WO1998017855A1 - Bahnförmiges halbzeug, nämlich putztapete und verfahren zu dessen herstellung - Google Patents
Bahnförmiges halbzeug, nämlich putztapete und verfahren zu dessen herstellung Download PDFInfo
- Publication number
- WO1998017855A1 WO1998017855A1 PCT/EP1997/005864 EP9705864W WO9817855A1 WO 1998017855 A1 WO1998017855 A1 WO 1998017855A1 EP 9705864 W EP9705864 W EP 9705864W WO 9817855 A1 WO9817855 A1 WO 9817855A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mortar
- mineral
- finished product
- layer
- semi
- Prior art date
Abstract
Description
Claims