WO2014156464A1 - リチウムイオン二次電池電極用シートの製造方法 - Google Patents

リチウムイオン二次電池電極用シートの製造方法 Download PDF

Info

Publication number
WO2014156464A1
WO2014156464A1 PCT/JP2014/055024 JP2014055024W WO2014156464A1 WO 2014156464 A1 WO2014156464 A1 WO 2014156464A1 JP 2014055024 W JP2014055024 W JP 2014055024W WO 2014156464 A1 WO2014156464 A1 WO 2014156464A1
Authority
WO
WIPO (PCT)
Prior art keywords
sheet
ion secondary
secondary battery
press roll
base material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2014/055024
Other languages
English (en)
French (fr)
Inventor
祐二 柴田
和幸 大西
英司 折坂
一裕 鈴木
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zeon Corp
Original Assignee
Zeon Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zeon Corp filed Critical Zeon Corp
Priority to KR1020157014505A priority Critical patent/KR102227863B1/ko
Priority to CN201480014224.6A priority patent/CN105190957B/zh
Publication of WO2014156464A1 publication Critical patent/WO2014156464A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

　回転軸が平行に配置された一対のプレス用ロール４のうちの一方のプレス用ロール４Ｂの回転速度と他方のプレス用ロール４Ａの回転速度とを異ならせることが可能な圧延装置２を用いて、粉体との摩擦係数が所定の範囲である基材２２上に前記粉体を圧縮成形することにより前記基材上に電極組成物層２８を成形する圧延工程と、前記圧延工程における前記基材に対する前記粉体の目付量を測定する測定工程と、前記測定工程による測定結果に基づいて、前記一方のプレス用ロールの回転速度の前記他方のプレス用ロールの回転速度に対する速度比を変更する変更工程とを含む。

Description

リチウムイオン二次電池電極用シートの製造方法
　本発明は、電極活物質等を含む粉体を圧縮成形してリチウムイオン二次電池電極用シートを製造するリチウムイオン二次電池電極用シートの製造方法に関するものである。
　小型で軽量、且つエネルギー密度が高く、繰り返し充放電が可能なリチウムイオン二次電池は、環境対応からも今後の需要の拡大が見込まれている。リチウムイオン二次電池は、エネルギー密度が大きく携帯電話やノート型パソコン等の分野で利用されているが、用途の拡大や発展に伴い、低抵抗化、大容量化等、より一層の性能向上が求められている。
　リチウムイオン二次電池電極は電極シートとして得ることができ、例えば、電極活物質を含む粉体から電極シート等の圧延シートを製造するために粉体圧延装置を用いた粉体の圧縮成形が行われている。粉体圧延装置では一対のプレス用ロールのロール間に供給される粉体を基材上に連続的に圧縮成形することにより圧延シートが得られる。ここで、圧延シートを製造する際には、薄膜であり、かつ、密度分布、膜厚分布のばらつきが少ない、精度のよい圧延シートを製造することが求められる。
　例えば、特許文献１においては、一対のプレス用ロールと一対のプレス用ロールの一方の上方に予備圧下ロールを設けた圧延装置を用いて圧延シートを成形することが開示されている。この圧延装置においては、予備圧下ロールが設けられた側のプレス用ロールと予備圧下ロールの速度比率を調整することで得られる圧延シートの厚さを制御している。即ち、プレス用ロールの周速度が一定である場合に、予備圧下ロールの回転速度を遅くすると得られる圧延シートは薄くなり、予備圧下ロールの周速度を速くすると得られる圧延シートは厚くなる。さらに、特許文献１においては、一対のプレス用ロールの回転速度を変化させることで得られる圧延シートの厚さを調節している。
特許第３８７３７１９号公報
　しかし、この圧延装置においては、圧延シートの膜厚を調整するための部材である予備圧下ロールを設けなければならず、さらに、一対のプレス用ロールの回転速度を変化させると生産ラインの速度が一定に保てないため生産能力に影響を及ぼしていた。
　本発明の目的は、生産能力に影響を及ぼさず、簡易な手段により基材への粉体の目付け量の制御を行うことができるリチウムイオン二次電池電極用シートの製造方法を提供することである。
　本発明者らは、鋭意検討の結果、粉体と基材との摩擦係数を所定範囲とし、また、一方のプレス用ロールの回転速度を他方のプレス用ロールの回転速度に対して変更することにより、上記目的を達成できることを見出し、本発明を完成するに至った。
　即ち、本発明によれば、
（１）　回転軸が平行に配置された一対のプレス用ロールのうちの一方のプレス用ロールの回転速度と他方のプレス用ロールの回転速度とを異ならせることが可能な圧延装置を用いて、粉体との摩擦係数が所定の範囲である基材上に前記粉体を圧縮成形することにより前記基材上に電極組成物層を成形する圧延工程と、前記圧延工程における前記基材に対する前記粉体の目付量を測定する測定工程と、前記測定工程による測定結果に基づいて、前記一方のプレス用ロールの回転速度の前記他方のプレス用ロールの回転速度に対する速度比を変更する変更工程とを含むことを特徴とするリチウムイオン二次電池電極用シートの製造方法、
（２）　前記一方のプレス用ロールの回転速度の前記他方のプレス用ロールの回転速度に対する速度比を１０～３００％の範囲で変更することを特徴とする（１）記載のリチウムイオン二次電池電極用シートの製造方法、
（３）　前記基材の表面粗度Ｒａが、０．１～５μｍであることを特徴とする（１）記載のリチウムイオン二次電池電極用シートの製造方法、
（４）　前記基材は、前記電極組成物層が成形される側の表面に接着剤層を有することを特徴とする（１）記載のリチウムイオン二次電池電極用シートの製造方法、
（５）　前記基材の表面は、表面改質されていることを特徴とする（１）記載のリチウムイオン二次電池電極用シートの製造方法、
（６）　前記粉体は、電極活物質および結着材を含む成分を造粒することにより得られる複合粒子であることを特徴とする（１）～（５）の何れかに記載のリチウムイオン二次電池電極用シートの製造方法
が提供される。
　本発明に係るリチウムイオン二次電池電極用シートの製造方法によれば、生産能力に影響を及ぼさず、簡易な手段により基材への粉体の目付け量の制御を行うことができる。
本発明の実施の形態に係る粉体圧延装置の概略を示す図である。
　以下、図面を参照して本発明の実施の形態に係るリチウムイオン二次電池電極用シートの製造方法について説明する。図１は、実施の形態に係るリチウムイオン二次電池電極用シートの製造方法に用いる粉体圧延装置の概略を示す図である。図１に示すように、粉体圧延装置２は、回転軸１４Ａ，１４Ｂが水平かつ平行に配列された一対のロール４Ａ，４Ｂを含むプレス用ロール４、プレス用ロール４により圧縮成形された圧延シート６の厚さを測定する膜厚検出センサ８、装置全体の制御を行う制御部１０、得られる圧延シート６のシート状成形物２８の目標膜厚の入力や圧延シート６の製造開始指示を受け付ける操作部１２、プレス用ロール４のロール４Ａを回転軸１４Ａを中心に回転させるモータ等を有する回転駆動部１６Ａ、ロール４Ｂを回転軸１４Ｂを中心に回転させるモータ等を有する回転駆動部１６Ｂを備えている。
　ここで、プレス用ロール４のロール４Ａ，４Ｂはそれぞれ図１に示す矢印方向へ回転することによりプレス用ロール４と仕切板２６により形成された空間に貯槽された粉体２０を咬み込み、粉体２０をバックアップ基材２２の一方の面に圧縮してシート状成形物２８を成形する。
　また、膜厚検出センサ８としては挟み込みタイプ、接触タイプ等のものを用いることができ、検出方式としてはレーザ式、Ｘ線式、赤外線式、ベータ線式、過電流式、電磁式、超音波式、光学式等を用いることができる。
　次に、粉体圧延装置２により圧延シート６を製造する手順について説明する。操作部１２を介して圧延シート６のシート状成形物２８の目標膜厚ＴDの入力および圧延シート６の製造開始指示が行われると、制御部１０は回転駆動部１６Ａ，１６Ｂを制御して、プレス用ロール４のロール４Ａ，４Ｂを図１に示す矢印方向に回転させる。
　ここで、回転駆動部１６Ａがロール４Ａを回転させる速度はバックアップ基材２２の搬送速度に応じた速度である。即ち、回転駆動部１６Ａは圧延シート６の生産ラインの速度に応じた回転速度でロール４Ａを回転させる。また、回転駆動部１６Ｂは入力された目標膜厚に応じた回転速度でロール４Ｂを回転させる。従って、ロール４Ａとロール４Ｂの回転速度は、同一の速度であっても、異なる速度であってもよい。前記一方のプレス用ロールの回転速度の前記他方のプレス用ロールの回転速度に対する速度比は、１～５００％、好ましくは１０～３００％の範囲で変更できる。
　ここで、ロール４Ａ及びロール４Ｂのそれぞれの回転速度と得られる圧延シート６におけるシート状成形物２８の膜厚との関係は、予め測定して制御部１０に記憶されている。また、プレス用ロール４によりバックアップ基材２２に圧縮成形される粉体２０の目付け量と膜厚との関係も予め制御部１０に記憶されている。
　プレス用ロール４を回転させることにより粉体２０の圧縮成形を開始すると、プレス用ロール４と仕切板２６とにより形成された空間に貯槽された粉体２０は、プレス用ロール４に咬み込まれバックアップ基材２２の一方の面に圧縮成形される。即ち、シート状成形物２８がバックアップ基材２２に積層された圧延シート６が得られる。
　次に、制御部１０は、操作部１２を介して入力された目標膜厚ＴDと膜厚検出センサ８からの出力に基づいて求められるシート状成形物２８の膜厚ＴAとを比較し、回転駆動部１６Ｂを制御してロール４Ｂの回転速度を変更させる。ここで、ロール４Ｂの回転速度が速くなるほど、粉体２０の咬み込み量を小さくすることができ、得られる圧延シート６（シート状成形物２８）の厚み（膜厚）を薄くすることができる。
　従って、目標膜厚ＴDよりもシート状成形物２８の膜厚ＴAの方が薄い場合には、制御部１０は回転駆動部１６Ｂを制御して、ロール４Ｂの回転速度を低下させる。一方、目標膜厚ＴDよりもシート状成形物２８の膜厚ＴAの方が厚い場合には、制御部１０は回転駆動部１６Ｂを制御して、ロール４Ｂの回転速度を増加させる。また、目標膜厚ＴDとシート状成形物２８の膜厚ＴAが一致する場合には、制御部１０は回転駆動部１６Ｂを制御したロール４Ｂの回転速度の変更を行わない。ここで、制御部１０は回転駆動部１６Ｂを制御してロール４Ｂの回転速度を変更させる際に、ロール４Ｂの回転速度を、ロール４Ａの回転速度の、１～５００％、好ましくは１０～３００％とする。
　バックアップ基材２２としては、薄いフィルム状の基材であればよく、通常、厚さ１μｍ～１０００μｍ、好ましくは５μｍ～１００μｍである。バックアップ基材２２としては、アルミニウム、白金、ニッケル、タンタル、チタン、ステンレス鋼、銅、その他の合金などの金属箔または炭素、導電性高分子、紙、天然繊維、高分子繊維、布帛、高分子樹脂フィルムなどが挙げられ、目的に応じて適宜選択することができる。高分子樹脂フィルムとしては、ポリエチレンテレフタレートやポリエチレンナフタレート等のポリエステル樹脂フィルム、ポリイミド、ポリプロピレン、ポリフェニレンサルファイド、ポリ塩化ビニル、アラミドフィルム、ＰＥＮ、ＰＥＥＫ等を含んで構成されるプラスチックフィルム、シート等が挙げられる。
　これらの中でも、圧延シート６として、リチウムイオン二次電池電極用シートを製造する場合には、バックアップ基材２２として、金属箔または炭素、導電性高分子を用いることができ、好適には金属が用いられる。これらの中で導電性、耐電圧性の面から銅、アルミニウムまたはアルミニウム合金を使用することが好ましい。
　また、バックアップ基材２２としては、後述する複合粒子等の粉体２０との摩擦係数が所定の範囲となるように処理されている基材を用いる。このような処理としては、バックアップ基材２２の粗面化処理、コロナ放電によるバックアップ基材２２の表面改質処理、バックアップ基材２２の表面に接着剤層を設ける処理等を用いることができる。なお、このような処理は、少なくともバックアップ基材２２のシート状成形物２８が形成される側の面に行われていればよい。
　バックアップ基材２２を粗面化処理する場合において、粗面化された面の表面粗さＲａは、粉体２０とバックアップ基材２２との密着性の観点から、好ましくは０．１～５μｍ、より好ましくは０．２～３μｍ、さらに好ましくは０．２～１μｍの範囲である。
　表面粗さＲａは、ＪＩＳ　Ｂ０６０１に準拠して、例えばナノスケールハイブリッド顕微鏡（ＶＮ－８０１０、キーエンス社製）を用いて、粗さ曲線を描き、下式により算出することができる。下式において、Ｌは測定長さ、ｘは平均線から測定曲線までの偏差である。
Figure JPOXMLDOC01-appb-M000001
 　バックアップ基材２２の表面を粗面化する方法は特に制限されず、バックアップ基材２２の表面をエンボス処理する方法、バックアップ基材２２の表面をサンドブラスト処理する方法、バックアップ基材２２を構成する材料にマット材を練り込む方法、マット材を含む層をバックアップ基材２２の表面にコーティングする方法などが挙げられる。中でも粉体２０として用いられる複合粒子との密着性の観点からバックアップ基材２２の表面をサンドブラスト処理する方法が好ましい。
　バックアップ基材２２として粉体２０との摩擦係数が所定の範囲となるように処理されている基材を用いることにより、プレス用ロール４のロール４Ａとロール４Ｂとの回転速度が異なる場合であっても、高速で回転している側のロールへ粉体２０の張り付きを防ぐことができる。従って、プレス用ロール４のロール４Ａとロール４Ｂとの回転速度が異なる場合であっても、圧延シート６を得ることができる。
　プレス用ロール４と仕切板２６とにより形成される空間に貯槽される粉体２０としては、例えば電極活物質を含む複合粒子が挙げられる。複合粒子は、電極活物質及び結着材を含み、必要に応じてその他の分散剤、導電材および添加剤を含んでもよい。粉体２０として電極活物質を含む複合粒子を用いる場合は、得られる圧延シート６を電極材料から成る電極層として用いることができる。
　複合粒子をリチウムイオン二次電池の電極材料として用いる場合、正極用活物質としては、リチウムイオンを可逆的にドープ・脱ドープ可能な金属酸化物が挙げられる。かかる金属酸化物としては、例えば、コバルト酸リチウム、ニッケル酸リチウム、マンガン酸リチウム、燐酸鉄リチウム、等を挙げることができる。なお、上記にて例示した正極活物質は適宜用途に応じて単独で使用してもよく、複数種混合して使用してもよい。
　なお、リチウムイオン二次電池用正極の対極としての負極の活物質としては、易黒鉛化性炭素、難黒鉛化性炭素、熱分解炭素などの低結晶性炭素（非晶質炭素）、グラファイト（天然黒鉛、人造黒鉛）、錫やケイ素等の合金系材料、ケイ素酸化物、錫酸化物、チタン酸リチウム等の酸化物等が挙げられる。なお、上記に例示した電極活物質は適宜用途に応じて単独で使用してもよく、複数種混合して使用してもよい。
　リチウムイオン二次電池電極用の電極活物質の形状は、粒状に整粒されたものが好ましい。粒子の形状が球形であると、電極成形時により高密度な電極が形成できる。
　リチウムイオン二次電池電極用の電極活物質の体積平均粒子径は、正極、負極ともに通常０．１～１００μｍ、好ましくは０．５～５０μｍ、より好ましくは０．８～３０μｍである。
　複合粒子に用いられる結着材としては、前記電極活物質を相互に結着させることができる化合物であれば特に制限はない。好適な結着材は、溶媒に分散する性質のある分散型結着材である。分散型結着材として、例えば、シリコン系重合体、フッ素含有重合体、共役ジエン系重合体、アクリレート系重合体、ポリイミド、ポリアミド、ポリウレタン等の高分子化合物が挙げられ、好ましくはフッ素系含有重合体、共役系ジエン重合体およびアクリレート系重合体、より好ましくは共役ジエン系重合体およびアクリレート系重合体が挙げられる。
　分散型結着材の形状は、特に制限はないが、粒子状であることが好ましい。粒子状であることにより、結着性が良く、また、作製した電極の容量の低下や充放電の繰り返しによる劣化を抑えることができる。粒子状の結着材としては、例えば、ラテックスのごとき結着材の粒子が水に分散した状態のものや、このような分散液を乾燥して得られる粒子状のものが挙げられる。
　結着材の量は、得られる電極活物質層と集電体との密着性が充分に確保でき、かつ、内部抵抗を低くすることができる観点から、電極活物質１００重量部に対して、乾燥重量基準で通常は０．１～５０重量部、好ましくは０．５～２０重量部、より好ましくは１～１５重量部である。
　複合粒子には、前述のように必要に応じて分散剤を用いてもよい。分散剤の具体例としては、カルボキシメチルセルロース、メチルセルロースなどのセルロース系ポリマー、ならびにこれらのアンモニウム塩またはアルカリ金属塩、ポリビニルアルコールなどが挙げられる。これらの分散剤は、それぞれ単独でまたは２種以上を組み合わせて使用できる。
　複合粒子には、前述のように必要に応じて導電材を用いてもよい。導電材の具体例としては、ファーネスブラック、アセチレンブラック、及びケッチェンブラック（アクゾノーベル　ケミカルズ　ベスローテン　フェンノートシャップ社の登録商標）などの導電性カーボンブラックが挙げられる。これらの中でも、アセチレンブラックおよびケッチェンブラックが好ましい。これらの導電材は、単独でまたは二種類以上を組み合わせて用いることができる。
　複合粒子は、電極活物質、結着材および必要に応じ添加される前記導電材等他の成分を用いて造粒することにより得られ、少なくとも電極活物質、結着材を含んでなるが、前記のそれぞれが個別に独立した粒子として存在するのではなく、構成成分である電極活物質、結着材を含む２成分以上によって一粒子を形成するものである。具体的には、前記２成分以上の個々の粒子の複数個が結合して二次粒子を形成しており、複数個（好ましくは数個～数十個）の電極活物質が、結着材によって結着されて粒子を形成しているものが好ましい。
　複合粒子の製造方法は特に制限されず、流動層造粒法、噴霧乾燥造粒法、転動層造粒法などの公知の造粒法により製造することができる。
　複合粒子の体積平均粒子径は、所望の厚みの電極活物質層を容易に得る観点から、通常０．１～１０００μｍ、好ましくは１～５００μｍ、より好ましくは３０～２５０μｍの範囲である。
　なお、複合粒子の平均粒子径は、レーザ回折式粒度分布測定装置（たとえば、ＳＡＬＤ－３１００；島津製作所製）にて測定し、算出される体積平均粒子径である。
　本実施の形態に係るリチウムイオン二次電池電極用シートの製造方法によれば、生産能力に影響を及ぼさず、簡易な手段により基材への粉体の目付け量の制御を行うことができる。また、低目付け量の電極用シート、即ち、薄膜の電極用シートを製造することができる。
　また、得られる圧延シートの膜厚の測定結果に基づいてロール４Ｂの回転速度を制御するフィードバック制御を行うことができるため、所望の膜厚の電極用シートを製造することができる。
　以下、実施例及び比較例を示し、本発明を更に具体的に説明するが、本発明は下記の実施例に制限されるものではない。また、部および％は、特に記載の無い限り重量基準である。
（造粒粒子の製造）
　負極活物質として人造黒鉛（体積平均粒子径：２４．５μｍ、黒鉛層間距離（Ｘ線回折法による（００２）面の面間隔（ｄ値））：０．３５４ｎｍ）を９７部、カルボキシメチルセルロースナトリウム塩を１．５部、結着材としてＢＭ－４００Ｂ（日本ゼオン社製）を固形分換算量で１．５部を混合し、さらにイオン交換水を固形分濃度が２０％となるように加え、混合分散して複合粒子用スラリーを得た。そして、得られた複合粒子用スラリーを、スプレー乾燥機（大川原化工機社製）を使用し、回転円盤方式のアトマイザ（直径６５ｍｍ）を用い、回転数２５，０００ｒｐｍ、熱風温度１６０℃、粒子回収出口の温度９０℃の条件にて、噴霧乾燥造粒を行い、負極電極用複合粒子を得た。得られた複合粒子の体積平均粒子径は７０μｍであった。
　（目付け量の測定）
　図１に示す装置構成の粉体圧延装置２において、粉体２０として粒子径が７０μｍの複合粒子を用い、ロール４Ａとロール４Ｂとのロール間隙を０．１ｍｍとして圧延シート６の作製を行った。また、バックアップ基材２２としての表面がサンドブラスト処理された厚さ５０μｍ表面粗度Ｒａが０．３５μｍのＰＥＴフィルムを用いた。ここで、プレス用ロール４のロール４Ａの回転速度（バックアップ基材２２の搬送速度）を５ｍ／ｍｉｎとし、ロール４Ｂの回転速度を４ｍ／ｍｉｎ、５ｍ／ｍｉｎ、６ｍ／ｍｉｎ、７．５ｍ／ｍｉｎ、１０ｍ／ｍｉｎとしてそれぞれシート状成形物２８の製造を行った。また、シート状成形物２８の製造の際に、複合粒子及びアルミニウム箔（バックアップ基材）を粉体圧延装置２に投入し、プレス用ロール４によりＰＥＴフィルムに目付けされる粉体の量（目付け量、単位：ｍｇ／ｃｍ2）を測定した。結果を表１に示す。
Figure JPOXMLDOC01-appb-T000002
 　表１の結果から、ロール４Ａの回転速度が一定の場合、ロール４Ｂの回転速度が速くなるほど、目付け量が減少することが示された。また、目付け量が少ないほど得られるシート状成形物２８の膜厚が薄くなるため、ロール４Ａの回転速度に対するロール４Ｂの回転速度が速くなるほど、得られる圧延シート６及びシート状成形物２８の膜厚が薄くなることが示された。

Claims (6)

  1. 　回転軸が平行に配置された一対のプレス用ロールのうちの一方のプレス用ロールの回転速度と他方のプレス用ロールの回転速度とを異ならせることが可能な圧延装置を用いて、粉体との摩擦係数が所定の範囲である基材上に前記粉体を圧縮成形することにより前記基材上に電極組成物層を成形する圧延工程と、
    　前記圧延工程における前記基材に対する前記粉体の目付量を測定する測定工程と、
    　前記測定工程による測定結果に基づいて、前記一方のプレス用ロールの回転速度の前記他方のプレス用ロールの回転速度に対する速度比を変更する変更工程と
    を含むことを特徴とするリチウムイオン二次電池電極用シートの製造方法。
  2. 　前記一方のプレス用ロールの回転速度の前記他方のプレス用ロールの回転速度に対する速度比を１０～３００％の範囲で変更することを特徴とする請求項１記載のリチウムイオン二次電池電極用シートの製造方法。
  3. 　前記基材の表面粗度Ｒａが、０．１～５μｍであることを特徴とする請求項１記載のリチウムイオン二次電池電極用シートの製造方法。
  4. 　前記基材は、前記電極組成物層が成形される側の表面に接着剤層を有することを特徴とする請求項１記載のリチウムイオン二次電池電極用シートの製造方法。
  5. 　前記基材の表面は、表面改質されていることを特徴とする請求項１記載のリチウムイオン二次電池電極用シートの製造方法。
  6. 　前記粉体は、電極活物質および結着材を含む成分を造粒することにより得られる複合粒子であることを特徴とする請求項１～５の何れか一項に記載のリチウムイオン二次電池電極用シートの製造方法。
PCT/JP2014/055024 2013-03-26 2014-02-28 リチウムイオン二次電池電極用シートの製造方法 Ceased WO2014156464A1 (ja)