Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/16—Nitrogen-containing compounds
  • C08K5/34—Heterocyclic compounds having nitrogen in the ring
  • C08K5/3412—Heterocyclic compounds having nitrogen in the ring having one nitrogen atom in the ring
  • C08K5/3432—Six-membered rings
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/54—Silicon-containing compounds
  • C08K5/5406—Silicon-containing compounds containing elements other than oxygen or nitrogen

Definitions

• the present invention relates to diene rubber compositions reinforced with a white or inorganic filler, intended in particular for the manufacture of tires or semi-finished products for tires, in particular the treads of these tires.
• carbon black exhibits such aptitudes, which is generally not the case for white or inorganic fillers.
• the particles of inorganic charge have an annoying tendency, in the elastomeric matrix, to agglomerate between them.
• These interactions have the harmful consequence of limiting the dispersion of the filler and therefore the reinforcing properties to a level substantially lower than that which would theoretically be possible to achieve if all the bonds (inorganic filler / elastomer) capable of being created. during the mixing operation, were actually obtained; on the other hand, these interactions tend to increase the consistency of the rubber compositions and therefore to make their use (“processability") in the raw state more difficult than in the presence of carbon black.
• a coupling agent also called a bonding agent, which has the function of ensuring the connection between the surface of the particles of inorganic filler and the elastomer, while facilitating the dispersion of this filler inorganic within the elastomeric matrix.
• coupling agent inorganic filler / elastomer
• an agent capable of establishing a sufficient connection, of chemical and / or physical nature, between the inorganic filler and the elastomer; such a coupling agent, at least bifunctional, has for example as simplified general formula "Y-T-X", in which:
• Y represents a functional group (“Y” function) which is capable of physically and / or chemically binding to the inorganic charge, such a bond being able to be established, for example, between a silicon atom of the coupling agent and the surface hydroxyl groups (OH) of the inorganic filler (for example surface silanols when it is silica);
• X represents a functional group ("X" function) capable of binding physically and / or chemically to the elastomer, for example via a sulfur atom; - T represents a hydrocarbon group making it possible to link Y and X.
• Coupling agents should in particular not be confused with simple inorganic charge covering agents which, in known manner, may comprise the active Y function with respect to the inorganic charge but are devoid of the active X function vis opposite the elastomer.
• Silica / elastomer coupling agents in particular, have been described in a large number of documents, the best known being bifunctional alkoxysilanes.
• TESPD bis 3-triethoxysilylpropyl disulphide
• TESPT bis 3-triethoxysilylpropyl tetrasulphide
• Si69 organic charge / diene elastomer
• a first subject of the invention relates to a rubber composition which can be used for the manufacture of tires, based on at least (i) a diene elastomer, (ii) an inorganic filler as a reinforcing filler, (iii) a polysulphurized alkoxysilane as coupling agent (inorganic filler / diene elastomer) with which are associated (iv) a 1,2-dihydropyridine and (v) a guanidine derivative.
• a subject of the invention is also the use of a rubber composition in accordance with the invention for the manufacture of rubber articles, in particular tires or semi-finished products intended for these tires, these semi-finished products.
• treads being chosen in particular from the group consisting of treads, the sub-layers intended for example to be placed under these treads, the crown plies, the sides, the carcass plies, the heels, the protectors, the chambers air and waterproof inner liners for tubeless tires.
• the invention relates more particularly to the use of such a rubber composition, because of its good hysteretic properties, for the manufacture of sidewalls or treads.
• the invention also relates to a process for the preparation of a composition in accordance with the invention, this process being characterized in that there is incorporated in (i) at least one diene elastomer, at least: (ii) an inorganic filler as reinforcing filler; (iii) a polysulfurized alkoxysilane; (iv) a 1,2-dihydropyridme, and (v) a guanidine derivative, and in that thermomechanically kneading the whole, in one or more stages, until reaching a maximum temperature of between 120 ° C. and 190 ° vs.
• composition in accordance with the invention is particularly suitable for making tire treads intended for equipping passenger vehicles, 4x4 vehicles, vans, two-wheeled and heavy goods vehicles, airplanes, civil engineering, agricultural or handling, these treads can be used during the manufacture of new tires or for retreading used tires.
• the subject of the invention is also these tires and these semi-finished rubber products themselves when they comprise a rubber composition in accordance with the invention.
• the invention relates in particular to tire treads; thanks to the compositions of the invention, these treads have both a low rolling resistance and a high resistance to wear, even in the presence of a reduced level of polysulphurized alkoxysilane coupling agent.
• the invention also relates, per se, to a coupling system (inorganic filler / diene elastomer) for diene rubber composition reinforced with an inorganic filler, usable for the manufacture of tires, said system being constituted by the association of a polysulphurized alkoxysilane, a 1,2-dihydropyridine and a guanidine derivative.
• the invention also relates to the use of such a coupling system (inorganic filler / diene elastomer) in a rubber composition for tires.
• the invention also relates to the use in combination of a 1,2-dihydropyridine and a guanidine derivative, in a rubber composition reinforced with a filler inorganic, to activate the coupling function (inorganic filler / diene elastomer) of polysulphurized alkoxysilanes.
• the invention finally relates to a process for coupling an inorganic filler and a diene elastomer, in a rubber composition, this process being characterized in that there is incorporated in (i) at least one diene elastomer, at least: (ii ) an inorganic filler as a reinforcing filler; (iii) a polysulfurized alkoxysilane; (iv) a 1,2-dihydropyridine and (v) a guanidine derivative, and in that thermomechanically kneading the whole, in one or more stages, until reaching a maximum temperature of between 120 ° C and 190 ° C .
• the rubber compositions are characterized before and after curing, as follows.
• An oscillating consistometer is used as described in standard AFNOR-NFT-43005 (November 1980).
• the Mooney plasticity measurement is carried out according to the following principle: the composition in the raw state (i.e. before baking) is molded in a cylindrical enclosure heated to 100 ° C. After one minute of preheating, the rotor turns within the test tube at 2 revolutions / minute and the torque useful for maintaining this movement is measured after 4 minutes of rotation.
• the measurements are carried out at 130 ° C, in accordance with standard AFNOR-NFT-43004 (November 1980).
• the evolution of the consistometric index as a function of time makes it possible to determine the toasting time of the rubber compositions, assessed in accordance with the aforementioned standard by the parameter T5, expressed in minutes, and defined as being the time necessary to obtain an increase.
• the consistometric index (expressed in MU) of 5 units above the minimum value measured for this index.
• a processing of the traction records also makes it possible to plot the module curve as a function of the elongation (see attached figures), the module used here being the true secant module measured in first elongation, and calculated by reducing to the real section of the test tube, and not in the initial section as previously for the nominal modules.
• Hysteretic losses are measured by rebound at 60 ° C on the 6th shock, and expressed in% according to the following relationship (W Q : energy supplied; Wi: energy restored):
• the rubber compositions according to the invention are based on the following constituents: (i) one (at least one) diene elastomer (component A), (ii) one (at least one) inorganic filler as reinforcing filler (component B ), (iii) one (at least one) polysulfurized alkoxysilane (component C - abbreviated ASPS) as coupling agent (inorganic filler / diene elastomer) with which are associated, to activate coupling, (iv) one (at minus one) 1, 2-dihydropyridine (component D - abbreviated as 1,2-DHP) and (v) one (at least one) guanidine derivative (component E).
• composition based on
• a composition comprising the mixture and / or the in situ reaction product of the various constituents used, some of these constituents being capable of, or intended to react with each other , at least in part, during the various phases of manufacturing the composition, in particular during its vulcanization.
• the coupling system according to the invention consists of an ASPS coupling agent, preferably the majority (ie, more than 50% by weight) and a coupling activator formed by the association of a 1,2-DHP and a guanidine derivative.
• iene elastomer or rubber in known manner an elastomer derived at least in part (i.e. a homopolymer or a copolymer) from diene monomers (monomers carrying two carbon-carbon double bonds, conjugated or not).
• diene elastomer derived at least in part from conjugated diene monomers, having a content of units or units of diene origin (conjugated dienes) which is greater than 15% (% by moles).
• diene elastomers such as butyl rubbers or copolymers of dienes and alpha-olefins of the EPDM type do not enter into the preceding definition and can be qualified in particular as "essentially saturated diene elastomers". "(rate of motifs of diene origin low or very low, always less than 15%).
• the expression “highly unsaturated” diene elastomer is understood in particular to mean a diene elastomer having a content of units of diene origin (conjugated dienes) which is greater than 50%.
• 1,3-butadiene, 2-methyl-1,3-butadiene, 2,3-di (C 1 -C 5 alkyl) -1,3-butadienes such as, for example, 2 are suitable.
• Suitable vinyl-aromatic compounds are, for example, styrene, ortho-, meta-, para-methylstyrene, the commercial "vinyl-toluene" mixture, para-tertiobutylstyrene, methoxystyrenes, chlorostyrenes, vinyl mesitylene, divinylbenzene. , vinylnaphthalene.
• the copolymers can contain between 99% and 20% by weight of diene units and between 1% and 80% by weight of vinyl-aromatic units.
• the elastomers can have any microstructure which is a function of the polymerization conditions used, in particular the presence or absence of a modifying and / or randomizing agent and quantities of modifying and / or randomizing agent used.
• the elastomers can for example be block, statistical, sequence, microsequenced, and be prepared in dispersion or in solution; they can be coupled and / or stars or functionalized with a coupling and / or star-forming or functionalizing agent.
• polybutadienes and in particular those having a content of units -1,2 between 4% and 80% or those having a content of cis-1,4 greater than 80%, polyisoprenes, butadiene copolymers- styrene and in particular those having a styrene content of between 5% and 50% by weight and more particularly between 20% and 40%>, a content of -1,2 bonds in the butadiene part of between 4%> and 65% , a content of trans-1,4 bonds of between 20% and 80%, butadiene-isoprene copolymers and in particular those having an isoprene content of between 5% and 90% by weight and a glass transition temperature (Tg) from -40 ° C to -80 ° C, isoprene-styrene copolymers and in particular those having a styrene content of between 5% and 50% by weight and a Tg of between -25 ° C and -50 ° C.
• butadiene-styrene-isoprene copolymers are particularly suitable those having a styrene content between 5% and 50% by weight and more particularly between 10% and 40%, an isoprene content between 15% and 60% by weight and more particularly between 20% and 50%, a butadiene content between 5% and 50% by weight and more particularly between 20% and 40%), a content of units -1,2 of the butadiene part included between 4% and 85%, a content in trans units -1.4 of the butadiene part between 6% and 80%, a content in units -1.2 plus -3.4 of the isoprene part between 5% and 70% and a content of trans units -1.4 of the isoprenic part of between 10%> and 50%, and more generally any butadiene-styrene-isoprene copolymer having a Tg of between -20 ° C and -70 ° C.
• the diene elastomer of the composition in accordance with the invention is chosen from the group of highly unsaturated diene elastomers constituted by polybutadienes (BR), polyisoprenes (IR), natural rubber (NR) , butadiene copolymers, isoprene copolymers and mixtures of these elastomers.
• BR polybutadienes
• IR polyisoprenes
• NR natural rubber
• butadiene copolymers butadiene copolymers
• isoprene copolymers and mixtures of these elastomers.
• Such copolymers are more preferably chosen from the group consisting of butadiene-styrene copolymers (SBR), isoprene-butadiene copolymers (BIR), isoprene-styrene copolymers (SIR) and isoprene copolymers- butadiene-styrene (SBIR).
• SBR butadiene-styrene copolymers
• BIR isoprene-butadiene copolymers
• SIR isoprene-styrene copolymers
• SBIR isoprene copolymers- butadiene-styrene
• composition according to the invention is particularly intended for a tread for a tire, whether it is a new or used tire (retreading).
• component A is for example an SBR or a cut (mixture) SBR / BR, SBR / NR (or SBR / IR), or even BR / NR (or BR / IR) .
• SBR elastomer use is in particular of an SBR having a styrene content of between 20% and 30% by weight, a vinyl bond content of the butadiene part of between 15% and 65%, a bond content trans- 1,4 between 15% and 75% and a Tg between -20 ° C and -55 ° C.
• Such an SBR copolymer preferably prepared in solution, is optionally used in admixture with a polybutadiene (BR) preferably having more than 90% of cis-1,4 bonds.
• BR polybutadiene
• component A is for example chosen from the group consisting of natural rubber, synthetic polyisoprenes, isoprene copolymers (isoprene-butadiene, isoprene-styrene, butadiene-styrene-isoprene) and mixtures of these elastomers.
• component A can also consist, in whole or in part, of another highly unsaturated elastomer such as, for example, an SBR elastomer.
• the composition according to the invention may contain at least one essentially saturated diene elastomer, in particular at least one EPDM copolymer, that this copolymer is for example used or not in admixture with one or more of the highly unsaturated diene elastomers mentioned above.
• compositions of the invention may contain a single diene elastomer or a mixture of several diene elastomers, the diene elastomer (s) can be used in combination with any type of synthetic elastomer other than diene, or even with polymers other than elastomers, for example thermoplastic polymers.
• the white or inorganic filler used as reinforcing filler can constitute all or only part of the total reinforcing filler, in the latter case associated for example with carbon black.
• the reinforcing inorganic filler constitutes the majority, that is to say more than 50% by weight of the total reinforcing filler, more preferably more than 80%> by weight of this total reinforcing load.
• the term "reinforcing inorganic filler” is understood, in a known manner, an inorganic or mineral filler, whatever its color and its origin (natural or synthetic), also called “white” filler or sometimes “clear” filler "in contrast to carbon black, this inorganic filler being capable of reinforcing on its own, without other means than an intermediate coupling agent, a rubber composition intended for the manufacture of tires, in other words capable of replacing, in its reinforcing function, a conventional charge of pneumatic grade carbon black.
• the reinforcing inorganic filler is a mineral filler of the siliceous or aluminous type, or a mixture of these two types of filler.
• the silica (Si ⁇ 2) used can be any reinforcing silica known to those skilled in the art, in particular any precipitated or pyrogenic silica having a BET surface as well as a CTAB specific surface, both less than 450 m 2 / g, preferably 30 at 400 m 2 / g.
• High dispersible precipitated silicas are preferred, in particular when the invention is implemented for the manufacture of tires having low rolling resistance;
• highly dispersible silica is understood to mean, in known manner, any silica having a significant ability to disaggregate and to disperse in an elastomeric matrix, observable in known manner by electron or optical microscopy, on fine sections.
• BV3380 and Ultrasil 7000 silicas from Degussa Zeosil 1165 MP and 1115 MP silicas from Rhodia, Hi-Sil 2000 silica from PPG, Zeopol 8715 or 8745 silicas from the company Huber, treated precipitated silicas such as for example the silicas "doped" with aluminum described in application EP-A-0 735 088.
• the reinforcing alumina (AI2O3) preferably used is a highly dispersible alumina having a BET surface area ranging from 30 to 400 m 2 / g, more preferably between 60 and 250 m 2 / g, an average particle size at most equal to 500 nm , more preferably at most equal to 200 nm, as described in the above-mentioned application EP-A-0 810 258.
• Such reinforcing aluminas there may be mentioned in particular the aluminas A125 or CR125 (company Baikowski), APA-100RDX (company Condea), Aluminoxid C (company Degussa) or AKP-G015 (Sumitomo Chemicals).
• the invention can also be implemented using as reinforcing inorganic filler the specific aluminum (oxide-) hydroxides as described in application WO 99/28376.
• reinforcing inorganic filler is also understood to mean mixtures of different reinforcing inorganic fillers, in particular highly dispersible siliceous and / or aluminous fillers as described above.
• the reinforcing inorganic filler used in particular if it is silica, preferably has a BET surface area of between 60 and 250 m 2 / g , more preferably between 80 and 230 m 2 / g.
• the reinforcing inorganic filler can also be used in cutting (mixing) with carbon black.
• carbon blacks all carbon blacks are suitable, in particular blacks of the HAF, ISAF, SAF type, conventionally used in tires and particularly in the treads of these tires.
• blacks NI 15, N134, N234, N339, N347, N375 mention may be made of blacks NI 15, N134, N234, N339, N347, N375.
• the quantity of carbon black present in the total reinforcing filler can vary within wide limits, this quantity being preferably less than the quantity of inorganic reinforcing filler present in the rubber composition.
• the rate of total reinforcing filler is included in a range ranging from 20 to 300 phr, more preferably from 30 to 150 phr, even more preferably from 50 to 130 phr (parts by weight percent of elastomer), the optimum being different according to the nature of the reinforcing inorganic filler used and according to the intended applications: the level of reinforcement expected on a bicycle tire, for example, is in known manner significantly lower than that required on a tire capable of traveling at high speed in a sustained manner, for example a motorcycle tire, a tire for passenger vehicle or for commercial vehicle such as Heavy weights.
• the quantity of reinforcing inorganic filler is preferably within a range of 50 to 100 phr.
• the BET specific surface is determined in a known manner, according to the Brunauer-Emmett-Teller method described in "The Journal of the American Chemical Society", vol. 60, page 309, February 1938 and corresponding to standard AFNOR-NFT-45007 (November 1987); the CTAB specific surface is the external surface determined according to the same standard AFNOR-NFT-45007 of November 1987.
• the coupling agent used in the rubber compositions in accordance with the invention is an ASPS, carrying in a known manner two types of functions denoted here "Y” and "X”, which can be grafted on the one hand on the inorganic filler by means of the "Y” function (alkoxysilyl function) and on the other hand on the elastomer by means of the "X" function (sulfur function).
• ASPS are widely known to those skilled in the art as coupling agents (inorganic filler / diene elastomer) in rubber compositions intended for the manufacture of tires.
• polysulphurized alkoxysilanes called “symmetrical” or “asymmetrical” according to their particular structure, are used, as described in patents US-A-3,842,111, US-A-3,873,489, US-A-3,978,103 , US-A-3,997,581, US-A-4,002,594, US-A-4,072,701, US-A-4,129,585, or in more recent patents or patent applications US-A-5,580,919 , US-A-5 583 245, US-A-5 650 457, US-A-5 663 358, US-A-5 663 395, US-A-5 663 396, US-A-5 674 932, US -A-5 675 014, US-A-5 684 171, US-A-5 684 172, US-A-5 6
• - n is an integer from 2 to 8 (preferably from 2 to 5);
• - A is a divalent hydrocarbon radical
• radicals R 1 substituted or unsubstituted, identical or different from each other, represent a C ⁇ -C ⁇ 8 alkyl, C 5 -C 18 cycloalkyl or C 6 -C 18 aryl group ;
• the radical A substituted or unsubstituted, is preferably a divalent hydrocarbon radical, saturated or unsaturated, containing from 1 to 18 carbon atoms.
• the radicals R 1 are preferably C ⁇ -C 6 alkyl, cyclohexyl or phenyl groups, in particular C ⁇ ⁇ C alkyl groups, more particularly methyl and / or ethyl.
• the radicals R 2 are preferably C 1 -C 8 alkoxyl or C 5 -C 8 cycloalkoxyl groups, more particularly methoxyl and / or ethoxyl.
• the ASPS used is a polysulphide, in particular a disulphide or a tetrasulphide, of bis-alkoxyl (C ⁇ -C 4 ) silylalkyl (C ⁇ -C ⁇ o), more preferably still of bis (alkoxyl (C ⁇ -C 4 ) silylpropyl) , in particular bis (trialkoxyl (C ⁇ -C ⁇ 0 ) silylpropyle), in particular bis (3-triethoxysilylpropyle) or bis (3-trimethoxysilylpropyle).
• Bis (triethoxysilylpropyl) disulfide or TESPD of formula [(C2H5 ⁇ ) 3 Si (CH2) 3S] 2 , is marketed for example by the company Degussa under the names Si266 or Si75 (in the second case, in the form of a mixture of disulfide (at 75% by weight) and of polysulfide), or also by the company Witco under the name Silquest Al 589.
• Bis (triethoxysilylpropyl) or TESPT tetrasulfide of formula [(C2H5 ⁇ ) 3Si (CH2) 3S2] 2, is marketed for example by the company Degussa under the name Si69 (or X50S when it is supported at 50% by weight on carbon black), or also by the company Witco under the name Silquest Al 289 (in both case commercial mixture of polysulphides with an average value for n which is close to 4).
• TESPT Most preferably TESPT is used.
• an advantageous embodiment of the invention consists in using TESPD, which is certainly less active than TESPT when it is used alone, but whose effectiveness is appreciably improved by the presence of 1,2-DHP and of the derivative. guanidine.
• ASPS organosilane there may be mentioned, for example, an organosilane of the oligomeric or polymeric type, as described for example in applications WO96 / 10604 or DE-A-44 35 311 and corresponding to the formula below:
• the ASPS content is preferably between 0.5 and 15% by weight relative to the amount of reinforcing inorganic filler, that is, in the majority of cases, between 1 and 10 phr , more preferably between 3 and 8 pce. But it is generally desirable to use as little as possible.
• the presence of 1,2-DHP and guanidine derivative in these compositions advantageously makes it possible to be able to use the ASPS at a preferential rate of less than 10%, or even less than 8%> by weight relative to the amount of filler reinforcing inorganic; rates between 4 and 8% are thus advantageously possible.
• ASPS could be grafted beforehand (via the "X” function) on the diene elastomer of the composition of the invention, the elastomer thus functionalized or “precoupled” then comprising the free “Y” function for the reinforcing inorganic filler .
• ASPS could also be grafted beforehand (via the "Y” function) onto the reinforcing inorganic filler, the filler thus “precoupled” can then be linked to the diene elastomer via the free function "X".
• the coupling agent either grafted onto the reinforcing inorganic filler, or in the free state (ie, not grafted) just like the 1,2-DHP and the guanidine derivative associated with it in the coupling system according to the invention.
• the coupling system according to the invention consists of the ASPS coupling agent defined above and of a coupling activator of this alkoxysilane.
• coupling activator is meant here a body (a compound or a combination of compounds) which, mixed with the coupling agent, increases the effectiveness of the latter.
• the coupling activator used in accordance with the invention is formed by the association of a 1,2-DHP and a guanidine derivative.
• DHP component D Dihydropyridines
• 1,2-dihydropyridines here denoted “1,2-DHP”
• DHP have been mainly used until now as additives in adhesive compositions, stabilizing agents, polymerization activators or even vulcanization accelerators (see for example EP-A-0 334 377; EP-A-0 502 733; EP-A -0 794 219; EP-A-0 867 491; US-A-4 450 030; US-A-5 747 601).
• radicals R to R which are identical or different from each other, are preferably chosen from hydrogen, a hydrocarbon group, OH, CN, NH 2 , SH groups or halogens.
• radicals R to R are more preferably chosen from hydrogen and hydrocarbon groups preferably having from 1 to 20 carbon atoms, these groups being able to be linear, cyclic or branched, substituted or unsubstituted.
• hydrocarbon groups examples include - C 18 alkyls, C 3 -C 8 cycloalkyls, C -C 2 o arylalkyls, C 6 -Cjg aryls, C 7 alkylaryls -C 20 , alkenyls in C 2 -C ⁇ 8 , alkoxyls (OR) in Cis, groups SR, NR 2 , NHR, COR, COOR, COOH, CONR 2 , CONHR, CONH 2 , SiR 3 , Si (OR) 3 .
• the radicals R to R are chosen from hydrogen, C 1 -C 10 alkyls (in particular methyl, ethyl, propyl, butyl, pentyl, hexyl, octyl), C 3 -C 8 cycloalkyls (in particular cyclopentyl , cyclohexyl, cycloheptyl), C 7 -C 12 arylalkyls (in particular benzyl, phenyl-ethyl), C 6 -C ⁇ 2 aryls (in particular phenyl, naphthyl), C -C -C 4 alkylaryl (in particular toluyl, xylyl, ethyl-phenyl), C 2 -C 10 alkenyls (in particular propenyl, butenyl).
• two of these radicals R 3 to R 9 could be joined to form a ring in which a
• 1,2-DHP has been detailed in "Development in Dihydropyridine chemistry" by J. Kuthan and A. Kurfurst, Ind. Eng. Chem. Prod. Res. Dev., 1982, 21, pp. 191-261. They can be obtained from pyridine derivatives, for example by reduction of the corresponding pyridinium salts or by the Hantzsch process. They are also synthesized in a known manner by condensation, in the presence of a catalyst (for example an acid), a primary amine and an aldehyde in which the Carbon at ⁇ of the carbonyl function carries at least two hydrogen atoms; this reaction is described for example in Chem. Commun., 1971, 476, by H. Charman and J.
• a catalyst for example an acid
• radicals R 6 , R 8 and at least one of the radicals R 3 or R 4 represent hydrogen.
• Any primary amine, aliphatic or aromatic, having from 1 to 18 carbon atoms can be used, for example ethylamine, n-butylamine, n-pentylamine, cyclopentylamine, n-hexylamine, cyclohexylamine, n-octylamine, n-decylamine, n- dodecylamine, n-hexadecylamine, n-octadecylamine, aniline, toluyl or xylyl amines.
• aldehydes mention may be made of any C 2 -C 12 aldehyde (in particular acetaldehyde, propionaldehyde, n-butyraldehyde, pentanal, cyclopentanal, hexanal, cyclohexanal, n-heptanal, n-decanal, n-dodecanal).
• C 2 -C 12 aldehyde in particular acetaldehyde, propionaldehyde, n-butyraldehyde, pentanal, cyclopentanal, hexanal, cyclohexanal, n-heptanal, n-decanal, n-dodecanal.
• the 1,2-DHP used is an N-phenyl-1,2-dihydropyridine, that is to say that the radical R 9 is a phenyl radical, substituted or not substituted.
• the amine used is a phenylamine (substituted or unsubstituted phenyl radical), in particular aniline (unsubstituted phenyl).
• 1,2-DHP which can be used in the compositions of the invention
• 3,5-dipentyl-1,2-dihydro-1-phenyl-2-hexylpyridine available for example in the form a heptaldehyde-aniline condensate, corresponding to the formula (II-1) below:
• condensates (aldehyde / amine) which can be used in the compositions of the invention
• condensates (aldehyde / amine) will be chosen whose content or purity in 1, 2-DHP (%> by weight) is as high as possible, preferably greater than 50%, more preferably greater than 70%.
• condensation product of aniline and butyraldehyde which, after purification, consists mainly of 3,5-dieth ⁇ l-1,2-dihydro-1-phenyl-2-propylpyridine. formula (II-2) above; this product is marketed for example by the company R.T. Vanderbilt under the name Vanax 808 HP (purity in 1,2-DHP of at least 85%).
• the optimal content of 1,2-DHP will be chosen, first of all, according to the quantity of ASPS used.
• the amount of 1,2-DHP represents between 1% and 20%) by weight relative to the amount of ASPS; below the minimum rates indicated the effect is likely to be insufficient, while beyond the maximum rates indicated above, there is generally no longer any improvement in coupling while the costs of the composition increase and the on the other hand, there is a risk of being exposed to the risk of toasting.
• the amount of 1,2-DHP is more preferably between 3%> and 17.5% by weight relative to the amount of ASPS.
• the total amount of ASPS and of 1,2-DHP represents less than 10%, more preferably between 5% and 10% in weight relative to the amount of reinforcing inorganic filler. This corresponds in the majority of cases to a rate (ASPS + 1,2-DHP) of between 1 and 10 phr, more preferably between 4 and 9 phr.
• the second component required for activation of the coupling is a guanidine derivative, that is to say a substituted guanidine.
• guanidine derivatives that is to say a substituted guanidine.
• Substituted guanidines are well known to those skilled in the art, in particular as vulcanizing agents, and have been described in numerous documents (see for example "Vulcanization and vulcanizing agents" by W. Hofmann, Ed. MacLaren and Sons Ltd ( London), 1967, pp. 180-182; EP-A-0 683 203 or US-A-5 569 721).
• N, N'-diphenylguanidine (abbreviated to "DPG") corresponding to the particular formula (III-1) below:
• guanidine derivatives other than DPG in particular other aromatic guanidine derivatives corresponding to the general formula (III) below:
• Ar 1 and Ar 2 represent a substituted or unsubstituted aryl group, preferably a phenyl group, and R 10 represents a hydrogen or a hydrocarbon group.
• R 10 represents a hydrogen or a hydrocarbon group.
• TPG triphenylguanidine
• DPG di-o-tolylguanidine
• the amount of guanidine derivative preferably represents between 0.5%> and 4% relative to the weight of reinforcing inorganic filler, more preferably between 1% and 3%, or preferably between 0, 25 and 4 pce, more preferably between 0.5 and 2 pce.
• the activation effect may be insufficient, while beyond the indicated maximums, there is generally no longer any improvement in coupling, while exposing oneself to the risk of toasting.
• the coupling system constituted by the ASPS and the coupling activator (1,2-DHP + guanidine derivative) represents in total between 2% and 20%, more preferably between 5 % and 15%) by weight relative to the amount of reinforcing inorganic filler.
• this coupling system has proven to be sufficiently effective, for the needs of compositions intended for the manufacture of tires, in particular those intended for tire treads for passenger vehicles, for a rate of less than 12%. , or even less than 10% by weight relative to the amount of reinforcing inorganic filler.
• the level of coupling system according to the invention is preferably between 2 and 15 phr, more preferably between 5 and 10 phr.
• the rubber compositions in accordance with the invention also comprise all or part of the additives usually used in diene rubber compositions crosslinkable with sulfur and intended for the manufacture of tires, such as for example plasticizers, pigments, protection of the antioxidant, antiozonant type, a crosslinking system based either on sulfur or on sulfur and / or peroxide and / or bismaleimide donors, vulcanization accelerators, vulcanization activators, extension oils, etc. ..
• a conventional non-reinforcing white filler such as for example particles of clay, bentonite, talc, chalk, kaolin, titanium oxides.
• compositions in accordance with the invention may also contain, in addition to the ASPS, recovery agents (comprising, for example, the only function Y) of the reinforcing inorganic filler or more generally agents for assisting in the implementation which are likely to known, thanks to an improvement in the dispersion of the inorganic filler in the rubber matrix and to a lowering of the viscosity of the compositions, to improve their ability to be used in the raw state, these agents being for example alkylalkoxysilanes (in particular alkyltriethoxysilanes), polyols, polyethers (for example polyethylene glycols), primary, secondary or tertiary amines, hydroxylated or hydrolysable polyorganosiloxanes, for example ⁇ , ⁇ - dihydroxy-polyorganosiloxanes (in particular ⁇ , ⁇ -dihydroxy -polydimethylsiloxanes).
• recovery agents comprising, for example, the only function Y
• recovery agents
• compositions are produced in suitable mixers, in a manner known to those skilled in the art, typically using two successive preparation phases, one first phase of thermo-mechanical work at high temperature followed by a second phase of mechanical work at lower temperature, as described for example in applications EP-A-0 501 227, EP-A-0 810 258 or WO99 / 28376 cited above.
• the first thermomechanical working phase (sometimes called a "non-productive" phase) is intended to intimately mix, by kneading, the various ingredients of the composition, with the exception of the vulcanization system. It is carried out in a suitable kneading device such as an internal mixer or a extruder until, under the effect of mechanical work and the high shear imposed on the mixture, a maximum temperature of between 120 ° C. and 190 ° C. is reached. , preferably between 130 ° C and 180 ° C.
• This first phase can itself include one or more thermo-mechanical working steps, separated for example by one or more intermediate cooling steps.
• the various ingredients of the composition, elastomer (s), reinforcing filler and its coupling system, and the various other components (“additives”) can be incorporated into the mixer in one or more stages, either during the first thermo step. -mechanical, or in a staggered manner during the various thermomechanical stages, if applicable.
• thermo-mechanical work typically between 1 and 20 min, for example between 2 and 10 min
• the total duration of this thermo-mechanical work is chosen according to the particular operating conditions, in particular the maximum temperature chosen, the nature and the volume of the constituents , the important thing being that is obtained in the elastomeric matrix a good dispersion of the different ingredients which react with each other, thus allowing first a good implementation of the composition in the raw state, then a sufficient level of reinforcement, after cooking, by the reinforcing filler and its intermediate coupling system.
• this finishing phase consists of incorporating the vulcanization (or crosslinking) system by mixing it into a suitable device, for example a cylinder tool. It is carried out for an appropriate duration (typically between 1 and 30 min, for example between 2 and 5 min) and at a sufficiently low temperature (typically below 120 ° C, for example between 60 ° C and 100 ° C), in all cases below the vulcanization temperature of the mixture, so as to protect against premature vulcanization (roasting).
• a suitable device for example a cylinder tool. It is carried out for an appropriate duration (typically between 1 and 30 min, for example between 2 and 5 min) and at a sufficiently low temperature (typically below 120 ° C, for example between 60 ° C and 100 ° C), in all cases below the vulcanization temperature of the mixture, so as to protect against premature vulcanization (roasting).
• all the basic constituents of the compositions according to the invention namely (ii) the reinforcing inorganic filler and the coupling system according to the invention constituted by the combination of (iii) the ASPS, (iv) 1,2-DHP and (v) guanidine derivative, are incorporated into (i) the diene elastomer during the first so-called non-productive phase, that is to say that is to say that one introduces into the mixer and that one thermomechanically kneads, in one or more steps, at least these different basic constituents until a maximum temperature of between 120 ° C. and 190 ° C. is reached, preferably between 130 ° C and 180 ° C.
• the first (non-productive) phase is carried out in two successive stages lasting 1 to 5 minutes, in a conventional internal paddle mixer of the "Banbury" type. whose initial tank temperature is around 60 ° C.
• the elastomer (or elastomers) is first introduced then, after 1 minute for example of kneading, the reinforcing filler and its associated coupling system; mixing is continued then, for example 1 minute later, the various additives are added, including any additional covering or processing agents, with the exception of the vulcanization system (sulfur and primary accelerator of the sulfenamide type).
• the apparent density of the reinforcing filler (or of one of the reinforcing fillers if several are used) is relatively low (case for example of silicas), it may be preferable to fractionate the introduction of the latter, and the if necessary that of its coupling system, to facilitate its incorporation into the elastomeric matrix, for example half or even 3/4 of the load after the first minute of mixing, the rest after two minutes of mixing.
• the thermomechanical work is thus carried out until a maximum temperature known as "falling" is reached, for example between 150 ° C. and 170 ° C.
• the block of mixture thus obtained is recovered and cooled to a temperature below 100 ° C.
• thermomechanical step is carried out in the same or another mixer in order to subject the mixture to an additional heat treatment and in particular to obtain better dispersion of the reinforcing filler; of course, some of the additives such as, for example, stearic acid, anti-ozone wax, antioxidant, zinc oxide or other additive, may only be introduced into the mixer, in whole or in part, until during this second stage of thermo-mechanical work.
• the result of this first thermo-mechanical phase is then taken up on an external cylinder mixer, at low temperature (for example between 30 ° C. and 60 ° C.) and the vulcanization system is added; the whole is then mixed (productive phase) for a few minutes, for example between 2 and 5 minutes.
• the final composition thus obtained is then calendered, for example in the form of a sheet or a plate, in particular for characterization in the laboratory, or else extruded, to form for example a rubber profile used for the manufacture of semi-finished products. finishes such as treads, crown plies, sidewalls, carcass plies, heels, protectors, air chambers or internal rubber compounds for tubeless tires.
• Vulcanization (or baking) is carried out in a known manner at a temperature generally between 130 ° C and 200 ° C, under pressure, for a sufficient time which can vary for example between 5 and 90 min depending in particular on the baking temperature. , the crosslinking system adopted and the vulcanization kinetics of the composition considered.
• the invention relates to the rubber compositions described above both in the so-called “raw” state (ie, before baking) and in the so-called “cooked” or vulcanized state (ie, after crosslinking or vulcanization). .
• compositions according to the invention can be used alone or as a blend (ie, as a mixture) with any other rubber composition which can be used for the manufacture of tires.
• thermo-mechanical stages separated by a cooling phase, as follows: the mixture is introduced into an internal laboratory mixer (0.4 liters), of the "Banbury” type, filled to 70% and whose initial temperature of the tank is approximately 60 ° C, successively the elastomer (s), approximately one minute later 2/3 of the reinforcing inorganic filler and its associated coupling system, another minute later the rest of the reinforcing filler, its associated coupling system, as well as the various additives with the exception of the antioxidant, zinc oxide and the vulcanization system (sulfur and sulfenamide); a first thermomechanical working step is thus carried out for approximately 3 to 4 minutes until a maximum fall temperature of approximately 165 ° C is reached; the elastomeric block is then recovered and then cooled.
• thermomechanical work of a duration of 3 to 4 minutes also, with addition of zinc oxide and antioxidant, until reaching a maximum drop temperature of about 165 ° C.
• compositions thus obtained are then calendered either in the form of plates (thickness of 2 to 3 mm) or thin sheets of rubber for the measurement of their physical or mechanical properties, or in the form of profiles which can be used directly, after cutting and / or assembly to the desired dimensions, for example as semi-finished products for tires, in particular as treads.
• the reinforcing white filler (silica and / or alumina) constitutes the whole of the reinforcing filler, used at a preferential rate comprised within a range of 50 to 100 phr; but it goes without saying that, in these tests, a fraction of the latter, preferably a minority, could be replaced by carbon black.
• the SBR elastomer is prepared in solution and comprises 26.5% styrene, 59.5%) of 1-2 polybutadiene units and 23%) of 1-4 trans polybutadiene units; the BR elastomer comprises 93%> of 1-4 cis units.
• composition No. 1 TESPT (6.4 pce) with DPG but without 1,2-DHP
• composition No. 2 TESPT (6.4 pce) which is associated with 0.25 pce (or 3.9%) by weight relative to the amount of TESPT) of 1,2-DHP and 1.5 pce of DPG ( or about 1.9% by weight relative to the amount of reinforcing inorganic filler)
• TESPT (6.4 pce) which is associated with 0.5 pce (or 7.8%) relative to the amount of TESPT) of 1,2-DHP and 1.5 pce of DPG.
• component D As component D is used here the condensate (aniline-butyraldehyde) Vanax 808 HP sold by the company RT Vanderbilt, consisting mainly of 3,5-diethyl-1,2-dihydro-l-phenyl-2-propylpyridine of formula ( II-2) mentioned above (advertised content of 1,2-DHP of at least 85% by weight).
• Composition No. 1 is the witness for this test, it contains a rate of TESPT of 8% by weight relative to the amount of reinforcing inorganic filler (6.4 pce of TESPT for 80 pce of silica), but is devoid of 1,2-DHP.
• the total amount (ASPS + 1,2-DHP) represents less than 10%> (8.3% and 8.6% respectively) by weight relative to the amount of reinforcing inorganic filler; as for the coupling system according to the invention (TESPT + 1,2-DHP + DPG), it is advantageously present at a rate lower than 12% (respectively, 10.2% and 10.5% o) by weight by relative to this amount of reinforcing inorganic filler.
• Tables 1 and 2 show the formulation of the different compositions (Table 1 - rate of the different products expressed in pce), their properties before and after cooking (40 min at 150 ° C).
• Figure 1 reproduces meanwhile the modulus curves (in MPa) as a function of the elongation (in%); these curves are denoted Cl, C2 and C3 and correspond respectively to compositions No. 1, No. 2 and No. 3.
• modules with higher deformations Ml 00 and M300
• M300 / M100 ratio also higher (in a manner known to those skilled in the art, indicators of stronger reinforcement); significantly lower hysteretic losses (PH) (indicative of lower rolling resistance for treads); equivalent breaking stresses.
• FIG. 1 confirms the above results: for elongations of 100% and more, all the modulus values are clearly higher in the case of compositions No. 2 and No. 3 (curves C2 and C3); for such an elongation domain, such behavior clearly illustrates a better interaction between the reinforcing inorganic filler and the elastomer.
• all the results obtained after curing are representative of a better coupling between the reinforcing inorganic filler and the diene elastomer, in other words of an activation, by 1,2-DHP and the guanidine derivative combined, of the ASPS coupling function.
• composition No. 4 TESPT (6.4 pce) with DPG, but without 1,2-DHP
• composition No. 5 TESPT (4 pce) with DPG, but without 1, 2-DHP
• composition No. 6 TESPT (4 pce) plus 0.5 pce of 1,2-DHP (i.e. 12.5% by weight relative to the amount of TESPT) and 1.5 pce of DPG.
• composition No. 6 Only composition No. 6 is therefore in accordance with the invention; composition No. 4 is the reference composition of the prior art, composition No. 5 represents a control with an identical level of TESPT compared to composition No. 6.
• Tables 3 and 4 give the formulation of the different compositions, their properties before and after cooking (150 ° C, 40 min).
• Figure 2 shows the modulus curves (in MPa) as a function of the elongation (in%); these curves are denoted C4 to C6 and correspond respectively to compositions No. 4 to No. 6.
• the level of TESPT represents 8% by weight relative to the amount of silica, which is 60% higher than the level of TESPT used in composition No. 6 in accordance with l 'invention.
• the quantity of ASPS as well as the total quantity (ASPS + 1,2- DHP) represent less than 6% (respectively, 5% and 5.6%>) by weight compared to the quantity of reinforcing inorganic filler.
• the coupling system itself (ASPS + 1,2-DHP + DPG), it is present at a rate advantageously less than 10% o (precisely 7.5%>) by weight relative to this same quantity.
• composition No. 6 in accordance with the invention has, compared on the one hand to the reference composition No. 4, equivalent performance after cooking despite a significantly lower level of TESPT, and compared on the other hand to control composition No. 5 containing the same amount of TESPT but devoid of 1,2-DHP, performances which are generally superior:
• Figure 2 attached confirms the activation effect of the coupling provided by 1,2-DHP and DPG: it is clearly seen that the modulus values, for elongations of 100% and more, are substantially identical for the compositions N ° 4 and N ° 6 (curves C4 and C6 very close), clearly superior to those observed on the control composition N ° 5.
• the reduction in the silane level leads, in an expected manner, to an increase in the viscosity in the raw state, but the variations observed remain acceptable; in particular, a person skilled in the art will be able to correct, if necessary, the increase in viscosity in the raw state by the addition of a small amount of covering agent (see test 10 below).
• composition No. 7 TESPT (6.4 pce) (with guanidine derivative, but without 1,2-DHP); - composition No. 8: TESPD (5.6 pce) (with guanidine derivative, but without 1,2-DHP); composition No. 9: TESPD (5.6 phr) plus 0.5 phr of 1,2-DHP (ie 8.9% by weight relative to the amount of TESPD) and 1.5 phr of guanidine derivative.
• composition No. 7 is the witness for this test (8%> of TESPT relative to the weight of reinforcing inorganic filler); composition No. 8. also not in accordance with the invention, contains TESPD at an isomolar rate relative to the rate of TESPT, that is to say that for the two compositions N ° 7 and N ° 8 the same rate of reactive triethoxysilane functions is used with respect to silica and its surface hydroxyl groups.
• Composition No. 9 is the only composition in accordance with the invention; its ASPS rate represents less than 8% (precisely 7%>) by weight relative to the amount of silica (80 phr), the amount
• composition No. 8 compared with composition No. 7, exhibits reinforcement properties after baking (M100, M300 and ratio M300 / M100) which are clearly lower, less resistance to rupture, as well as losses. higher hysteretics: all this is due to the lower coupling efficiency (inorganic charge / elastomer) of the alkoxysilane disulfide (TESPD) compared to the alkoxysilane tetrasulfide (TESPT).
• TESPD alkoxysilane disulfide
• TESPT alkoxysilane tetrasulfide
• composition No. 10 TESPT (6.4 pce), with DPG (1.5 pce) but without 1,2-DHP; composition No. 11: TESPT (6.4 pce) with DPG (1.5 pce) plus 0.5 pce of 1,2-DHP (i.e. 7.8%) by weight relative to the amount of TESPT).
• composition No. 10 is the witness for this test, it contains a rate of TESPT of 8%> by weight relative to the amount of reinforcing inorganic filler (6.4 pce of TESPT for 80 pce of silica), but is devoid of of 1,2- DHP.
• composition No. 10 contains a rate of TESPT of 8%> by weight relative to the amount of reinforcing inorganic filler (6.4 pce of TESPT for 80 pce of silica), but is devoid of of 1,2- DHP.
• the amount of alkoxysilane and of 1,2-DHP represents less than 10%> (precisely 8.6%) by weight relative to the amount of reinforcing inorganic filler ; as for the coupling system according to the invention (TESPT + 1,2-DHP + DPG), it is advantageously present at a rate of less than 12% (precisely 10.5%) by weight relative to the amount of inorganic filler reinforcing.
• Tables 7 and 8 give the formulation of the various compositions (Table 7 - rate of the various products expressed in pce), their properties before and after cooking (40 min at 150 ° C).
• Figure 4 reproduces the module curves (in MPa) as a function of the elongation (in%); these curves are denoted CIO and Ci l and correspond respectively to compositions No. 10 and No. 11.
• modules with higher deformations M100 and M300
• ratio M300 / M100 also higher (indicators of stronger reinforcement); lower hysteretic losses (PH); equivalent breaking stress.
• FIG. 4 appended confirms the above results: for elongations of 100%) and more, all the modulus values are greater in the case of the composition according to the invention (compare curves Ci 1 and CIO); for such an elongation range, such behavior clearly illustrates a better interaction between the reinforcing inorganic filler and the elastomer, thanks to the coupling system according to the invention.
• E Trial 5
• Three rubber compositions comprising, as reinforcing inorganic filler, a mixture (50/50) of silica and alumina; the alumina is a reinforcing alumina as described in the above-mentioned application EP-A-0 810 258.
• compositions are identical except for the following differences:
• composition No. 12 TESPT with DPG but without 1,2-DHP
• composition No. 13 TESPT activated by 1, 2-DHP and DPG
• - composition No. 14 TESPT activated by 1,2-DHP and DPG.
• Composition No. 12 is the test control, it contains an ASPS rate of less than 8% (precisely 6.6%) relative to the weight of inorganic filler (6.5 pce of TESPT compared to 99 pce dump).
• Compositions No. 13 and No. 14, in accordance with the invention, comprise the coupling system in accordance with the invention (ASPS + 1,2-DHP + DPG) at a rate which is also advantageously less than 8 % (precisely 7.9%) relative to the weight of total reinforcing inorganic filler.
• Tables 9 and 10 give the formulation of the different compositions and their properties before and after cooking (40 min at 150 ° C).
• FIG. 5 reproduces the module curves as a function of the elongation (curves denoted C12 to C14 and corresponding respectively to compositions No. 12 to No. 14).
• composition No. 15 TESPT with DPG but without 1,2-DHP
• composition No. 16 TESPT activated by 1, 2-DHP and DPG.
• composition No. 15 is the test witness.
• the total amount of the coupling system (TESPT + 1,2-DHP + DPG) is advantageously less than 8%> (precisely 7.5%) by weight relative to the amount inorganic charge.
• Tables 11 and 12 give the formulation of the compositions and their properties before and after cooking (40 min at 150 ° C.).
• FIG. 6 reproduces the module curves as a function of the elongation (denoted Cl 5 and Cl 6).
• composition of the invention compared with the control, has in the raw state an almost identical viscosity, a reduced but satisfactory roasting time, and in the cooked state properties indicative of better coupling: modules M100, M300, higher M300 / M100 ratio, significantly reduced PH losses.
• FIG. 6 confirms these results, with a curve C16 situated clearly above the control curve Cl 5.
• compositions tested are identical except for the following differences:
• composition No. 17 TESPT with DPG but without 1,2-DHP
• composition No. 18 TESPT with 1, 2-DHP but without guanidine derivative
• composition No. 19 TESPT with DPG and 1,2-DHP
• - composition No. 20 TESPT with DOTG and 1, 2-DHP. Only compositions No. 19 and No. 20 are therefore in accordance with the invention; Composition No. 17 is the control according to the prior art. Tables 13 and 14 give the formulation and properties of these compositions before and after baking (40 min at 150 ° C).
• FIG. 7 reproduces the module curves as a function of the elongation (denoted Cl 7 to C20 and corresponding respectively to compositions No. 17 to No. 20).
• compositions of the invention compared to control composition No. 17, exhibit significantly improved properties in the baked state: M100, M300 modules and M300 / M100 ratio clearly superior, very PH values. significantly reduced, as many clear indicators of an improved coupling, as is confirmed by FIG. 7: curves C19 and C20 located clearly above the control curve C17.
• composition No. 18 devoid of guanidine derivative, these properties appear overall degraded compared to those of the compositions of the invention, both in the raw state and after cooking (markedly higher viscosity; higher PH losses; lower M300 / M100 ratio; curve C18 slightly below curve C17).
• compositions tested are identical except for the following differences:
• composition No. 21 TESPD (5.6 phr) with DPG but without 1,2-DHP
• composition No. 22 TESPD (3.5 phr) with DPG but without 1,2-DHP
• composition N ° 23 TESPD (3.5 pce) with DPG (1.5 pce) and 1,2-DHP (0.5 pce or
• Composition No. 21 is the reference of the prior art; it is noted that its ASPS level is very clearly (60%) higher than the ASPS level of the composition according to invention No. 23.
• the total amount (TESPD + 1,2-DHP) represents less than 6% (precisely 5%>) by weight relative to the amount of silica.
• the coupling system itself (ASPS + 1,2-DHP + DPG), it is advantageously present at a rate of less than 8%> (precisely 6.9%) by weight relative to this same quantity.
• Tables 15 and 16 give the formulation of the different compositions, their properties before and after cooking (150 ° C, 40 min).
• FIG. 8 reproduces the modulus / elongation curves (curves denoted C21 to C23 and corresponding respectively to compositions No. 21 to No. 23).
• the results show that the composition N ° 23 according to the invention has, compared to the reference composition N ° 21, equivalent performances after cooking despite a significantly lower rate of TESPD: modules M100, M300, ratio M300 / M100, properties at break as well as substantially identical PH losses.
• the control composition No. 22 containing the same level of TESPD as the composition of the invention it shows performances clearly degraded in the absence of 1,2-DHP.
• FIG. 8 confirms these results well, the composition of the invention (curve C23) having modulus values slightly higher than those of reference composition No. 21 (curve C21), far beyond those of the control composition No. 22 lacking 1,2-DHP.
• the invention is implemented with an ASPS other than the symmetrical ASPS used in the previous tests, in this case an ASPS of the polymeric type.
• composition No. 24 ASPS with DPG but without 1, 2-DHP
• composition No. 25 ASPS activated by 1, 2-DHP and DPG.
• composition No. 24 is the witness for this test;
• composition No. 25, in accordance with the invention comprises the coupling system according to the invention (ASPS + 1,2-DHP + guanidine derivative) at a preferential rate of less than 12% (precisely 10.5%) relative to by weight of inorganic filler.
• Tables 17 and 18 give the formulation of the two compositions, their properties before and after cooking (40 min at 150 ° C).
• Figure 9 shows the module / elongation curves (noted C24 and C25).
• composition according to the invention compared to the control composition, exhibits substantially identical properties before cooking and improved properties after cooking: modules with strong deformations M100 and M300, higher M300 / M100 ratio (indicators of a higher reinforcement), lower PH losses (therefore better).
• FIG. 9 confirms these results, with, for elongations of 100%) and more, much higher modulus values for the composition of the invention (curve C24). All this clearly illustrates a better interaction between the inorganic load and the elastomer.
• the hydroxylated polyorganosiloxane in particular an ⁇ , ⁇ -dihydroxy-polyorganosiloxane, is then combined with the ASPS, as covering agent. teaching of patent application EP-A-0 784 072.
• composition No. 26 TESPT (6.4 pce) with DPG but without 1,2-DHP; - composition No. 27: TESPT (4 pce), with DPG but without 1,2-DHP; composition No. 28: TESPT (4 pce) activated by DPG and 1, 2-DHP; compositions No. 29 to No. 31: identical to composition No. 28 but also comprising variable rates (0.5 to 2.4 pce) of different collectors
• composition No. 26 is the reference of the prior art
• composition No. 27 represents a control with an identical level of TESPT compared to the compositions according to the invention No. 28 to No. 31.
• Tables 19 and 20 give the formulation of the different compositions, their properties before and after cooking (150 ° C, 40 min).
• the recovery agents were incorporated into the compositions according to the invention at the same time as the ASPS (non-productive step).
• the total amount of coupling system (TESPT + 1,2-DHP + DPG) advantageously represents less than 8% (precisely 7.5%) compared to by weight of inorganic filler.
• the invention is illustrated here by rolling tests of tires with a radial carcass of dimension 175/70 RI 4, manufactured in known manner and which are identical in all respects except for the constitution of the rubber composition constituting the tread.
• the compositions tested are identical to compositions N ° 26, N ° 28 and N ° 31 of the previous test, except that they also contain a small proportion (6 phr) of carbon black (N234), used essentially as coloring agent and anti-UV, and that they were prepared, for the needs of these tests in pneumatics, in suitable mixers of greater capacity.
• the tires thus prepared are subjected to rolling on the road, on a Citro ⁇ n Xsara brand vehicle, until the wear due to rolling reaches the wear indicators arranged in the grooves of the treads.
• the wear resistance of the rubber composition is directly correlated with the quality of the reinforcement provided by the reinforcing filler, that is to say at the coupling rate (filler / elastomer) obtained.
• the measurement of the resistance to wear is an excellent indicator, if not the best since evaluated on the final manufactured product, of the performance of the coupling system used.
• composition No. 31 incorporating the polyorganosiloxane covering agent, also offered the advantage of easier industrial processing (reduced plasticity in the raw state) compared with composition No. 28.
• the invention therefore makes it possible to have tire treads having very good wear resistance combined with low rolling resistance, even in the presence of a very significantly reduced rate of ASPS (in particular TESPT).
• ASPS in particular TESPT.
• all the previous results illustrate an improved coupling between the reinforcing inorganic filler and the diene elastomer when both 1,2-DHP and the guanidine derivative are used in combination with ASPS.
• these results are representative of an activation, by 1,2-DHP and the guanidine derivative combined, of the coupling function fulfilled by the ASPS.
• a reduction in the rate of ASPS also has the advantage, from an environmental point of view (release VOC - "Volatile Organic Compounds"), of leading to a reduction in the alcohol levels (ethanol in the presence of TESPT) emitted during the manufacture of rubber compositions, or during the firing of rubber articles incorporating these compositions.
• the invention also makes it possible, if a high rate of ASPS is kept, to obtain a higher level of coupling, and therefore to achieve an even better reinforcement of the rubber compositions by the reinforcing inorganic filler.
• the new coupling system inorganic filler / diene elastomer in accordance with the invention thus offers the compositions of the invention a compromise of advantageous properties compared to the compositions of the prior art reinforced with an inorganic filler.
• Tg -29 ° C; 75 pce dry SBR extended with 13.5 pce of aromatic oil (a total of 88.5 pce);

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Compositions Of Macromolecular Compounds (AREA)

Priority Applications (10)

Applications Claiming Priority (2)

Related Child Applications (1)

Publications (1)

Family

ID=8846981

Family Applications (1)

Country Status (13)

Cited By (4)

Families Citing this family (56)

Citations (2)

Family Cites Families (41)

• 2000
  • 2000-01-24 FR FR0001809A patent/FR2804121A1/fr active Pending
• 2001
  • 2001-01-22 CA CA002397989A patent/CA2397989A1/fr not_active Abandoned
  • 2001-01-22 DE DE60101324T patent/DE60101324T2/de not_active Expired - Lifetime
  • 2001-01-22 EP EP01901187A patent/EP1268649B1/fr not_active Expired - Lifetime
  • 2001-01-22 JP JP2001561098A patent/JP4860874B2/ja not_active Expired - Fee Related
  • 2001-01-22 CN CNB018040403A patent/CN1257212C/zh not_active Expired - Fee Related
  • 2001-01-22 AU AU2001226803A patent/AU2001226803A1/en not_active Abandoned
  • 2001-01-22 KR KR1020027009503A patent/KR20020069369A/ko not_active Withdrawn
  • 2001-01-22 AT AT01901187T patent/ATE255142T1/de not_active IP Right Cessation
  • 2001-01-22 BR BR0107848-8A patent/BR0107848A/pt not_active Application Discontinuation
  • 2001-01-22 WO PCT/EP2001/000661 patent/WO2001055252A1/fr not_active Ceased
  • 2001-01-22 MX MXPA02007177A patent/MXPA02007177A/es active IP Right Grant
• 2002
  • 2002-07-23 US US10/201,531 patent/US6984689B2/en not_active Expired - Fee Related