CN103224411A - Producing method of tiger fur glaze and tiger fur glaze used by same - Google Patents
Producing method of tiger fur glaze and tiger fur glaze used by same Download PDFInfo
- Publication number
- CN103224411A CN103224411A CN2013101158338A CN201310115833A CN103224411A CN 103224411 A CN103224411 A CN 103224411A CN 2013101158338 A CN2013101158338 A CN 2013101158338A CN 201310115833 A CN201310115833 A CN 201310115833A CN 103224411 A CN103224411 A CN 103224411A
- Authority
- CN
- China
- Prior art keywords
- parts
- coat enamel
- glaze
- ground
- tiger fur
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a producing method of tiger fur glaze and the tiger fur glaze used by same. The producing method of the tiger fur glaze comprises: (1) preparing ground coat and overglaze according to specified components by weight parts; (2) performing wet milling for the ground coat for 6-8 hours according to a proportion of the ground coat, ball and water being 1 : 1.5 : 0.5, sieving the milled glaze with a 160-mesh sieve, mixing into a ground coat slurry of 50-70 Baume degrees, immersing green body with smooth surface into the ground coat slurry, and drying for later use; and (3) performing wet milling for the overglaze for 6-8 hours according to a proportion of the overglaze, ball and water being 1 : 1.5 : 0.5, sieving the milled glaze with a 160-mesh sieve, mixing into a overglaze slurry of 50-70 Baume degrees, spraying the overglaze slurry onto the green body already with the ground coat slurry, and firing to obtain finish product under an oxidizing atmosphere of 1160-1200 DEG C. The tiger fur glaze produced by the invention shows a tiger fur pattern, is gorgeous and noble in appearance, thereby being memorable.
Description
Technical field
The present invention relates to a kind of making method of tiger fur glaze and the tiger fur glaze glaze of use thereof.
Background technology
At present, in ceramic industry, the moulding of porcelain base is that the allotment of the basic glaze of quality products makes porcelain more dazzling brilliant, the porcelain base of same moulding, often because of the glaze difference, and make human consumer's vision produce different influences, the sort of tiger fur decorative pattern that is, give the porcelain of the impression of a kind of magnificent wealth and rank of people, product when this also is current porcelain industry a kind of.
Summary of the invention
Technical problem to be solved by this invention is to overcome the deficiencies in the prior art, and a kind of making method of tiger fur glaze is provided, and the tiger fur glaze of making by it is the tiger fur decorative pattern, gives the impression of a kind of magnificent wealth and rank of people, and it is unforgettable that the people is looked over so as to check.
In order to solve the problems of the technologies described above, technical scheme of the present invention is: a kind of making method of tiger fur glaze, and the step of this method is as follows: get the raw materials ready according to following component and each component weight part (1): A, ground-coat enamel: 8 parts～10 parts of barium carbonates; 18 parts～20 parts of Feldspar Powders; 15 parts～18 parts of silica powders; 15 parts～18 parts in calcite; 30 parts～35 parts of low temperature frits; 15 parts～17 parts of kaolin; 6 parts～8 parts in zinc oxide; 6 parts～9 parts of manganous carbonate or ferric oxide; B, cover-coat enamel: 10 parts～15 parts of low temperature frits; 26 parts～30 parts of silica powders; 13 parts～18 parts in calcite; 6 parts～9 parts in zinc oxide; 6 parts～9 parts of talcum powder; 8 parts～12 parts of zirconium silicates; 4 parts～8 parts of kaolin; 8 parts～12 parts in silver grey colorant; (2) ground-coat enamel is pressed ground-coat enamel Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours, and after the glaze behind the ball milling was crossed 160 mesh sieves, the ground-coat enamel of furnishing 50 ~ 70 degree Beaume slurry was got the bright and clean base substrate of appearance and is immersed this ground-coat enamel slurry again, and dry back is stand-by; (3) cover-coat enamel is pressed cover-coat enamel Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours, after the glaze behind the ball milling was crossed 160 mesh sieves, the cover-coat enamel of furnishing 50 ~ 70 degree Beaume was starched again, the base substrate of upper base glaze slip is sprayed this cover-coat enamel slurry, under 1160 ~ 1200 ℃ oxidizing atmosphere, fire finished product.
The present invention also provides the tiger fur glaze that uses in a kind of making method of tiger fur glaze glaze, comprises ground-coat enamel and cover-coat enamel, and the component of described ground-coat enamel and each component weight part are as follows: 8 parts～10 parts of barium carbonates; 18 parts～20 parts of Feldspar Powders; 15 parts～18 parts of silica powders; 15 parts～18 parts in calcite; 30 parts～35 parts of low temperature frits; 15 parts～17 parts of kaolin; 6 parts～8 parts in zinc oxide; 6 parts～9 parts of manganous carbonate or ferric oxide; The component of described cover-coat enamel and each component weight part are as follows: 10 parts～15 parts of low temperature frits; 26 parts～30 parts of silica powders; 13 parts～18 parts in calcite; 6 parts～9 parts in zinc oxide; 6 parts～9 parts of talcum powder; 8 parts～12 parts of zirconium silicates; 4 parts～8 parts of kaolin; 8 parts～12 parts in silver grey colorant.
After having adopted technique scheme, find that through experimenter's repeatedly Experiment Preparation the present invention can make the porcelain glaze present tiger fur decorative pattern shape, give the impression of a kind of magnificent wealth and rank of people, make people's unforgettable effect of looking over so as to check.
Embodiment
Content of the present invention is easier to be expressly understood that below according to specific embodiment, the present invention is further detailed explanation in order to make,
Embodiment one
A kind of tiger fur glaze glaze comprises ground-coat enamel and cover-coat enamel, and the component of ground-coat enamel and each component weight part are as follows: 8 parts of barium carbonates; 18 parts of Feldspar Powders; 15 parts of silica powders; 15 parts in calcite; 30 parts of low temperature frits; 15 parts of kaolin; 6 parts in zinc oxide; 6 parts of manganous carbonates; The component of cover-coat enamel and each component weight part are as follows: 10 parts of low temperature frits; 26 parts of silica powders; 14 parts in calcite; 7 parts in zinc oxide; 6 parts of talcum powder; 8 parts of zirconium silicates; 4 parts of kaolin; 8 parts in silver grey colorant.
A kind of making method of tiger fur glaze, the step of this method is as follows:
(1) be equipped with ground-coat enamel material and glaze material respectively according to above component and each component weight part:
(2) ground-coat enamel is pressed ground-coat enamel Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours, and after the glaze behind the ball milling was crossed 160 mesh sieves, the ground-coat enamel of furnishing 50 ~ 70 degree Beaume slurry was got the bright and clean base substrate of appearance and is immersed this ground-coat enamel slurry again, and dry back is stand-by;
(3) cover-coat enamel is pressed cover-coat enamel Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours, after the glaze behind the ball milling was crossed 160 mesh sieves, the cover-coat enamel of furnishing 50 ~ 70 degree Beaume was starched again, the base substrate of upper base glaze slip is sprayed this cover-coat enamel slurry, under 1160 ~ 1200 ℃ oxidizing atmosphere, fire finished product.
The tiger fur glaze glaze that this method is burnt till presents tiger fur decorative pattern shape, gives the impression of a kind of magnificent wealth and rank of people, makes people's unforgettable effect of looking over so as to check.
Embodiment two
A kind of tiger fur glaze glaze comprises ground-coat enamel and cover-coat enamel, and the component of ground-coat enamel and each component weight part are as follows: 10 parts of barium carbonates; 19 parts of Feldspar Powders; 18 parts of silica powders; 18 parts in calcite; 34 parts of low temperature frits; 17 parts of kaolin; 8 parts in zinc oxide; 9 parts of ferric oxide; The component of cover-coat enamel and each component weight part are as follows: 15 parts of low temperature frits; 30 parts of silica powders; 18 parts in calcite; 9 parts in zinc oxide; 9 parts of talcum powder; 12 parts of zirconium silicates; 8 parts of kaolin; 12 parts in silver grey colorant.
A kind of making method of tiger fur glaze, the step of this method is as follows:
(1) be equipped with ground-coat enamel material and glaze material respectively according to above component and each component weight part:
(2) ground-coat enamel is pressed ground-coat enamel Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours, and after the glaze behind the ball milling was crossed 160 mesh sieves, the ground-coat enamel of furnishing 50 ~ 70 degree Beaume slurry was got the bright and clean base substrate of appearance and is immersed this ground-coat enamel slurry again, and dry back is stand-by;
(3) cover-coat enamel is pressed cover-coat enamel Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours, after the glaze behind the ball milling was crossed 160 mesh sieves, the cover-coat enamel of furnishing 50 ~ 70 degree Beaume was starched again, the base substrate of upper base glaze slip is sprayed this cover-coat enamel slurry, under 1160 ~ 1200 ℃ oxidizing atmosphere, fire finished product.
The tiger fur glaze glaze that this method is burnt till also presents tiger fur decorative pattern shape, gives the impression of a kind of magnificent wealth and rank of people, makes people's unforgettable effect of looking over so as to check.
Embodiment three
A kind of tiger fur glaze glaze comprises ground-coat enamel and cover-coat enamel, and the component of ground-coat enamel and each component weight part are as follows: 9 parts of barium carbonates; 19 parts of Feldspar Powders; 17 parts of silica powders; 16 parts in calcite; 34 parts of low temperature frits; 16 parts of kaolin; 7 parts in zinc oxide; 7 parts of ferric oxide; The component of cover-coat enamel and each component weight part are as follows: 12 parts of low temperature frits; 28 parts of silica powders; 15 parts in calcite; 7 parts in zinc oxide; 8 parts of talcum powder; 10 parts of zirconium silicates; 6 parts of kaolin; 10 parts in silver grey colorant.
A kind of making method of tiger fur glaze, the step of this method is as follows:
(1) be equipped with ground-coat enamel material and glaze material respectively according to above component and each component weight part:
(2) ground-coat enamel is pressed ground-coat enamel Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours, and after the glaze behind the ball milling was crossed 160 mesh sieves, the ground-coat enamel of furnishing 50 ~ 70 degree Beaume slurry was got the bright and clean base substrate of appearance and is immersed this ground-coat enamel slurry again, and dry back is stand-by;
(3) cover-coat enamel is pressed cover-coat enamel Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours, after the glaze behind the ball milling was crossed 160 mesh sieves, the cover-coat enamel of furnishing 50 ~ 70 degree Beaume was starched again, the base substrate of upper base glaze slip is sprayed this cover-coat enamel slurry, under 1160 ~ 1200 ℃ oxidizing atmosphere, fire finished product.
The tiger fur glaze glaze that this method is burnt till also presents tiger fur decorative pattern shape, gives the impression of a kind of magnificent wealth and rank of people, makes people's unforgettable effect of looking over so as to check.
Above-mentioned three embodiment, the value of having got three scopes in upper, middle and lower of each component weight part respectively detects, can draw preparation repeatedly through the experimenter, making method of the present invention and tiger fur glaze glaze still can make the porcelain glaze present tiger fur decorative pattern shape, give the impression of a kind of magnificent wealth and rank of people, make people's unforgettable effect of looking over so as to check.
Above-described specific embodiment; purpose of the present invention, technical scheme and beneficial effect are further described; institute is understood that; the above only is specific embodiments of the invention; be not limited to the present invention; within the spirit and principles in the present invention all, any modification of being made, be equal to replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (2)
1. the making method of a tiger fur glaze is characterized in that the step of this method is as follows:
(1) get the raw materials ready according to following component and each component weight part:
A, ground-coat enamel:
8 parts～10 parts of barium carbonates; 18 parts～20 parts of Feldspar Powders;
15 parts～18 parts of silica powders; 15 parts～18 parts in calcite;
30 parts～35 parts of low temperature frits; 15 parts～17 parts of kaolin;
6 parts～8 parts in zinc oxide; 6 parts～9 parts of manganous carbonate or ferric oxide;
B, cover-coat enamel:
10 parts～15 parts of low temperature frits; 26 parts～30 parts of silica powders;
13 parts～18 parts in calcite; 6 parts～9 parts in zinc oxide;
6 parts～9 parts of talcum powder; 8 parts～12 parts of zirconium silicates;
4 parts～8 parts of kaolin; 8 parts～12 parts in silver grey colorant;
(2) ground-coat enamel is pressed ground-coat enamel Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours, and after the glaze behind the ball milling was crossed 160 mesh sieves, the ground-coat enamel of furnishing 50 ~ 70 degree Beaume slurry was got the bright and clean base substrate of appearance and is immersed this ground-coat enamel slurry again, and dry back is stand-by;
(3) cover-coat enamel is pressed cover-coat enamel Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours, after the glaze behind the ball milling was crossed 160 mesh sieves, the cover-coat enamel of furnishing 50 ~ 70 degree Beaume was starched again, the base substrate of upper base glaze slip is sprayed this cover-coat enamel slurry, under 1160 ~ 1200 ℃ oxidizing atmosphere, fire finished product.
2. employed tiger fur glaze glaze in the making method of a tiger fur glaze as claimed in claim 1 comprises ground-coat enamel and cover-coat enamel, and it is characterized in that: the component of described ground-coat enamel and each component weight part are as follows: 8 parts～10 parts of barium carbonates; 18 parts～20 parts of Feldspar Powders; 15 parts～18 parts of silica powders; 15 parts～18 parts in calcite; 30 parts～35 parts of low temperature frits; 15 parts～17 parts of kaolin; 6 parts～8 parts in zinc oxide; 6 parts～9 parts of manganous carbonate or ferric oxide; The component of described cover-coat enamel and each component weight part are as follows: 10 parts～15 parts of low temperature frits; 26 parts～30 parts of silica powders; 13 parts～18 parts in calcite; 6 parts～9 parts in zinc oxide; 6 parts～9 parts of talcum powder; 8 parts～12 parts of zirconium silicates; 4 parts～8 parts of kaolin; 8 parts～12 parts in silver grey colorant.