WO2013125782A1 - 강화 페놀 폼 보드 - Google Patents

강화 페놀 폼 보드 Download PDF

Info

Publication number
WO2013125782A1
WO2013125782A1 PCT/KR2012/011563 KR2012011563W WO2013125782A1 WO 2013125782 A1 WO2013125782 A1 WO 2013125782A1 KR 2012011563 W KR2012011563 W KR 2012011563W WO 2013125782 A1 WO2013125782 A1 WO 2013125782A1
Authority
WO
WIPO (PCT)
Prior art keywords
phenolic foam
foam board
foam layer
honeycomb
flat plate
Prior art date
Application number
PCT/KR2012/011563
Other languages
English (en)
French (fr)
Inventor
김지문
이응기
김명희
이민희
김정근
Original Assignee
(주)엘지하우시스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)엘지하우시스 filed Critical (주)엘지하우시스
Priority to JP2014554657A priority Critical patent/JP5923623B2/ja
Publication of WO2013125782A1 publication Critical patent/WO2013125782A1/ko

Abstract

본 발명은 강화 페놀 폼 보드에 관한 것이다. 이는 일정두께의 플레이트의 형태를 취하고 하니컴 구조를 갖는 하니컴 평판체와; 상기 하니컴 평판체의 일측면 또는 양측면에 접착 고정되는 페놀발포층을 포함하여 구성된 것을 특징으로 한다. 상기와 같이 이루어지는 본 발명의 강화 페놀 폼 보드는, 미리 완성되어 있는 부품을 조립하여 구성하는 방식이므로 제작과정이 간단함은 물론, 특히 내부의 하니컴평판체의 내부가 비어 있으므로 밀도가 낮으면서도 단열성능과 내화성이 우수하고, 또한 굴곡탄성률이 좋아 높은 강성이 요구되는 외단열 견축자재로 더욱 적합하다.

Description

강화 페놀 폼 보드
본 발명은 강화 페놀 폼 보드에 관한 것이다.
최근 단열 및 소방기준이 강화되는 상황에서 단열재 자체의 성능 개선을 위한 많은 시도가 진행되고 있다. 건물의 시공 공법에 있어서도, 종래의 내단열 공법을 벗어나서 단열재를 건물의 외벽에 시공하는 이른바 외단열시스템이 주목되고 있다.
상기 외단열시스템에 사용될 수 있는 단열용 판재에는, 발포폴리스틸렌, 글라스울, 우레탄발포보드, 페놀수지발포보드 등이 제안되고 있다.
그런데 상기한 폴리스틸렌이나 우레탄 등의 합성수지로 제작한 단열용 판재는, 내열성이 부족하여 화재 발생시 유독가스를 방출하고, 더욱이 내압성과 내압축성이 떨어져 단열용 판재로서 그 성능이 좋지 못하였다. 또한 상기 페놀수지발포보드로 성형된 단열용 판재는 내열성 및 내화성은 우수하지만 내압성과 내충격성과 굴곡탄성률이 좋지 못하다는 한계를 가진다.
이러한 페놀수지발포보드의 문제를 해결하기 위하여, 하니컴재의 육각 셀 내부에 페놀수지를 주입 및 발포시키는 타입의 이른 바, 페놀 폼 보드도 제안된 바 있다.
도 1은 종래의 패놀 폼 보드의 일부를 도시한 측단면도이다.
도시한 바와같이, 종래의 패놀 폼 보드(11)는, 육각의 셀이 형성되며 일정두께의 평판의 형태를 취하는 하니컴재(13)와, 상기 허니텀재(13)의 각 셀 내부에 충진되는 페놀폼(15)과, 상기 허니컴재(13)의 상면과 저면에 밀착 결합하는 표면재(17)로 구성된다.
상기 하니컴재(13)는, 평판의 형태를 취하며 그 내부에 허니컴 구조의 육각 셀이 밀집 형성된 것으로서 두께 방향으로 일정 단면을 갖는다. 또한 상기 페놀폼(15)은 상기 각각의 셀에 충진되며 셀의 내벽면에 밀착 고정된 상태로 유지된다. 상기 페놀폼(15)은 페놀이 포함되어 있는 혼합액을 상기 셀의 내부에 수용시킨 상태로 발포시켜 상기 셀의 내부를 채운 구조를 갖는다.
상기 표면재(17)는, 상기 하니컴재(13)의 양면을 커버하며 하니컴재(13)와 페놀폼(15)을 보호하여 외부로 미감을 구현하는 판상 부재이다. 상기 표면재(17)는 알루미늄 재질이며 에폭시 접착제를 통해 하니컴재(13) 및 페놀폼(15)의 외측에 접착 고정된다.
그런데 상기 구조를 갖는 종래의 페놀 폼 보드(11)는 그 제작방법이 매우 번거롭다는 단점이 있었다.
상기 페놀 폼 보드(11)를 제작하는 공정에는, 페놀과, 포르말린과, 젓산과, 가성소다와, 발포제 등이 적정 비율로 혼합된 교반용액을, 준비된 용기내에 부어 넣은 상태로, 상기 하니컴재(13)를 수평으로 내려 상기 교반용액에 침지시킨 후, 발포를 진행하는 과정을 포함한다.
상기 발포를 통해 하니컴재(13)의 육각 셀 내부에 페놀이 충진되었다면, 상기 하니컴재(13)를 들어올려 냉각한 후 후처리 공정을 수행한다.
상기한 바와같이, 하나의 페놀 폼 보드(11)를 제작하기 위해서, 용액의 혼합 및 가열공정과, 크레인을 이용한 하니컴재(13) 이동 등의 공정이 포함되어야 하므로 그만큼 번거롭고, 특히 경우에 따라 각각의 육각 셀의 내부에 페놀폼(15)이 완전히 충진되지 않을 수 도 있다.
상기 하니컴재(13)의 내부에 페놀폼(15)이 고른 밀도로 충진되지 않을 경우, 목적하는 단열성과 기계적 강도를 기대할 수 없음은 물론이며, 나아가 페놀폼(15)이 고른 밀도로 충진되더라도 그 만큼 중량이 증가하는 문제점이 있다.
본 발명은 상기 문제점을 해소하고자 창출한 것으로서, 미리 완성되어 있는 부품을 조립하여 구성하는 방식이므로 제작과정이 간단함은 물론, 특히 내부의 하니컴평판체의 내부가 비어 있으므로 밀도가 낮으면서도 단열성능과 내화성이 우수하고, 또한 굴곡탄성률이 좋아 높은 강성이 요구되는 외단열 견축자재로 더욱 적합한 강화 페놀 폼 보드를 제공함에 목적이 있다.
상기 목적을 달성하기 위한 본 발명에 따른 강화 페놀 폼 보드는, 일정두께의 플레이트의 형태를 취하고 하니컴 구조를 갖는 하니컴 평판체와; 상기 하니컴 평판체의 일측면 또는 양측면에 접착 고정되는 페놀발포층을 포함하여 구성된 것을 특징으로 한다.
또한, 상기 페놀발포층은, 일정두께를 갖는 플레이트의 형태를 취하며, 상기 하니컴 평판체의 표면에 밀착 고정되는 것을 특징으로 한다.
또한, 상기 페놀발포층의 외측면에는, 일정두께의 플레이트 형태를 취하는 하니컴 평판체와, 상기 하니컴 평판체를 커버하는 페놀발포층이 더 구비되는 것을 특징으로 한다.
아울러, 상기 하니컴평판체는, 합성수지나 금속으로 제작된 것으로서, 두께 방향으로 일정 단면을 갖는 것을 특징으로 한다.
또한, 상기 합성수지는 폴리프로필렌을 포함하고, 상기 금속은 알루미늄을 포함하는 것을 특징으로 한다.
또한, 상기 페놀발포층은, 25kg/m3 내지 60kg/m3의 밀도를 갖는 것을 특징으로 한다.
또한, 상기 페놀발포층과 하니컴평판체가 접착된 완성품은 15kg/m3 내지 40kg/m3의 밀도를 갖는 것을 특징으로 한다.
또한, 상기 페놀발포층의 외측면에는, 페놀발포보드를 커버하며 보호하는 표면재가 더 적층되는 것을 특징으로 한다.
아울러, 상기 표면재에는, 종이, 부직포, 알루미늄호일, 글라스페이퍼가 포함되는 것을 특징으로 한다.
상기와 같이 이루어지는 본 발명의 강화 페놀 폼 보드는, 미리 완성되어 있는 부품을 조립하여 구성하는 방식이므로 제작과정이 간단함은 물론, 특히 내부의 하니컴평판체의 내부가 비어 있으므로 전체 보드의 밀도가 현저히 감소되면서도 단열성능과 내화성이 우수하고, 또한 굴곡탄성률과 압축강도가 우수하여 높은 강성이 요구되는 외단열 건축자재로 더욱 적합하다.
도 1은 종래의 패놀 폼 보드의 일부를 도시한 단면도이다.
도 2는 본 발명의 일 실시예에 따른 강화 페놀 폼 보드의 기본 구성을 설명하기 위하여 도시한 도면이다.
도 3은 본 발명의 일 실시예에 따른 강화 페놀 폼 보드의 다른 구성을 도시한 도면이다.
도 4는 상기 도 3에 도시한 강화 페놀 폼 보드의 일부를 절제하여 도시한 평면도이다.
도 5는 본 발명의 일 실시예에 따른 강화 페놀 폼 보드의 또 다른 예를 도시한 측단면도이다.
이하, 본 발명에 따른 하나의 실시예를 첨부된 도면을 참조하여 보다 상세히 설명하기로 한다.
도 2는 본 발명의 일 실시예에 따른 강화 페놀 폼 보드(31)의 기본 구성을 설명하기 위하여 도시한 측단면도이다.
도시한 바와 같이, 본 실시예에 따른 페놀 폼 보드(31)의 기본 구성은, 일정두께의 평판 형태를 취하는 하니컴평판체(33)와, 상기 하니컴평판체(33)의 양측면(도면상 상하면)에 밀착 고정되는 페놀발포층(35)으로 구성된다.
먼저, 상기 하니컴평판체(33)는, 범용 플라스틱이나 알루미늄으로 제작된 판상 부재로서, 일반적인 하니컴(honeycomb)이 그러하듯이 다수의 육각형의 셀(도 4의 33a)이 밀집된 구성을 갖는다.
상기 범용플라스틱을 이루는 재질에는 여러 가지가 포함될 수 있으며 예컨대 폴리프로필렌을 사용할 수도 있다.
하니컴 구조체의 다른 소재로는 알루미늄도 사용이 가능하며, 폴리프로필렌 하니컴에 비해서 더 우수한 기계적 강도를 나타낼 수 있으나, 단열성능 측면에서는 폴리프로필렌 하니컴구조체가 우수하다.
하니컴평판체(33)의 두께는 사용 목적에 따라 다르게 제작되며 육각 셀의 크기도 다양하게 변경 가능함은 물론이다.
특히 상기 하니컴평판체(33)는, 내부의 육각셀이 비어있는 상태로 상기 페놀발포층(35)에 의해 밀폐되므로 그 내부에 공기층을 유지한다. 상기 공기층에 의해 하니컴평판체(33) 자체의 단열 및 내화 능력이 높아지게 된다.
상기 하니컴평판체(33)의 양측면에 접착 고정되는 페놀발포층(35)은 일정두께로 형성된 플레이트형 부재로서, 상기 하니컴평판체(33)의 양측면에 밀착 고정되어 있다. 상기 페놀발포층(35)은 그 자체가 내화성이 있고 특히 한 쌍의 페놀발포층(35)이 하니컴평판체(33)를 그 사이에 개재하므로 매우 뛰어난 내화 및 단열성능을 제공한다.
상기 페놀발포층(35)은 일반적인 레졸 타입의 페놀수지 100에 대해서 경화촉매로서 파라톨루엔술폰산 5-15 중량부, 발포제로 싸이클로펜탄을 5-10 중량부 혼합하여 고속믹서로 혼련된 슬러리를 가열하여 팽창시키면서 경화된 발포체이다. 이 페놀발포층(35)은 제작하기에 따라서 내화 및 단열성능이 약간씩 차이가 나지만, 본 실시예에서는 25kg/cm3 내지 60kg/cm3 의 밀도를 가지도록 제작할 수 있다. 아울러 상기 페놀발포층(35)의 열전도율은 0.018 내지 0.023W/mk 정도이다.
더불어서, 상기 페놀발포층(35)은 폴리실록산 1-5 중량%, 파라톨루엔술폰산 10-18 중량%, 싸이클로펜탄 5-15 중량%, 폴리올 2-6 중량%를 포함하고, 그 독립기포율이 80-97%인 것으로 할 수 있다.
상기한 성능을 갖는 페놀발포층(35)의 두께도 필요에 따라 달라짐은 물론이다. 아울러 상기 페놀발포층(35)과 하니컴평판체(33)의 고정은 에폭시 수지나 기타 접착제를 통해 이루어진다. 접착을 통해 만들어진 강화 페놀 폼 보드의 밀도는 15kg/m3 내지 40kg/m3의 낮은 밀도를 갖게 되고, 열전도율은 0.020 W/mK 내지 0.030 W/mK를 갖게 된다.
도 3은 본 발명의 일 실시예에 따른 강화 페놀 폼 보드의 다른 구성을 도시한 도면이다.
도면을 참조하면, 상기 각 페놀발포층(35)의 외측면에 표면재(37)가 부착되어 있음을 알 수 있다. 상기 표면재(37)는 일정두께를 갖는 시트형 부재로서, 페놀발포층(35)을 커버하여 페놀발포층(35)을 보호하며 외부에서 페놀발포층(35)이 보이지 않도록 한다.
상기 역할을 할 수 있는 한 표면재(37)의 종류는 매우 다양하게 적용할 수 있다. 상기 표면재(37)로서 가령 종이나 부직포 또는 알루미늄호일이나 글라스페이퍼(glass paper) 정도를 예로 들 수 있다.
특히 상기 표면재(37)에 있어서, 양측 페놀발포층(35)에 부착되는 표면재의 종류는 동일할 수 도 있고 다를 수 도 있다. 이를테면, (도면상) 상부의 페놀발포층(35)에는 알루미늄호일을 적용하고 하부의 페놀발포층(35) 저면에는 부직포를 부착할 수 도 있는 것이다.
이에 따라 본 실시예의 강화 페놀 폼 보드(31)를 건물 외장재로 사용할 경우, 건축물의 미감과 콘크리트면에 대한 부착력을 고려하여, 페놀팔포층(35)의 상면에는 알루미늄호일을, 저면에는 부직포를 부착할 수 있다.
도 4는 상기 도 3에 도시한 강화 페놀 폼 보드(31)의 일부를 절제하여 도시한 평면도이다.
도시한 바와 같이, 본 실시예에 따른 강화 페놀 폼 보드(31)는, 하부로부터 표면재(37), 페놀발포층(35), 하니컴평판체(33), 페놀발포층(35), 표면재(37)로 적층 구성된다.
특히 상기 하니컴평판체(33)에는 다수의 육각형 형태의 셀(33a)이 형성되어 있다. 상기 셀(33a)은 밀집된 상태를 유지하며 그 내부에 아무것도 수용하지 않은 상태로 상기 페놀발포층(35)에 의해 밀폐된다. 상기 셀(33a) 자체의 크기는 경우에 따라 달라진다.
도 5는 본 발명의 일 실시예에 따른 강화 페놀 폼 보드(31)의 또 다른 예를 도시한 측단면도이다.
상기한 도면 부호와 동일한 도면부호는 동일한 기능의 동일한 부재를 가리킨다.
도시한 바와 같이, 본 실시예에 따른 강화 페놀 폼 보드(31)는, 상기 하니컴 평판체(33)를 이중으로 적층 구성할 수 도 있다.
즉, 도 5에 도시한 바와같이 다른 예에 따른 강화 페놀 폼 보드(31)는, 하측 표면재(37)와, 상기 하측 표면재(37)의 상부에 적층되는 하측 페놀발포층(35)과, 상기 하측 페놀발포층(35)의 상면에 고정되는 일정 두께의 하니컴평판체(33)와, 상기 하니컴평판체(33)의 상부에 적층되는 중간 페놀발포층(35)과, 상기 중간에 개재된 패놀발포층(35)의 상부에 고정되는 상측 하니컴평판체(33)와, 상기 상측 하니컴평판체(33)에 적층되는 페놀발포층(35)과, 상기 페놀발포층(35) 상부에 적층되는 표면재(37)로 구성된다.
상기 두 개의 하니컴평판체(33) 사이에 배치되어 있는 페놀발포층(35)은 하니컴평판체(33)를 상호 고정시키는 역할을 하면, 상측 하니컴평판체(33)와 하측 하니컴평판체(33)의 셀(33a)을 단절시켜, 각 셀(33a)을 밀봉시킨다.
결국 상기한 바와같이 구성되는 본 실시예에 다른 강화 페놀 폼 보드(31)는, 내구성을 제공하는 하니컴평판체(33)에, 단열 및 내화 성능을 갖는 페놀발포층(35)을 접목시키고 또한 그 외측에 표면재(37)를 부착하여, 건축용 단열 외장재로서 효과적으로 사용될 수 있는 것이다.
이하, 본 발명에 따른 구체적인 실시예와 비교예를 통해 본 발명의 강화 페놀 폼 보드의 장점을 살펴본다.
참고로, 실시예 1, 2 및 비교예 1, 2의 강화 페놀 폼 보드는 일반적인 강화 페놀 폼 보드 제조 공정에 따라 제조된 것으로 한다.
실시예 1
두께가 각각 0.2mm인 종이면재 사이에 폴리실록산 3중량%, 파라톨루엔술폰산 14중량%, 싸이클로펜탄 9중량%, 폴리올 3중량%를 포함하는 레졸형 페놀 수지 경화 발포체 형성용 슬러리를 투입하고, 독립기포율이 95%인 페놀 수지 경화 발포체를 형성하였다. 이후 상기 발포체를 포함하는 두께 20mm의 판넬을 80℃의 더블벨트 컨베이어에 10분 통과시킨 후, 양생고에서 360분 동안 양생시켜 보드 형태의 판넬을 제조하였다. 이어 2장의 발포보드와 그 사이에 폴리프로필렌으로 제조된 10mm 두께의 허니컴 구조체를 접착제를 이용하여 합판시켜서 최종적으로 50mm 두께의 복합판넬을 제조하였다.
실시예 2
상기 실시예 1과 동일한 조건으로 발포보드 판넬을 제조하여, 10mm 두께의 알루미늄 허니컴 구조체를 2장의 발포보드 사이에 넣고 접착제를 이용하여 접착시켜 제조하였다.
비교예 1
실시예 1과 달리 페놀수지 발포원료를 허니컴 구조체의 내부에 투하하여 페놀수지 허니컴 공간을 채움으로써 발포체가 가득 채워진 복합 패널을 제조하였다.
비교예 2
비교예 1과 구조 및 제조방법은 같으나, 허니컴 구조체의 내부에 페놀폼 대신 우레탄 폼을 채운 복합판넬을 제조하였다.
단열성능 및 기계적 물성 평가
상기한 실시예 및 비교예의 판넬에 대해서 열전도율과 기계적 강도를 측정하여 하기 표 1에 나타내었다. 이때, 열전도율의 측정은 HC-074-200(EKO사 제조) 열전도율 측정기를 사용하였다.
표 1
밀도(kg/m3) 열전도율(W/mK) 압축강도(kPa) 굴곡강도(N/cm2)
실시예1 27 0.023 116 65
실시예2 30 0.025 115 68
비교예1 35 0.022 116 68
비교예2 35 0.024 116 70
[표 1]을 보면, 본 발명에 의한 실시예 1, 2의 경우, 비교예 1, 2에 비해서 밀도가 현저히 낮음에도 불구하고 초기 열전도율과 압축강도, 굴곡강도 측면에서 큰 차이를 보이지 않고 있음을 알 수 있다.
따라서, 본 발명에 따른 허니컴 강화 페놀 폼 보드는 다른 물성을 유사한 수준으로 유지하면서도 낮은 밀도를 나타냄으로써 시공작업성이 향상되고, 고층건물의 하중 부담을 줄여주는 장점을 갖게 된다.
이상, 본 발명을 구체적인 실시예를 통하여 상세하게 설명하였으나, 본 발명은 상기 실시예에 한정하지 않고, 본 발명의 기술적 사상의 범위내에서 통상의 지식을 가진 자에 의하여 여러 가지 변형이 가능하다.
[부호의 설명]
11:페놀 폼 보드 13:하니컴재
15:페놀폼 17:표면재
31:강화 페놀 폼 보드 33:하니컴 구조체
33a:셀 35:페놀 발포층
37:표면재

Claims (11)

  1. 일정두께의 플레이트의 형태를 취하고 하니컴 구조를 갖는 하니컴 평판체와;
    상기 하니컴 평판체의 일측면 또는 양측면에 접착 고정되는 페놀발포층을 포함하여 구성된 것을 특징으로 하는 강화 페놀 폼 보드.
  2. 제 1항에 있어서,
    상기 페놀발포층은,
    일정두께를 갖는 플레이트의 형태를 취하며, 상기 하니컴 평판체의 표면에 밀착 고정되는 것을 특징으로 하는 강화 페놀 폼 보드.
  3. 제 1항에 있어서,
    상기 페놀발포층의 외측면에는,
    일정두께의 플레이트 형태를 취하는 하니컴 평판체와, 상기 하니컴 평판체를 커버하는 페놀발포층이 더 구비되는 것을 특징으로 하는 강화 페놀 폼 보드.
  4. 제 1항에 있어서,
    상기 하니컴 평판체는, 합성수지나 금속으로 제작된 것으로서, 두께 방향으로 일정 단면을 갖는 것을 특징으로 하는 강화 페놀 폼 보드.
  5. 제 1항에 있어서,
    상기 페놀발포층은, 25kg/m3 내지 60kg/m3의 밀도를 갖는 것을 특징으로 하는 강화 페놀 폼 보드.
  6. 제 1항에 있어서,
    상기 페놀발포층과 하니컴평판체가 접착된 보드는 15kg/m3 내지 40kg/m3의 밀도와 0.020 W/mK 내지 0.030 W/mK의 단열성능을 나타내는 것을 특징으로 하는 강화 페놀 폼 보드.
  7. 제 1항에 있어서,
    상기 강화 페놀 폼 보드의 최외각에 배치되는 페놀발포층의 외측면에는, 상기 페놀 폼 보드를 커버하며 보호하는 표면재가 더 적층되는 것을 특징으로 하는 강화 페놀 폼 보드.
  8. 제 7항에 있어서,
    상기 표면재에는, 종이, 부직포, 알루미늄호일, 글라스페이퍼가 포함되는 것을 특징으로 하는 강화 페놀 폼 보드.
  9. 제 1항에 있어서,
    상기 페놀발포층은,
    레졸 타입의 페놀수지 100에 대해서 경화촉매로서 파라톨루엔술폰산 5-15 중량부, 발포제로 싸이클로펜탄을 5-10 중량부를 포함하는 것을 특징으로 하는 강화 페놀 폼 보드.
  10. 제 1항에 있어서,
    상기 페놀발포층은,
    폴리실록산 1-5 중량%, 파라톨루엔술폰산 10-18 중량%, 싸이클로펜탄 5-15 중량%, 폴리올 2-6 중량%를 포함하는 레졸형 페놀 수지 경화 발포체 형성용 슬러리를 포함하는 것을 특징으로 하는 강화 페놀 폼 보드.
  11. 제 10항에 있어서,
    상기 페놀발포층은 독립기포율이 80-97%인 것을 특징으로 하는 강화 페놀 폼 보드.
PCT/KR2012/011563 2012-02-24 2012-12-27 강화 페놀 폼 보드 WO2013125782A1 (ko)