WO2015020083A1 - Dispositif d'affichage à cristaux liquides et agent d'alignement de cristaux liquides - Google Patents

Dispositif d'affichage à cristaux liquides et agent d'alignement de cristaux liquides Download PDF

Info

Publication number
WO2015020083A1
WO2015020083A1 PCT/JP2014/070713 JP2014070713W WO2015020083A1 WO 2015020083 A1 WO2015020083 A1 WO 2015020083A1 JP 2014070713 W JP2014070713 W JP 2014070713W WO 2015020083 A1 WO2015020083 A1 WO 2015020083A1
Authority
WO
WIPO (PCT)
Prior art keywords
liquid crystal
alignment film
crystal display
display device
polyorganosiloxane
Prior art date
Application number
PCT/JP2014/070713
Other languages
English (en)
Japanese (ja)
Inventor
博之 箱井
寺岡　優子
中田　正一
拓巳 的場
美智子 石川
Original Assignee
シャープ株式会社
Jsr株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by シャープ株式会社, Jsr株式会社 filed Critical シャープ株式会社
Publication of WO2015020083A1 publication Critical patent/WO2015020083A1/fr

Abstract

La présente invention concerne un dispositif d'affichage à cristaux liquides comprenant un film d'alignement ayant une excellente résistance/force de régulation d'uniformité d'alignement et un excellent taux de retention de tension, ainsi que d'excellentes propriétés d'impression, et un agent d'alignement de cristaux liquides par le biais duquel un tel film d'alignement peut être produit. Ce dispositif d'affichage à cristaux liquides présente une paire de substrats, une couche de cristaux liquides prise en sandwich entre la paire de substrats, et un film d'alignement disposé entre la couche de cristaux liquides et au moins l'un de la paire de substrats, le film d'alignement contenant un premier composant et un deuxième composant, le premier composant comprenant un produit de réaction d'un polyorganosiloxane ayant des groupe epoxy et un composé représenté par la formule (1) et un composé représenté par la formule (2), et le deuxième composant compernant un acide polyamique ou un polyamide. (1): R1-R2-COO-C6H4-CH=CH-COOH; (2): R3-C6H4-COO-C6H4-CH=CH-COOH (Dans la formule (1), R1 représente un groupe alkyle en C4-20, et R2 représente un groupe obtenu lorsque deux atomes d'hydrogène sont perdus d'un hydrocarbure alicyclique en C6-10. Dans la formule (2), R<sp /> représente un groupe contenant du fluor en C1-20.)　
PCT/JP2014/070713 2013-08-07 2014-08-06 Dispositif d'affichage à cristaux liquides et agent d'alignement de cristaux liquides WO2015020083A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013164553A JP2016173380A (ja) 2013-08-07 2013-08-07 液晶表示装置及び液晶配向剤
JP2013-164553 2013-08-07

Publications (1)

Publication Number Publication Date
WO2015020083A1 true WO2015020083A1 (fr) 2015-02-12

Family

ID=52461414

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/070713 WO2015020083A1 (fr) 2013-08-07 2014-08-06 Dispositif d'affichage à cristaux liquides et agent d'alignement de cristaux liquides

Country Status (2)

Country Link
JP (1) JP2016173380A (fr)
WO (1) WO2015020083A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017063301A1 (fr) * 2015-10-13 2017-04-20 深圳市华星光电技术有限公司 Panneau à cristaux liquides et son procédé de fabrication
WO2017094490A1 (fr) * 2015-12-01 2017-06-08 富士フイルム株式会社 Appareil d'affichage à cristaux liquides et procédé de fabrication d'appareil d'affichage à cristaux liquides
WO2018008485A1 (fr) * 2016-07-05 2018-01-11 シャープ株式会社 Dispositif de traitement de photo-alignement pour substrat de panneau d'affichage à cristaux liquides, et procédé de fabrication de panneau d'affichage à cristaux liquides
WO2018216769A1 (fr) * 2017-05-25 2018-11-29 シャープ株式会社 Composition et dispositif d'affichage à cristaux liquides
CN110998425A (zh) * 2017-08-22 2020-04-10 夏普株式会社 液晶显示面板和液晶显示面板的制造方法
WO2023224114A1 (fr) * 2022-05-20 2023-11-23 日産化学株式会社 Agent d'alignment de cristaux liquides, film d'alignment de cristaux liquides et élément d'affichage à cristaux liquides

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102547116B1 (ko) * 2017-03-27 2023-06-23 닛산 가가쿠 가부시키가이샤 경화막 형성 조성물, 배향재 및 위상차재

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010140010A (ja) * 2008-11-17 2010-06-24 Jsr Corp 液晶配向剤、液晶配向膜およびその形成方法ならびに液晶表示素子
WO2012056947A1 (fr) * 2010-10-26 2012-05-03 シャープ株式会社 Panneau d'affichage à cristaux liquides, affichage à cristaux liquides, et polymère pour matériau de film d'alignement

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010140010A (ja) * 2008-11-17 2010-06-24 Jsr Corp 液晶配向剤、液晶配向膜およびその形成方法ならびに液晶表示素子
WO2012056947A1 (fr) * 2010-10-26 2012-05-03 シャープ株式会社 Panneau d'affichage à cristaux liquides, affichage à cristaux liquides, et polymère pour matériau de film d'alignement

Cited By (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017063301A1 (fr) * 2015-10-13 2017-04-20 深圳市华星光电技术有限公司 Panneau à cristaux liquides et son procédé de fabrication
WO2017094490A1 (fr) * 2015-12-01 2017-06-08 富士フイルム株式会社 Appareil d'affichage à cristaux liquides et procédé de fabrication d'appareil d'affichage à cristaux liquides
JP2017102258A (ja) * 2015-12-01 2017-06-08 富士フイルム株式会社 液晶表示装置および液晶表示装置の製造方法
TWI703373B (zh) * 2015-12-01 2020-09-01 日商富士軟片股份有限公司 液晶顯示裝置及液晶顯示裝置的製造方法
CN108351558A (zh) * 2015-12-01 2018-07-31 富士胶片株式会社 液晶显示装置及液晶显示装置的制造方法
KR102061587B1 (ko) 2015-12-01 2020-01-02 후지필름 가부시키가이샤 액정 표시 장치 및 액정 표시 장치의 제조 방법
US20190324302A1 (en) * 2016-07-05 2019-10-24 Sharp Kabushiki Kaisha Photo-alignment treatment device for liquid crystal display panel substrate, and liquid crystal display panel manufacturing method
WO2018008485A1 (fr) * 2016-07-05 2018-01-11 シャープ株式会社 Dispositif de traitement de photo-alignement pour substrat de panneau d'affichage à cristaux liquides, et procédé de fabrication de panneau d'affichage à cristaux liquides
US10884269B2 (en) 2016-07-05 2021-01-05 Sharp Kabushiki Kaisha Method for manufacturing a liquid crystal display panel comprising performing a photo-alignment treatment using a photo-alignment treatment device having a light irradiation mechanism and a rotation adjustment mechanism
WO2018216769A1 (fr) * 2017-05-25 2018-11-29 シャープ株式会社 Composition et dispositif d'affichage à cristaux liquides
CN110662807A (zh) * 2017-05-25 2020-01-07 夏普株式会社 组合物及液晶显示装置
US11634637B2 (en) 2017-05-25 2023-04-25 Sharp Kabushiki Kaisha Composition and liquid crystal display device
CN110998425A (zh) * 2017-08-22 2020-04-10 夏普株式会社 液晶显示面板和液晶显示面板的制造方法
WO2023224114A1 (fr) * 2022-05-20 2023-11-23 日産化学株式会社 Agent d'alignment de cristaux liquides, film d'alignment de cristaux liquides et élément d'affichage à cristaux liquides

Also Published As

Publication number Publication date
JP2016173380A (ja) 2016-09-29

Similar Documents

Publication Publication Date Title
JP5492516B2 (ja) 液晶表示装置
WO2015020083A1 (fr) Dispositif d&#39;affichage à cristaux liquides et agent d&#39;alignement de cristaux liquides
JP4944217B2 (ja) 液晶表示装置
TWI457666B (zh) Liquid crystal aligning agent and liquid crystal display element
JP5477572B2 (ja) 液晶配向剤および液晶配向膜の形成方法
TWI567109B (zh) 液晶配向劑、液晶配向膜、液晶顯示元件、相位差膜及其製造方法、聚合物以及化合物
JP5773116B2 (ja) 液晶配向剤および液晶表示素子
CN112210390B (zh) 液晶取向剂、液晶取向膜、液晶取向膜的制造方法、液晶显示元件、聚合物及化合物
TWI582503B (zh) 液晶配向劑、液晶配向膜及其製造方法、液晶顯示元件
WO2011155413A1 (fr) Dispositif d&#39;affichage à cristaux liquides
WO2012029591A1 (fr) Panneau d&#39;affichage à cristaux liquides, dispositif d&#39;affichage à cristaux liquides et polymère pour matériau de film d&#39;alignement
JP6507937B2 (ja) 液晶配向剤、液晶配向膜及びその製造方法、液晶表示素子、並びに位相差フィルム及びその製造方法
KR102025168B1 (ko) 액정 디스플레이 장치 및 그의 제조 방법
TWI633375B (zh) 液晶配向劑、液晶配向膜及其製造方法、液晶顯示元件、相位差膜及其製造方法、聚合物以及化合物
JP6492509B2 (ja) 液晶配向剤、液晶配向膜、液晶表示素子及び液晶表示素子の製造方法
TWI541270B (zh) 液晶配向劑、液晶配向膜、液晶顯示元件以及液晶配向膜的製造方法
JP2016004271A (ja) 液晶配向剤、液晶配向膜および液晶表示素子
JP2007047762A (ja) 垂直液晶配向剤
WO2012029589A1 (fr) Panneau d&#39;affichage à cristaux liquides, dispositif d&#39;affichage à cristaux liquides et polymère pour matériau de couche d&#39;alignement
JP5041157B2 (ja) 垂直配向型液晶配向剤および垂直配向型液晶表示素子
JP5879861B2 (ja) 液晶配向膜の形成方法
WO2012056947A1 (fr) Panneau d&#39;affichage à cristaux liquides, affichage à cristaux liquides, et polymère pour matériau de film d&#39;alignement
JP5181066B2 (ja) 配向制御膜
CN106947498B (zh) 液晶取向剂、液晶取向膜、液晶元件、以及液晶取向膜及液晶元件的制造方法
JP4788890B2 (ja) 液晶配向剤および液晶表示素子

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14833851

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

NENP Non-entry into the national phase

Ref country code: JP

122 Ep: pct application non-entry in european phase

Ref document number: 14833851

Country of ref document: EP

Kind code of ref document: A1