WO2013161582A1 - Film de revêtement dur, et dispositif d'affichage de panneau tactile équipé de celui-ci - Google Patents

Film de revêtement dur, et dispositif d'affichage de panneau tactile équipé de celui-ci Download PDF

Info

Publication number
WO2013161582A1
WO2013161582A1 PCT/JP2013/060983 JP2013060983W WO2013161582A1 WO 2013161582 A1 WO2013161582 A1 WO 2013161582A1 JP 2013060983 W JP2013060983 W JP 2013060983W WO 2013161582 A1 WO2013161582 A1 WO 2013161582A1
Authority
WO
WIPO (PCT)
Prior art keywords
hard coat
film
plasticizer
cellulose ester
acid
Prior art date
Application number
PCT/JP2013/060983
Other languages
English (en)
Japanese (ja)
Inventor
亮太 久木
Original Assignee
コニカミノルタ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by コニカミノルタ株式会社 filed Critical コニカミノルタ株式会社
Priority to CN201380022035.9A priority Critical patent/CN104246541B/zh
Priority to JP2014512464A priority patent/JP5943070B2/ja
Priority to KR1020147029931A priority patent/KR101627958B1/ko
Publication of WO2013161582A1 publication Critical patent/WO2013161582A1/fr

Abstract

Selon l'invention, une couche de revêtement dur (42) d'un film de revêtement dur (40), est formée par application d'une composition pour formation de couche de revêtement dur sur un film d'ester de cellulose (41), puis durcissement de cette composition. L'épaisseur du film de revêtement dur (40) est supérieure ou égale à 15µm et inférieure ou égale à 35µm. Un plastifiant favorisant la formation d'une couche mixte (43) du film d'ester de cellulose (41) et de la couche de revêtement dur (42), est compris à raison d'au moins 6% en masse et d'au plus 12% en masse dans le film d'ester de cellulose (41), et en plus grande quantité côté couche de revêtement dur (42), que côté opposé à celui-ci dans le film d'ester de cellulose (41).
PCT/JP2013/060983 2012-04-27 2013-04-11 Film de revêtement dur, et dispositif d'affichage de panneau tactile équipé de celui-ci WO2013161582A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CN201380022035.9A CN104246541B (zh) 2012-04-27 2013-04-11 硬涂膜及具备该硬涂膜的触摸面板显示装置
JP2014512464A JP5943070B2 (ja) 2012-04-27 2013-04-11 ハードコートフィルム、ハードコートフィルムの製造方法およびタッチパネル表示装置
KR1020147029931A KR101627958B1 (ko) 2012-04-27 2013-04-11 하드 코팅 필름 및 그것을 구비한 터치 패널 표시 장치

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012-102641 2012-04-27
JP2012102641 2012-04-27

Publications (1)

Publication Number Publication Date
WO2013161582A1 true WO2013161582A1 (fr) 2013-10-31

Family

ID=49482910

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2013/060983 WO2013161582A1 (fr) 2012-04-27 2013-04-11 Film de revêtement dur, et dispositif d'affichage de panneau tactile équipé de celui-ci

Country Status (4)

Country Link
JP (1) JP5943070B2 (fr)
KR (1) KR101627958B1 (fr)
CN (1) CN104246541B (fr)
WO (1) WO2013161582A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016194575A (ja) * 2015-03-31 2016-11-17 株式会社Ｄｎｐファインケミカル ハードコート層用組成物、ハードコート層積層体の製造方法およびハードコート層積層体
CN107075148A (zh) * 2014-09-17 2017-08-18 柯尼卡美能达株式会社 纤维素酯膜及其制造方法

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6245803B2 (ja) * 2012-12-27 2017-12-13 日東電工株式会社 偏光板、光学フィルムおよび画像表示装置
CN106707384B (zh) * 2015-11-13 2019-05-24 宁波长阳科技股份有限公司 一种防翘曲反射膜及其制备方法
CN109192879B (zh) * 2018-08-31 2021-01-29 京东方科技集团股份有限公司 柔性显示用盖板及其制备方法和柔性显示装置

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005352011A (ja) * 2004-06-09 2005-12-22 Konica Minolta Opto Inc 偏光板、偏光板の製造方法及び液晶表示装置
JP2006182865A (ja) * 2004-12-27 2006-07-13 Konica Minolta Opto Inc ハードコートフィルム、その製造方法、それを用いた偏光板及び表示装置
JP2006297914A (ja) * 2005-03-25 2006-11-02 Fuji Photo Film Co Ltd ポリマーフィルム
WO2007000856A1 (fr) * 2005-06-28 2007-01-04 Nitto Denko Corporation Film de revetement dur anti-reflet

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4479175B2 (ja) * 2003-06-06 2010-06-09 コニカミノルタオプト株式会社 ハードコートフィルム、その製造方法、偏光板及び表示装置
JP2005054100A (ja) * 2003-08-06 2005-03-03 Konica Minolta Opto Inc セルロースエステルフィルム、ハードコートフィルム及び反射防止フィルム
JP4639682B2 (ja) * 2004-07-23 2011-02-23 コニカミノルタオプト株式会社 液晶表示装置用の偏光板及び液晶表示装置
JP5109370B2 (ja) 2006-12-28 2012-12-26 大日本印刷株式会社 ハードコート層用硬化性樹脂組成物、及びハードコートフィルム
JP5286960B2 (ja) * 2008-06-17 2013-09-11 日油株式会社 透明導電性フィルム及びそれを備えるタッチパネル
JP2010097005A (ja) * 2008-10-17 2010-04-30 Konica Minolta Opto Inc 反射防止フィルム、その製造方法、反射防止フィルムを用いた偏光板、及び表示装置
WO2011065531A1 (fr) 2009-11-30 2011-06-03 大日本印刷株式会社 Film optique et panneau tactile
JP5501800B2 (ja) * 2010-02-25 2014-05-28 株式会社ダイセル 透明導電性膜及びタッチパネル
KR101787131B1 (ko) * 2010-04-15 2017-10-18 닛토덴코 가부시키가이샤 하드 코트 필름, 편광판, 화상 표시 장치 및 하드 코트 필름의 제조 방법

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005352011A (ja) * 2004-06-09 2005-12-22 Konica Minolta Opto Inc 偏光板、偏光板の製造方法及び液晶表示装置
JP2006182865A (ja) * 2004-12-27 2006-07-13 Konica Minolta Opto Inc ハードコートフィルム、その製造方法、それを用いた偏光板及び表示装置
JP2006297914A (ja) * 2005-03-25 2006-11-02 Fuji Photo Film Co Ltd ポリマーフィルム
WO2007000856A1 (fr) * 2005-06-28 2007-01-04 Nitto Denko Corporation Film de revetement dur anti-reflet
CN101208620A (zh) * 2005-06-28 2008-06-25 日东电工株式会社 防眩性硬质薄膜
JP2008158536A (ja) * 2005-06-28 2008-07-10 Nitto Denko Corp 防眩性ハードコートフィルム
US20090086326A1 (en) * 2005-06-28 2009-04-02 Nitto Denko Corporation Antiglare hard-coated film

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107075148A (zh) * 2014-09-17 2017-08-18 柯尼卡美能达株式会社 纤维素酯膜及其制造方法
JP2016194575A (ja) * 2015-03-31 2016-11-17 株式会社Ｄｎｐファインケミカル ハードコート層用組成物、ハードコート層積層体の製造方法およびハードコート層積層体

Also Published As

Publication number Publication date
CN104246541B (zh) 2016-02-10
JPWO2013161582A1 (ja) 2015-12-24
CN104246541A (zh) 2014-12-24
KR101627958B1 (ko) 2016-06-07
JP5943070B2 (ja) 2016-06-29
KR20140146140A (ko) 2014-12-24

Similar Documents

Publication Publication Date Title
JP6048419B2 (ja) ハードコートフィルムの製造方法及び偏光板の製造方法
JP5895657B2 (ja) 光学フィルムの製造方法
JP5707856B2 (ja) 防眩性フィルムの製造方法
JP5423382B2 (ja) ハードコートフィルムの製造方法
JP5943070B2 (ja) ハードコートフィルム、ハードコートフィルムの製造方法およびタッチパネル表示装置
WO2012026245A1 (fr) Film de revêtement dur, plaque polarisante et dispositif d'affichage à cristaux liquides
JP2013083795A (ja) 防眩性フィルム、防眩性フィルムの製造方法、偏光板及び画像表示装置
JP5971121B2 (ja) 光学フィルムの製造方法
JP5994746B2 (ja) ハードコートフィルム、偏光板およびタッチパネル付き液晶表示装置
TWI599485B (zh) Optical film, polarizer and image display device
JP5888410B2 (ja) ハードコートフィルムの製造方法
JP6164050B2 (ja) 光学フィルム、偏光板及びそれらの製造方法、並びに画像表示装置
JP6048506B2 (ja) 光学フィルム
WO2015151795A1 (fr) Film optique, plaque de polarisation, procédé de production d'une plaque de polarisation, dispositif d'affichage d'image et procédé de fabrication d'un dispositif d'affichage d'image
JP2015025877A (ja) 光学フィルム、偏光板、及び液晶表示装置
JP2012068562A (ja) 画像表示装置
WO2016035404A1 (fr) Film optique, polariseur, et dispositif d'affichage d'image
JP2013088438A (ja) 光学フィルム、その製造方法及び画像表示装置
JP5707855B2 (ja) ハードコートフィルムの製造方法
WO2016009743A1 (fr) Film optique, plaque de polarisation et dispositif d'affichage d'images
WO2016038922A1 (fr) Film optique, plaque polarisante, et dispositif d'affichage d'image
JP2017021181A (ja) 光学フィルム、偏光板および画像表示装置
WO2016013261A1 (fr) Film optique, plaque polarisante et dispositif d'affichage d'image
JP2014061643A (ja) 光学フィルムの製造方法

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201380022035.9

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13782057

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2014512464

Country of ref document: JP

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 20147029931

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13782057

Country of ref document: EP

Kind code of ref document: A1