CN102672061B - 冲头加工工艺 - Google Patents

冲头加工工艺 Download PDF

Info

Publication number
CN102672061B
CN102672061B CN201210132929.0A CN201210132929A CN102672061B CN 102672061 B CN102672061 B CN 102672061B CN 201210132929 A CN201210132929 A CN 201210132929A CN 102672061 B CN102672061 B CN 102672061B
Authority
CN
China
Prior art keywords
drift
blank
grinding
finish turning
processing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210132929.0A
Other languages
English (en)
Other versions
CN102672061A (zh
Inventor
何沛均
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHONGQING JIANGJIN HONGSHENG MACHINERY MANUFACTURING Co Ltd
Original Assignee
CHONGQING JIANGJIN HONGSHENG MACHINERY MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHONGQING JIANGJIN HONGSHENG MACHINERY MANUFACTURING Co Ltd filed Critical CHONGQING JIANGJIN HONGSHENG MACHINERY MANUFACTURING Co Ltd
Priority to CN201210132929.0A priority Critical patent/CN102672061B/zh
Publication of CN102672061A publication Critical patent/CN102672061A/zh
Application granted granted Critical
Publication of CN102672061B publication Critical patent/CN102672061B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种冲头加工工艺，包括制坯、半精加工、淬火、精加工和终检，所述制坯包括毛坯制作和毛坯粗加工；所述半精加工包括半精车和铣槽；所述精加工包括精车、精磨、线切割、磨冲头顶端、修磨槽边和研磨抛光，本发明的冲头加工工艺，在热处理后的精加工工艺中先进行一道精车加工至表面粗糙度达到Ra1.6，再进行精磨加工及研磨抛光至成品，加工出冲头表面粗糙度可达Ra0.2，以满足其使用要求。

Description

冲头加工工艺
技术领域
本发明涉及一种冲头加工工艺，尤其涉及表面质量要求较高的翻孔冲头的加工工艺。
背景技术
翻孔冲头是安装在冲压模具上的金属零件，用于与材料的直接接触使材料发生形变，对孔结构进行翻边，可用于攻丝或连接自攻螺钉，翻边冲头一般采用具有较好淬透性、淬火回火的硬度、耐磨性和强度的合金工具钢制作，冲头表面粗糙度要求至少达到Ra0.2，传统加工工艺达不到粗糙度要求。
因此，需要一种用于加工翻孔冲头的加工工艺，使加工出冲头表面粗糙度可达Ra0.2，以满足其使用要求。
发明内容
有鉴于此，本发明的目的是提供一种冲头加工工艺，加工出冲头表面粗糙度可达Ra0.2，可满足其使用要求。
本发明的冲头加工工艺，包括制坯、半精加工、淬火、精加工和终检，所述制坯包括毛坯制作和毛坯粗加工；所述半精加工包括半精车和铣槽；所述精加工包括精车、精磨、线切割、磨冲头顶端、修磨槽边和研磨抛光；
具体包括以下步骤：
a.制坯：
a1.毛坯制作，采用锻造或铸造的方式加工毛坯，后对毛坯进行正火处理；
a2.毛坯粗加工，粗车削加工端面、外圆、锥面、台阶面和顶针孔，冲头顶端预留15～20mm余量用于加工顶针孔，冲头尾端端面、外圆、锥面、台阶面单边预留1～3mm加工余量，粗糙度达到Ra6.3；
b.半精加工：
b1.半精车，半精车削加工端面、外圆、锥面、台阶面和顶针孔，台阶面处导圆，单边预留0.2～0.5mm加工余量，粗糙度达到Ra3.2；
b2.铣槽，铣削加工废料槽，粗糙度达到Ra1.6；
c.淬火：采用盐浴淬火，淬火硬度达HRC67～69；
d.精加工：
d1.精车，精车加工去除冲头尾端端面、外圆和锥面加工余量，粗糙度达到Ra1.6；
d2.精磨，精磨加工端面、外圆和锥面，粗糙度达到Ra0.2；
d3.线切割，采用线切割加工去除冲头顶端工艺位并预留0.3～0.5mm加工余量；
d4.磨冲头顶端，磨削加工去除冲头顶端加工余量，锐边倒圆，粗糙度达到Ra0.8；
d5.修磨槽边，修磨废料槽边为R0.5圆角；
d6.研磨抛光，冲头顶端研磨抛光至粗糙度达到Ra0.2；
e.终检检测全部尺寸并填写尺寸检测报告，检测完后产品入库。
进一步，所述步骤a中毛坯制作采用锻造的方式加工毛坯，正火后硬度160～190HB；毛坯粗加工后对其进行超声波探伤检测，检测方法为在毛坯表面涂机油，然后用超声波检测仪对毛坯进行扫查，扫查速度小于150mm/s。
进一步，所述步骤d中，修磨槽边后进行磁粉探伤检测，包括预清洗、施加渗透剂、去除多余渗透剂、零件的干燥、显像、观察和复检后处理。
本发明的有益效果是：本发明的冲头加工工艺，在热处理后的精加工工艺中先进行一道精车加工至表面粗糙度达到Ra1.6，再进行精磨加工及研磨抛光至成品，加工出冲头表面粗糙度可达Ra0.2，以满足其使用要求。
附图说明
下面结合附图和实施例对本发明作进一步描述：
图1为冲头结构示意图。
具体实施方式
图1为冲头结构示意图，本实施例的冲头加工工艺，包括制坯、半精加工、淬火、精加工和终检，所述制坯包括毛坯制作和毛坯粗加工；所述半精加工包括半精车和铣槽；所述精加工包括精车、精磨、线切割、磨冲头顶端、修磨槽边和研磨抛光；
具体包括以下步骤：
a.制坯：
a1.毛坯制作，采用锻造或铸造的方式加工毛坯，后对毛坯进行正火处理；
a2.毛坯粗加工，粗车削加工端面、外圆、锥面3、台阶面4和顶针孔，冲头顶端1预留15～20mm余量用于加工顶针孔，冲头尾端2端面、外圆、锥面3、台阶面4单边预留1～3mm加工余量，粗糙度达到Ra6.3；
b.半精加工：
b1.半精车，半精车削加工端面、外圆、锥面3、台阶面4和顶针孔，台阶面4处导圆，单边预留0.2～0.5mm加工余量，粗糙度达到Ra3.2；
b2.铣槽，铣削加工废料槽5，粗糙度达到Ra1.6；
c.淬火：采用盐浴淬火，淬火硬度达HRC67～69；
d.精加工：
d1.精车，精车加工去除冲头尾端2端面、外圆和锥面3加工余量，粗糙度达到Ra1.6；
d2.精磨，精磨加工端面、外圆和锥面3，粗糙度达到Ra0.2；
d3.线切割，采用线切割加工去除冲头顶端1工艺位并预留0.3～0.5mm加工余量；
d4.磨冲头顶端，磨削加工去除冲头顶端1加工余量，锐边倒圆，粗糙度达到Ra0.8；
d5.修磨槽边，修磨废料槽5边为R0.5圆角；
d6.研磨抛光，冲头顶端研磨抛光至粗糙度达到Ra0.2；
e.终检检测全部尺寸并填写尺寸检测报告，检测完后产品入库。
本实施例中，所述步骤a中毛坯制作采用锻造的方式加工毛坯，正火后硬度160～190HB；毛坯粗加工后对其进行超声波探伤检测，检测方法为在毛坯表面涂机油，然后用超声波检测仪对毛坯进行扫查，扫查速度小于150mm/s，可保证坯件质量，避免内部组织缺陷。
本实施例中，所述步骤d中，修磨槽边后进行磁粉探伤检测，包括预清洗、施加渗透剂、去除多余渗透剂、零件的干燥、显像、观察和复检后处理。
最后说明的是，以上实施例仅用以说明本发明的技术方案而非限制，尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的宗旨和范围，其均应涵盖在本发明的权利要求范围当中。

Claims (3)

1.一种冲头加工工艺，其特征在于：包括制坯、半精加工、淬火、精加工和终检，所述制坯包括毛坯制作和毛坯粗加工；所述半精加工包括半精车和铣槽；所述精加工包括精车、精磨、线切割、磨冲头顶端、修磨槽边和研磨抛光；
具体包括以下步骤：
a.制坯：
a1.毛坯制作，采用锻造或铸造的方式加工毛坯，后对毛坯进行正火处理；
a2.毛坯粗加工，粗车削加工端面、外圆、锥面、台阶面和顶针孔，冲头顶端预留15～20mm余量用于加工顶针孔，冲头尾端端面、外圆、锥面、台阶面单边预留1～3mm加工余量，粗糙度达到Ra6.3；
b.半精加工：
b1.半精车，半精车削加工端面、外圆、锥面、台阶面和顶针孔，台阶面处导圆，单边预留0.2～0.5mm加工余量，粗糙度达到Ra3.2；
b2.铣槽，铣削加工废料槽，粗糙度达到Ra1.6；
c.淬火：采用盐浴淬火，淬火硬度达HRC67～69；
d.精加工：
d1.精车，精车加工去除冲头尾端端面、外圆和锥面加工余量，粗糙度达到Ra1.6；
d2.精磨，精磨加工冲头尾端端面、外圆和锥面，粗糙度达到Ra0.2；
d3.线切割，采用线切割加工去除冲头顶端工艺位并预留0.3～0.5mm加工余量；
d4.磨冲头顶端，磨削加工去除冲头顶端加工余量，锐边倒圆，粗糙度达到Ra0.8；
d5.修磨槽边，修磨废料槽边为R0.5圆角；
d6.研磨抛光，冲头顶端研磨抛光至粗糙度达到Ra0.2；
e.终检检测全部尺寸并填写尺寸检测报告，检测完后产品入库。
2.根据权利要求1所述的冲头加工工艺，其特征在于：所述步骤a中毛坯制作采用锻造的方式加工毛坯，正火后硬度160～190HB；毛坯粗加工后对其进行超声波探伤检测，检测方法为在毛坯表面涂机油，然后用超声波检测仪对毛坯进行扫查，扫查速度小于150mm/s。
3.根据权利要求1所述的冲头加工工艺，其特征在于：所述步骤d中，修磨槽边后进行磁粉探伤检测，包括预清洗、施加渗透剂、去除多余渗透剂、零件的干燥、显像、观察和复检后处理。
CN201210132929.0A 2012-04-28 2012-04-28 冲头加工工艺 Active CN102672061B (zh)