CN1765817A - Green glaze ink color ceramics production method - Google Patents
Green glaze ink color ceramics production method Download PDFInfo
- Publication number
- CN1765817A CN1765817A CN 200410073264 CN200410073264A CN1765817A CN 1765817 A CN1765817 A CN 1765817A CN 200410073264 CN200410073264 CN 200410073264 CN 200410073264 A CN200410073264 A CN 200410073264A CN 1765817 A CN1765817 A CN 1765817A
- Authority
- CN
- China
- Prior art keywords
- coat enamel
- kiln
- ground
- enamel
- degree
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to manufacture method for blue-glazed grisaille-painting ceramic, also names obscured ceramic, which uses the factory formula of Yaozhou celedon glaze, and belongs to its new product. This invention provides a Pick-Out-Flower design technique and comprises the process as: base-applying underglaze-designing Pick-Out-Flower-entering kiln for biscuit firing-out kiln to applying cover glaze-entering kiln to complete. Wherein, combining a plurality of chemical materials to prepare the underglaze combines, using Pick-Out-Flower technique to complete decoration; for the atmosphere and temperature difference in kiln, the underglaze flows gradually and forms the art effect similar to Chinese ink painting.
Description
The present invention relates to (having another name called dim porcelain) production method of a kind of green-enamel black porcelain, the green-enamel black porcelain cover-coat enamel adopts the production formula of credit state celadon glaze, is the new variety of credit state celadon.
Also do not occur like product in the market, green-enamel black porcelain (having another name called dim porcelain) is different with other faience, and general faience is to adopt single beramic color, is plotted on the embryo with paintbrush with liquid mediation back and (is commonly called as colored drawing) as bule and white porcelain.Promptly being colorful ceramic, as five color painting in the glaze, also is to adopt single pigment, is in harmonious proportion respectively to be depicted on the embryo respectively.
The object of the invention provides a kind of use design and picks colored technology, executes the making method of colorful ground-coat enamel, cover-coat enamel employing credit state celadon glaze on made-up article.Ground-coat enamel is to make ground-coat enamel with the comprehensive number of chemical raw material of clay glaze, finishes decoration to pick colored gimmick, utilizes poor, the temperature head of kiln atmosphere when burning till, the picture that produces changes, the existing look that progressively flows of ground-coat enamel cover-coat enamel, fused, transmutation generates the roughly the same artistic effect of ink traditional Chinese Painting.
The present invention realizes in the following way: technical process of the present invention is: made-up article, and------flower is picked in design, and------kiln discharge is affixed by cover-coat enamel (the blue or green glaze in credit state)---goes into klining to go into the kiln biscuiting to execute ground-coat enamel.At first be the base product, made-up article is executed ground-coat enamel after doing, and selects base: select the method for base identical with common credit state celadon blank-making method, the preparation ground-coat enamel divided for three steps finished: the first step system color base: Manganse Dioxide (Mno
2), ferric oxide (Fe
2o
3), zinc oxide (Zno) weight ratio: be mixed with color base after mixing at 6: 3: 0.5; The second step enamel frit makeing coloured silk: get 1 part in color base and add 0.8 part of fireclay (Dongshan cash is produced in anti-clay such as kaolin or Tongchuan) in addition and add suitable quantity of water, the water mill pulping is promptly made muffle painting; Make ground-coat enamel at last: the formulation by weight ratio of ground-coat enamel is between the natural loess mud 80-82, between the common white glaze 8-10, muffle painting 7-9, these materials are mixed through mixing and are made ground-coat enamel, execute ground-coat enamel and adopt the glaze method operation, glazing thickness is 0.4mm---between the 0.8mm, picked flower executing on the made-up article of ground-coat enamel design, go into the kiln biscuiting then, biscuiting is heated to 850 degree from normal temperature
+-Between 20 degree, the oxydizing flame operation is adopted in biscuiting, and oxygen level remains between the 4%-8% in the kiln, is affixed by credit state celadon cover-coat enamel after the kiln discharge cooling.The prescription of cover-coat enamel is that natural loess mud cooperates with common white glaze glaze slip for 6-5.5: 4-4.5, will execute the cover-coat enamel made-up article at last and go into klining.Burn till in two steps and finish: the first step progressively is heated to 1020 degree from normal temperature
+-20 degree, this stage calcining system adopts the oxidizing atmosphere operation, and oxygen level remains between 4% to 8% in the kiln, and second step was heated to 1300 from 1020
+-10Degree.In this temperature range, adopt the reducing atmosphere operation, the carbon monoxide content in the kiln should remain between the 2-3%.
The product transmutation that the present invention produces is strong, rich color, glaze light, line formula are clear, picture is suspended between the tire glaze with all ceramic in market all not roughly the same, have the effect of typical ink traditional Chinese Painting.
Embodiment:
Fig. 1, lines line formula picture, select the whiter fetus of quality, execute the thick picture of picking out svelteness for 0.5mm-7mm of ground-coat enamel, to execute cover-coat enamel thickness be that cover-coat enamel loading of kiln under 1310 temperature of 0.3-0.5mm is burnt till in biscuiting under 900 degree, just made that the cover-coat enamel light is revealed the exact details, the picture of white tire lines suspension.
Fig. 2, transmutation type, choosing are fit to do the big type of scenery with hills and waters pattern, draw domain scenery with hills and waters pattern, pick out pattern part for blank, burn through high temperature, flow and can have well-bedded ink scenery with hills and waters pattern by natural type.
Produce the different transmutation and the combination of picture, must grasp the high warm nature of ground-coat enamel cover-coat enamel, strive for that multiple gimmick obtains multiple effect.
Claims (2)
1, a kind of production method of green-enamel black porcelain, it picks by made-up article one design and spends one to execute cover-coat enamel one loading of kiln and burn till and finish, and the made-up article biscuiting temperature of executing ground-coat enamel is 850 degree
+-Between 20 degree, will execute the cover-coat enamel made-up article and go into kiln and burn till under the temperature, go into klining, progressively be heated to 1020 degree from normal temperature through the made-up article of executing the bottom surface glaze at 1310 degree
+-20 degree in this temperature range, adopt the oxidizing atmosphere operation, and the content of oxygen remains between the 2-8% in the kiln, is heated to 1300 from 1020
+-10 degree in this temperature range, adopt the reducing atmosphere operation, and the carbon monoxide content in the kiln should remain between the 2-3%, it is characterized in that: the preparation ground-coat enamel divided for three steps finished: the first step system color base: Manganse Dioxide (Mno
2), ferric oxide (Fe
2o
3), zinc oxide (Zno) weight ratio: be mixed with color base after mixing at 6: 3: 0.5; The second step enamel frit makeing coloured silk: get 1 part in color base and add 0.8 part of fireclay (Dongshan cash is produced in anti-clay such as kaolin or Tongchuan) in addition and add suitable quantity of water, the water mill pulping is promptly made muffle painting; Make ground-coat enamel at last: the formulation by weight ratio of ground-coat enamel is between the natural loess mud 80-82, between the common white glaze 8-10, muffle painting 7-9, these materials are mixed through mixing and are made ground-coat enamel, and the prescription of cover-coat enamel is that natural loess mud cooperates with basic white glaze glaze slip for 6-5.5: 4-4.5.
2, as the production method of a kind of green-enamel black porcelain as described in claims 1, it is characterized in that: executing ground-coat enamel thickness is 0.4-0.8mm.