CN102513157A - 一种基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物及其合成方法和应用 - Google Patents

一种基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物及其合成方法和应用 Download PDF

Info

Publication number
CN102513157A
CN102513157A CN2011104379530A CN201110437953A CN102513157A CN 102513157 A CN102513157 A CN 102513157A CN 2011104379530 A CN2011104379530 A CN 2011104379530A CN 201110437953 A CN201110437953 A CN 201110437953A CN 102513157 A CN102513157 A CN 102513157A
Authority
CN
China
Prior art keywords
pyridine
keggin type
simo
copper complex
room temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011104379530A
Other languages
English (en)
Other versions
CN102513157B (zh
Inventor
王秀丽
刘国成
徐闯
林宏艳
张巨文
田爱香
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bohai University
Original Assignee
Bohai University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bohai University filed Critical Bohai University
Priority to CN 201110437953 priority Critical patent/CN102513157B/zh
Publication of CN102513157A publication Critical patent/CN102513157A/zh
Application granted granted Critical
Publication of CN102513157B publication Critical patent/CN102513157B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物及其合成方法和应用，其分子式是下式中一种：[Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O；[Cu2(L2)3(H2O)6(SiMo12O40)]·9H2O；[Cu2(L2)3(H2O)6(SiW12O40)]·6H2O；[Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O；[Cu2(L3)3(H2O)6(SiW12O40)]·6H2O；其中，L1为N,N′-二(3-吡啶甲酰胺基)-1,2-乙烷；L2为N,N′-二(3-吡啶甲酰胺基)-1,4-丁烷；L3为N,N′-二(3-吡啶甲酰胺基)-1,6-己烷。将Cu(NO3)·3H2O、Keggin型的多酸、双吡啶双酰胺有机配体加入去离子水，在室温下搅拌，调pH值后，倒入高压反应釜中升温并在水热条件下保温，降温到室温得到块状蓝绿色晶体，用去离子水和乙醇交替清洗，室温下自然晾干，制得双吡啶双酰胺有机配体和Keggin型多酸的铜配合物。该配合物合成方法简单、易结晶、合成产率高，对水溶性污染物亲和能力强、催化降解效果好，可作为光催化材料应用。

Description

一种基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物及其合成方法和应用
技术领域
本发明属于光催化材料及合成方法，特别涉及一种基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物及其合成方法和应用。
背景技术
多酸基无机-有机功能配合物是一种无机功能材料，具有结构多样、催化性能良好、应用范围广的特点。然而，这类配合物的合成受到有机配体的配位点数量、配位能力、配齿间隔的制约，合成这类多酸基无机-有机功能配合物较困难。此外，目前用来合成多酸基有机-无机配合物的含氮配体普遍采用烃类结构单元连接的咪唑、吡啶等衍生物，该类衍生物具有憎水性，使用该类衍生物在合成多酸有机-无机配合物时相对结晶困难，导致多酸基无机-有机功能配合物的合成产率只有40%左右，合成产率较低。同时，基于烃类结构单元的咪唑、吡啶等衍生物的多酸基无机-有机功能配合物对水溶性的有机污染物的亲和能力较差，对水溶性有机污染物的催化降解效果较差。
发明内容
本发明所要解决的技术问题是提供一种合成方法简单、易结晶、合成产率高，对水溶性污染物亲和能力强、催化降解效果好的基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物及其合成方法和应用。
本发明的技术解决方案是：
一种基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物，其特殊之处是化合物的分子式为下式中的一种：
[Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O；
[Cu2(L2)3(H2O)6(SiMo12O40)]·9H2O；
[Cu2(L2)3(H2O)6(SiW12O40)]·6H2O；
[Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O；
[Cu2(L3)3(H2O)6(SiW12O40)]·6H2O；
其中，L1为 N,N′-二(3-吡啶甲酰胺基)-1,2-乙烷；L2为 N,N′-二(3-吡啶甲酰胺基)-1,4-丁烷；L3为N,N′-二(3-吡啶甲酰胺基)-1,6-己烷。
一种基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物的合成方法，其具体步骤是：
将Cu(NO3)·3H2O、Keggin型的多酸、双吡啶双酰胺有机配体加入去离子水，在室温下搅拌20min～40min形成悬浮混合物，其中双吡啶双酰胺有机配体与Keggin型多酸的摩尔比为1.0:1.1～1.0:1.5，双吡啶双酰胺有机配体与Cu(NO3)·3H2O的摩尔比为1.0:4.0~1.0:6.0，所述的Keggin型多酸是H4SiMo12O40·29H2O或H4SiW12O40·26H2O，所述的双吡啶双酰胺有机配体是N,N′-二(3-吡啶甲酰胺基)-1,2-乙烷或N,N′-二(3-吡啶甲酰胺基)-1,4-丁烷或N,N′-二(3-吡啶甲酰胺基)-1,6-己烷；用0.5mol/L～2.0mol/L的NaOH溶液调pH=4.0～5.5，倒入高压反应釜中升温至110℃～130℃，水热条件下保温3天～5天，降温到室温得到块状蓝绿色晶体，用去离子水和乙醇交替清洗2次～4次，室温下自然晾干，得双吡啶双酰胺有机配体和Keggin型多酸的铜配合物。
上述的基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物的合成方法，升温时升温速率为 10℃/小时～20℃/小时，降温时降温速率为5℃/小时～10℃/小时。
上述的基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物的合成方法，所述的去离子水的加入量为高压反应釜容积的30%～50%。
上述的基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物作为光催化材料的应用。
本发明以Keggin型多酸阴离子作为非配位模板剂，双吡啶双酰胺和铜构成多孔性一维或二维无机-有机配合物骨架。其中：[Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O的无机-有机配合物骨架为一维平行排列结构；[Cu2(L2)3(H2O)6(SiMo12O40)] ·9H2O、[Cu2(L2)3(H2O)6(SiW12O40)]·6H2O是同构化合物，它们的无机-有机配合物骨架为一维互锁结构； [Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O、[Cu2(L3)3(H2O)6(SiW12O40)]·6H2O是同构化合物，它们的无机-有机配合物骨架为二维层叠排列结构。
其优点是：合成方法简单，配齿间隔可调；采用双吡啶双酰胺作为含氮配体，双酰胺基团的亲水性好，加快了合成多酸有机-无机配合物时的结晶过程，提高了合成产率；合成的铜配合物对水溶性的有机污染物的亲和能力强、催化降解效果好，对亚甲蓝有机污染物的光催化降解率可达90%～99%，可作为光催化材料应用。
附图说明
图1是本发明合成的[Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O粉末衍射单晶拟合实验图；
图2是本发明合成的[Cu2(L2)3(H2O)6(SiMo12O40)]·9H2O粉末衍射单晶拟合实验图；
图3是本发明合成的[Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O粉末衍射单晶拟合实验图；
图4是本发明合成的基于双吡啶双酰胺和Keggin型多酸的铜配合物的热分析图；
图中：1- [Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O，2- [Cu2(L2)3(H2O)6(SiMo12O40)]·9H2O，
3-[Cu2(L2)3(H2O)6(SiW12O40)]·6H2O，4- [Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O，
5-[Cu2(L3)3(H2O)6(SiW12O40)]·6H2O；
图5是本发明合成的[Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O的配位环境图；
图6 是本发明合成的[Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O的堆积图；
图7是本发明合成的[Cu2(L2)3(H2O)6(SiMo12O40)]·9H2O和[Cu2(L2)3(H2O)6(SiW12O40)]·6H2O的配位环境图；
图8是本发明合成的[Cu2(L2)3(H2O)6(SiMo12O40)]·9H2O和[Cu2(L2)3(H2O)6(SiW12O40)]·6H2O的堆积图；
图9是本发明合成的[Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O和[Cu2(L3)3(H2O)6(SiW12O40)]·6H2O的配位环境图；
图10是本发明合成的[Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O和
[Cu2(L3)3(H2O)6(SiW12O40)]·6H2O的堆积图；
图11是无催化剂的亚甲蓝的光催化图；
图12是加入本发明合成的[Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O的亚甲蓝的光催化图；
图13是加入本发明合成的[Cu2(L2)3(H2O)6(SiMo12O40)]·9H2O的亚甲蓝的光催化图；
图14是加入本发明合成的[Cu2(L2)3(H2O)6(SiW12O40)]·6H2O的亚甲蓝的光催化图；
图15是加入本发明合成的Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O的亚甲蓝的光催化图；
图16是加入本发明合成的[Cu2(L3)3(H2O)6(SiW12O40)]·6H2O的亚甲蓝的光催化图。
具体实施方式
实施例1 合成[Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O，其中L1为N,N′-二(3-吡啶甲酰胺基)-1,2-乙烷
将0.1mmol N,N′-二(3-吡啶甲酰胺基)-1,2-乙烷、0.13mmol H4SiMo12O40•29H2O、0.5mmol Cu(NO3)·3H2O和10mL H2O依次加入到50mL烧杯中，室温下搅拌30min，用1.0mol/L的NaOH溶液调pH至5.5，倒入25mL的高压反应釜中，以20℃/小时的加热速率升温至120℃，水热条件下保温3天，以5℃/小时的降温速率将温度降至室温，得到蓝绿色块状晶体，用去离子水和乙醇交替清洗2次，室温下自然晾干，得[Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O，产率为64%，其配位环境图如图5所示，其堆积图如图6所示。
实施例2 合成[Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O，其中L1为N,N′-二(3-吡啶甲酰胺基)-1,2-乙烷
将0.1mmol N,N′-二(3-吡啶甲酰胺基)-1,2-乙烷、0.11mmol H4SiMo12O40•29H2O、0.4mmol Cu(NO3)·3H2O和8mL H2O依次加入到50mL烧杯中，室温下搅拌20min，用0.5mol/L 的NaOH溶液调pH至4，倒入25 mL的高压反应釜中，以20℃/小时的加热速率升温至110℃，水热条件下保温4天，以5℃/小时的降温速率将温度降至室温，得到蓝绿色块状晶体用去离子水和乙醇交替清洗3次，室温下自然晾干，得[Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O，产率为82%，其配位环境图如图5所示，其堆积图如图6所示。
实施例3 合成[Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O，其中L1为N,N′-二(3-吡啶甲酰胺基)-1,2-乙烷
将0.1mmol N,N′-二(3-吡啶甲酰胺基)-1,2-乙烷、0.15mmol H4SiMo12O40•29H2O、0.6mmol Cu(NO3)·3H2O和12 mL H2O依次加入到50mL烧杯中，室温下搅拌40min，用2.0mol/L 的NaOH溶液调pH至4.6，倒入25mL高压反应釜中，以10℃/小时的加热速率升温至130℃，水热条件下保温5天，以10℃/小时的降温速率将温度降至室温，得到蓝绿色块状晶体用去离子水和乙醇交替清洗3次，室温下自然晾干，得[Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O，产率为68%，其配位环境图如图5所示，其堆积图如图6所示。
实施例4 合成[Cu2(L2)3(H2O)6(SiMo12O40)]·9H2O，其中L2为N,N′-二(3-吡啶甲酰胺基)-1,4-丁烷
将0.1 mmol N,N′-二(3-吡啶甲酰胺基)-1,4-丁烷、0.12 mmol H4SiMo12O40•29H2O，0.45mmol Cu(NO3)·3H2O和10mL H2O依次加入到50mL烧杯中，室温下搅拌30min，用1.0 mol/L的 NaOH溶液调pH至5.5，倒入25 mL高压反应釜中，以20℃/小时的加热速率升温至120℃，水热条件下保温3天，以5℃/小时的降温速率将温度降至室温，得到蓝绿色块状晶体，用去离子水和乙醇交替清洗2次，室温下自然晾干，得[Cu2(L2)3(H2O)6(SiMo12O40)]·9H2O，产率76%，其配位环境图如图7所示，其堆积图如图8所示。
实施例5 合成[Cu2(L2)3(H2O)6(SiW12O40)]·6H2O，其中L2为N,N′-二(3-吡啶甲酰胺基)-1,4-丁烷
将0.1mmol N,N′-二(3-吡啶甲酰胺基)-1,4-丁烷、0.12mmol H4SiW12O40•26H2O、0.45 mmol Cu(NO3)·3H2O和10mL H2O依次加入到50mL烧杯中，室温下搅拌30min，用1.0 mol/L的 NaOH溶液调pH至5.5，倒入25 mL高压反应釜中，以20℃/小时的加热速率升温至120℃，水热条件下保温3天，以5℃/小时的降温速率将温度降至室温，得到蓝绿色块状晶体，用去离子水和乙醇交替清洗2次，室温下自然晾干，得[Cu2(L2)3(H2O)6(SiW12O40)]·6H2O，产率75% ，其配位环境图如图7所示，其堆积图如图8所示。
实施例6 [Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O，其中L3为N,N′-二(3-吡啶甲酰胺基)-1,6-己烷
将0.1 mmol N,N′-二(3-吡啶甲酰胺基)-1,6-己烷、0.12mmol H4SiMo12O40•29H2O、0.45mmol Cu(NO3)·3H2O和10mL H2O依次加入到50mL烧杯中，室温下搅拌30 min，用1.0mol/L的 NaOH溶液调pH至5.2，倒入25mL高压反应釜中，以20℃/小时的加热速率升温至120℃，水热条件下保温5天，以5℃/小时的降温速率将温度降至室温，得到蓝绿色块状晶体，用去离子水和乙醇交替清洗2次，室温下自然晾干，得[Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O，产率78%，其配位环境图如图9所示，其堆积图如图10所示。
实施例7 [Cu2(L3)3(H2O)6(SiW12O40)]·6H2O，其中L3为N,N′-二(3-吡啶甲酰胺基)-1,6-己烷
将0.1 mmol N,N′-二(3-吡啶甲酰胺基)-1,6-己烷、0.135mmol H4SiW12O40•26H2O、0.55mmol Cu(NO3)·3H2O和10mL H2O依次加入到50mL烧杯中，室温下搅拌30min，用1.0mol/L的NaOH溶液调pH至5.2，倒入25mL高压反应釜中，以20℃/小时的加热速率升温至125℃，水热条件下保温4天，以5℃/小时的降温速率将温度降至室温，得到蓝绿色块状晶体，用去离子水和乙醇交替清洗2次，室温下自然晾干，得[Cu2(L3)3(H2O)6(SiW12O40)]·6H2O，产率80%，其配位环境图如图9所示，其堆积图如图10所示。
实施例8
用N,N′-二(3-吡啶甲酰胺基)-1,4-丁烷代替实施例2、实施例3中N,N′-二(3-吡啶甲酰胺基)-1,2-乙烷，制得[Cu2(L2)3(H2O)6(SiMo12O40)]·9H2O。
实施例9
实施例2、实施例3中N,N′-二(3-吡啶甲酰胺基)-1,2-乙烷用N,N′-二(3-吡啶甲酰胺基)-1,4-丁烷代替，H4SiMo12O40•29H2O用H4SiW12O40·26H2O代替，制得[Cu2(L2)3(H2O)6(SiW12O40)]·9H2O。
实施例10
用N,N′-二(3-吡啶甲酰胺基)-1,6-己烷代替实施例2、实施例3中N,N′-二(3-吡啶甲酰胺基)-1,2-乙烷，制得[Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O。
实施例11
实施例2、实施例3中N,N′-二(3-吡啶甲酰胺基)-1,6-己烷用N,N′-二(3-吡啶甲酰胺基)-1,4-丁烷代替，H4SiMo12O40•29H2O用H4SiW12O40·26H2O代替，制得[Cu2(L3)3(H2O)6(SiW12O40)]·6H2O。
基于双吡啶双酰胺和Keggin型多酸的铜配合物的表征
(1)粉末衍射表征相纯度
在Rigaku D/Max-2500衍射仪上收集完成粉末衍射数据，操作电流为100 mA，电压为40 kV。采用铜靶X射线。固定扫描，接收狭缝宽为0.1mm。密度数据收集使用2θ/θ扫描模式，扫描范围5o到50o，扫描速度为5o/s，跨度为0.02o/次。数据拟合使用Cerius2程序，单晶结构粉末衍射谱模拟转化使用Mercury 1.4.1。
由于[Cu2(L2)3(H2O)6(SiMo12O40)]·9H2O与[Cu2(L2)3(H2O)6(SiW12O40)]·6H2O同构，所以只表征[Cu2(L2)3(H2O)6(SiMo12O40)]·9H2O粉末衍射；
[Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O与[Cu2(L3)3(H2O)6(SiW12O40)]·6H2O同构，只表征[Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O粉末衍射；如图1～图3所示，基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物的粉末X射线衍射谱图与拟合的XRD谱图基本吻合，表明配合物均为纯相。
(2)热重表征材料稳定性
热稳定性采用SDT 2960热分析仪完成，加热速率10℃/ min，温度范围30℃~800℃。图4表明本发明合成的配合物的分解温度范围为150℃~750℃。
(3)晶体结构测定
用显微镜选取合适大小的单晶，室温下采用Bruker SMART 1000 CCD衍射仪（石墨单色器，Mo-Ka，l = 0.71069 Å）收集衍射数据。扫描方式w- φ，衍射数据使用SADABS程序进行吸收校正。数据还原和结构解析分别使用SAINT和SHELXTL程序完成。最小二乘法确定全部非氢原子坐标，并用理论加氢法得到氢原子位置。采用最小二乘法对晶体结构进行精修。图5~图10展示出实施例1~实施例7中合成的基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物的基本配位情况和堆积方式。其晶体学衍射点数据收集与结构精修的部分参数如下表所示：
配合物 实施例1～3 实施例4 实施例5 实施例6 实施例7
CCDC 850463 850464 850465 850466 850467
分子量 2901.45 3111.74 4096.59 3105.80 4160.72
晶系 三斜 三斜 三斜 三斜 三斜
空间群 P -1 C 2/c C 2/c P -1 P -1
晶胞参数
a (Å) 12.035(5) 27.702(5) 27.885(5) 11.364(5) 11.380(5)
b (Å) 12.176(5) 21.936(5) 21.858(5) 12.956(5) 13.015(5)
c (Å) 15.337(5) 14.644(2) 14.863(5) 16.867(5) 16.866(5)
α (°) 97.253(5) 90 90 100.639(5) 101.322(5)
β (°) 102.281(5) 91.589(5) 90.450(5) 108.695(5) 108.603(5)
γ (°) 110.373(5) 90 90 91.221(5) 90.544(5)
V (Å 3) 2008.8(13) 8932(4) 9059(4) 2303.2(15) 2314.4(15)
Z 1 4 4 1 1
理论密度 (g cm–3) 2.451 2.314 3.004 2.239 2.985
吸收系数 (mm-1) 2.455 2.216 15.744 2.145 15.408
F (000) 1434 6077 7464 1518 1902
总衍射点 9798 22238 22547 36569 11738
独立衍射点/ Rint 6965/0.0332 7861/0.0504 7974/0.0594 10015/0.0199 8057/0.0259
GOF 1.020 0.948 1.011 1.003 1.069
R 1a [I > 2σ(I)] 0.0696 0.0681 0.0488 0.0463 0.0435
wR 2b (all data) 0.1913 0.1982 0.1226 0.1157 0.1142
亚甲蓝水溶液在紫外光下的降解实验
对实施例1~实施例3合成的 [Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O（化合物1）；
实施例4合成的[Cu2(L2)3(H2O)6(SiMo12O40)]·9H2O（化合物2）；
实施例5合成的[Cu2(L2)3(H2O)6(SiW12O40)]·6H2O（化合物3）；
实施例6合成的[Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O（化合物4）；
实施例7合成的[Cu2(L3)3(H2O)6(SiW12O40)]·6H2O（化合物5）进行亚甲蓝水溶液在紫外光下的降解实验，以亚甲蓝水溶液对紫外光的特性吸收作为判断亚甲蓝存在的依据，用于确定化合物1～化合物5对水溶性污染物的降解能力。
具体实验步骤如下：
将150mg的化合物1～化合物5分别加入100mL浓度为1mol/L的亚甲蓝水溶液中作为实验组，并取同体积的亚甲蓝水溶液作为对照组。搅拌实验组的亚甲蓝水溶液30min得到悬浮物，边搅拌边采用汞灯作为光源的紫外灯进行照射。每隔30min取出5mL溶液进行UV测试。如图11所示，对照组的亚甲蓝水溶液在紫外光照射150min后紫外吸收量几乎没有变化，表明该物质无法仅仅通过紫外光照射而降解。如图12～图16所示，实验组亚甲蓝水溶液在经过240min紫外光照射后，亚甲蓝的特征吸收已经基本消失，表明该物质已经分解殆尽。其中,化合物1的催化降解效率为90%，化合物2的催化降解效率为95%，化合物3的催化降解效率为99%，化合物4的催化降解效率为90%，化合物5的催化效率为90%。

Claims (5)

1.一种基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物，其特征在于，化合物的分子式为下式中的一种：
[Cu2(L1)3(H2O)6(SiMo12O40)]·2H2O；
[Cu2(L2)3(H2O)6(SiMo12O40)]·9H2O；
[Cu2(L2)3(H2O)6(SiW12O40)]·6H2O；
[Cu2(L3)3(H2O)6(SiMo12O40)]·6H2O；
[Cu2(L3)3(H2O)6(SiW12O40)]·6H2O；
其中，L1为 N,N′-二(3-吡啶甲酰胺基)-1,2-乙烷；L2为 N,N′-二(3-吡啶甲酰胺基)-1,4-丁烷；L3为N,N′-二(3-吡啶甲酰胺基)-1,6-己烷。
2.一种基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物的合成方法，其特征在于，具体步骤是：
将Cu(NO3)·3H2O、Keggin型的多酸、双吡啶双酰胺有机配体加入去离子水，在室温下搅拌20min～40min形成悬浮混合物，其中双吡啶双酰胺有机配体与Keggin型多酸的摩尔比为1.0:1.1～1.0:1.5，双吡啶双酰胺有机配体与Cu(NO3)·3H2O的摩尔比为1.0:4.0~1.0:6.0，所述的Keggin型多酸是H4SiMo12O40·29H2O或H4SiW12O40·26H2O，所述的双吡啶双酰胺有机配体是N,N′-二(3-吡啶甲酰胺基)-1,2-乙烷或N,N′-二(3-吡啶甲酰胺基)-1,4-丁烷或N,N′-二(3-吡啶甲酰胺基)-1,6-己烷；用0.5mol/L～2.0mol/L的NaOH溶液调pH=4.0～5.5，倒入高压反应釜中升温至110℃～130℃，水热条件下保温3天～5天，降温到室温得到块状蓝绿色晶体，用去离子水和乙醇交替清洗2次～4次，室温下自然晾干，得双吡啶双酰胺有机配体和Keggin型多酸的铜配合物。
3.根据权利要求2所述的基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物的合成方法，其特征在于，升温时升温速率为 10℃/小时～20℃/小时，降温时降温速率为5℃/小时～10℃/小时。
4.根据权利要求2所述的基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物的合成方法，其特征在于，所述的去离子水的加入量为高压反应釜容积的30%～50%。
5.如权利要求1所述的基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物作为光催化材料的应用。
CN 201110437953 2011-12-23 2011-12-23 一种基于双吡啶双酰胺有机配体和Keggin型多酸的铜配合物及其合成方法和应用 Expired - Fee Related CN102513157B (zh)