CN105132091A - 一种锡线拉丝润滑剂组合物 - Google Patents

一种锡线拉丝润滑剂组合物 Download PDF

Info

Publication number
CN105132091A
CN105132091A CN201510428426.1A CN201510428426A CN105132091A CN 105132091 A CN105132091 A CN 105132091A CN 201510428426 A CN201510428426 A CN 201510428426A CN 105132091 A CN105132091 A CN 105132091A
Authority
CN
China
Prior art keywords
lubricant composition
agent
wire drawing
drawing lubricant
solder wire
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510428426.1A
Other languages
English (en)
Inventor
黄福川
邓富康
李康春
韦开焕
马骁飞
黄旖瑶
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi University
Original Assignee
Guangxi University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi University filed Critical Guangxi University
Priority to CN201510428426.1A priority Critical patent/CN105132091A/zh
Publication of CN105132091A publication Critical patent/CN105132091A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种锡线拉丝润滑剂组合物，采用22号全损耗系统用油为基础油，配合多种添加剂，包括：油性剂、极压剂、抗磨剂、抗氧剂、抗泡剂、金属减活剂、摩擦改进剂、粘附剂、防锈剂。本发明的润滑剂组合物能直接用于锡线拉丝的润滑过程当中，具有足够的油膜厚度，较强的扩散、渗透性，油膜强度大，抗磨性和粘温性好，极压性强、冷却和润滑性好，有较小的流动剪切应力，提高金属丝的表面光洁度和规格精度，并有一定的化学稳定性和适当的闪点及着火点，低粘度、低含硫、低芳烃。

Description

一种锡线拉丝润滑剂组合物
技术领域
本发明属于金属加工润滑剂领域，特别涉及一种润滑性优良的锡线拉丝润滑剂组合物。
背景技术
锡，金属元素，一种略带蓝色的白色光泽的低熔点金属元素，是银白色的软金属，比重为7.3，熔点只有232℃，放进煤球炉中便会熔成水银般的液体。锡很柔软，用小刀能切开它。锡的化学性质很稳定，在常温下不易被氧气氧化；因此，它经常保持银闪闪的光泽。锡无毒，可塑性强而延性却很差，不能拉成细丝。它可以有各种表面处理工艺，能制成多种款式的产品，锡仍然是现代工业不可缺少的关键稀有金属，号称“工业味精”，广泛应用于电子、信息、电器、化工、冶金、建材、机械、食品包装等行业。
拉拔润滑剂种类：液体、半固体、固体润滑剂。拉拔过程中，润滑剂能减少金属拉拔时的摩擦，它不仅能降低拉拔温度，而且还能减缓拉模和设备的损耗，提高拉拔速度和拉拔件表面质量。金属的拉拔是极为苛刻条件下使金属发生塑性变形，通常认为：存在流体摩擦，边界摩擦，干摩擦和半干摩擦等几种摩擦形式。
通常锡线拉丝的变形抗力随旋压变形量增加而增大，应选择有效的润滑剂和润滑方法，进行润滑、清洗、冷却、防腐蚀以及降低粘连着现象，减少锡丝表面因润滑和冷却不良而造成的损伤和斑痕。拉拔润滑剂的作用包括：润滑、冷却、清洗等作用。.
发明内容
本发明要解决的技术问题是提供一种具有足够的油膜厚度，较强的扩散、渗透性，油膜强度大，抗磨性和粘温性好，极压性强、冷却和润滑性好，有较小的流动剪切应力，提高金属丝的表面光洁度和规格精度，并有一定的化学稳定性和适当的闪点及着火点，低粘度、低含硫、低芳烃的锡线拉丝润滑剂组合物。
本发明采用如下技术方案解决上述技术问题：
一种锡线拉丝润滑剂组合物，采用22号全损耗系统用油为基础油，配合多种添加剂，其各组分及其质量百分数为：
组分 质量百分数含量
基础油 余量
油性剂 16％～18％
极压剂 3％～4％
抗磨剂 3％～4％
抗氧剂 0.8％～1.2％
抗泡剂 10ppm～50ppm
金属减活剂 0.5％～1％
摩擦改进剂 3％～4％
粘附剂 2％～4％
防锈剂 0.8％～1.2％
油性剂是工业猪油。
极压剂为酸性亚磷酸二丁酯T304。
抗磨剂是氨基硫代酯T323。
抗氧剂是质量比50％的2,6-二叔丁基对甲酚与50％的N-苯基-α-萘胺复合。
抗泡剂是二甲基硅油。
金属减活剂是噻重氮。
摩擦改进剂是烷基亚磷酸酯。
粘附剂是聚异丁烯T603D。
防锈剂是质量比50％的苯骈三氮唑与50％的羊毛酯复合。
本发明的显著优点在于：具有足够的油膜厚度，较强的扩散、渗透性，油膜强度大，抗磨性和粘温性好，极压性强、冷却和润滑性好，有较小的流动剪切应力，提高金属丝的表面光洁度和规格精度，并有一定的化学稳定性和适当的闪点及着火点，低粘度、低含硫、低芳烃。
具体实施方式
实施例1：
将各组分按下列质量百分比调和而成：
组分 质量百分数含量
22号全损耗系统用油 余量
工业猪油 16％
酸性亚磷酸二丁酯(T304) 3％
氨基硫代酯(T323) 3％
质量比50％的2,6-二叔丁基对甲酚与50％的N-苯基-α-萘胺复合 0.8％
二甲基硅油 10ppm
噻重氮 0.5％
烷基亚磷酸酯 3％
聚异丁烯(T603D) 2％
质量比50％的苯骈三氮唑与50％的羊毛酯复合 0.8％
以上各组分质量百分数含量的总和为100％。
实施例2：
将各组分按下列质量百分比调和而成：
组分 质量百分数含量
22号全损耗系统用油 余量
工业猪油 17％
酸性亚磷酸二丁酯(T304) 3.5％
氨基硫代酯(T323) 3.5％
质量比50％的2,6-二叔丁基对甲酚与50％的N-苯基-α-萘胺复合 1％
二甲基硅油 30ppm
噻重氮 0.7％
烷基亚磷酸酯 3.5％
聚异丁烯(T603D) 3％
质量比50％的苯骈三氮唑与50％的羊毛酯复合 1％
以上各组分质量百分数含量的总和为100％。
实施例3：
将各组分按下列质量百分比调和而成：
组分 质量百分数含量
22号全损耗系统用油 余量
工业猪油 18％
酸性亚磷酸二丁酯(T304) 4％
氨基硫代酯(T323) 4％
质量比50％的2,6-二叔丁基对甲酚与50％的N-苯基-α-萘胺复合 1.2％
二甲基硅油 50ppm
噻重氮 1％
烷基亚磷酸酯 4％
聚异丁烯(T603D) 4％
质量比50％的苯骈三氮唑与50％的羊毛酯复合 1.2％
以上各组分质量百分数含量的总和为100％。
实施例3产品的主要理化指标：

Claims (10)

1.一种锡线拉丝润滑剂组合物，其特征在于：采用22号全损耗系统用油为基础油，配合多种添加剂，其各组分及其质量百分数为：
基础油余量，
油性剂16％～18％，
极压剂3％～4％，
抗磨剂3％～4％，
抗氧剂0.8％～1.2％，
抗泡剂10ppm～50ppm，
金属减活剂0.5％～1％，
摩擦改进剂3％～4％，
粘附剂2％～4％，
防锈剂0.8％～1.2％。
2.如权利要求1所述的一种锡线拉丝润滑剂组合物，其特征在于，油性剂是工业猪油。
3.如权利要求1所述的一种锡线拉丝润滑剂组合物，其特征在于，极压剂为酸性亚磷酸二丁酯T304。
4.如权利要求1所述的一种锡线拉丝润滑剂组合物，其特征在于，抗磨剂是氨基硫代酯T323。
5.如权利要求1所述的一种锡线拉丝润滑剂组合物，其特征在于，抗氧剂是质量比50％的2,6-二叔丁基对甲酚与50％的N-苯基-α-萘胺复合。
6.如权利要求1所述的一种锡线拉丝润滑剂组合物，其特征在于，抗泡剂是二甲基硅油。
7.如权利要求1所述的一种锡线拉丝润滑剂组合物，其特征在于，金属减活剂是噻重氮。
8.如权利要求1所述的一种锡线拉丝润滑剂组合物，其特征在于，摩擦改进剂是烷基亚磷酸酯。
9.如权利要求1所述的一种锡线拉丝润滑剂组合物，其特征在于，粘附剂是聚异丁烯T603D。
10.如权利要求1所述的一种锡线拉丝润滑剂组合物，其特征在于，防锈剂是质量比50％的苯骈三氮唑与50％的羊毛酯复合。
CN201510428426.1A 2015-07-20 2015-07-20 一种锡线拉丝润滑剂组合物 Pending CN105132091A (zh)