CN101386530A - 一种镍锌软磁铁氧体材料及其制备方法 - Google Patents
一种镍锌软磁铁氧体材料及其制备方法 Download PDFInfo
- Publication number
- CN101386530A CN101386530A CNA2008102184841A CN200810218484A CN101386530A CN 101386530 A CN101386530 A CN 101386530A CN A2008102184841 A CNA2008102184841 A CN A2008102184841A CN 200810218484 A CN200810218484 A CN 200810218484A CN 101386530 A CN101386530 A CN 101386530A
- Authority
- CN
- China
- Prior art keywords
- auxiliary material
- soft magnetic
- magnetic ferrite
- preparation
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
配方序号 | Fe2O3(mol%) | ZnO(mol%) | NiO(mol%) | CuO(mol%) | MgO(mol%) | Bi2O3(Wt%) | CO2O3(Wt%) | Mn3O4(Wt%) | CaCo3(Wt%) | 预烧 | 烧结 |
1 | 47.81 | 26 | 15.5 | 7 | 3.5 | 0.004 | 0.004 | 0.008 | 0.0005 | 930℃ | 1100℃ |
2 | 47.81 | 25.10 | 16.59 | 7 | 3.5 | 0.004 | 0.004 | 0.008 | 0.0005 | 930℃ | 1100℃ |
3 | 47.81 | 25.1 | 17 | 6.27 | 3.5 | 0.004 | 0.004 | 0.008 | 0.0005 | 930℃ | 1100℃ |
4 | 47.81 | 25.1 | 16.52 | 6.27 | 4.5 | 0.004 | 0.004 | 0.008 | 0.0005 | 930℃ | 1100℃ |
5 | 47.81 | 25.1 | 15.52 | 6.27 | 5.5 | 0.004 | 0.004 | 0.008 | 0.0005 | 930℃ | 1100℃ |
6 | 47.81 | 25.1 | 14.52 | 6.27 | 6.5 | 0.004 | 0.004 | 0.008 | 0.0005 | 930℃ | 1100℃ |
7 | 47.81 | 25.1 | 13.42 | 6.17 | 7.5 | 0.004 | 0.004 | 0.008 | 0.0005 | 930℃ | 1100℃ |
8 | 47.81 | 25.1 | 14.32 | 6.27 | 6.7 | 0.004 | 0.004 | 0.008 | 0.0005 | 930℃ | 1100℃ |
9 | 47.81 | 25.1 | 13.82 | 6.27 | 7.0 | 0.004 | 0.004 | 0.008 | 0.0005 | 930℃ | 1100℃ |
10 | 47.81 | 25.1 | 13.82 | 6.27 | 7.0 | 0.004 | 0.004 | 0.008 | 0.0005 | 930℃ | 1100℃ |
11 | 47.81 | 25.1 | 13.82 | 6.27 | 7.0 | 0.004 | 0.004 | 0.008 | 0.0005 | 930℃ | 1100℃ |
12 | 47.81 | 25.1 | 13.82 | 6.27 | 7.0 | 0.004 | 0.004 | 0.008 | 0.0005 | 930℃ | 1100℃ |
13 | 47.81 | 25.1 | 13.82 | 6.27 | 7.0 | 0.004 | 0.004 | 0.008 | 0.0005 | 930℃ | 1100℃ |
配方序号 | 外径(mm) | 内径(mm) | 高度(mm) | L(μH)(1KHz) | Q(2.52MHz) | 绝缘电阻(MΩ) | Tc(℃) | μi | Bm | 测试结论 |
1 | 25.05 | 15.04 | 7.52 | 14.7 | 112 | >500 | 210 | 192 | 281 | OK |
2 | 25.12 | 15.13 | 7.50 | 14.8 | 120 | >500 | 182 | 195 | 282 | OK |
3 | 25.10 | 15.11 | 7.52 | 15.0 | 133 | >500 | 192 | 197 | 270 | OK |
4 | 25.15 | 15.08 | 7.49 | 15.1 | 129 | >500 | 208 | 197 | 299 | OK |
5 | 25.13 | 15.09 | 7.45 | 15 | 125 | >500 | 206 | 198 | 294 | OK |
6 | 25.11 | 15.12 | 7.52 | 14.8 | 123 | >500 | 205 | 194 | 295 | OK |
7 | 25.16 | 15.11 | 7.61 | 12.8 | 121 | >500 | 204 | 165 | 293 | OK |
8 | 25.14 | 15.07 | 7.52 | 15.5 | 126 | >500 | 202 | 208 | 296 | OK |
9 | 25.11 | 15.05 | 7.49 | 15.2 | 124 | >500 | 198 | 205 | 295 | OK |
10 | 25.12 | 15.06 | 7.49 | 15.3 | 125 | >500 | 200 | 208 | 295 | OK |
11 | 25.12 | 15.05 | 7.50 | 15.2 | 124 | >500 | 198 | 206 | 296 | OK |
12 | 25.11 | 15.04 | 7.51 | 15.4 | 126 | >500 | 200 | 205 | 295 | OK |
13 | 25.13 | 15.03 | 7.50 | 15.2 | 124 | >500 | 197 | 206 | 296 | OK |
Claims (9)