CN104387091A - High-grade ceramic underglaze color manufacturing and decorating method - Google Patents
High-grade ceramic underglaze color manufacturing and decorating method Download PDFInfo
- Publication number
- CN104387091A CN104387091A CN201410620879.XA CN201410620879A CN104387091A CN 104387091 A CN104387091 A CN 104387091A CN 201410620879 A CN201410620879 A CN 201410620879A CN 104387091 A CN104387091 A CN 104387091A
- Authority
- CN
- China
- Prior art keywords
- temperature
- glaze
- color
- biscuiting
- firing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-grade ceramic underglaze color manufacturing and decorating method. The underglaze color is manufactured in a three-time firing mode. The method comprises the following steps: performing biscuit firing on the green body, performing colored firing, and finally performing glaze firing; the method is characterized in that according to the three-time firing mode, the underglaze color ceramics are manufactured by virtue of a three-times firing method comprising high-temperature biscuit firing, high-temperature colored firing and low-temperature glaze firing, wherein the high-temperature biscuit firing is performed under the temperature condition of 1150-1250 DEG C; the high-temperature colored firing is performed under the temperature condition of 1000-1250 DEG C; and the low-temperature glaze firing is performed under the temperature condition of 1000-1140 DEG C.
Description
Technical field
The present invention relates to the technologic improvement of a kind of traditional ceramics, particularly a kind of oxydizing flame of middle gentle pyroceramic and the improvement of reducing flame under glazed method of manufacturing technology, can be applicable to oxydizing flame and the manufacture of reducing flame under glazed of middle gentle pyroceramic, is innovate the one of under-glaze decoration ceramic manufacture craft.
background technology:
Under glazed is the one of porcelain muffle painting decoration, also known as " kiln is color ".Under glazed mainly above draws various decorative pattern with colorant at the molded biscuit (i.e. work in-process) dried, and then covers with white clear glaze or other light cover-coat enamels, enters kiln high temperature (1200-1400 DEG C) once-firing.Pattern after burning till is covered below by the glaze film of layer of transparent, and surface-brightening is soft, smoothly do not protrude, and seems sparkling and crystal-clear bright.Its feature is that color is intact, does not prolongedly move back.Under the bule and white porcelain that we see usually, under-glaze red porcelain, blue and white with copper red colors, glaze, three faiences, five color painting in the glaze porcelain etc. all belong under glazed.
Though the appearance of under glazed porcelain should trace back to the Chinese end the period of Three Kingdoms, until continuing for the research of under glazed today always, people are improving this kind of ceramic primary decoration gimmick all the time; Existing under glazed many employings double-firing process, namely first makes base substrate by high temperature biscuiting; Then on base substrate, carry out painting decoration with color painting on low temperature glaze, pigment is attached on base substrate; Base substrate after painting decoration is sent into low-temperature enamel firing kiln and carries out low temperature baking, the pigment on base substrate and base substrate are combined; Transparent on base substrate after low temperature baking; The upper base substrate crossing transparent is sent into high temperature kiln, carries out high-temperature firing, make under-glaze decoration ceramic.Though this twice firing process is simple, there is color and be difficult to grasp, be difficult to fire high-grade five color painting in the glaze pottery.In order to change this situation, though also there is now the technique proposing to take to burn till for three times, but from actual effect, still be not and ideal, mainly present ceramic under glazed produce in look burn and only have burning techniques under middle temperature 700 degree-800 degree oxydizing flame glaze, reducing flame can not be realized and burn look technology, and higher to color requirement, production cost is high, cannot realize the requirement of high-grade under enamel colored ceramic process.Therefore necessary this to be improved.
Do not find that there is the patent literature constructed with the present invention by patent retrieval, related to the present invention mainly containing is following:
1, the patent No. is CN201310239284.5, name is called the patent of invention of " a kind of method of high-temperature firing under glazed look crack ceramic ", which disclose a kind of method of high-temperature firing under glazed look crack ceramic, belong to manufacturing method of ceramic technical field, its technical essential comprises the steps: that (1) makes ceramic paste preforms body and carries out drying, for subsequent use; (2) dried ceramic paste preforms body to be immersed in the transparent glaze slip of high temperature feldspar 3 ~ 8 seconds, take out dry after for subsequent use; (3) low-firing is carried out by after the loading of kiln of dried for leaching glaze ceramic paste preforms body; (4) take out ceramic semi-finished product, leave standstill 1 ~ 3 day at normal temperatures, the glaze layer on ceramic semi-finished product surface is cracked; (5) immerse in colored glaze slip by the ceramic semi-finished product cracked, the immersion time is 3 ~ 8 seconds, takes out dry rear for subsequent use; (6) high-temperature firing is carried out by after dried for double dipping ceramic semi-finished product loading of kiln.
2, the patent No. is CN200710016537.7, name is called the patent of invention of " a kind of manufacturing method of under-glaze decoration ceramic of twice firing ", which disclose a kind of manufacturing method of under-glaze decoration ceramic of twice firing, its step is, a. makes the base substrate of high temperature biscuiting; B. on base substrate, carry out painting decoration with color painting on low temperature glaze, pigment is attached on base substrate; C. the base substrate after painting decoration is sent into low-temperature enamel firing kiln and carry out low temperature baking, the pigment on base substrate and base substrate are combined; D. transparent on the base substrate after low temperature baking; E. the upper base substrate crossing transparent is sent into high temperature kiln, carry out high-temperature firing, make under-glaze decoration ceramic.
3, the patent No. is CN02136786.8, name is called the patent of invention of " ceramics technique for color under glaze in high temp ", which disclose ceramics technique for color under glaze in high temp, this technique comprises the following steps: (1) is shaping: ceramic raw material is shaped to required article shape, makes unpainted clay idol; (2) biscuiting: the unpainted clay idol after shaping is carried out biscuiting, obtains plain tire, biscuiting temperature is 700 ~ 800 DEG C; (3) polishing: the plain tire after biscuiting is carried out surface finish processing treatment, obtains the plain tire that surfacing is smooth; (4) colored drawing: carry out colored drawing or applique on the glabrificin tire surface after polishing, obtain the color tire with colour picture; (5) look burns: the color tire after colored drawing is carried out look burning, and with the color of fixing colored drawing, it is 700 ~ 800 DEG C that look burns temperature; (6) water glaze or leaching glaze: carry out on the color tire surface of burning through look watering glaze or leaching glaze, glaze is covered whole color tire surface; (7) grand feu: carry out grand feu by watering the color tire after glaze, temperature of glaze firing is 1320 ~ 1400 DEG C; (8) porcelain is become: after grand feu, tire glaze sinters porcelain into, namely obtains ceramic high temperature under glazed goods.
These patents above-mentioned mostly are double-firing process, only have CN02136786.8 patent to propose employing to burn till for three times, but it is still that in employing 700 ~ 800 DEG C, warm colour burns that the look proposed burns, and glaze firing employing is high temperature, the easy like this problem that heavy metal overflows when there is glaze firing, is unfavorable for making high-grade under enamel colored pottery.Therefore how to propose a kind of suitable high-grade under enamel colored manufacture craft, still need to be studied further.
Summary of the invention
The object of the invention is to solve some problems existing for the making of current under-glaze decoration ceramic, exploitation one is not easy to occur that metal overflows, the under glazed trailing that color is more gorgeous, this kind of method is not only easy and simple to handle, and it is beautiful in colour simple and honest and can not wear and tear and fade and effectively isolate the metallics strippings such as plumbous cadmium, and glaze paint has the effect of killing fungi under photosynthesis, effectively can control human body diseases, under-glaze decoration ceramic manufacture can be widely used in.
Based on above-mentioned imagination, the technical scheme that the present invention proposes is: a kind of high-grade under enamel colored ceramic decoration method, takes three firing modes to make, first base substrate is carried out biscuiting, and then is that look burns, and is finally glaze firing; Its feature is, burning till for described three times is burnt by high temperature biscuiting, high-temperature color and three process for calcining making under-glaze decoration ceramics of end temperature glaze firing, wherein:
Described high temperature biscuiting carries out biscuiting under temperature is the condition of 1150-1250 DEG C;
It is carry out look burning under temperature is the condition of 1000-1250 DEG C that described high-temperature color is burnt;
Described low temperature sinter carries out glaze firing under temperature is the condition of 1000-1140 DEG C.
Further, described high temperature biscuiting is placed in by biscuit in biscuiting saggar to carry out button burning; The biscuit made is put into saggar with cover, buckles well saggar lid, make biscuit be in closed state in saggar; Again the saggar that biscuit is housed is placed in biscuiting stove, carries out biscuiting by the temperature of 1100-1250 DEG C.
Further, it is the color tire of drawn pattern is placed in look to burn in stove that described high-temperature color is burnt, and carries out burning look by the reducing flames of 1150-1380 DEG C.
Further, described low temperature sinter is that color blank look burned is carried out glazing treatment, then is placed in glaze firing stove by the color blank of first-class glaze, carries out glaze firing by the oxydizing flame of 1000-1140 DEG C.
Further, three times described firing process are as follows:
1, base: the raw material making under-glaze decoration ceramic is refined into moulded pottery not yet put in a kiln to bake material, then is made into required shape biscuit as required;
2, high temperature biscuiting: the shaping biscuit of making is placed in biscuiting saggar and carries out button burning; It is that the biscuit made is put into saggar with cover that described button burns, and buckles well saggar lid, makes biscuit be in closed state in saggar; Again the saggar that biscuit is housed is placed in biscuiting stove, carries out biscuiting by the temperature of 1150-1250 DEG C;
3, colored drawing: by the biscuit surface grinding after biscuiting, then the pattern needed for the surface rendering of biscuit, obtain the color tire with colour picture;
4, high-temperature color is burnt: be placed in by the color tire after colored drawing in look burning stove and carry out look burning, and with the color of fixing colored drawing, look burns temperature and is 1150-1380 DEG C, and takes reducing flame to carry out burning look, obtains the color blank with multi color pattern;
5, glazing: color blank surface carried out watering glaze or leaching glaze, covers whole color tire surface by glaze;
6, low temperature sinter: be placed in glaze firing stove by the glaze blank of first-class glaze, carry out glaze firing by oxydizing flame, firing temperature is 1000-1140 DEG C.
Further, the pattern needed for described surface rendering is Freehandhand-drawing or applique.
Beneficial effect of the present invention:
1. burnt and three process for calcining of end temperature glaze firing by high temperature biscuiting, high-temperature color, change warm biscuiting in routine completely, the making method of grand feu; Blank is just being shaped after biscuiting, can greatly reduce so color tire when burning look produce the situation of distortion, improve the qualification rate of color tire, greatly reduce the production cost of under glazed porcelain, improve production efficiency.
2. the present invention takes the manufacture craft of low temperature sinter, can reduce glaze overflow in sintering procedure heavy metal may, effectively isolation heavy metal lead cadmium overflows, without lead poisoning, acid and alkali-resistance, wear-resistant, will never fade.
3. take high-temperature color to burn, and take reducing flame to carry out burning look, there is color and luster more bright-coloured; It is good white as a jade that the under glazed of burning till has porcelain, bright as mirror, thin as a piece of paper, and sound is as the feature used up.
Embodiment
Below in conjunction with embodiment, the present invention will be further described.
Embodiment one
A kind of high-grade under enamel colored ceramic decoration method, takes three firing modes to make, first base substrate is carried out biscuiting, and then is that look burns, and is finally glaze firing; Its feature is, burning till for described three times is burnt by high temperature biscuiting, high-temperature color and three process for calcining making under-glaze decoration ceramics of end temperature glaze firing; Concrete manufacturing process steps is as follows:
1, base: the raw material making under-glaze decoration ceramic is refined into moulded pottery not yet put in a kiln to bake material, then is made into required shape biscuit as required;
2, high temperature biscuiting: the shaping biscuit of making is placed in biscuiting saggar and carries out button burning; It is that the biscuit made is put into saggar with cover that described button burns, and buckles well saggar lid, makes biscuit be in closed state in saggar; Again the saggar that biscuit is housed is placed in biscuiting stove, carries out biscuiting by the temperature of 1250 DEG C;
3, colored drawing: by the biscuit surface grinding after biscuiting, then the pattern needed for being made by applique on the surface of biscuit, obtain the color tire with colour picture;
4, high-temperature color is burnt: be placed in by the color tire after colored drawing in look burning stove and carry out look burning, with the color of fixing colored drawing, it is 1380 DEG C that look burns temperature, and takes reducing flame to carry out burning look, obtains the color blank with multi color pattern;
5, glazing: color blank surface carried out watering glaze or leaching glaze, covers whole color tire surface by glaze;
6, low temperature sinter: be placed in glaze firing stove by the glaze blank of first-class glaze, carry out glaze firing by oxydizing flame, firing temperature is 1000 DEG C.
It is high that the under-glaze decoration ceramic burnt out in this way has intensity, bright in colour, and porcelain is good white as a jade, bright as mirror, thin as a piece of paper, and sound is as used up, and without lead poisoning, acid and alkali-resistance, wear-resistant, will never fade feature.
Embodiment two
A kind of high-grade under enamel colored ceramic decoration method, takes three firing modes to make, first base substrate is carried out biscuiting, and then is that look burns, and is finally glaze firing; Its feature is, burning till for described three times is burnt by high temperature biscuiting, high-temperature color and three process for calcining making under-glaze decoration ceramics of end temperature glaze firing; Concrete manufacturing process steps is as follows:
1, base: the raw material making under-glaze decoration ceramic is refined into moulded pottery not yet put in a kiln to bake material, then is made into required shape biscuit as required;
2, high temperature biscuiting: the shaping biscuit of making is placed in biscuiting saggar and carries out button burning; It is that the biscuit made is put into saggar with cover that described button burns, and buckles well saggar lid, makes biscuit be in closed state in saggar; Again the saggar that biscuit is housed is placed in biscuiting stove, carries out biscuiting by the temperature of 1150 DEG C;
3, colored drawing: by the biscuit surface grinding after biscuiting, then on the surface of biscuit by the pattern needed for manual drawing, obtain the color tire with colour picture;
4, high-temperature color is burnt: be placed in by the color tire after colored drawing in look burning stove and carry out look burning, with the color of fixing colored drawing, it is 1150 DEG C that look burns temperature, and takes reducing flame to carry out burning look, obtains the color blank with multi color pattern;
5, glazing: color blank surface carried out watering glaze or leaching glaze, covers whole color tire surface by glaze;
6, low temperature sinter: be placed in glaze firing stove by the glaze blank of first-class glaze, carry out glaze firing by oxydizing flame, firing temperature is 1100 DEG C.
It is higher that the under-glaze decoration ceramic burnt out in this way has intensity, and color and luster is more bright-coloured, and porcelain is good white as a jade, bright as mirror, thin as a piece of paper, and sound is as used up, and without lead poisoning, acid and alkali-resistance, wear-resistant, will never fade feature.
Embodiment two
A kind of high-grade under enamel colored ceramic decoration method, takes three firing modes to make, first base substrate is carried out biscuiting, and then is that look burns, and is finally glaze firing; Its feature is, burning till for described three times is burnt by high temperature biscuiting, high-temperature color and three process for calcining making under-glaze decoration ceramics of end temperature glaze firing; Concrete manufacturing process steps is as follows:
1, base: the raw material making under-glaze decoration ceramic is refined into moulded pottery not yet put in a kiln to bake material, then is made into required shape biscuit as required;
2, high temperature biscuiting: the shaping biscuit of making is placed in biscuiting saggar and carries out button burning; It is that the biscuit made is put into saggar with cover that described button burns, and buckles well saggar lid, makes biscuit be in closed state in saggar; Again the saggar that biscuit is housed is placed in biscuiting stove, carries out biscuiting by the temperature of 1200 DEG C;
3, colored drawing: by the biscuit surface grinding after biscuiting, then on the surface of biscuit by the pattern needed for manual drawing, obtain the color tire with colour picture;
4, high-temperature color is burnt: be placed in by the color tire after colored drawing in look burning stove and carry out look burning, with the color of fixing colored drawing, it is 1150 DEG C that look burns temperature, and takes reducing flame to carry out burning look, obtains the color blank with multi color pattern;
5, glazing: color blank surface carried out watering glaze or leaching glaze, covers whole color tire surface by glaze;
6, low temperature sinter: be placed in glaze firing stove by the glaze blank of first-class glaze, carry out glaze firing by oxydizing flame, firing temperature is 1050 DEG C.
It is higher that the under-glaze decoration ceramic burnt out in this way has intensity, and color and luster is more bright-coloured, and porcelain is good white as a jade, bright as mirror, thin as a piece of paper, and sound is as used up, and without lead poisoning, acid and alkali-resistance, wear-resistant, will never fade feature.
Can be found out by above-described embodiment, the present invention relates to a kind of high-grade under enamel colored ceramic decoration method, take three firing modes to make, first base substrate is carried out biscuiting, and then be that look burns, be finally glaze firing; Its feature is, burning till for described three times is burnt by high temperature biscuiting, high-temperature color and three process for calcining making under-glaze decoration ceramics of end temperature glaze firing, wherein:
Described high temperature biscuiting carries out biscuiting under temperature is the condition of 1150-1250 DEG C;
It is carry out look burning under temperature is the condition of 1000-1250 DEG C that described high-temperature color is burnt;
Described low temperature sinter carries out glaze firing under temperature is the condition of 1000-1140 DEG C.
Further, described high temperature biscuiting is placed in by biscuit in biscuiting saggar to carry out button burning; The biscuit made is put into saggar with cover, buckles well saggar lid, make biscuit be in closed state in saggar; Again the saggar that biscuit is housed is placed in biscuiting stove, carries out biscuiting by the temperature of 1100-1250 DEG C.
Further, it is the color tire of drawn pattern is placed in look to burn in stove that described high-temperature color is burnt, and carries out burning look by the reducing flames of 1150-1380 DEG C.
Further, described low temperature sinter is that color blank look burned is carried out glazing treatment, then is placed in glaze firing stove by the color blank of first-class glaze, carries out glaze firing by the oxydizing flame of 1000-1140 DEG C.
Further, three times described firing process are as follows:
1, base: the raw material making under-glaze decoration ceramic is refined into moulded pottery not yet put in a kiln to bake material, then is made into required shape biscuit as required;
2, high temperature biscuiting: the shaping biscuit of making is placed in biscuiting saggar and carries out button burning; It is that the biscuit made is put into saggar with cover that described button burns, and buckles well saggar lid, makes biscuit be in closed state in saggar; Again the saggar that biscuit is housed is placed in biscuiting stove, carries out biscuiting by the temperature of 1150-1250 DEG C;
3, colored drawing: by the biscuit surface grinding after biscuiting, then the pattern needed for the surface rendering of biscuit, obtain the color tire with colour picture;
4, high-temperature color is burnt: be placed in by the color tire after colored drawing in look burning stove and carry out look burning, and with the color of fixing colored drawing, look burns temperature and is 1150-1380 DEG C, and takes reducing flame to carry out burning look, obtains the color blank with multi color pattern;
5, glazing: color blank surface carried out watering glaze or leaching glaze, covers whole color tire surface by glaze;
6, low temperature sinter: be placed in glaze firing stove by the glaze blank of first-class glaze, carry out glaze firing by oxydizing flame, firing temperature is 1000-1140 DEG C.
Further, the pattern needed for described surface rendering is Freehandhand-drawing or applique.
Beneficial effect of the present invention:
The temperature that the present invention is burnt till for three times by change, fires three times and changes high temperature biscuiting into, high-temperature color is burnt and low temperature sinter, effectively can solve the deficiency existing for current conventional under glazed making, mainly contain following advantages:
1. burnt and three process for calcining of end temperature glaze firing by high temperature biscuiting, high-temperature color, change the middle temperature biscuiting of conventional secondary under glazed completely, the making method of grand feu; The quality of product can be improved by the change of three firing temperatures, improve the intensity of pottery itself, meet the requirement of high-grade under enamel colored ceramic making completely.
2. take high temperature biscuiting, blank just shaped after biscuiting, can greatly reduce so color tire when burning look produce the situation of distortion, improve the qualification rate of color tire, greatly reduce the production cost of under glazed porcelain, improve production efficiency.
3. take reducing flame high-temperature color to burn, make the color and luster that burns out more bright-coloured; It is good white as a jade that the under glazed of burning till has porcelain, bright as mirror, thin as a piece of paper, and sound is as the feature used up, and wear-resistant, will never fade.
4. the present invention takes the manufacture craft of low temperature sinter, and can reduce the possibility that glaze overflows heavy metal in sintering procedure, effectively isolation heavy metal lead cadmium overflows, and has without lead poisoning, the feature of acid and alkali-resistance.
Obviously, above-described embodiment is just in order to illustrate the several examples cited by the present invention, and simple change and the replacement of any those ordinary skill in the art are all within protection of the present invention.
Claims (6)
1. a high-grade under enamel colored ceramic decoration method, takes three firing modes to make, first base substrate is carried out biscuiting, and then is that look burns, and is finally glaze firing; It is characterized in that, burning till for described three times is burnt by high temperature biscuiting, high-temperature color and three process for calcining making under-glaze decoration ceramics of end temperature glaze firing, wherein:
Described high temperature biscuiting carries out biscuiting under temperature is the condition of 1150-1250 DEG C;
It is carry out look burning under temperature is the condition of 1000-1250 DEG C that described high-temperature color is burnt;
Described low temperature sinter carries out glaze firing under temperature is the condition of 1000-1140 DEG C.
2. high-grade under enamel colored ceramic decoration method as claimed in claim 1, is characterized in that, described high temperature biscuiting is placed in by biscuit in biscuiting saggar to carry out button burning; The biscuit made is put into saggar with cover, buckles well saggar lid, make biscuit be in closed state in saggar; Again the saggar that biscuit is housed is placed in biscuiting stove, carries out biscuiting by the temperature of 1100-1250 DEG C.
3. high-grade under enamel colored ceramic decoration method as claimed in claim 1, is characterized in that, it is the color tire of drawn pattern is placed in look to burn in stove that described high-temperature color is burnt, and carries out burning look by the reducing flames of 1150-1380 DEG C.
4. high-grade under enamel colored ceramic decoration method as claimed in claim 1, it is characterized in that, described low temperature sinter is that color blank look burned is carried out glazing treatment, then is placed in glaze firing stove by the color blank of first-class glaze, carries out glaze firing by the oxydizing flame of 1000-1140 DEG C.
5. high-grade under enamel colored ceramic decoration method as claimed in claim 1, it is characterized in that, three times described firing process are as follows:
1) base: the raw material making under-glaze decoration ceramic is refined into moulded pottery not yet put in a kiln to bake material, then is made into required shape biscuit as required;
2) high temperature biscuiting: the shaping biscuit of making is placed in biscuiting saggar and carries out button burning; It is that the biscuit made is put into saggar with cover that described button burns, and buckles well saggar lid, makes biscuit be in closed state in saggar; Again the saggar that biscuit is housed is placed in biscuiting stove, carries out biscuiting by the temperature of 1150-1250 DEG C;
3) colored drawing: by the biscuit surface grinding after biscuiting, then the pattern needed for the surface rendering of biscuit, obtain the color tire with colour picture;
4) high-temperature color is burnt: be placed in by the color tire after colored drawing in look burning stove and carry out look burning, and with the color of fixing colored drawing, look burns temperature and is 1150-1380 DEG C, and takes reducing flame to carry out burning look, obtains the color blank with multi color pattern;
5) glazing: color blank surface carried out watering glaze or leaching glaze, covers whole color tire surface by glaze;
6) low temperature sinter: be placed in glaze firing stove by the glaze blank of first-class glaze, carry out glaze firing by oxydizing flame, firing temperature is 1000-1140 DEG C.
6. high-grade under enamel colored ceramic decoration method as claimed in claim 5, it is characterized in that, the pattern needed for described surface rendering is Freehandhand-drawing or applique.