CN109293237A - A kind of roe Bluepoint shape pottery glaze and preparation method thereof - Google Patents
A kind of roe Bluepoint shape pottery glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109293237A CN109293237A CN201811089048.9A CN201811089048A CN109293237A CN 109293237 A CN109293237 A CN 109293237A CN 201811089048 A CN201811089048 A CN 201811089048A CN 109293237 A CN109293237 A CN 109293237A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- glaze
- white
- glaze raw
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of roe Bluepoint shape pottery glaze and preparation method thereof, it is made of white-based glaze and blue glaze two parts, according to weight ratio, the raw material for forming the blue glaze is long green stone 15-20 parts, 30-40 parts of melilite, feldspar 5-10 parts white, 5-9 parts of quartz, 2-3 parts of cobalt, 4-5 parts of this medicine, 7-13 parts of calcite, 2-6 parts of quartz, 2-3 parts of Copper Ores, 1-5 parts of zinc oxide, 0.1-0.6 parts of tin oxide；The raw material for forming the white-based glaze is melilite 30-50 parts, 15-20 parts of this medicine, 3-5 parts of montmorillonite, 2-4 parts of bauxite, it is 5-6 parts quartzy, 10-15 parts of calcite, 3-5 parts of talcum, 6-8 parts of frit, 5-7 parts of Copper Ores, 0.8-1.2 parts of tin oxide, 0.8-1.2 parts of bone ash, 2-3 parts of tourmaline, compared with prior art, blue glaze raw material provided by the invention increases cobalt, improve the brightness of color, by being layered glazing to blue glaze raw material and white-based glaze raw material, after realizing to pottery glaze glazing, it is stacked with and assembles containing colorant of the same race or different colorant glaze, pottery glaze layer after glaze firing is like starry sky, it is more aesthetically pleasing.
Description
Technical field
The present invention relates to glaze fields, and in particular to a kind of roe Bluepoint shape pottery glaze and preparation method thereof.
Background technique
Ceramics development history be Chinese civilization history an important component part, China as four major acids ancient country it
One, brilliant contribution is made that for mankind's social progress and development, wherein the invention and development of ceramics have more unique meaning
Justice, each Chao Gedai has different artistic styles and different technical characteristics on Chinese history." china " in English existing China
The meaning, and have the meaning of ceramics, clearly demonstrate that China is exactly " native places of ceramics ".Porcelain, which is grasped, early in European manufactures skill
As soon as before more than thousand years of art, Han nationality has produced very exquisite ware.China is the country for applying pottery earliest in the world
One, and Chinese porcelain due to its high practicability and artistry by the high praise of common people.
An ancient unit of weight kiln of Yuzhou of Henan is northern celadon kiln system, still has very big achievement at present, generally uses bavin, coal, charcoal
It is fired with natural gas, the glaze color change that different burning process generates is also different.Outside is glaze production when by high-temperature fusion
Raw gorgeous colorful variation, for reason mainly in the formula of glaze, this is an important factor for influencing pottery finished product exogenic color, simultaneously
And cause pottery to enter kiln is of the same colour, the color key factor of kiln discharge ten thousand.
Glaze is exactly one layer of decorative layer on pottery surface, is the principal element for determining pottery glaze colours and being formed.Using natural
Raw mineral materials or the certain industrial chemicals of addition cooperate according to a certain percentage, melt under high temperature reducing atmospheres effect and are covered on embryo
Moisten gloss and colorful vitreum layer rich in jade-like stone in body surface face.With dicoration abundant, increase pottery natural trend
Aesthetic feeling makes pottery have certain artistic value and enjoying value.
Summary of the invention
Splendid, the novel roe Bluepoint of proportion that in view of the deficiencies of the prior art, it is an object of the present invention to provide a kind of colors
Shape pottery glaze and preparation method thereof.
To achieve the goals above, the present invention adopts the following technical scheme: a kind of roe Bluepoint shape pottery glaze, by white-based glaze
Formed with blue glaze two parts, according to weight ratio, the raw material for forming the blue glaze is long green stone 15-20 parts, 30-40 parts of melilite,
5-10 parts of Bai Changshi, 5-9 parts of quartz, 2-3 parts of cobalt, 4-5 parts of this medicine, 7-13 parts of calcite, 2-3 parts of Copper Ores of 2-6 parts of quartz,
1-5 parts of zinc oxide, 0.1-0.6 parts of tin oxide.
The raw material for forming the white-based glaze is melilite 30-50 parts, 15-20 parts of this medicine, 3-5 parts of montmorillonite, bauxite 2-
4 parts, 5-6 parts of quartz, 10-15 parts of calcite, 3-5 parts of talcum, 6-8 parts of frit, 5-7 parts of Copper Ores, 0.8-1.2 parts of tin oxide,
0.8-1.2 parts of bone ash, 2-3 parts of tourmaline.
Preferably, according to weight ratio, the raw material for forming the blue glaze is 16 parts of long green stone, 30 parts of melilite, white feldspar 6
Part, quartzy 5 parts, 3 parts of cobalt, 4 parts of this medicine, 7 parts of calcite, 2 parts of quartz, 2 parts of Copper Ores, 1 part of zinc oxide, 0.3 part of tin oxide.
The raw material for forming the white-based glaze is 30 parts of melilite, 20 parts of this medicine, 3 parts of montmorillonite, 3 parts of bauxite, quartz 5
Part, 10 parts of calcite, 3 parts of talcum, 6 parts of frit, 5 parts of Copper Ores, 0.8 part of tin oxide, 0.8 part of bone ash, 2 parts of tourmaline.
A kind of preparation method of roe Bluepoint shape pottery glaze, steps are as follows:
Step 1: by blue glaze raw material and white-based glaze raw material, ball milling, blue glaze raw material carry out wet in the ball mill in the ball mill respectively
Mill, wherein blue glaze raw material: ball: ball milling liquid=1.5:1:1.5 is dried after ball milling 18-22h, is sieved by 270-330 mesh net,
Obtain blue glaze raw material powder；White-based glaze raw material ball milling in dry method ball mill, wherein white-based glaze raw material: ball=1:1.5, white-based glaze are former
After pellet grinds 30-40h, it is sieved by 230-300 mesh mesh screen, obtains white-based glaze raw material powder；
Step 2: being separately added into water into blue glaze raw material powder and white-based glaze raw material powder, and stir evenly, obtains blue glaze raw material
Slurry and white-based glaze raw material slurry；
Step 3: with hairbrush by the lime-ash on the pottery element tire surface Jing Guo biscuiting and inner cavity, then the element after clearing up lime-ash
Tire surface spraying water erases the floating ash on plain tire surface layer with sponge or cotton later, obtains pretreated plain tire；
Step 4: pretreated plain tire is placed on glazing platform, blue glaze raw material slurry is coated on pretreated plain tire
Surface layer after the completion of coating, sprays blue glaze raw material slurry on the surface of white-based glaze raw material slurry, to blue glaze raw material slurry and white-based glaze
After raw material slurry air-dries, the plain tire of a glazing is obtained；It is circulation with the process of a glazing, continues the plain tire table in a glazing
Layer coating white-based glaze raw material slurry and blue glaze raw material slurry obtain the plain tire of secondary glazing after air-drying；Glazing 1-3 times in total of plain tire,
Obtain pottery glazed body；
Step 5: the glaze of pottery glazed body foot bottom is removed after glazing；
Step 6: through step 5 treated pottery glazed body enters kiln firing.
Beneficial effect
Compared with prior art, blue glaze raw material provided by the invention increases cobalt, the brightness of color is improved, by blue glaze
Raw material and white-based glaze raw material are layered glazing, after realizing to pottery glaze glazing, contain colorant of the same race or different colorant glaze
It is stacked with and assembles, the pottery glaze layer after glaze firing shows the dot pattern of roe indigo plant, and the appearance of entire porcelain is like starry sky
Equally, more aesthetically pleasing.
Specific embodiment
A specific embodiment of the invention is further described below.
A kind of roe Bluepoint shape pottery glaze, is made of white-based glaze and blue glaze two parts, according to weight ratio, forms the blue glaze
Raw material be long green stone 15-20 parts, 30-40 parts of melilite, feldspar 5-10 parts white, 5-9 parts of quartz, 2-3 parts of cobalt, 4-5 parts of this medicine,
7-13 parts of calcite, 2-6 parts of quartz, 2-3 parts of Copper Ores, 1-5 parts of zinc oxide, 0.1-0.6 parts of tin oxide.
The raw material for forming the white-based glaze is melilite 30-50 parts, 15-20 parts of this medicine, 3-5 parts of montmorillonite, bauxite 2-
4 parts, 5-6 parts of quartz, 10-15 parts of calcite, 3-5 parts of talcum, 6-8 parts of frit, 5-7 parts of Copper Ores, 0.8-1.2 parts of tin oxide,
0.8-1.2 parts of bone ash, 2-3 parts of tourmaline.
Preferably, according to weight ratio, the raw material for forming the blue glaze is 16 parts of long green stone, 30 parts of melilite, white feldspar 6
Part, quartzy 5 parts, 3 parts of cobalt, 4 parts of this medicine, 7 parts of calcite, 2 parts of quartz, 2 parts of Copper Ores, 1 part of zinc oxide, 0.3 part of tin oxide.
The raw material for forming the white-based glaze is 30 parts of melilite, 20 parts of this medicine, 3 parts of montmorillonite, 3 parts of bauxite, quartz 5
Part, 10 parts of calcite, 3 parts of talcum, 6 parts of frit, 5 parts of Copper Ores, 0.8 part of tin oxide, 0.8 part of bone ash, 2 parts of tourmaline.
A kind of preparation method of roe Bluepoint shape pottery glaze, steps are as follows:
Step 1: by blue glaze raw material and white-based glaze raw material, ball milling, blue glaze raw material carry out wet in the ball mill in the ball mill respectively
Mill, wherein blue glaze raw material: ball: ball milling liquid=1.5:1:1.5 is dried after ball milling 18-22h, is sieved by 270-330 mesh net,
Obtain blue glaze raw material powder；White-based glaze raw material ball milling in dry method ball mill, wherein white-based glaze raw material: ball=1:1.5, white-based glaze are former
After pellet grinds 30-40h, it is sieved by 230-300 mesh mesh screen, obtains white-based glaze raw material powder；
Step 2: being separately added into water into blue glaze raw material powder and white-based glaze raw material powder, and stir evenly, obtains blue glaze raw material
Slurry and white-based glaze raw material slurry；
Step 3: with hairbrush by the lime-ash on the pottery element tire surface Jing Guo biscuiting and inner cavity, then the element after clearing up lime-ash
Tire surface spraying water erases the floating ash on plain tire surface layer with sponge or cotton later, obtains pretreated plain tire；
Step 4: pretreated plain tire is placed on glazing platform, blue glaze raw material slurry is coated on pretreated plain tire
Surface layer after the completion of coating, sprays blue glaze raw material slurry on the surface of white-based glaze raw material slurry, to blue glaze raw material slurry and white-based glaze
After raw material slurry air-dries, the plain tire of a glazing is obtained；It is circulation with the process of a glazing, continues the plain tire table in a glazing
Layer coating white-based glaze raw material slurry and blue glaze raw material slurry obtain the plain tire of secondary glazing after air-drying；Glazing 1-3 times in total of plain tire,
Obtain pottery glazed body；
Step 5: the glaze of pottery glazed body foot bottom is removed after glazing；
Step 6: through step 5 treated pottery glazed body enters kiln firing.
Embodiment 1:
A kind of roe Bluepoint shape pottery glaze, is made of white-based glaze and blue glaze two parts, according to weight ratio, forms the original of the blue glaze
Material is 16 parts of long green stone, 32 parts of melilite, 5 parts of white feldspar, quartzy 5 parts, 3 parts of cobalt, 4 parts of this medicine, 7 parts of calcite, quartz 2
Part, 2 parts of Copper Ores, 2 parts of zinc oxide, 0.1 part of tin oxide.
The raw material for forming the white-based glaze is 30 parts of melilite, 15 parts of this medicine, 3 parts of montmorillonite, 2 parts of bauxite, quartz 5
Part, 10 parts of calcite, 3 parts of talcum, 6 parts of frit, 5 parts of Copper Ores, 0.8 part of tin oxide, 0.8 part of bone ash, 2 parts of tourmaline.
A kind of preparation method of roe Bluepoint shape pottery glaze, steps are as follows:
Step 1: by blue glaze raw material and white-based glaze raw material, ball milling, blue glaze raw material carry out wet in the ball mill in the ball mill respectively
Mill, wherein blue glaze raw material: ball: ball milling liquid=1.5:1:1.5 is dried after ball milling 18-22h, is sieved by 270-330 mesh net,
Obtain blue glaze raw material powder；White-based glaze raw material ball milling in dry method ball mill, wherein white-based glaze raw material: ball=1:1.5, white-based glaze are former
After pellet grinds 30-40h, it is sieved by 230-300 mesh mesh screen, obtains white-based glaze raw material powder；
Step 2: being separately added into water into blue glaze raw material powder and white-based glaze raw material powder, and stir evenly, obtains blue glaze raw material
Slurry and white-based glaze raw material slurry；
Step 3: with hairbrush by the lime-ash on the pottery element tire surface Jing Guo biscuiting and inner cavity, then the element after clearing up lime-ash
Tire surface spraying water erases the floating ash on plain tire surface layer with sponge or cotton later, obtains pretreated plain tire；
Step 4: pretreated plain tire is placed on glazing platform, white-based glaze raw material slurry is coated on pretreated element
Tire surface layer after the completion of coating, sprays blue glaze raw material slurry on the surface of white-based glaze raw material slurry, to blue glaze raw material slurry and white background
After glaze raw material slurry air-dries, the plain tire of a glazing is obtained；It is circulation with the process of a glazing, continues the plain tire in a glazing
Surface layer coats white-based glaze raw material slurry and blue glaze raw material slurry, and the plain tire of secondary glazing is obtained after air-drying；Plain tire glazing 1-3 in total
It is secondary, obtain pottery glazed body；
Step 5: the glaze of pottery glazed body foot bottom is removed after glazing；
Step 6: through step 5 treated pottery glazed body enters kiln firing.
Embodiment 2:
A kind of roe Bluepoint shape pottery glaze, is made of white-based glaze and blue glaze two parts, according to weight ratio, forms the original of the blue glaze
Material is 18 parts of long green stone, 30 parts of melilite, 5 parts of white feldspar, quartzy 5 parts, 3 parts of cobalt, 5 parts of this medicine, 7 parts of calcite, quartz 2
Part, 2 parts of Copper Ores, 3 parts of zinc oxide, 0.3 part of tin oxide.
The raw material for forming the white-based glaze is 35 parts of melilite, 15 parts of this medicine, 4 parts of montmorillonite, 2 parts of bauxite, quartz 5
Part, 10 parts of calcite, 3 parts of talcum, 6 parts of frit, 6 parts of Copper Ores, 1 part of tin oxide, 1 part of bone ash, 2 parts of tourmaline.
A kind of preparation method of roe Bluepoint shape pottery glaze, steps are as follows:
Step 1: by blue glaze raw material and white-based glaze raw material, ball milling, blue glaze raw material carry out wet in the ball mill in the ball mill respectively
Mill, wherein blue glaze raw material: ball: ball milling liquid=1.5:1:1.5 is dried after ball milling 18-22h, is sieved by 270-330 mesh net,
Obtain blue glaze raw material powder；White-based glaze raw material ball milling in dry method ball mill, wherein white-based glaze raw material: ball=1:1.5, white-based glaze are former
After pellet grinds 30-40h, it is sieved by 230-300 mesh mesh screen, obtains white-based glaze raw material powder；
Step 2: being separately added into water into blue glaze raw material powder and white-based glaze raw material powder, and stir evenly, obtains blue glaze raw material
Slurry and white-based glaze raw material slurry；
Step 3: with hairbrush by the lime-ash on the pottery element tire surface Jing Guo biscuiting and inner cavity, then the element after clearing up lime-ash
Tire surface spraying water erases the floating ash on plain tire surface layer with sponge or cotton later, obtains pretreated plain tire；
Step 4: pretreated plain tire is placed on glazing platform, blue glaze raw material slurry is coated on pretreated plain tire
Surface layer after the completion of coating, sprays white-based glaze raw material slurry on the surface of blue glaze raw material slurry, former to blue glaze raw material slurry and blue glaze
After slurry material air-dries, the plain tire of a glazing is obtained；It is circulation with the process of a glazing, continues on the plain tire surface layer of a glazing
Blue glaze raw material slurry and white-based glaze raw material slurry are coated, the plain tire of secondary glazing is obtained after air-drying；Glazing 1-3 times in total of plain tire, obtains
Pottery glazed body；
Step 5: the glaze of pottery glazed body foot bottom is removed after glazing；
Step 6: through step 5 treated pottery glazed body enters kiln firing.
After the completion of pottery glazed body in such embodiment is fired, what pottery surface was presented is blue cloud.
The above described is only a preferred embodiment of the present invention, be not intended to limit the present invention in any form, though
So the present invention has been disclosed as a preferred embodiment, and however, it is not intended to limit the invention, any technology people for being familiar with this profession
Member, without departing from the scope of the present invention, when the technology contents using the disclosure above are modified or are modified
It is right according to the technical essence of the invention for the equivalent embodiment of equivalent variations, but without departing from the technical solutions of the present invention
Any simple modification, equivalent change and modification made by above embodiments, all of which are still within the scope of the technical scheme of the invention.
Claims (3)
1. a kind of roe Bluepoint shape pottery glaze, is made of white-based glaze and blue glaze two parts, it is characterised in that: according to weight ratio, group
At the blue glaze raw material be long green stone 15-20 parts, 30-40 parts of melilite, feldspar 5-10 parts white, 5-9 parts of quartz, 2-3 parts of cobalt,
4-5 parts of this medicine, 7-13 parts of calcite, 2-6 parts of quartz, 2-3 parts of Copper Ores, 1-5 parts of zinc oxide, 0.1-0.6 parts of tin oxide；
Form the white-based glaze raw material be melilite 30-50 parts, 15-20 parts of this medicine, 3-5 parts of montmorillonite, 2-4 parts of bauxite,
5-6 parts quartzy, 10-15 parts of calcite, 3-5 parts of talcum, 6-8 parts of frit, 5-7 parts of Copper Ores, 0.8-1.2 parts of tin oxide, bone ash
0.8-1.2 parts, 2-3 parts of tourmaline.
2. a kind of roe Bluepoint shape pottery glaze according to claim 1, it is characterised in that: according to weight ratio, described in composition
The raw material of blue glaze be 16 parts of long green stone, 30 parts of melilite, 6 parts of white feldspar, quartz 5 parts, 3 parts of cobalt, 4 parts of this medicine, 7 parts of calcite,
2 parts of quartz, 2 parts of Copper Ores, 1 part of zinc oxide, 0.3 part of tin oxide；
The raw material for forming the white-based glaze is 30 parts of melilite, 20 parts of this medicine, 3 parts of montmorillonite, 3 parts of bauxite, 5 parts of quartz, side
Solve 10 parts of stone, 3 parts of talcum, 6 parts of frit, 5 parts of Copper Ores, 0.8 part of tin oxide, 0.8 part of bone ash, 2 parts of tourmaline.
3. the preparation method of roe Bluepoint shape pottery glaze described in any one of -2 according to claim 1, which is characterized in that step
It is as follows:
Step 1: by blue glaze raw material and white-based glaze raw material, ball milling, blue glaze raw material carry out wet in the ball mill in the ball mill respectively
Mill, wherein blue glaze raw material: ball: ball milling liquid=1.5:1:1.5 is dried after ball milling 18-22h, is sieved by 270-330 mesh net,
Obtain blue glaze raw material powder；White-based glaze raw material ball milling in dry method ball mill, wherein white-based glaze raw material: ball=1:1.5, white-based glaze are former
After pellet grinds 30-40h, it is sieved by 230-300 mesh mesh screen, obtains white-based glaze raw material powder；
Step 2: being separately added into water into blue glaze raw material powder and white-based glaze raw material powder, and stir evenly, obtains blue glaze raw material
Slurry and white-based glaze raw material slurry；
Step 3: with hairbrush by the lime-ash on the pottery element tire surface Jing Guo biscuiting and inner cavity, then the element after clearing up lime-ash
Tire surface spraying water erases the floating ash on plain tire surface layer with sponge or cotton later, obtains pretreated plain tire；
Step 4: pretreated plain tire is placed on glazing platform, white-based glaze raw material slurry is coated on pretreated element
Tire surface layer after the completion of coating, sprays blue glaze raw material slurry on the surface of white-based glaze raw material slurry, to blue glaze raw material slurry and white background
After glaze raw material slurry air-dries, the plain tire of a glazing is obtained；It is circulation with the process of a glazing, continues the plain tire in a glazing
Surface layer coats white-based glaze raw material slurry and blue glaze raw material slurry, and the plain tire of secondary glazing is obtained after air-drying；Plain tire glazing 1-3 in total
It is secondary, obtain pottery glazed body；
Step 5: the glaze of pottery glazed body foot bottom is removed after glazing；
Step 6: through step 5 treated pottery glazed body enters kiln firing.