CN104843998A - Ru-porcelain ru red glaze and preparation method therefor - Google Patents
Ru-porcelain ru red glaze and preparation method therefor Download PDFInfo
- Publication number
- CN104843998A CN104843998A CN201510143200.7A CN201510143200A CN104843998A CN 104843998 A CN104843998 A CN 104843998A CN 201510143200 A CN201510143200 A CN 201510143200A CN 104843998 A CN104843998 A CN 104843998A
- Authority
- CN
- China
- Prior art keywords
- glaze
- porcelain
- accounts
- kiln
- red
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a ru-porcelain ru red glaze and a preparation method therefor. The ru-porcelain ru red glaze is prepared from the following glaze raw materials in part by weight: 15 to 16 parts of white feldspar, 26 to 28 parts of melilite, 12 to 15 parts of calcite, 8 to 10 parts of quartz stone, 29 to 31 parts of potassium feldspar, 0.3 to 0.7 part of plant ash, 1.0 to 1.5 parts of bone meal and 0.5 to 1.0 part of talcum powder. According to the ru-porcelain ru red glaze and the preparation method therefor disclosed by the invention, the potassium feldspar containing a great deal of iron element is used in a formula, so that the iron element serves as a color developing agent to present red, namely a ru red glaze color referred to in the invention, in the firing process of the oxidizing atmosphere of a biscuit in the early stage; and the ru red glaze color is the color of an intermediate temperate transmutation glaze, the types of ru porcelain glaze colors are increased, and fired ru porcelain is bright in glaze color, moist and soft in glaze surface, pure like jade and attractive in appearance and practical.
Description
Technical field
The present invention relates to your enamel and manufacture craft thereof a kind of, be specially your red glaze and manufacture craft thereof of your porcelain.
Background technology
One of your Ci Shi China five your name porcelain, its manufacturing process is once once lost, by technician's lucubrate, now resumes production.Ruyao enamel essential tone is a kind of light Celeste, and be commonly called as " duck's egg cyan ", glaze layer is not thick, with the transition variation of moulding, presents the layer variability of the deep or light depth.Glaze paint Crack sheet, mostly is in picturesque disorder superfine line sheet, is commonly called as " crab claw line ".Glaze colours changes irregularly with light, and glaze paint is grown has obvious butter feel, and glaze is slightly bright, is milkiness or crystalloid more, beautiful, gentle simple and unsophisticated just as " the sun shines again after the rain cloud tear ".
But in the manufacture craft of your enamel look existing except the glaze colours of green grass or young crops, blue cast, fresh rare red glaze, reduces aesthetic measure and the economic benefit of your porcelain to a certain extent.
Summary of the invention
In order to solve the problem, the object of the invention is to propose your red glaze and manufacture craft thereof of your porcelain, your red glaze colours is warm furnace transmutation glaze in one, adds the kind of your enamel look, and your the enamel look burnt out is gorgeous, and glaze paint is moistened soft, pure in beautiful, both artistic and practical.
The present invention in order to the taked technical scheme that solves the problem is: your red glaze of your porcelain, adopt white feldspar, melilith, calcite, quartzite, potassium felspar sand, plant ash, bone meal and talcum powder to be glaze raw material, the ratio of weight and number of each raw material add-on is: white feldspar accounts for 15-16 part, melilith accounts for 26-28 part, calcite accounts for 12-15 part, quartzite accounts for 8-10 part, potassium felspar sand accounts for 29-31 part, plant ash accounts for 0.3-0.7 part, bone meal accounts for 1.0-1.5 part and talcum powder accounts for 0.5-1.0 part; The potassium felspar sand of Ruzhou City of Henan Province when real estate taken from by described potassium felspar sand raw material.
Your your red glaze of porcelain makes the manufacture craft of your porcelain, and described preparation method is:
Step one, by after described glaze raw material pulverizing, ball mill is put into according to aforementioned proportion mixing, add the water of the 29-33% of mixing raw material gross weight, start wet-milling 14-18 hour, slip through wet-milling crosses 300 mesh sieves, leaves standstill 24 hours, uses moisture content tester to detect water content, and water content is adjusted to 58-60%, for subsequent use;
Step 2, with water, wiping dedusting is carried out to biscuit, while wiping by step one gained slip by stirring clockwise or counterclockwise, during stirring from the center of slip, and move to circumference gradually, churning time is 20 minutes, after having stirred, biscuit is put into glaze slip, carries out leaching glaze to biscuit outside surface, after leaching glaze completes, finishing base substrate;
Step 3, the base substrate trimmed in step 2 is put into kiln, ventilate in kiln, base substrate is fired in oxidizing atmosphere, control the firing temperature in kiln, make temperature evenly rise to 1055-1060 DEG C in 4.3-4.7 hour; Reduce the ventilation of kiln; kiln combustion atmosphere is made to transfer reducing atmosphere to gradually; after base substrate is incubated 30 minutes at 1055-1060 DEG C; control the firing temperature in kiln; temperature is made evenly to rise to 1235-1240 DEG C in 3-3.5 hour; be incubated 30 minutes, cease fire after being cooled to normal temperature and take out, namely obtain your porcelain of your red glaze colours.
In described step 3, base substrate is fired in oxidizing atmosphere, controls the firing temperature in kiln, preferably, makes temperature evenly rise to 1058 DEG C in 4.5 hours.
In described step 3, base substrate is fired in reducing atmosphere, controls the firing temperature in kiln, preferably, makes temperature evenly rise to 1238 DEG C in 3.2 hours.
The potassium felspar sand of Ruzhou City of Henan Province when real estate taken from by described potassium felspar sand raw material, and predominant amount per-cent is Al
2o
3account for 17.6%, SiO
2account for 53.59%, Fe
2o
3account for 11.79%, CaO accounts for 5.8%, K
2o accounts for 2.17%, Na
2o accounts for 0.82%, impurity accounts for 8.23%.
In described sintering procedure, when oxidizing atmosphere used and oxygen provide abundance, the flame atmosphere in complete combustion of fuel situation; Reducing atmosphere used and oxygen supply deficiency, the flame atmosphere in non-complete combustion of fuel situation, now can produce a large amount of carbon monoxide, have reductive action.
Beneficial effect of the present invention:
Your red glaze and manufacture craft thereof of your porcelain of the present invention, the potassium felspar sand containing a large amount of ferro element and kaolin is employed in formula, in the sintering procedure of biscuit oxidizing atmosphere in early stage, ferro element presents redness as developer, your the red glaze colours namely mentioned in the present invention; In glaze formula, the component proportions of aluminium element and element silicon is comparatively large, while minimizing biscuit carcass and glazed thickness, can improve intensity and the thermostability of porcelain, make your porcelain fired be thin tire starved glaze; Adding bone meal is jade sense in order to add glaze colours, and make the glaze colours that burns more gentle exquisitely carved, glaze paint is moistened soft, pure in beautiful; Talcum is a kind of common silicate minerals, its quality is very soft and have satiny feel, high temperature resistantly can to use as refractory materials, talcum is added in formula of the present invention, to prevent glaze layer in the suddenly cold and hot process firing and cool from bursting, avoiding glaze layer to occur unnecessary hacking.
Your ceramic handiwork that the formula mentioned in the present invention and manufacture craft burn out, glaze colours is that you is red, and good looking appearance, for your porcelain adds new glaze colours, improves the economic benefit of your porcelain.
Embodiment
In conjunction with following specific embodiment, the present invention is described in further detail, and protection scope of the present invention is not limited to following examples.Implement process of the present invention, condition, reagent, experimental technique etc., except the following content mentioned specially, be universal knowledege and the common practise of this area, the present invention is not particularly limited content.
Your red glaze of your porcelain, adopt white feldspar, melilith, calcite, quartzite, potassium felspar sand, plant ash, bone meal and talcum powder to be glaze raw material, the ratio of weight and number of each raw material add-on is: white feldspar accounts for 15-16 part, melilith accounts for 26-28 part, calcite accounts for 12-15 part, quartzite accounts for 8-10 part, potassium felspar sand accounts for 29-31 part, plant ash accounts for 0.3-0.7 part, bone meal accounts for 1.0-1.5 part and talcum powder accounts for 0.5-1.0 part; The potassium felspar sand of Ruzhou City of Henan Province when real estate taken from by described potassium felspar sand raw material.
Your your red glaze of porcelain makes the manufacture craft of your porcelain, and described preparation method is:
Step one, by after described glaze raw material pulverizing, ball mill is put into according to aforementioned proportion mixing, add the water of the 29-33% of mixing raw material gross weight, start wet-milling 14-18 hour, slip through wet-milling crosses 300 mesh sieves, leaves standstill 24 hours, uses moisture content tester to detect water content, and water content is adjusted to 58-60%, for subsequent use;
Step 2, with water, wiping dedusting is carried out to biscuit, while wiping by step one gained slip by stirring clockwise or counterclockwise, during stirring from the center of slip, and move to circumference gradually, churning time is 20 minutes, after having stirred, biscuit is put into glaze slip, carries out leaching glaze to biscuit outside surface, after leaching glaze completes, finishing base substrate;
Step 3, the base substrate trimmed in step 2 is put into kiln, ventilate in kiln, base substrate is fired in oxidizing atmosphere, control the firing temperature in kiln, make temperature evenly rise to 1055-1060 DEG C in 4.3-4.7 hour; Reduce the ventilation of kiln; kiln combustion atmosphere is made to transfer reducing atmosphere to gradually; after base substrate is incubated 30 minutes at 1055-1060 DEG C; control the firing temperature in kiln; temperature is made evenly to rise to 1235-1240 DEG C in 3-3.5 hour; be incubated 30 minutes, cease fire after being cooled to normal temperature and take out, namely obtain your porcelain of your red glaze colours.
The potassium felspar sand of Ruzhou City of Henan Province when real estate taken from by described potassium felspar sand raw material, and predominant amount per-cent is Al
2o
3account for 17.6%, SiO
2account for 53.59%, Fe
2o
3account for 11.79%, CaO accounts for 5.8%, K
2o accounts for 2.17%, Na
2o accounts for 0.82%, impurity accounts for 8.23%.
In sintering procedure, when oxidizing atmosphere used and oxygen provide abundance, the flame atmosphere in complete combustion of fuel situation; Reducing atmosphere used and oxygen supply deficiency, the flame atmosphere in non-complete combustion of fuel situation, now can produce a large amount of carbon monoxide, have reductive action.
Embodiment 1
Your red glaze of your porcelain, adopt white feldspar, melilith, calcite, quartzite, potassium felspar sand, plant ash, bone meal and talcum powder to be glaze raw material, the ratio of weight and number of each raw material add-on is: white feldspar accounts for 15 parts, melilith accounts for 26 parts, calcite accounts for 12 parts, quartzite accounts for 8 parts, potassium felspar sand accounts for 29 parts, plant ash accounts for 0.3 part, bone meal accounts for 1.0 parts and talcum powder accounts for 0.5 part; The potassium felspar sand of Ruzhou City of Henan Province when real estate taken from by described potassium felspar sand raw material.
Your your red glaze of porcelain makes the manufacture craft of your porcelain, and described preparation method is:
Step one, by after described glaze raw material pulverizing, ball mill is put into according to aforementioned proportion mixing, add the water of 29% of mixing raw material gross weight, start wet-milling 14 hours, slip through wet-milling crosses 300 mesh sieves, leaves standstill 24 hours, uses moisture content tester to detect water content, and water content is adjusted to 58%, for subsequent use;
Step 2, with water, wiping dedusting is carried out to biscuit, while wiping by step one gained slip by stirring clockwise or counterclockwise, during stirring from the center of slip, and move to circumference gradually, churning time is 20 minutes, after having stirred, biscuit is put into glaze slip, carries out leaching glaze to biscuit outside surface, after leaching glaze completes, finishing base substrate;
The base substrate trimmed in step 2 is put into kiln, ventilates in kiln, base substrate is fired in oxidizing atmosphere, control the firing temperature in kiln, make temperature evenly rise to 1055 DEG C in 4.3 hours; Reduce the ventilation of kiln; kiln combustion atmosphere is made to transfer reducing atmosphere to gradually; after base substrate is incubated 30 minutes at 1055 DEG C; control the firing temperature in kiln; temperature is made evenly to rise to 1235 DEG C in 3 hours; be incubated 30 minutes, cease fire after being cooled to normal temperature and take out, namely obtain your porcelain of your red glaze colours.
Embodiment 2
Your red glaze of your porcelain, adopt white feldspar, melilith, calcite, quartzite, potassium felspar sand, plant ash, bone meal and talcum powder to be glaze raw material, the ratio of weight and number of each raw material add-on is: white feldspar accounts for 16 parts, melilith accounts for 27 parts, calcite accounts for 13 parts, quartzite accounts for 9 parts, potassium felspar sand accounts for 30 parts, plant ash accounts for 0.4 part, bone meal accounts for 1.1 parts and talcum powder accounts for 0.6 part; The potassium felspar sand of Ruzhou City of Henan Province when real estate taken from by described potassium felspar sand raw material.
Your red glaze of porcelain makes the manufacture craft of your porcelain, and described preparation method is:
Step one, by after described glaze raw material pulverizing, ball mill is put into according to aforementioned proportion mixing, add the water of 30% of mixing raw material gross weight, start wet-milling 15 hours, slip through wet-milling crosses 300 mesh sieves, leaves standstill 24 hours, uses moisture content tester to detect water content, and water content is adjusted to 59%, for subsequent use;
Step 2, with water, wiping dedusting is carried out to biscuit, while wiping by step one gained slip by stirring clockwise or counterclockwise, during stirring from the center of slip, and move to circumference gradually, churning time is 20 minutes, after having stirred, biscuit is put into glaze slip, carries out leaching glaze to biscuit outside surface, after leaching glaze completes, finishing base substrate;
Step 3, the base substrate trimmed in step 2 is put into kiln, ventilate in kiln, base substrate is fired in oxidizing atmosphere, control the firing temperature in kiln, make temperature evenly rise to 1056 DEG C in 4.4 hours; Reduce the ventilation of kiln; kiln combustion atmosphere is made to transfer reducing atmosphere to gradually; after base substrate is incubated 30 minutes at 1056 DEG C; control the firing temperature in kiln; temperature is made evenly to rise to 1236 DEG C in 3.1 hours; be incubated 30 minutes, cease fire after being cooled to normal temperature and take out, namely obtain your porcelain of your red glaze colours.
Embodiment 3
Your red glaze of your porcelain, adopt white feldspar, melilith, calcite, quartzite, potassium felspar sand, plant ash, bone meal and talcum powder to be glaze raw material, the ratio of weight and number of each raw material add-on is: white feldspar accounts for 15 parts, melilith accounts for 28 parts, calcite accounts for 14 parts, quartzite accounts for 10 parts, potassium felspar sand accounts for 31 parts, plant ash accounts for 0.5 part, bone meal accounts for 1.2 parts and talcum powder accounts for 0.7 part; The potassium felspar sand of Ruzhou City of Henan Province when real estate taken from by described potassium felspar sand raw material.
Your your red glaze of porcelain makes the manufacture craft of your porcelain, and described preparation method is:
Step one, by after described glaze raw material pulverizing, ball mill is put into according to aforementioned proportion mixing, add the water of 31% of mixing raw material gross weight, start wet-milling 16 hours, slip through wet-milling crosses 300 mesh sieves, leaves standstill 24 hours, uses moisture content tester to detect water content, and water content is adjusted to 60%, for subsequent use;
Step 2, with water, wiping dedusting is carried out to biscuit, while wiping by step one gained slip by stirring clockwise or counterclockwise, during stirring from the center of slip, and move to circumference gradually, churning time is 20 minutes, after having stirred, biscuit is put into glaze slip, carries out leaching glaze to biscuit outside surface, after leaching glaze completes, finishing base substrate;
Step 3, the base substrate trimmed in step 2 is put into kiln, ventilate in kiln, base substrate is fired in oxidizing atmosphere, control the firing temperature in kiln, make temperature evenly rise to 1058 DEG C in 4.5 hours; Reduce the ventilation of kiln; kiln combustion atmosphere is made to transfer reducing atmosphere to gradually; after base substrate is incubated 30 minutes at 1057 DEG C; control the firing temperature in kiln; temperature is made evenly to rise to 1237 DEG C in 3.3 hours; be incubated 30 minutes, cease fire after being cooled to normal temperature and take out, namely obtain your porcelain of your red glaze colours.
Embodiment 4
Your red glaze of your porcelain, adopt white feldspar, melilith, calcite, quartzite, potassium felspar sand, plant ash, bone meal and talcum powder to be glaze raw material, the ratio of weight and number of each raw material add-on is: white feldspar accounts for 16 parts, melilith accounts for 28 parts, calcite accounts for 15 parts, quartzite accounts for 10 parts, potassium felspar sand accounts for 31 parts, plant ash accounts for 0.6 part, bone meal accounts for 1.4 parts and talcum powder accounts for 0.9 part; The potassium felspar sand of Ruzhou City of Henan Province when real estate taken from by described potassium felspar sand raw material.
Your your red glaze of porcelain makes the manufacture craft of your porcelain, and described preparation method is:
Step one, by after described glaze raw material pulverizing, ball mill is put into according to aforementioned proportion mixing, add the water of 29% of mixing raw material gross weight, start wet-milling 17 hours, slip through wet-milling crosses 300 mesh sieves, leaves standstill 24 hours, uses moisture content tester to detect water content, and water content is adjusted to 58%, for subsequent use;
Step 2, with water, wiping dedusting is carried out to biscuit, while wiping by step one gained slip by stirring clockwise or counterclockwise, during stirring from the center of slip, and move to circumference gradually, churning time is 20 minutes, after having stirred, biscuit is put into glaze slip, carries out leaching glaze to biscuit outside surface, after leaching glaze completes, finishing base substrate;
Step 3, the base substrate trimmed in step 2 is put into kiln, ventilate in kiln, base substrate is fired in oxidizing atmosphere, control the firing temperature in kiln, make temperature evenly rise to 1058 DEG C in 4.6 hours; Reduce the ventilation of kiln; kiln combustion atmosphere is made to transfer reducing atmosphere to gradually; after base substrate is incubated 30 minutes at 1058 DEG C; control the firing temperature in kiln; temperature is made evenly to rise to 1238 DEG C in 3.4 hours; be incubated 30 minutes, cease fire after being cooled to normal temperature and take out, namely obtain your porcelain of your red glaze colours.
Embodiment 5
Your red glaze of your porcelain, adopt white feldspar, melilith, calcite, quartzite, potassium felspar sand, plant ash, bone meal and talcum powder to be glaze raw material, the ratio of weight and number of each raw material add-on is: white feldspar accounts for 16 parts, melilith accounts for 28 parts, calcite accounts for 15 parts, quartzite accounts for 10 parts, potassium felspar sand accounts for 31 parts, plant ash accounts for 0.7 part, bone meal accounts for 1.5 parts and talcum powder accounts for 1.0 parts; The potassium felspar sand of Ruzhou City of Henan Province when real estate taken from by described potassium felspar sand raw material.
Your your red glaze of porcelain makes the manufacture craft of your porcelain, and described preparation method is:
Step one, by after described glaze raw material pulverizing, ball mill is put into according to aforementioned proportion mixing, add the water of 33% of mixing raw material gross weight, start wet-milling 18 hours, slip through wet-milling crosses 300 mesh sieves, leaves standstill 24 hours, uses moisture content tester to detect water content, and water content is adjusted to 60%, for subsequent use;
Step 2, with water, wiping dedusting is carried out to biscuit, while wiping by step one gained slip by stirring clockwise or counterclockwise, during stirring from the center of slip, and move to circumference gradually, churning time is 20 minutes, after having stirred, biscuit is put into glaze slip, carries out leaching glaze to biscuit outside surface, after leaching glaze completes, finishing base substrate;
Step 3, the base substrate trimmed in step 2 is put into kiln, ventilate in kiln, base substrate is fired in oxidizing atmosphere, control the firing temperature in kiln, make temperature evenly rise to 1060 DEG C in 4.7 hours; Reduce the ventilation of kiln; kiln combustion atmosphere is made to transfer reducing atmosphere to gradually; after base substrate is incubated 30 minutes at 1060 DEG C; control the firing temperature in kiln; temperature is made evenly to rise to 1240 DEG C in 3.5 hours; be incubated 30 minutes, cease fire after being cooled to normal temperature and take out, namely obtain your porcelain of your red glaze colours.
Claims (4)
1. your red glaze of your porcelain, it is characterized in that: adopt white feldspar, melilith, calcite, quartzite, potassium felspar sand, plant ash, bone meal and talcum powder to be glaze raw material, the ratio of weight and number of each raw material add-on is: white feldspar accounts for 15-16 part, melilith accounts for 26-28 part, calcite accounts for 12-15 part, quartzite accounts for 8-10 part, potassium felspar sand accounts for 29-31 part, plant ash accounts for 0.3-0.7 part, bone meal accounts for 1.0-1.5 part and talcum powder accounts for 0.5-1.0 part; The potassium felspar sand of Ruzhou City of Henan Province when real estate taken from by described potassium felspar sand raw material.
2. your your red glaze of porcelain makes the manufacture craft of your porcelain as claimed in claim 1, it is characterized in that: described preparation method is:
Step one, by after described glaze raw material pulverizing, ball mill is put into according to aforementioned proportion mixing, add the water of the 29-33% of mixing raw material gross weight, start wet-milling 14-18 hour, slip through wet-milling crosses 300 mesh sieves, leaves standstill 24 hours, uses moisture content tester to detect water content, and water content is adjusted to 58-60%, for subsequent use;
Step 2, with water, wiping dedusting is carried out to biscuit, while wiping by step one gained slip by stirring clockwise or counterclockwise, during stirring from the center of slip, and move to circumference gradually, churning time is 20 minutes, after having stirred, biscuit is put into glaze slip, carries out leaching glaze to biscuit outside surface, after leaching glaze completes, finishing base substrate;
Step 3, the base substrate trimmed in step 2 is put into kiln, ventilate in kiln, base substrate is fired in oxidizing atmosphere, control the firing temperature in kiln, make temperature evenly rise to 1055-1060 DEG C in 4.3-4.7 hour; Reduce the ventilation of kiln; kiln combustion atmosphere is made to transfer reducing atmosphere to gradually; after base substrate is incubated 30 minutes at 1055-1060 DEG C; control the firing temperature in kiln; temperature is made evenly to rise to 1235-1240 DEG C in 3-3.5 hour; be incubated 30 minutes, cease fire after being cooled to normal temperature and take out, namely obtain your porcelain of your red glaze colours.
3. your your red glaze of porcelain as claimed in claim 2 makes the manufacture craft of your porcelain, it is characterized in that: in described step 3, base substrate is fired in oxidizing atmosphere, controls the firing temperature in kiln, makes temperature evenly rise to 1058 DEG C in 4.5 hours.
4. your your red glaze of porcelain as claimed in claim 2 makes the manufacture craft of your porcelain, it is characterized in that: in described step 3, base substrate is fired in reducing atmosphere, controls the firing temperature in kiln, makes temperature evenly rise to 1238 DEG C in 3.2 hours.