WO2006126448A1 - 導電性高分子積層体 - Google Patents
導電性高分子積層体 Download PDFInfo
- Publication number
- WO2006126448A1 WO2006126448A1 PCT/JP2006/309943 JP2006309943W WO2006126448A1 WO 2006126448 A1 WO2006126448 A1 WO 2006126448A1 JP 2006309943 W JP2006309943 W JP 2006309943W WO 2006126448 A1 WO2006126448 A1 WO 2006126448A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- conductive
- group
- composition
- complex
- conductive polymer
- Prior art date
Abstract
Description
Claims