WO2005104239A1 - 薄膜トランジスタ及びその製造方法 - Google Patents

薄膜トランジスタ及びその製造方法 Download PDF

Info

Publication number
WO2005104239A1
WO2005104239A1 PCT/JP2005/007808 JP2005007808W WO2005104239A1 WO 2005104239 A1 WO2005104239 A1 WO 2005104239A1 JP 2005007808 W JP2005007808 W JP 2005007808W WO 2005104239 A1 WO2005104239 A1 WO 2005104239A1
Authority
WO
WIPO (PCT)
Prior art keywords
silicon
gas
film
silicon oxide
silicon nitride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2005/007808
Other languages
English (en)
French (fr)
Inventor
Sadatsugu Wakamatsu
Toru Kikuchi
Masanori Hashimoto
Takaomi Kurata
Shin Asari
Kazuya Saito
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ulvac Inc
Original Assignee
Ulvac Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ulvac Inc filed Critical Ulvac Inc
Priority to JP2006519508A priority Critical patent/JP5066361B2/ja
Priority to KR1020067005921A priority patent/KR101184232B1/ko
Publication of WO2005104239A1 publication Critical patent/WO2005104239A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

　良好な生産性を確保しつつ、優れた特性と信頼性の高いゲート絶縁層を有する薄膜トランジスタ及びその製造方法を提供する。 　基板９上にソース領域１７、チャンネル領域１８、ドレイン領域１９を有する活性層１１と、ゲート電極層１６と、活性層１１とゲート電極層１６との間に形成されるゲート絶縁層１５とを有する薄膜トランジスタであって、ゲート絶縁層１５を、活性層１１側に形成される第１の酸化珪素膜１２と、ゲート電極層１６側に形成される第２の酸化珪素膜１４と、第１の酸化珪素膜１２と第２酸化珪素膜１４の間に形成される窒化珪素膜１３とで形成した。

Description

明 細 書
薄膜トランジスタ及びその製造方法
技術分野
[0001] 本発明は、酸ィ匕珪素膜をゲート絶縁層とする薄膜トランジスタ及びその製造方法に 関する。
背景技術
[0002] 従来より液晶ディスプレイ (LCD)や有機エレクト口ルミネッセンス (OLED)等のデ バイスには、アモルファスシリコン (a— Si)ゃ窒化珪素膜 (SiNx)、酸ィ匕珪素膜 (SiO X)といった薄膜から形成される、薄膜トランジスタであるアモルファスシリコン TFT(a — SiTFT)、低温ポリシリコン TFT(LTPS— TFT)が利用されている。とりわけ低温ポ リシリコン TFTは、アモルファスシリコン TFTよりも高移動度化が可能であり、かつ透 明で絶縁性のある例えばガラス基板のような基板上に作製することができる。
[0003] 低温ポリシリコン TFTの代表的な構造としては、例えば図 18に示すようなコプレー ナ型トランジスタが挙げられる。
コプレーナ型トランジスタの構成は、図 18に示すように、透明性及び絶縁性を有す るガラス基板 100上に、活性層 101となる多結晶珪素薄膜が形成される。この活性層 101は、 N型又は P型不純物がドーピングされてなるソース領域 102、チャネル領域 1 03、ドレイン領域 104に分けられており、この活性層 101を覆うようにゲート絶縁層 10 5が形成され、ゲート電極 106がチャネル領域 103上に形成される。更に、層間絶縁 層 107上にソース電極 108とドレイン電極 109が配置される。
ところで、低温ポリシリコン TFTの製造工程においては、その利用される半導体素 子が大面積を必要とするため安価なガラス基板が用いられており、その耐熱性が十 分でな!、ため、比較的低温 (およそ 600°C程度以下）のプロセス温度で作製しなくて はならない。
一方、シリコン単結晶基板を用いたシリコン TFTの製造工程においては、その表面 を水蒸気雰囲気中もしくは酸素雰囲気中で表面を高温 (900°C〜1100°C程度)酸 化することで、ゲート絶縁膜である酸化珪素膜を形成する。この熱酸化により形成さ れたゲート絶縁膜は、膜中の欠陥が少ない非常に高品質な膜であり、また活性層と ゲート絶縁膜の界面もクリーンな状態に保たれるため、ゲート絶縁膜とシリコン基板と の界面特性も良質である。
[0004] これに対して、上記した従来の低温ポリシリコン TFTの製造方法では、界面特性の 良好なゲート絶縁膜を得ることが難しカゝつたが、近年、低温ポリシリコン TFTでも界面 特性の良好なゲート絶縁膜を得ることができる製造方法が提案されている (例えば、 特許文献 1参照。）。
上記特許文献 1によるゲート絶縁膜の製造方法では、多結晶珪素薄膜上に酸化膜 を形成した後に触媒金属を堆積し、 600°C以下の酸化雰囲気中で熱処理するように している。
特許文献 1 :特開平 10— 163193号公報
発明の開示
発明が解決しょうとする課題
[0005] ところで、上記特許文献 1のような従来の低温ポリシリコン TFTの製造方法では、触 媒金属を塗布する工程ならびに熱処理により絶縁層を形成する工程、さらに実用性 を考慮し、最終的に触媒金属を活性層から除去する工程があり、生産性が良くなか つた o
また、図 18に示したような従来の低温ポリシリコン TFT (コプレーナ型トランジスタ） の製造工程では、ゲート絶縁層 105の形成前に活性層 101 (ソース領域 102及びド レイン領域 104と、チャネル領域 103)のパターユング工程が必要となる。このため、 この活性層 101とゲート絶縁層 105の界面特性は、上記したシリコン TFTの製造ェ 程のような良好な特性を得ることが難し力つた。
[0006] その結果、キャリアのトラップ及び散乱が生じ、低温ポリシリコン TFTの特性のひと つであるスレツショルド電圧（閾値電圧）の変位 (シフト）が大きくなつたり、サブスレツ ショルドスイング（S値）が大きくなつてしまうと 、う問題があった。
そこで本発明は、良好な生産性を確保しつつ、優れた特性と信頼性の高いゲート 絶縁層を有する薄膜トランジスタ及びその製造方法を提供することを目的とする。 課題を解決するための手段 [0007] 上記目的を達成するために本発明の薄膜トランジスタのうち請求項 1記載の発明は 、基板上にソース領域、ドレイン領域、チャンネル領域を有する活性層と、ゲート電極 層と、活性層とゲート電極層との間に形成されるゲート絶縁層とを有する薄膜トランジ スタであって、ゲート絶縁層が、活性層に接して形成される第 1の酸ィ匕珪素膜と、第 1 の酸ィ匕珪素膜とゲート電極層との間に第 1の酸ィ匕珪素膜に接して形成される窒化珪 素膜とを含むことを特徴として 、る。
[0008] さらに、請求項 2記載の発明は、上記構成に加え、窒化珪素膜とゲート電極層との 間に第 2の酸ィ匕珪素膜を有することを特徴とするものである。
請求項 3記載の発明は、活性層がポリシリコンで形成されることを特徴としている。 請求項 4記載の発明は、第 1の酸化珪素膜、窒化珪素膜の膜厚さの比が、 4〜5 : 1 〜2であることを特徴として 、る。
請求項 5記載の発明は、第 1の酸化珪素膜、窒化珪素膜、第 2の酸ィヒ珪素膜のそ れぞれの膜厚さの比力 4〜5： 1〜2 :4〜5であることを特徴としている。
請求項 6記載の発明は、第 1の酸ィ匕珪素膜の膜厚が、 40nm以上 50nm以下であ る、ことを特徴としている。
請求項 7記載の発明は、窒化珪素膜の膜厚が lOnm以上 20nm以下であることを 特徴としている。
請求項 8記載の発明は、ゲート絶縁層全体の層厚が、 50nm以上 200nm以下であ ることを特徴としている。
[0009] 本発明の薄膜トランジスタの製造方法のうち請求項 9記載の発明は、基板表面に活 性層を形成する工程と、活性層上に第 1の酸化珪素膜を形成する工程と、第 1の酸 化珪素膜上に窒化珪素膜を形成する工程と、窒化珪素膜上にゲート電極層を形成 する工程とを含むことを特徴として 、る。
さらに請求項 10記載の発明は、上記構成に加え、ゲート電極層を形成する工程が 、窒化珪素膜上に第 2の酸ィ匕珪素膜を形成後、ゲート電極層を形成する工程である ことを特徴とするものである。
また請求項 11記載の発明は、第 1の酸ィ匕珪素膜を形成する工程においては、圧力 調整された反応容器内に珪素原子を含む第 1の珪素付与ガス、酸素原子を含む酸 素付与ガスのそれぞれの少なくとも一種類ずつを導入して、プラズマ CVD法により酸 化珪素膜を形成し、窒化珪素膜を形成する工程においては、圧力調整された反応 容器内に珪素原子を含む第 2の珪素付与ガス、窒素原子を含む窒素付与ガス、希 釈ガスのそれぞれの少なくとも一種類ずつを導入して、プラズマ CVD法により窒化珪 素膜を形成することを特徴として 、る。
[0010] 請求項 12記載の発明は、第 1の珪素付与ガスは、テトラエトキシオルソシリケートと 、へキサメチルジシラザンと、モノシランと、ジシラン力 なる群より選択されるいずれ カゝ 1種類のガスであり、酸素付与ガスは、酸素、亜酸化窒素、オゾン、二酸化炭素、 水からなる群より選択される 、ずれか 1種類のガスであることを特徴として 、る。
請求項 13記載の発明は、第 1の珪素付与ガスと前記酸素付与ガスの組成比が、 1 : 30〜50であることを特徴として!/、る。
請求項 14記載の発明は、酸ィ匕珪素膜の成膜時の圧力は 80〜200Paであり、基板 温度は 330〜430°Cであることを特徴として！/、る。
請求項 15記載の発明は、第 2の珪素付与ガスは、テトラエトキシオルソシリケートと 、へキサメチルジシラザンと、モノシランと、ジシラン力 なる群より選択されるいずれ 力 1種類のガスであり、窒素付与ガスは、アンモニア、一酸化窒素、ヒドラジン力 なる 群より選択される 、ずれか 1種類のガスであることを特徴として 、る。
請求項 16記載の発明は、第 2の珪素付与ガス、窒素付与ガス、希釈ガスの組成比 力 1： 10-25： 10〜30であることを特徴として!/、る。
請求項 17記載の発明は、窒化珪素膜の成膜時の圧力は 200〜400Paであり、基 板温度は 330〜430°Cであることを特徴としている。
請求項 18記載の発明は、プラズマ CVD法で第 1の酸ィ匕珪素膜、第 2の酸化珪素 膜、窒化珪素膜をそれぞれ形成する際の、電極に印加する高周波電圧の周波数が 27.1MHzであることを特徴として!/、る。
発明の効果
[0011] 本発明の薄膜トランジスタによれば、閾値電圧及び S値を小さくすることができ、優 れた特性を有することができる。
さらに、本発明の薄膜トランジスタの製造方法によれば、良好な生産性を確保しつ つ、ゲート絶縁層の膜中の欠陥ならびに珪素薄膜との界面の欠陥密度を大幅に低 減して界面特性の良好なゲート絶縁層を有する薄膜トランジスタを得ることができる。 図面の簡単な説明
[図 1]本発明の実施形態に係る製造方法によって形成された薄膜トランジスタとして のポリシリコン TFTを示す概略断面図。
[図 2]本発明に係るポリシリコン TFTのゲート絶縁層を成膜するためのプラズマ CVD 装置を示す概略断面図。
[図 3]本発明に係るゲート絶縁層と従来のゲート絶縁層のそれぞれの成膜プロセス条 件を示す図。
[図 4]本発明に係るゲート絶縁層の第 1、第 3層としての酸ィ匕珪素膜の形成時におけ る、成膜温度と成膜速度の関係を示す図。
[図 5]本発明に係るゲート絶縁層の第 1、第 3層としての酸ィ匕珪素膜の形成時におけ る、成膜温度と Dit、 Vlの関係の関係を示す図。
[図 6]本発明に係るゲート絶縁層の第 1、第 3層としての酸ィ匕珪素膜の形成時におけ る、珪素付与ガスに対する酸素ガス組成比と成膜速度の関係を示す図。
[図 7]本発明に係るゲート絶縁層の第 1、第 3層としての酸ィ匕珪素膜の形成時におけ る、酸素ガス組成比と Dit、 Vlbの関係を示す図。
[図 8]本発明に係るゲート絶縁層の第 1、第 3層としての酸ィ匕珪素膜を形成時におけ る、プロセス圧力と成膜速度及び基板面内分布の関係を示す図。
[図 9]本発明に係るゲート絶縁層の第 2層としての窒化珪素膜を形成時における、珪 素付与ガスに対する窒素付与ガスとしてのアンモニアガス組成比と成膜速度の関係 を示す図。
[図 10]本発明に係るゲート絶縁層の第 2層としての窒化珪素膜を形成時における、ァ ンモ-ァガス組成比と Dit、 Vlの関係を示す図。
[図 11]本発明に係るゲート絶縁層の第 2層としての窒化珪素膜を形成時における、 珪素付与ガスに対する窒素付与ガスの組成比と、成膜速度と基板面内分布の関係 を示す図。
[図 12]本発明に係るゲート絶縁層の第 2層としての窒化珪素膜を形成時における、プ ロセス圧力と、成膜速度と基板面内分布の関係を示す図。
圆 13]本発明に係るゲート絶縁層の第 2層としての窒化珪素膜を形成時における、 成膜温度と成膜速度の関係を示す図。
圆 14]本発明に係るゲート絶縁層の第 2層としての窒化珪素膜を形成時における、 成膜温度と Dit、 Vlbの関係を示す図。
圆 15]本発明に係るゲート絶縁層の第 1、第 2層としての各酸ィ匕珪素膜における膜厚 と、 Dit、 Vlbの関係を示す図。
圆 16]本発明に係るゲート絶縁層の第 2層としての窒化珪素膜における膜厚と、 Dit、 Vlの関係を示す図。
[図 17]本発明に係るゲート絶縁層と従来のゲート絶縁層を使用した各ポリシリコン TF Tにおける、サブスレツショルドスイング値（S値）とスレツショルド電圧（Vth)を示す図。 圆 18]従来例に係る製造方法によって形成された薄膜トランジスタとしてのポリシリコ ン TFTを示す概略断面図。
符号の説明
1 CVD装置
2 反応容器
5 上部電極
6 下部電極
9 基板
12 第 1の酸ィ匕珪素膜
13 窒化珪素膜
14 第 2の酸ィ匕珪素膜
15 ゲート絶縁層
16 ゲート電極
21 層間絶縁層
22 ソース電極
23 ドレイン電極
発明を実施するための最良の形態 [0014] 以下、本発明を図示の実施形態に基づいて説明する。
図 1は、本発明に係る製造方法によって形成された薄膜トランジスタとしての低温ポ リシリコン TFT (以下、ポリシリコン TFTという）を示す概略断面図であり、（a)はゲート 絶縁層が第 1の酸ィ匕珪素膜、窒化珪素膜及び第 2の酸ィ匕珪素膜の三層積層構造の もの、 (b)は第 1の酸化珪素膜及び窒化珪素膜の二層積層構造のものを示す。 図 1 (a)を参照して、本実施形態の薄膜トランジスタは、基板 9上にソース領域 17、 ドレイン領域 19、チャンネル領域 18を有する活性層 11と、ゲート電極層 16と、活性 層 11とゲート電極層 16との間に形成されるゲート絶縁層 15とを備え、ゲート絶縁層 1 5が、活性層 11側に形成される第 1の酸ィ匕珪素膜 12と、ゲート電極層 16側に形成さ れる第 2の酸ィ匕珪素膜 14と、第 1の酸ィ匕珪素膜 12と第 2酸ィ匕珪素膜 14の間に形成 される窒化珪素膜 13とを有している。
[0015] このような構成の本実施形態の薄膜トランジスタでは、閾値電圧及び S値を小さくす ることがでさる。
また図 1 (b)に示すように、ゲート絶縁層が第 1の酸ィ匕珪素膜及び窒化珪素膜の二 層構造でも、ゲート絶縁膜の絶縁性が満足するものであれば、図 1 (a)で示した第 2 の酸ィ匕珪素膜を成膜しなくてもょ ヽ。
[0016] 次に本実施形態の製造装置について説明する。
図 2は、このポリシリコン TFTのゲート絶縁層を成膜するためのプラズマ CVD装置 を示す概略断面図である。
このプラズマ CVD装置 1の反応容器 2の上部には、ガスボンベ等の複数のガス源（ 不図示)等が接続されているガス導入系 3が設けられており、反応容器 2の下部には 、真空ポンプ (不図示)等が接続されている排気系 4が設けられている。反応容器 2内 には、 2個の平板状の上部電極 5と下部電極 6が対向して設置されており、上側に位 置する上部電極 5には高周波電力をパルス変調させる変調器 7を介して外部の高周 波電源 8が接続され、下側に位置する下部電極 6上には成膜が施される基板 9が載 置され、下部電極 6は基板ホルダーも兼ねている。高周波電源 8は、上部電極 5に対 して 27. 12MHzの高周波電圧を印加するように構成されている。なお、高周波電圧 として 13. 56MHzも可能である力 上記 27. 12MHzの高周波電圧の方力 ガスの 分解効率が上がり好ましい。
上部電極 5は、その前面側（下部電極 6側）にシャワープレート 10が設けられるよう に中空部 5aを有しており、その中空部 5aと連通するようにしてガス導入系 3の先端側 を接続して、シャワープレート 10に形成されている多数のガス噴出口 10aから下部電 極 6上の基板 9に向けて均一に原料ガスを噴出させるように構成されている。また、下 部電極 6は、載置される基板 9を所定温度に加熱するヒータ (不図示）が内蔵されて おり、成膜中はアース電位に維持されるように構成されて 、る。
[0017] 次に、本発明に係るポリシリコン TFTの製造方法について説明する。
先ず、基板 9上に減圧熱 CVD法やプラズマ CVD法などによって非晶質珪素膜を 5 Onmの厚さに成膜した後に、キセノンクロライド (XeCl)エキシマレーザー（波長 308 nm)又はクリプトンフロライド (KrF)エキシマレーザー（波長 248nm)を照射すること により、非晶質珪素膜を結晶化させて結晶性珪素膜であるポリシリコン (Poly— Si)を 得ることができる。これをフォトリソグラフィー及びエッチングを用いてパターユングして 、活性層 11を形成する。
そして、活性層 11が形成された基板 9を、上記したプラズマ CVD装置 1の反応容 器 2内の下部電極 6上に載置して、ヒータ（不図示）に通電して抵抗加熱し、基板 9を 所定温度に加熱する。この際、反応容器 2内を排気系 4を通して排気して所定の圧 力に調整する。
[0018] そして、ガス導入系 3を通して反応容器 2内に第 1の珪素付与ガスとしてのテトラエト キシオルソシリケート (TEOS)等のシラン系ガスと、酸素等の酸素付与ガスからなる 混合ガス（原料ガス）を導入し、シャワープレート 10の多数のガス噴出口 10aから下 部電極 6上の基板 9に向けて均一に混合ガスを噴出させる。この際、高周波電源 8か ら上部電極 5に対して 27. 12MHzの高周波電圧を印加して、上部電極 5と下部電 極 6との間の空間に放電を発生させて上記混合ガスをプラズマ化し、活性層 11上に 第 1の絶縁層である第 1の酸ィ匕珪素膜 12を 40〜50nmの厚さで成膜する。
なお、第 1の酸化珪素膜 12を成膜する際に、第 1の珪素付与ガスとして上記したテ トラエトキシオルソシリケート (TEOS)等のシラン系ガス以外にも、例えばモノシランと 、ジシラン力もなる群より選択されるいずれか 1種類のガスを用いてもよぐまた、酸素 付与ガスとして酸素以外にも、例えば亜酸化窒素、オゾン、二酸化炭素、水からなる 群より選択される 、ずれか 1種類のガスを用いることができる。
[0019] そして、その後、同様にして第 2の珪素付与ガスとしてのモノシラン (SiH )等のシラ
4 ン系ガスと、アンモニア等の窒素付与ガスと、窒素等の希釈ガスからなる混合ガスを 導入し、放電により上記混合ガスをプラズマ化して、第 1の酸ィ匕珪素膜 12上に第 2の 絶縁層である窒化珪素膜 13を 10〜20nmの厚さで成膜する。
なお、窒化珪素膜 13を成膜する際に、第 2の珪素付与ガスとしてモノシラン以外に も、例えばテトラエトキシオルソシリケートと、へキサメチルジシラザンと、ジシランから なる群より選択されるいずれか 1種類のガスを用いてもよぐまた、前記窒素付与ガス としてアンモニア以外にも、例えば一酸化窒素、ヒドラジン力もなる群より選択される V、ずれ力 1種類のガスを用いることができる。
[0020] そして、その後、第 1の酸ィ匕珪素膜 12と同じガス系の混合ガスを導入し、放電により 上記混合ガスをプラズマ化して、窒化珪素膜 13上に第 3の絶縁層である第 2の酸ィ匕 珪素膜 14を 50nmの厚さで成膜する。そして、これをフォトリソグラフィー及びエッチ ングを用いてパターユングして、ゲート絶縁層 15を形成する。本発明の特徴であるゲ ート絶縁層 15の詳細については後述する。
この第 2の酸ィ匕珪素膜 14はゲート絶縁膜の絶縁性が満足するものであれば成膜し なくてもよい。
なお、第 1、 2の酸ィ匕珪素膜 12、 14を形成する混合ガスとしては、シラン系ガス、酸 素付与ガスのそれぞれから少なくとも 1種類ずつ選んで所定量混合してなる混合ガス を用いており、窒化珪素膜 13を形成する混合ガスとしては、シラン系ガス、窒素付与 ガス、希釈ガスのそれぞれから少なくとも 1種類ずつ選んで所定量混合してなる混合 ガスを用いている。
[0021] 次に、上記ゲート絶縁層 15 (第 2の酸ィ匕珪素膜 14)上に、アルミニウム膜をスパッタ 法で 250nmの厚さに成膜した後にモリブデン膜 50nmをスパッタ法で成膜する。この アルミニウム膜中にはスカンジウムを 0. 2重量0 /0含有させる。これは、後の工程にお いてヒロックゃゥイスカーと呼ばれる針状の突起物が形成されることを抑制するためで ある。そして、これをフォトリソグラフィー及びエッチングを用いてパターユングすること により、ゲート電極 16を形成する。
そして、ゲート電極 16を形成したら次にソース Zドレイン領域を形成するための不 純物（一導電型を付与するための不純物）のドーピングを行う。ここでは、 Nチャネル 型の薄膜トランジスタを得るために、 P (リン)のドーピングをプラズマドーピング法によ つて行う。ドーピングの終了後にァニールを行うことにより、ドーピングされた不純物の 活性ィ匕とドーピング時の損傷のァニールとを行う。上記の工程において、それぞれソ ース領域 17、チャネル領域 18、ドレイン領域 19が自己整合的に形成される。
[0022] 次に、ゲート電極 16とゲート絶縁層 15上に、 CVD法（プラズマ CVD法、熱 CVD法 、 ECRプラズマ CVD法など）により酸ィ匕珪素膜 20を 250nmの厚さで成膜する。そし て、これをフォトリソグラフィー及びエッチングを用いてコンタクトホールの形成を行な つて層間絶縁層 21を形成した後、モリブデン膜をスパッタ法で 50nmの厚さに成膜し た後にアルミニウム膜 300nmを成膜し、ソース電極 22とドレイン電極 23の形成する ことにより、図 1に示した本発明に係るポリシリコン TFTが得られる。
[0023] 次に、上記した触媒 CVD装置 1によって製造される本発明に係るゲート絶縁層 15 の成膜条件等について説明する。
本発明に係るゲート絶縁層 15の膜厚は、第 1層（第 1の酸ィ匕珪素膜 12)：第 2層（窒 化珪素膜 13)：第 3層（第 2の酸ィ匕珪素膜 14) = 50nm: 10nm: 50nmであり、それぞ れの成膜プロセス条件は、図 3に示した通りである。なお、比較のために、従来のポリ シリコン TFTのゲート絶縁層で使用されている TEOSを原料ガスとした酸ィ匕珪素膜 の代表的な成膜プロセス条件も併せて図 3に示した。なお、成膜速度、基板面内で の膜厚分布については、 730mm X 920mmサイズのガラス基板上に成膜した場合 の結果である。また、 Vl (単位: V)は、ゲート絶縁層中の欠陥の量を示す指標として フラットバンド電圧であり、 Dit (単位: Cm_2'eV_1)は、ゲート絶縁層と珪素薄膜の界 面の欠陥密度を示す指標としての界面準位密度である。また、この場合の基板は、 P 型の Si[001]単結晶ウェハ（Na = 2 X 1015cm"3)を用いて!/、る。
図 3に示したように、従来のゲート絶縁層の場合は、 TEOSを原料ガスとした酸ィ匕珪 素膜の成膜速度: 80nmZmin程度で、基板面内での膜厚分布 (10mm端 )： ± 7. 5 %程度である。また、その膜厚を l lOnmとした場合、 Vl =— 1. 5〜― 2. 0Vであり 、 Dit = 8 X 10 cm 'eV であった。
[0024] このことを踏まえると、後述する図 4〜図 16に示す測定結果から、本発明における ゲート絶縁層の成膜プロセス条件は、ゲート絶縁層の全体の成膜速度： 78〜83nm Zmin程度で、基板面内での膜厚分布 (10mm端)： ± 5. 5〜7. 0%程度である。ま た、その膜厚を l lOnmとした場合、 Vl =— 1. 0〜一 1. 5Vであり、 Dit=4. 3 X 101 °〜9. 6 X 1010cm_2'eV_1である。
図 4は、第 1、第 3層としての酸ィ匕珪素膜 (第 1、第 2の酸ィ匕珪素膜 12、 14)の形成 時における、成膜温度と成膜速度の関係を示す測定結果であり、図 5は、酸化珪素 膜 (第 1、第 2の酸ィ匕珪素膜 12、 14)の形成時における、成膜温度と Dit、 Vlの関係 を示す測定結果である。なお、図 5において、 aは Ditであり、 bは Vlである。
図 4に示す測定結果力も明らかなように、成膜温度を上げると成膜速度が低下し生 産性が落ちる。また、図 5に示す結果力も明らかなように、 Ditは成膜温度が上がると 減少して界面の欠陥密度が低下するが、 430°C程度以上で概ね一定値になる。一 方、 Vl は成膜温度が上がると上昇して層内の欠陥量の減少を示すが、 430°C以上 で一定値となる。なお、基板の耐熱温度ならびに装置材料の都合上力 450°C程度 以下が好ましい。
このため、酸ィ匕珪素膜 (第 1、第 2の酸ィ匕珪素膜 12、 14)の成膜速度を高く維持し、 Ditを低ぐ Vlを高く成膜するためには、 330°C〜430°C程度の範囲で成膜すること が好ましい。
[0025] 図 6は、酸ィ匕珪素膜 (第 1、第 2の酸ィ匕珪素膜 12、 14)の形成時における、珪素付 与ガスに対する酸素ガス組成比と成膜速度の関係を示す測定結果であり、図 7は、 酸ィ匕珪素膜 (第 1、第 2の酸ィ匕珪素膜 12、 14)の形成における、酸素ガス組成比と D it、 Vl の関係を示す測定結果である。なお、図 7において、 aは Ditであり、 bは Vlで ある。
図 6に示す結果力も明らかなように、酸素ガス組成比を上げると成膜速度が低下し 生産性が落ちる。また、図 7に示す結果から明らかなように、 Ditは酸素ガス組成比が 上がると減少して界面の欠陥密度が低下し、酸素ガス組成比が 30以下で急激に低 下して、 50以上で概ね一定値となる。一方、 Vlbは酸素ガス組成比が上がると上昇し て層内の欠陥量の減少を示すが、 30以下で急激に上昇し 50以上で概ね一定値と なる。
このため、酸ィ匕珪素膜 (第 1、第 2の酸ィ匕珪素膜 12、 14)の成膜速度を高く維持し、 Ditを低ぐ Vlを高く成膜するためには、珪素付与ガスに対する酸素ガス組成比が 3 0〜50の範囲で成膜することが好まし!/、。
[0026] 図 8は、酸ィ匕珪素膜 (第 1、第 2の酸ィ匕珪素膜 12、 14)を形成時における、プロセス 圧力と成膜速度及び基板面内分布の関係を示す測定結果である。なお、図 8におい て、 aは成膜速度、 bは基板面内分布である。この測定結果から明らかなように、プロ セス圧力を上げると成膜速度が減少する。また、基板面内分布は、プロセス圧力 125 Pa付近で最小値を取る。
このため、酸ィ匕珪素膜 (第 1、第 2の酸ィ匕珪素膜 12、 14)の基板面内分布を小さく するためには、プロセス圧力 80〜200Pa程度の範囲で成膜することが好ましい。 図 9は、窒化珪素膜 (第 2の絶縁層としての窒化珪素膜 13)の形成時における、珪 素付与ガスに対する窒素付与ガスとしてのアンモニアガス組成比と成膜速度の関係 を示す測定結果であり、図 10は、窒化珪素膜 (第 2の絶縁層としての窒化珪素膜 13 )の形成時における、アンモニアガス組成比と Dit、 Vl の関係を示す測定結果である 。なお、図 10において、 aは Ditであり、 bは Vlである。
[0027] 図 9に示す測定結果力も明らかなように、アンモニアガス組成比を上げると成膜速 度が低下し生産性が落ちる。また、図 10に示す結果から明らかなように、アンモニア ガス組成比が上がると Ditは減少して界面の欠陥密度が低下し、アンモニアガス組成 比が 20程度まで Ditは急激に低下して、 20以上で概ね一定値となる。一方、 Vlbはァ ンモユアガス組成比が上がると上昇して層内の欠陥量の減少を示す力 20程度まで 急激に上昇し 20以上で概ね一定値となる。
したがって、窒化珪素膜 (第 2の絶縁層としての窒化珪素膜 13)の成膜速度を高く 維持し、 Ditを低ぐ Vlbを高く成膜するためには、アンモニアガス組成比が 10〜25程 度の範囲で成膜することが好ま 、。
図 11は、窒化珪素膜 (第 2の絶縁層としての窒化珪素膜 13)の形成時における、珪 素付与ガスに対する窒素ガス (希釈ガス)の組成比と、成膜速度と基板面内分布の関 係を示す測定結果である。なお、図 11において、 aは成膜速度であり、 bは基板面内 分布である。
[0028] 図 11に示す測定結果から明らかなように、窒素ガスの組成比を上げると成膜速度 が減少する。また、基板面内分布は、窒素ガスの組成比 20付近で最小値を取る。こ のため、窒化珪素膜 (第 2の絶縁層としての窒化珪素膜 13)の基板面内分布を小さく するためには、窒素ガスの組成比 10〜30程度の範囲で成膜することが好ましい。 図 12は、窒化珪素膜 (第 2の絶縁層としての窒化珪素膜 13)の形成時における、プ ロセス圧力と、成膜速度と基板面内分布の関係を示す測定結果である。なお、図 12 において、 aは成膜速度であり、 bは基板面内分布である。
図 12に示す測定結果力も明らかなように、プロセス圧力を上げると成膜速度が減少 し、基板面内分布はプロセス圧力 250Pa付近で最小値を取る。このため、窒化珪素 膜 (第 2の絶縁層としての窒化珪素膜 13)の基板面内分布を小さくするためには、プ ロセス圧力 200〜400Pa程度の範囲で成膜することが好まし!/、。
[0029] 図 13は、窒化珪素膜 (第 2の絶縁層としての窒化珪素膜 13)の形成時における、成 膜温度と成膜速度の関係を示す測定結果であり、図 14は、窒化珪素膜 (第 2の絶縁 層としての窒化珪素膜 13)の形成時における、成膜温度と Dit、 Vlbの関係を示す測 定結果である。なお、図 14において、 aは Ditであり、 bは Vlbである。
図 13に示す測定結果力も明らかなように、成膜温度を上げると成膜速度が低下し 生産性が落ちる。また、図 14に示す結果力も明らかなように、 Ditは成膜温度が上が ると減少して界面の欠陥密度が低下するが、 430°C程度以上で概ね一定値になる。 一方、 Vl は成膜温度が上がると上昇して層内の欠陥量の減少を示すが、 430°C程 度以上で一定値となる。なお、基板の耐熱温度力も 450°C程度以下が好ましい。 このため、窒化珪素膜（(第 2の絶縁層としての窒化珪素膜 13)の成膜速度を高く 維持し、 Ditを低ぐ Vlbを高く成膜するためには、 330°C〜430°C程度の範囲で成膜 することが好ましい。
[0030] 図 15は、本発明におけるゲート絶縁層 15の第 1、第^ i (第 1、第 2の酸ィ匕珪素膜 1 2、 14)における膜厚と、 Dit、 Vlの関係を示す測定結果である。図 16は、本発明に おけるゲート絶縁層 15の第 2層（窒化珪素膜 13)における膜厚と、 Dit、 Vlの関係を 示す測定結果である。なお、図 15、図 16において、 aは Ditであり、 bは Vlである。 図 15、図 16に示す測定結果力も明らかなように、第 2層（窒化珪素膜 13)の膜厚を 10〜20nmとした場合に、第 1、第^ i (第 1、第 2の酸ィ匕珪素膜 12、 14)の膜厚がそ れぞれ 40〜50nmの範囲で良質な膜質（Ditが低ぐかつ Vlが高い）のゲート絶縁 層を得ることができた。
[0031] また、上記した本発明に係るゲート絶縁層 15と、 TEOSを原料ガスとした酸ィ匕珪素 膜からなる従来のゲート絶縁層をそれぞれ有する上記ポリシリコン TFTを製造した場 合における、サブスレツショルドスイング値（S値、単位: VZdec)とスレツショルド電圧 (Vth,単位: V)を測定したところ、図 17に示すような測定結果が得られた。なお、こ のときの各ゲート絶縁層の成膜プロセス条件は、図 3の場合と同様である。
図 17に示す測定結果力も明らかなように、本発明に係る 3層構造のゲート絶縁層 ( 第 1の酸ィ匕珪素膜 12、窒化珪素膜 13、第 2の酸ィ匕珪素膜 14) 15を成膜することによ り、従来の単層構造のゲート絶縁層（酸化珪素膜）に比べて、サブスレツショルドスィ ング値（S値）を小さぐかつスレツショルド電圧 (Vth)の小さ 、高性能なポリシリコン T FTを作製することができる。
[0032] このように、発明に係る製造方法によれば、良好な生産性を確保しつつ、優れた特 性 (低い基板温度 (450°C程度以下）にてゲート絶縁層の膜中の欠陥ならびに珪素 薄膜との界面の欠陥密度を大幅に低減した)のゲート絶縁層を有するポリシリコン TF Tを得ることがでさる。

Claims

請求の範囲
[1] 基板上にソース領域、ドレイン領域、チャンネル領域を有する活性層と、ゲート電極 層と、前記活性層と前記ゲート電極層との間に形成されるゲート絶縁層とを有する薄 膜トランジスタであって、
前記ゲート絶縁層が、前記活性層に接して形成される第 1の酸化珪素膜と、この第 1の酸ィ匕珪素膜と前記ゲート電極層との間に前記第 1の酸ィ匕珪素膜に接して形成さ れる窒化珪素膜とを含む、ことを特徴とする薄膜トランジスタ。
[2] 前記窒化珪素膜と前記ゲート電極層との間に第 2の酸ィ匕珪素膜を有することを特 徴とする請求項 1に記載の薄膜トランジスタ。
[3] 前記活性層がポリシリコンで形成される、ことを特徴とする請求項 1又は 2に記載の 薄膜トランジスタ。
[4] 前記第 1の酸ィ匕珪素膜、前記窒化珪素膜の膜厚の比が、 4〜5： 1〜2である、こと を特徴とする請求項 1記載の薄膜トランジスタ。
[5] 前記第 1の酸ィヒ珪素膜、前記窒化珪素膜、前記第 2の酸ィヒ珪素膜のそれぞれの膜 厚の比力 4〜5 : 1〜2 :4〜5である、ことを特徴とする請求項 2に記載の薄膜トラン ジスタ。
[6] 前記第 1の酸ィ匕珪素膜の膜厚が 40nm以上 50nm以下である、ことを特徴とする請 求項 1又は 2に記載の薄膜トランジスタ。
[7] 前記窒化珪素膜の膜厚が lOnm以上 20nm以下である、ことを特徴とする請求項 1 又は 2に記載の薄膜トランジスタ。
[8] 前記ゲート絶縁層全体の層厚が、 50nm以上 200nm以下である、ことを特徴とする 請求項 1〜7に記載の薄膜トランジスタ。
[9] 基板表面に活性層を形成する工程と、
前記活性層上に第 1の酸ィ匕珪素膜を形成する工程と、
前記第 1の酸ィヒ珪素膜上に窒化珪素膜を形成する工程と、
前記窒化珪素膜上にゲート電極層を形成する工程とを含む、ことを特徴とする薄膜 トランジスタの製造方法。
[10] 前記ゲート電極層を形成する工程が、前記窒化珪素膜上に第 2の酸ィ匕珪素膜を形 成後、ゲート電極層を形成する工程であることを特徴とする請求項 9記載の薄膜トラ ンジスタの製造方法。
[11] 前記第 1の酸ィ匕珪素膜を形成する工程においては、圧力調整された反応容器内に 珪素原子を含む第 1の珪素付与ガス、酸素原子を含む酸素付与ガスのそれぞれの 少なくとも一種類ずつを導入して、プラズマ CVD法により酸ィ匕珪素膜を形成し、 前記窒化珪素膜を形成する工程においては、圧力調整された反応容器内に珪素 原子を含む第 2の珪素付与ガス、窒素原子を含む窒素付与ガス、希釈ガスのそれぞ れの少なくとも一種類ずつを導入して、プラズマ CVD法により窒化珪素膜を形成す る、ことを特徴とする請求項 9又は 10に記載の薄膜トランジスタの製造方法。
[12] 前記第 1の珪素付与ガスは、テトラエトキシオルソシリケートと、へキサメチルジシラ ザンと、モノシランと、ジシラン力 なる群より選択されるいずれ力 1種類のガスであり、 前記酸素付与ガスは、酸素、亜酸化窒素、オゾン、二酸化炭素、水からなる群より 選択される!、ずれか 1種類のガスである、ことを特徴とする請求項 11に記載の薄膜ト ランジスタの製造方法。
[13] 前記第 1の珪素付与ガスと前記酸素付与ガスの組成比が、 1： 30〜50である、こと を特徴とする請求項 11又は 12に記載の薄膜トランジスタの製造方法。
[14] 前記酸ィ匕珪素膜の成膜時の圧力は 80〜200Paであり、基板温度は 330〜430°C である、ことを特徴とする請求項 11〜13のいずれか 1項に記載の薄膜トランジスタの 製造方法。
[15] 前記第 2の珪素付与ガスは、テトラエトキシオルソシリケートと、へキサメチルジシラ ザンと、モノシランと、ジシラン力 なる群より選択されるいずれ力 1種類のガスであり、 前記窒素付与ガスは、アンモニア、一酸化窒素、ヒドラジン力 なる群より選択され る!、ずれか 1種類のガスである、ことを特徴とする請求項 11〜14の 、ずれか 1項に記 載の薄膜トランジスタの製造方法。
[16] 前記第 2の珪素付与ガス、前記窒素付与ガス、前記希釈ガスの組成比が、 1： 10〜
25 : 10〜30である、ことを特徴とする請求項 11〜15のいずれか 1項に記載の薄膜ト ランジスタの製造方法。
[17] 前記窒化珪素膜の成膜時の圧力は 200〜400Paであり、基板温度は 330〜430 °Cである、ことを特徴とする請求項 11〜16のいずれか 1項に記載の薄膜トランジスタ の製造方法。
プラズマ CVD法で前記第 1の酸ィヒ珪素膜、前記第 2の酸ィヒ珪素膜、前記窒化珪素 膜をそれぞれ形成する際の、電極に印加する高周波電圧の周波数が 27.1MHzで ある、ことを特徴とする請求項 11〜17のいずれか 1項に記載の薄膜トランジスタの製 造方法。
PCT/JP2005/007808 2004-04-23 2005-04-25 薄膜トランジスタ及びその製造方法 Ceased WO2005104239A1 (ja)