CN105712747B - The porcelain and preparation technology that yellowish pea green glaze is combined with plum branch speckled glaze - Google Patents
The porcelain and preparation technology that yellowish pea green glaze is combined with plum branch speckled glaze Download PDFInfo
- Publication number
- CN105712747B CN105712747B CN201610165752.2A CN201610165752A CN105712747B CN 105712747 B CN105712747 B CN 105712747B CN 201610165752 A CN201610165752 A CN 201610165752A CN 105712747 B CN105712747 B CN 105712747B
- Authority
- CN
- China
- Prior art keywords
- glaze
- speckled
- pea green
- plum branch
- porcelain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to ceramic technology field, is specifically related to porcelain and preparation technology that a kind of yellowish pea green glaze is combined with plum branch speckled glaze.This kind of yellowish pea green glaze is outwards had pea green glaze layer and plum branch spot glaze layer by base substrate successively with the porcelain that plum branch speckled glaze is combined, and the glaze colours of the yellowish pea green glaze is whitens in green grass or young crops, glaze paint gloss, cyan is plain, and light transmittance is high；Color sample is depicted by plum branch speckled glaze in the outer layer of yellowish pea green glaze, the plum branch speckled glaze is in taupe, and the limb of color such as trees, glaze paint are more coarse；Yellowish pea green glaze provided by the invention can be merged mutually with plum branch speckled glaze, plum branch speckled glaze can impose on implements opening's edge portion, with the background color of yellowish pea green glaze formed it is pseudo-classic, do old effect, also can be in patterns such as the surface rendering trees of yellowish pea green glaze, limb, houses, fine and smooth gentle background color forms a sharp contrast with thick mad colored drawing, forms the aesthetic of uniqueness, two kinds of glaze once-firings, 20 30% fuel can be saved, effectively reduces energy resource consumption.
Description
Technical field
The present invention relates to ceramic technology field, be specifically related to a kind of porcelain that yellowish pea green glaze is combined with plum branch speckled glaze and
Preparation technology.
Background technology
Yellowish pea green glaze, blue or green glaze derive from one of glaze colours, Longqun Cave originating from the Song Dynasty.Micro- nearly yellow before bright, it is pure near to the Qing Dynasty
Green, its glaze colours are yellowing in green grass or young crops, and glaze paint gloss is weaker than pale blue, plum green.The basic tone of yellowish pea green glaze with green grass or young crops dodge Huang based on,
Cyan is simple and elegant.Traditional pea green glaze is single color glaze, simple and elegant soft, if the light lake water of the shallow person of color, the green middle yellowing of color depth person, and glaze paint
Solidifying thickness.The Qing Dynasty begin to appear in fire yellowish pea green glaze while, also imposed on glaze various colors enter kiln it is secondary burning make, simple and elegant glaze
Color set off under color, it is more gorgeous charming, but yellowish pea green glaze transparency is not as good as white glaze, the effect obtained by pea green overglaze color
It is not fully up to expectations.
With the high speed development of economic society, the quality of life of people increasingly improves, continuous to aesthetic multifarious demand
Change, traditional yellowish pea green glaze is although very popular, but monochromatic glazing effect and speckle can not meet the need of people
Ask, if a kind of inheriting tradition yellowish pea green glaze can be provided, and shown on traditional glazing effect and be different from traditional glaze
The decorative pattern in face, with provide it is a kind of can meet that the continually changing demand of people has the porcelain of unique artistic effect, have positive
Economic and social benefit.
The content of the invention
To overcome deficiency of the prior art, the present invention provide the porcelain that a kind of yellowish pea green glaze is combined with plum branch speckled glaze and
Preparation technology.
To achieve the above object, the technical solution adopted by the present invention is as follows：
The porcelain that yellowish pea green glaze is combined with plum branch speckled glaze, it is characterised in that the porcelain outwards has beans successively by base substrate
Blue or green glaze layer and plum branch spot glaze layer,
The yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 30-35, calcined kaolin 10-15, chalk
10-15, quartzy 10-15, Suzhou soil 5-10, zirconium silicate 5-10, talcum 5-10, dolomite 3-5, barium carbonate 1-5, iron oxide 1-3；
The plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 35-40, quartzy 15-25, pine ash 5-
20th, Suzhou soil 5-10, solo flight powder 5-10, iron oxide 5-10, talcum 1-5, barium carbonate 1-5, manganese dioxide 1-5, bone meal 1-5, oxygen
Change cobalt 1-3.
Optimization, yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 33, calcined kaolin 10, chalk 10, stone
English 15, Suzhou soil 10, zirconium silicate 8, talcum 5, dolomite 5, barium carbonate 2.5, iron oxide 1.5.
Optimization, plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 30, quartz 25, pine ash 14, Soviet Union
State soil 5, solo flight powder 10, iron oxide 6, talcum 3, barium carbonate 2, manganese dioxide 2, bone meal 2, cobalt oxide 1.
Optimization, yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 33, calcined kaolin 13, chalk 11, stone
English 13, Suzhou soil 8, zirconium silicate 6, talcum 7, dolomite 4, barium carbonate 3, iron oxide 2.
Optimization, plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 36, quartz 18, pine ash 9, Soviet Union
State soil 8, solo flight powder 7, iron oxide 8, talcum 2, barium carbonate 4, manganese dioxide 3, bone meal 3, cobalt oxide 2.
Optimization, yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 34, calcined kaolin 13, chalk 12, stone
English 10, Suzhou soil 10, zirconium silicate 9, talcum 8, dolomite 2, barium carbonate 1, iron oxide 1.
Optimization, plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 38, quartz 25, pine ash 7, Soviet Union
State soil 7, solo flight powder 8, iron oxide 6, talcum 3, barium carbonate 2, manganese dioxide 2, bone meal 1, cobalt oxide 1.
The preparation technology for the porcelain that yellowish pea green glaze is combined with plum branch speckled glaze, it is characterised in that use the claims
The porcelain that yellowish pea green glaze in 1-7 described in any one is combined with plum branch speckled glaze, it is comprised the following steps that：
Step 1, yellowish pea green glaze and plum branch speckled glaze are prepared；
Step 2, yellowish pea green glaze is applied on ceramic body；
Step 3, plum branch speckled glaze is applied in pea green glaze paint by way of colored drawing after ceramic blank drying；
Step 4, after the drying of plum branch speckled glaze, ceramic body is put into kiln and fired；
Step 5, furnace heating-up, under reducing atmosphere, firing temperature is 1200-1300 DEG C；
Step 6, blow-on, the porcelain that yellowish pea green glaze is combined with plum branch speckled glaze is obtained after cooling.
Further, yellowish pea green glaze described in step 1 is milled into using wet bulb, wherein expecting：Ball：Water=1：2：0.8, the plum branch
Speckled glaze is milled into using wet bulb, wherein expecting：Ball：Water=1：2：1.
Further, firing temperature is 1290 DEG C in step 5.
From the above-mentioned description of this invention, yellowish pea green glaze provided by the invention has with the porcelain that plum branch speckled glaze is combined
There is the background color of yellowish pea green glaze, the glaze colours of the yellowish pea green glaze is whitens in green grass or young crops, glaze paint gloss, cyan is plain, and light transmittance is high；In yellowish pea green glaze
Outer layer depicts color sample by plum branch speckled glaze, and the plum branch speckled glaze is in taupe, and the limb of color such as trees, glaze paint are more thick
It is rough；Present invention offer yellowish pea green glaze adds with the porcelain that plum branch speckled glaze is combined in traditional yellowish pea green glaze effect can be with its phase
The plum branch speckled glaze of fusion, plum branch speckled glaze can impose on implements opening's edge portion, with the background color of yellowish pea green glaze formed it is pseudo-classic, do old effect
Fruit, also can be in patterns such as the surface rendering trees of yellowish pea green glaze, limb, houses, and fine and smooth gentle background color is formed with thick mad colored drawing
Striking contrast, form the artistic effect of uniqueness；Two kinds of glaze once-firings, can save 20-30% fuel, efficiently reduce
Energy resource consumption.
Embodiment
Below by way of embodiment, the invention will be further described.
The porcelain that a kind of yellowish pea green glaze is combined with plum branch speckled glaze, it is characterised in that the porcelain is outside successively by base substrate
There are pea green glaze layer and plum branch spot glaze layer,
The yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 30-35, calcined kaolin 10-15, chalk
10-15, quartzy 10-15, Suzhou soil 5-10, zirconium silicate 5-10, talcum 5-10, dolomite 3-5, barium carbonate 1-5, iron oxide 1-3；
The plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 35-40, quartzy 15-25, pine ash 5-
20th, Suzhou soil 5-10, solo flight powder 5-10, iron oxide 5-10, talcum 1-5, barium carbonate 1-5, manganese dioxide 1-5, bone meal 1-5, oxygen
Change cobalt 1-3.
Specific embodiment one：
Yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 33, calcined kaolin 10, chalk 10, quartz 15, Soviet Union
State soil 10, zirconium silicate 8, talcum 5, dolomite 5, barium carbonate 2.5, iron oxide 1.5；
Plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 30, quartz 25, pine ash 14, Suzhou soil 5,
Solo flight powder 10, iron oxide 6, talcum 3, barium carbonate 2, manganese dioxide 2, bone meal 2, cobalt oxide 1.
Specific embodiment two：
Yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 33, calcined kaolin 13, chalk 11, quartz 13, Soviet Union
State soil 8, zirconium silicate 6, talcum 7, dolomite 4, barium carbonate 3, iron oxide 2；
Plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 36, quartz 18, pine ash 9, Suzhou soil 8, list
Fly powder 7, iron oxide 8, talcum 2, barium carbonate 4, manganese dioxide 3, bone meal 3, cobalt oxide 2.
Specific embodiment three：
Yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 34, calcined kaolin 13, chalk 12, quartz 10, Soviet Union
State soil 10, zirconium silicate 9, talcum 8, dolomite 2, barium carbonate 1, iron oxide 1；
Plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 38, quartz 25, pine ash 7, Suzhou soil 7, list
Fly powder 8, iron oxide 6, talcum 3, barium carbonate 2, manganese dioxide 2, bone meal 1, cobalt oxide 1.
The preparation technology for the porcelain that yellowish pea green glaze is combined with plum branch speckled glaze, it is characterised in that use specific embodiment one
The porcelain that yellowish pea green glaze into three described in any one is combined with plum branch speckled glaze, it is comprised the following steps that：
Step 1, yellowish pea green glaze and plum branch speckled glaze are prepared；
Step 2, yellowish pea green glaze is applied on ceramic body；
Step 3, plum branch speckled glaze is applied in pea green glaze paint by way of colored drawing after ceramic blank drying；
Step 4, after the drying of plum branch speckled glaze, ceramic body is put into kiln and fired；
Step 5, furnace heating-up, under reducing atmosphere, firing temperature is 1200-1300 DEG C；
Step 6, blow-on, the porcelain that yellowish pea green glaze is combined with plum branch speckled glaze is obtained after cooling.
Optimization, yellowish pea green glaze is milled into using wet bulb described in step 1, wherein expecting：Ball：Water=1：2：0.8, the plum branch spot
Point glaze is milled into using wet bulb, wherein expecting：Ball：Water=1：2：1；
Optimization, firing temperature is 1290 DEG C in step 5.
There is the background color of yellowish pea green glaze using the yellowish pea green glaze prepared by the above method with the porcelain that plum branch speckled glaze is combined, should
The glaze colours of yellowish pea green glaze is whitens in green grass or young crops, glaze paint gloss, cyan is plain, and light transmittance is high；Pass through plum branch spot in the outer layer of yellowish pea green glaze
Glaze depicts color sample, and the plum branch speckled glaze is in taupe, and the limb of color such as trees, glaze paint are more coarse, beans provided by the invention
Blue or green glaze can be merged mutually with plum branch speckled glaze, form the aesthetic of uniqueness, plum branch speckled glaze can impose on implements opening's edge portion, with beans
The background color of blue or green glaze formed it is pseudo-classic, do old effect, also can be in patterns such as the surface rendering trees of yellowish pea green glaze, limb, houses, two kinds
Glaze once-firing, 20-30% fuel can be saved, effectively reduces energy resource consumption.
Some embodiments of the present invention are above are only, but the design concept of the present invention is not limited thereto, all profits
The change of unsubstantiality is carried out to the present invention with this design, the behavior for invading the scope of the present invention all should be belonged to.
Claims (10)
1. the porcelain that yellowish pea green glaze is combined with plum branch speckled glaze, it is characterised in that the porcelain is outwards had pea green successively by base substrate
Glaze layer and plum branch spot glaze layer,
The yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 30-35, calcined kaolin 10-15, chalk 10-15,
Quartzy 10-15, Suzhou soil 5-10, zirconium silicate 5-10, talcum 5-10, dolomite 3-5, barium carbonate 1-5, iron oxide 1-3；
The plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 35-40, quartzy 15-25, pine ash 5-20,
Suzhou soil 5-10, solo flight powder 5-10, iron oxide 5-10, talcum 1-5, barium carbonate 1-5, manganese dioxide 1-5, bone meal 1-5, cobalt oxide
1-3。
2. the porcelain that yellowish pea green glaze according to claim 1 is combined with plum branch speckled glaze, it is characterised in that the yellowish pea green glaze
It is prepared by the raw material of following parts by weight：Feldspar 33, calcined kaolin 10, chalk 10, quartz 15, Suzhou soil 10, zirconium silicate
8th, talcum 5, dolomite 5, barium carbonate 2.5, iron oxide 1.5.
3. the porcelain that yellowish pea green glaze according to claim 1 or 2 is combined with plum branch speckled glaze, it is characterised in that the plum
Branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 30, quartz 25, pine ash 14, Suzhou soil 5, solo flight powder 10, oxygen
Change iron 6, talcum 3, barium carbonate 2, manganese dioxide 2, bone meal 2, cobalt oxide 1.
4. the porcelain that yellowish pea green glaze according to claim 1 is combined with plum branch speckled glaze, it is characterised in that the yellowish pea green glaze
It is prepared by the raw material of following parts by weight：Feldspar 33, calcined kaolin 13, chalk 11, quartz 13, Suzhou soil 8, zirconium silicate 6,
Talcum 7, dolomite 4, barium carbonate 3, iron oxide 2.
5. the porcelain that the yellowish pea green glaze according to claim 1 or 4 is combined with plum branch speckled glaze, it is characterised in that the plum
Branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 36, quartz 18, pine ash 9, Suzhou soil 8, solo flight powder 7, oxidation
Iron 8, talcum 2, barium carbonate 4, manganese dioxide 3, bone meal 3, cobalt oxide 2.
6. the porcelain that yellowish pea green glaze according to claim 1 is combined with plum branch speckled glaze, it is characterised in that the yellowish pea green glaze
It is prepared by the raw material of following parts by weight：Feldspar 34, calcined kaolin 13, chalk 12, quartz 10, Suzhou soil 10, zirconium silicate
9th, talcum 8, dolomite 2, barium carbonate 1, iron oxide 1.
7. the porcelain that the yellowish pea green glaze according to claim 1 or 6 is combined with plum branch speckled glaze, it is characterised in that plum branch spot
Point glaze is prepared by the raw material of following parts by weight：Feldspar 38, quartz 25, pine ash 7, Suzhou soil 7, solo flight powder 8, iron oxide 6,
Talcum 3, barium carbonate 2, manganese dioxide 2, bone meal 1, cobalt oxide 1.
8. the preparation technology for the porcelain that yellowish pea green glaze is combined with plum branch speckled glaze, it is characterised in that use the claims 1-7
The porcelain that yellowish pea green glaze described in middle any one is combined with plum branch speckled glaze, it is comprised the following steps that：
Step 1, yellowish pea green glaze and plum branch speckled glaze are prepared；
Step 2, yellowish pea green glaze is applied on ceramic body；
Step 3, plum branch speckled glaze is applied in pea green glaze paint by way of colored drawing after ceramic blank drying；
Step 4, after the drying of plum branch speckled glaze, ceramic body is put into kiln and fired；
Step 5, furnace heating-up, under reducing atmosphere, firing temperature is 1200-1300 DEG C；
Step 6, blow-on, the porcelain that yellowish pea green glaze is combined with plum branch speckled glaze is obtained after cooling.
9. the preparation technology for the porcelain that yellowish pea green glaze according to claim 8 is combined with plum branch speckled glaze, it is characterised in that：
Yellowish pea green glaze is milled into using wet bulb described in step 1, wherein expecting：Ball：Water=1：2：0.8, the plum branch speckled glaze uses wet ball mill
It is made, wherein expecting：Ball：Water=1：2：1.
10. the preparation technology for the porcelain that yellowish pea green glaze according to claim 8 is combined with plum branch speckled glaze, its feature exist
In：Firing temperature is 1290 DEG C in the step 5.