WO2012172619A1 - 非水電解質蓄電デバイス用セパレータ、非水電解質蓄電デバイス及びそれらの製造方法 - Google Patents
非水電解質蓄電デバイス用セパレータ、非水電解質蓄電デバイス及びそれらの製造方法 Download PDFInfo
- Publication number
- WO2012172619A1 WO2012172619A1 PCT/JP2011/006317 JP2011006317W WO2012172619A1 WO 2012172619 A1 WO2012172619 A1 WO 2012172619A1 JP 2011006317 W JP2011006317 W JP 2011006317W WO 2012172619 A1 WO2012172619 A1 WO 2012172619A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- epoxy resin
- separator
- electricity storage
- nonaqueous electrolyte
- sheet
- Prior art date
Abstract
Description
10~50μmの範囲の厚さを有する非水電解質蓄電デバイス用セパレータを製造する方法であって、
エポキシ樹脂、硬化剤及びポロゲンを含むエポキシ樹脂組成物を調製する工程と、
エポキシ樹脂シートが得られるように、前記エポキシ樹脂組成物の硬化体をシート状に成形する又は前記エポキシ樹脂組成物のシート状成形体を硬化させる工程と、
ハロゲンフリーの溶剤を用いて前記エポキシ樹脂シートから前記ポロゲンを除去する工程と、
を含む、非水電解質蓄電デバイス用セパレータの製造方法を提供する。
カソード、アノード及びセパレータを準備する工程と、
前記カソード、前記アノード及び前記セパレータを用いて電極群を組み立てる工程と、
を含み、
前記セパレータが10~50μmの範囲の厚さを有し、
前記セパレータを準備する工程が、
(i)エポキシ樹脂、硬化剤及びポロゲンを含むエポキシ樹脂組成物を調製する工程と、
(ii)エポキシ樹脂シートが得られるように、前記エポキシ樹脂組成物の硬化体をシート状に成形する又は前記エポキシ樹脂組成物のシート状成形体を硬化させる工程と、
(iii)ハロゲンフリーの溶剤を用いて前記エポキシ樹脂シートから前記ポロゲンを除去する工程と、
を含む、非水電解質蓄電デバイスの製造方法を提供する。
エポキシ樹脂で構成された三次元網目状骨格と、
当該セパレータの表面と裏面との間でイオンが移動できるように連通している空孔と、
を備え、
10~50μmの範囲の厚さを有する、非水電解質蓄電デバイス用セパレータを提供する。
カソードと、
アノードと、
前記カソードと前記アノードとの間に配置された、上記本発明のセパレータと、
イオン伝導性を有する電解質と、
を備えた、非水電解質蓄電デバイスを提供する。
空孔率(%)=100×(V-(W/D))/V
V:体積(cm3)
W:重量(g)
D:構成成分の平均密度(g/cm3)
エポキシ樹脂組成物のシート状成形体が得られるように、エポキシ樹脂、硬化剤及びポロゲンを含むエポキシ樹脂組成物を基板上に塗布する。その後、エポキシ樹脂組成物のシート状成形体を加熱してエポキシ樹脂を三次元架橋させる。その際、エポキシ樹脂架橋体とポロゲンとの相分離により共連続構造が形成される。その後、得られたエポキシ樹脂シートからポロゲンを洗浄によって除去し、乾燥させることにより、三次元網目状骨格と連通する空孔とを有するエポキシ樹脂多孔質膜が得られる。基板の種類は特に限定されず、プラスチック基板、ガラス基板、金属板等を基板として使用できる。
エポキシ樹脂、硬化剤及びポロゲンを含むエポキシ樹脂組成物を基板上に塗布する。その後、塗布したエポキシ樹脂組成物の上に別の基板を被せてサンドイッチ構造体を作製する。なお、基板と基板との間に一定の間隔を確保するために、基板の四隅にスペーサー(例えば、両面テープ)を設けてもよい。次に、サンドイッチ構造体を加熱してエポキシ樹脂を三次元架橋させる。その際、エポキシ樹脂架橋体とポロゲンとの相分離により共連続構造が形成される。その後、得られたエポキシ樹脂シートを取り出し、ポロゲンを洗浄によって除去し、乾燥させることにより、三次元網目状骨格と連通する空孔とを有するエポキシ樹脂多孔質膜が得られる。基板の種類は特に制限されず、プラスチック基板、ガラス基板、金属板等を基板として使用できる。特に、ガラス基板を好適に使用できる。
エポキシ樹脂、硬化剤及びポロゲンを含むエポキシ樹脂組成物を所定形状の金型内に充填する。その後、エポキシ樹脂を三次元架橋させることによって、円筒状又は円柱状のエポキシ樹脂組成物の硬化体を作製する。その際、エポキシ樹脂架橋体とポロゲンとの相分離により共連続構造が形成される。その後、エポキシ樹脂組成物の硬化体を円筒軸又は円柱軸を中心に回転させながら、硬化体の表層部を所定の厚さに切削して長尺状のエポキシ樹脂シートを作製する。そして、エポキシ樹脂シートに含まれたポロゲンを洗浄によって除去し、乾燥させることにより、三次元網目状骨格と連通する空孔とを有するエポキシ樹脂多孔質膜が得られる。
(i)エポキシ樹脂組成物を調製する。
(ii)エポキシ樹脂組成物の硬化体をシート状に成形する。
(iii)エポキシ樹脂シートからポロゲンを除去する。
70重量部のビスフェノールA型エポキシ樹脂(三菱化学社製、jER(登録商標)828)、30重量部のビスフェノールA型エポキシ樹脂(三菱化学社製、jER(登録商標)1009)、及び202重量部のポリエチレングリコール(三洋化成社製、PEG200)を混合し、エポキシ樹脂のポリエチレングリコール溶液を調製した。
実施例1と同じ硬化体を用い、実施例1と同じ方法で約40μmの厚さを有するエポキシ樹脂多孔質膜を作製した。
ポリエチレングリコールの量を202重量部から258重量部に変更した点を除き、実施例1と同じ方法で約150μmの厚さを有するエポキシ樹脂多孔質膜を作製した。
参照例1の多孔質膜として、以下に説明する方法に従って、ポリエチレン多孔質膜を作製した。まず、15重量部の超高分子量ポリエチレン(重量平均分子量100万、融点137℃)及び85重量部の流動パラフィンを均一に混合してスラリーを得た。170℃の温度で二軸押出機にてスラリーを溶解及び混練し、コートハンガーダイスにて厚さ2mmのシートの形状に押し出した。得られたシートをロールに巻き取りながら冷却して、厚さ1.3mmのゲルシートを得た。このゲルシートを123℃の温度に加熱し、MD方向(機械方向)及びTD方向(幅方向)にそれぞれ4.5倍×5倍の倍率で同時二軸延伸して、延伸フィルムを得た。デカンを用いて延伸フィルムから流動パラフィンを除去した後、室温でデカンを乾燥させて、ポリエチレン多孔質膜を得た。得られたポリエチレン多孔質膜を空気中、125℃の温度で3分間熱処理した。このようにして、参照例1のポリエチレン多孔質膜を得た。参照例1のポリエチレン多孔質膜は、約16μmの厚さを有していた。
参照例2の多孔質膜として、ポリプロピレン多孔質膜(セルガード社製、Celgard2400、厚さ25μm)を準備した。
実施形態で説明した方法に従って、実施例、比較例及び参照例の多孔質膜の空孔率を算出した。実施例及び比較例の空孔率を算出するために、多孔質膜の作製に用いた2種類のエポキシ樹脂とアミン(硬化剤)とを用いてエポキシ樹脂の無孔体を作製し、この無孔体の比重を平均密度Dとして用いた。結果を表1に示す。
日本工業規格(JIS)P8117で規定された方法に従って、実施例、比較例及び参照例の多孔質膜の通気度(ガーレー値)を測定した。結果を表1に示す。
実施例、比較例及び参照例の多孔質膜の保液性を以下の方法で評価した。具体的には、まず、10mm×10mmの寸法に切断した多孔質膜の重量Aを測定した。次に、多孔質膜を溶媒(プロピレンカーボネート)に十分に浸漬した後、多孔質膜を引き上げ、ワイピングクロスで表面の余分な溶媒を除去し、重量Bを測定した。下記式に基づいて保液度を算出した。結果を表1に示す。
(保液度)=B/A
次に、実施例1のエポキシ樹脂多孔質膜をセパレータとして使用し、以下に説明する方法に従って、実施例1のリチウムイオン二次電池を作製した。
各電池を25℃の温度で、4.2Vに到達するまでは、0.2Cに相当する定電流で充電し、4.2Vに到達した後は、4.2V定電圧で電流値が0.2C相当の5%に減衰するまで充電を行って、これを1充電とし、次いで0.2Cに相当する電流値で電圧が2.75Vに到達するまで放電を行って、これらを1充放電サイクルとした。この充放電サイクルを2回行った。このとき、1回目の放電容量を初期放電容量として測定した。参照例2(Celgard2400)の電池の初期容量を基準値として、他の電池の初期容量を評価した。参照例2の電池の初期容量の±5%の初期容量を有していた電池の評価を「○」、それ以外の電池の評価を「×」とした。結果を表1に示す。
電池を温度60℃の恒温槽に入れ、0.2CmA、4.25Vの定電流定電圧充電を行なった。0.2CmAの電流での充電において、電池の電圧が4.25Vに達すると、電流値は減衰する。しかし、一旦減少した電流値が再び上昇する現象が観測されることがある。この現象は、高電圧で活性の高いカソードの近傍で何らかの化学反応が起こっていることを示唆していると考えられる。従って、セパレータの耐酸化性を評価する指標として、上記の連続充電における電流挙動を7日間観測した。7日間の観測で電流値の再上昇が観測されなかった場合には「○」、観測された場合には「×」と評価した。結果を表1に示す。
実施例1、実施例2、比較例1、参照例1及び参照例2の電池を室温にて0.2CmAの定電流、4.2Vの定電圧で20時間連続して充電した。次に、満充電状態を維持しつつ、80℃の温度の恒温槽に4日間保持した後、80℃の温度で電池の電圧を測定した。結果を表1に示す。
Claims (8)
- 10~50μmの範囲の厚さを有する非水電解質蓄電デバイス用セパレータを製造する方法であって、
エポキシ樹脂、硬化剤及びポロゲンを含むエポキシ樹脂組成物を調製する工程と、
エポキシ樹脂シートが得られるように、前記エポキシ樹脂組成物の硬化体をシート状に成形する又は前記エポキシ樹脂組成物のシート状成形体を硬化させる工程と、
ハロゲンフリーの溶剤を用いて前記エポキシ樹脂シートから前記ポロゲンを除去する工程と、
を含む、非水電解質蓄電デバイス用セパレータの製造方法。 - 前記硬化体が円筒又は円柱の形状を有し、
前記硬化体をシート状に成形する工程が、長尺の形状を有する前記エポキシ樹脂シートが得られるように、前記硬化体の表層部を所定の厚さに切削する工程を含む、請求項1に記載の非水電解質蓄電デバイス用セパレータの製造方法。 - 前記切削工程において、前記硬化体の円筒軸又は円柱軸を中心として、切削刃に対して前記硬化体を相対的に回転させながら前記硬化体の表層部を切削する、請求項2に記載の非水電解質蓄電デバイス用セパレータの製造方法。
- 前記ポロゲンが、ポリエチレングリコール及びポリプロピレングリコールから選ばれる少なくとも1つを含む、請求項1に記載の非水電解質蓄電デバイス用セパレータの製造方法。
- 前記溶剤が、水、ジメチルホルムアミド、ジメチルスルホキシド及びテトラヒドロフランからなる群より選ばれる少なくとも1つを含む、請求項1に記載の非水電解質蓄電デバイス用セパレータの製造方法。
- カソード、アノード及びセパレータを準備する工程と、
前記カソード、前記アノード及び前記セパレータを用いて電極群を組み立てる工程と、
を含み、
前記セパレータが10~50μmの範囲の厚さを有し、
前記セパレータを準備する工程が、
(i)エポキシ樹脂、硬化剤及びポロゲンを含むエポキシ樹脂組成物を調製する工程と、
(ii)エポキシ樹脂シートが得られるように、前記エポキシ樹脂組成物の硬化体をシート状に成形する又は前記エポキシ樹脂組成物のシート状成形体を硬化させる工程と、
(iii)ハロゲンフリーの溶剤を用いて前記エポキシ樹脂シートから前記ポロゲンを除去する工程と、
を含む、非水電解質蓄電デバイスの製造方法。 - エポキシ樹脂で構成された三次元網目状骨格と、
当該セパレータの表面と裏面との間でイオンが移動できるように連通している空孔と、
を備え、
10~50μmの範囲の厚さを有する、非水電解質蓄電デバイス用セパレータ。 - カソードと、
アノードと、
前記カソードと前記アノードとの間に配置された、請求項7に記載のセパレータと、
イオン伝導性を有する電解質と、
を備えた、非水電解質蓄電デバイス。