WO2011030916A1 - 相変化材料および相変化型メモリ素子 - Google Patents
相変化材料および相変化型メモリ素子 Download PDFInfo
- Publication number
- WO2011030916A1 WO2011030916A1 PCT/JP2010/065991 JP2010065991W WO2011030916A1 WO 2011030916 A1 WO2011030916 A1 WO 2011030916A1 JP 2010065991 W JP2010065991 W JP 2010065991W WO 2011030916 A1 WO2011030916 A1 WO 2011030916A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- phase change
- change material
- phase
- temperature
- memory
- Prior art date
Abstract
Description
GexMyTe100−x−y
で示される組成を有し、式中、Mは、Al、Si、Cu、In及びSnからなる群から選択した1種類の元素を示し、xは5.0~50.0(at.%)、yは4.0~45.0(at.%)の範囲内で、40(at.%)≦x+y≦60(at.%)となるように選択されている、相変化材料を提供する。
GexMyLzTe100−x−y−z
の形で含み、ここでzを、40(at.%)≦x+y+z≦60(at.%)となるように選択してもよい。
図1(b)は、本発明の更なる実施形態に係る相変化材料と比較例の組成とその物理特性を表にして示す図である。
図2(a)は、本発明の種々の実施形態に係る相変化材料薄膜の電気抵抗の温度依存性を示すグラフである。
図2(b)は、本発明の種々の実施形態に係る相変化材料薄膜の電気抵抗の温度依存性を示すグラフである。
図3は、図1に示す実施例28の等温保持における電気抵抗変化を示すグラフである。
図4は、図3のグラフから求めた故障時間tFと温度との関係を示すグラフである。
図5は、本発明の一実施形態であるGe17.4Cu30.7Te51.9薄膜試料の、電気抵抗の温度依存性を示すグラフである。
図6は、図5の試料の等温保持における電気抵抗変化を示すグラフである。
図7は、図6のグラフから求めた故障時間tFと温度との関係を示すグラフである。
図8は、図1に示す比較例2の等温保持における電気抵抗変化を示すグラフである。
図9は、図8のグラフから求めた故障時間tFと温度との関係を示すグラフである。
図10(a)は、本発明の一実施形態に係る相変化型メモリ素子の概略断面図である。
図10(b)は、図10(a)に示す素子の平面図である。
図11は、本発明の他の実施形態に係る相変化型メモリ素子の概略構造を示す断面図である。
化学式1
GexMyTe100−x−y
M:Al、Si、Cu、In及びSnからなる群から選択した1種類の元素。
x、yは原子濃度(at.%)であり、xは5.0~50.0、yは4.0~45.0の範囲で、且つ、40(at.%)≦x+y≦60(at.%)となる様に選択される。
ln(α/(Tc)2)=−Ea/kTc+Const.
ここでα:昇温速度、Tc:結晶化温度、Ea:活性化エネルギー、k:ボルツマン定数である。
Claims (12)
- 一般化学式、
GexMyTe100−x−y
で示される組成を有し、式中、Mは、Al、Si、Cu、In及びSnからなる群から選択した1種類の元素を示し、xは5.0~50.0(at.%)、yは4.0~45.0(at.%)の範囲内で、40(at.%)≦x+y≦60(at.%)となるように選択されている、相変化材料。 - 追加元素Lとして、さらにN、O、Al、Si、P、Cu、InおよびSnからなる群から選択した少なくとも1種類の元素Lを、
GexMyLzTe100−x−y−z
の形で含み、ここでzは、40(at.%)≦x+y+z≦60(at.%)となるように選択されている、請求項1に記載の相変化材料。 - 前記選択した1種類の元素MがCuである場合、前記yは、4.0~38.0(at.%)であることを特徴とする、請求項1又は2に記載の相変化材料。
- 前記選択した1種類の元素MがAlである場合、前記yは、4.0~15.0(at.%)であることを特徴とする、請求項1又は2に記載の相変化材料。
- 前記選択した1種類の元素MがSiである場合、前記yは、4.0~15.0(at.%)であることを特徴とする、請求項1又は2に記載の相変化材料。
- 前記選択した1種類の元素MがCuであり、前記追加元素LがSiである場合、前記yは10.0~38.0(at.%)、前記zは0.5~30(at.%)であることを特徴とする、請求項2に記載の相変化材料。
- 前記選択した1種類の元素MがInである場合、前記yは20.0~40.0(at.%)であることを特徴とする、請求項1又は2に記載の相変化材料。
- 前記選択した1種類の元素MがSnである場合、前記yは4.0~15.0(at.%)であることを特徴とする、請求項1又は2に記載の相変化材料。
- 基板と、前記基板の上部に請求項1乃至9の何れか1項に記載の相変化材料で形成したメモリ層と、前記メモリ層に通電するための第1、第2の電極と、を備える、相変化型メモリ素子。
- 前記第1、第2の電極は前記基板上で前記メモリ層の両端に接して形成されていることを特徴とする、請求項10に記載の相変化型メモリ素子。
- 前記第1の電極は前記基板上に形成した下部電極層と発熱性電極層とで形成され、前記第2の電極は前記メモリ層上に形成されていることを特徴とする、請求項10に記載の相変化メモリ素子。
- 前記メモリ層と少なくとも前記基板間に拡散バリア層が形成されていることを特徴とする、請求項10または11に記載の相変化型メモリ素子。