Classifications

• • G—PHYSICS
  • G01—MEASURING; TESTING
  • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
  • G01N15/00—Investigating characteristics of particles; Investigating permeability, pore-volume or surface-area of porous materials
  • G01N15/08—Investigating permeability, pore-volume, or surface area of porous materials
• • G—PHYSICS
  • G01—MEASURING; TESTING
  • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
  • G01N15/00—Investigating characteristics of particles; Investigating permeability, pore-volume or surface-area of porous materials
  • G01N15/08—Investigating permeability, pore-volume, or surface area of porous materials
  • G01N15/082—Investigating permeability by forcing a fluid through a sample
• • G—PHYSICS
  • G01—MEASURING; TESTING
  • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
  • G01N15/00—Investigating characteristics of particles; Investigating permeability, pore-volume or surface-area of porous materials
  • G01N15/10—Investigating individual particles
  • G01N15/1031—Investigating individual particles by measuring electrical or magnetic effects
  • G01N15/12—Investigating individual particles by measuring electrical or magnetic effects by observing changes in resistance or impedance across apertures when traversed by individual particles, e.g. by using the Coulter principle
  • G01N15/131—Details
  • G01N15/132—Circuits
• • G—PHYSICS
  • G01—MEASURING; TESTING
  • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
  • G01N15/00—Investigating characteristics of particles; Investigating permeability, pore-volume or surface-area of porous materials
  • G01N15/08—Investigating permeability, pore-volume, or surface area of porous materials
  • G01N2015/086—Investigating permeability, pore-volume, or surface area of porous materials of films, membranes or pellicules

Definitions

• the invention relates to a method for measuring the permeation rate of a substrate, especially a flexible substrate such as a polymer (plastic) substrate for use in liquid crystal display devices, polyLED and other (organic) LED display devices.
• a flexible substrate such as a polymer (plastic) substrate for use in liquid crystal display devices, polyLED and other (organic) LED display devices.
• the electroluminescent organic materials are easily oxidized and react with water.
• the cathode material usually reactive metals are used, which degrade even faster.
• the state of the art glass is used as a substrate, which is highly impermeable.
• the main concern related to permeability resides in the permeation rate of the seal line. In LCD's the water may react with the liquid crystal material.
• the invention has as its purpose to solve one or more of these problems To this end it provides a method for measuring a permeation rate, a test method and an apparatus for measuring and testing in which permeation rates as low as 10 "5 g/m 2 /day for water or even lower can be measured.
• a method according to the invention comprises the steps of a) applying a layer of a reactive material to a first side of the substrate in an substantially inert atmosphere b) positioning said first side of the substrate within a substantially hermetically sealed environment c) exposing the other side of the substrate to an environment containing compounds which react with the reactive material and d) comparing the light reflectivity or the light absorption of the layer of ref active material with a calibration value.
• the invention is based on the insight that because of e.g. oxidation due to the presence of water and oxygen a reactive material like barium or calcium evolves to an increasingly transparent layer.
• the transmission or reflection characteristics of the layer can be measured and for instance by storing successive measurements (e.g. CCD images) image analysis, like grey value determination, can be used to determine the thickness of the residual metal layer, which is related to the amount of absorbed compounds, especially water. So these transmission or reflection characteristics are directly related to the permeation rate.
• the method according to the invention has the advantages of faster testing.
• a substantially impermeable substrate metal or glass
• permeability of a seal or a sealing rim on the substrate may determine the permeation rate.
• substrate is meant to comprise said seal or a sealing rim.
• a sealing rim having more walls is used if necessary. Providing a getter in a double walled seal can prevent further sensibility to penetration through said walls.
• the reactive material used for the test can be used as getter when applied between the two seal rings.
• a test method In a test method according to the invention at least one sample substrate is tested with said method and discriminating between batches to have them pass or not pass the test is based on a threshold value of the permeation rate .
• the threshold value may either be a mean value or be an extreme value of the permeation rate within a batch.
• An apparatus comprises a) a first chamber in which an substantially inert atmosphere can be generated b) means for introducing a reactive material into said chamber c) means for positioning said first side of the substrate within a substantially hermetically sealed environment d) means for exposing the hermetically sealed environment to compounds which react with the reactive material e) means for comparing the light reflectivity or the light absorption of the reactive material with a calibration value It appears that the test method on the other hand can be used for testing the permeability of encapsulations, like seals, lids or measurement capsules.
• Figure 1 shows a plane view of a sample substrate within a substantially hermetically sealed environment
• Figure 2 shows a cross section along line H-II in Figure 1.
• Figure 3 shows transmission curves for a CaO/Ca layer on glass for different wavelengths as a function of the layer thickness
• Figure 4 shows transmission curves for a CaO/Ca layer on glass for different values of the layer thickness as a function of the wavelength
• Figure 6 shows the results of some sample tests.
• Figure 7 shows a schematic embodiment of a measuring and testing equipment for measuring or testing the permeation rate.
• Figure 8 shows means for obtaining a sample substrate within a substantially hermetically sealed environment,
• Figures 9 and 10 show embodiments of devices for measuring the light reflectivity or the light absorption of a layer
• Figure 11 shows another embodiment according to the invention, while Figure 12 shows a cross section along line XJJ-XII in Figure 11 and
• Figure 13 shows another example of using the invention.
• a thin layer 2 (e.g. 100 nm) of a reactive material, in this example Ca, is deposited in an substantially inert atmosphere on a substrate 1 to be tested.
• the Ca is deposited in a pattern of 16 squares.
• a glass sheet or lid 3 is interconnected to the substrate 1 along its edge via a substantially hermetic seal 4, e. g. a glue, a metal like In or a solder metal to form a closed box.
• the Ca layer may be covered by a hermetic coating (silicon nitride, silicon oxide or a metal layer( to provide a hermetic sealing of said layer. Water or oxygen permeating into the box reacts with Ca according to the reactions
• Figure 3 shows calculated transmission curves for a CaO/Ca layer on glass for different wavelengths, viz. 500 nm (curve a), 600 nm (curve b), 700 nm (curve c), 800 nm (curve d) and the substrate 1 (curve e), as a function of the layer thickness. Since the layer thickness is in the order of the wavelength of light the transmission or reflection of the layer the transmission and reflection of the layers depend strongly on the wavelength too. This is shown by way of example in Figure 4, which shows calculated transmission curves for a CaO/Ca layer on glass for different values of the layer, viz.
• Figure 5 shows transmission curves for a CaO/Ca layer on glass at a fixed wavelength as a function of the layer thickness for different values of the original layer thickness.
• ⁇ 500 nm for layers having an original layer thickness of 90 nm (curve d), 100 nm (curve e), 120 nm (curve g), and 150 nm (curve i)
• Said curve can be stored as a function relating the transmission or reflection to a certain layer thickness.
• the intermediate values of transmission or reflection can be measured as (average) grey-values by means of a CCD device or a digital camera.
• a black border is introduced in the device of Figure 1 to measure the transmission of an average black area; the reference value for average white is determined by measuring the transmission of the transmissive area between the squares of deposited Ca. Since the thickness of the original Ca layer as well as the total area is known a (difference in) grey- value can be attributed to a (difference in) layer thickness. The total amount of Ca having reacted according to reactions (1), (2) and (3) and the amount of water required to convert the residual calcium volume is known. . This is shown for a number of samples in Figure 6, which shows the residual calcium volume as a function of time. The difference between two moments of measuring determines the difference in grey-values between said two moments of measuring.
• the slope of a curve is a measure for the permeation rate.
• the sample of curve c shows a permeation rate of about 2.10 "3 g m 2 /day for water
• the sample of curves e and f show permeation rates of about 2.10 " g/m /day for water
• sample of curve d shows a permeation rate of ⁇ 10 "5 g/m 2 /day for water. This shows that the method can measure permeation rates up to a factor 100 or more better than existing equipment. Similar experiments show that the method is suitable for testing oxygen 9 permeability to a level of 10 " cc/m /day/bar or lower.
• Figure 7 shows a measuring and testing equipment 5 for measuring or testing the permeation rate in which means 6 for obtaining a sample substrate and a device 7 for measuring the light reflectivity or the light absorption of a layer are both present within the same substantially hermetically sealed environment, for example a glove box 8 with manipulating means 9.
• the means 6 for obtaining a sample substrate and the device 7 for measuring the light reflectivity or the light absorption of a layer may be placed in different glove boxes 8, provided the samples can be transported from the means 6 for obtaining a sample substrate to the device 7 for measuring in a substantially hermetically sealed environment.
• a sample substrate is obtained by calcium deposition of a predetermined thickness, e. g.
• Figures 9 shows in more detail a possible device 7 for measuring the light transmission of a CaO/Ca layer on glass in a sample as prepared with reference to Figure 8, which sample is exposed to an H 2 O atmosphere.
• the sample 15 is placed on top of an optical system 16, which is illuminated by means of fiber illumination via a fiber 17.
• the light passes the sample via a mirror 18 and digital images are taken by means of a digital camera 19.
• the images 20 may be taken on a continuous base and are stored via interconnections 21 in a computer or dataprocessing equipment 22.
• Figure 10 shows another implementation in which the transmission is measured for a single colour by introducing a colour filter 23.
• the sample 15 is now vertically placed within a hole 26 in a support 24 and is illuminated by means of a backlight 25.
• the camera 19 is in this example a CCD camera optimized for the colour used.
• the camera 19, a colour filter 23 and the support 24 are placed on an optical rail 27.
• Image processing of the obtained grey - values can be performed in different ways. As mentioned above, a calibration curve can be determined in advance, as is shown with reference to Figures 3 - 5. Other methods such as deconvolution of spectra are also possible.
• steps of the method preferably are performed in dedicated sub-apparatuses, such as a first sub-apparatus for deposition, a second one for exposing to environmental conditions and a third one for measuring, although some of these may be combined e.g. in the case of continuous monitoring of the Ca layer, which may be useful when testing is performed at elevated temperatures.
• FIGs 11 and 12 finally show another implementation in which a (non- transparent) substrate 1 is sealed to a housing 30, comparable to the lid 3 in Figures 1,2, whereas the Ca pattern 3 now has been deposited on a transmissive substrate 31 of a measuring cell 32.
• the housing 30 is interconnected to the measuring cell 32 via a glass tube 33. Water or oxygen permeating into the housing 30 via substrate 1 passes the tube 33 and reacts with Ca.
• the Ca layer is affected in a similar method as mentioned above.
• the transparency of the layer is measured again for example in a similar method as shown with respect to Figures 9, 10 to determine the permeation rate. In some cases, if the substrates have very small permeability the leaking of the seal sets the lower boundary of the sensitivity of the measurement method.
• the seal is split in two walls (an outer wall 4' and an inner wall 4", as shown in Fig.13 for a measurement to be discussed below). Between these two walls a cavity is created where a getter (desiccant) 15 is placed. If for the desiccant the same reactive material that as for the measurement,is chosen they can be applied in the same process step.
• the making of two chambers in the seal does not have to be an additional step, e.g. when using a glass lid, where the cavities are made by powderblasting.
• the measure of reflection of the layers is an indication for its thickness and can be used to determine the permeation rate.
• Another reactive material like barium or natrium can be used in stead of calcium.
• gadolinium which is very suitable for the testing of permeation of hydrogen.
• the layer 2 comprises a stack of metals, e.g. Gd/Pd or Mg x Gd x /Pd. The reactive compound reacts well with diffusing hydrogen.
• the reaction leads to a change in the appearance of the layer again.
• a catalyst might be necessary. This means that instead of a single Ca-layer a stack of two layers is deposited, for instance lOOnmGd + 10 nm Pd. For a surface area of 1 cm 2 this represents 5.10 "7 mole Gd. This silvery Gd reacts to dark blue GdH 2 . The change in colour is measured again as a change in reflection ( or transmission. If 5 .10 "7 mole H 2 reacts in 1 day this represents a hydrogen flux of 10 "2 g H 2 per day per m 2 . Hydrogen fluxes between 10 "4 and 10 2 g H2 per day per m 2 can be measured with this set up.
• the Pd layer not only acts as a catalyst but also protects the Gd from corrosion in air.
• the insensitivity of the indicator metal layer makes this method very suitable for making half fabricates for the metod or for an apparatus according to the invention, like ready-to-use cover lids 3 (with indicator metal layer 2', See Figure 13 ) or measuring cells 32.

Landscapes

• Chemical & Material Sciences (AREA)
• Biochemistry (AREA)
• Physics & Mathematics (AREA)
• Health & Medical Sciences (AREA)
• Life Sciences & Earth Sciences (AREA)
• Analytical Chemistry (AREA)
• Dispersion Chemistry (AREA)
• General Health & Medical Sciences (AREA)
• General Physics & Mathematics (AREA)
• Immunology (AREA)
• Pathology (AREA)
• Investigating Or Analysing Materials By Optical Means (AREA)
• Investigating Or Analysing Materials By The Use Of Chemical Reactions (AREA)
• Investigating Or Analyzing Non-Biological Materials By The Use Of Chemical Means (AREA)

Priority Applications (4)

Applications Claiming Priority (4)

Publications (2)

Family

ID=26076870

Family Applications (1)

Country Status (8)

Cited By (3)

Families Citing this family (38)

Family Cites Families (29)

• 2002
  • 2002-03-13 KR KR1020027016047A patent/KR100859818B1/ko not_active Expired - Fee Related
  • 2002-03-13 WO PCT/IB2002/000754 patent/WO2002079757A2/en not_active Ceased
  • 2002-03-13 EP EP02703801A patent/EP1373861A2/en not_active Withdrawn
  • 2002-03-13 AU AU2002237478A patent/AU2002237478A1/en not_active Abandoned
  • 2002-03-13 CN CNB028008804A patent/CN1242250C/zh not_active Expired - Fee Related
  • 2002-03-13 JP JP2002577538A patent/JP4209194B2/ja not_active Expired - Fee Related
  • 2002-03-18 TW TW091105083A patent/TWI229733B/zh not_active IP Right Cessation
  • 2002-03-26 US US10/106,951 patent/US6993956B2/en not_active Ceased
• 2005
  • 2005-12-12 US US11/298,651 patent/US7117720B2/en not_active Expired - Fee Related

Also Published As

Similar Documents

Legal Events