WO2011099534A1 - 剥離剤組成物 - Google Patents
剥離剤組成物 Download PDFInfo
- Publication number
- WO2011099534A1 WO2011099534A1 PCT/JP2011/052779 JP2011052779W WO2011099534A1 WO 2011099534 A1 WO2011099534 A1 WO 2011099534A1 JP 2011052779 W JP2011052779 W JP 2011052779W WO 2011099534 A1 WO2011099534 A1 WO 2011099534A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- monomer
- group
- release agent
- agent composition
- meth
- Prior art date
Abstract
Description
単量体(a):下式(1)で表される化合物。
(Z-Y)nX ・・・(1)
ただし、Zは、炭素数1~6のポリフルオロアルキル基または下式(2)で表される基であり、
Yは、2価有機基または単結合であり、
nは、1または2であり、
Xは、nが1の場合は、下式(3-1)~(3-5)で表される基のいずれかであり、nが2の場合は、下式(4-1)~(4-4)で表される基のいずれかである。
CmF2m+1O(CF2CF(CF3)O)dCF(CF3)- ・・・(2)。
ただし、mは、1~6の整数であり、dは、1~4の整数である。
-C(R)=CH2 ・・・(3-1)、
-C(O)OC(R)=CH2 ・・・(3-2)、
-OC(O)C(R)=CH2 ・・・(3-3)、
-OCH2-φ-C(R)=CH2 ・・・(3-4)、
-OCH=CH2 ・・・(3-5)。
ただし、Rは、水素原子、メチル基またはハロゲン原子であり、φは、フェニレン基である。
-CH[-(CH2)pC(R)=CH2]- ・・・(4-1)、
-CH[-(CH2)pC(O)OC(R)=CH2]- ・・・(4-2)、
-CH[-(CH2)pOC(O)C(R)=CH2]- ・・・(4-3)、
-OC(O)CH=CHC(O)O- ・・・(4-4)。
ただし、Rは、水素原子、メチル基またはハロゲン原子であり、pは、0~4の整数である。
単量体(b):ポリフルオロアルキル基を有さず、炭素数が18~30のアルキル基を有する(メタ)アクリレート。
単量体(c):ハロゲン化オレフィン。
単量体(d):ポリフルオロアルキル基を有さず、架橋しうる官能基を有する単量体。
[4]ノニオン性界面活性剤およびカチオン性界面活性剤をさらに含む、[1]~[3]のいずれかに記載の剥離剤組成物。
[6]前記含フッ素共重合体が媒体中に粒子として分散しており、含フッ素共重合体の平均粒子径が、10~1000nmである、[1]~[5]のいずれかに記載の剥離剤組成物。
[7]下記単量体(a)と下記単量体(b)を含み、単量体(a)と単量体(b)の質量比(単量体(a)/単量体(b))が1/1~1/10である単量体混合物を、重合開始剤存在下、共重合させる工程を有することを特徴とする剥離剤組成物の製造方法。
単量体(a):下式(1)で表される化合物。
(Z-Y)nX ・・・(1)。
ただし、Zは、炭素数1~6のポリフルオロアルキル基または下式(2)で表される基であり、
Yは、2価有機基または単結合であり、
nは、1または2であり、
Xは、nが1の場合は、下式(3-1)~(3-5)で表される基のいずれかであり、nが2の場合は、下式(4-1)~(4-4)で表される基のいずれかである。
CmF2m+1O(CF2CF(CF3)O)dCF(CF3)- ・・・(2)。
ただし、mは、1~6の整数であり、dは、1~4の整数である。
-C(R)=CH2 ・・・(3-1)、
-C(O)OC(R)=CH2 ・・・(3-2)、
-OC(O)C(R)=CH2 ・・・(3-3)、
-OCH2-φ-C(R)=CH2 ・・・(3-4)、
-OCH=CH2 ・・・(3-5)。
ただし、Rは、水素原子、メチル基またはハロゲン原子であり、φは、フェニレン基である。
-CH[-(CH2)pC(R)=CH2]- ・・・(4-1)、
-CH[-(CH2)pC(O)OC(R)=CH2]- ・・・(4-2)、
-CH[-(CH2)pOC(O)C(R)=CH2]- ・・・(4-3)、
-OC(O)CH=CHC(O)O- ・・・(4-4)。
ただし、Rは、水素原子、メチル基またはハロゲン原子であり、pは、0~4の整数である。
単量体(b):ポリフルオロアルキル基を有さず、炭素数が18~30のアルキル基を有する(メタ)アクリレート。
本発明の剥離剤組成物は、含フッ素共重合体と媒体を必須成分として含み、必要に応じて、界面活性剤、添加剤を含む。
(含フッ素共重合体)
本発明における含フッ素共重合体は、単量体(a)に基づく構成単位と、単量体(b)に基づく構成単位を必須構成単位として有し、必要に応じて、単量体(c)~(e)に基づく構成単位を有する含フッ素共重合体である。
単量体(a)は、化合物(1)である。
(Z-Y)nX ・・・(1)
Zは、炭素数が1~6のRf基、または下記基(2)である。
CmF2m+1O(CF2CF(CF3)O)dCF(CF3)- ・・・(2)。
ただし、mは、1~6の整数であり、dは、1~4の整数である。
Rf基の炭素数は、4~6が好ましい。Rf基は、直鎖状であってもよく、分岐状であってもよく、直鎖状が好ましい。
Zとしては、下記の基が挙げられる。
F(CF2)4-
F(CF2)5-
F(CF2)6-
(CF3)2CF(CF2)2-
2価有機基としては、アルキレン基が好ましい。アルキレン基は、直鎖状であってもよく、分岐状であってもよい。アルキレン基は、-O-、-NH-、-CO-、-SO2-、-CD1=CD2-(ただし、D1、D2は、それぞれ水素原子またはメチル基である。)等を有していてもよい。
-CH2-
-CH2CH2-
-(CH2)3-
-CH2CH2CH(CH3)-
-CH=CH-CH2-等。
Xは、nが1の場合は、基(3-1)~基(3-5)のいずれかであり、nが2の場合は、基(4-1)~基(4-4)のいずれかである。
-CR=CH2 ・・・(3-1)
-COOCR=CH2 ・・・(3-2)
-OCOCR=CH2 ・・・(3-3)
-OCH2-Φ-CR=CH2 ・・・(3-4)
-OCH=CH2 ・・・(3-5)
ただし、Rは、水素原子、メチル基またはハロゲン原子であり、Φはフェニレン基である。
-CH[-(CH2)pC(R)=CH2]- ・・・(4-1)、
-CH[-(CH2)pC(O)OC(R)=CH2]- ・・・(4-2)、
-CH[-(CH2)pOC(O)C(R)=CH2]- ・・・(4-3)、
-OC(O)CH=CHC(O)O- ・・・(4-4)。
ただし、Rは、水素原子、メチル基またはハロゲン原子であり、pは0~4の整数である。
単量体(b)は、ポリフルオロアルキル基を有さず、炭素数が18~30のアルキル基を有する(メタ)アクリレートである。アルキル基の炭素数が18以上であれば、剥離性が良好となる。アルキル基の炭素数が30以下であれば、相対的に融点が低く、ハンドリングしやすい。具体的には、ステアリル(メタ)アクリレート、ベヘニル(メタ)アクリレートが好ましく、得られる剥離剤組成物の機械的安定性が優れることから特にベヘニルアクリレートが好ましい。単量体(b)は、1種を単独で用いてもよく、2種以上を併用しても用いてもよい。単量体(b)として、ステアリル(メタ)アクリレートおよびベヘニル(メタ)アクリレートを併用する場合、単量体(b)全体におけるベヘニル(メタ)アクリレートの含有割合は、5質量%以上とすることが好ましい。
単量体(c)は、ハロゲン化オレフィンである。単量体(c)に基づく構成単位を有することにより、含フッ素共重合体からなる被膜の強度が向上し、被膜と物品との接着性が向上する。
単量体(d)は、Rf基を有さず、架橋しうる官能基を有する単量体である。架橋しうる官能基としては、共有結合、イオン結合または水素結合のうち少なくとも1つ以上の結合を有する官能基、または、該結合の相互作用により架橋構造を形成できる官能基が好ましい。単量体(d)に基づく構成単位を有することにより、含フッ素共重合体の被膜の耐熱性や耐摩耗性が向上する。単量体(d)の炭素数は2~50が好ましく、2~12がより好ましい。
該官能基としては、イソシアネート基、ブロックドイソシアネート基、アルコキシシリル基、アミノ基、アルコキシメチルアミド基、シラノール基、アンモニウム基、アミド基、エポキシ基、水酸基、オキサゾリン基、カルボキシル基、アルケニル基、スルホン酸基等が好ましい。特に、エポキシ基、水酸基、ブロックドイソシアネート基、アルコキシシリル基、アミノ基、またはカルボキシル基が好ましい。
単量体(d)としては、(メタ)アクリレート類、アクリルアミド類、ビニルエーテル類、またはビニルエステル類が好ましい。
2-イソシアナトエチル(メタ)アクリレート、3-イソシアナトプロピル(メタ)アクリレート、4-イソシアナトブチル(メタ)アクリレート、2-イソシアナトエチル(メタ)アクリレートの2-ブタノンオキシム付加体、2-イソシアナトエチル(メタ)アクリレートのピラゾール付加体、2-イソシアナトエチル(メタ)アクリレートの3,5-ジメチルピラゾール付加体、2-イソシアナトエチル(メタ)アクリレートの3-メチルピラゾール付加体、2-イソシアナトエチル(メタ)アクリレートのε-カプロラクタム付加体、3-イソシアナトプロピル(メタ)アクリレートの2-ブタノンオキシム付加体、3-イソシアナトプロピル(メタ)アクリレートのピラゾール付加体。
単量体(e)は、単量体(a)、単量体(b)、単量体(c)、および単量体(d)を除く単量体である。単量体(e)に基づく構成単位を有することにより、含フッ素共重合体の被膜の耐熱性や耐摩耗性の向上、変色の抑制などの効果が得られる。
メチルアクリレート、エチルアクリレート、プロピル(メタ)アクリレート、ブチル(メタ)アクリレート、シクロヘキシル(メタ)アクリレート、2-エチルヘキシル(メタ)アクリレート、ブチルメタクリレート、n-ヘキシル(メタ)アクリレート、酢酸ビニル、プロピオン酸ビニル、ブテン、イソプレン、ブタジエン、エチレン、プロピレン、ビニルエチレン、ペンテン、エチル-2-プロピレン、ブチルエチレン、シクロヘキシルプロピルエチレン、デシルエチレン、ドデシルエチレン、ヘキセン、イソヘキシルエチレン、ネオペンチルエチレン、(1,2-ジエトキシカルボニル)エチレン、(1,2-ジプロポキシカルボニル)エチレン、メトキシエチレン、エトキシエチレン、ブトキシエチレン、2-メトキシプロピレン、ペンチルオキシエチレン、シクロペンタノイルオキシエチレン、シクロペンチルアセトキシエチレン、スチレン、α-メチルスチレン、p-メチルスチレン、ヘキシルスチレン、オクチルスチレン、ノニルスチレン、クロロプレン、テトラフルオロエチレン、フッ化ビニリデン。
単量体(a)~(e)は、各単量体の中から適宜1種を単独で用いてもよく、2種以上を併用してもよい。
含フッ素共重合体における単量体(a)に基づく構成単位の割合は、剥離剤組成物の剥離強度の点から1~45質量%が好ましく、10~30質量%がより好ましく、15~20質量%が特に好ましい。
含フッ素共重合体における単量体(b)に基づく構成単位の割合は、剥離剤組成物の剥離強度の点から55~99質量%が好ましく、55~90質量%がより好ましく、55~85質量%が特に好ましい。
含フッ素共重合体における単量体(c)に基づく構成単位の割合は、物品との密着性および被膜強度の点から0~30質量%が好ましく、5~25質量%がより好ましく、10~25質量%が特に好ましい。
含フッ素共重合体における単量体(d)に基づく構成単位の割合は、被膜の剥離強度、耐熱性や耐摩耗性の点から0~20質量%が好ましく、0~10質量%がより好ましく、0.5~5質量%が特に好ましい。
含フッ素共重合体における単量体(e)に基づく構成単位の割合は、被膜の耐熱性や耐摩耗性の向上、変色の抑制などの効果の点から、0~15質量%が好ましく、0.1~10質量%がより好ましく、0.1~5質量%が特に好ましい。
本発明における単量体に基づく構成単位の割合は、含フッ素共重合体の製造時の単量体の仕込み量に基づいて算出する。
含フッ素共重合体の数平均分子量(Mn)は、20000以上が好ましく、30000以上が特に好ましい。一方、含フッ素共重合体の数平均分子量(Mn)は、500000以下が好ましく、200000以下が特に好ましい。
含フッ素共重合体の質量平均分子量(Mw)および数平均分子量(Mn)は、ゲルパーミエイションクロマトグラフィ(GPC)で測定される、ポリスチレン換算の分子量である。
媒体としては、水、アルコール、グリコール、グリコールエーテル、ハロゲン化合物、炭化水素、ケトン、エステル、エーテル、窒素化合物、有機酸等が挙げられ、溶解性、取扱いの容易さの点から、水、アルコール、グリコール、グリコールエーテルおよびグリコールエステルからなる群から選ばれた1種以上の水系媒体が好ましい。
ハロゲン化炭化水素としては、ハイドロクロロフルオロカーボン、ハイドロフルオロカーボン、ハイドロブロモカーボン等が挙げられる。
ハイドロフルオロエーテルとしては、分離型ハイドロフルオロエーテル、非分離型ハイドロフルオロエーテル等が挙げられる。分離型ハイドロフルオロエーテルとは、エーテル性酸素原子を介してRF基またはパーフルオロアルキレン基、および、アルキル基またはアルキレン基が結合している化合物である。非分離型ハイドロフルオロエーテルとは、部分的にフッ素化されたアルキル基またはアルキレン基を含むハイドロフルオロエーテルである。
脂肪族炭化水素としては、ペンタン、2-メチルブタン、3-メチルペンタン、ヘキサン、2,2-ジメチルブタン、2,3-ジメチルブタン、ヘプタン、オクタン、2,2,4-トリメチルペンタン、2,2,3-トリメチルヘキサン、デカン、ウンデカン、ドデカン、2,2,4,6,6-ペンタメチルヘプタン、トリデカン、テトラデカン、ヘキサデカン等が挙げられる。
脂環式炭化水素としては、シクロペンタン、メチルシクロペンタン、シクロヘキサン、メチルシクロヘキサン、エチルシクロヘキサン等が挙げられる。
芳香族炭化水素としては、ベンゼン、トルエン、キシレン等が挙げられる。
エステルとしては、酢酸メチル、酢酸エチル、酢酸ブチル、プロピオン酸メチル、乳酸メチル、乳酸エチル、乳酸ペンチル等が挙げられる。
エーテルとしては、ジイソプロピルエーテル、ジオキサン、テトラヒドロフラン等が挙げられる。
有機酸としては、酢酸、プロピオン酸、りんご酸、乳酸等が挙げられる。
界面活性剤としては、炭化水素系界面活性剤またはフッ素系界面活性剤が挙げられ、それぞれ、アニオン性界面活性剤、ノニオン性界面活性剤、カチオン性界面活性剤、または両性界面活性剤が挙げられる。
界面活性剤としては、分散安定性の点から、ノニオン性界面活性剤とカチオン性界面活性剤または両性界面活性剤との併用、または、アニオン性界面活性剤の単独が好ましく、ノニオン性界面活性剤とカチオン性界面活性剤との併用が好ましい。
ノニオン性界面活性剤とカチオン性界面活性剤との比(ノニオン性界面活性剤/カチオン性界面活性剤)は、97/3~40/60(質量比)が好ましい。
ノニオン性界面活性剤とカチオン性界面活性剤との特定の組み合わせにおいては、含フッ素共重合体(100質量%)に対する合計量を、5質量%以下にできるため、剥離剤組成物の親水性が小さくなり、物品に優れた剥離性を付与できる。
界面活性剤s1は、ポリオキシアルキレンモノアルキルエーテル、ポリオキシアルキレンモノアルケニルエーテル、ポリオキシアルキレンモノアルカポリエニルエーテル、またはポリオキシアルキレンモノポリフルオロアルキルエーテルである。
界面活性剤s1としては、ポリオキシアルキレンモノアルキルエーテル、ポリオキシアルキレンモノアルケニルエーテル、またはポリオキシアルキレンモノポリフルオロアルキルエーテルが好ましい。界面活性剤s1は、1種を単独で用いてもよく、2種以上を併用してもよい。
R10O[CH2CH(CH3)O]s-(CH2CH2O)rH ・・・(s11)
ただし、R10は、炭素数が8以上のアルキル基または炭素数が8以上のアルケニル基であり、rは、5~50の整数であり、sは、0~20の整数である。R10は、水素原子の一部がフッ素原子に置換されていてもよい。
sが20以下であれば、水に可溶となり、水系媒体中に均一に溶解するため、剥離剤組成物の基材への浸透性が良好となる。
R10としては、直鎖状または分岐状のものが好ましい。
rは、10~30の整数が好ましい。
sは、0~10の整数が好ましい。
C18H37O[CH2CH(CH3)O]2-(CH2CH2O)30H、
C18H35O-(CH2CH2O)30H、
C16H33O[CH2CH(CH3)O]5-(CH2CH2O)20H、
C12H25O[CH2CH(CH3)O]2-(CH2CH2O)15H、
(C8H17)(C6H13)CHO-(CH2CH2O)15H、
C10H21O[CH2CH(CH3)O]2-(CH2CH2O)15H、
C6F13CH2CH2O-(CH2CH2O)15H、
C6F13CH2CH2O[CH2CH(CH3)O]2-(CH2CH2O)15H、
C4F9CH2CH2O[CH2CH(CH3)O]2-(CH2CH2O)15H。
界面活性剤s2は、分子中に1個以上の炭素-炭素三重結合および1個以上の水酸基を有する化合物からなるノニオン性界面活性剤である。
界面活性剤s2としては、分子中に1個の炭素-炭素三重結合、および1個または2個の水酸基を有する化合物からなるノニオン性界面活性剤が好ましい。
界面活性剤s2は、分子中にPOA鎖を有してもよい。POA鎖としては、POE鎖、POP鎖、POE鎖とPOP鎖とがランダム状に連結された鎖、またはPOE鎖とPOP鎖とがブロック状に連結された鎖が挙げられる。
界面活性剤s2としては、化合物(s21)~(s24)が好ましい。
uおよびvは、それぞれ0以上の整数であり、(u+v)は、1以上の整数である。
wは、1以上の整数である。
u、v、wが、それぞれ2以上である場合、A1~A3は、それぞれ同一であってもよく、異なっていてもよい。
POA鎖としては、POE鎖、POP鎖、またはPOE鎖とPOP鎖とを含む鎖が好ましい。POA鎖の繰り返し単位の数は、1~50が好ましい。
アルキル基としては、炭素数が1~12のアルキル基が好ましく、炭素数が1~4のアルキル基がより好ましい。アルキル基としては、メチル基、エチル基、プロピル基、ブチル基、イソブチル基等が挙げられる。
化合物(s22)としては、化合物(s25)が好ましい。
化合物(s25)は、1種を単独で用いてもよく、2種以上を併用してもよい。
化合物(s25)としては、xおよびyが0である化合物、xとyとの和が平均1~4である化合物、またはxとyとの和が平均10~30である化合物が好ましい。
界面活性剤s3は、POE鎖と、炭素数が3以上のオキシアルキレンが2個以上連続して連なったPOA鎖とが連結し、かつ、両末端が水酸基である化合物からなるノニオン性界面活性剤である。
該POA鎖としては、ポリオキシテトラメチレン(以下、POTと記す。)および/またはPOP鎖が好ましい。
HO(CH2CH2O)g1(C3H6O)t(CH2CH2O)g2H ・・・(s31)、
HO(CH2CH2O)g1(CH2CH2CH2CH2O)t(CH2CH2O)g2H ・・・(s32)。
tは、2~100の整数である。
g2は、0~200の整数である。
g1が0の場合、g2は、2以上の整数である。g2が0の場合、g1は、2以上の整数である。
POA鎖は、ブロック状である。
HO-(CH2CH2O)15-(C3H6O)35-(CH2CH2O)15H、
HO-(CH2CH2O)8-(C3H6O)35-(CH2CH2O)8H、
HO-(CH2CH2O)45-(C3H6O)17-(CH2CH2O)45H、
HO-(CH2CH2O)34-(CH2CH2CH2CH2O)28-(CH2CH2O)34H。
界面活性剤s4は、分子中にアミンオキシド部分を有するノニオン性界面活性剤である。
界面活性剤s4としては、化合物(s41)が好ましい。
本発明においては、アミンオキシドを有する界面活性剤をノニオン性界面活性剤として扱う。
化合物(s41)は、1種を単独で用いてもよく、2種以上を併用してもよい。
化合物(s41)としては、含フッ素共重合体の分散安定性の点から、化合物(s42)が好ましい。
化合物(s42)としては、下記の化合物が挙げられる。
界面活性剤s5は、ポリオキシエチレンモノ(置換フェニル)エーテルの縮合物またはポリオキシエチレンモノ(置換フェニル)エーテルからなるノニオン性界面活性剤である。
置換フェニル基としては、1価炭化水素基で置換されたフェニル基が好ましく、アルキル基、アルケニル基またはスチリル基で置換されたフェニル基がより好ましい。
界面活性剤s6は、ポリオールの脂肪酸エステルからなるノニオン性界面活性剤である。
ポリオールとは、グリセリン、ソルビタン、ソルビット、ポリグリセリン、ポリエチレングリコール、ポリオキシエチレングリセリルエーテル、ポリオキシエチレンソルビタンエーテル、ポリオキシエチレンソルビットエーテルを表わす。
界面活性剤がカチオン性界面活性剤を含む場合、該カチオン性界面活性剤としては、界面活性剤s7が好ましい。
界面活性剤s7は、置換アンモニウム塩形のカチオン性界面活性剤である。
[(R21)4N+]・X- ・・・(s71)。
R21は、水素原子、炭素数が1~22のアルキル基、炭素数が2~22のアルケニル基、炭素数が1~9のフルオロアルキル基、または末端が水酸基であるPOA鎖である。4つのR21は、同一であってもよく、異なっていてもよいが、4つのR21は同時に水素原子ではない。
R21が長鎖アルキル基以外のアルキル基の場合、R21としては、メチル基またはエチル基が好ましい。
R21が、末端が水酸基であるPOA鎖の場合、POA鎖としては、POE鎖が好ましい。
X-は、対イオンである。
X-としては、塩素イオン、エチル硫酸イオン、または酢酸イオンが好ましい。
界面活性剤が両性界面活性剤を含む場合、該両性界面活性剤としては、界面活性剤s8が好ましい。
界面活性剤s8は、アラニン類、イミダゾリニウムベタイン類、アミドベタイン類または酢酸ベタインである。
界面活性剤s8としては、ドデシルベタイン、ステアリルベタイン、ドデシルカルボキシメチルヒドロキシエチルイミダゾリニウムベタイン、ドデシルジメチルアミノ酢酸ベタイン、脂肪酸アミドプロピルジメチルアミノ酢酸ベタイン等が挙げられる。
界面活性剤として、界面活性剤s9を用いてもよい。
界面活性剤s9は、親水性単量体と炭化水素系疎水性単量体および/またはフッ素系疎水性単量体との、ブロック共重合体、ランダム共重合体、または親水性共重合体の疎水性変性物からなる高分子界面活性剤である。
界面活性剤s91:親油性単量体とフッ素系単量体とのブロック共重合体またはランダム共重合体(そのポリフルオロアルキル変性体)からなる高分子界面活性剤。
界面活性剤s91の市販品としては、セイミケミカル社のサーフロン(商品番号:S-383、SC-100シリーズ)が挙げられる。
界面活性剤の合計量は、含フッ素共重合体(100質量%)に対して1~6質量%がより好ましい。
添加剤としては、浸透剤、消泡剤、吸水剤、帯電防止剤、防皺剤、風合い調整剤、造膜助剤、水溶性高分子(ポリアクリルアミド、ポリビニルアルコール等。)、熱硬化剤(メラミン樹脂、ウレタン樹脂等。)、エポキシ硬化剤(イソフタル酸ジヒドラジド、アジピン酸ジヒドラジド、セバチン酸ジヒドラジド、ドデカン二酸ジヒドラジド、1,6-ヘキサメチレンビス(N,N-ジメチルセミカルバジド)、1,1,1’,1’-テトラメチル-4,4’-(メチレン-ジ-パラ-フェニレン)ジセミカルバジド、スピログリコール等。)、熱硬化触媒、架橋触媒、合成樹脂、繊維安定剤等が挙げられる。
本発明の剥離剤組成物は、たとえば、下記(i)または(ii)の方法で製造できる。
(i)界面活性剤、重合開始剤の存在下、媒体中にて単量体(a)、(b)、必要に応じて単量体(c)、(d)、(e)を含む単量体混合物を重合して含フッ素共重合体の溶液、分散液またはエマルションを得た後、必要に応じて、他の媒体、他の界面活性剤、添加剤を加える方法。
(ii)界面活性剤、重合開始剤の存在下、媒体中にて単量体(a)、(b)、必要に応じて単量体(c)、(d)、(e)を含む単量体混合物を重合して含フッ素共重合体の溶液、分散液またはエマルションを得た後、含フッ素共重合体を分離し、含フッ素共重合体に媒体、界面活性剤、必要に応じて添加剤を加える方法。
本発明における含フッ素共重合体の重合法としては、分散重合法、乳化重合法、懸濁重合法等が挙げられる。
含フッ素共重合体の収率が向上する点から、乳化重合の前に、単量体、界面活性剤および水系媒体からなる混合物を前乳化することが好ましい。たとえば、単量体、界面活性剤および水系媒体からなる混合物を、ホモミキサーまたは高圧乳化機で混合分散する。
ラジカル重合開始剤としては、アゾ系重合開始剤、過酸化物系重合開始剤、レドックス系開始剤等の汎用の開始剤が、重合温度に応じて用いられる。ラジカル重合開始剤としては、アゾ系化合物が特に好ましく、水系媒体中で重合を行う場合、アゾ系化合物の塩がより好ましい。重合温度は20~150℃が好ましい。ラジカル重合開始剤の添加量は、単量体混合物100質量部に対して、0.1~1質量部が好ましく、0.3~0.6質量部が特に好ましい。
単量体混合物における単量体(b)の含有割合は、剥離剤組成物の剥離強度の点から55~99質量%が好ましく、55~90質量%がより好ましく、55~85質量%が特に好ましい。
単量体混合物における単量体(c)の含有割合は、物品との密着性および被膜強度の点から0~30質量%が好ましく、5~25質量%がより好ましく、10~25質量%が特に好ましい。
単量体混合物における単量体(d)の含有割合は、被膜の剥離強度や耐熱性、耐摩耗性の点から0~20質量%が好ましく、0~10質量%がより好ましく、0.5~5質量%が特に好ましい。
単量体混合物における単量体(e)の含有割合は、被膜の耐熱性や耐摩耗性の向上、変色の抑制などの効果の点から、0~15質量%が好ましく、0.1~10質量%がより好ましく、0.1~5質量%が特に好ましい。
基材を処理する場合には、製造直後の剥離剤組成物を上述の媒体にて希釈することが好ましい。
基材を処理する場合、本発明の剥離剤組成物の固形分濃度は、剥離剤組成物(100質量%)中、0.2~5質量%が好ましい。
剥離剤組成物の固形分濃度は、加熱前の剥離剤組成物の質量と、120℃の対流式乾燥機にて4時間乾燥した後の質量とから計算される。
本発明の剥離剤組成物で処理することにより、不織布、樹脂、紙、皮革、金属、石、コンクリート、石膏、ガラス等様々な基材の表面に剥離性を付与することができる。なかでも、紙に適用することが好ましい。
処理方法としては、たとえば、公知の塗工方法によって物品に剥離剤組成物を塗布または含浸した後、乾燥する方法が挙げられる。
例1~7は実施例、例8は比較例である。
単量体(a):
C6FMA:C6F13C2H4OC(O)C(CH3)=CH2
単量体(b):
BeA:ベヘニルアクリレート
StA:ステアリルアクリレート
単量体(c):
VCM:塩化ビニル
単量体(d):
HEMA:2-ヒドロキシエチルメタクリレート
HEA:2-ヒドロキシエチルアクリレート
NMAM:N-メチロールアクリルアミド
TAC:トリアリルシアヌレート
MOI-BP:2-イソシアナトエチル(メタ)アクリレートの3,5-ジメチルピラゾール付加体(昭和電工社製、カレンズMOI-BP)
単量体(e):
DOM:マレイン酸ジ-2-エチルヘキシル。
PEO-20:ポリオキシエチレンオレイルエーテル(花王社製、エマルゲンE430、エチレンオキシド約26モル付加物。)の10質量%水溶液。
界面活性剤s7:
STMC:モノステアリルトリメチルアンモニウムクロリド(ライオン社製、アーカード18-63)の10質量%水溶液。
界面活性剤s3:
P-204:エチレンオキシドプロピレンオキシド重合物(日本油脂社製、プロノン204、エチレンオキシドの割合は40質量%。)の10質量%水溶液。
nDoSH:n-ドデシルメルカプタン、
重合開始剤:
VA-061A:2,2’-アゾビス[2-(2-イミダゾリン-2-イル)プロパン](和光純薬社製、VA-061)の酢酸塩の10質量%水溶液。
媒体:
DPG:ジプロピレングリコール、
水:イオン交換水。
ガラス製ビーカーに、C6FMAの43.3g、BeAの146.4g、DOMの10.2g、HEMAの2.5g、nDoSHの2.5g、PEO-20の63.7g、P-204の12.7g、STMCの12.7g、DPGの76.4g、水の314.5gを入れ、60℃で30分間加温した後、ホモミキサー(日本精機製作所社製、バイオミキサー)を用いて混合して混合液を得た。
得られた混合液を、60℃に保ちながら高圧乳化機(APVラニエ社製、ミニラボ)を用いて、40MPaで処理して乳化液を得た。得られた乳化液をステンレス製反応容器に入れ、40℃以下となるまで冷却した。VA-061の12.7gを加えて、気相を窒素置換した後、VCMの52.2gを導入し、撹拌しながら60℃で15時間重合反応を行い、含フッ素共重合体のエマルションを得た。各単量体に基づく構成単位の割合(質量比)を表2に示す。
各単量体の種類または仕込み量を表1に示す量に変更した以外は、例1と同様にして共重合体のエマルションを得た。各単量体に基づく構成単位の割合(質量比)を表2に示す。
(基材の作成)
例1~8の剥離剤組成物と10gの酸化デンプン(日本食品化工社製MS-3600)を80~90gの水で希釈(剥離剤組成物の固形分濃度:2質量%)し、それをPPC用紙に塗布し、100℃で60秒間乾燥させた。希釈液の塗布量は約30g/m2とした。
処理した基材に長さ25mmのポリエステルテープ(日東電工社製)を貼り付け、その上を2kgの圧着ローラーで2往復した。ポリエステルテープを貼り付けた基材を引っ張り試験機にセットし、剥離強度を評価した。引っ張り試験機の測定条件は、スピード300mm/分、つかみ幅25mm、剥離距離50mmとした。結果を表3に示す。
例1~8の剥離剤組成物を炭酸カルシウムにより硬度を150に調整した水で希釈し、アニオン物質としてディマフィックスES(明成化学工業社製)を添加した。このとき、剥離剤組成物の濃度は6g/L、アニオン物質の濃度は0.15g/Lとした。これらの混合液をホモミキサーにより撹拌後、黒色の織物でろ過し、沈殿物の発生程度を目視により良好なものを5点とし、1点までの5段階で評価した。結果は表4に示す。
なお、2010年2月15日に出願された日本特許出願2010-030189号の明細書、特許請求の範囲、及び要約書の全内容をここに引用し、本発明の明細書の開示として、取り入れるものである。
Claims (7)
- 下記単量体(a)に基づく構成単位および下記単量体(b)に基づく構成単位を有する含フッ素共重合体および媒体を含み、単量体(a)に基づく構成単位と単量体(b)に基づく構成単位の質量比(単量体(a)に基づく構成単位/単量体(b)に基づく構成単位)が1/1~1/10であることを特徴とする剥離剤組成物。
単量体(a):下式(1)で表される化合物。
(Z-Y)nX ・・・(1)
ただし、Zは、炭素数1~6のポリフルオロアルキル基または下式(2)で表される基であり、
Yは、2価有機基または単結合であり、
nは、1または2であり、
Xは、nが1の場合は、下式(3-1)~(3-5)で表される基のいずれかであり、nが2の場合は、下式(4-1)~(4-4)で表される基のいずれかである。
CmF2m+1O(CF2CF(CF3)O)dCF(CF3)- ・・・(2)。
ただし、mは、1~6の整数であり、dは、1~4の整数である。
-C(R)=CH2 ・・・(3-1)、
-C(O)OC(R)=CH2 ・・・(3-2)、
-OC(O)C(R)=CH2 ・・・(3-3)、
-OCH2-φ-C(R)=CH2 ・・・(3-4)、
-OCH=CH2 ・・・(3-5)。
ただし、Rは、水素原子、メチル基またはハロゲン原子であり、φは、フェニレン基である。
-CH[-(CH2)pC(R)=CH2]- ・・・(4-1)、
-CH[-(CH2)pC(O)OC(R)=CH2]- ・・・(4-2)、
-CH[-(CH2)pOC(O)C(R)=CH2]- ・・・(4-3)、
-OC(O)CH=CHC(O)O- ・・・(4-4)。
ただし、Rは、水素原子、メチル基またはハロゲン原子であり、pは、0~4の整数である。
単量体(b):ポリフルオロアルキル基を有さず、炭素数が18~30のアルキル基を有する(メタ)アクリレート。 - 前記含フッ素共重合体が、下記単量体(c)に基づく構成単位をさらに有する、請求項1に記載の剥離剤組成物。
単量体(c):ハロゲン化オレフィン。 - 前記含フッ素共重合体が、下記単量体(d)に基づく構成単位をさらに有する、請求項1または2に記載の剥離剤組成物。
単量体(d):ポリフルオロアルキル基を有さず、架橋しうる官能基を有する単量体。 - ノニオン性界面活性剤およびカチオン性界面活性剤をさらに含む、請求項1~3のいずれかに記載の剥離剤組成物。
- 前記媒体が、水、アルコール、グリコール、グリコールエーテルおよびグリコールエステルからなる群から選ばれた1種以上の水系媒体である、請求項1~4のいずれかに記載の剥離剤組成物。
- 前記含フッ素共重合体が媒体中に粒子として分散しており、含フッ素共重合体の平均粒子径が、10~1000nmである、請求項1~5のいずれかに記載の剥離剤組成物。
- 下記単量体(a)と下記単量体(b)を含み、単量体(a)と単量体(b)の質量比(単量体(a)/単量体(b))が1/1~1/10である単量体混合物を、重合開始剤存在下、共重合させる工程を有することを特徴とする剥離剤組成物の製造方法。
単量体(a):下式(1)で表される化合物。
(Z-Y)nX ・・・(1)。
ただし、Zは、炭素数1~6のポリフルオロアルキル基または下式(2)で表される基であり、
Yは、2価有機基または単結合であり、
nは、1または2であり、
Xは、nが1の場合は、下式(3-1)~(3-5)で表される基のいずれかであり、nが2の場合は、下式(4-1)~(4-4)で表される基のいずれかである。
CmF2m+1O(CF2CF(CF3)O)dCF(CF3)- ・・・(2)。
ただし、mは、1~6の整数であり、dは、1~4の整数である。
-C(R)=CH2 ・・・(3-1)、
-C(O)OC(R)=CH2 ・・・(3-2)、
-OC(O)C(R)=CH2 ・・・(3-3)、
-OCH2-φ-C(R)=CH2 ・・・(3-4)、
-OCH=CH2 ・・・(3-5)。
ただし、Rは、水素原子、メチル基またはハロゲン原子であり、φは、フェニレン基である。
-CH[-(CH2)pC(R)=CH2]- ・・・(4-1)、
-CH[-(CH2)pC(O)OC(R)=CH2]- ・・・(4-2)、
-CH[-(CH2)pOC(O)C(R)=CH2]- ・・・(4-3)、
-OC(O)CH=CHC(O)O- ・・・(4-4)。
ただし、Rは、水素原子、メチル基またはハロゲン原子であり、pは、0~4の整数である。
単量体(b):ポリフルオロアルキル基を有さず、炭素数が18~30のアルキル基を有する(メタ)アクリレート。