WO2003060992A1 - Appareil a semi-conducteurs et procede de fabrication - Google Patents
Appareil a semi-conducteurs et procede de fabrication Download PDFInfo
- Publication number
- WO2003060992A1 WO2003060992A1 PCT/JP2003/000141 JP0300141W WO03060992A1 WO 2003060992 A1 WO2003060992 A1 WO 2003060992A1 JP 0300141 W JP0300141 W JP 0300141W WO 03060992 A1 WO03060992 A1 WO 03060992A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- semiconductor device
- trench
- heat treatment
- oxide film
- Prior art date
Description
Claims