WO2011155717A2 - 직선형 절취특성을 갖는 파우치 및 제조방법 그리고 그 파우치 제조장치 - Google Patents

직선형 절취특성을 갖는 파우치 및 제조방법 그리고 그 파우치 제조장치 Download PDF

Info

Publication number
WO2011155717A2
WO2011155717A2 PCT/KR2011/003834 KR2011003834W WO2011155717A2 WO 2011155717 A2 WO2011155717 A2 WO 2011155717A2 KR 2011003834 W KR2011003834 W KR 2011003834W WO 2011155717 A2 WO2011155717 A2 WO 2011155717A2
Authority
WO
WIPO (PCT)
Prior art keywords
pouch
adhesive
layer
cutting
base film
Prior art date
Application number
PCT/KR2011/003834
Other languages
English (en)
French (fr)
Other versions
WO2011155717A3 (ko
Inventor
김원태
이한일
Original Assignee
삼아알미늄(주)
플레어 플렉시블 패키징 코포레이션
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 삼아알미늄(주), 플레어 플렉시블 패키징 코포레이션 filed Critical 삼아알미늄(주)
Priority to MX2012007691A priority Critical patent/MX2012007691A/es
Priority to CA2786039A priority patent/CA2786039A1/en
Priority to US13/520,315 priority patent/US20130008134A1/en
Priority to CN2011800062445A priority patent/CN102753447A/zh
Publication of WO2011155717A2 publication Critical patent/WO2011155717A2/ko
Publication of WO2011155717A3 publication Critical patent/WO2011155717A3/ko

Abstract

직선형 절취특성을 갖는 파우치 및 제조방법 그리고 그 파우치 제조장치를 제공한다. 상기 파우치는 습기나 산소로부터 장기적인 보존성이 요구되는 내용물 포장을 위한 포장재로서, 전면시트와 후면시트 2매의 합성수지시트를 기반으로 하며, 개구 위치에 찢김 개시점을 나타내는 노치를 갖고, 노치로부터 개구 위치를 따라 직선상으로 연속되는 다수의 절취홈이 일정한 간격으로 이격 형성된 구성을 갖고, 파우치 제조방법은, 기재필름 제작, 절취홈 가공, 표면보호층에 접착제 도포 및 건조, 기재필름과 표면보호층 접합, 대면적 시트 씰링 및, 씰링 처리된 대면적 시트 재단 및 노치 형성 과정을 포함하며, 상기 파우치 제조장치는, 제1 권취부 및 제2 권취부와, 접착제 도포부, 챔버, 형상가공장치, 라미네이팅 처리부, 히트씰 및 커팅부를 포함하여 구성되는 것을 요지로 한다.

Description

직선형 절취특성을 갖는 파우치 및 제조방법 그리고 그 파우치 제조장치
본 발명은 습기나 산소로부터 장기적인 보존성이 요구되는 내용물 포장을 위한 파우치에 관한 것으로, 상세하게는 항상 규정된 직선형 절취라인을 따라 매끄러운 절취가 이루어질 수 있도록 절취라인를 형성한 직선형 절취특성을 갖는 파우치 및 제조방법 그리고 그 파우치 제조장치에 관한 것이다.
포장의 가장 중요한 목적은 내용물 보호와 보존이다. 특히, 습기나 산소에 의해 보존성이 좌우되는 제품에 대해서는 수증기 및 가스 배리어성이 우수한 포장 재료를 사용하고, 용기를 밀봉, 봉합하기 위해 확실한 씰을 할 필요가 있다.
하지만 보호기능과 함께 내용물을 꺼낼 때의 간편성, 즉 개봉 용이성(Easy opening)도 매우 중요한 포장의 기능이며, 이 밀봉성과 개봉성의 상반하는 두 가지 요소를 양립시켜야 비로서 우수한 포장이라 할 수 있다.
플라스틱 필름을 주체로 한 라미네이트 포장재를 이용한 식품/의약품용 파우치나 필로우파우치, 또는 스틱 포장 파우치 등의 히트씰 연포장 파우치는 상품이 필요한 여러 가지 포장 기능을 발휘할 수 있어서 포장분야에서 널리 이용되고 있다.
라미네이트 필름은 기본적으로 베이스 필름, 배리어층 및 실란트 필름으로 구성되고, 포장공정에 따라서 제대, 충진 봉합되지만 일반적으로 제대 및 봉합은 히트씰로 행해진다.
히트씰 연포장 파우치의 밀봉에는 전술한 것과 같이 내용물의 보호가 충분히 유지될 수 있도록 균일하고, 확실한 씰이 필요하지만, 자칫하면 내용물을 꺼낼 때 톱 씰을 간단히 벗겨내기 어려운 경향이 있다. 이 때문에 대부분의 연포장 파우치에서는 개구수단으로써 이지커트(Easy cut) 기능이 필요하다.
히트씰 연포장 파우치의 개봉 용이 수단으로써 일반적으로 행해지는 것은 개구 위치에 찢김 개시점(notch)을 나타내는 칼자국을 넣는 방법이다. 이처럼 찢김 개시점 즉, 노치를 형성하면 노치로 인해 커트의 개시는 용이하지만, 파우치를 구성하는 기재 즉, 필름의 특성에 따라 인열 방향(찢겨지는 방향)이 불규칙한 경우라면, 커트성이 나쁘고 방향성도 불규칙하여 매끄럽지 못한 패턴으로 찢겨져 버리는 문제가 있다.
이에 대한 개선책으로, 레이져 가공을 통해 절취선(切取線)을 따라 미세한 구멍을 일정한 간격으로 내어 개봉 시 절취부위가 매끄럽고 반듯하게 절취될 수 있도록 한 방법이 이용되고는 있다. 하지만 이는 천공된 구멍들로 인하여 작은 충격이나 눌림과 같은 조그만 외압에도 파우치가 쉽게 터질 수 있어서, 일회용 커피, 조미료와 같이 분말제품을 포장하는 소형 파우치에 국한되어 주로 사용되고 있는 실정이다.
본 발명이 해결하고자 하는 기술적 과제는, 파우치를 구성하는 기재 즉, 필름의 특성에 따라 인열 방향이 불규칙한 경우라도 용이한 커트성을 보장할 수 있는 직선형 절취특성을 갖는 파우치 및 제조방법 그리고 그 파우치 제조장치를 제공하고자 하는 것이다.
본 발명이 해결하고자 하는 다른 기술적 과제는, 커트가 시작되는 시점에서의 힘이 방향성이 지정된 방향으로부터 어긋나게 작용하더라도 절취에 있어서는 항상 규정된 직선형 절취라인을 따라 매끄러운 절취가 이루어질 수 있는 파우치 및 제조방법 그리고 그 파우치 제조장치를 제공하고자 하는 것이다.
상기한 과제를 해결하기 위한 기술적인 수단으로서 본 발명은, 습기나 산소로부터 장기적인 보존성이 요구되는 내용물 포장을 위한 포장재로서, 전면시트와 후면시트 2매의 합성수지시트를 기반으로 하며, 개구 위치에 찢김 개시점을 나타내는 노치를 갖고, 노치로부터 개구 위치를 따라 직선상으로 연속되는 다수의 절취홈이 일정한 간격으로 이격되게 형성된 절취라인을 갖는 직선형 절취특성을 갖는 파우치를 제공한다.
여기서 상기 전면시트 및 후면시트는, 보강층과 열접착수지층으로 이루어진 기재필름 상에 표면보호층이 적층형성된 구성을 갖고, 상기 절취홈은 표면보호층과 접합하는 방향의 기재필름 일면에 형성되는 것을 특징으로 한다.
그리고 상기 절취홈은, 적어도 2개 이상을 상하방향으로 일정한 간격으로 형성하여, 절취 과정 중 파우치를 찢는 힘이 지정된 방향으로부터 어긋나더라도 절취에 있어서는 이웃하는 다른 절취홈을 따라 거의 일직선에 가까운 절취패턴을 유지할 수 있도록 하는 것이 바람직하고, 이를 위한 절취홈 간의 간격은 0.1mm ~ 2mm 정도가 적당하다.
바람직한 실시예로서 상기 표면보호층, 보강층, 열접착수지층은 순차적으로, 폴리에스터 필름(PET), 나일론 필름, 무연신 필름(CPP) 또는 PE 필름을 소재로 하거나, 폴리에스터 필름(PET), 나일론 표면에 알루미늄이 증착된 합성필름, 무연신 필름(CPP) 또는 PE 필름이 소재로 이용될 수 있다.
이때, 상기 표면보호층, 보강층, 열접착수지층은, 각 층 사이에 접착층을 형성시켜 라미네이팅을 통해 접합시키는 것이 바람직하다.
상기한 과제를 해결하기 위한 다른 기술적인 수단으로서 본 발명은, (a) 보강층과 열접착수지층으로 이루어진 기재필름을 형성하는 단계; (b) 내용물 정보가 인쇄처리된 표면보호층 이면에 접착제를 도포하고 이를 건조시키는 단계; (c) 표면보호층과 접속하게 될 기재필름 일면에 일정한 간격으로 직선형 절취홈을 가공하여 절취라인을 형성시키는 단계; (d) 기재필름의 보강층 위에 상기 표면보호층을 접합시켜 대면적의 전면시트와 후면시트를 형성하는 단계; (e) 전, 후면 두 개의 대면적 시트를 접촉시킨 상태로 이송시키면서 일정한 구획으로 대면적 시트를 씰링하는 단계; (f) 씰링 처리된 대면적 시트를 구획된 크기별로 재단함과 동시에 각각의 파우치에 찢김 개시점이 되는 노치를 형성시키는 단계;를 포함하는 매끄러운 절취특성을 갖는 파우치 제작방법을 제공한다.
이때, 상기 (b)단계에서의 접착제 도포는, 상기 표면보호층 이면이 접착제를 수용하고 있는 수용부에 일부가 노출가능하게 장착된 접착제 도포 로울러 표면에 접촉된 상태로 이동하면서 연속적으로 도포되도록 하는 것이 바람직하다.
나아가, 상기 (b)단계에서의 접착제 건조는, 입구와 출구를 갖고 내부에 열풍(熱風)이 분사되는 챔버(30)에 상기 표면보호층을 연속적으로 통과시켜 건조가 이루어지도록 하는 것이 좋다.
또한, 상기 (c)단계에서의 절취라인은, 상기 기재필름을 원주면에 미세한 요철패턴의 형상가공면을 형성한 형상가공 로울러 및 이와 맞물려 회전하는 로울러로 구성된 형상가공장치를 연속통과시켜서 연속적으로 가공이 이루어지도록 하는 것이 바람직하다.
바람직하게, 형상가공 로울러에 형성된 요철패턴의 폭(W)은 파우치에 형상가공 되어지는 상기한 절취라인 간의 간격을 고려하여, 0.1mm ~ 2mm 정도의 간격으로 형성되도록 구성하는 것이 좋다.
또한 본 발명은, 내용물 정보가 인쇄처리된 표면보호층을 권취한 제1 권취부; 상기 제1 권취부에 권취된 표면보호층 이면에 연속적으로 접착제를 도포하는 접착제 도포부; 표면보호층 이면에 도포된 접착제 건조를 위한 챔버; 보강층과 열접착수지층으로 이루어진 기재필름을 권취한 제2 권취부; 상기 기재필름에 일정한 간격으로 직선형 절취홈을 연속적으로 가공하는 형상가공장치; 접착제가 도포된 표면보호층과 절취홈이 형성된 기재필름을 라미네이팅 처리하여 접착시키는 라미네이팅 처리부; 접촉상태로 이송되는 2 매의 대면적 시트를 일정한 구획으로 씰링하는 히트씰; 및 씰링 처리된 대면적 시트를 구획된 크기별로 재단함과 동시에 각각의 파우치에 찢김 개시점이 되는 노치를 형성하는 커팅부;를 포함하여 구성되는 것을 특징으로 하는 직선형 절취특성을 갖는 파우치 제조장치를 제공한다.
여기서, 상기 접착제 도포부는, 접착제가 수용된 수용부에 접착제 도포 로울러 일부가 외부로 노출가능하게 회전장착된 구성일 수 있다.
그리고 상기 챔버는, 이면에 접착제가 도포된 상기 표면보호층이 수평방향으로 연속통과가능한 구성의 입구와 출구를 갖고, 내부에는 상기 접착제 건조를 위한 열풍이 분사하는 열풍분사노즐이 일정한 이격패턴으로 다수 설치된 구성일 수 있다.
또한, 상기 형상가공장치는, 원주면에 미세한 요철패턴의 형상가공면을 형성한 형상가공 로울러 및 이와 맞물려 회전하는 로울러를 포함하며, 상기 형상가공 로울러는 실린더 및 이 실린더에 연동하는 리니어 가이드로서 전, 후방으로 진퇴 가능하게 구성될 수 있다.
이때, 상기 형상가공 로울러에 형성된 요철패턴의 폭(W)은, 파우치에 형상가공 되어지는 상기한 절취홈 사이의 간격을 고려하여, 0.1mm ~ 2mm 정도의 간격으로 형성되도록 구성하는 것이 좋다.
바람직하게, 본 발명에 따른 시트 제조장치는 라미네이팅 처리부를 거치면서 표면보호층과 기재필름의 접착으로 이루어진 대면적 시트 냉각을 위한 냉각로울러;를 더 포함하는 구성일 수 있다.
상기한 본 발명에 따른 파우치에 의하면, 파우치를 구성하는 기재 즉, 필름의 특성에 따라 인열 방향이 불규칙한 경우라도 용이한 커트성이 보장되고, 커트가 시작되는 시점에서의 힘이 방향성이 지정된 방향으로부터 어긋나게 작용하더라도 절취에 있어서는 항상 규정된 직선형 절취라인을 따라 매끄러운 절취가 이루어질 수 있다.
즉, 본 발명에 의한 파우치는, 커트성이 좋고 찢김의 방향성도 규칙적이어서, 개봉과정에서 매끄럽지 못한 개봉으로 인하여 내용물이 원치 않게 외부로 쏟아지거나 개구 주위에 지저분한 형태로 존재하는 것을 방지할 수 있다.
또한 상기한 본 발명에 따른 파우치 제조방법 및 제조장치를 이용하여 파우치 및 시트를 제조함에 있어서는, 절취라인을 갖는 대면적 시트지의 제작, 씰링, 커트, 노치형성 등의 공정이 단계별 독립된 작업이 아닌 연속되는 하나의 공정을 통해 진행됨에 따라, 생산성 향상 및 대량생산에 있어 유리하다는 이점이 있다.
도 1은 본 발명인 직선형 절취특성을 갖는 파우치의 사시도.
도 2는 본 발명의 일 실시예에 따른 파우치의 개구 위치 확대 단면도.
도 3은 본 발명의 다른 실시예에 따른 파우치의 개구 위치 확대 단면도.
도 4는 본 발명에 따른 파우치의 찢김 과정을 보여주는 위한 작동상태 사시도.
도 5는 본 발명에 따른 파우치 제작과정을 보여주기 위한 공정 흐름도.
도 6은 본 발명에 따른 파우치의 시트를 제조하기 위한 장치의 개략 구성도.
도 7, 도 8은 도 6에 도시된 시트 제조장치에서 시트에 절취홈 가공을 수행하는 형상가공장치의 평면도 및 측면도.
이하, 본 발명의 바람직한 실시예를 첨부도면을 참조하여 상세히 설명하기로 한다.
도 1 내지 도 3을 참조하여 본 발명의 실시예에 따른 파우치에 대해 먼저 살펴보면, 상기 파우치는 습기나 산소로부터 장기적인 보존성이 요구되는 내용물 포장을 위한 포장재로서, 전면시트와 후면시트 2매의 합성수지시트를 기반으로 하며, 개구 위치에 찢김 개시점을 나타내는 노치(5)를 갖고, 이 노치(5)로부터 개구 위치를 따라 직선상으로 연속되는 다수의 절취홈(40)이 일정한 간격으로 이격되어 형성된 절취라인(4)을 갖는 구성으로 이루어진다.
본 발명에서 상기 전면시트 및 후면시트는, 보강층(20)과 열접착수지층(30)으로 이루어진 기재필름(25) 상에 표면보호층(10)이 적층형성된 구성을 가지며, 표면보호층(10), 보강층(20), 열접착수지층(30)은 접착제 도포를 통한 라미네이팅(Laminating)을 통해 그 사이에 접착층이 존재하는 형태로 상호 접착이 이루어진다.
상기 표면보호층(10)은 수분침투나 산소투과와 같은 것으로부터 내용물을 보호하기 위한 배리어(Barrier)기능을 수행하며, 상기 열접착수지층(30)은 포장 내용물의 위생성 확보를 위한 것이다. 그리고 상기 보강층(20)은 파우치가 포장재로서 역할을 수행함에 있어서의 파단강성 확보 및 내열성, 내한성 등의 특성을 부여하며, 특히 파우치의 찢김이 개시된 시점에서의 용이한 커트성을 부여한다.
상기 표면보호층(10)으로는 포장(Packaging)과 증착(Metallizing)에 적합한 투명성, 내열성, 고장력, 뛰어난 치수안정성, 비투과성, 내습성, 내수성, 내화학성이 우수한 폴리에스터 필름(PET FILM 'PET 필름'이라 한다)이 적합하며, 열접착수지층(30)은 두께가 균일하며 매우 위생적인 필름으로 식품포장 등 유연포장의 소재로서 폭넓게 이용되는 무연신 필름 또는 폴리에틸렌 필름(PE film)이 소재로 이용될 수 있다.
상기 보강층(20)은 도 2의 실시예와 같이 내열 및 내한성 및 파대강도가 우수하면서 파우치를 개봉함에 있어 찢김 방향성 및 용이한 커트성을 부여하기에 적합한 나일론을 단독으로 한 소재 또는, 도 3의 다른 실시예에서와 같이 나일론(Nylon) 표면에 알루미늄 박판이 증착된 합성필름이 소재로 이용될 수 있다.
상기한 소재를 주체로 한 전, 후면 시트에 절취홈(40)을 형성시킴에 있어 상기 절취홈(40)은, 보강층(20)을 형성하는 나일론 필름 또는 나일론 합성필름에 열접착수지층(30)을 형성하는 무연신 필름이 접합되어 이루어진 기재필름(25)에 형성시키는 것이 바람직하다. 구체적으로는, 표면보호층(10)과 접속하는 방향에 위치한 기재필름(20)의 보강층(20) 일면에 형성시키는 것이 좋다.
표면보호층(10), 보강층(20), 열접착수지층(30)을 접합시켜 시트를 완성시킨 상태에서 절취홈(40)을 성형하는 것과 같이 표면가공을 수행하면, 상기 표면보호층(10)을 구성하는 PET 필름의 막이 손상될 수 있기 때문이다.
다시 말해, PET 필름의 경우 실리카(SILICA), 알루미나(ALUMINA)를 필름에 증착시켜 수분 및 산소투과를 억제시킴으로써 내용물(주로, 식품 또는 의약품)을 장기 보존할 수 있게 한 것이어서, 절취홈(40)을 성형하는 것과 같은 장력/충격 등의 외압을 받게 되면, 실리카(SILICA)와 알루미나(ALUMINA)에 의한 증착층의 막이 손상되며, 결과적으로는 내수성, 차단성이 떨어져 포장재로서 기능을 잃게 된다.
위와 같은 이유로서 상기 기재필름(25)에 절취홈(40)을 형성함에 있어서도, 상기 절취홈(40)은 적어도 2개 이상이 상하방향으로 일정한 간격으로 형성되도록 하는 것이 바람직하다. 이는 절취 과정 중 파우치를 찢는 힘의 방향성이 일정치 않아 최초 찢김이 개시된 절취홈(40)으로부터 다소 벗어나더라도 인접해 있는 다른 절취홈(40)에 의해서 직선에 가까운 절취패턴을 유지할 수 있도록 하기 위함이며, 이를 위한 절취홈(40)의 간격은 0.1mm ~ 2mm 정도가 적당하다.
상기한 본 발명의 파우치에 의하면, 파우치의 개구 위치를 따라 직선상으로 연속되는 다수의 절취홈(40)이 일정한 간격으로 이격형성되어 절취라인(4)을 형성함으로써, 파우치를 구성하는 기재 즉, 필름의 특성에 따라 인열 방향이 불규칙한 경우라도 용이한 커트성이 보장되고, 커트가 시작되는 시점에서의 힘이 방향성이 지정된 방향으로부터 어긋나게 작용하더라도 절취에 있어서는 도 4에 도시한 바와 같이 항상 규정된 직선형 절취라인(4)을 따라 매끄러운 절취가 이루어질 수 있다.
다음은 상기한 구성으로 이루어진 본 발명의 실시예에 따른 파우치 제조방법에 대해 설명하기로 한다.
상기 파우치를 제조하기 위한 과정은 도 5에 도시한 바와 같이, 기재필름 제작, 표면보호층에 접착제 도포 및 건조, 절취홈 가공, 기재필름과 표면보호층 접합, 대면적 시트 씰링 및, 씰링 처리된 대면적 시트 재단 및 노치 형성 등 크게, 6 단계로 구성된 공정으로 구성된다.
단계별로는 먼저, 보강층(20)과 열접착수지층(30)을 접합시켜 기재필름(25)을 제작하는 단계로서, 상기 보강층(20)으로는 앞서 설명한 바와 같이 내열 및 내한성이 우수하면서 파우치를 개봉함에 있어 찢김 방향성 및 용이한 커트성을 부여하기에 적합한 나일론을 단독으로 한 소재 또는, 나일론 표면에 알루미늄 박판이 증착된 합성필름이 소재로 이용되며, 열접착수지층(30)으로는 유연포장의 소재로서 폭넓게 이용되며 매우 위생적인 무연신 또는 폴리에틸렌 필름을 소재로 한다.
위와 같은 과정에서 보강층(20)과 열접착수지층(30)의 접합은, 보강층(20) 또는 열접착수지층(30)에 접착제를 도포하고 건조시켜 접착층(15)을 형성시킨 상태에서, 상기 보강층(20)과 열접착수지층(30)을 맞댄 상태로 압착 로울러를 통과시켜 층간 접촉을 구현하는 라미네이트(LAMINATE) 가공으로 접합을 구현할 수 있으나, 열융착 테이프를 이용하는 것과 같이 보강층(20)과 열접착수지층(30)을 손상시키지 않으면서 접합을 구현할 수 있다면 특정한 접합방법에 구애됨이 없이 적용 가능하다.
기재필름(25)에 접합시켜 대면적 시트를 형성하기 위한 표면보호층(10)은, 그 표면에 내용물 정보(로고, 내용물 사진, 조리방법...등등)를 인쇄처리한 후 그 이면에 접착제를 도포하고 건조 챔버(30)를 이용하여 열풍 건조시켜 형성시킨다.
위 과정에서의 접착제 도포는, 상기 표면보호층(10) 이면이 접착제를 수용하고 있는 수용부(202)에 일부가 노출가능하게 장착된 접착제 도포 로울러(204) 표면에 접촉된 상태로 이동하면서 연속적인 도포가 이루어지도록 하는 것이 바람직하며, 접착제 건조는, 입구(302)와 출구(304)를 갖고 내부에 열풍(熱風)이 분사되는 챔버(300)에 상기 표면보호층(10)을 연속적으로 통과시켜 건조가 이루어지도록 하는 것이 좋다.
다음은 상기 과정을 통해 제작된 기재필름(25)에 일정한 간격으로 직선형 절취홈(40)을 가공하여 절취라인(4)을 형성시키는 과정으로서, 이 과정에서는 도 7 내지 도 8에 도시된 형태의 형상가공장치(500)(상세한 설명은 후술하기로 함)를 이용하여 추후 파우치의 개구 위치가 되는 기재필름(25) 적소에 절취라인(4)을 연속적으로 형성하며, 절취라인(4)을 형성하는 절취홈 사이의 간격은 0.1mm ~ 2mm 정도가 되도록 하는 것이 좋다.
상기한 과정을 통해 제작된 기재필름(25) 및 표면보호층(10)은 라미네이션(LAMINATION) 공정을 통해 상호 접합시킴으로써, 대면적의 전면시트와 후면시트를 형성하게 된다. 도 5에서 참조부호 720를 대면적 전면시트가 권취된 권취로울러라 하면, 참조부호 740는 대면적 후면시트가 권취된 권취로울러이며, 이 대면적 후면시트 역시 앞서 설명한 과정과 동일한 방법으로 제작된다.
다음으로, 파우치를 형성하기에 적합한 크기로 2 매의 전, 후면 대면적 시트를 씰링하는 과정으로서, 일반적인 히트씰(800)을 이용하여 전, 후면 두 개의 대면적 시트(1, 2)를 접촉시킨 상태로 이송시키면서 파우치 형성에 적합한 구획(도 5의 부분 확대도에서 빗금친 곳이 씰링처리된 부분에 해당한다)으로 2 매의 대면적 시트(1, 2)를 씰링시킨다.
마지막으로, 씰링 처리된 대면적 시트를 구획된 크기별로 재단함과 동시에 각각의 파우치의 개구 위치에 찢김 개시점이 되는 노치(5)를 형성시킴으로써 본 발명의 실시예에 따른 직선형 절취특성을 갖는 파우치가 완성되는 것이다.
상기한 공정을 따라 파우치를 제조함에 있어 이용되는 파우치 제조장치에 대해 간단히 살펴보기로 한다.
본 실시예에 따른 직선형 절취특성을 갖는 파우치를 제조함에 있어 이용되는 파우치 제조장치는 도 5에서와 같이, 제1 권취부(100) 및 제2 권취부(400)와, 접착제 도포부(200), 챔버(300), 형상가공장치(500), 라미네이팅 처리부(600), 히트씰(800) 및 커팅부(900)를 포함하는 구성으로 이루어진다.
상기 제1 권취부(100)와 제2 권취부(400)에는 각각, 로고, 내용물 사진, 조리방법 등의 내용물 정보가 인쇄처리된 표면보호층(10) 및 보강층(20)과 열접착수지층(30) 접합으로 이루어진 기재필름(25)이 권취되어 있으며, 상기 접착제 도포부(200)는 상기 제1 권취부(100)에 권취된 표면보호층(10) 이면에 연속적으로 접착제를 도포하는 역할을 수행한다.
상기 접착제 도포부(200)는 접착제를 수용하고 있는 수용부(202)에 일부가 노출가능하게 장착된 접착제 도포 로울러(204)를 포함하며, 상기 표면보호층(10) 이면이 외부로 노출된 상기 도포 로울러(204) 표면에 접촉된 상태로 이동하면서 연속적으로 도포가 수행된다.
상기 챔버(300)는 표면보호층(10) 이면에 도포된 접착제를 건조시키기 위한 것이며, 입구와 출구를 갖고 내부에는 접착제 건조를 위한 열풍(熱風)이 전체에 걸쳐 고르게 분사될 수 있는 구성을 가진다. 따라서, 상기 이면에 접착제를 도포한 표면보호층(10)이 라인을 따라 연속적으로 이동하더라도 이러한 챔버(300)에 의해 이동되는 피 건조물에 대한 건조가 무리 없이 진행될 수 있다.
상기 형상가공장치(500)는 본 발명에 따른 파우치 개구 위치에 본 발명의 핵심이 되는 절취홈(40)을 형성시키기 위한 장치로서, 도 7 내지 도 8과 같이, 원주면에 미세한 요철패턴의 형상가공면을 형성한 형상가공 로울러(502) 및 이와 맞물려 회전하는 로울러(504)를 포함하며, 상기 형상가공 로울러(502)가 실린더(506) 및 이 실린더(506)에 연동하는 리니어 가이드(508)로서 전, 후방으로 진퇴 가능한 구조로 되어 있다.
이에 따라, 상기 형상가공 로울러(502) 및 이와 맞물려 회전하는 로울러(504) 사이를 기재필름(25)을 통과시키면, 상기 형상가공 로울러(502) 표면의 요철패턴의 형상가공면에 의해 기재필름(25)에 요철패턴의 단면을 가지며 기재필름(25) 이동방향으로 연속되는 절취홈(40)을 형성시킬 수 있다. 이때, 기재필름(25)에 형상가공 되어지는 상기한 절취홈(40) 사이의 간격을 고려하면, 상기 형상가공면에 형성된 요철패턴의 폭(W) 역시 0.1mm ~ 2mm 정도의 간격으로 형성함이 적당하다.
상기 라미네이팅 처리부(600)는 긴밀히 맞닿아 회전하는 2 개의 로울러 사이로 접착제가 도포된 표면보호층(10)과 절취홈(40)이 형성된 기재필름(25)을 통과시켜 공기층을 배재시키는 형태로 접착을 수행하는 공지된 형태이며, 상기 히트씰(800)은 상, 하로 상호 이격되거나 접속가능한 여러 쌍의 씰링 바가 2 매의 대면적 시트에 여러 개의 파우치를 형성시키기에 적합한 구획으로 배치(배치 형태 미도시)된 구성을 가진다.
상기 커팅부(900)는 씰링 처리된 대면적 시트를 가로, 세로 구획된 크기별로 재단하기에 적합한 배치를 갖는 다수의 커터(부호 생략)를 포함하며, 각각의 파우치에 찢김 개시점이 되는 노치(5)를 형성시키는 펀칭 또한 포함하고 있다. 미설명 부호 650은 라미네이팅 처리부(600)를 거치면서 표면보호층(10)과 기재필름(25)의 접착으로 이루어진 대면적 시트를 냉각시키는 냉각로울러를 가르킨다.
상기한 본 발명에 따른 파우치 제조방법 및 제조장치에 의하면, 절취라인을 갖는 대면적 시트지의 제작, 씰링, 커트, 노치형성 등의 공정이 단계별 독립된 작업이 아닌 연속되는 하나의 공정으로 수행가능하므로, 생산성 및 대량생산에 있어 유리하다.
이상의 본 발명의 상세한 설명에서는 그에 따른 특별한 실시 예에 대해서만 기술하였다. 하지만 본 발명은 상세한 설명에서 언급되는 특별한 형태로 한정되는 것이 아닌 것으로 이해되어야 하며, 오히려 첨부된 청구범위에 의해 정의되는 본 발명의 정신과 범위 내에 있는 모든 변형물과 균등물 및 대체물을 포함하는 것으로 이해되어야 한다.
(부호의 설명)
<파우치>
1, 2 : 시트 4 : 절취라인
5 : 노치(Notch) 10 : 표면보호층
20 : 보강층 25 : 기재필름
30 : 열접착수지층 40 : 절취홈
<파우치 제조장치>
100 : 제1 권취부 200 : 접착제 도포부
202 : 접착제 수용부 204 : 접착제 도포 로울러
300 : 챔버 302, 304 : 챔버 입구, 출구
400 : 제2 권취부 500 : 형상 가공장치
502 : 형상가공 로울러 504 : 로울러
506 : 실린더 508 : 리니어 가이드
600 : 라미네이팅 처리부 650 : 냉각 로울러
800 : 히트씰(Heat seal) 900 : 커팅부

Claims (17)

  1. 습기나 산소로부터 장기적인 보존성이 요구되는 내용물 포장을 위한 포장재이며, 전면시트(1)와 후면시트(2) 2매의 합성수지시트를 기반으로 하며, 개구 위치에 찢김 개시점을 나타내는 노치(5)를 갖고, 노치(5)로부터 개구 위치를 따라 직선상으로 연속되는 다수의 절취홈(40)이 일정한 간격으로 이격 형성된 절취라인(4)을 갖는 파우치에 있어서,
    상기 전면시트(1) 및 후면시트(2)는, 보강층(20)과 열접착수지층(30)으로 이루어진 기재필름(25) 상에 표면보호층(10)이 적층형성된 구성을 갖고, 상기 절취홈(40)은 표면보호층(10)과 접합하는 기재필름(25)의 보강층(20) 일면에 형성되는 것을 특징으로 하는 직선형 절취특성을 갖는 파우치.
  2. 제 1 항에 있어서,
    상기 절취홈(40)은 2개 이상이 상하방향으로 일정한 간격으로 이격 형성된 구성인 것을 특징으로 하는 직선형 절취특성을 갖는 파우치.
  3. 제 1 항에 있어서,
    상기 절취홈(40)의 간격은 0.1mm ~ 2mm 인 것을 특징으로 하는 직선형 절취특성을 갖는 파우치.
  4. 제 1 항에 있어서,
    상기 표면보호층(10), 보강층(20), 열접착수지층(30)은 순차적으로, 폴리에스터 필름(PET), 나일론 필름, 무연신 또는 PE 필름을 소재로 하는 것을 특징으로 하는 직선형 절취특성을 갖는 파우치.
  5. 제 1 항에 있어서,
    상기 표면보호층(10), 보강층(20), 열접착수지층(30)은 순차적으로, 폴리에스터 필름(PET), 나일론 표면에 알루미늄이 증착된 합성필름, 무연신 또는 PE 필름을 소재로 하는 것을 특징으로 하는 직선형 절취특성을 갖는 파우치.
  6. 제 4 항 또는 제 5 항에 있어서,
    상기 표면보호층(10), 보강층(20), 열접착수지층(30)은, 각 층 사이에 접착층(15)을 형성시켜 라미네이팅을 통해 접합되는 것을 특징으로 하는 직선형 절취특성을 갖는 파우치.
  7. (a) 보강층과 열접착수지층으로 이루어진 기재필름을 형성하는 단계;
    (b) 내용물 정보가 인쇄처리된 표면보호층 이면에 접착제를 도포하고 이를 건조시키는 단계;
    (c) 표면보호층과 접합하게 될 기재필름의 보강층 일면에 일정한 간격으로 직선형 절취홈을 가공하여 절취라인을 형성시키는 단계;
    (d) 기재필름의 보강층 위에 상기 표면보호층을 접합시켜 대면적의 전면시트와 후면시트를 형성하는 단계;
    (e) 전, 후면 두 개의 대면적 시트를 접촉시킨 상태로 이송시키면서 일정한 구획으로 대면적 시트를 씰링하는 단계;
    (f) 씰링 처리된 대면적 시트를 구획된 크기별로 재단함과 동시에 각각의 파우치에 찢김 개시점이 되는 노치를 형성시키는 단계;를 포함하는 매끄러운 절취특성을 갖는 파우치 제조방법.
  8. 제 7 항에 있어서,
    상기 (b)단계에서의 접착제 도포는, 상기 표면보호층 이면이 접착제를 수용하고 있는 수용부에 일부가 노출가능하게 장착된 접착제 도포 로울러 표면에 접촉된 상태로 이동하면서 연속적으로 도포되도록 하는 것을 특징으로 하는 직선형 절취특성을 갖는 파우치 제조방법.
  9. 제 7 항에 있어서,
    상기 (b)단계에서의 접착제 건조는, 입구와 출구를 갖고 내부에 열풍(熱風)이 분사되는 챔버에 상기 표면보호층을 연속적으로 통과시켜 건조가 이루어지도록 하는 것을 특징으로 하는 직선형 절취특성을 갖는 파우치 제조방법.
  10. 제 7 항에 있어서,
    상기 (c)단계에서의 절취라인은, 상기 기재필름은 원주면에 미세한 요철패턴의 형상가공면을 형성한 형상가공 로울러 및 이와 맞물려 회전하는 로울러로 구성된 형상가공장치를 연속통과시킴으로써 형성시키는 것을 특징으로 하는 직선형 절취특성을 갖는 파우치 제조방법.
  11. 제 10 항에 있어서,
    상기 형상가공 로울러에 형성되는 요철패턴의 폭(W)은 0.1mm ~ 2mm 이 되도록 하는 것을 특징으로 하는 직선형 절취특성을 갖는 파우치 제조방법.
  12. 내용물 정보가 인쇄처리된 표면보호층을 권취한 제1 권취부(100);
    상기 제1 권취부(100)에 권취된 표면보호층 이면에 연속적으로 접착제를 도포하는 접착제 도포부(200);
    표면보호층 이면에 도포된 접착제 건조를 위한 챔버(30);
    보강층(20)과 열접착수지층(30)으로 이루어진 기재필름(25)을 권취한 제2 권취부(400);
    상기 기재필름(25)의 보강층(20) 일면에 일정한 간격으로 직선형 절취홈(40)을 연속적으로 가공하는 형상가공장치(500);
    접착제가 도포된 표면보호층과 절취홈(40)이 형성된 기재필름(25)을 라미네이팅하여 대면적 시트를 형성시키는 라미네이팅 처리부(600);
    접촉상태로 이송되는 2 매의 대면적 시트를 일정한 구획으로 씰링하는 히트씰(800); 및
    씰링 처리된 대면적 시트를 구획된 크기별로 재단함과 동시에 각각의 파우치에 찢김 개시점이 되는 노치를 형성하는 커팅부(900);를 포함하여 구성되는 것을 특징으로 하는 직선형 절취특성을 갖는 파우치 제조장치.
  13. 제 12 항에 있어서,
    상기 접착제 도포부(200)는, 접착제가 수용된 수용부(202)에 접착제 도포 로울러(204) 일부가 외부로 노출가능하게 회전장착된 구성인 것을 특징으로 하는 직선형 절취특성을 갖는 파우치 제조장치.
  14. 제 12 항에 있어서,
    상기 챔버(30)는, 이면에 접착제가 도포된 상기 표면보호층이 수평방향으로 연속통과가능한 구성의 입구(302)와 출구(304)를 갖고, 내부에는 상기 접착제 건조를 위한 열풍이 분사하는 열풍분사노즐이 일정한 이격패턴으로 다수 설치된 구성인 것을 특징으로 하는 직선형 절취특성을 갖는 파우치 제조장치.
  15. 제 12 항에 있어서,
    상기 형상가공장치(500)는, 원주면에 미세한 요철패턴의 형상가공면을 형성한 형상가공 로울러(502) 및 이와 맞물려 회전하는 로울러(504)를 포함하며, 상기 형상가공 로울러(502)는 실린더(506) 및 이 실린더(506)에 연동하는 리니어 가이드(508)로서 전, 후방으로 진퇴 가능하게 구성되는 것을 특징으로 하는 직선형 절취특성을 갖는 파우치 제조장치.
  16. 제 15 항에 있어서,
    상기 형상가공 로울러(502)에 형성된 요철패턴의 폭(W)은 0.1mm ~ 2mm 인 것을 특징으로 하는 직선형 절취특성을 갖는 파우치 제조장치.
  17. 제 12 항에 있어서,
    라미네이팅 처리부(600)를 거치면서 표면보호층과 기재필름(25)의 접착으로 이루어진 대면적 시트 냉각을 위한 냉각로울러(650);를 더 포함하는 직선형 절취특성을 갖는 파우치 제조장치.
PCT/KR2011/003834 2010-06-08 2011-05-25 직선형 절취특성을 갖는 파우치 및 제조방법 그리고 그 파우치 제조장치 WO2011155717A2 (ko)