WO2013087414A1 - Verfahren zur herstellung von verbundisolatoren mittels uv-vernetzung von siliconkautschuk - Google Patents
Verfahren zur herstellung von verbundisolatoren mittels uv-vernetzung von siliconkautschuk Download PDFInfo
- Publication number
- WO2013087414A1 WO2013087414A1 PCT/EP2012/073842 EP2012073842W WO2013087414A1 WO 2013087414 A1 WO2013087414 A1 WO 2013087414A1 EP 2012073842 W EP2012073842 W EP 2012073842W WO 2013087414 A1 WO2013087414 A1 WO 2013087414A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- silicone rubber
- mold
- irradiation
- radicals
- crosslinking
- Prior art date
Abstract
Description
Claims