧设有上对接槽；所述的下贴合面上侧设有下对接槽；所述的上对接槽和下对接槽对接形成粉体空腔；所述的防腐环体贴合安装在粉体空腔的四周内壁；所述的防腐环体内侧的粉体空腔内灌注苎麻纤维粉体；本发明经过上贴合面的制备、下贴合面的制备、安装灌注贴合、热压贴合，得到本发明的装饰革，本发明环保性能高、透气吸湿性高、防腐蚀性能强。

Description

一种基于苎麻纤维粉体的新型装饰革及其制备方法
技术领域
本发明涉及新型装饰革领域，尤其涉及基于苎麻纤维粉体的新型装饰革及其制备方法。
背景技术
随着社会的不断发展，人民生活水平日益提高，人们对于居住环境的要求也日益提高。目前，室内墙壁装饰主要是用装饰墙纸和天然皮革。墙纸不耐潮、不耐光、易破损，难以达到高档装饰效果。对于天然皮革，由于受到自然条件制约，同时全世界对保护动物的意识逐步加强，天然皮革正在逐年减少。目前，市场上开发的家用装饰合成革，一般包括装饰层和基材层，装饰层和基材层通过PVC树脂混合各种改性剂混炼而成，然后将装饰层和基材层进行热压贴合，但是，这样的装饰革的环保性能差、透气吸湿性差、防腐蚀性能不好。
发明内容
针对上述现有技术的不足之处，本发明解决的问题为：提供一种环保性能高、透气吸湿性高、防腐蚀性能强的基于苎麻纤维粉体的新型装饰革及其制备方法。
为解决上述问题，本发明采取的技术方案如下：
一种基于苎麻纤维粉体的新型装饰革，包括上贴合面、下贴合面、防腐环体、苎麻纤维粉体；所述的下贴合面各组分以及重量份如下：PVC树脂100份、稳定剂4至5份、发泡剂3至4份、碳酸钙30至40份；所述的上贴合面各组分以及重量份如下：PVC树脂100份、增塑剂40至50份、色饼10至20份；所述的上贴合面和下贴合面通过热压贴合对接；所述的上贴合面下侧设有上对接槽；所述的下贴合面上侧设有下对接槽；所述的上对接槽和下对接槽对接形成粉体空腔；所述的防腐环体贴合安装在粉体空腔的四周内壁；所述的防腐环体内侧的粉体空腔内灌注苎麻纤维粉体。
进一步，所述的增塑剂为DOP邻苯二甲酸二辛酯。
进一步，所述的防腐环体为聚四氟乙烯材料制成。
进一步，所述的粉体空腔呈矩形结构；所述的防腐环体呈矩形结构。
进一步，所述的PVC树脂为三型PVC树脂。
一种基于苎麻纤维粉体的新型装饰革的制备方法，步骤如下：
S1、上贴合面的制备：将上贴合面中的PVC树脂、增塑剂、色饼各组分送入搅拌机中进行搅拌；将搅拌好的上贴合面的各组分进行混炼、开炼，得到上贴合面浆料；然后将上贴合面浆料注射至上贴合面模具中经过模具挤压、加热固化、冷却成型、脱模，得到带有上对接槽的上贴合面；
S2、下贴合面的制备：将下贴合面中的PVC树脂、稳定剂、发泡剂、碳酸钙送入搅拌机中进行搅拌；将搅拌好的下贴合面的各组分进行混炼、开炼，得到下贴合面浆料；然后将下贴合面浆料注射至下贴合面模具中经过模具挤压、加热固化、冷却成型、脱模，得到带有下对接槽的下贴合面；
S3、安装灌注贴合：首先将防腐环体下半部四周外侧贴合安装在下贴合面的下对接槽的四周内壁；然后将苎麻纤维通过研磨机进行研磨成苎麻纤维粉体，在防腐环体内灌注苎麻纤维粉体，使得苎麻纤维粉体充满整个防腐环体内；最后将上贴合面对接在下贴合面上，使得防腐环体上半部四周外侧贴合安装在上贴合面的上对接槽的四周内壁；如此形成如下结构：上对接槽和下对接槽对接形成粉体空腔，防腐环体贴合安装在粉体空腔的四周内壁，防腐环体内侧的粉体空腔内灌注苎麻纤维粉体；
S4、热压贴合：将步骤S3中的上贴合面和下贴合面至于贴合机上，经过预热、贴合、冷却工序，得到本发明的基于苎麻纤维粉体的新型装饰革。
进一步，所述的步骤S1中控制搅拌机的温度为170至180℃，加热固化时间为20至30min。
进一步，所述的步骤S2中控制搅拌机的温度为180至190℃，加热固化时间为30至40min。
进一步，所述的步骤S3中将苎麻纤维粉体压实在防腐环体内。
进一步，所述的步骤S4中贴合机的贴合压力为26kg/cm2至28 kg/cm2。
本发明的有益效果
本发明设计巧妙，利用防腐环体作为载体将苎麻纤维粉体置于上贴合面和下贴合面内部，本发明在上贴合面下侧设有上对接槽，下贴合面上侧设有下对接槽，上对接槽和下对接槽对接形成粉体空腔，防腐环体贴合安装在粉体空腔的四周内壁，防腐环体内侧的粉体空腔内灌注苎麻纤维粉体，本发明改变了传统将各种组分一起高温搅拌后进行混炼开炼、再进行贴合的制备方法，因为苎麻纤维粉体经过混炼开炼之后的环保性能、透气吸湿性能会受到极大的削减，本发明将苎麻纤维粉体不进行混炼开炼而直接活性灌注于上贴合面和下贴合面的内部，极大的提升了本发明环保性能、透气吸湿性能，利用聚四氟乙烯材料制备的防腐环体作为苎麻纤维粉体的载体提升了腐蚀性能。
附图说明
图1为本发明的俯视结构剖视图。
图2为本发明纵向截面结构剖视图。
具体实施方式
下面结合附图对本发明内容作进一步详细说明。
实施例1
如图1和2所示，一种基于苎麻纤维粉体的新型装饰革，包括上贴合面2、下贴合面1、防腐环体3、苎麻纤维粉体5；防腐环体3可为聚四氟乙烯材料制成；所述的下贴合面1各组分以及重量份如下：PVC树脂100份、稳定剂4份、发泡剂3份、碳酸钙30份；所述的上贴合面2各组分以及重量份如下：PVC树脂100份、增塑剂40份、色饼10份；增塑剂为DOP邻苯二甲酸二辛酯；所述的上贴合面2和下贴合面1通过热压贴合对接；所述的上贴合面2下侧设有上对接槽；所述的下贴合面1上侧设有下对接槽；所述的上对接槽和下对接槽对接形成粉体空腔4；所述的防腐环体3贴合安装在粉体空腔4的四周内壁；所述的防腐环体3内侧的粉体空腔4内灌注苎麻纤维粉体5。粉体空腔4呈矩形结构；所述的防腐环体3呈矩形结构；PVC树脂为三型PVC树脂。
一种基于苎麻纤维粉体的新型装饰革的制备方法，步骤如下：
S1、上贴合面的制备：将上贴合面中的PVC树脂、增塑剂、色饼各组分送入搅拌机中进行搅拌，控制搅拌机的温度为170℃；将搅拌好的上贴合面的各组分进行混炼、开炼，得到上贴合面浆料；然后将上贴合面浆料注射至上贴合面模具中经过模具挤压、加热固化、冷却成型、脱模，得到带有上对接槽的上贴合面；加热固化时间为20 min；
S2、下贴合面的制备：将下贴合面中的PVC树脂、稳定剂、发泡剂、碳酸钙送入搅拌机中进行搅拌，控制搅拌机的温度为180℃；将搅拌好的下贴合面的各组分进行混炼、开炼，得到下贴合面浆料；然后将下贴合面浆料注射至下贴合面模具中经过模具挤压、加热固化、冷却成型、脱模，得到带有下对接槽的下贴合面；加热固化时间为30 min；
S3、安装灌注贴合：首先将防腐环体下半部四周外侧贴合安装在下贴合面的下对接槽的四周内壁；然后将苎麻纤维通过研磨机进行研磨成苎麻纤维粉体，在防腐环体内灌注苎麻纤维粉体，使得苎麻纤维粉体充满整个防腐环体内，将苎麻纤维粉体压实在防腐环体内；最后将上贴合面对接在下贴合面上，使得防腐环体上半部四周外侧贴合安装在上贴合面的上对接槽的四周内壁；如此形成如下结构：上对接槽和下对接槽对接形成粉体空腔，防腐环体贴合安装在粉体空腔的四周内壁，防腐环体内侧的粉体空腔内灌注苎麻纤维粉体；
S4、热压贴合：将步骤S3中的上贴合面和下贴合面至于贴合机上，经过预热、贴合、冷却工序，得到本发明的基于苎麻纤维粉体的新型装饰革。贴合机的贴合压力为26kg/cm2。
实施例2
如图1和2所示，一种基于苎麻纤维粉体的新型装饰革，包括上贴合面2、下贴合面1、防腐环体3、苎麻纤维粉体5；防腐环体3可为聚四氟乙烯材料制成；所述的下贴合面1各组分以及重量份如下：PVC树脂100份、稳定剂4.5份、发泡剂3.5份、碳酸钙35份；所述的上贴合面2各组分以及重量份如下：PVC树脂100份、增塑剂45份、色饼15份；增塑剂为DOP邻苯二甲酸二辛酯；所述的上贴合面2和下贴合面1通过热压贴合对接；所述的上贴合面2下侧设有上对接槽；所述的下贴合面1上侧设有下对接槽；所述的上对接槽和下对接槽对接形成粉体空腔4；所述的防腐环体3贴合安装在粉体空腔4的四周内壁；所述的防腐环体3内侧的粉体空腔4内灌注苎麻纤维粉体5。粉体空腔4呈矩形结构；所述的防腐环体3呈矩形结构；PVC树脂为三型PVC树脂。
一种基于苎麻纤维粉体的新型装饰革的制备方法，步骤如下：
S1、上贴合面的制备：将上贴合面中的PVC树脂、增塑剂、色饼各组分送入搅拌机中进行搅拌，控制搅拌机的温度为175℃；将搅拌好的上贴合面的各组分进行混炼、开炼，得到上贴合面浆料；然后将上贴合面浆料注射至上贴合面模具中经过模具挤压、加热固化、冷却成型、脱模，得到带有上对接槽的上贴合面；加热固化时间为25min；
S2、下贴合面的制备：将下贴合面中的PVC树脂、稳定剂、发泡剂、碳酸钙送入搅拌机中进行搅拌，控制搅拌机的温度为185℃；将搅拌好的下贴合面的各组分进行混炼、开炼，得到下贴合面浆料；然后将下贴合面浆料注射至下贴合面模具中经过模具挤压、加热固化、冷却成型、脱模，得到带有下对接槽的下贴合面；加热固化时间为35min；
S3、安装灌注贴合：首先将防腐环体下半部四周外侧贴合安装在下贴合面的下对接槽的四周内壁；然后将苎麻纤维通过研磨机进行研磨成苎麻纤维粉体，在防腐环体内灌注苎麻纤维粉体，使得苎麻纤维粉体充满整个防腐环体内，将苎麻纤维粉体压实在防腐环体内；最后将上贴合面对接在下贴合面上，使得防腐环体上半部四周外侧贴合安装在上贴合面的上对接槽的四周内壁；如此形成如下结构：上对接槽和下对接槽对接形成粉体空腔，防腐环体贴合安装在粉体空腔的四周内壁，防腐环体内侧的粉体空腔内灌注苎麻纤维粉体；
S4、热压贴合：将步骤S3中的上贴合面和下贴合面至于贴合机上，经过预热、贴合、冷却工序，得到本发明的基于苎麻纤维粉体的新型装饰革。贴合机的贴合压力为27 kg/cm2 。
实施例3
如图1和2所示，一种基于苎麻纤维粉体的新型装饰革，包括上贴合面2、下贴合面1、防腐环体3、苎麻纤维粉体5；防腐环体3可为聚四氟乙烯材料制成；所述的下贴合面1各组分以及重量份如下：PVC树脂100份、稳定剂5份、发泡剂4份、碳酸钙40份；所述的上贴合面2各组分以及重量份如下：PVC树脂100份、增塑剂50份、色饼20份；增塑剂为DOP邻苯二甲酸二辛酯；所述的上贴合面2和下贴合面1通过热压贴合对接；所述的上贴合面2下侧设有上对接槽；所述的下贴合面1上侧设有下对接槽；所述的上对接槽和下对接槽对接形成粉体空腔4；所述的防腐环体3贴合安装在粉体空腔4的四周内壁；所述的防腐环体3内侧的粉体空腔4内灌注苎麻纤维粉体5。粉体空腔4呈矩形结构；所述的防腐环体3呈矩形结构；PVC树脂为三型PVC树脂。
一种基于苎麻纤维粉体的新型装饰革的制备方法，步骤如下：
S1、上贴合面的制备：将上贴合面中的PVC树脂、增塑剂、色饼各组分送入搅拌机中进行搅拌，控制搅拌机的温度为180℃；将搅拌好的上贴合面的各组分进行混炼、开炼，得到上贴合面浆料；然后将上贴合面浆料注射至上贴合面模具中经过模具挤压、加热固化、冷却成型、脱模，得到带有上对接槽的上贴合面；加热固化时间为30min；
S2、下贴合面的制备：将下贴合面中的PVC树脂、稳定剂、发泡剂、碳酸钙送入搅拌机中进行搅拌，控制搅拌机的温度为190℃；将搅拌好的下贴合面的各组分进行混炼、开炼，得到下贴合面浆料；然后将下贴合面浆料注射至下贴合面模具中经过模具挤压、加热固化、冷却成型、脱模，得到带有下对接槽的下贴合面；加热固化时间为40min；
S3、安装灌注贴合：首先将防腐环体下半部四周外侧贴合安装在下贴合面的下对接槽的四周内壁；然后将苎麻纤维通过研磨机进行研磨成苎麻纤维粉体，在防腐环体内灌注苎麻纤维粉体，使得苎麻纤维粉体充满整个防腐环体内，将苎麻纤维粉体压实在防腐环体内；最后将上贴合面对接在下贴合面上，使得防腐环体上半部四周外侧贴合安装在上贴合面的上对接槽的四周内壁；如此形成如下结构：上对接槽和下对接槽对接形成粉体空腔，防腐环体贴合安装在粉体空腔的四周内壁，防腐环体内侧的粉体空腔内灌注苎麻纤维粉体；
S4、热压贴合：将步骤S3中的上贴合面和下贴合面至于贴合机上，经过预热、贴合、冷却工序，得到本发明的基于苎麻纤维粉体的新型装饰革。贴合机的贴合压力为28 kg/cm2 。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (10)

1.一种基于苎麻纤维粉体的新型装饰革，其特征在于，包括上贴合面、下贴合面、防腐环体、苎麻纤维粉体；所述的下贴合面各组分以及重量份如下：PVC树脂100份、稳定剂4至5份、发泡剂3至4份、碳酸钙30至40份；所述的上贴合面各组分以及重量份如下：PVC树脂100份、增塑剂40至50份、色饼10至20份；所述的上贴合面和下贴合面通过热压贴合对接；所述的上贴合面下侧设有上对接槽；所述的下贴合面上侧设有下对接槽；所述的上对接槽和下对接槽对接形成粉体空腔；所述的防腐环体贴合安装在粉体空腔的四周内壁；所述的防腐环体内侧的粉体空腔内灌注苎麻纤维粉体。
2.根据权利要求1所述的基于苎麻纤维粉体的新型装饰革，其特征在于，所述的增塑剂为DOP邻苯二甲酸二辛酯。
3.根据权利要求1所述的基于苎麻纤维粉体的新型装饰革，其特征在于，所述的防腐环体为聚四氟乙烯材料制成。
4.根据权利要求1所述的基于苎麻纤维粉体的新型装饰革，其特征在于，所述的粉体空腔呈矩形结构；所述的防腐环体呈矩形结构。
5.根据权利要求1所述的基于苎麻纤维粉体的新型装饰革，其特征在于，所述的PVC树脂为三型PVC树脂。
6.一种根据权利要求1至5任意一项所述的基于苎麻纤维粉体的新型装饰革的制备方法，其特征在于，步骤如下：
S1、上贴合面的制备：将上贴合面中的PVC树脂、增塑剂、色饼各组分送入搅拌机中进行搅拌；将搅拌好的上贴合面的各组分进行混炼、开炼，得到上贴合面浆料；然后将上贴合面浆料注射至上贴合面模具中经过模具挤压、加热固化、冷却成型、脱模，得到带有上对接槽的上贴合面；
S2、下贴合面的制备：将下贴合面中的PVC树脂、稳定剂、发泡剂、碳酸钙送入搅拌机中进行搅拌；将搅拌好的下贴合面的各组分进行混炼、开炼，得到下贴合面浆料；然后将下贴合面浆料注射至下贴合面模具中经过模具挤压、加热固化、冷却成型、脱模，得到带有下对接槽的下贴合面；
S3、安装灌注贴合：首先将防腐环体下半部四周外侧贴合安装在下贴合面的下对接槽的四周内壁；然后将苎麻纤维通过研磨机进行研磨成苎麻纤维粉体，在防腐环体内灌注苎麻纤维粉体，使得苎麻纤维粉体充满整个防腐环体内；最后将上贴合面对接在下贴合面上，使得防腐环体上半部四周外侧贴合安装在上贴合面的上对接槽的四周内壁；如此形成如下结构：上对接槽和下对接槽对接形成粉体空腔，防腐环体贴合安装在粉体空腔的四周内壁，防腐环体内侧的粉体空腔内灌注苎麻纤维粉体；
S4、热压贴合：将步骤S3中的上贴合面和下贴合面置于贴合机上，经过预热、贴合、冷却工序，得到基于苎麻纤维粉体的新型装饰革。
7.根据权利要求6所述的基于苎麻纤维粉体的新型装饰革的制备方法，其特征在于，所述的步骤S1中控制搅拌机的温度为170至180℃，加热固化时间为20至30min。
8.根据权利要求6所述的基于苎麻纤维粉体的新型装饰革的制备方法，其特征在于，所述的步骤S2中控制搅拌机的温度为180至190℃，加热固化时间为30至40min。
9.根据权利要求6所述的基于苎麻纤维粉体的新型装饰革的制备方法，其特征在于，所述的步骤S3中将苎麻纤维粉体压实在防腐环体内。
10.根据权利要求6所述的基于苎麻纤维粉体的新型装饰革的制备方法，其特征在于，所述的步骤S4中贴合机的贴合压力为26kg/cm2至28 kg/cm2。
CN201810674788.2A 2018-06-27 2018-06-27 一种基于苎麻纤维粉体的新型装饰革及其制备方法 Active CN108995331B (zh)