CN106807419B - 浸渍法制备加氢处理催化剂的方法 - Google Patents
浸渍法制备加氢处理催化剂的方法 Download PDFInfo
- Publication number
- CN106807419B CN106807419B CN201710137221.7A CN201710137221A CN106807419B CN 106807419 B CN106807419 B CN 106807419B CN 201710137221 A CN201710137221 A CN 201710137221A CN 106807419 B CN106807419 B CN 106807419B
- Authority
- CN
- China
- Prior art keywords
- acid
- solution
- compound
- hydrotreating catalyst
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种浸渍法制备加氢处理催化剂的方法,包括如下步骤:1)配制浸渍溶液,溶液中含有:含钼化合物以MoO3计为10~80g/100ml,含镍化合物以NiO计为1~15g/100ml,含磷化合物以P元素计为0.5~5g/100ml,碳酸盐浓度为0~20g/100ml,溶液pH为2~6;2)制备氧化铝载体;3)用步骤1)所得浸渍溶液浸渍步骤2)所得氧化铝载体,然后干燥、焙烧得到最终加氢处理催化剂。该方法制备的加氢处理催化剂,比表面积与孔容都有不同程度的提高,且有利于活性金属在载体表面分布均匀,同时活性金属与载体之间相互作用力均匀,使该催化剂加氢脱硫与加氢脱氮性能都有较大提升。
Description
技术领域
本发明涉及一种加氢处理催化剂,特别是指一种浸渍法制备加氢处理催化剂的方法。
背景技术
随着原油质量逐年变重变差,环保法规日趋严格,市场对清洁油品的需求量不断增长,使得生产清洁燃料的加氢技术获得越来越广泛得应用。馏分油加氢处理是指高温高压下,原料油和氢气在催化剂表面上发生加氢脱硫、加氢脱氮、加氢脱氧、加氢脱金属以及不饱和烃加氢饱和等催化反应。
目前,工业上所用的加氢处理催化剂,通常是以无机氧化物(如氧化铝、二氧化硅、氧化铝-二氧化硅等)为载体,按一定方式负载一些加氢活性金属组分(一般为ⅥB族金属和Ⅷ族金属,如Mo、W和Ni、Co等)。常见的负载活性金属组分的方法有浸渍法、混捏法等。考虑到高加氢活性以及对活性金属的充分利用,使用浸渍法制备加氢催化剂较为广泛。
用浸渍法制备加氢催化剂时,浸渍溶液的性质至关重要。特别是浸渍溶液pH值对催化剂表面上活性金属(如Mo)的结构、分散度及其与载体(如Al2O3)的相互作用有很大影响。根据pH值的不同,目前常用的加氢处理催化剂浸渍溶液有两种类型:
第一类为ⅥB族、Ⅷ族元素的碱性溶液,例如同时含有钼和钴(镍)的氨水溶液,此浸渍溶液为碱性,如果要一次浸渍制成催化剂,需要配成浓度很高的钼-钴(镍)-氨溶液,这种溶液不稳定,给浸渍操作带来困难,很难用这种浸渍溶液一次性负载制备高金属含量催化剂。
第二类为ⅥB族、Ⅷ族元素的酸性溶液,例如Mo-Ni-P浸渍溶液,制备时将磷酸与钼盐及镍盐以一定比例混合,加热回流,最终制得Mo-Ni-P溶液。加氢处理催化剂大多以γ-Al2O3为载体,其等电点为7~9,而Mo-Ni-P浸渍液的pH一般在2以下,过低的pH值不仅会使载体比表面积在浸渍过程中产生损失从而使催化剂比表面积有所降低;还会引起活性组分与载体相互作用过强,使活性金属分散性降低,导致加氢处理催化剂的活性降低。
针对Mo-Ni-P浸渍液PH偏低的问题,行业中有在酸性浸渍液中添加碱性含氮化合物(例如氨水溶液),使其pH值在2~6之间变化。这样虽然可以使浸渍溶液pH提高,但在调整溶液pH时加入大量的含氮化合物,使浸渍溶液中活性金属含量大大降低。因此,利用该方法制备浸渍溶液并制备高负载量加氢催化剂时,对于浸渍溶液初始活性金属含量要求过高,不易实现。
发明内容
本发明的目的在于提供一种催化剂比表面积和孔容较大、加氢活性较高的浸渍法制备加氢处理催化剂的方法。
为实现上述目的,本发明所提供的浸渍法制备加氢处理催化剂的方法,包括如下步骤:
1)配制浸渍溶液,溶液中含有:含钼化合物以MoO3计为10~80g/100ml,含镍化合物以NiO计为1~15g/100ml,含磷化合物以P元素计为0.5~5g/100ml,碳酸盐浓度为0.7~3.2g/100ml,溶液pH为2~6;
2)制备氧化铝载体;
3)采用步骤1)所得浸渍溶液浸渍步骤2)所得氧化铝载体,然后干燥、焙烧得到最终加氢处理催化剂。浸渍可以是等体积浸渍,也可以是过量浸渍,可以是分步浸渍,也可是共浸渍。优选为等体积共浸渍。
优选地,步骤1)中,所述碳酸盐为碱金属的碳酸正盐或酸式盐,如Na2CO3、NaHCO3;或者铵的碳酸正盐或酸式盐,如(NH4)2CO3、NH4HCO3,优选为(NH4)2CO3。
优选地,步骤1)中,所述含钼化合物为氧化钼、钼酸铵、仲钼酸铵中的一种或几种;所述含镍化合物为硝酸镍、醋酸镍、碱式碳酸镍、碳酸镍、氯化镍中的一种或几种;所述含磷化合物为磷酸、磷酸二氢铵、磷酸氢二铵、磷酸二氢钠及磷酸氢二钠中的一种及几种。所述含钼化合物优选为氧化钼,所述含镍化合物优选为碱式碳酸镍,所述含磷化合物优选为磷酸。
优选地,步骤2)中,所述氧化铝载体以大孔拟薄水铝石为原料,加入助挤剂、助剂与胶溶剂,经混捏、碾压、成型、干燥、焙烧步骤后制得。载体的成型、干燥和焙烧的方法为常规方法。载体成型,视不同要求可制成各种易于操作的成型载体,例如球形、蜂窝状、鸟巢状、片剂或条形(三叶草、蝶形、圆柱形等)。成型可按常规方法进行,成型方式优选为挤出成型。载体干燥和焙烧的条件均是常规的,例如,干燥温度为70℃~200℃,优选为100℃~150℃,干燥时间为0.5h~20h,优选为1h~6h;焙烧温度为300℃~600℃,优选为450℃~550℃,焙烧时间为0.5h~20h,优选为1h~6h。
优选地,所述助挤剂为田菁粉、多元羧酸助挤剂或者田菁粉与多元羧酸复合助挤剂,优选为田菁粉与多元羧酸复合助挤剂,所述多元羧酸优选为柠檬酸、酒石酸、草酸中一种或几种。
优选地,所述助剂为磷、氟、硼、锆、硅各元素的化合物中的一种或几种,所述助剂的引入量以氧化物计为成型载体总质量的5.5%以下,优选为0.5%~4%;助剂的引入方式可为直接加入与原料粉混合或者与胶溶剂溶液混合均匀后再加入原料粉中混捏。
优选地,所述胶溶剂为无机酸和/或有机酸,所述无机酸为硝酸或盐酸;所述有机酸为甲酸、乙酸、柠檬酸、三氯乙酸或丙二酸中一种或几种;所述胶溶剂优选为硝酸;所述胶溶剂的引入量为成型载体总质量的0.5%~10%,优选为1%~5%。
优选地,步骤3)中,浸渍过程采用等体积共浸渍;干燥温度为70℃~200℃,优选为100℃~160℃,干燥时间为0.5h~20h,优选为1h~6h;焙烧温度为300℃~600℃,优选为400℃~500℃,焙烧时间为0.5h~20h,优选为1h~6h。
优选地,步骤1)中,浸渍溶液按如下方式配制:1.1)向水中加入含钼化合物、含镍化合物、含磷化合物,混合均匀;1.2)采用两步加热升温,第一步升温至温度35~60℃,并恒温反应0~1.5h;第二步继续升温至温度90~110℃,并恒温回流0~3h,使步骤1)中加入的溶质全部溶解,得墨绿澄清透明溶液;在第一步恒温后或第二步恒温后加入碳酸盐,调节浸渍溶液的pH至2~6。
优选地,步骤1.2)中,第一步升温至温度40~50℃,并恒温反应0.5~1h;第二步继续升温至温度90~100℃,并恒温回流1~2h。
本发明的有益效果是:该方法通过在浸渍液配制反应中或者反应后引入碳酸盐,调节浸渍液pH,使该浸渍液pH较高且可调、活性金属含量高、稳定性好,用此浸渍液制备加氢处理催化剂,催化剂比表面积与孔容都有不同程度的提高,且有利于活性金属在载体表面分布均匀,同时活性金属与载体之间相互作用力均匀,使该催化剂加氢脱硫与加氢脱氮性能都有较大提升。
具体实施方式
下面通过具体实施例对本发明作进一步的详细说明。以下除特别说明外,涉及的百分含量为重量百分含量,干基测定方式为550℃下焙烧4h。
实施例1
本实施例介绍载体的制备方式。称取大孔拟薄水铝石(烟台恒辉化工有限公司,比表面350m2/g,孔容0.92ml/g,干基72.8%)275g,加入柠檬酸(湖北七八九化工)6g,田菁粉(武汉陌兴生物科技有限公司)4g,加入8.80g HNO3(65~68wt%)、7.2g H3BO3(99.5wt%)和220ml H2O混合均匀溶液,碾压20min,用两叶最大间距1.6mm三叶草孔板挤条成型,120℃干燥4h,500℃焙烧4h。焙烧后载体记为Z1。
对比例1
本对比例介绍不加碳酸盐常规Mo-Ni-P浸渍溶液制备方法。取9.3g磷酸(质量浓度85.0%)与150ml水混合加入三口烧瓶,在搅拌中加入三氧化钼(工业级)105.1g和碱式碳酸镍(以Ni计,44.0重量%)29.4g,升温至40~50℃,反应0.5h,升温至90~100℃,反应1h,停止加热,冷却至室温后对所得溶液过滤,定容至250ml,即得墨绿色澄清透明溶液A。测溶液pH为2.63。溶液中各物质浓度(金属浓度以氧化物计)为:MoO3为42g/ml,NiO为7g/ml,P为1g/100ml。
实施例2
本实施例介绍用对比例1中所制备溶液A加入碳酸铵调节浸渍溶液pH至4~6左右方法。取50ml溶液A放入烧杯,在不断搅拌条件下,缓慢加入碳酸铵(以NH3计,40.0重量%),控制加入速度。通过pH计及时测量溶液pH值,当pH达到目标值时停止加入碳酸铵,继续搅拌至溶液均匀稳定。在本实施例中,共制备三份溶液,分别调整pH值到4.10、4.99、6.04,所加碳酸铵量为0.38g、0.66g、1.1g,所得浸渍溶液分别为B、C、D。溶液中各物质浓度(金属浓度以氧化物计)都为:MoO3为42g/ml,NiO为7g/ml,P为1g/100ml。
实施例3
本实施例介绍在反应中加入碳酸盐制备Mo-Ni-P浸渍溶液pH值至4~6左右方法。取9.3g磷酸(质量浓度85.0%)与150ml水混合加入三口烧瓶,在搅拌中加入三氧化钼(工业级)105.1g和碱式碳酸镍(以Ni计,44.0重量%)29.4g,升温至40~50℃,反应0.5h,缓慢加入一定量碳酸铵(以NH3计,40.0重量%),碳酸铵量根据所需pH进行调整,升温至90~100℃,反应1h,停止加热,冷却至室温后对所得溶液过滤,定容至250ml,即得墨绿色澄清透明溶液。在本实施例中,共制备三份溶液,分别调整pH值到4.07、5.10、6.02,所加碳酸铵量为3.0g、5.1g、8.0g,所得浸渍溶液分别为E、F、G。溶液中各物质浓度(金属浓度以氧化物计)都为:MoO3为42g/ml,NiO为7g/ml,P为1g/100ml。
试验例1
本试验例列出浸渍溶液A~G主要性质,具体见表1。
表1 浸渍溶液A~G主要性质
实施例4
本实施例介绍用通过碳酸铵调节至较高pH值的溶液B~G浸渍制备催化剂。
取实施例1中所制备载体Z1,用溶液B进行等体积浸渍,浸渍完成后110℃干燥2h,460℃焙烧3h,制得催化剂C1。
与催化剂C1制备条件相同,分别用浸渍溶液C、D、E、F、G制备催化剂C2、C3、C4、C5、C6。
对比例2
本对比例介绍用未经碳酸铵调节pH的浸渍溶液A制备催化剂。
取实施例1中所制备载体Z1,用溶液A进行等体积浸渍,浸渍完成后110℃干燥2h,460℃焙烧3h,制得催化剂DC1。
试验例2
本试验例列出上述制备催化剂主要性质,具体见表2。
表2 制备催化剂主要性质
编号 | C<sub>1</sub> | C<sub>2</sub> | C<sub>3</sub> | C<sub>4</sub> | C<sub>5</sub> | C<sub>6</sub> | DC<sub>1</sub> |
MoO<sub>3</sub>,% | 23.31 | 23.65 | 23.88 | 23.28 | 23.60 | 23.82 | 23.11 |
NiO,% | 3.88 | 3.94 | 3.99 | 3.87 | 3.95 | 4.01 | 3.81 |
P,% | 1.01 | 1.01 | 1.05 | 1.00 | 1.02 | 1.02 | 1.00 |
B<sub>2</sub>O<sub>3</sub>,% | 2.89 | 2.89 | 2.89 | 2.89 | 2.89 | 2.89 | 2.89 |
比表面积/m<sup>2</sup>·g<sup>-1</sup> | 188 | 195 | 203 | 185 | 190 | 199 | 177 |
孔容/ml·g<sup>-1</sup> | 0.38 | 0.39 | 0.41 | 0.37 | 0.37 | 0.40 | 0.35 |
平均孔径/nm | 7.1 | 7.1 | 7.2 | 7.1 | 7.2 | 7.2 | 7.1 |
试验例3
本试验例为催化剂活性评价试验。催化剂活性评价试验在30ml小型装置上进行,活性评价前需要对催化剂进行预硫化。催化剂评价条件为在反应总压8.0MPa,体积空速1.0h-1,氢油比1000:1,反应温度380℃。活性评价试验用原料油性质见表3,活性评价结果见表4。
表3 原料油性质
原料油 | 伊朗VGO |
密度(20℃),g·cm<sup>-3</sup> | 0.9168 |
馏程,℃ | |
IBP | 336 |
EBP | 542 |
S,% | 1.59 |
N,% | 1681 |
表4 活性评价结果
催化剂 | C<sub>1</sub> | C<sub>2</sub> | C<sub>3</sub> | C<sub>4</sub> | C<sub>5</sub> | C<sub>6</sub> | DC<sub>1</sub> |
相对脱硫活性,% | 130 | 137 | 145 | 128 | 133 | 140 | 100 |
相对脱氮活性,% | 127 | 136 | 140 | 125 | 133 | 136 | 100 |
由上表可知,本发明通过用特定方法所制备的pH较高且可调、活性金属含量高、稳定性好浸渍溶液来制备催化剂,使催化剂比表面积和孔容都有所提高,对于该催化剂的加氢脱硫与加氢脱氮性能都有较大的提升。
Claims (5)
1.一种浸渍法制备加氢处理催化剂的方法,其特征在于:包括如下步骤:
1)配制浸渍溶液,溶液中含有:含钼化合物以MoO3计为10~80g/100ml,含镍化合物以NiO计为1~15g/100ml,含磷化合物以P元素计为0.5~5g/100ml,碳酸盐浓度为0.7~3.2g/100ml,溶液pH为4~6;其中:所述碳酸盐为碱金属的碳酸正盐或酸式盐,或者铵的碳酸正盐或酸式盐;所述含钼化合物为氧化钼、钼酸铵、仲钼酸铵中的一种或几种;所述含镍化合物为硝酸镍、醋酸镍、碱式碳酸镍、碳酸镍、氯化镍中的一种或几种;所述含磷化合物为磷酸、磷酸二氢铵、磷酸氢二铵、磷酸二氢钠及磷酸氢二钠中的一种及几种;
所述浸渍溶液按如下方式配制:1.1)向水中加入含钼化合物、含镍化合物、含磷化合物,混合均匀;1.2)采用两步加热升温,第一步升温至温度40~50℃,并恒温反应0.5~1h;第二步继续升温至温度90~100℃,并恒温回流1~2h,使步骤1)中加入的溶质全部溶解,得墨绿澄清透明溶液;在第一步恒温后或第二步恒温后加入碳酸盐,调节浸渍溶液的pH至4~6;
2)制备氧化铝载体;
3)采用步骤1)所得浸渍溶液浸渍步骤2)所得氧化铝载体,然后干燥、焙烧得到最终加氢处理催化剂;其中,浸渍过程采用等体积共浸渍;干燥温度为70℃~200℃,干燥时间为0.5h~20h;焙烧温度为300℃~600℃,焙烧时间为0.5h~20h。
2.根据权利要求1所述的浸渍法制备加氢处理催化剂的方法,其特征在于:步骤2)中,所述氧化铝载体以大孔拟薄水铝石为原料,加入助挤剂、助剂与胶溶剂,经混捏、碾压、成型、干燥、焙烧步骤后制得。
3.根据权利要求2所述的浸渍法制备加氢处理催化剂的方法,其特征在于:所述助挤剂为田菁粉、多元羧酸助挤剂或田菁粉与多元羧酸复合助挤剂。
4.根据权利要求2所述的浸渍法制备加氢处理催化剂的方法,其特征在于:所述助剂为磷、氟、硼、锆、硅各元素的化合物中的一种或几种,所述助剂的引入量以氧化物计为成型载体总质量的5.5%以下。
5.根据权利要求2所述的浸渍法制备加氢处理催化剂的方法,其特征在于:所述胶溶剂为无机酸和/或有机酸,所述无机酸为硝酸或盐酸;所述有机酸为甲酸、乙酸、柠檬酸、三氯乙酸或丙二酸中一种或几种;所述胶溶剂的引入量为成型载体总质量的0.5%~10%。