CN103525358A - 一种含梯形聚倍半硅氧烷的透明硅橡胶的制备方法与应用 - Google Patents
一种含梯形聚倍半硅氧烷的透明硅橡胶的制备方法与应用 Download PDFInfo
- Publication number
- CN103525358A CN103525358A CN201310285809.9A CN201310285809A CN103525358A CN 103525358 A CN103525358 A CN 103525358A CN 201310285809 A CN201310285809 A CN 201310285809A CN 103525358 A CN103525358 A CN 103525358A
- Authority
- CN
- China
- Prior art keywords
- polysiloxane
- ladder
- silicon rubber
- chain link
- hydroxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (8)