CN101367642A - Double firing manufacturing method of under-glaze decoration ceramic - Google Patents
Double firing manufacturing method of under-glaze decoration ceramic Download PDFInfo
- Publication number
- CN101367642A CN101367642A CNA2007100165377A CN200710016537A CN101367642A CN 101367642 A CN101367642 A CN 101367642A CN A2007100165377 A CNA2007100165377 A CN A2007100165377A CN 200710016537 A CN200710016537 A CN 200710016537A CN 101367642 A CN101367642 A CN 101367642A
- Authority
- CN
- China
- Prior art keywords
- glaze
- unburnt
- decoration
- low temperature
- under
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a manufacturing method for an under-glaze decoration pottery and porcelain twice fired, which has the steps that: firstly, an unburnt earthenware body fired by high temperature is made; secondly, low temperature over-glaze decoration paint is used to carry out painting decoration on the unburnt earthenware body, and the paint is adhered on the unburnt earthenware body; thirdly, the unburnt earthenware body after decorated by the painting is sent into a low temperature decorating kiln to carry out low temperature baking, and the paint on the unburnt earthenware body and the unburnt earthenware body are combined together; fourthly, transparent glaze is painted on the unburnt earthenware body after baked by the low temperature; fifthly, the unburnt earthenware body after painted by the transparent glaze is sent into a high temperature kiln to be fired by high temperature, and the under-glaze decoration pottery and porcelain is made. The pottery and porcelain manufactured by the method solves the problem that the picture wears after the under-glaze decoration pottery and porcelain is used for a long time. After fired in high temperature, the paint and glaze are tightly blent, the effect similar to rain drop glaze appears in the place where the paint is thick, artistic quality is strong, decoration effect is good, and esthetics is increased.
Description
Technical field
The invention provides a kind of production method of pottery.
Background technology
At present, in the production of high-grade household china, be the processing method that adopts twice firing and carry out the applique decoration of in-glaze decoration, over-glaze decoration mostly.The main production of in-glaze decoration pottery is, draws a design on moulded pottery not yet put in a kiln to bake, and glaze spraying is again put into kiln then and carried out high-temperature firing and form.Over-glaze decoration is being exactly to burn till the white glaze porcelain earlier, after carrying out applique on the white glaze, reenters kiln and forms through 600 ℃ of-900 ℃ of temperature bakings, and shortcoming after being to use the time long the picture wear problems can take place.And this applique decorative picture effect is blunt, lack artistry.
Also has a kind of under glazed processing method, it is that decoration adds coloured silk, cover glaze on green compact, biscuiting mold or glaze tire, through 1340 ℃ of left and right sides high temperature once-firings, colorant fully permeates among the base glaze, acid and alkali-resistance bright in luster does not have lead poisoning, but Yin Gaowen burns till, and the colorant of adaptation is few, and colour-change is extremely difficult to be grasped.In the production of high-grade household china, seldom use.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of manufacturing method of under-glaze decoration ceramic of twice firing, to solve the picture wear problems, the raising decorative effect.
The present invention is achieved in that a kind of manufacturing method of under-glaze decoration ceramic of twice firing, and the step of described production method is,
A makes the base substrate of high temperature biscuiting;
B, on the base substrate with low temperature glaze on color painting carry out painting decoration, with pigment attached on the base substrate;
C sends into the low temperature decorating firing kiln to the base substrate behind the painting decoration and carries out the low temperature baking, and pigment on the base substrate and base substrate are combined;
D, transparent on the base substrate after the low temperature baking;
E sends the last base substrate of crossing transparent into high temperature kiln, carries out high-temperature firing, makes under-glaze decoration ceramic.
The pottery that the manufacturing method of under-glaze decoration ceramic of this twice firing is produced has solved the long-time back picture wear problems of using of over-glaze decoration pottery.And behind the high-temperature firing, pigment and glaze merge closely, the effect of similar rain drop glaze also occurred in the thick and heavy place of pigment, rich artistry, and good decorating effect has strengthened its sight.
Embodiment
Further specify the present invention below.
When the base substrate behind the painting decoration was sent into the low temperature decorating firing kiln and carried out the low temperature baking, the kiln temperature was identical with the existing decoration firing firing time at 790 ℃-820 ℃, baking time.After the low temperature baking, slight crackle can appear in the thick and heavy part of pigment.
During high-temperature firing, identical in firing temperature, time and used kiln and the existing under-glaze decoration ceramic technology.
Other production stages among the present invention are as making the base substrate of high temperature biscuiting, identical in the technical scheme of taking and the existing ceramic production technology.
Claims (1)
1. the manufacturing method of under-glaze decoration ceramic of a twice firing is characterized in that, the step of described production method is,
A makes the base substrate of high temperature biscuiting;
B, on the base substrate with low temperature glaze on color painting carry out painting decoration, with pigment attached on the base substrate;
C sends into the low temperature decorating firing kiln to the base substrate behind the painting decoration and carries out the low temperature baking, and pigment on the base substrate and base substrate are combined;
D, transparent on the base substrate after the low temperature baking;
E sends the last base substrate of crossing transparent into high temperature kiln, carries out high-temperature firing, makes under-glaze decoration ceramic.