CN1038661A - 聚乙烯组合物及其制品和它的泡沫制品的制造方法 - Google Patents

聚乙烯组合物及其制品和它的泡沫制品的制造方法 Download PDF

Info

Publication number
CN1038661A
CN1038661A CN89103319A CN89103319A CN1038661A CN 1038661 A CN1038661 A CN 1038661A CN 89103319 A CN89103319 A CN 89103319A CN 89103319 A CN89103319 A CN 89103319A CN 1038661 A CN1038661 A CN 1038661A
Authority
CN
China
Prior art keywords
polyethylene
composition
polyethylene composition
density
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN89103319A
Other languages
English (en)
Inventor
弗朗西斯卡斯·约翰内斯·约瑟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Stamicarbon BV
Original Assignee
Stamicarbon BV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Stamicarbon BV filed Critical Stamicarbon BV
Publication of CN1038661A publication Critical patent/CN1038661A/zh
Priority to CN 92108756 priority Critical patent/CN1025433C/zh
Pending legal-status Critical Current

Abstract

本发明涉及聚乙烯组合物及其制品，它包括20—98％(重量)的密度在915和940kg/m3之间、熔体流动指数在0.05和40dg/分之间的由高压自由基引发法制备的支化聚乙烯(a)和2—80％(重量)的密度在850和915kg/m3之间、熔体流动指数在0.05和25dg/分的、23℃下DSC结晶度不低于10％的由过渡金属催化剂法制备的基本上是线型的聚乙烯(b)。此聚乙烯组合物制成泡沫制品，具有高耐高温性能和柔顺性。

Description

本发明涉及聚乙烯组合物及其制品。本发明亦涉及由此聚乙烯组合物制造泡沫制品的方法。
低密度聚乙烯（LDPE）泡沫制品可以用早已熟知的技术制造。（参见Plastic Foams，Part 1，Kurtc.Frisch和James.H.Saunders编，第281-292页）。这样的聚乙烯的密度在915至940Kg/m3，是用一种或一些自由基引发剂引发的高压法生产出来的。从这种LDPE得到的泡沫制品具有可任意调节以适于广泛应用的优良性质，例如，根据需要，通过制成开孔的或闭孔的，大孔的或小孔的，密度和形状大幅度变化的泡孔的方法进行调节。
由于这些性质，泡沫LDPE制品可广泛地用，例如用作绝缘材料;例如，开孔泡沫制品可作为隔音材料，闭孔泡沫制品可作为隔热材料。再者，由于它有良好的能量吸收的性质和在一般情况下的高抗化学物品的性质，LDPE泡沫制品可适用于作为易碎物品或精密物品的包装材料。
不同的应用对这些泡沫制品有不同的要求，例如柔软度、柔顺性、冷脆性、抗环境开裂性（ESCR）等等。已经知道，如果这些泡沫制品是由较低密度的LDPE和/或递增量掺入的极性共聚单体如醋酸乙烯酯、丙烯酸酯、甲基丙烯酸酯、甲基丙烯酸甲酯等所制成的，则这些性质更加明显。当这些极性共聚物被使用时，与LDPE均聚物的情况相比，LDPE泡沫制品的上述性质可以在更大程度上进行调节以适应需要。
然而，极性共聚物泡沫制品的缺点是，虽然柔顺性随着共聚单体用量的增加而增加，但此泡沫制品的耐高温性却降低了。与LDPE均聚物的软化范围及熔化范围相比，极性共聚物的软化范围及熔化范围处于较低的温度范围内。这限制了柔性泡沫制品的应用范围。再者，当它们转化为泡沫制品的过程中，极性共聚物似乎出现较大的粘附的问题。
本发明的目的在于获得一种聚乙烯组合物，当它制成泡沫制品时，具有高的耐高温性及高的柔顺性。
本发明目的是这样达到的，即制备一种含20-98%（重量）的支化聚乙烯（a）和2-80%（重量）的基本上是线型的聚乙烯（b）的聚乙烯组合物。支化聚乙烯（a）的密度在915至940Kg/m3，熔体流动指数在0.05至40dg/分，它是用高压自由基引发法制备的;线型聚乙烯（b）的密度在850至915Kg/m3，其熔体流动指数为0.05至25dg/分。在23℃时的样品DSC测得的结晶度至少为10%，它是用过渡金属催化剂法制得的。支化聚乙烯（a）的最高DSC结晶温度和线型聚乙烯（b）的最高DSC结晶温度之差至多为10℃，此混合物的弹性模量最高为280N/mm2。
已经发现，当熔融物质呈现高的熔体拉伸力和高的最大熔体拉伸比时，具有优良性能的LDPE泡沫制品便可以得到。用此方法，可以避免当用物理起泡剂发泡时在由熔融泡沫体向结晶泡沫体转化的过程中泡孔的塌扁，或避免当用化学起泡剂发泡膨胀时泡孔的毁坏。为此，熔体拉伸力应至少为10cN，最好至少为15cN，熔体最大拉伸比应至少为30，最好至少为40。
作为未发泡起始原料刚性的量度的E-模量（弹性模量），对LDPE均聚物来说，它的值往往高于那些加工为泡沫制品后仍希望有良好柔软性的材料的数值。为了具有良好的柔软性，E-模量不能高于280N/mm2，最好不高于250N/mm2，尤其不高于230N/mm2。而密度为915Kg/m3的LDPE，其E-模量约为160N/mm2，并随密度之增加而增加。但是，在许多应用中，从这种材料制成的泡沫制品的耐高温性能太低（低于100℃）。一种由密度为925Kg/m3的LDPE制成的泡沫制品可耐100℃以上的温度，但这种LDPE的E-模量约为350N/mm2。
令人惊讶地发现，本发明的聚乙烯组合物的熔体拉伸力至少为10cN，尤其至少为15cN，其熔体拉伸比至少为30，尤其至少为40，并发现当它们被加工为泡沫制品时，可得到具有良好耐高温性能（高于100℃）的软而柔顺的制品。从GB-A-1，552，435和EP-A-0016348可知，密度为915至935Kg/m3的支化聚乙烯和密度为918至940Kg/m3的线型聚乙烯的混合物是已知的。这些混合物都有已知LDPE的优良性能，但它们都太缺乏柔顺性和柔软度。
本发明组合物中的聚乙烯（a）最好是密度为918至928Kg/m3，尤其是922至928Kg/cm3的聚乙烯均聚物（LDPE），其熔体流动指数最好是为0.1至30dg/分，尤其是低于10dg/分。它是按通常方式在一种或多种自由基引发剂存在下用高压法生产的。这方法所得的聚乙烯具有长侧链，因而有时亦称之为支化聚乙烯。
本发明的聚乙烯（a）亦可以是乙烯和醋酸乙烯、丙烯酸等的共聚物，掺入极性共聚单体的百分数最多为2%（摩尔）;亦可以是LDPE和极性共聚物的混合物（在此情况下，掺入共聚物的百分数可以高于2%（摩尔），例如8%（摩尔）或更高）。在此情况下，推荐LDPE均聚物的重量百分数为50。
本发明组合物中的聚乙烯（b）是线型聚乙烯，其密度最好为880至912Kg/m3，尤其是低于910Kg/m3，其熔体流动指数最好为0.1至20dg/分，尤以低于15dg/分为宜。它是乙烯和一种或多种具有3至18个碳原子的烯烃-1（相对于乙烯的量为10至50%（重量））的共聚物，其中可能有少量的双烯。与4至12个碳原子的烯烃，尤其是和丁烯-1、己烯-1、4-甲基戊烯-1和辛烯-1的共聚物是较好的。它主要含短的侧链，与LDPE相比，其长侧链要少得多，这就是它之所以被称之谓线型聚乙烯之缘故。用示差扫描量热计法测定，其在23℃时的结晶度大于10%，较好的是大于15%，尤以大于20%为好。它是用过渡金属催化剂，最好是所谓Ziegler-Natta催化剂，尤其是那些至少包括钛化合物和铝化合物、镁化合物和/或钒化合物和/或可能有氯化物在其中的催化剂的方法生产出来的。这方法本身是已知的，它可以在高压或低压、在高温或低温下进行。具体优选的条件可以是：在分散剂存在下，所用压力不超过200巴，尤以不超过100巴为宜，所用温度高于110℃，最好是高于135℃。
聚乙烯成分（a）和（b）的量略依赖于其用途。一般，较好的是30-90%（重量）的聚乙烯（a）和10-70%（重量）的聚乙烯（b），最好为40-85%（重量）的聚乙烯（a）和15-60%（重量）的聚乙烯（b），而50-85%（重量）的聚乙烯（a）和15-50%（重量）的聚乙烯（b）则更好。
可用一般的方法进行混合，例如，对粒状聚乙烯用桶混机，对粉末聚乙烯用汉歇尔混合机，或用班伯里混炼机或格塑混合机。聚乙烯（a）和（b）亦可以以适当配比很好地直接供料至通常用以生产聚乙烯制品的挤塑装置中而不须预先混合，在通常的时间及温度范围内，本发明对混合方式并无严格限制。
本发明的聚乙烯组合物可以用许多已知的方法转变为制品，例如用注射、滚塑、吹塑、型材挤塑、薄塑制造等。但是，本聚乙烯组合物特别适于做成泡沫制品。这可采取不同的方式，一般将其分为用化学起泡剂法和物理起泡剂法。
在化学起泡中，加入某种物质于聚乙烯混合物中作为起泡剂，起泡剂在本领域中普通技术人员所熟知的一定条件下（例如升高温度）分解为气态组分并产生压力，这样，就使得聚乙烯起泡。
在物理起泡中，聚乙烯组合物处在增压增温下（一般是在挤塑机中）和一种或几种在常压及室温下是气态的起泡剂混合，然后置于较低压力和温度下，由于混合物膨胀的结果，聚乙烯开始发泡。在这方法中，聚乙烯亦冷却及结晶。在物理起泡中，常用的是由卤代烃（或它们的混合物），或气态烷烃（或它们的混合物），或此两者的混合物。通常的用量为，例如，每100份聚乙烯用0.01-0.6克分子的起泡剂。这样，泡沫制品的密度可以在5至400Kg/m3范围内变动，这取决于所用的条件（起泡剂的类型、晶种剂的类型、温度、压力、添加剂等等）。本领域中普通技术人员熟知如何按照需要来改变这些条件。
在泡沫制品的生产中，能否获得良好质量的泡沫制品在很重要的程度上决定于聚乙烯的结晶行为。聚合物的结晶行为可以用示差扫描量热计法（DSC）来测定。用此法测定的结晶化曲线显示出一个或多个峰，这决定于被测物质的分子结构。这些峰的顶部对应的温度称为结晶化温度。已经发现支化聚乙烯（a）的最高DSC结晶化温度和线型聚乙烯（b）的最高结晶化温度之差不能超过10℃，否则生成的混合物将跨越过宽的结晶化范围结晶，结果产生所不希望的分层现象。这个温差以不超过8℃较好，不超过7℃更好。本发明组合物的DSC结晶化曲线在125℃与95℃之间最多只应有一个峰，这个峰可能是肩峰，或可能是一个宽峰（其对应于基线处超过10℃）或窄峰（其在基线上不足10℃）。无肩的峰是较理想的，尤以窄峰更佳。
本发明的聚乙烯组合物尤其适于制造泡沫制品。可推荐使用物理起泡剂，例如戊烷、氯氟代烃、二氧化碳、氮气以及这些物质的混合物等。应用化学起泡剂，如偶氮二羰酰胺或偶氮二甲酰胺之类的物质也是可以的。
如果使用如有机过氧化物、氧、多官能团烯丙基和/或乙烯基单体、带叠氮基或带乙烯基官能团的硅烷等交联剂时，本发明聚乙烯组合物的耐高温性能可大大地增加。根据需要，交联可在大小不同程度上发生，这可借改变交联剂的量来达到，例如其量可在组合物总量的0.005至5.0%（重量）之间加以改变的方法达到。这样，其良好的柔软性可以保持。
此外，聚乙烯组合物还可以包括其他物质，譬如晶种剂、泡沫稳定剂、热稳定剂、紫外光稳定剂、抗静电剂、润滑剂、抗氧剂、防粘剂、填料、颜料、加工助剂等。
对上述的物理发泡技术，润滑剂（如0.05-1.5%（重量）的油酸酰胺）是需要的。在化学发泡工艺中，通常亦要有所谓催发剂，以保证交联剂和起泡剂的同步分解。一般，这是一种金属氧化物，特别是氧化锌。
本发明的泡沫制品可以加工成任何所需要的形状，例如型料（如棒体或管子）、颗粒、薄膜、在其他材料上的膜层等等。将已发泡的颗粒加热粘结或熔合的办法亦可制得本发明的泡沫制品。这个技术本身是已知的。
现在，参考一些实例详细说明本发明，但是本发明并不受这些实例所局限。
各种聚乙烯混合物的组成在各实例中指明。
所有共聚物都是与辛烯-1的共聚物，在23℃时的DSC结晶度大于10%。
图1表示实例Ⅰ中组合物的DSC结晶化曲线，图2表示实例Ⅱ的，图3表示实例Ⅲ的，图4表示实例Ⅳ的，图5表示实例Ⅴ的，图6表示实例Ⅵ的，图7表示实例Ⅶ的，图8表示实例Ⅷ的，图9表示实例Ⅸ的，图10表示实例Ⅹ的DSC结晶化曲线;图11表示对比例1的，图12表示对比例2的，图13表示对比例3的、图14表示对比例4的，图15表示对比例5的，图16表示对比例6的DSC结晶化曲线。
密度（d）是按照ISO        1183（D）方法测量的，熔体流动指数（MEI）是按照ISO        1133（A/4）方法测量的。
熔体拉伸力（MDF）和最大熔体拉伸比（MDR）是这样测定的：通过高的8.0mm和直径为2.0mm的模口挤出一定量的聚乙烯，挤出温度为130℃，产生0.25g/分的挤出物，同时拉伸此挤出物成细丝至其断裂。断裂时拉伸所需的力及拉伸比即分别为熔体拉伸力（牛顿）和最大熔体拉伸比。
按DIN 53457（N/mm2）测定E-模量。
对DSC的测量，其测量装置包括Perkin-Elmer DSC-2和Tektronix 4052计算机、Hewlett-Packard 3495A多路扫描器（scanner-multiplexer）和HP-3455A数字电压表（5 1/2 -5 1/2 位数）等在线联用。
测量是按照V.B.F.Mathot等的“连续”测量法（参见J.Thermal        Anal.，Vol28，349-358（1983））进行的，并按相对大小复制。
测量是在氮气下进行的;加热至180℃并停留5分钟之后，在扫描速度为5℃/分下冷却样品至45℃。样品用Mettler        Me        22/36电子微量天平称量5mg称准至1微克。每隔0.2℃，记录温度及相应于该温度的测量结果。
在下列各表中所列的结晶化温度为用这种DSC方法所测定。
实例Ⅰ
聚乙烯（a）：d＝923.5kg/m3;MFI＝0.8dg/分
聚乙烯（b）：d＝911kg/m3;MFI＝2.5dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        34        38        254        98.5        窄
75/25        28        55        227        103        宽
0/100        4        ＞757        177        107.5        窄
实例Ⅱ
聚乙烯（a）：d＝923.5kg/m3;MFI＝0.8dg/分
聚乙烯（b）：d＝906kg/m3;MFI＝2.5dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        34        38        254        98.5        窄
75/25        29        53        221        102        窄
0/100        2        ＞757        133        105.5        窄
实例Ⅲ
聚乙烯 a）：d＝923.5kg/m3;MFI＝0.8dg/分
聚乙烯 b）：d＝902kg/m3;MFI＝2.9dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        34        38        254        98.5        窄
75/25        27        54        215        102        窄
0/100        2        ＞757        110        105.5        窄
实例Ⅳ
聚乙烯 a）：d＝926kg/m3;MFI＝2.0dg/分
聚乙烯 b）：d＝911kg/m3;MFI＝2.5dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        36        65        302        101        窄
75/25        28        86        264        103.5        宽
0/100        4        ＞757        177        107.5        窄
实例Ⅴ
聚乙烯 a）：d＝926kg/m3;MFI＝2.0dg/分
聚乙烯 b）：d＝902kg/m3;MFI＝2.9dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        36        65        302        101        窄
85/15        22.5        67        259        101.5        窄
75/25        21.5        98        242        102.5        窄
0/100        2        ＞757        110        105.5        窄
实例Ⅵ
聚乙烯 a）：d＝926kg/m3;MFI＝1.6dg/分
聚乙烯 b）：d＝902kg/m3;MFI＝2.9dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        28        78        295        100        窄
75/25        22        105        243        102        窄
0/100        2        ＞757        110        105.5        窄
实例Ⅶ
聚乙烯 a）：d＝926kg/m3;MFI＝1.4dg/分
聚乙烯 b）：d＝902kg/m3;MFI＝2.9dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        38        72        304        100        窄
75/25        23        97        248        102        窄
0/100        2        ＞757        110        105.5        窄
实例Ⅷ
聚乙烯 a）：d＝926kg/m3;MFI＝0.3dg/分
聚乙烯 b）：d＝902kg/m3;MFI＝2.9dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        25        29        308        100        窄
75/25        25        101        245        102        窄
0/100        2        ＞757        110        105.5        窄
实例Ⅸ
聚乙烯 a）：d＝927kg/m3;MFI＝1.3dg/分
聚乙烯 b）：d＝902kg/m3;MFI＝2.9dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        21        40        320        102        窄
75/25        22？        90        269        104        窄
70/30        27.4        71        263        104.5        窄
0/100        2        ＞757        110        105.5        窄
实例Ⅹ
聚乙烯 a）：d＝927kg/m3;MFI＝1.5dg/分
聚乙烯 b）：d＝902kg/m3;MFI＝2.9dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        17.9        64        323        101.5        窄
75/25        20.5        110        263        103        宽
70/30        23.1        100        253        103.5        宽
0/100        2        ＞757        110        105.5        窄
对比例1
聚乙烯 a）：d＝920kg/m3;MFI＝1.9dg/分
聚乙烯 b）：d＝921kg/m3;MFI＝4.1dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        29        43        195        95        窄
75/25        26        66        228        97，105        -
0/100        5        ＞757        318        107.5        窄
对比例2
聚乙烯 a）：d＝920kg/m3;MFI＝1.9dg/分
聚乙烯 b）：d＝911kg/m3;MFI＝5.5dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        29        43        195        95        窄
85/15        24        58        193        96.5，103        肩峰
75/25        22        76        190        96，105        -
50/50        17.5        147        186        95，107        -
0/100        4        ＞757        177        108        窄
对比例3
聚乙烯 a）：d＝920kg/m3;MFI＝1.9dg/分
聚乙烯 b）：d＝919kg/m3;MFI＝4.6dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        29        43        195        95        窄
75/25        25        80        215        95，105        -
0/100        4        ＞757        283        107.5        窄
对比例4
聚乙烯 a）：d＝922kg/m3;MFI＝0.8dg/分
聚乙烯 b）：d＝911kg/m3;MFI＝5.5dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        31        30        236        97        窄
90/10        24.5        35        218        98        宽
85/15        27        28        215        99        宽
75/25        26        45        211        97.5，104.5        -
0/100        5        ＞757        177        108        窄
对比例5
聚乙烯 a）：d＝931kg/m3;MFI＝1.7dg/分
聚乙烯 b）：d＝921kg/m3;MFI＝5.5dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        39        85        428        104.5        窄
85/15        20        82        402        107        窄
75/25        17        97        392        107        窄
50/50        14        198        361        108        窄
0/100        5        ＞757        318        107.5        窄
对比例6
聚乙烯 a）：d＝931kg/m3;MFI＝1.7dg/分
聚乙烯 b）：d＝911kg/m3;MFI＝5.5dg/分
a/b        MDF        MDR        弹性模量        DSC结晶化        峰形
cN x N/mm2温度，℃
100/0        39        85        428        104.5        窄
75/25        17        135        346        106.5        窄
0/100        4        ＞757        177        108        窄
实例Ⅺ
用若干个上面各例中的聚乙烯组合物为原料，用通常用于挤塑泡沫体的挤塑机将其制成圆形泡沫型材。挤塑机头温度设定在高于聚乙烯组合物（最高的）结晶化温度以上3（Ω0.5）℃。
作为发泡剂，加入氟利昂12（二氯四氟乙烷）和氟利昂114（二氯氟甲烷）的50/50（m/m）混合物，其量为15份（重量）发泡剂对85份（重量）聚合物。将0.2%晶种剂加入到作为母料的聚合物（LDPE和20%（重量）的碳酸氢钠和柠檬酸）中，同时加入润滑剂（0.2%（重量）的油酸酰胺）。
这样得到的圆形泡沫成型材料采用手工弯曲和压缩法分别评定柔顺性和柔软度。
耐高温性是用将圆形型材在100℃保持6星期的方法来测定。6星期后，如果此型材变粘，则评为“-”号，如它不变粘，则评为“+”号。
这些结果列于下表。
实例及        泡沫物        泡沫物        闭孔        耐高
对比例        加工性能        密度        %        柔顺性        柔软度        温性
kg/m3
Ⅳ        100/o
Ⅴ        100/o        好        36        82        -        -        +
Ⅵ        100/o        好        37        83        -        -        +
1        100/o
2        100/o        好        36        77        +        +        -
3        100/o
5        100/o
6        100/o        好        38        84        -        -        +
Ⅲ        o/100
Ⅴ        o/100
Ⅵ        o/100
Ⅶ        o/100        塌扁
Ⅷ        o/100
Ⅸ        o/100
Ⅹ        o/100
1        o/100        塌扁
5        o/100
2        o/100
2        o/100        塌扁
6        o/100
Ⅵ        75/25        好        38        78        ++        ++        +
Ⅶ        75/25        好        34        80        ++++        ++++        +
Ⅸ        70/30        好        36        72        +++        ++++        +
Ⅹ        70/30        好        34        79        ++        ++        +
1        75/25        塌扁
4        75/25        塌扁
6        75/25        好        35        74        -        -        +

Claims (11)

1、一种聚乙烯组合物，此组合物包含20-98%(重量)支化聚乙烯(a)和2-80%(重量)基本上是线型的聚乙烯(b)；所说的聚乙烯(a)密度在915和940Kg/m3之间，而且熔体流动指数在0.05和40dg/分之间，是由高压自由基引发法制备的；所说的聚乙烯(b)密度在850和915kg/m3之间，而且熔体流动指数在0.05和25dg/分之间，23℃下的DSC结晶度至少为10%，是用过渡金属催化剂法制备出来的；其中支化聚乙烯(a)的最高结晶化温度和线型聚乙烯(b)的最高DSC结晶化温度之差不超过10℃，此混合物的弹性模量不高于280N/mm2。
2、根据权利要求1的聚乙烯组合物，其特征在于聚乙烯（a）的密度在918和928Kg/m3之间，聚乙烯（b）的密度在880和912Kg/m3之间。
3、根据权利要求1-2中任一项的聚乙烯组合物，其特征在于聚乙烯（a）的熔体流动指数在0.1和30dg/分之间，聚乙烯（b）的熔体流动指数在0.1和20dg/分之间。
4、根据权利要求1-3中任一项的聚乙烯组合物，其特征在于此组合物包含30-90%（重量）的聚乙烯（a）和10-70%（重量）的聚乙烯（b）。
5、根据权利要求1-4中任一项的聚乙烯组合物，其特征在于此聚乙烯组合物的DSC结晶化曲线上在125至95℃之间至多只出现一个结晶化峰。
6、用权利要求1-5中任一项中的聚乙烯组合物制成的制品。
7、泡沫制品的制造方法，其中包括将聚乙烯组合物和至少一种或多种起泡剂在增压增温下混合，然后用挤塑机将此组合物经由挤塑机孔挤至一个较低压力和温度的区域，其特征在于所说的聚乙烯组合物是权利要求1-6中任一项的组合物。
8、根据权利要求7的方法，其特征在于其中所说的起泡剂是物理起泡剂。
9、根据权利要求7-8中任一项的方法，其特征在于所说的聚乙烯组合物另外还混和有一种或多种交联剂。
10、根据权利要求7-9中任一项的方法，其特征在于所说的聚乙烯组合物另外还混和有一种或多种润滑剂。
11、用权利要求1-6中任一项的聚乙烯组合物制成的泡沫制品。
CN89103319A 1988-05-19 1989-05-18 聚乙烯组合物及其制品和它的泡沫制品的制造方法 Pending CN1038661A (zh)