CN109369012A - Furnace transmutation glaze and its preparation process - Google Patents
Furnace transmutation glaze and its preparation process Download PDFInfo
- Publication number
- CN109369012A CN109369012A CN201811518507.0A CN201811518507A CN109369012A CN 109369012 A CN109369012 A CN 109369012A CN 201811518507 A CN201811518507 A CN 201811518507A CN 109369012 A CN109369012 A CN 109369012A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- component
- furnace transmutation
- frit
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of furnace transmutation glaze and its preparation process, the component and each component mass parts contained in glaze used in furnace transmutation glaze is as follows: potassium feldspar: 20-22 parts；Albite: 20-22 parts；Quartz: 8-10 parts；Calcite: 30-32 parts；Guizhou clay: 8-10 parts；Frit: 4-5 parts；Aluminium powder: 8-10 parts；Black pigment: 10-12 parts.Glaze surface of the present invention floating is uneven, has the effect of just as chiseling and carving.
Description
Technical field
The present invention relates to a kind of furnace transmutation glaze and its preparation processes.
Background technique
Currently, the moulding of porcelain billet is the basis of quality product in porcelain industry, the allotment of glaze keeps porcelain more gorgeous
Colorful, the porcelain billet of same moulding often because of the difference of glaze paint, and generates different influences to the vision of consumer.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of furnace transmutation glaze is provided, its glaze surface
Floating is uneven, has the effect of just as chiseling and carving.
In order to solve the above-mentioned technical problem, the technical scheme is that a kind of furnace transmutation glaze, contain in glaze used in it
Some components and each component mass parts are as follows:
Potassium feldspar: 20-22 parts；
Albite: 20-22 parts；
Quartz: 8-10 parts；
Calcite: 30-32 parts；
Guizhou clay: 8-10 parts；
Frit: 4-5 parts；
Aluminium powder: 8-10 parts；
Black pigment: 10-12 parts.
The present invention also provides a kind of furnace transmutation glaze, the component and each component mass parts contained in glaze used in it is such as
Under:
Potassium feldspar: 28-30 parts；
Quartz: 20-22 parts；
Calcite: 10-12 parts；
Guizhou clay: 6-8 parts；
Frit: 10-12 parts；
Aluminium powder: 8-10 parts；
Zirconium dioxide: 8-10 parts.
Further, the component of the frit and each component mass parts are as follows: feldspar powder: 20~25 parts；Lithium carbonate: 25 parts~
30 parts；Borax: 20 parts~30 parts；Silica flour: 25 parts~30 parts.
The present invention also provides a kind of preparation process of furnace transmutation glaze, the step of technique in contain:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: glaze: ball: mass ratio=1:1:(1.4~1.6 of water is pressed), wet ball grinding 15~18 hours, the glaze after ball milling
Material is sieved and removes iron, then is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1200 DEG C -1300 DEG C of oxidizing atmospheres
Product.
After above-mentioned technical proposal, using the formula of furnace transmutation glaze of the invention, after firing, surface floating is uneven,
Have the effect of just as chiseling and carving.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one
A kind of furnace transmutation glaze, the component and each component mass parts contained in glaze used in it are as follows:
Potassium feldspar: 20 parts；
Albite: 20 parts；
Quartz: 8 parts；
Calcite: 30 parts；
Guizhou clay: 8 parts；
Frit: 4 parts；
Aluminium powder: 8 parts；
Black pigment: 10 parts.
The component and each component mass parts of the frit are as follows: feldspar powder: 20 parts；Lithium carbonate: 25 parts；Borax: 20 parts；Stone
Ying Fen: 25 parts.
Contain in the step of preparation process of the furnace transmutation glaze, technique:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: glaze: ball: mass ratio=1:1:1.4 of water is pressed, wet ball grinding 15 hours, the glaze after ball milling was sieved and removes
Iron, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1200 DEG C -1300 DEG C of oxidizing atmospheres
Product.
Embodiment two
A kind of furnace transmutation glaze, the component and each component mass parts contained in glaze used in it are as follows:
Potassium feldspar: 22 parts；
Albite: 22 parts；
Quartz: 10 parts；
Calcite: 32 parts；
Guizhou clay: 10 parts；
Frit: 5 parts；
Aluminium powder: 10 parts；
Black pigment: 12 parts.
The component and each component mass parts of the frit are as follows: feldspar powder: 25 parts；Lithium carbonate: 30 parts；Borax: 30 parts；Stone
Ying Fen: 30 parts.
Contain in the step of preparation process of the furnace transmutation glaze, technique:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: glaze: ball: mass ratio=1:1:1.6 of water is pressed, wet ball grinding 18 hours, the glaze after ball milling was sieved and removes
Iron, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1200 DEG C -1300 DEG C of oxidizing atmospheres
Product.
Embodiment three
A kind of furnace transmutation glaze, the component and each component mass parts contained in glaze used in it are as follows:
Potassium feldspar: 21 parts；
Albite: 21 parts；
Quartz: 9 parts；
Calcite: 31 parts；
Guizhou clay: 9 parts；
Frit: 4 parts；
Aluminium powder: 9 parts；
Black pigment: 11 parts.
The component and each component mass parts of the frit are as follows: feldspar powder: 23 parts；Lithium carbonate: 26 parts；Borax: 25 parts；Stone
Ying Fen: 27 parts.
Contain in the step of preparation process of the furnace transmutation glaze, technique:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: glaze: ball: mass ratio=1:1:1.5 of water is pressed, wet ball grinding 16 hours, the glaze after ball milling was sieved and removes
Iron, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1200 DEG C -1300 DEG C of oxidizing atmospheres
Product.
Example IV
A kind of furnace transmutation glaze, the component and each component mass parts contained in glaze used in it are as follows:
Potassium feldspar: 28 parts；
Quartz: 20 parts；
Calcite: 10 parts；
Guizhou clay: 6 parts；
Frit: 10 parts；
Aluminium powder: 8 parts；
Zirconium dioxide: 8 parts.
The component and each component mass parts of the frit are as follows: feldspar powder: 20 parts；Lithium carbonate: 25 parts；Borax: 20 parts；Stone
Ying Fen: 25 parts.
Contain in the step of preparation process of the furnace transmutation glaze, technique:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: glaze: ball: mass ratio=1:1:1.4 of water is pressed, wet ball grinding 15 hours, the glaze after ball milling was sieved and removes
Iron, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1200 DEG C -1300 DEG C of oxidizing atmospheres
Product.
Embodiment five
A kind of furnace transmutation glaze, the component and each component mass parts contained in glaze used in it are as follows:
Potassium feldspar: 30 parts；
Quartz: 22 parts；
Calcite: 12 parts；
Guizhou clay: 8 parts；
Frit: 12 parts；
Aluminium powder: 10 parts；
Zirconium dioxide: 10 parts.
The component and each component mass parts of the frit are as follows: feldspar powder: 25 parts；Lithium carbonate: 30 parts；Borax: 30 parts；Stone
Ying Fen: 30 parts.
Contain in the step of preparation process of the furnace transmutation glaze, technique:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: glaze: ball: mass ratio=1:1:1.6 of water is pressed, wet ball grinding 18 hours, the glaze after ball milling was sieved and removes
Iron, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1200 DEG C -1300 DEG C of oxidizing atmospheres
Product.
Embodiment six
A kind of furnace transmutation glaze, the component and each component mass parts contained in glaze used in it are as follows:
Potassium feldspar: 29 parts；
Quartz: 21 parts；
Calcite: 11 parts；
Guizhou clay: 7 parts；
Frit: 11 parts；
Aluminium powder: 9 parts；
Zirconium dioxide: 9 parts.
The component and each component mass parts of the frit are as follows: feldspar powder: 22 parts；Lithium carbonate: 27 parts；Borax: 25 parts；Stone
Ying Fen: 27 parts.
Contain in the step of preparation process of the furnace transmutation glaze, technique:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: glaze: ball: mass ratio=1:1:1.5 of water is pressed, wet ball grinding 18 hours, the glaze after ball milling was sieved and removes
Iron, then it is tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through being fired under 1200 DEG C -1300 DEG C of oxidizing atmospheres
Product.
The furnace transmutation glaze that above six embodiments are prepared, by it has been observed that the equal floating injustice of its glaze paint, all has shape
With the effect chiseled and carved, meet design requirement.
Particular embodiments described above, pair present invention solves the technical problem that, technical scheme and beneficial effects carry out
It is further described, it should be understood that the above is only a specific embodiment of the present invention, is not limited to this
Invention, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should be included in this hair
Within bright protection scope.
Claims (4)
1. a kind of furnace transmutation glaze, which is characterized in that the component and each component mass parts contained in glaze used in it is as follows:
Potassium feldspar: 20-22 parts；
Albite: 20-22 parts；
Quartz: 8-10 parts；
Calcite: 30-32 parts；
Guizhou clay: 8-10 parts；
Frit: 4-5 parts；
Aluminium powder: 8-10 parts；
Black pigment: 10-12 parts.
2. a kind of furnace transmutation glaze, which is characterized in that the component and each component mass parts contained in glaze used in it is as follows:
Potassium feldspar: 28-30 parts；
Quartz: 20-22 parts；
Calcite: 10-12 parts；
Guizhou clay: 6-8 parts；
Frit: 10-12 parts；
Aluminium powder: 8-10 parts；
Zirconium dioxide: 8-10 parts.
3. furnace transmutation glaze according to claim 1 or 2, it is characterised in that: the component and each component mass parts of the frit are such as
Under: feldspar powder: 20~25 parts；Lithium carbonate: 25 parts~30 parts；Borax: 20 parts~30 parts；Silica flour: 25 parts~30 parts.
4. a kind of preparation process of the furnace transmutation glaze as described in claims 1 or 2 or 3, it is characterised in that: contain in the step of technique
Have:
S1: it stocks up according to the component and each component mass parts of glaze；
S2: glaze: ball: mass ratio=1:1:(1.4~1.6 of water is pressed), wet ball grinding 15~18 hours, the glaze mistake after ball milling
It sieves and removes iron, then be tuned into the glaze slip of 40~45 Baume degrees；
S3: after the chinaware body for taking appearance bright and clean immerses the glaze slip, through firing finished product under 1200 DEG C -1300 DEG C of oxidizing atmospheres.