CN109133646A - Bilayer reaction fancy glaze and preparation method thereof - Google Patents
Bilayer reaction fancy glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109133646A CN109133646A CN201811143817.9A CN201811143817A CN109133646A CN 109133646 A CN109133646 A CN 109133646A CN 201811143817 A CN201811143817 A CN 201811143817A CN 109133646 A CN109133646 A CN 109133646A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- glaze
- coat enamel
- ground coat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of double-deck reaction fancy glazes and preparation method thereof, and bilayer reaction fancy glaze contains ground coat enamel and overglaze, wherein, the component and each component mass parts that ground coat enamel material contains used in ground coat enamel are as follows: 10~15 parts of low temperature frit, 20~25 parts of feldspar powder, 30~35 parts of silica flour, 18~22 parts of calcite, 5~10 parts of spodumene of calcining, 2~4 parts of calcinated talc powder, 8~12 parts of calcining zinc oxide, 8~10 parts of barium carbonate, 4~6 parts of zirconium silicate, 10~15 parts of Jiepai clay；The component and each component mass parts that glaze material used in overglaze contains are as follows: 15~20 parts of low temperature frit, 20~25 parts of silica flour, 28~32 parts of calcite, 4~8 parts of calcining zinc oxide, 2~4 parts of barium carbonate, 4~8 parts of aluminium powder, 2~4 parts of calcinated talc powder, 3~6 parts of titanium oxide, 3~6 parts of Guizhou clay.The effect of reaction fancy glaze is presented in the glaze paint of bilayer reaction fancy glaze, with bright and colourful beauty, people is allowed to feel that all things on earth is recovered, the vigor full of sunlight is deep to be liked by the majority of consumers.
Description
Technical field
The present invention relates to a kind of double-deck reaction fancy glazes and preparation method thereof.
Background technique
Currently, the moulding of porcelain billet is the basis of quality product in porcelain industry, the allotment of glaze keeps porcelain more gorgeous
Colorful, the porcelain billet of same moulding often because of the difference of glaze paint, and generates different influences to the vision of consumer.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of double-deck reaction fancy glaze is provided, it
Glaze paint the effect of reaction fancy glaze be presented allow people to feel that all things on earth is recovered with bright and colourful beauty, the vigor full of sunlight,
It is deep to be liked by the majority of consumers.
In order to solve the above-mentioned technical problem, the technical scheme is that a kind of double-deck reaction fancy glaze, it contain ground coat enamel and
Overglaze, wherein the component and each component mass parts that ground coat enamel material contains used in ground coat enamel are as follows:
10~15 parts of low temperature frit, 20~25 parts of feldspar powder, 30~35 parts of silica flour, 18~22 parts of calcite, calcine lithium
5~10 parts of pyroxene, 2~4 parts of calcinated talc powder, 8~12 parts of calcining zinc oxide, 8~10 parts of barium carbonate, 4~6 parts of zirconium silicate, boundary
10~15 parts of board mud；
The component and each component mass parts that glaze material used in overglaze contains are as follows:
15~20 parts of low temperature frit, 20~25 parts of silica flour, 28~32 parts of calcite, 4~8 parts of calcining zinc oxide, carbonic acid
2~4 parts of barium, 4~8 parts of aluminium powder, 2~4 parts of calcinated talc powder, 3~6 parts of titanium oxide, 3~6 parts of Guizhou clay.
Further, the component of the low temperature frit and the mass parts of each component are as follows: feldspar powder: 20~25 parts；Lithium carbonate:
20 parts~25 parts；Borax: 25 parts~30 parts；Silica flour: 25 parts~30 parts.
Further, 1350~1400 DEG C of temperature calcination of spodumene, forms calcining spodumene.
Further, 1160~1200 DEG C of temperature calcination of zinc oxide, forms calcining zinc oxide.
The present invention also provides a kind of preparation method of double-deck reaction fancy glaze, the step of method in contain:
S1: ground coat enamel slurry and overglaze slurry are prepared respectively；Wherein, the preparation process that the preparation process of ground coat enamel slurry and overglaze are starched is such as
Under: it stocks up respectively according to the mass parts of each component and each component；According to material: ball: mass ratio=1:1.5:0.5 of water, wet process ball
Then mill 8~10 hours crosses 160 mesh screens, then be tuned into the glaze slip that concentration is 53-63 Baume degrees；
S2: ground coat enamel is applied on biscuit using ground coat enamel slurry, then spray plane glaze is starched using overglaze, enters kiln after dry, by 1160-
1200 DEG C of temperature environment burns finished product.
After above-mentioned technical proposal, the effect of reaction fancy glaze is presented in the glaze paint of the double-deck reaction fancy glaze of the invention, with
Bright and colourful beauty, allows people to feel that all things on earth is recovered, and the vigor full of sunlight is deep to be liked by the majority of consumers.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one
A kind of double-deck reaction fancy glaze, it contains ground coat enamel and overglaze, wherein ground coat enamel material contains used in ground coat enamel component and
Each component mass parts are as follows:
10 parts of low temperature frit, 20 parts of feldspar powder, 30 parts of silica flour, 18 parts of calcite, 5 parts of spodumene are calcined, calcination of talc
2 parts of powder, 8 parts of calcining zinc oxide, 8 parts of barium carbonate, 4 parts of zirconium silicate, 10 parts of Jiepai clay；
The component and each component mass parts that glaze material used in overglaze contains are as follows:
It 15 parts of low temperature frit, 20 parts of silica flour, 28 parts of calcite, 4 parts of calcining zinc oxide, 2 parts of barium carbonate, 4 parts of aluminium powder, forges
2 parts of burning talcum powder, 3 parts of titanium oxide, 3 parts of Guizhou clay.
The component of the low temperature frit and the mass parts of each component are as follows: feldspar powder: 20 parts；Lithium carbonate: 20 parts；Borax:
25 parts；Silica flour: 25 parts.
1350~1400 DEG C of temperature calcination of spodumene, forms calcining spodumene.
1160~1200 DEG C of temperature calcination of zinc oxide, forms calcining zinc oxide.
Contain in the step of preparation method of bilayer reaction fancy glaze, method:
S1: ground coat enamel slurry and overglaze slurry are prepared respectively；Wherein, the preparation process that the preparation process of ground coat enamel slurry and overglaze are starched is such as
Under: it stocks up respectively according to the mass parts of each component and each component；According to material: ball: mass ratio=1:1.5:0.5 of water, wet process ball
Then mill 8 hours crosses 160 mesh screens, then be tuned into the glaze slip that concentration is 53-63 Baume degrees；
S2: ground coat enamel is applied on biscuit using ground coat enamel slurry, then spray plane glaze is starched using overglaze, enters kiln after dry, by 1160-
1200 DEG C of temperature environment burns finished product.
Embodiment two
A kind of double-deck reaction fancy glaze, it contains ground coat enamel and overglaze, wherein ground coat enamel material contains used in ground coat enamel component and
Each component mass parts are as follows:
15 parts of low temperature frit, 25 parts of feldspar powder, 35 parts of silica flour, 22 parts of calcite, 10 parts of spodumene are calcined, calcination of talc
4 parts of powder, 12 parts of calcining zinc oxide, 10 parts of barium carbonate, 6 parts of zirconium silicate, 15 parts of Jiepai clay；
The component and each component mass parts that glaze material used in overglaze contains are as follows:
It 20 parts of low temperature frit, 25 parts of silica flour, 32 parts of calcite, 8 parts of calcining zinc oxide, 4 parts of barium carbonate, 8 parts of aluminium powder, forges
4 parts of burning talcum powder, 6 parts of titanium oxide, 6 parts of Guizhou clay.
The component of the low temperature frit and the mass parts of each component are as follows: feldspar powder: 25 parts；Lithium carbonate: 25 parts；Borax:
30 parts；Silica flour: 30 parts.
1350~1400 DEG C of temperature calcination of spodumene, forms calcining spodumene.
1160~1200 DEG C of temperature calcination of zinc oxide, forms calcining zinc oxide.
Contain in the step of preparation method of bilayer reaction fancy glaze, method:
S1: ground coat enamel slurry and overglaze slurry are prepared respectively；Wherein, the preparation process that the preparation process of ground coat enamel slurry and overglaze are starched is such as
Under: it stocks up respectively according to the mass parts of each component and each component；According to material: ball: mass ratio=1:1.5:0.5 of water, wet process ball
Then mill 10 hours crosses 160 mesh screens, then be tuned into the glaze slip that concentration is 53-63 Baume degrees；
S2: ground coat enamel is applied on biscuit using ground coat enamel slurry, then spray plane glaze is starched using overglaze, enters kiln after dry, by 1160-
1200 DEG C of temperature environment burns finished product.
Embodiment three
A kind of double-deck reaction fancy glaze, it contains ground coat enamel and overglaze, wherein ground coat enamel material contains used in ground coat enamel component and
Each component mass parts are as follows:
13 parts of low temperature frit, 22 parts of feldspar powder, 32 parts of silica flour, 20 parts of calcite, 8 parts of spodumene are calcined, calcination of talc
3 parts of powder, 10 parts of calcining zinc oxide, 9 parts of barium carbonate, 5 parts of zirconium silicate, 13 parts of Jiepai clay；
The component and each component mass parts that glaze material used in overglaze contains are as follows:
It 17 parts of low temperature frit, 22 parts of silica flour, 30 parts of calcite, 6 parts of calcining zinc oxide, 3 parts of barium carbonate, 6 parts of aluminium powder, forges
3 parts of burning talcum powder, 4 parts of titanium oxide, 5 parts of Guizhou clay.
The component of the low temperature frit and the mass parts of each component are as follows: feldspar powder: 22 parts；Lithium carbonate: 22 parts；Borax:
27 parts；Silica flour: 27 parts.
1350~1400 DEG C of temperature calcination of spodumene, forms calcining spodumene.
1160~1200 DEG C of temperature calcination of zinc oxide, forms calcining zinc oxide.
Contain in the step of preparation method of bilayer reaction fancy glaze, method:
S1: ground coat enamel slurry and overglaze slurry are prepared respectively；Wherein, the preparation process that the preparation process of ground coat enamel slurry and overglaze are starched is such as
Under: it stocks up respectively according to the mass parts of each component and each component；According to material: ball: mass ratio=1:1.5:0.5 of water, wet process ball
Then mill 9 hours crosses 160 mesh screens, then be tuned into the glaze slip that concentration is 53-63 Baume degrees；
S2: ground coat enamel is applied on biscuit using ground coat enamel slurry, then spray plane glaze is starched using overglaze, enters kiln after dry, by 1160-
1200 DEG C of temperature environment burns finished product.
The double-deck reaction fancy glaze that three above embodiment is prepared, by it has been observed that reaction can be presented in its glaze paint
The effect of fancy glaze, meets design requirement.
Particular embodiments described above, pair present invention solves the technical problem that, technical scheme and beneficial effects carry out
It is further described, it should be understood that the above is only a specific embodiment of the present invention, is not limited to this
Invention, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should be included in this hair
Within bright protection scope.
Claims (5)
1. a kind of double-deck reaction fancy glaze, it is characterised in that it contains ground coat enamel and overglaze, wherein ground coat enamel material used in ground coat enamel contains
Component and each component mass parts it is as follows:
10~15 parts of low temperature frit, 20~25 parts of feldspar powder, 30~35 parts of silica flour, 18~22 parts of calcite, calcine spodumene 5
~10 parts, 2~4 parts of calcinated talc powder, 8~12 parts of calcining zinc oxide, 8~10 parts of barium carbonate, 4~6 parts of zirconium silicate, Jiepai clay 10
~15 parts；
The component and each component mass parts that glaze material used in overglaze contains are as follows:
15~20 parts of low temperature frit, 20~25 parts of silica flour, 28~32 parts of calcite, 4~8 parts of calcining zinc oxide, barium carbonate 2~
4 parts, 4~8 parts of aluminium powder, 2~4 parts of calcinated talc powder, 3~6 parts of titanium oxide, 3~6 parts of Guizhou clay.
2. the double-deck reaction fancy glaze according to claim 1, it is characterised in that: the component of the low temperature frit and each component
Mass parts are as follows: feldspar powder: 20~25 parts；Lithium carbonate: 20 parts~25 parts；Borax: 25 parts~30 parts；Silica flour: 25 parts~30
Part.
3. the double-deck reaction fancy glaze according to claim 1, it is characterised in that: spodumene is forged with 1350~1400 DEG C of temperature
It burns, forms calcining spodumene.
4. the double-deck reaction fancy glaze according to claim 1, it is characterised in that: zinc oxide is forged with 1160~1200 DEG C of temperature
It burns, forms calcining zinc oxide.
5. a kind of preparation method of the double-deck reaction fancy glaze as described in Claims 1 to 4, it is characterised in that contain in the step of method
Have:
S1: ground coat enamel slurry and overglaze slurry are prepared respectively；Wherein, the preparation process of ground coat enamel slurry and the preparation process of overglaze slurry are as follows:
It stocks up respectively according to the mass parts of each component and each component；According to material: ball: mass ratio=1:1.5:0.5 of water, wet ball grinding 8
~10 hours, 160 mesh screens are then crossed, then are tuned into the glaze slip that concentration is 53-63 Baume degrees；
S2: ground coat enamel is applied on biscuit using ground coat enamel slurry, then spray plane glaze is starched using overglaze, enters kiln after dry, by 1160-1200
DEG C temperature environment burn finished product.