WO2005019131A1 - 吹付け材料及びそれを用いた吹付け工法 - Google Patents
吹付け材料及びそれを用いた吹付け工法 Download PDFInfo
- Publication number
- WO2005019131A1 WO2005019131A1 PCT/JP2004/012247 JP2004012247W WO2005019131A1 WO 2005019131 A1 WO2005019131 A1 WO 2005019131A1 JP 2004012247 W JP2004012247 W JP 2004012247W WO 2005019131 A1 WO2005019131 A1 WO 2005019131A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- parts
- quick
- setting
- cement
- material according
- Prior art date
Abstract
Description
Claims