CN108298815A - A kind of preparation process of porcelain - Google Patents
A kind of preparation process of porcelain Download PDFInfo
- Publication number
- CN108298815A CN108298815A CN201810163120.1A CN201810163120A CN108298815A CN 108298815 A CN108298815 A CN 108298815A CN 201810163120 A CN201810163120 A CN 201810163120A CN 108298815 A CN108298815 A CN 108298815A
- Authority
- CN
- China
- Prior art keywords
- glaze
- speckled
- pea green
- plum branch
- yellowish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to ceramic technology fields, are specifically related to a kind of preparation process for the porcelain being combined with plum branch speckled glaze with yellowish pea green glaze.It is to whiten in blueness that this kind of yellowish pea green glaze is had pea green glaze layer and plum branch spot glaze layer, the glaze colours of the yellowish pea green glaze by green body successively outward with the porcelain that plum branch speckled glaze is combined, and glaze gloss, cyan is plain, and light transmittance is high；Color sample is depicted by plum branch speckled glaze in the outer layer of yellowish pea green glaze, plum branch speckled glaze is in taupe, and the limb of color such as trees, glaze are more coarse；Yellowish pea green glaze provided by the invention can be merged mutually with plum branch speckled glaze, plum branch speckled glaze can impose on implements opening's edge portion, with the background color of yellowish pea green glaze formed it is pseudo-classic, do old effect, it also can be in patterns such as the surface rendering trees of yellowish pea green glaze, limb, houses, fine and smooth gentle background color forms a sharp contrast with thick mad colored drawing, forms unique aesthetic, two kinds of glaze once-firings, the fuel that 20 30% can be saved, effectively reduces energy consumption.
Description
The application is the divisional application of " yellowish pea green glaze is with the plum porcelain that is combined of branch speckled glaze and preparation process ", original application
The applying date is on March 20th, 2016, application No. is：CN201610165752.2.
Technical field
The present invention relates to ceramic technology field, it is specifically related to the porcelain that a kind of yellowish pea green glaze is combined with plum branch speckled glaze
Preparation process.
Background technology
Yellowish pea green glaze, green glaze derive from one of glaze colours, originate from Longqun Cave of Song Dynasty.Micro- nearly yellow before bright, until the Qing Dynasty is pure close
Green, glaze colours are yellowing in blueness, and glaze gloss is weaker than pale blue, plum green.The basic tone of yellowish pea green glaze in blueness dodge Huang based on,
Cyan is simple and elegant.Traditional pea green glaze is single color glaze, simple and elegant soft, if the light lake water of the shallow person of color, the green middle yellowing of color depth person, and glaze
Solidifying thickness.The Qing Dynasty begin to appear in fire yellowish pea green glaze while, also imposed on glaze various colors enter kiln it is secondary burning make, simple and elegant glaze
Color set off under color, it is more gorgeous charming, but yellowish pea green glaze transparency is not as good as white glaze, in the obtained effect of pea green overglaze color
It is not fully up to expectations.
With the high speed development of economic society, people’s lives quality increasingly improves, continuous to aesthetic multifarious demand
Variation, traditional yellowish pea green glaze is although very popular, but monochromatic glazing effect and speckle cannot meet the need of people
It asks, if a kind of inheriting tradition yellowish pea green glaze can be provided, and is shown on traditional glazing effect and be different from traditional glaze
The decorative pattern in face has actively to provide a kind of porcelain that can meet the continually changing demand of people and have unique artistic effect
Economic and social benefit.
Invention content
To overcome deficiency in the prior art, the present invention to provide a kind of preparation process of porcelain.
To achieve the above object, the technical solution adopted by the present invention is as follows：
The porcelain that yellowish pea green glaze is combined with plum branch speckled glaze, which is characterized in that the porcelain has beans successively outward by green body
Green glaze layer and plum branch spot glaze layer,
The yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 30-35, calcined kaolin 10-15, chalk
10-15, quartz 10-15, Suzhou soil 5-10, zirconium silicate 5-10, talcum 5-10, dolomite 3-5, barium carbonate 1-5, iron oxide 1-3；
The plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 35-40, quartz 15-25, pine ash 5-
20, Suzhou soil 5-10, solo flight powder 5-10, iron oxide 5-10, talcum 1-5, barium carbonate 1-5, manganese dioxide 1-5, bone meal 1-5, oxygen
Change cobalt 1-3.
Optimization, yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 33, calcined kaolin 10, chalk 10, stone
English 15, Suzhou soil 10, zirconium silicate 8, talcum 5, dolomite 5, barium carbonate 2.5, iron oxide 1.5.
Optimization, plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 30, quartz 25, pine ash 14, Soviet Union
State soil 5, solo flight powder 10, iron oxide 6, talcum 3, barium carbonate 2, manganese dioxide 2, bone meal 2, cobalt oxide 1.
Optimization, yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 33, calcined kaolin 13, chalk 11, stone
English 13, Suzhou soil 8, zirconium silicate 6, talcum 7, dolomite 4, barium carbonate 3, iron oxide 2.
Optimization, plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 36, quartz 18, pine ash 9, Soviet Union
State soil 8, solo flight powder 7, iron oxide 8, talcum 2, barium carbonate 4, manganese dioxide 3, bone meal 3, cobalt oxide 2.
Optimization, yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 34, calcined kaolin 13, chalk 12, stone
English 10, Suzhou soil 10, zirconium silicate 9, talcum 8, dolomite 2, barium carbonate 1, iron oxide 1.
Optimization, plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 38, quartz 25, pine ash 7, Soviet Union
State soil 7, solo flight powder 8, iron oxide 6, talcum 3, barium carbonate 2, manganese dioxide 2, bone meal 1, cobalt oxide 1.
The preparation process for the porcelain that yellowish pea green glaze is combined with plum branch speckled glaze, which is characterized in that use above-mentioned yellowish pea green glaze
With the porcelain that plum branch speckled glaze is combined, it is as follows：
Step 1, yellowish pea green glaze and plum branch speckled glaze are prepared；
Step 2, yellowish pea green glaze is applied on ceramic body；
Step 3, plum branch speckled glaze is applied on pea green glaze by way of colored drawing after ceramic blank drying；
Step 4, after plum branch speckled glaze drying, ceramic body is put into kiln and is fired；
Step 5, furnace heating-up, under reducing atmosphere, firing temperature is 1200-1300 DEG C；
Step 6, blow-on obtains the porcelain that yellowish pea green glaze is combined with plum branch speckled glaze after cooling.
Further, yellowish pea green glaze described in step 1 is milled into using wet bulb, wherein expecting：Ball：Water=1：2：0.8, the plum branch
Speckled glaze is milled into using wet bulb, wherein expecting：Ball：Water=1：2：1.
Further, firing temperature is 1290 DEG C in step 5.
By the above-mentioned description of this invention it is found that the porcelain tool that yellowish pea green glaze provided by the invention is combined with plum branch speckled glaze
It is to whiten in blueness to have the background color of yellowish pea green glaze, the glaze colours of the yellowish pea green glaze, and glaze gloss, cyan is plain, and light transmittance is high；In yellowish pea green glaze
Outer layer depicts color sample by plum branch speckled glaze, and plum branch speckled glaze is in taupe, and the limb of color such as trees, glaze are more thick
It is rough；Present invention offer yellowish pea green glaze is increased with the porcelain that plum branch speckled glaze is combined in traditional yellowish pea green glaze effect can be with its phase
Fusion plum branch speckled glaze, plum branch speckled glaze can impose on implements opening's edge portion, with the background color of yellowish pea green glaze formed it is pseudo-classic, do old effect
Fruit, also can be in patterns such as the surface rendering trees of yellowish pea green glaze, limb, houses, and fine and smooth gentle background color is formed with thick mad colored drawing
Striking contrast forms unique artistic effect；Two kinds of glaze once-firings, can save the fuel of 20-30%, efficiently reduce
Energy consumption.
Specific implementation mode
Below by way of specific implementation mode, the invention will be further described.
The porcelain that a kind of yellowish pea green glaze is combined with plum branch speckled glaze, which is characterized in that the porcelain by green body outward successively
There are pea green glaze layer and plum branch spot glaze layer,
The yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 30-35, calcined kaolin 10-15, chalk
10-15, quartz 10-15, Suzhou soil 5-10, zirconium silicate 5-10, talcum 5-10, dolomite 3-5, barium carbonate 1-5, iron oxide 1-3；
The plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 35-40, quartz 15-25, pine ash 5-
20, Suzhou soil 5-10, solo flight powder 5-10, iron oxide 5-10, talcum 1-5, barium carbonate 1-5, manganese dioxide 1-5, bone meal 1-5, oxygen
Change cobalt 1-3.
Specific embodiment one：
Yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 33, calcined kaolin 10, chalk 10, quartz 15, Soviet Union
State soil 10, zirconium silicate 8, talcum 5, dolomite 5, barium carbonate 2.5, iron oxide 1.5；
Plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 30, quartz 25, pine ash 14, Suzhou soil 5,
Solo flight powder 10, iron oxide 6, talcum 3, barium carbonate 2, manganese dioxide 2, bone meal 2, cobalt oxide 1.
Specific embodiment two：
Yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 33, calcined kaolin 13, chalk 11, quartz 13, Soviet Union
State soil 8, zirconium silicate 6, talcum 7, dolomite 4, barium carbonate 3, iron oxide 2；
Plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 36, quartz 18, pine ash 9, Suzhou soil 8, list
Fly powder 7, iron oxide 8, talcum 2, barium carbonate 4, manganese dioxide 3, bone meal 3, cobalt oxide 2.
Specific embodiment three：
Yellowish pea green glaze is prepared by the raw material of following parts by weight：Feldspar 34, calcined kaolin 13, chalk 12, quartz 10, Soviet Union
State soil 10, zirconium silicate 9, talcum 8, dolomite 2, barium carbonate 1, iron oxide 1；
Plum branch speckled glaze is prepared by the raw material of following parts by weight：Feldspar 38, quartz 25, pine ash 7, Suzhou soil 7, list
Fly powder 8, iron oxide 6, talcum 3, barium carbonate 2, manganese dioxide 2, bone meal 1, cobalt oxide 1.
The preparation process for the porcelain that yellowish pea green glaze is combined with plum branch speckled glaze, which is characterized in that use specific embodiment one
The porcelain being combined to the yellowish pea green glaze described in any one of three with plum branch speckled glaze, is as follows：
Step 1, yellowish pea green glaze and plum branch speckled glaze are prepared；
Step 2, yellowish pea green glaze is applied on ceramic body；
Step 3, plum branch speckled glaze is applied on pea green glaze by way of colored drawing after ceramic blank drying；
Step 4, after plum branch speckled glaze drying, ceramic body is put into kiln and is fired；
Step 5, furnace heating-up, under reducing atmosphere, firing temperature is 1200-1300 DEG C；
Step 6, blow-on obtains the porcelain that yellowish pea green glaze is combined with plum branch speckled glaze after cooling.
Optimization, yellowish pea green glaze described in step 1 is milled into using wet bulb, wherein expecting：Ball：Water=1：2：0.8, the plum branch spot
Point glaze is milled into using wet bulb, wherein expecting：Ball：Water=1：2：1；
Optimization, firing temperature is 1290 DEG C in step 5.
The background color with the porcelain that plum branch speckled glaze is combined using the yellowish pea green glaze prepared by the above method with yellowish pea green glaze, should
The glaze colours of yellowish pea green glaze is to whiten in blueness, and glaze gloss, cyan is plain, and light transmittance is high；Pass through plum branch spot in the outer layer of yellowish pea green glaze
Glaze depicts color sample, and plum branch speckled glaze is in taupe, and the limb of color such as trees, glaze are more coarse, beans provided by the invention
Green glaze can be merged mutually with plum branch speckled glaze, form unique aesthetic, plum branch speckled glaze can impose on implements opening's edge portion, with beans
The background color of green glaze formed it is pseudo-classic, do old effect, also can be in patterns such as the surface rendering trees of yellowish pea green glaze, limb, houses, two kinds
Glaze once-firing can save the fuel of 20-30%, effectively reduce energy consumption.
Several specific implementation modes of the present invention are above are only, but the design concept of the present invention is not limited thereto, all profits
The change for carrying out unsubstantiality to the present invention with this design, should all belong to the behavior for invading the scope of the present invention.
Claims (3)
1. a kind of preparation process of porcelain, which is characterized in that it is as follows：
Step 1, yellowish pea green glaze and plum branch speckled glaze are prepared；
Step 2, yellowish pea green glaze is applied on ceramic body；
Step 3, plum branch speckled glaze is applied on pea green glaze by way of colored drawing after ceramic blank drying；
Step 4, after plum branch speckled glaze drying, ceramic body is put into kiln and is fired；
Step 5, furnace heating-up, under reducing atmosphere, firing temperature is 1200-1300 DEG C；
Step 6, blow-on obtains the porcelain that yellowish pea green glaze is combined with plum branch speckled glaze after cooling.
2. the preparation process for the porcelain that yellowish pea green glaze according to claim 8 is combined with plum branch speckled glaze, it is characterised in that：
Yellowish pea green glaze described in step 1 is milled into using wet bulb, wherein expecting：Ball：Water=1：2：0.8, the plum branch speckled glaze uses wet ball mill
It is made, wherein expecting：Ball：Water=1：2：1.
3. the preparation process for the porcelain that yellowish pea green glaze according to claim 8 is combined with plum branch speckled glaze, it is characterised in that：
Firing temperature is 1290 DEG C in the step 5.