CN109912218A - With high temperature skyblue sagging decoration and preparation method thereof - Google Patents
With high temperature skyblue sagging decoration and preparation method thereof Download PDFInfo
- Publication number
- CN109912218A CN109912218A CN201711325507.4A CN201711325507A CN109912218A CN 109912218 A CN109912218 A CN 109912218A CN 201711325507 A CN201711325507 A CN 201711325507A CN 109912218 A CN109912218 A CN 109912218A
- Authority
- CN
- China
- Prior art keywords
- parts
- coat enamel
- overglaze
- ground coat
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high temperature skyblue sagging decoration, including ground coat enamel and overglaze, the component and each component mass parts of the ground coat enamel are as follows: 35 parts~42 parts of feldspar；14 parts~23 parts of dolomite；8 parts~16 parts of wollastonite；3 parts~6 parts of zinc oxide；6 parts~9 parts of barium carbonate；7 parts~11 parts of kaolin；13 parts~16 parts of zirconium silicate；The each component and each component content of overglaze are as follows: 30 parts~35 parts of potassium feldspar；10 parts~12 parts of calcite；14 parts~16 parts of dolomite；4 parts~6 parts of Jiepai clay；4 parts~5 parts of lithium carbonate；15 parts~16 parts of zinc oxide；5 parts~8 parts of iron oxide.The present invention is burnt under 1270 DEG C of oxidizing atmosphere by the double-deck gradual change between two kinds of glaze, and product sagging clapped in the plane is blue, and ground coat enamel is taupe brown crystallization effect, this is the combination of a kind of Modern Beauty and allusion；Product has certain mobility in the transmutation effect that skyblue is presented in cup class type, and the repacking decorations made compare more naturally, striking contrast is presented on product with artistry.This product is suitable for mass production, can adapt to demand both domestic and external.
Description
Technical field
The present invention relates to one kind to have high temperature skyblue sagging decoration and preparation method thereof.
Background technique
Currently, the moulding of porcelain billet is that the allotment of the base glaze of quality product makes porcelain more shine in ceramic industry
Brilliant, the porcelain billet of same moulding of eye often because of glaze difference, and makes the vision of consumer generate different influences, which exists
Sky blue transmutation effect is presented in plane, it is pure and fresh, it is natural；Sapphire transmutation effect, which is presented, in cup class type in product has one
Fixed mobility, the repacking decorations made are more naturally, more graduated colors are presented in color can adapt to more user crowds.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, provide a kind of with high temperature skyblue stream
Sapphire transmutation effect is presented with certain mobility in glaze decoration, product, and the repacking decorations made are more naturally, color is presented
More graduated colors can adapt to more user crowds.
In order to solve the above-mentioned technical problem, the technical scheme is that a kind of have high temperature skyblue sagging decoration, packet
Ground coat enamel and overglaze are included, the component and each component mass parts of the ground coat enamel are as follows:
35 parts~42 parts of feldspar；14 parts~23 parts of dolomite；8 parts~16 parts of wollastonite；3 parts~6 parts of zinc oxide；Barium carbonate
6 parts~9 parts；7 parts~11 parts of kaolin；13 parts~16 parts of zirconium silicate；The each component and each component content of overglaze are as follows: potassium feldspar
30 parts~35 parts；10 parts~12 parts of calcite；14 parts~16 parts of dolomite；4 parts~6 parts of Jiepai clay；4 parts~5 parts of lithium carbonate；Oxygen
Change 15 parts~16 parts of zinc；5 parts~8 parts of iron oxide.
The present invention also provides a kind of these to have the step of production method of high temperature skyblue sagging decoration, this method such as
Under:
A) it stocks up according to each component and each component mass parts:
B) ground coat enamel is by 1.45 ︰ 0.55 of ground coat enamel Liao ︰ Qiu ︰ water=1 ︰, and wet ball grinding 10~12 hours, the glaze mistake after ball milling
After 160 meshes, then it is tuned into the ground coat enamel slurry of 55~60 Baume degrees, the green body for taking appearance bright and clean immerses ground coat enamel slurry, stand-by after dry；
C) overglaze presses overglaze Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.6, and wet ball grinding 11~13 hours, the glaze after ball milling crossed 160
After mesh, then it is tuned into the overglaze slurry of 50~55 Baume degrees, the green body for having gone up ground coat enamel slurry is sprayed into overglaze slurry, through 1270~1280
DEG C oxidizing atmosphere under fire finished product.
After above-mentioned technical proposal, keep high temperature skyblue sagging decoration more steady by using new process production
It is fixed, by the double-deck reaction effect, so that the effect that transmutation is presented in glaze is made by mobile performance of the glaze in high-temperature fusion
The gradient color that possesses of the glaze, it is neither complicated ugly, but will not simple and aobvious dullness, and in 1270~1280 DEG C of down-draft kiln
It is rapidly fired to, it is novel to make glaze, and firing range is wide, glaze is beautiful, does things creatively, is well received by consumers.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one
The technical scheme is that a kind of have high temperature skyblue sagging decoration, including ground coat enamel and overglaze, the bottom
The component and each component mass parts of glaze are as follows:
35 parts~42 parts of feldspar；14 parts~23 parts of dolomite；8 parts~16 parts of wollastonite；3 parts~6 parts of zinc oxide；Barium carbonate
6 parts~9 parts；7 parts~11 parts of kaolin；13 parts~16 parts of zirconium silicate；The each component and each component content of overglaze are as follows: potassium feldspar
30 parts~35 parts；14 parts~16 parts of calcite；14 parts~16 parts of dolomite；4 parts~6 parts of Jiepai clay；4 parts~5 parts of lithium carbonate；Oxygen
Change 13 parts~15 parts of zinc；5 parts~8 parts of iron oxide.
The present invention also provides a kind of these to have the step of production method of high temperature skyblue sagging decoration, this method such as
Under:
A) it stocks up according to each component and each component mass parts:
B) ground coat enamel is by 1.45 ︰ 0.55 of ground coat enamel Liao ︰ Qiu ︰ water=1 ︰, and wet ball grinding 10~12 hours, the glaze mistake after ball milling
After 160 meshes, then it is tuned into the ground coat enamel slurry of 55~60 Baume degrees, the green body for taking appearance bright and clean immerses ground coat enamel slurry, stand-by after dry；
C) overglaze presses overglaze Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.6, and wet ball grinding 11~13 hours, the glaze after ball milling crossed 160
After mesh, then it is tuned into the overglaze slurry of 50~55 Baume degrees, the green body for having gone up ground coat enamel slurry is sprayed into overglaze slurry, through 1270~1280
DEG C oxidizing atmosphere under fire finished product.
Embodiment two
The technical scheme is that a kind of have high temperature skyblue sagging decoration, including ground coat enamel and overglaze, the bottom
The component and each component mass parts of glaze are as follows:
35 parts~42 parts of feldspar；14 parts~23 parts of dolomite；8 parts~16 parts of wollastonite；3 parts~6 parts of zinc oxide；Barium carbonate
6 parts~9 parts；7 parts~11 parts of kaolin；13 parts~16 parts of zirconium silicate；The each component and each component content of overglaze are as follows: potassium feldspar
30 parts~35 parts；4 parts~6 parts of calcite；14 parts~16 parts of dolomite；10 parts~12 parts of Jiepai clay；4 parts~5 parts of lithium carbonate；Oxygen
Change 15 parts~16 parts of zinc；5 parts~8 parts of iron oxide.
The present invention also provides a kind of these to have the step of production method of high temperature skyblue sagging decoration, this method such as
Under:
A) it stocks up according to each component and each component mass parts:
B) ground coat enamel is by 1.45 ︰ 0.55 of ground coat enamel Liao ︰ Qiu ︰ water=1 ︰, and wet ball grinding 10~12 hours, the glaze mistake after ball milling
After 160 meshes, then it is tuned into the ground coat enamel slurry of 55~60 Baume degrees, the green body for taking appearance bright and clean immerses ground coat enamel slurry, stand-by after dry；
C) overglaze presses overglaze Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.6, and wet ball grinding 11~13 hours, the glaze after ball milling crossed 160
After mesh, then it is tuned into the overglaze slurry of 50~55 Baume degrees, the green body for having gone up ground coat enamel slurry is sprayed into overglaze slurry, through 1270~1280
DEG C oxidizing atmosphere under fire finished product.
Embodiment three
The technical scheme is that a kind of have high temperature skyblue sagging decoration, including ground coat enamel and overglaze, the bottom
The component and each component mass parts of glaze are as follows:
35 parts~42 parts of feldspar；14 parts~23 parts of dolomite；8 parts~16 parts of wollastonite；3 parts~6 parts of zinc oxide；Barium carbonate
6 parts~9 parts；7 parts~11 parts of kaolin；13 parts~16 parts of zirconium silicate；The each component and each component content of overglaze are as follows: potassium feldspar
30 parts~35 parts；10 parts~12 parts of calcite；14 parts~16 parts of dolomite；4 parts~6 parts of Jiepai clay；4 parts~5 parts of lithium carbonate；Oxygen
Change 15 parts~16 parts of zinc；5 parts~8 parts of iron oxide.
The present invention also provides a kind of these to have the step of production method of high temperature skyblue sagging decoration, this method such as
Under:
A) it stocks up according to each component and each component mass parts:
B) ground coat enamel is by 1.45 ︰ 0.55 of ground coat enamel Liao ︰ Qiu ︰ water=1 ︰, and wet ball grinding 10~12 hours, the glaze mistake after ball milling
After 160 meshes, then it is tuned into the ground coat enamel slurry of 55~60 Baume degrees, the green body for taking appearance bright and clean immerses ground coat enamel slurry, stand-by after dry；
C) overglaze presses overglaze Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.6, and wet ball grinding 11~13 hours, the glaze after ball milling crossed 160
After mesh, then it is tuned into the overglaze slurry of 50~55 Baume degrees, the green body for having gone up ground coat enamel slurry is sprayed into overglaze slurry, through 1270~1280
DEG C oxidizing atmosphere under fire finished product.
Above three embodiments preparation has high temperature skyblue sagging decoration, and transmutation effect is presented in glaze, simultaneously
With certain mobility, example one: temperature flowing is too strong, so that the product haftplatte；Example two: temperature flowing is weaker, so that
The product fade effect is weaker, and sense organ is undesirable.Example three: the product meets needed for this invention.Day is presented in product in the plane
Blue transmutation effect, it is pure and fresh, it is natural；Sapphire transmutation effect, which is presented, in cup class type in product has certain mobility,
The repacking decorations made are more naturally, color is presented with more graduated colors.This product is suitable for mass production, can adapt to the country
Outer demand.
Particular embodiments described above, pair present invention solves the technical problem that, technical scheme and beneficial effects carry out
It is further described, it should be understood that the above is only a specific embodiment of the present invention, is not limited to this
Invention, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should be included in this hair
Within bright protection scope.
Claims (2)
1. the invention discloses one kind to have high temperature skyblue sagging decoration, including ground coat enamel and overglaze, the component of the ground coat enamel
It is as follows with each component mass parts:
35 parts~42 parts of feldspar；14 parts~23 parts of dolomite；8 parts~16 parts of wollastonite；3 parts~6 parts of zinc oxide；6 parts of barium carbonate
~9 parts；7 parts~11 parts of kaolin；13 parts~16 parts of zirconium silicate；The each component and each component content of overglaze are as follows: potassium feldspar 30
Part~35 parts；10 parts~12 parts of calcite；14 parts~16 parts of dolomite；4 parts~6 parts of Jiepai clay；4 parts~5 parts of lithium carbonate；Oxidation
15 parts~16 parts of zinc；5 parts~8 parts of iron oxide.
2. a kind of production method as described in claim 1 with high temperature skyblue sagging decoration, it is characterised in that this method
The step of it is as follows:
A) it stocks up according to each component and each component mass parts:
B) ground coat enamel presses ground coat enamel Liao ︰ Qiu ︰ water=1 ︰, 1.45 ︰ 0.55, and wet ball grinding 10~12 hours, the glaze after ball milling crossed 160 mesh
After sieve, then it is tuned into the ground coat enamel slurry of 55~60 Baume degrees, the green body for taking appearance bright and clean immerses ground coat enamel slurry, stand-by after dry；
C) overglaze presses overglaze Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.6, and wet ball grinding 11~13 hours, the glaze after ball milling crossed 160 meshes
Afterwards, then be tuned into 50~55 Baume degrees overglaze slurry, will go up ground coat enamel slurry green body spray the overglaze starch, through 1270~1280 DEG C
Finished product is fired under oxidizing atmosphere.