CN108298815B - Preparation process of porcelain - Google Patents
Preparation process of porcelain Download PDFInfo
- Publication number
- CN108298815B CN108298815B CN201810163120.1A CN201810163120A CN108298815B CN 108298815 B CN108298815 B CN 108298815B CN 201810163120 A CN201810163120 A CN 201810163120A CN 108298815 B CN108298815 B CN 108298815B
- Authority
- CN
- China
- Prior art keywords
- glaze
- parts
- bean
- green
- branch spot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to the technical field of ceramics, in particular to a preparation process of a porcelain with a combination of bean green glaze and plum branch spot glaze. The porcelain combining the bean green glaze and the plum branch spot glaze is provided with a bean green glaze layer and a plum branch spot glaze layer from a blank body to the outside in sequence, the glaze color of the bean green glaze is bluish-white, the glaze surface is glossy, the color of cyan is simple and elegant, and the light transmittance is high; the outer layer of the bean-green glaze is painted with a color through plum branch spot glaze, and the plum branch spot glaze is grey brown and is as rough as branches and trunks of trees and glaze; the green bean glaze and the green plum branch spot glaze provided by the invention can be fused with each other, the green plum branch spot glaze can be applied to the edge of an opening of an implement to form retro and antique effects with the ground color of the green bean glaze, and patterns of trees, branches, houses and the like can be drawn on the surface of the green bean glaze, so that the delicate and mild ground color and the rough color drawing form bright contrast to form unique artistic aesthetic feeling, the two glazes are fired at one time, 20-30% of fuel can be saved, and the energy consumption is effectively reduced.
Description
The application is a divisional application of porcelain and preparation technology combining bean green glaze and plum branch spot glaze, the application date of the original application is 2016, 3 and 20 days, and the application numbers are as follows: CN 201610165752.2.
Technical Field
The invention relates to the technical field of ceramics, in particular to a preparation process of a porcelain combining bean green glaze and plum branch spot glaze.
Background
The bean-green glaze is one of glaze colors derived from green glaze and originates from Song dynasty Longquan kiln. The glaze color is greenish-medium yellowish, and the glaze luster is weaker than that of pink green and plum green. The basic color tone of the bean-green glaze is mainly green and medium yellow, and the color is light and elegant. The traditional bean-green glaze material is single-color glaze, is elegant and soft, light in color like lake water, dark in color like green and yellowish in middle, and thick in glaze surface. The limpid glaze is manufactured by firing the soyabean glaze, and simultaneously, various colors are applied on the glaze, and the color is manufactured in a kiln for two times, so that the color is in contrast with the elegant glaze color, and the charming is more colorful, but the transparency of the soyabean glaze is not as good as that of the white glaze, and the effect obtained by coloring the soyabean glaze is not as good as that of the soyabean glaze.
With the rapid development of economic society, the quality of life of people is improved day by day, the demand for aesthetic diversity constantly changes, although traditional azure-lazed soy glaze is deeply loved by people, the monochromatic glaze effect and stripes can not meet the demand of people, if the advantages of the traditional azure-lazed soy glaze can be provided, the patterns different from the traditional glaze can be displayed on the traditional glaze effect, so that the porcelain which can meet the constantly changing demand of people and has unique artistic effect can be provided, and the porcelain has positive economic and social benefits.
Disclosure of Invention
In order to overcome the defects in the prior art, the invention provides a preparation process of porcelain.
In order to achieve the purpose, the technical scheme adopted by the invention is as follows:
the porcelain combining the bean green glaze and the plum branch spot glaze is characterized in that a bean green glaze layer and a plum branch spot glaze layer are sequentially arranged on the porcelain from a blank body to the outside,
the bean-green glaze is prepared from the following raw materials in parts by weight: 30-35 parts of feldspar, 10-15 parts of calcined kaolin, 10-15 parts of chalk, 10-15 parts of quartz, 5-10 parts of Suzhou clay, 5-10 parts of zirconium silicate, 5-10 parts of talc, 3-5 parts of dolomite, 1-5 parts of barium carbonate and 1-3 parts of iron oxide;
the plum branch spot glaze is prepared from the following raw materials in parts by weight: 35-40 parts of feldspar, 15-25 parts of quartz, 5-20 parts of pine ash, 5-10 parts of Suzhou soil, 5-10 parts of fly ash, 5-10 parts of ferric oxide, 1-5 parts of talc, 1-5 parts of barium carbonate, 1-5 parts of manganese dioxide, 1-5 parts of bone meal and 1-3 parts of cobalt oxide.
Preferably, the bean-green glaze is prepared from the following raw materials in parts by weight: feldspar 33, calcined kaolin 10, chalk 10, quartz 15, suzhou clay 10, zirconium silicate 8, talc 5, dolomite 5, barium carbonate 2.5, iron oxide 1.5.
Preferably, the plum branch spot glaze is prepared from the following raw materials in parts by weight: 30 parts of feldspar, 25 parts of quartz, 14 parts of pine ash, 5 parts of Suzhou soil, 10 parts of fly ash, 6 parts of iron oxide, 3 parts of talc, 2 parts of barium carbonate, 2 parts of manganese dioxide, 2 parts of bone meal and 1 part of cobalt oxide.
Preferably, the bean-green glaze is prepared from the following raw materials in parts by weight: feldspar 33, calcined kaolin 13, chalk 11, quartz 13, suzhou clay 8, zirconium silicate 6, talc 7, dolomite 4, barium carbonate 3, iron oxide 2.
Preferably, the plum branch spot glaze is prepared from the following raw materials in parts by weight: feldspar 36, quartz 18, pine ash 9, Suzhou soil 8, fly ash 7, iron oxide 8, talc 2, barium carbonate 4, manganese dioxide 3, bone meal 3 and cobalt oxide 2.
Preferably, the bean-green glaze is prepared from the following raw materials in parts by weight: feldspar 34, calcined kaolin 13, chalk 12, quartz 10, suzhou clay 10, zirconium silicate 9, talc 8, dolomite 2, barium carbonate 1, iron oxide 1.
Preferably, the plum branch spot glaze is prepared from the following raw materials in parts by weight: feldspar 38, quartz 25, pine ash 7, Suzhou soil 7, flyash 8, iron oxide 6, talc 3, barium carbonate 2, manganese dioxide 2, bone meal 1 and cobalt oxide 1.
The preparation process of the porcelain combining the bean green glaze and the plum branch spot glaze is characterized in that the porcelain combining the bean green glaze and the plum branch spot glaze is used, and the preparation process comprises the following specific steps:
step 1, preparing bean green glaze and plum branch spot glaze;
step 2, applying bean-green glaze on the ceramic blank;
step 3, after the ceramic blank body is dried, applying plum branch spot glaze on the surface of the bean-green glaze in a color painting mode;
step 4, after the plum branch spot glaze is dried, putting the ceramic green body into a kiln for firing;
step 5, heating the kiln, wherein the firing temperature is 1200-1300 ℃ in a reducing atmosphere;
and 6, opening the furnace, and cooling to obtain the porcelain combining the bean green glaze and the plum branch spot glaze.
Further, the bean blue glaze in the step 1 is prepared by wet ball milling, wherein the raw materials comprise: ball: water 1: 2: 0.8, the plum branch spot glaze is prepared by wet ball milling, wherein the mass ratio of the raw materials is as follows: ball: water 1: 2: 1.
further, in step 5, the firing temperature is 1290 ℃.
The porcelain combining the bean-green glaze and the plum branch spot glaze has the base color of the bean-green glaze, the glaze color of the bean-green glaze is bluish-white, the glaze surface is glossy, the cyan is simple and elegant, and the light transmittance is high; the outer layer of the bean-green glaze is painted with a color through plum branch spot glaze, and the plum branch spot glaze is grey brown and is as rough as branches and trunks of trees and glaze; the invention provides a porcelain combining bean-green glaze and plum branch spot glaze, which is characterized in that the plum branch spot glaze capable of being fused with the bean-green glaze is added on the traditional bean-green glaze effect, the plum branch spot glaze can be applied to the edge part of an opening of an appliance to form the effects of vintage and antiquity with the ground color of the bean-green glaze, and the patterns of trees, branches, houses and the like can be drawn on the surface of the bean-green glaze, so that the delicate and warm ground color and the rough and wild colored drawing form bright contrast to form a unique artistic effect; the two glazes are fired at one time, so that 20-30% of fuel can be saved, and the energy consumption is effectively reduced.
Detailed Description
The invention is further described below by means of specific embodiments.
A porcelain combining bean green glaze and plum branch spot glaze is characterized in that a bean green glaze layer and a plum branch spot glaze layer are sequentially arranged on the porcelain from a blank body to the outside,
the bean-green glaze is prepared from the following raw materials in parts by weight: 30-35 parts of feldspar, 10-15 parts of calcined kaolin, 10-15 parts of chalk, 10-15 parts of quartz, 5-10 parts of Suzhou clay, 5-10 parts of zirconium silicate, 5-10 parts of talc, 3-5 parts of dolomite, 1-5 parts of barium carbonate and 1-3 parts of iron oxide;
the plum branch spot glaze is prepared from the following raw materials in parts by weight: 35-40 parts of feldspar, 15-25 parts of quartz, 5-20 parts of pine ash, 5-10 parts of Suzhou soil, 5-10 parts of fly ash, 5-10 parts of ferric oxide, 1-5 parts of talc, 1-5 parts of barium carbonate, 1-5 parts of manganese dioxide, 1-5 parts of bone meal and 1-3 parts of cobalt oxide.
The first embodiment is as follows:
the bean-green glaze is prepared from the following raw materials in parts by weight: feldspar 33, calcined kaolin 10, chalk 10, quartz 15, suzhou clay 10, zirconium silicate 8, talc 5, dolomite 5, barium carbonate 2.5, iron oxide 1.5;
the plum branch spot glaze is prepared from the following raw materials in parts by weight: 30 parts of feldspar, 25 parts of quartz, 14 parts of pine ash, 5 parts of Suzhou soil, 10 parts of fly ash, 6 parts of iron oxide, 3 parts of talc, 2 parts of barium carbonate, 2 parts of manganese dioxide, 2 parts of bone meal and 1 part of cobalt oxide.
The second embodiment is as follows:
the bean-green glaze is prepared from the following raw materials in parts by weight: feldspar 33, calcined kaolin 13, chalk 11, quartz 13, suzhou clay 8, zirconium silicate 6, talc 7, dolomite 4, barium carbonate 3, iron oxide 2;
the plum branch spot glaze is prepared from the following raw materials in parts by weight: feldspar 36, quartz 18, pine ash 9, Suzhou soil 8, fly ash 7, iron oxide 8, talc 2, barium carbonate 4, manganese dioxide 3, bone meal 3 and cobalt oxide 2.
The third concrete embodiment:
the bean-green glaze is prepared from the following raw materials in parts by weight: feldspar 34, calcined kaolin 13, chalk 12, quartz 10, suzhou clay 10, zirconium silicate 9, talc 8, dolomite 2, barium carbonate 1, iron oxide 1;
the plum branch spot glaze is prepared from the following raw materials in parts by weight: feldspar 38, quartz 25, pine ash 7, Suzhou soil 7, flyash 8, iron oxide 6, talc 3, barium carbonate 2, manganese dioxide 2, bone meal 1 and cobalt oxide 1.
The preparation process of the porcelain combining the bean green glaze and the plum branch spot glaze is characterized in that the porcelain combining the bean green glaze and the plum branch spot glaze in any one of the first embodiment to the third embodiment is used, and the preparation process comprises the following specific steps:
step 1, preparing bean green glaze and plum branch spot glaze;
step 2, applying bean-green glaze on the ceramic blank;
step 3, after the ceramic blank body is dried, applying plum branch spot glaze on the surface of the bean-green glaze in a color painting mode;
step 4, after the plum branch spot glaze is dried, putting the ceramic green body into a kiln for firing;
step 5, heating the kiln, wherein the firing temperature is 1200-1300 ℃ in a reducing atmosphere;
and 6, opening the furnace, and cooling to obtain the porcelain combining the bean green glaze and the plum branch spot glaze.
Optimally, the bean blue glaze in the step 1 is prepared by wet ball milling, wherein the raw materials are as follows: ball: water 1: 2: 0.8, the plum branch spot glaze is prepared by wet ball milling, wherein the mass ratio of the raw materials is as follows: ball: water 1: 2: 1;
preferably, the firing temperature in the step 5 is 1290 ℃.
The porcelain combining the bean-green glaze and the plum branch spot glaze prepared by the method has the base color of the bean-green glaze, the glaze color of the bean-green glaze is bluish-white, the glaze surface is glossy, the color of cyan is simple and elegant, and the light transmittance is high; the outer layer of the bean-green glaze is painted with a color sample through the plum branch spot glaze, the plum branch spot glaze is gray brown, and is as rough as branches and trunks of trees and glaze surfaces, the bean-green glaze and the plum branch spot glaze provided by the invention can be fused with each other to form unique artistic aesthetic feeling, the plum branch spot glaze can be applied to the edge part of an appliance to form retro and antique effects with the bottom color of the bean-green glaze, patterns of trees, branches, houses and the like can be painted on the surface of the bean-green glaze, and the two glazes are fired at one time, so that 20-30% of fuel can be saved, and the energy consumption is effectively reduced.
The above description is only a few specific embodiments of the present invention, but the design concept of the present invention is not limited thereto, and any insubstantial modifications made by the design concept should fall within the scope of the present invention.
Claims (2)
1. The preparation process of the porcelain is characterized by comprising the following specific steps:
step 1, preparing a bean green glaze and a plum branch spot glaze, wherein the bean green glaze in the step 1 is prepared by wet ball milling, and the raw materials comprise: ball: water = 1: 2: 0.8, the plum branch spot glaze is prepared by wet ball milling, wherein the mass ratio of the raw materials is as follows: ball: water = 1: 2: 1;
step 2, applying a bean-green glaze on the ceramic blank, wherein the bean-green glaze is prepared from the following raw materials in parts by weight: 30-35 parts of feldspar, 10-15 parts of calcined kaolin, 10-15 parts of chalk, 10-15 parts of quartz, 5-10 parts of Suzhou clay, 5-10 parts of zirconium silicate, 5-10 parts of talc, 3-5 parts of dolomite, 1-5 parts of barium carbonate and 1-3 parts of iron oxide;
step 3, after the ceramic blank body is dried, applying plum branch spot glaze on the surface of the bean-green glaze in a color painting mode, wherein the plum branch spot glaze is prepared from the following raw materials in parts by weight: 35-40 parts of feldspar, 15-25 parts of quartz, 5-20 parts of pine ash, 5-10 parts of Suzhou soil, 5-10 parts of fly ash, 5-10 parts of ferric oxide, 1-5 parts of talc, 1-5 parts of barium carbonate, 1-5 parts of manganese dioxide, 1-5 parts of bone meal and 1-3 parts of cobalt oxide;
step 4, after the plum branch spot glaze is dried, putting the ceramic green body into a kiln for firing;
step 5, heating the kiln, wherein the firing temperature is 1200-1300 ℃ in a reducing atmosphere;
and 6, opening the furnace, and cooling to obtain the porcelain combining the bean green glaze and the plum branch spot glaze.
2. The process for preparing porcelain according to claim 1, wherein: the firing temperature in the step 5 is 1290 ℃.