CN111233332A - Combined glaze for teabowl and preparation method thereof - Google Patents
Combined glaze for teabowl and preparation method thereof Download PDFInfo
- Publication number
- CN111233332A CN111233332A CN202010133532.8A CN202010133532A CN111233332A CN 111233332 A CN111233332 A CN 111233332A CN 202010133532 A CN202010133532 A CN 202010133532A CN 111233332 A CN111233332 A CN 111233332A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- teabowl
- tiger skin
- dolomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a combined glaze for teabowls, which comprises a dolomite glaze applied to the inner side surface of the teabowl and a tiger skin brown glaze applied to the bowl mouth of the inner side surface of the teabowl; the glaze used for the dolomite glaze comprises the following components in parts by mass: 10 parts of potash feldspar, 10 parts of albite, 20 parts of quartz, 15 parts of calcite, 5 parts of talcum, 9 parts of titanium dioxide, 5 parts of Guizhou soil and 30 parts of frit; the glaze used for the tiger skin brown glaze comprises the following components in parts by mass: 25 parts of potassium feldspar, 25 parts of albite, 20 parts of quartz, 15 parts of calcite, 3 parts of barium carbonate, 4 parts of Guizhou soil, 15 parts of clinker, 12 parts of ferric oxide and 5 parts of manganese carbonate. The inner side surface of the teabowl is made of the dolomite glaze, the glaze is blue in white, white covering performance is kept, high-temperature fluidity of the glaze is guaranteed, and a tiger skin effect is formed by mixing the inner side surface bowl opening and the dolomite glaze, so that the teabowl is natural, smooth and unique in layering.
Description
Technical Field
The invention relates to a combined glaze for teabowls and a preparation method thereof.
Background
At present, glaze needs to be applied to the inner side surface of porcelain, particularly a teabowl, zirconium silicate is generally used as an opacifier for white glaze on the inner side surface of the teabowl in the prior art, the white glaze is yellowish in white, the high-temperature fluidity of the glaze is poor, and the white glaze is adopted on the whole inner side surface, so that the appearance is not attractive.
Disclosure of Invention
The invention aims to overcome the defects of the prior art and provide the combined glaze for the teabowl, the inner side surface of the teabowl made of the combined glaze is the cloudy glaze, the white glaze is blue, the white covering property is kept, the high-temperature fluidity of the glaze is ensured, and the tiger skin effect is achieved by mixing the inner side bowl opening and the cloudy glaze, so that the combined glaze is natural, smooth and unique in layering. .
In order to solve the technical problems, the technical scheme of the invention is as follows: a combined glaze for teabowls comprises a dolomite glaze applied on the inner side surface of a teabowl and a tiger skin brown glaze applied on the bowl mouth on the inner side surface of the teabowl; wherein the content of the first and second substances,
the glaze used for the dolomite glaze comprises the following components in parts by mass: 10 parts of potash feldspar, 10 parts of albite, 20 parts of quartz, 15 parts of calcite, 5 parts of talcum, 9 parts of titanium dioxide, 5 parts of Guizhou soil and 30 parts of frit;
the glaze used for the tiger skin brown glaze comprises the following components in parts by mass:
25 parts of potassium feldspar, 25 parts of albite, 20 parts of quartz, 15 parts of calcite, 3 parts of barium carbonate, 4 parts of Guizhou soil, 15 parts of clinker, 12 parts of ferric oxide and 5 parts of manganese carbonate.
The invention also provides a preparation method of the combined glaze for teabowls, which comprises the following steps:
preparing dolomitic glaze slip and tiger skin brown glaze slip;
the method comprises the following steps of applying a dolomitic glaze on the inner side surface of a teabowl blank by adopting a dolomitic glaze slurry, and applying a tiger skin brown glaze on the bowl mouth on the inner side surface of the teabowl blank by adopting a tiger skin brown glaze slurry;
and firing the glazed teabowl blank at 1189-1190 ℃.
After the technical scheme is adopted, the dolomite glaze on the inner side surface has two advantages: firstly, replace traditional opacifier zirconium silicate with titanium white powder, secondly use high temperature resistant mica powder, the tradition uses zirconium silicate to make the white glaze of opacifier, in the white yellowing, and the high temperature fluidity of glaze is poor, and use titanium white powder as opacifier, through adjusting the glaze formulation, the area is blue in the white glaze, has kept white covering nature promptly, can guarantee the high temperature fluidity of glaze again, the mica lamella in the glaze can not melt because of can nai 1800 ℃ high temperature, because of can blockking the high temperature flow of glaze and form the effect of piling up the overlapping. Because of good high temperature fluidity, the three-dimensional drapery pattern is formed by combining the green lines of filaments formed by the mutual fusion of the verdigris. The tiger skin brown glaze has the advantages of low glaze melting point, high brightness, old paint effect, bright and dark antique effect, tiger skin effect combined with the cloud glaze, natural smoothness and unique layering.
Detailed Description
In order that the present invention may be more clearly understood, the following detailed description of the present invention is given with reference to specific examples.
A combined glaze for teabowls comprises a dolomite glaze applied on the inner side surface of a teabowl and a tiger skin brown glaze applied on the bowl mouth on the inner side surface of the teabowl; wherein the content of the first and second substances,
the glaze used for the dolomite glaze comprises the following components in parts by mass: 10 parts of potash feldspar, 10 parts of albite, 20 parts of quartz, 15 parts of calcite, 5 parts of talcum, 9 parts of titanium dioxide, 5 parts of Guizhou soil and 30 parts of frit;
the glaze used for the tiger skin brown glaze comprises the following components in parts by mass:
25 parts of potassium feldspar, 25 parts of albite, 20 parts of quartz, 15 parts of calcite, 3 parts of barium carbonate, 4 parts of Guizhou soil, 15 parts of clinker, 12 parts of ferric oxide and 5 parts of manganese carbonate.
The preparation method of the combined glaze for teabowls comprises the following steps:
preparing dolomitic glaze slip and tiger skin brown glaze slip;
the method comprises the following steps of applying a dolomitic glaze on the inner side surface of a teabowl blank by adopting a dolomitic glaze slurry, and applying a tiger skin brown glaze on the bowl mouth on the inner side surface of the teabowl blank by adopting a tiger skin brown glaze slurry;
and firing the glazed teabowl blank at 1189-1190 ℃.
The teabowl prepared from the combined glaze of the embodiment is observed, so that the inner side surface of the teabowl presents a very soft and natural white glaze effect, and the bowl mouth is matched with the tiger skin brown glaze to form a tiger skin texture effect, so that the teabowl is very attractive in appearance.
In this example, the frit is a commercially available frit.
The above embodiments are described in further detail to solve the technical problems, technical solutions and advantages of the present invention, and it should be understood that the above embodiments are only examples of the present invention and are not intended to limit the present invention, and any modifications, equivalent substitutions, improvements and the like made within the spirit and principle of the present invention should be included in the protection scope of the present invention.
Claims (2)
1. A combined glaze for teabowls is characterized by comprising a dolomite glaze applied to the inner side surface of a teabowl and a tiger skin brown glaze applied to the bowl mouth of the inner side surface of the teabowl; wherein the content of the first and second substances,
the glaze used for the dolomite glaze comprises the following components in parts by mass: 10 parts of potash feldspar, 10 parts of albite, 20 parts of quartz, 15 parts of calcite, 5 parts of talcum, 9 parts of titanium dioxide, 5 parts of Guizhou soil and 30 parts of frit;
the glaze used for the tiger skin brown glaze comprises the following components in parts by mass:
25 parts of potassium feldspar, 25 parts of albite, 20 parts of quartz, 15 parts of calcite, 3 parts of barium carbonate, 4 parts of Guizhou soil, 15 parts of clinker, 12 parts of ferric oxide and 5 parts of manganese carbonate.
2. A method of preparing a composite glaze for teabowls as claimed in claim 1, characterized by comprising the steps of:
preparing dolomitic glaze slip and tiger skin brown glaze slip;
the method comprises the following steps of applying a dolomitic glaze on the inner side surface of a teabowl blank by adopting a dolomitic glaze slurry, and applying a tiger skin brown glaze on the bowl mouth on the inner side surface of the teabowl blank by adopting a tiger skin brown glaze slurry;
and firing the glazed teabowl blank at 1189-1190 ℃.