WO2002072285A2 - Beschichtete aluminiumhalbzeuge und/oder -bauteile und verfahren zu ihrer herstellung - Google Patents
Beschichtete aluminiumhalbzeuge und/oder -bauteile und verfahren zu ihrer herstellung Download PDFInfo
- Publication number
- WO2002072285A2 WO2002072285A2 PCT/DE2002/000924 DE0200924W WO02072285A2 WO 2002072285 A2 WO2002072285 A2 WO 2002072285A2 DE 0200924 W DE0200924 W DE 0200924W WO 02072285 A2 WO02072285 A2 WO 02072285A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- aluminum
- coated
- semi
- components
- products
- Prior art date
Abstract
Description
Claims