WO2021132398A1 - 歯ブラシ - Google Patents

歯ブラシ Download PDF

Info

Publication number
WO2021132398A1
WO2021132398A1 PCT/JP2020/048297 JP2020048297W WO2021132398A1 WO 2021132398 A1 WO2021132398 A1 WO 2021132398A1 JP 2020048297 W JP2020048297 W JP 2020048297W WO 2021132398 A1 WO2021132398 A1 WO 2021132398A1
Authority
WO
WIPO (PCT)
Prior art keywords
flocking
hole
thickness
depth
average molecular
Prior art date
Application number
PCT/JP2020/048297
Other languages
English (en)
French (fr)
Inventor
希絵子 今井
Original Assignee
サンスター株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by サンスター株式会社 filed Critical サンスター株式会社
Priority to EP20904567.3A priority Critical patent/EP4082389A4/en
Priority to CN202080089948.2A priority patent/CN114901104A/zh
Priority to US17/787,540 priority patent/US20220378183A1/en
Priority to JP2021567579A priority patent/JPWO2021132398A1/ja
Publication of WO2021132398A1 publication Critical patent/WO2021132398A1/ja

Abstract

【課題】毛束の抜け強度を維持しつつ、台割れや外観不良が抑えられ、ヘッド部のさらなる薄型化が可能となる歯ブラシを提供せんとする。 【解決手段】ヘッド部が、重量平均分子量１３００００以上のポリアセタール樹脂により成形され、厚みが３．０ｍｍ以下の薄型ヘッドであり、前記植毛台の厚さである台厚をＴ１（ｍｍ）、植毛穴の穴深さをＵ１（ｍｍ）、植毛面から打込まれた平線上端までの深さである平線打込深さをＨ１（ｍｍ）、前記ポリアセタール樹脂の重量平均分子量をＭｗとした場合に、下記式（１）を満たすことを特徴とする歯ブラシ。

Description

歯ブラシ
　本発明は、薄型のヘッド部の複数の植毛穴に平線を用いて毛束を植設してなる歯ブラシに関する。
　歯ブラシは、ヘッド部の植毛台の植毛穴に毛束よりなる毛束が植毛されている。口腔内での操作性を高めるため、歯ブラシのヘッド部及びネック部は樹脂の材質や植毛の仕様、形状等を検討することで薄型化のための工夫が行われている（例えば、特許文献１参照。）。特許文献１では、平線の長さや幅、植毛穴の直径、深さ、樹脂の材質等につき適切な組み合わせとすることで、ヘッド部を薄型化することが提案されている。
　しかしながら、特許文献１からも分かるように、ヘッド部の樹脂材料としてポリアセタール樹脂（ＰＯＭ）を用いた場合、薄型のヘッド部に対して平線により抜け強度を維持しつつ毛束を植毛すると亀裂（台割れ）や白化などの不具合が発生する（文献表２実施例８参照）。すなわちヘッド部の材料としてＰＯＭを用いる場合には、ヘッド厚を厚く設定しなければ安定した生産を行うことができなかった。
特許第５４２７４８６号公報
　そこで、本発明が前述の状況に鑑み、解決しようとするところは、毛束の抜け強度を維持しつつ、台割れや外観不良が抑えられ、ヘッド部のさらなる薄型化が可能となる歯ブラシを提供する点にある。
　本発明は、以下の発明を包含する。
　［１］　ヘッド部に植毛穴を有する植毛台を有し、該植毛台の各植毛穴に平線打ち込みにより毛束が植毛された歯ブラシにおいて、ヘッド部が、重量平均分子量１３００００以上のポリアセタール樹脂により成形され、厚みが３．０ｍｍ以下の薄型ヘッドであり、前記植毛台の厚さである台厚をＴ１（ｍｍ）、植毛穴の穴深さをＵ１（ｍｍ）、植毛面から打込まれた平線上端までの深さである平線打込深さをＨ１（ｍｍ）、前記ポリアセタール樹脂の重量平均分子量をＭｗとした場合に、下記式（１）を満たすことを特徴とする歯ブラシ。
Figure JPOXMLDOC01-appb-M000003
  
　［２］　ヘッド部に植毛穴を有する植毛台を有し、該植毛台の各植毛穴に平線打ち込みにより毛束が植毛された歯ブラシにおいて、ヘッド部が、重量平均分子量１３００００以上のポリアセタール樹脂により成形され、厚みが３．０ｍｍ以下の薄型ヘッドであり、前記植毛台の厚さである台厚をＴ１（ｍｍ）、植毛穴の穴深さをＵ１（ｍｍ）、植毛面から打込まれた平線上端までの深さである平線打込深さをＨ１（ｍｍ）、前記ポリアセタール樹脂の重量平均分子量をＭｗとした場合に、下記式（２）を満たすことを特徴とする歯ブラシ。
Figure JPOXMLDOC01-appb-M000004
  
　以上にしてなる本発明によれば、毛束の抜け強度を維持しつつ、台割れや外観不良が抑えられ、ヘッド部のさらなる薄型化が可能となる。具体的には、ヘッド部が、厚みが３．０ｍｍ以下の薄型ヘッドとされることで、口腔内での操作性が向上する。また、ヘッド部が、重量平均分子量１３００００以上のポリアセタール樹脂により成形され、植毛台の厚さである台厚をＴ１（ｍｍ）、植毛穴の穴深さをＵ１（ｍｍ）、植毛面から打込まれた平線上端までの深さである平線打込深さをＨ１（ｍｍ）、前記ポリアセタール樹脂の重量平均分子量をＭｗとした場合に、下記式（１）を満たすように構成されることで、台割れを抑えることができる。
Figure JPOXMLDOC01-appb-M000005
  
　また、ヘッド部が、重量平均分子量１３００００以上のポリアセタール樹脂により成形され、植毛台の厚さである台厚をＴ１（ｍｍ）、植毛穴の穴深さをＵ１（ｍｍ）、植毛面から打込まれた平線上端までの深さである平線打込深さをＨ１（ｍｍ）、前記ポリアセタール樹脂の重量平均分子量をＭｗとした場合に、下記式（２）を満たすように構成されることで、台割れに加えて外観不良（凹凸の発生）も確実に抑えることができる。
Figure JPOXMLDOC01-appb-M000006
  
本発明の代表的実施形態に係る歯ブラシのヘッド部の横断面図。 同じくヘッド部の植毛部を示す説明図。
　次に、本発明の実施形態を添付図面に基づき詳細に説明する。
　本発明に係る歯ブラシ１は、図１に示すように薄型のヘッド部２に複数の植毛穴２０を有する植毛台５を有し、各植毛穴２０に平線を用いて毛束４を植設したものである。本例の歯ブラシ１は、ヘッド部と首部と柄部が合成樹脂で一体成形された手動の歯ブラシでもよいし、駆動機構を内蔵する把持部としての本体部の先端側に、ヘッド部及び首部からなる歯ブラシ清掃体が接続される電動歯ブラシでもよく、その他の形態でも勿論よい。
　ヘッド部２は、重量平均分子量１３００００以上のポリアセタール樹脂によって一体成形されている。ポリアセタール樹脂は、非晶部分だけでなく、結晶部分が存在していれば、ホモポリマーでもコポリマーでもよい。重量平均分子量が高いほど結晶化度が高くなるため、割れにくくなり、外観も良くなる。ヘッド部２は、厚さ（台厚）Ｔ１が３．０ｍｍ以下の薄型の植毛台５からなるヘッドに構成されている。好ましくは２．９ｍｍ以下、より好ましくは２．６ｍｍ以下、さらに好ましくは２．５ｍｍ以下の薄型ヘッドに構成される。植毛台５の厚さである台厚Ｔ１の下限については、２ｍｍ以上が好ましく、２．２ｍｍ以上がより好ましい。２ｍｍ未満だと十分な抜け強度を確保することが難しくなる。台厚Ｔ１は、少なくとも毛束４が植設される植毛面の部分に関する。
　ヘッド部２（植毛台５）の毛束４が突設される腹側の植毛面２１には、断面視略円形の有底の植毛穴２０が複数形成されている。植毛穴２０の個数、配列形態などは本例に何ら限定されず、開口径、深さ、縦断面形状、毛束一つあたりのフィラメントの本数、その材質など、種々の条件に応じて適切な範囲から選択される。例えば、開口径（内径Ｄ１）が１．２～２．４ｍｍ程度で適宜決められる。本例の植毛穴２０は、図２に示すように、基本的に断面円形のストレート状の穴であり、底部の周壁には円錐台状に縮径した傾斜面が形成されている。
　植毛穴２０の穴深さＵ１は、植毛面２１の開口から植毛穴２０の底面２００までの深さである。底部の厚みＴ２、すなわち植毛穴底面２００からヘッド部（植毛台５）の背面２２までの距離を、本明細書では「穴下～台下」と称す。なお、植毛穴２０は、その他の形状でもよい。穴深さ（Ｕ１）は、０．９ｍｍ以上とすることが、毛束の良好な抜け強度を維持する点で好ましい。
　穴下～台下（Ｔ２）は、０．１５ｍｍ以上、より好ましくは０．２ｍｍ以上、さらに好ましくは０．２５ｍｍ以上である。穴下～台下が０．５ｍｍ以上になると、本発明の薄型ヘッドでは毛束の抜け強度が維持できなくなるため、下穴～台下は０．５ｍｍ未満、より好ましくは０．４５ｍｍ以下に抑えることが好ましい。
　各植毛穴２０には、それぞれ複数本のフィラメントを束ねて二つ折りにした毛束が平線３を用いて植設される。平線３の材質は特に限定されず、一般的な歯ブラシで用いられている金属製や硬質合成樹脂製などの公知の材質とすればよい。平線３の厚さは、０．１ｍｍ以上０．２ｍｍ以下、より好ましくは０．１５ｍｍ以上０．１８５ｍｍ以下に設定される。厚さが０．１ｍｍより薄くなると打ち込みの際に変形して抜け強度が維持できない。厚さが０．２１ｍｍ以上になると特に薄型ヘッドの場合にヘッド部が白化したり台割れの虞が生じる。
　植毛穴２０に対する平線３の掛かり代（植毛穴２０の穴径Ｄ１に対する平線３の打込み方向に直交する横方向の長さＬの差）は、好ましくは＋０．３５ｍｍ以上＋０．６ｍｍ以下、より好ましくは＋０．４５ｍｍ以上＋０．６ｍｍ以下に設定される。＋０．３５ｍｍより小さいと食い込み量が少なく抜け強度が維持できない。＋０．６ｍｍより大きくなると平線の変形に繋がり、結果として毛束やフィラメント１本の抜け強度が低下してしまう。平線３の長さ方向の各端部が同じだけ食い込むように打ち込むと、それぞれ植毛穴２０の周壁に対して、好ましくは０．１７５ｍｍ以上０．３ｍｍ以下の長さ食い込んだ状態となる。
　平線３の横方向に垂直な面で切断した断面積は、０．１ｍｍ２以上０．３ｍｍ２未満、より好ましくは０．１２ｍｍ２以上０．３ｍｍ２以下に設定されている。断面積が０．１ｍｍ２より小さいと平線が屈曲してしまい、結果として毛束やフィラメント１本の抜け強度が低下する。この断面形状は本例では長円形状とし、打ち込み方向基端側及び先端側に曲面を有し、毛束４に負担を掛けないように考慮されている。本例の平線３の厚さｔは、両端の曲面部分を除く部分のストレート領域の厚さである。
　平線３の打ち込みは、図２の仮想線のようになる。本明細書では、植毛穴が開口する植毛面２１から打ち込んだ平線３の上端までの距離Ｈ１を「平線打込深さ」と称す。また、同じく植毛面２１から打ち込んだ平線３の下端までの距離Ｈ２を平線３の縦寸法を含む打ち込み深さとして「プラス平線」と称す。さらに、平線の下端から植毛穴底面２００までの距離Ｈ３を「平線～穴底」と称す。平線打込深さ（Ｈ１）は、０．０７ｍｍ～０．５ｍｍの間の値に設定することが、台割れを防止し、優れた外観、抜毛強度ともに維持できる点で好ましい。また、平線～穴底（Ｈ３）については、０．５ｍｍ以上、より好ましくは０．５８ｍｍ以上確保することが台割れ防止および良好な外観を維持する点で好ましい。
　フィラメントの材質は特に限定されず、ナイロン、ポリエステル、ポリオレフィンなどの樹脂材料からなる人工毛でもよく、豚毛などの天然毛でもよい。またこれらを組み合わせてもよい。その他、断面形状や断面の大きさ、長さ、先細形状の有無など、公知の形態を広く採用できる。
　このような本発明に係る歯ブラシ１のヘッド部２は、台厚Ｔ１（ｍｍ）、植毛穴の穴深さＵ１（ｍｍ）、平線打込深さをＨ１（ｍｍ）、ポリアセタール樹脂の重量平均分子量Ｍｗについて、下記式（３）のＸ１の値が、２．９６以上になるように構成されている。このＸ１が２．９６未満になる場合、台割れが生じる可能性が出てくる。
Figure JPOXMLDOC01-appb-M000007
  
　また、本発明に係る歯ブラシ１のヘッド部２は、台厚Ｔ１（ｍｍ）、植毛穴の穴深さＵ１（ｍｍ）、平線打込深さＨ１（ｍｍ）、ポリアセタール樹脂の重量平均分子量Ｍｗについて、下記式（４）のＸ２の値が、３．３３以上になるように構成されている。このＸ２が３．３３未満になる場合、台割れ或いは外観不良（凹凸の発生）が生じる可能性が出てくる。３．３３以上とすれば、台割れに加えて外観不良（凹凸の発生）も確実に抑えることができる。
Figure JPOXMLDOC01-appb-M000008
  
　以上、本発明の実施形態について説明したが、本発明はこうした形態に何ら限定されるものではなく、本発明の要旨を逸脱しない範囲において種々なる形態で実施し得ることは勿論である。
＜台割れ、外観の評価＞
　次に、ポリアセタール樹脂により成形した台厚３．０ｍｍ以下の薄型ヘッド部のサンプルを、台厚Ｔ１、穴深さＵ１，平線打込深さＨ１、穴下～台下Ｔ２、ポリアセタール樹脂の重量平均分子量Ｍｗをそれぞれ変更して作製し、表１～表８に示すような台割れ、外観（凹凸）の評価を得た。
（サンプル）
　台厚Ｔ１、穴深さＵ１，平線打込深さＨ１、穴下～台下Ｔ２、平線～穴底Ｈ３、ポリアセタール樹脂の重量平均分子量Ｍｗ、上述の数式（３）で求まるＸ１の値、ポリアセタール樹脂の種類「Ｐ１」～「Ｐ６」は、表１～表４に示す内容で作成した。植毛穴の内径（開口部）は１．５ｍｍとした。
　ポリアセタール樹脂「Ｐ１」は、ポリアセタールコポリマー（数平均分子量（Ｍｎ）２４９００、重量平均分子量（Ｍｗ）１２２０００、ｚ平均分子量（Ｍｚ）２４７０００、ＭＦＲ２７ｇ／１０ｍｉｎ、引張弾性率２８００Ｍｐａ、曲げ弾性率２５５０Ｍｐａ）である。
　また、ポリアセタール樹脂「Ｐ２」は、ポリアセタールホモポリマー（数平均分子量（Ｍｎ）５５４００、重量平均分子量（Ｍｗ）１３００００、ｚ平均分子量（Ｍｚ）２６１０００、ＭＦＲ２５ｇ／１０ｍｉｎ、引張弾性率３３００Ｍｐａ、曲げ弾性率３０００Ｍｐａ）である。また、ポリアセタール樹脂「Ｐ３」は、ポリアセタールホモポリマー（数平均分子量（Ｍｎ）５８２００、重量平均分子量（Ｍｗ）１４３０００、ｚ平均分子量（Ｍｚ）３０１０００、ＭＦＲ１５ｇ／１０ｍｉｎ、引張弾性率３１００Ｍｐａ、曲げ弾性率３０００Ｍｐａ）である。
　また、ポリアセタール樹脂「Ｐ４」は、ポリアセタールホモポリマー（数平均分子量（Ｍｎ）６７１００、重量平均分子量（Ｍｗ）１８４０００、ｚ平均分子量（Ｍｚ）４７１０００、ＭＦＲ７ｇ／１０ｍｉｎ、引張弾性率３３００Ｍｐａ、曲げ弾性率３１００Ｍｐａ）である。また、ポリアセタール樹脂「Ｐ５」は、ポリアセタールホモポリマー（数平均分子量（Ｍｎ）８５０００、重量平均分子量（Ｍｗ）２２７０００、ｚ平均分子量（Ｍｚ）５４９０００、ＭＦＲ２．５ｇ／１０ｍｉｎ、引張弾性率３２００Ｍｐａ、曲げ弾性率３０００Ｍｐａ）である。また、ポリアセタール樹脂「Ｐ６」は、
ポリアセタールコポリマー（数平均分子量（Ｍｎ）２４８００、重量平均分子量（Ｍｗ）
１４１０００、ｚ平均分子量（Ｍｚ）３０２０００、引張弾性率２８５０Ｍｐａ、曲げ弾性率２７００Ｍｐａ）である。
　植毛する毛束１つあたりのフィラメントの本数は２１～２３本（平均２２本）本、径は０．１９ｍｍ、長さは２９ｍｍ、材質はナイロンとした。打ち込みに用いる平線の打込み方向である縦方向の長さは１．２ｍｍ、これに直交する横方向の長さは２．０～２．０５ｍｍ（平均２．０３ｍｍ）、厚さは０．１８５ｍｍとした。
（台割れの評価方法）
　台割れは、目視にて次の５段階の基準で判定する。「５」：クラックなし。「４」：わすかに薄いクラックが見られる穴がある。「３」：多くの穴に薄いクラックが見られるが、穴間は繋がっていない。「２」：多くの穴に薄いクラックが観察され、穴間が繋がっている。「１」：亀裂（クラック間に隙間がある）が見える、又は複数穴間にまたがるクラックあり。
Figure JPOXMLDOC01-appb-T000009
  
Figure JPOXMLDOC01-appb-T000010
  
Figure JPOXMLDOC01-appb-T000011
  
Figure JPOXMLDOC01-appb-T000012
  
　表１～表４に示すように、ポリアセタール樹脂の重量平均分子量Ｍｗが１３００００未満であるＰ１の場合を除き、Ｘ１の値が２．９６以上であれば、台割れの評価をすべて「３」以上に維持できることが分かる。
　表５～表８は、同じサンプルについて、Ｘ１の値の代わりに、上述の数式（４）で求まるＸ２の値を示し、台割れ評価とともに外観（凹凸）評価の結果を加えたものである。
（外観の評価方法）
　外観は、ヘッド部の背面の外観を次の５段階の基準で判定する。「５」：凹凸なし。「４」：わずかに凹凸が見える。「３」：指で触ると、若干凹凸を感じる。「２」：指で触ると凹凸を感じる。「１」：指で触ると引っ掛かりを感じる程度の凹凸がある。
Figure JPOXMLDOC01-appb-T000013
  
Figure JPOXMLDOC01-appb-T000014
  
Figure JPOXMLDOC01-appb-T000015
  
Figure JPOXMLDOC01-appb-T000016
  
　表５～表８に示すように、ポリアセタール樹脂の重量平均分子量Ｍｗが１３００００未満のＰ１のサンプルを除き、Ｘ２の値が３．３３以上であれば、台割れの評価と外観（凹凸）の評価をすべて「３」以上に維持できることが分かる。
　１　歯ブラシ
　２　ヘッド部
　３　平線
　４　毛束
　５　植毛台
　２０ 　植毛穴
　２１　植毛面
　２２　背面
　Ｄ１　植毛穴の穴径
　Ｈ１　植毛面から平線上端までの深さ（「平線打込深さ」）
　Ｈ２　植毛面から平線下端までの深さ（「プラス平線」）
　Ｈ３　平線下端から植毛穴の底面までの距離（「平線～穴底」）
　Ｔ１　ヘッド部（植毛台）の厚さ（「台厚」）
　Ｔ２　植毛穴底部の厚み（「穴下～台下」）
　Ｕ１　植毛穴の穴深さ
　Ｌ　平線の横方向の長さ
 

Claims (2)

  1. 　ヘッド部に植毛穴を有する植毛台を有し、該植毛台の各植毛穴に平線打ち込みにより毛束が植毛された歯ブラシにおいて、
    　ヘッド部が、重量平均分子量１３００００以上のポリアセタール樹脂により成形され、厚みが３．０ｍｍ以下の薄型ヘッドであり、
    　前記植毛台の厚さである台厚をＴ１（ｍｍ）、植毛穴の穴深さをＵ１（ｍｍ）、植毛面から打込まれた平線上端までの深さである平線打込深さをＨ１（ｍｍ）、前記ポリアセタール樹脂の重量平均分子量をＭｗとした場合に、下記式（１）を満たすことを特徴とする歯ブラシ。
    Figure JPOXMLDOC01-appb-M000001
      
  2. 　ヘッド部に植毛穴を有する植毛台を有し、該植毛台の各植毛穴に平線打ち込みにより毛束が植毛された歯ブラシにおいて、
    　ヘッド部が、重量平均分子量１３００００以上のポリアセタール樹脂により成形され、厚みが３．０ｍｍ以下の薄型ヘッドであり、
    　前記植毛台の厚さである台厚をＴ１（ｍｍ）、植毛穴の穴深さをＵ１（ｍｍ）、植毛面から打込まれた平線上端までの深さである平線打込深さをＨ１（ｍｍ）、前記ポリアセタール樹脂の重量平均分子量をＭｗとした場合に、下記式（２）を満たすことを特徴とする歯ブラシ。
    Figure JPOXMLDOC01-appb-M000002
      
PCT/JP2020/048297 2019-12-25 2020-12-23 歯ブラシ WO2021132398A1 (ja)