CN106045576A - Sand glaze and preparation method thereof - Google Patents
Sand glaze and preparation method thereof Download PDFInfo
- Publication number
- CN106045576A CN106045576A CN201610367602.XA CN201610367602A CN106045576A CN 106045576 A CN106045576 A CN 106045576A CN 201610367602 A CN201610367602 A CN 201610367602A CN 106045576 A CN106045576 A CN 106045576A
- Authority
- CN
- China
- Prior art keywords
- glaze
- coat enamel
- ground
- enamel glaze
- cover
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a sand glaze and a preparation method thereof. The sand glaze comprises a bottom glaze and a surface glaze. The bottom glaze is prepared from, by weight, 15-30% of potassium feldspar, 10-20% of albite, 15-25% of quartz, 25-30% of fire clay, 10-15% of calcite and 10-15% of iron oxide red, wherein the sum of weight percentages of all components is 100%. The surface glaze is prepared from, by weight, 25-35% of potassium feldspar, 15-25% of quartz, 10-12% of calcite, 5-10% of talc, 8-10% of spodumene, 10-12% of refractory clay, 6-8% of titanium oxide and 8-12% of zinc oxide, wherein the sum of weight percentages of all components is 100%. The sand glaze is superior in hue, purity and brightness, attractive in appearance and high in ornamental value. The preparation method is simple, convenient, high in operability, easy to learn and suitable for industrial production.
Description
Technical field
The present invention relates to porcelain field, be specifically related to a kind of sandy beach glaze and preparation method thereof.
Background technology
Glaze is the nature of glass thin layer covering the colorless or colored on ceramic surface, is with raw mineral materials (Anhydrite, stone
English, Talcum, Kaolin etc.) and industrial chemicals coordinate (part material can first make frit) to make glaze through grinding by a certain percentage
Slurry, imposes on billet surface, forms through uniform temperature calcining.The mechanical strength of goods, heat stability and dielectric strength can be increased, also
Have and beautify implements, be easy to wipe and wash, not by features such as the dust dirty erosions of raw meat.
At present, in porcelain industry, kind and the color of glaze are multifarious, but because seldom seeing sandy beach glaze, sandy beach glaze because of
Its color is difficult to allotment, processes accidentally, be easily caused and be off color, affect attractive in appearance in dispensing, sintering procedure.
Summary of the invention
For the defect existing for prior art, the present invention is just providing a kind of glaze colours, and ornamental value is high, and preparation method is simple
Sandy beach glaze and preparation method thereof.
The technical solution adopted for the present invention to solve the technical problems is,
The sandy beach glaze of the present invention, including ground-coat enamel and cover-coat enamel, described ground-coat enamel is made up of following components in percentage by weight: potassium is long
Stone 15-30%, albite 10-20%, quartz 15-25%, high chamotte 25-30%, calcite 10-15%, iron oxide red 10-15%,
Each component percentages sum is 100%；
Described cover-coat enamel is made up of following components in percentage by weight: potassium feldspar 25-35%, quartz 15-25%, calcite
10-12%, Talcum 5-10%, spodumene 8-10%, Guangxi mud 10-12%, titanium oxide 6-8%, zinc oxide 8-12%, each component
Percentage composition sum is 100%.
The preparation method of the sandy beach glaze of the present invention, comprises the following steps:
(1) each component taking above-mentioned percentage by weight mixes to obtain ground-coat enamel glaze, then wet ball grinding, ground-coat enamel glaze: ball: water
=1:2:0.5, the time of wet ball grinding is 12h, and it is standby that 250 mesh sieves crossed by the ground-coat enamel glaze after ball milling, then furnishing 45-50 Baume degrees
Ground-coat enamel glaze slip, ground-coat enamel glaze slip is coated on the base substrate that appearance is bright and clean, natural drying；
(2) each component taking above-mentioned percentage by weight mixes to obtain ground-coat enamel glaze, then wet ball grinding, cover-coat enamel glaze: ball: water
=1:2:0.6, the time of wet ball grinding is 14h, and it is standby that 270 mesh sieves crossed by the ground-coat enamel glaze after ball milling, then furnishing 35-40 Baume degrees
Cover-coat enamel glaze slip, be plotted in outside the base substrate of the most coated ground-coat enamel glaze with cover-coat enamel glaze slip, fire through 1190-1220 DEG C of temperature, i.e.
Obtain sandy beach glaze.
Further, the glazed thickness that described ground-coat enamel glaze prepares is 0.3-0.5mm, the glaze thickness that described cover-coat enamel glaze prepares
Degree is 0.1-0.2mm.
Further, the glaze that described ground-coat enamel glaze prepares is golden glaze, and the glaze that described cover-coat enamel glaze prepares is yellow
Glaze.
Further, described ground-coat enamel glaze slip is coated on the base substrate that appearance is bright and clean by bell jar glaze pouring, described cover-coat enamel glaze slip
It is plotted in outside the base substrate of the most coated ground-coat enamel glaze by coloring bruss.
Compared with prior art, the method have the advantages that form and aspect that the sandy beach glaze of the present invention presents, purity,
Lightness is splendid, good looking appearance, great ornamental value, reasonably combined between ground-coat enamel and each component of cover-coat enamel, ball milling and the condition fired
Control；The method of the present invention is easy, and strong operability is easily grasped, and is suitable to industrialization and produces.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1
The sandy beach glaze of the present embodiment, including ground-coat enamel and cover-coat enamel, described ground-coat enamel is made up of following components in percentage by weight: potassium
Anhydrite 20%, albite 10%, quartz 20%, high chamotte 25%, calcite 12%, iron oxide red 13%；
Described cover-coat enamel is made up of following components in percentage by weight: potassium feldspar 28%, quartz 16%, and calcite 11% is sliding
Stone 9%, spodumene 9%, Guangxi mud 11%, titanium oxide 8%, zinc oxide 8%.
The preparation method of the sandy beach glaze of the present embodiment, comprises the following steps:
(1) each component taking above-mentioned percentage by weight mixes to obtain ground-coat enamel glaze, then wet ball grinding, ground-coat enamel glaze: ball: water
=1:2:0.5, the time of wet ball grinding is 12h, and it is standby that 250 mesh sieves crossed by the ground-coat enamel glaze after ball milling, then furnishing 45-50 Baume degrees
Ground-coat enamel glaze slip, ground-coat enamel glaze slip is coated on the base substrate that appearance is bright and clean, natural drying；
(2) each component taking above-mentioned percentage by weight mixes to obtain ground-coat enamel glaze, then wet ball grinding, cover-coat enamel glaze: ball: water
=1:2:0.6, the time of wet ball grinding is 14h, and it is standby that 270 mesh sieves crossed by the ground-coat enamel glaze after ball milling, then furnishing 35-40 Baume degrees
Cover-coat enamel glaze slip, be plotted in outside the base substrate of the most coated ground-coat enamel glaze with cover-coat enamel glaze slip, fire through 1200 DEG C of temperature, i.e. obtain sand
Beach glaze.
In the present embodiment, the glazed thickness that described ground-coat enamel glaze prepares is 0.4mm, the glaze thickness that described cover-coat enamel glaze prepares
Degree is 0.14mm.
In the present embodiment, the glaze that described ground-coat enamel glaze prepares is golden glaze, and the glaze that described cover-coat enamel glaze prepares is
Yellow glaze.
In the present embodiment, described ground-coat enamel glaze slip is coated on the base substrate that appearance is bright and clean by bell jar glaze pouring, described cover-coat enamel
Glaze slip is plotted in outside the base substrate of the most coated ground-coat enamel glaze by coloring bruss.
Sandy beach glaze form and aspect, purity, lightness are splendid, good looking appearance, great ornamental value；Preparation method is easy, strong operability,
Easily grasp, be suitable to industrialization and produce.
Embodiment 2
The sandy beach glaze of the present embodiment, including ground-coat enamel and cover-coat enamel, described ground-coat enamel is made up of following components in percentage by weight: potassium
Anhydrite 20%, albite 12%, quartz 22%, high chamotte 26%, calcite 10%, iron oxide red 10%；
Described cover-coat enamel is made up of following components in percentage by weight: potassium feldspar 28%, quartz 20%, and calcite 10% is sliding
Stone 6%, spodumene 8%, Guangxi mud 10%, titanium oxide 7%, zinc oxide 11%.
The preparation method of the sandy beach glaze of the present embodiment, comprises the following steps:
(1) each component taking above-mentioned percentage by weight mixes to obtain ground-coat enamel glaze, then wet ball grinding, ground-coat enamel glaze: ball: water
=1:2:0.5, the time of wet ball grinding is 12h, and it is standby that 250 mesh sieves crossed by the ground-coat enamel glaze after ball milling, then furnishing 45-50 Baume degrees
Ground-coat enamel glaze slip, ground-coat enamel glaze slip is coated on the base substrate that appearance is bright and clean, natural drying；
(2) each component taking above-mentioned percentage by weight mixes to obtain ground-coat enamel glaze, then wet ball grinding, cover-coat enamel glaze: ball: water
=1:2:0.6, the time of wet ball grinding is 14h, and it is standby that 270 mesh sieves crossed by the ground-coat enamel glaze after ball milling, then furnishing 35-40 Baume degrees
Cover-coat enamel glaze slip, be plotted in outside the base substrate of the most coated ground-coat enamel glaze with cover-coat enamel glaze slip, fire through 1210 DEG C of temperature, i.e. obtain sand
Beach glaze.
In the present embodiment, the glazed thickness that described ground-coat enamel glaze prepares is 0.3mm, the glaze thickness that described cover-coat enamel glaze prepares
Degree is 0.2mm.
In the present embodiment, the glaze that described ground-coat enamel glaze prepares is golden glaze, and the glaze that described cover-coat enamel glaze prepares is
Yellow glaze.
In the present embodiment, described ground-coat enamel glaze slip is coated on the base substrate that appearance is bright and clean by bell jar glaze pouring, described cover-coat enamel
Glaze slip is plotted in outside the base substrate of the most coated ground-coat enamel glaze by coloring bruss.
Sandy beach glaze form and aspect, purity, lightness are splendid, good looking appearance, great ornamental value；Preparation method is easy, strong operability,
Easily grasp, be suitable to industrialization and produce.
Embodiment 3
The sandy beach glaze of the present embodiment, including ground-coat enamel and cover-coat enamel, described ground-coat enamel is made up of following components in percentage by weight: potassium
Anhydrite 21%, albite 11%, quartz 21%, high chamotte 25%, calcite 10%, iron oxide red 12%；
Described cover-coat enamel is made up of following components in percentage by weight: potassium feldspar 30%, quartz 18%, and calcite 10% is sliding
Stone 7%, spodumene 8%, Guangxi mud 10%, titanium oxide 7%, zinc oxide 10%.
The preparation method of the sandy beach glaze of the present embodiment, comprises the following steps:
(1) each component taking above-mentioned percentage by weight mixes to obtain ground-coat enamel glaze, then wet ball grinding, ground-coat enamel glaze: ball: water
=1:2:0.5, the time of wet ball grinding is 12h, and it is standby that 250 mesh sieves crossed by the ground-coat enamel glaze after ball milling, then furnishing 45-50 Baume degrees
Ground-coat enamel glaze slip, ground-coat enamel glaze slip is coated on the base substrate that appearance is bright and clean, natural drying；
(2) each component taking above-mentioned percentage by weight mixes to obtain ground-coat enamel glaze, then wet ball grinding, cover-coat enamel glaze: ball: water
=1:2:0.6, the time of wet ball grinding is 14h, and it is standby that 270 mesh sieves crossed by the ground-coat enamel glaze after ball milling, then furnishing 35-40 Baume degrees
Cover-coat enamel glaze slip, be plotted in outside the base substrate of the most coated ground-coat enamel glaze with cover-coat enamel glaze slip, fire through 1210 DEG C of temperature, i.e. obtain sand
Beach glaze.
In the present embodiment, the glazed thickness that described ground-coat enamel glaze prepares is 0.4mm, the glaze thickness that described cover-coat enamel glaze prepares
Degree is 0.14mm.
In the present embodiment, the glaze that described ground-coat enamel glaze prepares is golden glaze, and the glaze that described cover-coat enamel glaze prepares is
Yellow glaze.
In the present embodiment, described ground-coat enamel glaze slip is coated on the base substrate that appearance is bright and clean by bell jar glaze pouring, described cover-coat enamel
Glaze slip is plotted in outside the base substrate of the most coated ground-coat enamel glaze by coloring bruss.
Sandy beach glaze form and aspect, purity, lightness are splendid, good looking appearance, great ornamental value；Preparation method is easy, strong operability,
Easily grasp, be suitable to industrialization and produce.
Claims (5)
1. a sandy beach glaze, it is characterised in that including ground-coat enamel and cover-coat enamel, described ground-coat enamel is by following components in percentage by weight system
Become: potassium feldspar 15-30%, albite 10-20%, quartz 15-25%, high chamotte 25-30%, calcite 10-15%, iron oxide red
10-15%, each component percentages sum is 100%；
Described cover-coat enamel is made up of following components in percentage by weight: potassium feldspar 25-35%, quartz 15-25%, calcite 10-
12%, Talcum 5-10%, spodumene 8-10%, Guangxi mud 10-12%, titanium oxide 6-8%, zinc oxide 8-12%, each component hundred
Dividing content sum is 100%.
2. the preparation method of a sandy beach as claimed in claim 1 glaze, it is characterised in that comprise the following steps:
(1) take each component of above-mentioned percentage by weight and mix to obtain ground-coat enamel glaze, then wet ball grinding, ground-coat enamel glaze: ball: water=1:
2:0.5, the time of wet ball grinding is 12h, and it is standby that 250 mesh sieves crossed by the ground-coat enamel glaze after ball milling, then the end of furnishing 45-50 Baume degrees
Glaze glaze slip, is coated in ground-coat enamel glaze slip on the base substrate that appearance is bright and clean, natural drying；
(2) take each component of above-mentioned percentage by weight and mix to obtain ground-coat enamel glaze, then wet ball grinding, cover-coat enamel glaze: ball: water=1:
2:0.6, the time of wet ball grinding is 14h, and it is standby that 270 mesh sieves crossed by the ground-coat enamel glaze after ball milling, then the face of furnishing 35-40 Baume degrees
Glaze glaze slip, is plotted in outside the base substrate of the most coated ground-coat enamel glaze with cover-coat enamel glaze slip, fires through 1190-1220 DEG C of temperature, i.e. obtain
Sandy beach glaze.
The preparation method of sandy beach the most according to claim 2 glaze, it is characterised in that the glaze thickness that described ground-coat enamel glaze prepares
Degree is 0.3-0.5mm, and the glazed thickness that described cover-coat enamel glaze prepares is 0.1-0.2mm.
4. according to the preparation method of the sandy beach glaze described in Claims 2 or 3, it is characterised in that the glaze that described ground-coat enamel glaze prepares
Face is golden glaze, and the glaze that described cover-coat enamel glaze prepares is yellow glaze.
5. according to the preparation method of the sandy beach glaze described in Claims 2 or 3, it is characterised in that described ground-coat enamel glaze slip passes through bell jar
Glaze pouring is coated on the base substrate that appearance is bright and clean, and described cover-coat enamel glaze slip is plotted in the base of the most coated ground-coat enamel glaze by coloring bruss
External.