CN102442841A - Panther print glaze and preparation and use method thereof - Google Patents
Panther print glaze and preparation and use method thereof Download PDFInfo
- Publication number
- CN102442841A CN102442841A CN2011103080790A CN201110308079A CN102442841A CN 102442841 A CN102442841 A CN 102442841A CN 2011103080790 A CN2011103080790 A CN 2011103080790A CN 201110308079 A CN201110308079 A CN 201110308079A CN 102442841 A CN102442841 A CN 102442841A
- Authority
- CN
- China
- Prior art keywords
- weight parts
- parts
- glaze
- ceramic
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a panther print glaze and a preparation and use method thereof. The ceramic glaze comprises dry powder and water and is characterized in that the dry powder is prepared from the following raw materials in part by weight: 60 parts of feldspar, 7-10 parts of calcite, 6-10 parts of magnesia, 5-7 parts of quartz, 8-10 parts of kaolin, 3-7 parts of alumina powder, 6-8 parts of barium carbonate, 1-2 parts of cobalt oxide, 2-4 parts of ferric oxide, 2-4 parts of manganese oxide and 1-2 parts of nickel oxide. According to the panther print glaze and the preparation and use method thereof provided by the invention, due to the adoption of a unique ceramic formula and a production process, ceramic products with the panther print effect are obtained and stronger decorative effect is obtained.
Description
Technical field
The present invention relates to a kind of leopard line glaze and preparation and method of use, belong to the ceramic technology field.
Background technology
Along with ceramic gets into huge numbers of families, ceramic glaze is the indispensable finishing material of ceramic, and existing ceramic glaze is can rough classification following according to classification and purposes: 1, lead glaze and leadless glaze; 2, raw glaze and fritted glaze; 3, once-firing or twice firing are used glaze; 4, ceramic tile, tableware, snitaryware and electroceramics are used glaze; 5, soak glaze, glaze spraying, water glaze by what enameling method was divided; 6, high melting glaze and low temperature glaze; 7, high expansion glaze and low bulk glaze; 8, firing atmosphere oxydizing flame, neutral flame and reducing flame; 9, coloured glaze and colourless glaze; 10, transparent and opaque glaze; 11, bright glaze, matt glaze, semi-mat glaze or figure glaze or the like.The stability of ceramic glaze, variety, glaze is decorated, pattern decoration has become the target that China pottery producer is pursued.
Summary of the invention
The purpose of this invention is to provide a kind of leopard line glaze and preparation and method of use.
In order to achieve the above object; The invention provides a kind of ceramic glaze; Comprise dry powder and water; It is characterized in that described dry powder is processed by feldspar 60 weight parts, calcite 7～10 weight parts, Natural manganese dioxide 6～10 weight parts, quartzy 5～7 weight parts, kaolin 8～10 weight parts, aluminum oxide powder 3～7 weight parts, barium carbonate 6～8 weight parts, powder blue 1～2 weight part, red stone 2～4 weight parts, manganese oxide 2～4 weight parts and nickel oxide 1～2 weight part.
The present invention also provides the preparation method of above-mentioned ceramic glaze; It is characterized in that; Comprise: feldspar, calcite, Natural manganese dioxide, quartz, kaolin, aluminum oxide powder, barium carbonate, powder blue, red stone, manganese oxide and nickel oxide proportional mixing are obtained dry powder; Dry powder and water are mixed according to weight ratio 100:45～55, be ground to 150～250 orders, obtain ceramic glaze.
The present invention also provides the method for use of above-mentioned ceramic glaze; It is characterized in that; Comprise: ceramic glaze is mixed with water, and the weight concentration of ceramic glaze is 39～49% in the gained mixed solution, thereby ceramic body is immersed in the mixed solution mixed solution is applied on the ceramic body; In reducing atmosphere, fired the ceramic product that obtains having leopard line effect 8～10 hours at 1280～1300 ℃.
Advantage of the present invention is:
1, the present invention has adopted distinctive ceramic glaze prescription and manufacture craft, the ceramic product that has obtained having leopard line effect, and decorative effect is stronger.
2, preparation and method of use are simple, and production cost is low.
Embodiment
Specify the present invention below in conjunction with embodiment.Ceramic body among the embodiment 1-3 is for to fire the biscuit that forms by commercially available ceramic base-material, and described reducing atmosphere is a carbon monoxide atmosphere.
Embodiment 1
Potassium felspar sand 60 weight parts, calcite 7 weight parts, Natural manganese dioxide 6 weight parts, quartzy 5 weight parts, kaolin 8 weight parts, aluminum oxide powder 3 weight parts, barium carbonate 6 weight parts, powder blue 1 weight part, red stone 2 weight parts, manganese oxide 2 weight parts and nickel oxide 1 weight part proportional mixing are obtained dry powder; Dry powder and water are mixed according to weight ratio 100:45; Be ground to 150 orders, obtain ceramic glaze.
Ceramic glaze is mixed with water; The weight concentration of ceramic glaze is 39% in the gained mixed solution; Thereby ceramic body is immersed in the mixed solution mixed solution is applied on the ceramic body, in reducing atmosphere, fired the ceramic product that obtains having leopard line effect 8 hours at 1280 ℃.
Embodiment 2
Albite 60 weight parts, calcite 10 weight parts, Natural manganese dioxide 10 weight parts, quartzy 7 weight parts, kaolin 10 weight parts, aluminum oxide powder 7 weight parts, barium carbonate 8 weight parts, powder blue 2 weight parts, red stone 4 weight parts, manganese oxide 4 weight parts and nickel oxide 2 weight part proportional mixing are obtained dry powder; Dry powder and water are mixed according to weight ratio 100:55; Be ground to 250 orders, obtain ceramic glaze.
Ceramic glaze is mixed with water; The weight concentration of ceramic glaze is 49% in the gained mixed solution; Thereby ceramic body is immersed in the mixed solution mixed solution is applied on the ceramic body, in reducing atmosphere, fired the ceramic product that obtains having leopard line effect 10 hours at 1300 ℃.
Embodiment 3
Lime feldspar 60 weight parts, calcite 8 weight parts, Natural manganese dioxide 8 weight parts, quartzy 6 weight parts, kaolin 9 weight parts, aluminum oxide powder 5 weight parts, barium carbonate 7 weight parts, powder blue 1.5 weight parts, red stone 3 weight parts, manganese oxide 3 weight parts and nickel oxide 1.5 weight part proportional mixing are obtained dry powder; Dry powder and water are mixed according to weight ratio 100:50; Be ground to 200 orders, obtain ceramic glaze.
Ceramic glaze is mixed with water; The weight concentration of ceramic glaze is 44% in the gained mixed solution; Thereby ceramic body is immersed in the mixed solution mixed solution is applied on the ceramic body, in reducing atmosphere, fired the ceramic product that obtains having leopard line effect 9 hours at 1290 ℃.
Claims (3)
1. ceramic glaze; Comprise dry powder and water; It is characterized in that described dry powder is processed by feldspar 60 weight parts, calcite 7～10 weight parts, Natural manganese dioxide 6～10 weight parts, quartzy 5～7 weight parts, kaolin 8～10 weight parts, aluminum oxide powder 3～7 weight parts, barium carbonate 6～8 weight parts, powder blue 1～2 weight part, red stone 2～4 weight parts, manganese oxide 2～4 weight parts and nickel oxide 1～2 weight part.
2. the preparation method of the described ceramic glaze of claim 1; It is characterized in that; Comprise: feldspar, calcite, Natural manganese dioxide, quartz, kaolin, aluminum oxide powder, barium carbonate, powder blue, red stone, manganese oxide and nickel oxide proportional mixing are obtained dry powder; Dry powder and water are mixed according to weight ratio 100:45～55, be ground to 150～250 orders, obtain ceramic glaze.
3. the method for use of the described ceramic glaze of claim 1; It is characterized in that; Comprise: ceramic glaze is mixed with water, and the weight concentration of ceramic glaze is 39～49% in the gained mixed solution, thereby ceramic body is immersed in the mixed solution mixed solution is applied on the ceramic body; In reducing atmosphere, fired the ceramic product that obtains having leopard line effect 8～10 hours at 1280～1300 ℃.