WO2019168008A1 - ポリエステルフィルム - Google Patents

ポリエステルフィルム Download PDF

Info

Publication number
WO2019168008A1
WO2019168008A1 PCT/JP2019/007506 JP2019007506W WO2019168008A1 WO 2019168008 A1 WO2019168008 A1 WO 2019168008A1 JP 2019007506 W JP2019007506 W JP 2019007506W WO 2019168008 A1 WO2019168008 A1 WO 2019168008A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyester film
layer
particle
particles
release layer
Prior art date
Application number
PCT/JP2019/007506
Other languages
English (en)
French (fr)
Inventor
慧美 中山
泰人 棟
泰史 川崎
Original Assignee
三菱ケミカル株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三菱ケミカル株式会社 filed Critical 三菱ケミカル株式会社
Priority to KR1020207024802A priority Critical patent/KR102689393B1/ko
Priority to JP2020503558A priority patent/JP7334720B2/ja
Priority to CN201980012433.XA priority patent/CN111699092B/zh
Priority to KR1020247010823A priority patent/KR20240048022A/ko
Publication of WO2019168008A1 publication Critical patent/WO2019168008A1/ja

Abstract

粗面化されたフィルム表面を有し、その表面状態を転写する用途に用いるポリエステルフィルムに関し、転写時のポリエステルフィルムの視認性言い換えれば識別性に優れ、しかも、離型層を形成しても、前記粗面化状態が平滑化されることなく、期待するマット感を対象物に付与することができる、新たなポリエステルフィルムを提供する。　平均粒径２．０μｍ以上の粒子を含有する粒子含有層を備えたポリエステルフィルム基材の前記粒子含有層表面に離型層を形成してなる構成を備え、透過濃度ＯＤ値が０．１０以上であることを特徴とするポリエステルフィルムを提案する。

Description

ポリエステルフィルム
　本発明は、マット調の外観を転写することができる、離形性能を備えたポリエステルフィルムに関する。
　ポリエチレンテレフタレートやポリエチレンナフタレートに代表されるポリエステルフィルムは、機械的強度、寸法安定性、平坦性、耐熱性、耐薬品性、光学特性等に優れた特性を有し、コストパフォーマンスに優れるため、各種用途に使用されている。
　ポリエステルフィルムの用途の一例として、電磁波シールド用途を挙げることができる。プラズマディスプレイ（ＰＤＰ）などでは、電磁波シールドフィルムすなわち導電性フィルムを表示パネルの前面に装着することが行われており、この電磁波シールドフィルムとして、ポリエステルフィルムに網目状の金属の細線を設けた導電性フィルムが一般的に使用されている。
　この種の電磁波シールドフィルムとして、支持フィルム上に電磁波シールドフィルムを形成し、これを各種機器表面に高温プレス圧着して電磁波シールドフィルムを転写することが行われている。
　このような転写型の電磁波シールドフィルムの支持フィルムとしては、従来は、平坦なポリエステルフィルムが一般的に用いられてきた。しかし、製品の外観を艶消し外観に仕上げるため、表面をマット調に仕上げたポリエステルフィルムを当該支持フィルムに使用して、このマット調表面を製品に転写することが提案されている。
　例えば特許文献１には、無機粒子および／または有機粒子を、ポリエステルＡ層全体を１００質量％として０．１質量％以上１０質量％以下含有するポリエステルＡ層を最外層に有する基材フィルムのＡ層にメラミン樹脂を主成分とする塗膜層が積層されてなり、該塗膜層が積層された面の光沢度が３０以下である離型用二軸配向ポリエステルフィルムが開示されている。
　特許文献２には、基材層と少なくとも一方の表面に粒子含有の艶消し層とを有する積層ポリエステルフィルムであって、該艶消し層表面の平均表面粗さ（Ｒａ）が４００～１０００ｎｍ、１０点平均粗さ（Ｒｚ）が４０００～８０００ｎｍであり、該表面における光沢度（Ｇ６０）が６～２０であり、かつ、表面の突起のボイド破れ率が２０％以下であることを特徴とする、二軸配向ポリエステルフィルムが開示されている。
　特許文献３には、無機粒子および／または有機粒子を含有するポリエステルＡ層を少なくとも一方の最外層に有し、該最外層のポリエステルＡ層表面の平均表面粗さＲａが０．３８μｍ以上１．０μｍ以下であり、ポリエステルＡ層表面の粗さ曲線要素の平均長さＲＳｍが１０μｍ以上８０μｍ以下である、離型用二軸配向ポリエステルフィルムが開示されている。
特開２０１５－６６８０５号公報 特開２０１６－９７５２２号公報 特開２０１６－１７５２２９号公報
　上述のように、ポリエステルフィルムの表面を粗面化してマット調に形成することにより、当該ポリエステルフィルムの表面を対象物表面に当接してプレス圧着し、その後、当該ポリエステルフィルムを剥離することで、当該対象物表面に前記粗面化した表面状態を転写してマット調の外観に仕上げることができる。
　従来提案されているこの種の転写用ポリエステルフィルムは、当該ポリエステルフィルムの表面に離型フィルムを積層したり、離型剤を塗布したりして、別途離型層を形成する必要があったため、離型層を形成した際にポリエステルフィルム表面の粗面化状態が平滑化されて、対象物表面に期待するマット感を付与することができない場合があった。
　また、離型性能を備えたポリエステルフィルムとしては、視認性言い換えれば識別性に優れていることが期待されることもあった。
　そこで本発明の第１の目的は、粗面化されたフィルム表面を有し、その表面状態を転写する用途に用いるポリエステルフィルムに関し、転写時のポリエステルフィルムの視認性言い換えれば識別性に優れ、しかも、離型層を形成しても、前記粗面化状態が平滑化されることなく、期待するマット感を対象物に付与することができる、新たなポリエステルフィルムを提供することにある。
　本発明の第２の目的は、ポリエステルフィルム全体のカール（巻き癖）を防ぎつつ、ハンドリング性を高めて、さらには、ポリエステルフィルムを積層する製品との密着性を高めることができる、新たなポリエステルフィルムを提供することにある。
　本発明は、上記第１の目的を達成するため、平均粒径２．０μｍ以上の粒子を含有する粒子含有層を備えたポリエステルフィルム基材を有し、透過濃度ＯＤ値が０．２５以上であることを特徴とする第１のポリエステルフィルムを提案する。
　本発明はまた、同じく上記第１の目的を達成するため、平均粒径２．０μｍ以上の粒子を含有する粒子含有層を備えたポリエステルフィルム基材の前記粒子含有層表面に離型層を形成してなる構成を備え、透過濃度ＯＤ値が０．１０以上であることを特徴とする第２のポリエステルフィルムを提案する。
　本発明は、上記第２の目的を達成するため、基材層の片面に、平均粒径２．０μｍ以上の粒子を含有する粒子含有層Ａを備え、基材層の他方の片面に、平均粒径２．０μｍ以上の粒子を含有する粒子含有層Ｂを備えたポリエステルフィルム基材を有し、平均粒径２．０μｍ以上の粒子の含有量は、粒子含有層Ａよりも粒子含有層Ｂの方が少ないことを特徴とする第３のポリエステルフィルムを提案する。
　本発明が提案する第１及び第２のポリエステルフィルムは、離型層を備えた状態で提供することができるから、離型層を形成した際にポリエステルフィルム表面の粗面化状態が平滑化されることがなく、期待するマット感を対象物に付与することができる。また、ポリエステルフィルムの透過濃度ＯＤ値が０．１０以上又は０．２５以上であるから、転写時のポリエステルフィルムの視認性言い換えれば識別性に優れたものである。
　本発明が提案する第３のポリエステルフィルムは、基材層の両面に粒子含有層Ａ、Ｂを備えたポリエステルフィルム基材を有し、平均粒径２．０μｍ以上の粒子の含有量が、粒子含有層Ａよりも粒子含有層Ｂの方が少ないことを特徴とするポリエステルフィルムは、基材層の両面に粒子含有層Ａ、Ｂを備えているから、ポリエステルフィルム全体のカールを防ぐことができる。しかも、粒子含有層Ａの表面側で対象物表面へのマット感の付与する一方、粒子含有層Ｂについては、粒子の含有量を粒子含有層Ａよりも少なくすることで、表面加工適性を確保することができ、粒子含有層Ｂの表面に所望の層を積層し易くすることができるから、例えば積層する製品との密着性を高めることができる。
本発明の実施形態の一例に係るポリエステルフィルムの構成例を示した断面図である。
　次に、実施の形態例に基づいて本発明を説明する。但し、本発明が次に説明する実施形態に限定されるものではない。
＜＜本ポリエステルフィルム１＞＞
　本発明の実施形態の一例に係るポリエステルフィルム（「本ポリエステルフィルム１」と称する）は、平均粒径２．０μｍ以上の粒子を含有する粒子含有層Ａを備えたポリエステルフィルムである。
　本ポリエステルフィルム１は、無延伸フィルム（シート）であっても延伸フィルムであってもよい。中でも、一軸方向又は二軸方向に延伸された延伸フィルムであるのが好ましい。その中でも、力学特性のバランスや平面性に優れる点で、二軸延伸フィルムであるのが好ましい。
　本ポリエステルフィルム１は、平均粒径２．０μｍ以上の粒子を含有する粒子含有層Ａを備えたポリエステルフィルムのみからなるものであっても、該ポリエステルフィルムに他の層が積層してなるものであってもよい。
＜＜本ポリエステルフィルム１０＞＞
　本発明の実施形態の別の一例に係るポリエステルフィルム（「本ポリエステルフィルム１０」と称する）は、ポリエステルフィルム基材の片面側又は両面側に離型層を形成してなる構成を備えたポリエステルフィルムである。
　本ポリエステルフィルム１０の積層構成としては、ポリエステルフィルム基材の片面側に離型層を形成し、他方の片面側はポリエステルフィルム基材の表面をそのままにした構成であってもよいし、当該他方の片面側に他の層を形成してなる構成であってもよい。また、ポリエステルフィルム基材の両面側に離型層を形成してなる構成であってもよい。
　さらにまた、ポリエステルフィルム基材と離型層との間に他の層を設けてもよい。
　但し、当該離型層は、少なくとも一方の最表面であることが好ましい。
＜ポリエステルフィルム基材＞
　ポリエステルフィルム基材は、平均粒径２．０μｍ以上の粒子を含有する粒子含有層Ａを備えたものであるのが好ましい。すなわち、前記本ポリエステルフィルム１をポリエステルフィルム基材として使用するのが好ましい。よって、以下のポリエステルフィルム基材についての説明は、前記本ポリエステルフィルム１の説明でもある。
　ポリエステルフィルム基材の構成としては、粒子含有層Ａのみからなるものであってもよいし、基材層の片面側又は両面側に粒子含有層Ａを備えたものであってもよい。後者の具体例としては、例えば基材層の両面側に粒子含有層Ａを備えたものであってもよいし、基材層の一面側に粒子含有層Ａを備え、基材層の他面側には粒子含有層Ａとは異なる粒子含有層Ｂを形成したものであってもよいし、基材層の一面側に粒子含有層Ａを備え、基材層の他面側には層を形成しないものであってもよいし、また、基材層の一面側に粒子含有層Ａを備え、基材層の他面側には粒子を含有しない層を形成したものであってもよい。
　中でも、ポリエステルフィルム基材は、基材層の一面側に粒子含有層Ａを備え、基材層の他面側には粒子含有層Ａとは異なる粒子含有層Ｂを形成した構成が好ましいため、この構成については後で詳述する。
　ポリエステルフィルム基材は、透過濃度ＯＤ値が０．１０以上であるのが好ましい。
　透過濃度ＯＤ値が０．１０以上であるということは、不透明さが大きい、言い換えれば白色度が大きいことを意味しており、より白色度が大きい。
　かかる観点から、０．１０～１．０であるのがより好ましく、中でも０．１５以上或いは０．９０以下、その中でも０．２０以上或いは０．８０以下、その中でも０．２５以上であるのがさらに好ましい。
　ポリエステルフィルム基材の透過濃度ＯＤ値が上記範囲であれば、視認性言い換えれば識別性が良好であるので、転写対象物に粗面を転写後に、本ポリエステルフィルム１０を剥離することが容易となる。
　ポリエステルフィルム基材の透過濃度ＯＤ値を０．１０以上にする方法としては、例えば、白色顔料を含有させたり、基材の主成分樹脂との屈折率差が大きな材料を含有させたり、微粒子を含有するフィルムを延伸してフィルム基材中にボイドを形成させたりするなど、公知の方法を採用可能である。
　中でも、白色顔料、例えば金属化合物粒子を含有させて白色化を図る場合、例えば前記基材層、前記粒子含有層、及び、前記基材層の前記粒子含有層とは反対側に設けた層のうちの何れかの層又はこれらのうちの２層以上に、金属化合物粒子を含有させて白色化を図ることができる。この際、上記の白色顔料としては、後述する平均粒径２．０μｍ未満の粒子Ｙを例示することができる。
　なお、ポリエステルフィルム基材の透過濃度ＯＤ値よりも、本ポリエステルフィルム１０の透過濃度ＯＤ値の方が低くなることは当然である。
（各層の主成分樹脂としてのポリエステル）
　ポリエステルフィルム基材を構成する層、例えば上記の基材層、粒子含有層Ａ、粒子含有層Ｂ、さらなる他の層は、ポリエステルを主成分樹脂とする層であるのが好ましい。
　ここで、「主成分樹脂」とは、各層を構成する樹脂成分のうち最も含有割合の多い樹脂の意味である。
　上記ポリエステルは、芳香族ジカルボン酸と脂肪族グリコールとを重縮合させて得られるものであればよい。
　前記芳香族ジカルボン酸としては、例えばテレフタル酸、２，６－ナフタレンジカルボン酸などを挙げることができ、他方の脂肪族グリコールとしては、例えばエチレングリコール、ジエチレングリコール、１，４－シクロヘキサンジメタノール等を挙げることができる。
　また、上記ポリエステルは、ホモポリエステルであっても共重合ポリエステルであってもよい。かかる共重合ポリエステルのジカルボン酸成分として、例えばイソフタル酸、フタル酸、テレフタル酸、２，６－ナフタレンジカルボン酸、アジピン酸、セバシン酸およびオキシカルボン酸等から選ばれる一種または二種以上を挙げることができ、他方のグリコール成分として、例えばエチレングリコール、ジエチレングリコール、プロピレングリコール、ブタンジオール、１，４－シクロヘキサンジメタノール、ネオペンチルグリコール等から選ばれる一種または二種以上を挙げることができる。効果的にマット感を付与するという観点から、含有される第三成分がイソフタル酸であることが好ましい。
　共重合ポリエステルは、含有される第三成分は３０モル％以下であるのが好ましく、中でも５モル％以上或いは３０モル％以下、その中でも２５モル％以下、その中でも特に７モル％以上或いは２２モル％以下であるのがさらに好ましい。この範囲にあることにより、製膜安定性を維持しつつ、効果的にマット感を付与することができる。
　代表的なポリエステルとして、ポリエチレンテレフタレート（ＰＥＴ）、ポリエチレン－２，６－ナフタレンジカルボキシレート（ＰＥＮ）等を例示することができる。
（基材層）
　ポリエステルフィルム基材の基材層は、ポリエステルフィルム基材を構成する各層の中でも最も厚い層であり、上記ポリエステルを主成分樹脂としていれば、その組成は任意である。
　基材層は、粒子を含有する層を備えたものであってもよいし、粒子を含有する層のみからなるものであってもよい。但し、コストの観点から、後述する有機粒子、無機粒子などの粒子を含有しない層であるのが好ましい。
　基材層の厚さは、本ポリエステルフィルム１０のカールを防止するという観点から、ポリエステルフィルム基材厚さの６０～９９％であるのが好ましく、中でも６５％以上或いは９９％以下、その中でも７０％以上或いは９９％以下であるのがさらに好ましい。この範囲にあることにより、基材層自体にコシが出るために本ポリエステルフィルム１０のカールが発生しにくくなる。
（粒子含有層Ａ）
　粒子含有層Ａは、平均粒径２．０μｍ以上の粒子Ｘを含有する層であり、その表面には後述する離型層が設けられることが好ましい。
　粒子含有層Ａが含有する粒子Ｘは平均粒径２．０μｍ以上であるのが好ましい。
　粒子含有層Ａが平均粒径２．０μｍ以上の粒子Ｘを含有することにより、粒子含有層Ａの表面を粗面化することができ、マット調とすることができる。但し、粒子Ｘが大き過ぎると、フィルム製造時のポリエステル押出工程におけるフィルターの圧力上昇が大きくなり生産性が低下する可能性があり、また、粒子Ｘが粒子含有層Ａから脱落するおそれがある。
　よって、粒子Ｘの平均粒径は２．０μｍ以上であるのが好ましく、中でも１０．０μｍ以下、その中でも３．０μｍ以上或いは９．０μｍ以下、その中でも４．０μｍ以上或いは８．０μｍ以下であるのがさらに好ましい。
　なお、粒子Ｘの平均粒径は、粒子が粉体の場合には、遠心沈降式粒度分布測定装置（例えば、株式会社島津製作所社製、ＳＡ－ＣＰ３型）を用いて粉体を測定した等価球形分布における積算体積分率５０％の粒径（ｄ５０）を平均粒径とすることができる。フィルム又は層中の粒子の平均粒径については、１０個以上の粒子Ｘを走査型電子顕微鏡（ＳＥＭ）観察して粒子Ｘの直径を測定し、その平均値として求めることができる。その際、非球状粒子の場合は、最長径と最短径の平均値を各粒子Ｘの直径として測定することができる。後述する粒子Ｙについても同様である。
　粒子Ｘの形状は任意である。例えば球状、塊状、棒状、扁平状等のいずれでもよい。但し、均一なマット面を得られるという観点から、球状であるのが好ましい。
　粒子Ｘの硬度、比重、色等については特に制限はないし、種類の異なる２種類以上を併用してもよい。
　上記平均粒径２．０μｍ以上の粒子Ｘは、マット感付与可能な粒子であれば特に限定されるものではない。例えば無機粒子であっても、有機粒子であっても、架橋高分子粒子であってもよい。
　無機粒子は、延伸した際にフィルムにボイドを形成することがあり、視認性向上のために白色顔料を添加する必要がないという観点から好ましく、有機粒子はボイドが生じにくいためにフィルムの強度が下がらないという観点で好ましい。
　無機粒子としては、例えばシリカ、炭酸カルシウム、カオリン、タルク、炭酸マグネシウム、炭酸バリウム、硫酸カルシウム、硫酸バリウム、リン酸リチウム、リン酸カルシウム、リン酸マグネシウム、酸化アルミニウム、酸化チタン、酸化ジルコニウム、フッ化リチウム、フッ化カルシウム、フッ化リチウム、ゼオライト、硫化モリブデンなどを挙げることができる。
　なお、上記シリカ粒子は、二酸化ケイ素（ＳｉＯ２）の他にも、例えば含水二酸化ケイ素などを含んでいてもよい。
　有機粒子としては、例えばアクリル樹脂、スチレン樹脂、尿素樹脂、フェノール樹脂、エポキシ樹脂、ベンゾグアナミン樹脂等を挙げることができる。
　中でも、メタクリル酸メチル又はスチレン又は両方を共重合成分とする樹脂からなる粒子は、特にＰＥＴフィルムとの相性が良いため、好ましい。
　架橋高分子粒子としては、例えばジビニルベンゼン、スチレン、アクリル酸、メタクリル酸、アクリル酸またはメタクリル酸のビニル系モノマーの単独または共重合体が挙げられる。その他ポリテトラフルオロエチレン、ベンゾグアナミン樹脂、熱硬化エポキシ樹脂、不飽和ポリエステル樹脂、熱硬化性尿素樹脂、熱硬化性フェノール樹脂などの架橋性高分子粒子を用いてもよい。
　粒子含有層Ａにおける粒子Ｘの含有量は、粒子含有層Ａの表面を好適に粗面化することができ、しかも、フィルム延伸時に破断等が生じないようにするなどの観点から、０．１～２０質量％であるのが好ましく、その中でも１質量％以上或いは１８質量％以下、その中でも２質量％以上或いは１５質量％以下、その中でも３質量％以上或いは１０質量％以下であるのがさらに好ましい。
　また、粒子含有層Ａは後述する粒子Ｙを含有してもよい。
　粒子含有層Ａの厚さは、１．０～２０μｍであるのが好ましく、中でも２．０μｍ以上或いは２０μｍ以下、その中でも３．０μｍ以上或いは２０μｍ以下、その中でも特に４．０μｍ以上或いは１５μｍ以下であるのがさらに好ましい。
　粒子含有層Ａの厚さを１．０μｍ以上とすることにより、効果的にマット感を付与することができる。また、粒子含有層Ａの厚さが２０μｍを超えると、マット感の改善効果は低くなり、粒子Ｘに起因するフィルム表面の粗面化が低減するおそれがある。
　粒子含有層Ａの厚さと粒子Ｘの平均粒径の関係は、フィルム表面の粗面化および粒子の脱落抑制の観点から、（粒子Ｘの平均粒径）／（粒子含有層Ａの厚さ）が０．１以上、５．０以下が好ましく、０．３以上、４．０以下がより好ましく、０．５以上、３．０以下が特に好ましい。
（粒子含有層Ｂ）
　前述したように、基材層の一面側に粒子含有層Ａを備え、基材層の他面側には、粒子含有層Ａとは異なる粒子含有層Ｂを形成することができる。粒子含有層Ｂの表面には、後述する離型層が設けられている必要は無いが、離型層を設ける構成を排除するものではない。
　本ポリエステルフィルム１０全体のカールを防ぐことができる点で、粒子含有層Ｂにおいても、平均粒径２．０μｍ以上の粒子Ｘを含有するのが好ましい。
　但し、粒子含有層Ｂの面は、ハンドリング性を好適にする程度に粗面化できればよいから、粒子含有層Ａの面ほど粗面化する必要はない。よって、平均粒径２．０μｍ以上の粒子Ｘの含有量は粒子含有層Ａよりも少なくてよい。粒子含有層Ａよりも粒子含有層Ｂの方が、平均粒径２．０μｍ以上の粒子Ｘの含有量が少ないことにより、ポリエステルフィルム１０全体のカールを防ぐことができつつ、粒子含有層Ａの表面側で対象物表面へマット感を付与する一方、粒子含有層Ｂの表面に所望の層を積層し易くすることができる。
　具体的には、粒子含有層Ｂが含有する粒子Ｘの含有量（質量％）は、粒子含有層Ａが含有する粒子Ｘの含有量（質量％）の０．１～１００％とするのが好ましく、中でも１％以上或いは９５％以下、その中でも５％以上或いは９０％以下であるのがさらに好ましく、その中でも１０％以上或いは８０％以下、その中でも６０％以下であるのがさらに好ましい。
　粒子含有層Ｂは、本ポリエステルフィルム１０を白色化するために、平均粒径２．０μｍ未満の粒子Ｙを含有したものであってもよい。
　この際、粒子含有層Ｂは、粒子Ｘを含有しないで粒子Ｙを含有してもよいし、粒子Ｘと共に粒子Ｙを含有してもよい。
　粒子Ｘと共に粒子Ｙを含有する場合、粒子Ｘと粒子Ｙの含有質量比率は１：９９～９９：１であるのが好ましく、中でも１０：９０～９０：１０、その中でも１５：８５～８５：１５であるのがさらに好ましい。
　粒子Ｙの形状は任意である。例えば球状、塊状、棒状、扁平状等のいずれでもよい。但し、凝集による粗大突起を引き起こしにくいという観点から、球状であるのが好ましい。
　粒子Ｙの硬度、比重、色等については特に制限はないし、種類の異なる２種類以上を併用してもよい。
　粒子Ｙの平均粒径は、光散乱効果による白色不透明性を付与する観点から、０．０５μｍ～０．５０μｍであるのが好ましく、中でも０．１０μｍ以上或いは０．４５μｍ以下、その中でも０．２０μｍ以上或いは０．４０μｍ以下、その中でも０．２５μｍ以上であるのがさらに好ましい。
　粒子Ｙとしては、光散乱効果による白色不透明性を付与する観点から、金属化合物粒子であるのが好ましい。
　金属化合物粒子としては、例えば酸化チタン、炭酸カルシウム、硫酸バリウム、炭酸マグネシウム、炭酸バリウム、硫酸カルシウム、リン酸カルシウム、リン酸マグネシウム、カオリン、酸化アルミニウム、酸化ジルコニウム等を挙げることができ、中でも酸化チタン、炭酸カルシウム、硫酸バリウムなどの金属化合物粒子を挙げることができる。
　なお、粒子含有層Ｂにおいて、粒子Ｘに相当する粒子と粒子Ｙに相当する粒子が同一の材質である場合は、原料としては異なる平均粒径を有する別個の粒子であるものの、混合（配合）すると、それらの中間に平均粒径を有する１種の粒子にほかならない。そのような場合は、混合後の平均粒径をもって粒子Ｘ又は粒子Ｙの何れかとして認識するものとする。
　粒子含有層Ｂの厚さは、本ポリエステルフィルム１０のカールを防止する観点から、粒子含有層Ａの厚さと同様の範囲であるのが好ましい。かかる観点から、粒子含有層Ｂの厚さも１．０～２０μｍであるのが好ましく、中でも２．０μｍ以上或いは１８μｍ以下、その中でも３．０μｍ以上或いは１７μｍ以下、その中でも特に４．０μｍ以上或いは１５μｍ以下であるのがさらに好ましい。
　粒子含有層Ａと粒子含有層Ｂの厚さの比は、本ポリエステルフィルム１０のカールを防止する観点から、（粒子含有層Ａの厚さ）／（粒子含有層Ｂの厚さ）が０．１以上、１０以下が好ましく、中でも０．２以上、或いは５．０以下がより好ましく、その中でも０．５以上、或いは２．０以下が特に好ましい。
（その他の成分）
　ポリエステルフィルム基材を構成する各層には、必要に応じて従来公知の耐候剤、耐光剤、遮光剤、酸化防止剤、熱安定剤、潤滑剤、帯電防止剤、蛍光増白剤、染料、顔料等を添加することができる。また用途によっては、紫外線吸収剤、特にベンゾオキサジノン系紫外線吸収剤等を含有させてもよい。
＜離型層＞
　本ポリエステルフィルム１０は、ポリエステルフィルム基材の前記粒子含有層Ａ表面に離型層を形成してなる構成を備えたものであることが好ましい。
　離型層は、架橋剤由来の架橋構造を有するのが好ましい。このような架橋構造を有していれば、優れた硬度を有することができるから、本ポリエステルフィルム１０を対象物にプレス圧着した際に十分に耐えることができる。
　離型層の厚さは、離型性を有しつつ、ポリエステルフィルム基材表面の粗さを平滑化しない（低減させない）ようにする観点から、０．００１～１μｍであるのが好ましく、中でも０．００２μｍ以上或いは０．５μｍ以下、その中でも０．００５μｍ以上或いは０．２μｍ以下、その中でも０．００８μｍ以上或いは０．１５μｍ以下、その中でも０．０１μｍ以上或いは０．１μｍ以下、その中でも特に０．０１μｍ以上或いは０．０８μｍ以下であるのがさらに好ましい。
　離型層の厚さは、前記離型層を設ける表面の平均表面粗さ（Ｒａ）の０．１～１００％、中でも０．２％以上或いは５０％以下、その中でも１．０％以上或いは２５％以下であるのが好ましい。
（離型層の形成）
　離型層は、前記粒子含有層Ａの表面、すなわち、粗面化された表面に、極めて薄い薄膜として設けるのが好ましいため、塗布延伸法（インラインコーティング）を採用して形成するのが好ましい。但し、この方法に限定するものではない。
　塗布延伸法としては、例えば、逐次二軸延伸においては特に１段目の延伸が終了して、２段目の延伸前に、「離型層形成組成物」を粒子含有層Ａの表面にコーティング処理するのが好ましい。このようにすれば、延伸と同時に塗布が可能になると共に離型層の厚みを延伸倍率に応じて薄くすることができ、ポリエステルフィルムとして好適なフィルムを製造することができる。
　離型層形成組成物からなる塗布液を塗布する方法としては、例えば、エアドクターコート、ブレードコート、ロッドコート、バーコート、ナイフコート、スクイズコート、含浸コート、リバースロールコート、トランスファロールコート、グラビアコート、キスロールコート、キャストコート、スプレーコート、カーテンコート、カレンダコート、押出コート等従来公知の塗布方法を用いることができる。
　より具体的には、例えば、逐次二軸延伸においては、特に長手方向（縦方向）に延伸された一軸延伸フィルムに、離型層形成組成物からなる塗布液をコーティングした後に横方向に延伸してポリエステルフィルムを形成する方法が優れている。かかる方法によれば、ポリエステルフィルムの製膜と離型層の形成を同時に行うことができるため製造コスト上のメリットがあり、また、コーティング後に延伸を行うために、離型層の厚みを延伸倍率により変化させることもでき、オフラインコーティングに比べ、薄膜コーティングをより容易に行うことができる。
　また、延伸前にポリエステルフィルム上に離型層を設けることにより、離型層をポリエステルフィルムと共に延伸することができ、それにより離型層をポリエステルフィルムに強固に密着させることができる。さらに、二軸延伸ポリエステルフィルムの製造において、クリップ等によりフィルム端部を把持しつつ延伸することで、フィルムを縦および横方向に拘束することができ、熱固定工程において、しわ等が入らず平面性を維持したまま高温をかけることができる。
　それゆえ、コーティング後に施される熱処理が他の方法では達成されない高温とすることができるために、離型層の造膜性が向上し、離型層とポリエステルフィルムをより強固に密着させることができ、さらには、強固な離型層とすることができる。
　また、離型層は、オフラインコーティングあるいはインラインコーティングによる形成に係わらず、必要に応じて熱処理と紫外線照射等の活性エネルギー線照射とを併用してもよい。離型層を形成する塗布液のポリエステルフィルムへの塗布性、接着性を改良するため、塗布前にポリエステルフィルムに化学処理やコロナ放電処理、プラズマ処理、オゾン処理、薬品処理、溶剤処理等の表面処理を施してもよい。
　上記離型層形成組成物すなわち塗布液としては、離型剤及びバインダーを含有する樹脂組成物を挙げることができる。
　上記離型層形成組成物に配合する「離型剤」としては、特に制限はなく、従来公知の離型剤を使用することが可能である。例えば長鎖アルキル基含有化合物、フッ素化合物、シリコーン化合物、ワックス等を挙げることができる。
　中でも、光学用途に適用しても汚染の可能性が少ないという観点から長鎖アルキル基含有化合物、ワックスが好ましく、加熱しても剥離性が顕著に低下することがないという観点から、ワックスが好ましい。
　上記ワックスとしては、天然ワックス、合成ワックス、変性ワックスなどを挙げることができる。
　天然ワックスとは、植物系ワックス、動物系ワックス、鉱物系ワックス、石油ワックスである。
　植物系ワックスとしては、キャンデリラワックス、カルナウバワックス、ライスワックス、木ロウ、ホホバ油等が挙げられる。
　動物系ワックスとしては、みつろう、ラノリン、鯨ロウ等が挙げられる。鉱物系ワックスとしてはモンタンワックス、オゾケライト、セレシン等が挙げられる。
　石油ワックスとしてはパラフィンワックス、マイクロクリスタリンワックス、ペトロラタム等が挙げられる。
　合成ワックスとしては、例えば、合成炭化水素、変性ワックス、水素化ワックス、脂肪酸、酸アミド、アミン、イミド、エステル、ケトンやフィッシャー・トロプシュワックス（別名サゾールワックス）、ポリエチレンワックスなどを挙げることができる。このほかに比較的低分子量の高分子（具体的には数平均分子量５００から２００００の高分子）である以下のポリマー、すなわち、ポリプロピレン、エチレン・アクリル酸共重合体、ポリエチレングリコール、ポリプロピレングリコール、ポリエチレングリコールとポリプロピレングリコールのブロックまたはグラフト結合体等を挙げることができる。
　変性ワックスとしては、例えばモンタンワックス誘導体、パラフィンワックス誘導体、マイクロクリスタリンワックス誘導体等を挙げることができる。ここでの誘導体とは、精製、酸化、エステル化、ケン化のいずれかの処理、またはそれらの組み合わせによって得られる化合物である。水素化ワックスとしては硬化ひまし油、および硬化ひまし油誘導体を挙げることができる。
　中でも、ブロッキング等の特性が安定するという観点において、離型層における離型剤としては合成ワックスが好ましく、その中でもポリエチレンワックスがより好ましく、酸化ポリエチレンワックスがさらに好ましい。
　合成ワックスの数平均分子量は、ブロッキング等の特性の安定性、取扱い性の観点から、通常５００～３００００、好ましくは１０００～１５０００、より好ましくは２０００～８０００である。
　また、離型層を形成する際、架橋などのために加熱することを考慮すると、上記ワックスの中でも、融点または軟化点が８０℃以上、特に１１０℃以上のものが好ましい。ワックスの融点または軟化点の上限は限定されず、通常３００℃以下である。
　離型層形成組成物中の離型剤の割合は、不揮発成分中の１～５０質量％であるのが好ましく、中でも５質量％以上或いは４０質量％以下、その中でも１０質量％以上或いは３０質量％以下であるのがさらに好ましい。
　離型層形成組成物中の離型剤の割合が上記範囲であることにより、良好な離型性を維持しながら、塗膜強度を高めることができる。
　離型層の強度を上げるため、さらには濡れ性向上のため、離型層形成組成物には架橋剤を含有することが好ましい。離型層形成組成物に架橋剤を含有する場合、形成後の離型層は架橋剤に由来する架橋構造を有することになる。
　また、離型層の強度を上げため、さらにはポリエステルフィルム基材と離型層の密着性向上のため、離型層形成組成物にはバインダーを含有することが好ましい。
　前記架橋剤としては、従来公知の材料を使用することができる。例えばオキサゾリン化合物、イソシアネート系化合物、エポキシ化合物、メラミン化合物、カルボジイミド系化合物、シランカップリング化合物、ヒドラジド化合物、アジリジン化合物等が挙げられる。それらの中でも、オキサゾリン化合物、イソシアネート系化合物、エポキシ化合物、メラミン化合物、カルボジイミド系化合物、シランカップリング化合物が好ましい。より離型層の強度を強化するためには、メラミン化合物やオキサゾリン化合物が好ましく、基材のフィルムとの密着性を向上させるためには、オキサゾリン化合物、イソシアネート系化合物、エポキシ化合物、カルボジイミド系化合物が好ましく、特にオキサゾリン化合物やイソシアネート系化合物が好ましい。
　バインダーの具体例としては、アクリル樹脂、ポリビニル（ポリビニルアルコール、塩化ビニル酢酸ビニル共重合体等）、ポリエステル樹脂、ウレタン樹脂、ポリアルキレングリコール、ポリアルキレンイミン、メチルセルロース、ヒドロキシセルロース、でんぷん類等が挙げられる。これらの中でも、ポリエステルフィルム基材と離型層の密着性向上という観点において、ポリエステル樹脂が好ましい。
　前記アクリル樹脂とは、アクリル系、メタアクリル系のモノマーを含む重合性モノマーからなる重合体である。これらは、単独重合体あるいは共重合体、さらにはアクリル系、メタアクリル系のモノマー以外の重合性モノマーとの共重合体、いずれでも差し支えない。また、それら重合体と他のポリマー（例えばポリエステル、ポリウレタン等）との共重合体も含まれる。例えば、ブロック共重合体、グラフト共重合体である。あるいは、ポリエステル溶液、またはポリエステル分散液中で重合性モノマーを重合して得られたポリマー（場合によってはポリマーの混合物）も含まれる。同様にポリウレタン溶液、ポリウレタン分散液中で重合性モノマーを重合して得られたポリマー(場合によってはポリマーの混合物）も含まれる。同様にして他のポリマー溶液、または分散液中で重合性モノマーを重合して得られたポリマー（場合によってはポリマー混合物）も含まれる。また、基材との密着性をより向上させるために、ヒドロキシル基、アミノ基を含有することも可能である。
　上記重合性モノマーとしては、特に限定はしないが、特に代表的な化合物としては、例えば、アクリル酸、メタクリル酸、クロトン酸、イタコン酸、フマル酸、マレイン酸、シトラコン酸のような各種カルボキシル基含有モノマー類、およびそれらの塩；２－ヒドロキシエチル（メタ）アクリレート、２－ヒドロキシプロピル（メタ）アクリレート、４－ヒドロキシブチル（メタ）アクリレート、モノブチルヒドロキルフマレート、モノブチルヒドロキシイタコネートのような各種の水酸基含有モノマー類；メチル（メタ）アクリレート、エチル（メタ）アクリレート、プロピル（メタ）アクリレート、ブチル（メタ）アクリレート、ラウリル（メタ）アクリレートのような各種の（メタ）アクリル酸エステル類；（メタ）アクリルアミド、ジアセトンアクリルアミド、Ｎ－メチロールアクリルアミドまたは（メタ）アクリロニトリル等のような種々の窒素含有化合物；スチレン、α－メチルスチレン、ジビニルベンゼン、ビニルトルエンのような各種スチレン誘導体、プロピオン酸ビニルのような各種のビニルエステル類；γ－メタクリロキシプロピルトリメトキシシラン、ビニルトリメトキシシラン等のような種々の珪素含有重合性モノマー類；燐含有ビニル系モノマー類；塩化ビニル、塩化ビリデンのような各種のハロゲン化ビニル類；ブタジエンのような各種共役ジエン類が挙げられる。
　前記アクリル樹脂がヒドロキシル基を含有する場合、アクリル樹脂の水酸基価は、好ましくは２～１００ｍｇＫＯＨ／ｇ、より好ましくは５～５０ｍｇＫＯＨ／ｇである。水酸基価が上記範囲に入る場合は、塗布外観や透明性が良化する。
　前記ポリビニルアルコールとは、ポリビニルアルコール部位を有する化合物であり、例えば、ポリビニルアルコールに対し、部分的にアセタール化やブチラール化等された変成化合物も含め、従来公知のポリビニルアルコールを使用することができる。ポリビニルアルコールの重合度は特に限定されるものではないが、通常１００以上、好ましくは３００～４００００の範囲である。重合度が１００未満の場合、離型層の耐水性が低下する場合がある。また、ポリビニルアルコールのケン化度は特に限定されるものではないが、通常７０モル％以上、好ましくは７０～９９．９モル％の範囲、より好ましくは８０～９７モル％、特に好ましくは８６～９５モル％であるポリ酢酸ビニルケン化物が実用上用いられる。
　前記ポリエステル樹脂とは、主な構成成分として、例えば、下記のような多価カルボン酸および多価ヒドロキシ化合物からなるものが挙げられる。すなわち、多価カルボン酸としては、テレフタル酸、イソフタル酸、オルトフタル酸、フタル酸、４，４’－ジフェニルジカルボン酸、２，５－ナフタレンジカルボン酸、１，５－ナフタレンジカルボン酸および、２，６－ナフタレンジカルボン酸、２，７－ナフタレンジカルボン酸、１，４－シクロヘキサンジカルボン酸、２－カリウムスルホテレフタル酸、５－ソジウムスルホイソフタル酸、アジピン酸、アゼライン酸、セバシン酸、ドデカンジカルボン酸、グルタル酸、コハク酸、トリメリット酸、トリメシン酸、ピロメリット酸、無水トリメリット酸、無水フタル酸、ｐ－ヒドロキシ安息香酸、トリメリット酸モノカリウム塩およびそれらのエステル形成性誘導体などを用いることができ、多価ヒドロキシ化合物としては、エチレングリコール、１，２－プロピレングリコール、１，３－プロピレングリコール、１，３－プロパンジオ－ル、１，４－ブタンジオール、１，６－ヘキサンジオ－ル、２－メチル－１，５－ペンタンジオ－ル、ネオペンチルグリコール、１，４－シクロヘキサンジメタノ－ル、ｐ－キシリレングリコ－ル、ビスフェノ－ルＡ－エチレングリコ－ル付加物、ジエチレングリコール、トリエチレングリコール、ポリエチレングリコ－ル、ポリプロピレングリコ－ル、ポリテトラメチレングリコ－ル、ポリテトラメチレンオキシドグリコ－ル、ジメチロ－ルプロピオン酸、グリセリン、トリメチロ－ルプロパン、ジメチロ－ルエチルスルホン酸ナトリウム、ジメチロ－ルプロピオン酸カリウムなどを用いることができる。これらの化合物の中から、それぞれ適宜１つ以上を選択し、常法の重縮合反応によりポリエステル樹脂を合成すればよい。
　前記ウレタン樹脂とは、ウレタン結合を分子内に有する高分子化合物のことである。通常ウレタン樹脂はポリオールとイソシアネートの反応により作成される。ポリオールとしては、ポリカーボネートポリオール類、ポリエステルポリオール類、ポリエーテルポリオール類、ポリオレフィンポリオール類、アクリルポリオール類が挙げられ、これらの化合物は単独で用いても、複数種用いてもよい。
　前記ポリカーボネートポリオール類は、多価アルコール類とカーボネート化合物とから、脱アルコール反応によって得られる。多価アルコール類としては、エチレングリコール、１，２－プロピレングリコール、１，３－プロピレングリコール、１，２－ブタンジオール、１，３－ブタンジオール、１，４－ブタンジオール、１，５－ペンタンジオール、１，６－ヘキサンジオール、１，４－シクロヘキサンジオール、１，４－シクロヘキサンジメタノール、１，７－ヘプタンジオール、１，８－オクタンジオール、１，９－ノナンジオール、１，１０－デカンジオール、ネオペンチルグリコール、３－メチル－１，５－ペンタンジオール、３，３－ジメチロールヘプタン等が挙げられる。カーボネート化合物としては、ジメチルカーボネート、ジエチルカーボネート、ジフェニルカーボネート、エチレンカーボネート等が挙げられ、これらの反応から得られるポリカーボネート系ポリオール類としては、例えば、ポリ（１，６－ヘキシレン）カーボネート、ポリ（３－メチル－１，５－ペンチレン）カーボネート等が挙げられる。
　前記ポリエステルポリオール類としては、多価カルボン酸（マロン酸、コハク酸、グルタル酸、アジピン酸、ピメリン酸、スベリン酸、セバシン酸、フマル酸、マレイン酸、テレフタル酸、イソフタル酸等）またはそれらの酸無水物と多価アルコール（エチレングリコール、ジエチレングリコール、トリエチレングリコール、プロピレングリコール、ジプロピレングリコール、トリプロピレングリコール、ブタンジオール、１，３－ブタンジオール、１，４－ブタンジオール、２，３－ブタンジオール、２－メチル－１，３－プロパンジオール、１，５－ペンタンジオール、ネオペンチルグリコール、１，６－ヘキサンジオール、３－メチル－１，５－ペンタンジオール、２－メチル－２，４－ペンタンジオール、２－メチル－２－プロピル－１，３－プロパンジオール、１，８－オクタンジオール、２，２，４－トリメチル－１，３－ペンタンジオール、２－エチル－１，３－ヘキサンジオール、２，５－ジメチル－２，５－ヘキサンジオール、１，９－ノナンジオール、２－メチル－１，８－オクタンジオール、２－ブチル－２－エチル－１，３－プロパンジオール、２－ブチル－２－ヘキシル－１，３－プロパンジオール、シクロヘキサンジオール、ビスヒドロキシメチルシクロヘキサン、ジメタノールベンゼン、ビスヒドロキシエトキシベンゼン、アルキルジアルカノールアミン、ラクトンジオール等）の反応から得られるものが挙げられる。
　前記ポリエーテルポリオール類としては、ポリエチレングリコール、ポリプロピレングリコール、ポリエチレンプロピレングリコール、ポリテトラメチレンエーテルグリコール、ポリヘキサメチレンエーテルグリコール等が挙げられる。
　ウレタン樹脂を得るために使用されるポリイソシアネート化合物としては、トリレンジイソシアネート、キシリレンジイソシアネート、メチレンジフェニルジイソシアネート、フェニレンジイソシアネート、ナフタレンジイソシアネート、トリジンジイソシアネート等の芳香族ジイソシアネート、α，α，α’，α’－テトラメチルキシリレンジイソシアネート等の芳香環を有する脂肪族ジイソシアネート、メチレンジイソシアネート、プロピレンジイソシアネート、リジンジイソシアネート、トリメチルヘキサメチレンジイソシアネート、ヘキサメチレンジイソシアネート等の脂肪族ジイソシアネート、シクロヘキサンジイソシアネート、メチルシクロヘキサンジイソシアネート、イソホロンジイソシアネート、ジシクロヘキシルメタンジイソシアネート、イソプロピリデンジシクロヘキシルジイソシアネート等の脂環族ジイソシアネート等が例示される。これらは単独で用いても、複数種併用してもよい。
　ウレタン樹脂を合成する際に鎖延長剤を使用してもよく、鎖延長剤としては、イソシアネート基と反応する活性基を２個以上有するものであれば特に制限はなく、一般的には、水酸基またはアミノ基を２個有する鎖延長剤を主に用いることができる。
　水酸基を２個有する鎖延長剤としては、例えば、エチレングリコール、プロピレングリコール、ブタンジオール等の脂肪族グリコール、キシリレングリコール、ビスヒドロキシエトキシベンゼン等の芳香族グリコール、ネオペンチルグリコールヒドロキシピバレート等のエステルグリコールといったグリコール類を挙げることができる。また、アミノ基を２個有する鎖延長剤としては、例えば、トリレンジアミン、キシリレンジアミン、ジフェニルメタンジアミン等の芳香族ジアミン、エチレンジアミン、プロピレンジアミン、ヘキサンジアミン、２，２－ジメチル－１，３－プロパンジアミン、２－メチル－１，５－ペンタンジアミン、トリメチルヘキサンジアミン、２－ブチル－２－エチル－１，５－ペンタンジアミン、１ ，８－オクタンジアミン、１ ，９－ノナンジアミン、１ ，１０－デカンジアミン等の脂肪族ジアミン、１－アミノ－３－アミノメチル－３，５，５－トリメチルシクロヘキサン、ジシクロヘキシルメタンジアミン、イソプロピリデンシクロヘキシル－４，４’－ジアミン、１，４－ジアミノシクロヘキサン、１ ，３－ビスアミノメチルシクロヘキサン等の脂環族ジアミン等が挙げられる。
　本発明におけるウレタン樹脂は、溶剤を媒体とするものであってもよいが、好ましくは水を媒体とするものである。ウレタン樹脂を水に分散または溶解させるには、乳化剤を用いる強制乳化型、ウレタン樹脂中に親水性基を導入する自己乳化型あるいは水溶型等がある。特に、ウレタン樹脂の構造中にイオン基を導入しアイオノマー化した自己乳化タイプが、液の貯蔵安定性や得られる離型層の耐水性、透明性に優れており好ましい。
　また、導入するイオン基としては、カルボキシル基、スルホン酸、リン酸、ホスホン酸、第４級アンモニウム塩等、種々のものが挙げられるが、カルボキシル基が好ましい。ウレタン樹脂にカルボキシル基を導入する方法としては、重合反応の各段階の中で種々の方法が取り得る。
　例えば、プレポリマー合成時に、カルボキシル基を持つ樹脂を共重合成分として用いる方法や、ポリオールやポリイソシアネート、鎖延長剤などの一成分としてカルボキシル基を持つ成分を用いる方法がある。特に、カルボキシル基含有ジオールを用いて、この成分の仕込み量によって所望の量のカルボキシル基を導入する方法が好ましい。例えば、ウレタン樹脂の重合に用いるジオールに対して、ジメチロールプロピオン酸、ジメチロールブタン酸、ビス－（２－ヒドロキシエチル）プロピオン酸、ビス－（２－ヒドロキシエチル）ブタン酸等を共重合させることができる。またこのカルボキシル基はアンモニア、アミン、アルカリ金属類、無機アルカリ類等で中和した塩の形にするのが好ましい。特に好ましいものは、アンモニア、トリメチルアミン、トリエチルアミンである。かかるポリウレタン樹脂は、塗布後の乾燥工程において中和剤が外れたカルボキシル基を、他の架橋剤による架橋反応点として用いることができる。これにより、塗布前の液の状態での安定性に優れる上、得られる離型層の耐久性、耐溶剤性、耐水性、耐ブロッキング性等をさらに改善することが可能となる。
　離型層形成組成物中にバインダーが占める割合は、不揮発成分中の２０～７０質量％であるのが好ましく、中でも３０質量％以上或いは６５質量％以下、その中でも４０質量％以上或いは６０質量％以下であるのがさらに好ましい。
　架橋剤が占める割合は、不揮発成分中の１０～７０質量％であるのが好ましく、中でも１５質量％以上或いは６０質量％以下、その中でも２０質量％以上或いは４０質量％以下であるのがさらに好ましい。
　なお、離型層形成組成物からなる塗布液は、水を溶媒とする水性塗布液であっても有機溶剤を主成分とする塗布液であってもよいが、水性塗布液であることが好ましい。
　水性塗布液には、少量の有機溶剤を含有していてもよい。
　当該有機溶剤としては、エタノール、イソプロパノール、エチレングリコール、グリセリン等のアルコール類；エチルセロソルブ、ｔ－ブチルセロソルブ、プロピレングリコールモノメチルエーテル、テトラヒドロフラン等のエーテル類；アセトン、メチルエチルケトン等のケトン類；酢酸エチル等のエステル類；メチルエタノールアミン等のアミン類等を例示することができる。これらは単独、もしくは複数を組み合わせて用いることができる。水性塗布液に、必要に応じてこれらの有機溶剤を適宜選択し、含有させることで、塗布液の安定性、塗布性を良好にすることができる。
　上記離型層形成組成物には、必要に応じて、ブロッキングや滑り性改良のために、粒子を含有させることも可能である。さらに、機能層に、消泡剤、塗布性改良剤、増粘剤、有機系潤滑剤、紫外線吸収剤、酸化防止剤、発泡剤等を含有させることも可能である。
＜本ポリエステルフィルム１０＞
（厚み）
　本ポリエステルフィルム１０の厚みは、フィルムとして製膜可能な範囲であれば特に限定されるものではない。中でも、機械的強度、ハンドリング性および生産性などの点から、１μｍ～３００μｍであるのが好ましく、中でも５μｍ以上或いは１２５μｍ以下、その中でも８μｍ以上或いは１００μｍ以下であることがさらに好ましい。
（透過濃度ＯＤ値）
　本ポリエステルフィルム１０は、透過濃度ＯＤ値が０．１０以上であるのが好ましい。
　透過濃度ＯＤ値が０．１０以上であるということは、不透明さが大きい、言い換えれば白色度が大きいことを意味している。
　かかる観点から、本ポリエステルフィルム１０の透過濃度ＯＤ値は、０．１０～１．０であるのがより好ましく、中でも０．１５以上或いは０．９０以下、その中でも０．２０以上或いは０．８０以下、その中でも０．２５以上、その中でも０．３０以上、その中でも０．５０以上であるのがさらに好ましい。
　本ポリエステルフィルム１０の透過濃度ＯＤ値が上記範囲であれば、視認性言い換えれば識別性が良好であるので、転写対象物に粗面を転写後に、本ポリエステルフィルム１０を剥離することが容易となる。
　本ポリエステルフィルム１０の透過濃度ＯＤ値を０．１０以上にする方法としては、例えば、ポリエステルフィルム基材又はいずれかの層に白色顔料を含有させたり、ポリエステルフィルム基材の主成分樹脂との屈折率差が大きな材料を当該基材又は粒子含有層に含有させたり、微粒子を含有するフィルムを延伸してポリエステルフィルム基材中にボイドを形成させたりするなど、公知の方法を採用可能である。
　中でも、白色顔料、例えば金属化合物粒子を含有させて白色化を図る場合、例えば前記基材層、前記粒子含有層、前記基材層の前記粒子含有層とは反対側に設けた層のうちの何れかの層若しくはこれらのうちの２層以上に金属化合物粒子を含有させて白色化を図ることができる。この際、上記の白色顔料としては、前述の平均粒径２．０μｍ未満の粒子Ｙを例示することができる。
（フィルムの表面粗さ）
　本ポリエステルフィルム１０の平均表面粗さ（Ｒａ）は０．０５μｍ～２．０μｍであるのが好ましい。
　ここで、本ポリエステルフィルム１０の平均表面粗さ（Ｒａ）とは、ポリエステルフィルム基材の一方側に離型層を形成した場合はその表面を意味し、ポリエステルフィルム基材の両方の側にそれぞれ離型層を形成した場合はその両表面を意味する。
　本ポリエステルフィルム１０表面の平均表面粗さ（Ｒａ）が上記範囲であれば、マット感を表現することができ、この表面を、対象物にプレス圧着して離型させることで、対象物表面に当該マット感を付与することができる。
　かかる観点から、本ポリエステルフィルム１０の平均表面粗さ（Ｒａ）は０．０５μｍ～２．０μｍであるのが好ましく、中でも０．１μｍ以上或いは１．０μｍ以下、その中でも０．２μｍ以上或いは０．９μｍ以下であるのがさらに好ましい。
　本ポリエステルフィルム１０の平均表面粗さ（Ｒａ）は、表面粗さ測定器を用いて求めることができ、例えば、株式会社小坂研究所社製の表面粗さ測定機（ＳＥ－３５００）を用いて求めることができる。
　本ポリエステルフィルム１０の平均表面粗さ（Ｒａ）を０．１μｍ～２．０μｍとするには、例えば、粒子含有層Ａを設けてポリエステルフィルム基材の片方又は両方の表面の平均表面粗さ（Ｒａ）を０．１μｍ～２．０μｍとし、且つ、離型層の厚さを平均表面粗さ（Ｒａ）に対して十分に薄く形成すればよい。但し、この方法に限定するものではない。
　なお、本ポリエステルフィルム１０の一方側の表面をマット調とすれば、他方の表面は、ハンドリングに支障がない程度に粗面化していれば十分であり、マット調である必要はない。
　よって、ポリエステルフィルム基材の粒子含有層Ａ側、すなわち離型層側の表面の平均表面粗さ（Ｒａ）１を０．１μｍ～２．０μｍとし、反対側の本ポリエステルフィルム１０の表面の平均表面粗さ（Ｒａ）２を０．１μｍ未満とすることもできる。この際、上記（Ｒａ）１に対する（Ｒａ）２の比率は０．０１～１００％であるのが好ましく、中でも０．１％以上、その中でも１％以上、その中でも３％以上或いは９０％以下であるのがさらに好ましい。
（光沢度）
　本ポリエステルフィルム１０において、少なくとも離型層側表面の光沢度は３０％以下であるのが好ましい。
　フィルム表面の光沢度が３０％以下であれば、高級感のあるマット調とすることができる。但し、その下限は０．１％程度である。
　かかる観点から、本ポリエステルフィルム１０において、少なくとも離型層側表面の光沢度は３０％以下であるのが好ましく、中でも０．１％以上或いは３０％以下、その中でも２５％以下、その中でも２０％以下であるのがさらに好ましい。
　なお、本ポリエステルフィルム１０の離型層側表面の光沢度は、光沢度計を用いて測定することができ、例えば、日本電色株式会社製グロスメ－タ－ＶＧ２０００型を用いて、ＪＩＳ　Ｚ８７４１の方法に準じて光沢度を測定することができる。
　本ポリエステルフィルム１０において、少なくとも離型層側表面の光沢度を３０％以下とするには、上述のように、ポリエステルフィルム基材の片方又は両方の表面の平均表面粗さ（Ｒａ）を０．０５μｍ～２．０μｍとし、且つ、離型層の厚さを平均表面粗さ（Ｒａ）に対して十分に薄くすることにより、そのように形成することができる。但し、この方法に限定するものではない。
（離型層の剥離力）
　本ポリエステルフィルム１０において、離型層の剥離力は１００～３５００ｍＮ／ｃｍであるのが好ましく、中でも５００ｍＮ／ｃｍ以上或いは３０００ｍＮ／ｃｍ以下、その中でも１０００ｍＮ／ｃｍ以上或いは２５００ｍＮ／ｃｍ以下であるのがさらに好ましい。かかる範囲とすることで、剥離作業が容易なものとなる。なお、当該剥離力の値は、後述する「加熱前の離型層の剥離力」に相当する。
　加熱前の離型層の剥離力は、離型層表面に粘着テープ（日東電工株式会社製ポリエステル粘着テープ「Ｎｏ．３１Ｂ」）を２ｋｇゴムローラーにて１往復圧着し、室温にて１時間放置したものを株式会社島津製作所製「ＡＧＸ－ｐｌｕｓ」を使用し、引張速度３００ｍｍ／分の条件下、１８０°剥離を行うことで測定することができる。
　また、加熱後における離型層の剥離力は１００～４５００ｍＮ／ｃｍであるのが好ましく、中でも５００ｍＮ／ｃｍ以上或いは３９００ｍＮ／ｃｍ以下、その中でも１０００ｍＮ／ｃｍ以上或いは３５００ｍＮ／ｃｍ以下であるのがさらに好ましい。かかる範囲とすることで、加熱後でも剥離を十分に行うことができる。
　なお、加熱後における離型層の剥離力は、離型層表面に粘着テープ（日東電工株式会社製ポリエステル粘着テープ「Ｎｏ．３１Ｂ」）を２ｋｇゴムローラーにて１往復圧着したものを１００℃のオーブン内にて１時間加熱した後、室温にて１時間放置して測定することができる。剥離力は、株式会社島津製作所製「ＡＧＸ－ｐｌｕｓ」を使用し、引張速度３００ｍｍ／分の条件下、１８０°剥離を行うことで測定することができる。
　また、加熱前後での離型層の剥離力のコントロールのし易さを考慮すると、加熱前後の剥離力を比較し、加熱前後剥離力差＝（加熱後剥離力－加熱前剥離力）の値は、好ましくは０～３０００ｍＮ／ｃｍ、より好ましくは０～２０００ｍＮ／ｃｍ、さらに好ましくは０～１５００ｍＮ／ｃｍである。
＜本ポリエステルフィルム１又は１０の製造方法＞
　以下、本ポリエステルフィルム１０の製造方法の一例について説明する。但し、本ポリエステルフィルム１０の製造方法が、次に説明する方法に限定されるものではない。
　先ず、公知の手法により、乾燥又は未乾燥の各層毎、すなわち基材層、粒子含有層Ａ、粒子含有層Ｂ及びさらなる他の層毎にそれぞれの原料を調製し、それぞれ各溶融押出装置に供給し、それぞれのポリマーの融点以上である温度に加熱し溶融する。次いで、各層の溶融ポリマーを、通常マルチマニホールドまたはフィードブロックを経てダイへ導き積層する。
　次に、ダイから押出された溶融シートを、回転冷却ドラム上でガラス転移温度以下の温度になるように急冷固化し、実質的に非晶状態の未配向シートを得る。この場合、シートの平面性を向上させるため、シートと回転冷却ドラムとの密着性を高めることが好ましく、静電印加密着法および／または液体塗布密着法が好ましく採用される。
　次に、得られた未延伸シートを一方向にロールまたはテンター方式の延伸機により延伸する。延伸温度は、通常７０～１５０℃、好ましくは８０～１４０℃であり、延伸倍率は通常２．５～７倍、好ましくは３．０～６倍である。次いで、一段目の延伸方向と直交する方向に、通常７０～１７０℃で、延伸倍率は通常２．５～７倍、好ましくは３．０～６倍で延伸する。引き続き１８０～２７０℃の温度で緊張下または３０％以内の弛緩下で熱処理を行い、二軸配向フィルムを得る方法が挙げられる。上記の延伸においては、一方向の延伸を２段階以上で行う方法を採用することもできる。その場合、最終的に二方向の延伸倍率がそれぞれ上記範囲となるように行うのが好ましい。
　熱処理工程後は、熱処理の最高温度ゾーンおよび／または熱処理出口のクーリングゾーンにおいて、縦方向および／または横方向に２～２０％弛緩する方法が好ましい。また、必要に応じて再縦延伸、再横延伸を付加することも可能である。
　上記製造方法において、離型層は、上述した塗布延伸法として、上記縦延伸と横延伸の間に、上記「離型層形成組成物」をコーティング処理するのが好ましい。このようにすれば、延伸と同時に塗布が可能になると共に離型層の厚みを延伸倍率に応じて薄くすることができ、ポリエステルフィルムとして好適なフィルムを製造することができる。
　ポリエステルフィルム１に関して、上述したポリエステルフィルム１０におけるフィルム厚みを、ポリエステルフィルム１におけるフィルム厚みと読み替え、上述したポリエステルフィルム１０における透過濃度ＯＤ値を、上述したポリエステルフィルム１における透過濃度ＯＤ値と読み替え、上述したポリエステルフィルム１０における平均表面粗さ（Ｒａ）を、ポリエステルフィルム１における平均表面粗さ（Ｒａ）と読み替える。
　本ポリエステルフィルム１および本ポリエステルフィルム１０は、粗面化されたフィルム表面を有し、その表面状態を対象製品の表面へ転写することができるため、マット調の表面が必要な表面賦形用途に用いることができ、特に、電磁波シールド部材の表面賦形用フィルムとして好適に用いることができる。
＜語句の説明＞
　本明細書において「Ｘ～Ｙ」（Ｘ，Ｙは任意の数字）と表現する場合、特にことわらない限り「Ｘ以上Ｙ以下」の意と共に、「好ましくはＸより大きい」或いは「好ましくはＹより小さい」の意も包含する。
　また、「Ｘ以上」（Ｘは任意の数字）或いは「Ｙ以下」（Ｙは任意の数字）と表現した場合、「Ｘより大きいことが好ましい」或いは「Ｙ未満であることが好ましい」旨の意図も包含する。
　以下、本発明を下記実施例及び比較例に基づいてさらに詳述する。
　先ず、下記実施例及び比較例での各種物性の測定方法・評価方法について説明する。
　なお、実施例および比較例中「部」とあるのは「質量部」を示す。また、本発明で用いた測定法は次のとおりである。
（１）ポリエステルの極限粘度
　ポリエステルに非相溶な粒子を除去したポリエステル１ｇを精秤し、フェノール／テトラクロロエタン＝５０／５０（質量比）の混合溶媒１００ｍｌを加えて溶解させ、３０℃で測定した。
（２）粒子の平均粒径
　株式会社島津製作所社製の遠心沈降式粒度分布測定装置、ＳＡ－ＣＰ３型を用いて沈降法によって粒子の大きさを測定した。測定により得られた粒子の等価球形分布における積算（体積基準）５０％の値を用いて平均粒径とした。
（３）平均表面粗さ（Ｒａ）の測定方法
　株式会社小坂研究所社製表面粗さ測定機（ＳＥ－３５００）を用いて次のようにして求めた。すなわち、フィルム断面曲線からその平均線の方向に基準長さＬ（２．５ｍｍ）の部分を抜き取り、この抜き取り部分の平均線をｘ軸、縦倍率の方向をｙ軸として粗さ曲線 ｙ＝ｆ（ｘ）で表わしたとき、次の式で与えられた値を〔ｎｍ〕で表わす。算術平均粗さは、試料フィルム表面から１０本の粗さ曲線を求め、これらの粗さ曲線から求めた抜き取り部分の算術平均粗さの平均値で表わした。なお、触針の先端半径は２μｍ、荷重は３０ｍｇとし、カットオフ値は０．０８ｍｍとした。
　Ｒａ＝（１／Ｌ）∫Ｌ０｜ｆ（ｘ）｜ｄｘ
（４）ポリエステルフィルムの光沢度評価
　日本電色（株）社製グロスメーターＶＧ２０００型を用いて、ＪＩＳ　Ｚ８７４１の方法に準じて光沢度を測定した。入射角、反射角６０度に於ける黒色標準板の反射率を基準に試料の反射率を求め光沢度とした。
（５）離型層の膜厚
　離型層の表面をＲｕＯ４で染色し、エポキシ樹脂中に包埋した。その後、超薄切片法により作成した切片をＲｕＯ４で染色し、離型層の断面を透過型電子顕微鏡（株式会社日立ハイテクノロジーズ製　Ｈ－７６５０、加速電圧１００ｋＶ）を用いて測定した。
（６）透過濃度ＯＤ値
　ＪＩＳ　Ｋ５６００－４に準じて、マクベス濃度計ＴＤ－９０４型を使用し、白色光による透過濃度を測定した。測定は５点行い、その平均値をＯＤ値とした。この値が大きい程光線透過率が低いことを示す。
（７）加熱前剥離力
　離型層表面に粘着テープ（日東電工株式会社製ポリエステル粘着テープ「Ｎｏ．３１Ｂ」）を２ｋｇゴムローラーにて１往復圧着し、室温にて１時間放置後の剥離力を測定した。剥離力は、株式会社島津製作所製「ＡＧＸ－ｐｌｕｓ」を使用し、引張速度３００ｍｍ／分の条件下、１８０°剥離を行い、その時の剥離力を測定した。
（８）加熱後剥離力
　離型層表面に粘着テープ（日東電工株式会社製ポリエステル粘着テープ「Ｎｏ．３１Ｂ」）を２ｋｇゴムローラーにて１往復圧着した後、１００℃のオーブン内にて１時間加熱した。その後、室温にて１時間放置後の剥離力を測定した。剥離力は、株式会社島津製作所製「ＡＧＸ－ｐｌｕｓ」を使用し、引張速度３００ｍｍ／分の条件下、１８０°剥離を行った。
（９）離型層の耐熱性の評価
　上記（７）および（８）で測定した剥離力を用いて、加熱剥離力差＝（加熱後剥離力－加熱前剥離力）として、加熱剥離力差を計算した。
（１０）離型層の強度の評価
　離型層表面を太平理化工業製ラビングテスターおよび専用フェルトを用いて１０往復した後にフェルトを観察し、白粉が見られなかったものを○（very　good）、わずかに見られたものを○△（good）、やや見られたものを△（usual）、全面に見られたものを×（poor）とした。　
（１１）カール性の評価
　フィルムロールの状態で、室温環境下に２４時間保管したポリエステルフィルム（サンプル）を、１５０ｍｍ×１５０ｍｍに切り出して測定サンプル片を得た。該測定サンプル片をガラス板上に置き、ガラス板からの四隅の浮き上がりを測定し、以下の基準でカール性を評価した。
　　　◎(very　good)：四隅の浮き上がりの平均値が０ｍｍ以上６ｍｍ未満
　　　○(good)：四隅の浮き上がりの平均値が６ｍｍ以上１０ｍｍ未満
　　　△(usual)：四隅の浮き上がりの平均値が１０ｍｍ以上３０ｍｍ未満
　　　×(poor)：四隅の浮き上がりの平均値が３０ｍｍ以上
　実施例および比較例において使用したポリエステルは、以下のようにして準備したものである。
＜ポリエステル（Ａ）＞
　ポリエチレンテレフタレートホモポリマー（極限粘度が０．６５ｄｌ／ｇ）
＜ポリエステル（Ｂ）＞
　平均粒径４．５μｍのメタクリル酸アルキル－スチレン共重合体の架橋有機粒子を１０質量％含有するポリエチレンテレフタレートホモポリマー
＜ポリエステル（Ｃ）＞
　ジカルボン酸成分としてイソフタル酸が２２モル％共重合された共重合ポリエチレンテレフタレート
＜ポリエステル（Ｄ）＞
　平均粒径４．０μｍのシリカ粒子を１５質量％含有するポリエチレンテレフタレートホモポリマー
＜ポリエステル（Ｅ）＞
　平均粒径１．５μｍのシリカ粒子を１５質量％含有するポリエチレンテレフタレートホモポリマー
＜ポリエステル（Ｆ）＞
　平均粒径０．３μｍの酸化チタン粒子を５０質量％含有するポリエチレンテレフタレートホモポリマー
　離型層の形成に用いた化合物は以下のとおりである。
＜ワックスエマルション（ＩＡ）＞
　攪拌機、温度計、温度コントローラーを備えた内容量１．５Ｌの乳化設備に融点１４０℃の酸化ポリエチレンワックス３００ｇ、イオン交換水６５０ｇとデカグリセリンモノオレエート界面活性剤を５０ｇ、４８％水酸化カリウム水溶液１０ｇを加え窒素で置換後、密封し１５０℃で１時間高速攪拌した後１３０℃に冷却し、高圧ホモジナイザーを４００気圧下で通過させ４０℃に冷却してワックスエマルション（ＩＡ）を得た。
＜ワックスエマルション（ＩＢ）＞
　ワックスエマルション（ＩＡ）の製造方法において、融点６０℃のパラフィンワックスを使用すること以外はワックスエマルション（ＩＡ）の製造方法と同様の方法を用いてワックスエマルション（ＩＢ）を得た。
＜長鎖アルキル化合物（ＩＣ）＞
　４つ口フラスコにキシレン２００部、オクタデシルイソシアネート６００部を加え、攪拌下に加熱した。キシレンが還流し始めた時点から、平均重合度５００、ケン化度８８モル％のポリビニルアルコール１００部を少量ずつ１０分間隔で約２時間にわたって加えた。ポリビニルアルコールを加え終わってから、さらに２時間還流を行い、反応を終了した。反応混合物を約８０℃まで冷却してから、メタノール中に加えたところ、反応生成物が白色沈殿として析出したので、この沈殿を濾別し、キシレン１４０部を加え、加熱して完全に溶解させた後、再びメタノールを加えて沈殿させるという操作を数回繰り返した後、沈殿をメタノールで洗浄し、乾燥粉砕して長鎖アルキル化合物（ＩＣ）を得た。
＜フッ素化合物（ＩＤ）＞
　ガラス製反応容器中に、パーフルオロアルキル基含有アクリレートであるＣＦ３（ＣＦ２）ｎＣＨ２ＣＨ２ＯＣＯＣＨ＝ＣＨ２（ｎ＝５～１１、ｎの平均＝９）８０．０ｇ、アセトアセトキシエチルメタクリレート２０．０ｇ、ドデシルメルカプタン０．８ｇ、脱酸素した純水３５４．７ｇ、アセトン４０．０ｇ、Ｃ１６Ｈ３３Ｎ（ＣＨ３）３Ｃｌ１．０ｇおよびＣ８Ｈ１７Ｃ６Ｈ４Ｏ（ＣＨ２ＣＨ２Ｏ）ｎＨ（ｎ＝８）３．０ｇを入れ、アゾビスイソブチルアミジン二塩酸塩０．５ｇを加え、窒素雰囲気下で攪拌しつつ６０℃で１０時間共重合反応させて、フッ素化合物の共重合体エマルション（ＩＤ）を得た。
＜メラミン化合物（IIＡ）＞
　ヘキサメトキシメチロールメラミン
＜イソシアネート系化合物（IIＢ）＞
　ヘキサメチレンジイソシアネート１０００部を６０℃で攪拌し、触媒としてテトラメチルアンモニウム・カプリエート０．１部を加えた。４時間後、リン酸０．２部を添加して反応を停止させ、イソシアヌレート型ポリイソシアネート組成物を得た。得られたイソシアヌレート型ポリイソシアネート組成物１００部、数平均分子量４００のメトキシポリエチレングリコール４２．３部、プロピレングリコールモノメチルエーテルアセテート２９．５部を仕込み、８０℃で７時間保持した。その後反応液温度を６０℃に保持し、イソブタノイル酢酸メチル３５．８部、マロン酸ジエチル３２．２部、ナトリウムメトキシドの２８％メタノール溶液０．８８部を添加し、４時間保持した。ｎ－ブタノール５８．９部を添加し、反応液温度８０℃で２時間保持し、その後、２－エチルヘキシルアシッドホスフェート０．８６部を添加してブロックポリイソシアネートとしてのイソシアネート系化合物（IIＢ）を得た。
＜ポリエステル樹脂（III）＞
　（酸成分）テレフタル酸／イソフタル酸／５－ソジウムスルホイソフタル酸／／（ジオール成分）エチレングリコール／１，４－ブタンジオール／ジエチレングリコール＝５６／４０／４／／７０／２０／１０（モル％）の割合で共重合したポリエステル樹脂の水分散体。
[実施例１]
　ポリエステル（Ｂ）、（Ｃ）をそれぞれ８０％、２０％の質量割合で混合した原料をＡ層（粒子含有層Ａ）の原料とし、ポリエステル（Ａ）を基材層の原料とし、ポリエステル（Ａ）、（Ｅ）、（Ｆ）をそれぞれ７０％、１５％、１５％の質量割合で混合した原料をＢ層（粒子含有層Ｂ）の原料とし、３台の押出機に各々を供給し、各々２８５℃で溶融した後、３５℃に設定した冷却ロール上に、３種３層（Ａ層／基材層／Ｂ層＝５：４０：５の吐出量）の層構成で共押出し、冷却固化させて未延伸シートを得た。次いで、ロール周速差を利用してフィルム温度８５℃で縦方向に３．０倍延伸した後、この縦延伸フィルムのＡ層表面に、下記表１に示す塗布液１を塗布し、テンターに導き、横方向に９５℃で４．１倍延伸し、２３５℃で熱処理を行った後、横方向に２％弛緩し、厚さ５０μｍ（Ａ層／基材層／Ｂ層＝５μｍ／４０μｍ／５μｍ）のポリエステルフィルム基材のＡ層側に、乾燥後の膜厚が０．０３μｍの離型層を有し、離型層側表面の平均表面粗さ（Ｒａ）が０．６μｍのポリエステルフィルム（サンプル）を得た。
　このポリエステルフィルム（サンプル）の特性を下記表２に示す。
[実施例２～１２]
　塗布液の組成を表１に示す組成に変更した以外は、実施例１と同様に製造して、ポリエステルフィルム（サンプル）を得た。得られたポリエステルフィルム（サンプル）の特性を表２に示す。
　いずれの実施例のポリエステルフィルム（サンプル）も、平均表面粗さ（Ｒａ）及び光沢度が良好であり、加熱前後の剥離力差、離型層の強度も良好であった。
[実施例１３]
　ポリエステル（Ａ）、（Ｂ）、（Ｃ）、（Ｆ）をそれぞれ６５％、１０％、１０％、１５％の質量割合で混合した原料をＢ層（粒子含有層Ｂ）の原料とし、塗布液１の代わりに下記表１に示す塗布液５を塗布した以外は実施例１と同様に製造して、厚さ５０μｍ（Ａ層／基材層／Ｂ層＝５μｍ／４０μｍ／５μｍ）のポリエステルフィルム基材のＡ層側に、乾燥後の膜厚が０．０３μｍの離型層を有し、離型層側表面の平均表面粗さ（Ｒａ）が０．６μｍのポリエステルフィルム（サンプル）を得た。
　このポリエステルフィルム（サンプル）の特性を下記表３に示す。
[実施例１４]
　ポリエステル（Ａ）、（Ｄ）をそれぞれ６５％、３５％の質量割合で混合した原料をＡ層（粒子含有層Ａ）の原料とし、ポリエステル（Ａ）を基材層の原料とし、ポリエステル（Ａ）、（Ｅ）をそれぞれ８５％、１５％の割合で混合した混合原料をＢ層（粒子含有層Ｂ）の原料とし、３台の押出機に各々を供給し、各々２８５℃で溶融した後、４０℃に設定した冷却ロール上に、３種３層（Ａ層／基材層／Ｂ層＝５：４０：５の吐出量）の層構成で共押出し、冷却固化させて未延伸シートを得た以外は実施例１と同様に製造して、厚さ５０μｍ（Ａ層／基材層／Ｂ層＝５μｍ／４０μｍ／５μｍ）のポリエステルフィルム基材のＡ層側に、乾燥後の膜厚が０．０３μｍの離型層を有し、離型層側表面の平均表面粗さ（Ｒａ）が０．４μｍのポリエステルフィルム（サンプル）を得た。
　このポリエステルフィルム（サンプル）の特性を下記表２に示す。
[実施例１５～２５]
　塗布液の組成を表１に示す組成に変更した以外は、実施例１４と同様に製造して、ポリエステルフィルム（サンプル）を得た。得られたポリエステルフィルム（サンプル）の特性を表２に示す。
　いずれの実施例のポリエステルフィルム（サンプル）も、平均表面粗さ（Ｒａ）及び光沢度が良好であり、加熱前後の剥離力差、離型層の強度も良好であった。
[比較例３]
　ポリエステル（Ａ）、（Ｅ）をそれぞれ６５％、３５％の質量割合で混合した原料をＡ層（粒子含有層Ａ）の原料とし、ポリエステル（Ａ）を基材層の原料とし、塗布液１の代わりに下記表１に示す塗布液５を塗布した以外は実施例１４と同様に製造して、厚さ５０μｍ（Ａ層／基材層／Ｂ層＝５μｍ／４０μｍ／５μｍ）のポリエステルフィルム基材のＡ層側に、乾燥後の膜厚が０．０３μｍの離型層を有し、離型層側表面の平均表面粗さ（Ｒａ）が０．２μｍのポリエステルフィルム（サンプル）を得た。
　このポリエステルフィルム（サンプル）の特性を下記表２および３に示す通り、光沢度が高く、視認性が悪いフィルムであった。
［比較例４］
ポリエステル（Ａ）、（Ｂ）をそれぞれ２０％、８０％の質量割合で混合した原料をＡ層（粒子含有層Ａ）の原料とし、ポリエステル（Ａ）、（Ｂ）（Ｆ）をそれぞれ９０％、８％、２％の質量割合で混合した原料をＢ層（粒子含有層Ｂ）の原料とし、２台の押出機に各々を供給し、各々２８５℃で溶融した後、４０℃に設定した冷却ロール上に、２種２層（Ａ層／Ｂ層＝５：４５の吐出量）の層構成で共押出し、冷却固化させて未延伸シートを得た以外は実施例１と同様に製造して、厚さ５０μｍ（Ａ層／Ｂ層＝５μｍ／４５μｍ）のポリエステルフィルム基材のＡ層側に、乾燥後の膜厚が０．０３μｍの離型層を有し、離型層側表面の平均表面粗さ（Ｒａ）が０．５μｍのポリエステルフィルム（サンプル）を得た。
　このポリエステルフィルム（サンプル）の特性を下記表３に示す通り、カール性が悪いフィルムであった。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
Figure JPOXMLDOC01-appb-T000003
　上記表２は本発明の第１および第２のポリエステルフィルムを実証するものであり、上記表３は本発明の第３のポリエステルフィルムを実証するものである。
　上記実施例の結果並びに本発明者がこれまでに行ってきた試験結果から、ポリエステルフィルムの透過濃度ＯＤ値が０．１０以上であれば、転写時のポリエステルフィルムの視認性に優れたものとすることができることが分かった。
　また、基材層の片面側又は両面側に、平均粒径２．０μｍ以上の粒子を含有する粒子含有層を形成し、さらに当該粒子含有層表面に離型層を形成するようにすれば、ポリエステルフィルム表面を好適に粗面化することができ、期待するマット感を対象物に転写することができることが分かった。
　本ポリエステルフィルム１０は、転写時の視認性言い換えれば識別性に優れ、かつ粗面化されたフィルム表面を有するため、離型層を形成しても、前記粗面化状態が平滑化されることなく、期待するマット感を対象物に付与することができるため、マット調表面を対象物に転写する用途、特に電磁波シールド部材の表面賦形用ポリエステルフィルムに好適に用いることができる。
１：ポリエステルフィルム
１１：ポリエステルフィルム基材
１１１：基材層
１１２：粒子含有層Ａ
１１３：離型層

Claims (15)

  1. 　平均粒径２．０μｍ以上の粒子を含有する粒子含有層を備えたポリエステルフィルム基材を有し、透過濃度ＯＤ値が０．２５以上であることを特徴とするポリエステルフィルム。
  2. 　基材層の片面に、平均粒径２．０μｍ以上の粒子を含有する粒子含有層Ａを備え、基材層の他方の片面に、平均粒径２．０μｍ以上の粒子を含有する粒子含有層Ｂを備えたポリエステルフィルム基材を有し、平均粒径２．０μｍ以上の粒子の含有量は、粒子含有層Ａよりも粒子含有層Ｂの方が少ないことを特徴とするポリエステルフィルム。
  3. 　前記ポリエステルフィルムは、透過濃度ＯＤ値が０．１０以上であることを特徴とする請求項２に記載のポリエステルフィルム。
  4. 　前記ポリエステルフィルム基材は、平均粒径２．０μｍ以上の粒子を含有する粒子含有層のみからなるものであることを特徴とする請求項１に記載のポリエステルフィルム。
  5. 　前記粒子含有層のうち少なくとも１つの表面に離型層を備えることを特徴とする請求項１又は４に記載のポリエステルフィルム。
  6. 　前記粒子含有層Ａ表面に離型層を備えることを特徴とする請求項２又は３に記載のポリエステルフィルム。
  7. 　前記離型層側表面の光沢度が３０％以下であることを特徴とする請求項５又は６に記載のポリエステルフィルム。
  8. 　前記離型層側表面の平均表面粗さ（Ｒａ）が０．１μｍ～２．０μｍであることを特徴とする請求項５～７の何れかに記載のポリエステルフィルム。
  9. 　平均粒径２．０μｍ以上の前記粒子が有機粒子であることを特徴とする請求項１～８の何れかに記載のポリエステルフィルム。
  10. 　平均粒径２．０μｍ以上の前記粒子がシリカ粒子であることを特徴とする請求項１～８の何れかに記載のポリエステルフィルム。
  11. 　前記粒子含有層が、金属化合物粒子を含有することを特徴とする請求項１、４および５の何れかにに記載のポリエステルフィルム。
  12. 　前記基材層、前記粒子含有層Ａ及び前記粒子含有層Ｂのうちの何れかの層又はこれらのうちの２層以上が、金属化合物粒子を含有することを特徴とする請求項２、３および６の何れかに記載のポリエステルフィルム。
  13. 　前記離型層は、離型剤を含有することを特徴とする請求項５～８の何れかに記載のポリエステルフィルム。
  14. 　前記離型層は、架橋剤由来の架橋構造を有することを特徴とする請求項５～８及び１３の何れかに記載のポリエステルフィルム。
  15. 　平均粒径２．０μｍ以上の粒子を含有する粒子含有層を備えた、透過濃度ＯＤ値が０．１０以上である電磁波シールド部材の表面賦形用ポリエステルフィルム。
PCT/JP2019/007506 2018-02-27 2019-02-27 ポリエステルフィルム WO2019168008A1 (ja)