US20150174799A1 - Molding method of resin molded product and resin molded product - Google Patents

Molding method of resin molded product and resin molded product Download PDF

Info

Publication number
US20150174799A1
US20150174799A1 US14/130,003 US201214130003A US2015174799A1 US 20150174799 A1 US20150174799 A1 US 20150174799A1 US 201214130003 A US201214130003 A US 201214130003A US 2015174799 A1 US2015174799 A1 US 2015174799A1
Authority
US
United States
Prior art keywords
resin
core member
molded product
resin sheets
sheets
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/130,003
Other languages
English (en)
Inventor
Takehiko Sumi
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kyoraku Co Ltd
Original Assignee
Kyoraku Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kyoraku Co Ltd filed Critical Kyoraku Co Ltd
Assigned to KYORAKU CO., LTD. reassignment KYORAKU CO., LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: SUMI, TAKEHIKO
Publication of US20150174799A1 publication Critical patent/US20150174799A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/001—Combinations of extrusion moulding with other shaping operations
    • B29C48/0017—Combinations of extrusion moulding with other shaping operations combined with blow-moulding or thermoforming
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C44/00—Shaping by internal pressure generated in the material, e.g. swelling or foaming ; Producing porous or cellular expanded plastics articles
    • B29C44/02—Shaping by internal pressure generated in the material, e.g. swelling or foaming ; Producing porous or cellular expanded plastics articles for articles of definite length, i.e. discrete articles
    • B29C44/12—Incorporating or moulding on preformed parts, e.g. inserts or reinforcements
    • B29C44/1228—Joining preformed parts by the expanding material
    • B29C44/1233—Joining preformed parts by the expanding material the preformed parts being supported during expanding
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/001—Combinations of extrusion moulding with other shaping operations
    • B29C48/0021—Combinations of extrusion moulding with other shaping operations combined with joining, lining or laminating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/25—Component parts, details or accessories; Auxiliary operations
    • B29C48/30—Extrusion nozzles or dies
    • B29C48/305—Extrusion nozzles or dies having a wide opening, e.g. for forming sheets
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C49/00—Blow-moulding, i.e. blowing a preform or parison to a desired shape within a mould; Apparatus therefor
    • B29C49/20—Blow-moulding, i.e. blowing a preform or parison to a desired shape within a mould; Apparatus therefor of articles having inserts or reinforcements ; Handling of inserts or reinforcements
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C51/00—Shaping by thermoforming, i.e. shaping sheets or sheet like preforms after heating, e.g. shaping sheets in matched moulds or by deep-drawing; Apparatus therefor
    • B29C51/10—Forming by pressure difference, e.g. vacuum
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C51/00—Shaping by thermoforming, i.e. shaping sheets or sheet like preforms after heating, e.g. shaping sheets in matched moulds or by deep-drawing; Apparatus therefor
    • B29C51/12—Shaping by thermoforming, i.e. shaping sheets or sheet like preforms after heating, e.g. shaping sheets in matched moulds or by deep-drawing; Apparatus therefor of articles having inserts or reinforcements
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C51/00—Shaping by thermoforming, i.e. shaping sheets or sheet like preforms after heating, e.g. shaping sheets in matched moulds or by deep-drawing; Apparatus therefor
    • B29C51/26—Component parts, details or accessories; Auxiliary operations
    • B29C51/266—Auxiliary operations after the thermoforming operation
    • B29C51/267—Two sheets being thermoformed in separate mould parts and joined together while still in the mould
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/18—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by features of a layer of foamed material
    • B32B5/20—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by features of a layer of foamed material foamed in situ
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C49/00—Blow-moulding, i.e. blowing a preform or parison to a desired shape within a mould; Apparatus therefor
    • B29C49/20—Blow-moulding, i.e. blowing a preform or parison to a desired shape within a mould; Apparatus therefor of articles having inserts or reinforcements ; Handling of inserts or reinforcements
    • B29C2049/2008—Blow-moulding, i.e. blowing a preform or parison to a desired shape within a mould; Apparatus therefor of articles having inserts or reinforcements ; Handling of inserts or reinforcements inside the article
    • B29C2049/2013—Blow-moulding, i.e. blowing a preform or parison to a desired shape within a mould; Apparatus therefor of articles having inserts or reinforcements ; Handling of inserts or reinforcements inside the article for connecting opposite walls, e.g. baffles in a fuel tank
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C2948/00—Indexing scheme relating to extrusion moulding
    • B29C2948/92—Measuring, controlling or regulating
    • B29C2948/92504—Controlled parameter
    • B29C2948/92561—Time, e.g. start, termination, duration or interruption
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
    • B29C48/03—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor characterised by the shape of the extruded material at extrusion
    • B29C48/07—Flat, e.g. panels
    • B29C48/08—Flat, e.g. panels flexible, e.g. films
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C51/00—Shaping by thermoforming, i.e. shaping sheets or sheet like preforms after heating, e.g. shaping sheets in matched moulds or by deep-drawing; Apparatus therefor
    • B29C51/26—Component parts, details or accessories; Auxiliary operations
    • B29C51/261—Handling means, e.g. transfer means, feeding means
    • B29C51/262—Clamping means for the sheets, e.g. clamping frames
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C65/00—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor
    • B29C65/02—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor by heating, with or without pressure
    • B29C65/022—Particular heating or welding methods not otherwise provided for
    • B29C65/028—Particular heating or welding methods not otherwise provided for making use of inherent heat, i.e. the heat for the joining comes from the moulding process of one of the parts to be joined
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C65/00—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor
    • B29C65/74—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor by welding and severing, or by joining and severing, the severing being performed in the area to be joined, next to the area to be joined, in the joint area or next to the joint area
    • B29C65/743—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor by welding and severing, or by joining and severing, the severing being performed in the area to be joined, next to the area to be joined, in the joint area or next to the joint area using the same tool for both joining and severing, said tool being monobloc or formed by several parts mounted together and forming a monobloc
    • B29C65/7441—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor by welding and severing, or by joining and severing, the severing being performed in the area to be joined, next to the area to be joined, in the joint area or next to the joint area using the same tool for both joining and severing, said tool being monobloc or formed by several parts mounted together and forming a monobloc for making welds and cuts of other than simple rectilinear form
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C66/00—General aspects of processes or apparatus for joining preformed parts
    • B29C66/01—General aspects dealing with the joint area or with the area to be joined
    • B29C66/05—Particular design of joint configurations
    • B29C66/10—Particular design of joint configurations particular design of the joint cross-sections
    • B29C66/11—Joint cross-sections comprising a single joint-segment, i.e. one of the parts to be joined comprising a single joint-segment in the joint cross-section
    • B29C66/112—Single lapped joints
    • B29C66/1122—Single lap to lap joints, i.e. overlap joints
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C66/00—General aspects of processes or apparatus for joining preformed parts
    • B29C66/01—General aspects dealing with the joint area or with the area to be joined
    • B29C66/05—Particular design of joint configurations
    • B29C66/10—Particular design of joint configurations particular design of the joint cross-sections
    • B29C66/11—Joint cross-sections comprising a single joint-segment, i.e. one of the parts to be joined comprising a single joint-segment in the joint cross-section
    • B29C66/114—Single butt joints
    • B29C66/1142—Single butt to butt joints
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C66/00—General aspects of processes or apparatus for joining preformed parts
    • B29C66/40—General aspects of joining substantially flat articles, e.g. plates, sheets or web-like materials; Making flat seams in tubular or hollow articles; Joining single elements to substantially flat surfaces
    • B29C66/41—Joining substantially flat articles ; Making flat seams in tubular or hollow articles
    • B29C66/43—Joining a relatively small portion of the surface of said articles
    • B29C66/433—Casing-in, i.e. enclosing an element between two sheets by an outlined seam
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C66/00—General aspects of processes or apparatus for joining preformed parts
    • B29C66/70—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material
    • B29C66/72—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the structure of the material of the parts to be joined
    • B29C66/721—Fibre-reinforced materials
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C66/00—General aspects of processes or apparatus for joining preformed parts
    • B29C66/70—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material
    • B29C66/72—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the structure of the material of the parts to be joined
    • B29C66/727—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the structure of the material of the parts to be joined being porous, e.g. foam
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C66/00—General aspects of processes or apparatus for joining preformed parts
    • B29C66/80—General aspects of machine operations or constructions and parts thereof
    • B29C66/81—General aspects of the pressing elements, i.e. the elements applying pressure on the parts to be joined in the area to be joined, e.g. the welding jaws or clamps
    • B29C66/814—General aspects of the pressing elements, i.e. the elements applying pressure on the parts to be joined in the area to be joined, e.g. the welding jaws or clamps characterised by the design of the pressing elements, e.g. of the welding jaws or clamps
    • B29C66/8141—General aspects of the pressing elements, i.e. the elements applying pressure on the parts to be joined in the area to be joined, e.g. the welding jaws or clamps characterised by the design of the pressing elements, e.g. of the welding jaws or clamps characterised by the surface geometry of the part of the pressing elements, e.g. welding jaws or clamps, coming into contact with the parts to be joined
    • B29C66/81427—General aspects of the pressing elements, i.e. the elements applying pressure on the parts to be joined in the area to be joined, e.g. the welding jaws or clamps characterised by the design of the pressing elements, e.g. of the welding jaws or clamps characterised by the surface geometry of the part of the pressing elements, e.g. welding jaws or clamps, coming into contact with the parts to be joined comprising a single ridge, e.g. for making a weakening line; comprising a single tooth
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C66/00—General aspects of processes or apparatus for joining preformed parts
    • B29C66/80—General aspects of machine operations or constructions and parts thereof
    • B29C66/81—General aspects of the pressing elements, i.e. the elements applying pressure on the parts to be joined in the area to be joined, e.g. the welding jaws or clamps
    • B29C66/814—General aspects of the pressing elements, i.e. the elements applying pressure on the parts to be joined in the area to be joined, e.g. the welding jaws or clamps characterised by the design of the pressing elements, e.g. of the welding jaws or clamps
    • B29C66/8141—General aspects of the pressing elements, i.e. the elements applying pressure on the parts to be joined in the area to be joined, e.g. the welding jaws or clamps characterised by the design of the pressing elements, e.g. of the welding jaws or clamps characterised by the surface geometry of the part of the pressing elements, e.g. welding jaws or clamps, coming into contact with the parts to be joined
    • B29C66/81431—General aspects of the pressing elements, i.e. the elements applying pressure on the parts to be joined in the area to be joined, e.g. the welding jaws or clamps characterised by the design of the pressing elements, e.g. of the welding jaws or clamps characterised by the surface geometry of the part of the pressing elements, e.g. welding jaws or clamps, coming into contact with the parts to be joined comprising a single cavity, e.g. a groove
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2025/00—Use of polymers of vinyl-aromatic compounds or derivatives thereof as moulding material
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2025/00—Use of polymers of vinyl-aromatic compounds or derivatives thereof as moulding material
    • B29K2025/04—Polymers of styrene
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
    • B29L2009/00—Layered products
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2250/00—Layers arrangement
    • B32B2250/03—3 layers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2250/00—Layers arrangement
    • B32B2250/24—All layers being polymeric
    • B32B2250/246—All polymers belonging to those covered by groups B32B27/32 and B32B27/30
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2451/00—Decorative or ornamental articles
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/249921—Web or sheet containing structurally defined element or component
    • Y10T428/249953—Composite having voids in a component [e.g., porous, cellular, etc.]

Definitions

  • the present invention relates to a resin molded product in which a core member including a foaming element is interposed between at least two resin sheets into a laminated product.
  • patent document 1 WO2009/157197
  • patent document 2 Japanese Patent Laid-Open Ser. No. 2011-51224
  • patent document 3 Japanese Patent Laid-Open Ser. No. 2011-51227
  • the reinforcing core member is welded onto the sheet-shaped parisons formed in a contour along cavities of the split molds; hence, the sheet-shaped parisons are cooled by the split molds and are easily hardened, and the welding strength between the reinforcing core member and the sheet-shaped parisons is lowered depending on cases.
  • patent document 4 Japanese Patent Laid-Open Ser. No. 2008-222208 discloses a core board obtained by monoblock-pressing a laminated structure in which a first fibrous substrate, a thermoplastic foam core layer, and a second fibrous substrate are laminated in this order.
  • the fibrous substrate includes entangled nonwoven fabric including a fibrous material and a resin binder, and the melting point of the resin element constituting the thermoplastic foam core layer is higher than that of the resin binder.
  • PATENT DOCUMENT 2 Japanese Patent Laid-Open Ser. No. 2011-51224
  • PATENT DOCUMENT 3 Japanese Patent Laid-Open Ser. No. 2011-51227
  • PATENT DOCUMENT 4 Japanese Patent Laid-Open Ser. No. 2008-222208
  • thermoplastic foam core layer on assumption that the contour of the thermoplastic foam core layer is stably retained even during the heating in the monoblock press, the surface of the thermoplastic foam core layer is not melted.
  • the present invention has been made in consideration of the situation above and aims at providing a molding method of a resin molded product and a resin molded product in which it is possible to increase the welding strength between the core member and the resin sheets.
  • the present invention has the following aspects.
  • the molding method of a resin molded product in accordance with the present invention is
  • a molding method of a resin molded product in which a core member including a foaming element is interposed between at least two resin sheets in a melted state into a laminated product characterized in that:
  • the resin sheets comprise fibrous filler, the method comprising:
  • a molding step in which the core member and the resin sheets are clamped by a metallic mold, to mold the resin molded product.
  • the resin molded product in accordance with the present invention is
  • a resin molded product in which a core member including a foaming element is interposed between at least two resin sheets into a laminated product, characterized in that:
  • the resin sheets comprise fibrous filler
  • the resin molded product comprises a laminated structure in which the core member with melted surfaces and the resin sheets in a melted state are welded onto each other into one block.
  • the resin sheets in the melted state include the fibrous filler, it is possible to suppress the draw-down; hence, the molding can be conducted by extruding the resin sheets at a high temperature and it is possible to more securely melt the surfaces of the core member to weld the core member onto the resin sheets. As a result, the welding strength between the core member and the resin sheets can be improved. Also, by making the resin sheets in the melted state include the fibrous filler, it is possible to enhance rigidity of the molded product.
  • FIG. 1 is a diagram showing a configuration example of a resin molded product 100 of the present embodying mode.
  • FIG. 2 is a diagram showing a general configuration example of a molding device 60 to mold the resin molded product 100 of the present embodying mode.
  • FIG. 3 is a diagram showing a state in which a flask member 128 is brought into contact with a resin sheet P.
  • FIG. 4 is a diagram showing a state in which the resin sheet P is brought into contact with a split mold 32 .
  • FIG. 5 is a diagram showing a state in which one of the resin sheets P is formed in a contour.
  • FIG. 6 is a diagram showing a state in which a core member 102 is welded onto one of the resin sheets P.
  • FIG. 7 is a diagram showing a state in which the other one of the resin sheets P is formed in a contour.
  • FIG. 8 is a diagram showing a state in which the split mold 32 is clamped.
  • FIG. 9 is a diagram showing a state in which the split mold 32 is unclamped.
  • FIG. 10 is diagram showing a relationship example among thickness A of the resin sheets P, thickness B of the core member 102 , and depth C of the split mold 32 in a situation in which the resin sheets P and the core member 102 are compressed by the split mold 32 .
  • FIG. 1 shows a configuration example of an embodying mode of the resin molded product 100 in accordance with the present invention
  • FIGS. 2 , 6 , and 8 show a molding method example of the embodying mode of the resin molded product 100 in accordance with the present invention.
  • the resin molded product 100 in accordance with the present invention is, as shown in FIG. 1 , a resin molded product 100 in which a core member 102 including a foaming element is interposed between at least two resin sheets 101 into a laminated product.
  • the resin sheets 101 configuring the resin molded product 100 in accordance with the present invention contain fibrous filler.
  • the molding is conducted by use of, for example, a molding device 60 shown in FIG. 2 ; as shown in FIGS. 6 and 8 , while melting the surfaces of the core member 102 by heat of the resin sheets P, the core member 102 and the resin sheets P are welded onto each other. Also, as shown in FIG. 8 , the core member 102 and the resin sheets P are clamped by the mold 32 , to mold the resin molded product 100 .
  • the resin sheets P in the melted state contain fibrous filler, it is possible to suppress the draw-down.
  • This makes it possible to conduct the molding by extruding the resin sheets P at a high temperature, and it is possible to more securely melt the surfaces of the core member 102 to weld the core member 102 and the resin sheets P onto each other.
  • the welding strength between the core member 102 and the resin sheets P can be improved.
  • FIG. 1 is a diagram showing a configuration example of the resin molded product 100 of the present embodying mode.
  • the resin molded product 100 of the present embodying mode may be employed, for example, for a deck board of a car.
  • the resin molded product 100 of the present embodying mode includes lamination in which a core member 102 including a foaming element is interposed between the resin sheets 101 .
  • the core member 102 including a foaming element configures the inner side of the resin molded product 100 and includes styrene-based resin as its main component (at least 30 wt % or more). By configuring it using styrene-based resin as the main component, it is possible to enhance rigidity in a high-temperature environment (for example, 90° C. or more).
  • styrene-based resins acrylonitrile-styrene copolymer (AS), acrylonitrile-butadiene-styrene copolymer (ABS), polystyrene (PS), and anti-shock polystyrene (HIPS) may be considered.
  • an item obtained through the molding in which resin beads including a foaming agent are filled in a mold and are heated to foam and an item molded by foam extrusion may be employed.
  • heat-resistive foaming polystyrene-based beads for example, Kanepearl (registered trademark) and Heatmax (registered trademark) made by Kaneka Inc.
  • low-foaming molding heat-resistive foaming polystyrene-based beads for example, Kanepearl (registered trademark) and Heatmax (registered trademark) HM5 made by Kaneka Inc.
  • foaming heat-resistive AS-based resin for example, Heatpole (registered trademark) made by JSP Inc.
  • the core member 102 employed as the car deck board preferably has, from a point of view of decrease in weight, a foaming rate of 15 times or more. Also, it favorably has a heat resistive property, specifically, a dimensional change ratio of ⁇ 0.5% in 168 hours at 80° C.
  • the monomer composition configuring the resin beads favorably includes ⁇ -methyl styrene at 10 wt % or more and 80 wt % or less, acrylonitrile at 5 wt % or more and 50 wt % or less, and styrene-based monomer at 85 wt % or less; more favorably, ⁇ -methyl styrene at 10 wt % or more and 50 wt % or less, acrylonitrile at 5 wt % or more and 35 wt % or less, and styrene-based monomer at 80 wt % or less.
  • the core member 102 is highly heat resistive and is suitably used for the car deck board.
  • the styrene-based monomers there may be considered styrene, and various substituted styrene such as chlorstyrene, para-methyl styrene, and t-butyl styrene.
  • the resin beads used for the core member 102 may contain a fire retardant agent.
  • a fire retardant agent which develops the fire retardant property and which does not deteriorate the heat resistive property and the foaming property, it is favorable that the fire retardant agent has a decomposition temperature of 210° C. or more, and more favorably, the melting point of the fire retardant agent is 80° C. or more.
  • halogen-based fire retardant agent can be considered; specifically, hexabrom cyclododecan, tetrabrom bisphenol A, diallyl ether, and monochlor penthabrom cyclohexane can be considered; among these, hexabrom cyclododecan is favorable.
  • the dose of the fire retardant agent favorably ranges from 1 wt % to 15 wt % in the resin beads, more favorably, 3 wt % to 10 wt % therein.
  • the fire retardant assistant agent employed for such purpose a radical generating agent such as peroxide is used in general; however, as a favorable fire retardant assistant agent to develop the fire retardant property in the present embodying mode, a fire retardant assistant agent having a half-life temperature per hour of 150° C. or more and 250° C. or less is favorable.
  • the resin sheet 101 configures the outer side of the resin molded product 100 and, in the resin sheet 101 , like in the core member 102 , styrene-based resin is contained at least 30 wt % or more.
  • the core member 102 and the resin sheet 101 contain styrene-based resin at least 30 wt % or more; hence, it is possible to enhance rigidity in a high-temperature environment (for example, 90° C. or more).
  • the resin sheet 101 of the present embodying mode includes fibrous filler. Since the resin sheet 101 of the present embodying mode includes fibrous filler, it is possible to enhance rigidity.
  • the fibrous filler there can be considered Warastonite, potassium titanate whiskers, glass fiber, carbon fiber, and the like; particularly, glass fiber and carbon fiber are favorable.
  • the value (aspect ratio) obtained by dividing the length of fiber by the diameter of fiber favorably ranges from 250 to 2000; in particular, from 500 to 1200 from the viewpoint of appropriate molding and improvement of rigidity.
  • the length of fiber ranges from 8 mm to 20 mm and the diameter of fiber is equal to or less than 30 ⁇ m. This is because when the fiber length is less than 8 mm, the improvement due to filler mixing is small for the heat resistive property and for the rigidity at a high temperature; and when the fiber length is more than 20 mm, the filler is not easily mixed with the substrate resin.
  • fibrous filler with the fiber length from 10 mm to 20 mm and the fiber diameter from about 14 ⁇ m to about 17 ⁇ m is contained in a range from 20 wt % to 40 wt % (more favorably, about 30 wt %) in the resin sheet 101 .
  • the melting point of the styrene-based resin used for the resin sheet 101 is favorably higher than that of the styrene-based resin used for the core member 102 . This makes it possible that while melting the surfaces of the core member 102 by the heat of the resin sheet 101 in the melted state, the core member 102 and the resin sheet 101 are welded onto each other.
  • FIG. 2 shows a configuration example of a molding device 60 to mold the resin molded product 100 of the present embodying mode
  • FIGS. 2 to 9 show a molding process example to mold the resin molded product 100 of the present embodying mode.
  • the molding device 60 of the present embodying mode includes an extruding machine 12 , a clamping machine 14 , and a core member inserting machine (not shown).
  • the molding device 60 of the present embodying mode two resin sheets P in a melted state are extruded from the extruding machine 12 to arrange the two resin sheets P between the split molds 32 configuring the clamping machine 14 .
  • one of the resin sheets P is formed in a contour along a cavity 116 of the split mold 32 , and onto the one resin sheet P thus formed, a core member 102 beforehand molded is welded by the core member inserting machine (not shown).
  • the other one resin sheet P is formed in a contour along a cavity 116 of the split mold 32 , and the split mold 32 is clamped to weld the core member 102 onto the other one resin sheet P, and the resin sheets P are welded onto each other, to mold a resin molded product 100 in which the core member 102 and the other one resin sheet P are configured in one block.
  • the extruding machine 12 includes a cylinder 18 equipped with a hopper 16 , a screw (not shown) disposed in the cylinder 18 , an electric motor 20 coupled with the screw, an accumulator 22 communicatively connected to the cylinder 18 , a plunger 24 communicatively connected to the accumulator 22 , and a T die 28 .
  • the resin sheet P extruded from the extruding slit of the T die 28 is clamped by a pair of rollers 30 disposed with a gap therebetween and is delivered downward to be suspended between the split molds 32 .
  • the resin sheet P is arranged between the split molds 32 in a state in which the sheet P has uniform thickness in the perpendicular direction (extruding direction).
  • Extruding performance of the extruding machine 12 is appropriately selected in consideration of the size of the resin molded product to be molded and the prevention of occurrence of the draw-down or the neck-in of the resin sheet P.
  • the extruding quantity of one shot in the intermittent extrusion favorably ranges from 1 kg to 10 kg
  • the extruding speed of the resin sheet P from the extruding slit is several hundreds of kg/h or more; or, more preferably, 700 kg/h or more.
  • the extrusion of the resin sheet P is favorably as short as possible; although depending on the kind of resin, the MFR value, and the melt tension value, it is favorable in general that the extrusion is completed within 40 seconds; or, more preferably, in a range from 10 seconds to 20 seconds.
  • the extruding quantity per unitary area (1 cm 2 ) and unitary time (h) of the thermoplastic resin from the extruding slit is 50 kg/h cm 2 or more; or, more preferably, 150 kg/h cm 2 or more.
  • thermoplastic resin having a density of 0.9 g/cm 3 it is regarded that the thermoplastic resin having a weight of 1.8 kg is extruded per one shot in 15 seconds, to obtain through calculation that the extruding speed is 432 kg/h and the extruding speed per unitary area is about 86 kg/h cm 2 .
  • the extruding slit disposed in the T die 28 is arranged downward in a perpendicular direction, and the resin sheet P extruded from the extruding slit is perpendicularly transported downward in a state in which it suspends directly from the extruding slit.
  • the extruding slit by changing the slit gap, it is possible to change thickness of the resin sheet P.
  • the resin sheet P extruded from the T die 28 is favorably adjusted such that in a state in which it is suspended between the split molds 32 , that is, when it is clamped, thickness thereof in the extruding direction is uniform. In this situation, it is also possible to change the slit gap such that the slit gap is gradually enlarged beginning at the extrusion start point to be maximum at the extrusion end point.
  • the thickness of the resin sheet P extruded from the T die 28 is gradually enlarged beginning at the extrusion start point; however, the resin sheet P extruded in the melted state is extended by its own weight to be gradually thinner from the lower end to the upper end of the sheet; hence, the thick portion extruded by enlarging the slit gap cancels the thin portion due to extension by the draw-down phenomenon, to thereby conduct the adjustment for the uniform thickness from the upper end to the lower end of the sheet.
  • a resin sheet P pinched between a pair of rollers 30 is downward fed by the rotations of the pair of rollers 30 , to extend and to thin down the resin sheet P; by adjusting the relationship between the extruding speed of the resin sheet P extruded from the T die 28 and the feeding speed of the resin sheet P fed by the pair of rollers 30 , it is possible to prevent occurrence of the draw-down or the neck-in of the resin sheet P. Hence, it is possible to mitigate restrictions on the kind of resin to be adopted, in particular, on the MFR value, the MT value, and the extruding quantity per unitary time.
  • the pair of rollers 30 are arranged to have axial symmetry with respect to the resin sheet P extruded in a state in which it downward suspends from the extruding slit.
  • the diameter of the rollers 30 and the length in the axial direction of the rollers 30 are appropriately set according to the extruding speed of the resin sheet P to be molded, the length in the extruding direction of the resin sheet P, the width thereof, the kind of resin, and the like. Further, in respective outer surfaces of the pair of rollers 30 , there are disposed wrinkles in the contour of depressions and projections.
  • the wrinkles in the contour of depressions and projections are favorably disposed in the outer surfaces of the rollers 30 , to be uniformly distributed throughout the surfaces to be brought into contact with the resin sheet P, and the depth and the density thereof are only to be appropriately determined so that the resin sheet P is smoothly fed downward by the pair of rollers 30 , in consideration of prevention of occurrence of slippage between the respective outer surfaces of the pair of rollers 30 and the corresponding surfaces of the resin sheet P.
  • it is possible to form the wrinkles in the contour of depressions and projections for example, by the sand-blast process, it is favorable to form them by a blast machine by adopting a coarse level of about coarse 60 .
  • the wrinkles in the contour of depressions and projections disposed respectively in the pair of rollers 30 are not disposed to transcribe the wrinkle pattern onto the surfaces of the resin sheet P, but, intrinsically, are disposed to prevent occurrence of slippage between the respective outer surfaces of the pair of rollers 30 and the corresponding surfaces of the resin sheet P.
  • one of the pair of rollers is a wrinkle roll and the other one thereof is a lubber roll; however, in the pair of rollers 30 of the present embodying mode, by disposing wrinkles in the outer surfaces respectively of the pair of rollers 30 , the pair of rollers 30 respectively and securely hold the corresponding surfaces of the resin sheet P; on the other hand, by restricting the pushing force onto the resin sheet P due to the pair of rollers 30 , it is possible to prevent, immediately after feeding the resin sheet P by the pair of rollers 30 , the transcription of the wrinkle pattern onto the surfaces of the resin sheet P.
  • the pair of rollers 30 are made of metal, for example, aluminum; each of the paired rollers 30 is equipped with surface temperature adjusting means to adjust, depending on the temperature of the resin sheet P in the melted state, the surface temperature of the roller 30 ; in the configuration thereof, by flowing coolant through the inside of the roller 30 and by circulating the coolant, heat exchange is performed such that the surface of the roller 30 is not excessively heated by the resin sheet P in the melted state clamped by the pair of rollers 30 .
  • the outer surfaces of the pair of rollers 30 are heated through heat conduction when the pair of rollers 30 are brought into contact with the resin sheet P in the melted state; by cooling the outer surfaces of the pair of rollers 30 from the inside, an event is prevented in which the resin sheet P in the melted state clamped by the pair of rollers 30 adheres onto the outer surface of the roller 30 and is wound around the roller 30 by the rotations of the roller 30 , and the resin sheet P is not fed downward.
  • the surface temperature of the rollers 30 it is favorable to lower the surface temperature of the rollers 30 ; however, from the viewpoint of the molding of the resin sheet P later, when the surface temperature of the rollers 30 is too low, the resin sheet P in the melted state is contrarily cooled too much by the surfaces of the rollers 30 , to cause hindrances in the molding.
  • the predetermined range of temperature is determined according to the kind of the resin sheet P in the melted state.
  • the clamping machine 14 of the present embodying mode includes the split molds 32 and a mold driving machine (not shown) to move the split molds 32 in a direction substantially vertical to the supply direction of the resin sheets P between an open position and a closed position.
  • the split molds 32 are arranged in a state in which the cavities 116 oppose each other, and the respective cavities 116 face substantially the perpendicular direction.
  • depressions and projections are disposed according to the outer contour and the surface contour of the molded product to be molded based on the resin sheets P in the melted state.
  • pinch-off sections 118 are formed in the peripheries of the cavities 116 of the split molds 32 .
  • the pinch-off sections 118 are formed in a circular contour in peripheries of the cavities 116 and project toward the opposing split molds 32 .
  • flask members 33 are arranged between the split molds 32 .
  • the flask members 33 include openings 130 ; by use of flask member driving machines, not shown, the flask members 33 are moved toward the resin sheets P, and the flask members 33 are brought into contact with the resin sheets P, to hold the resin sheets P. Also, in the state in which the resin sheets P are kept held, the flask members 33 moves in the reverse direction, to bring the resin sheets P into contact with the tip ends of the pinch-off sections 118 of the split molds 32 ; and a sealed space is formed by the sheets of resin P, the pinch-off sections 118 , and the cavities 116 .
  • the split molds 32 are driven by the mold driving machine (not shown) so that the resin sheets P in the melted state are arranged between the split molds 32 at the open position. Further, at the closed position, the pinch-off sections 118 of the split molds 32 make contact with each other, to form a sealed space in the split molds 32 . Incidentally, for the movement of each split mold 32 from the open position to the closed position, the closed position is the position of the central line of the resin sheets P in the melted state; each split mold 32 is driven by the mold driving machine and moves toward the position.
  • the resin sheets P includes styrene-based resin as the main component.
  • styrene-based resin as the main component.
  • styrene-based resin employed for the resin sheets P a styrene-based resin which has MFR (measured at a test temperature of 230° C. and with a test load of 2.16 kg according to JIS K-7210) equal to or less than 3.5 g/10 min at 230° C. is applicable.
  • MFR measured at a test temperature of 230° C. and with a test load of 2.16 kg according to JIS K-7210
  • the resin sheets P of the present embodying mode include fibrous filler in order to possess the heat resistive property and rigidity.
  • fibrous filler in order to possess the heat resistive property and rigidity.
  • the draw-down is conspicuous and the molding is difficult; however, when the fibrous filler is contained in the resin sheets P, it is possible to suppress the influence of the draw-down.
  • the surfaces of the core member 102 are melted by the heat of the resin sheets P; hence, it is favorable that when the resin sheets P are extruded from the T dies 28 , the temperature of the resin sheets P is 210° C. or more, and more preferably, 250° C. or more.
  • the resin sheets P of the present embodying mode include fibrous filler.
  • the resin sheets P of the present embodying mode from the viewpoint of the reduction in thickness and the improvement in rigidity, it is also possible to further add powder inorganic filler such as silica, mica, talc, calcium carbonate, and the like.
  • powder inorganic filler such as silica, mica, talc, calcium carbonate, and the like.
  • the quantity of added inorganic filler is increased, roughness appears on the surface of the molded product, and pinholes easily take place.
  • plasticizers such as plasticizers, stabilizers, coloring agents, antistatic agents, fire retardants, foaming agents, and the like.
  • the resin sheets P are extruded from the T dies 28 , and the extruded resin sheets P are fed through a pair of rollers 30 to adjust thickness of the resin sheets P and then are suspended between the pair of split molds 32 .
  • the relative speed difference between the extruding speed of the resin sheets P and the feed speed at which the resin sheets P are fed downward by the pair of rollers 30 is adjusted by the rotation speed of the pair of rollers 30 such that when the resin sheets P pass between the pair of rollers 30 , they are drawn downward by the pair of rollers 30 and are extended to be reduced in thickness; as a result, occurrence of the draw-down or the neck-in is prevented.
  • each of the pair of rollers 30 coolant is circulated through the roller 30 to cool the roller 30 , to set the temperature of the outer surface of each roller 30 to be lower in a predetermined temperature range than the temperature of the resin sheet P in a melted state, to prevent the event in which when the resin sheet P in a melted state is clamped by the pair of rollers 30 , the resin sheet P in a melted state adheres onto the surface the roller 30 and is wound around the roller 30 by the rotations of the roller 30 ; on the other hand, the resin sheet P is kept in a melted state suitable for the molding.
  • the extruding slit gap adjustment may also be carried out.
  • flask members 128 are moved by a flask member driving machine (not shown) toward the corresponding sheets of resin P, and as shown in FIG. 3 , the flask members 128 are brought into contact with the sheets of resin P, to hold the sheets of resin P by the flask members 128 .
  • the flask members 128 are moved toward the split molds 32 , and as shown in FIG. 4 , the sheets of resin P are brought into contact with the pinch-off sections 118 of the split molds 32 , to form a sealed space 117 by the sheets of resin P, the pinch-off sections 118 , and the cavities 116 . Further, the core member 102 held by adsorbing plates 119 of a manipulator (not shown) is inserted between the split molds 32 as shown in FIG. 4 .
  • the air in the sealed space 117 is sucked via the split molds 32 to push one of the sheets of resin P onto the cavity 116 , to form, as shown in FIG. 5 , the one sheet of resin P in a contour according to the cavity 116 .
  • the manipulator is moved toward the split mold 32 on the right side, to push, as shown in FIG. 6 , the core member 102 onto the one resin sheet P adsorbed onto the cavity 116 of the split mold 32 on the right side, to weld the core member 102 onto the one resin sheet P.
  • the resin sheet P of the present embodying mode includes styrene-based resin and fibrous filler; hence, even after the resin sheet P is formed in the contour of the cavity 116 , it is possible to retain the state of temperature to melt the surfaces of the core member 102 . Hence, when the core member 102 is pushed onto the resin sheet P, the surfaces of the core member 102 can be melted by the heat of the resin sheet P. As a result, in the present embodying mode, while melting the surfaces of the core member 102 by the heat of the resin sheet P, the core member 102 can be welded onto the resin sheet P.
  • the adsorbing plates 119 are removed from the core member 102 and the manipulator is pulled to be removed from the space between the two split molds 32 , and the other one resin sheet P is pushed onto the cavity 116 , to form, as shown in FIG. 7 , the other one resin sheet P in the contour along the cavity 116 .
  • the two split molds 32 are clamped by the mold driving machine, and as shown in FIG. 8 , the core member 102 is pushed onto the other one resin sheet P adsorbed onto the cavity 116 of the split mold 32 on the left side, to weld the core member 102 onto the other one resin sheet P. Moreover, peripheries respectively of the two resin sheets P are welded onto each other to form parting lines PL.
  • the surfaces of the core member 102 of the present embodying mode are melted by the heat of the resin sheets P; hence, when the split molds 32 are clamped to mold a resin molded product 100 in which the core member 102 and the resin sheets P are formed in one block, it is favorable to compress the core member 102 and the resin sheets P by the split molds 32 . As a result, the welding strength between the core member 102 and the resin sheets P is further enhanced.
  • the fibrous filler contained in the resin sheets P is easily pushed into the core member 102 ; hence, it is possible that the welding between the resin sheets P and the core member 102 is stronger and it is possible to mold the resin molded product 100 with high rigidity.
  • it is favorable that the compression is performed in a range from about 0.5 mm to about 1.0 mm by each of the split molds 32 .
  • the two split molds 32 are unclamped and the cavities 116 are removed from the completed resin molded product 100 , and then burrs formed in peripheries of the parting lines PL are removed. This completes the molding of the resin molded product 100 .
  • the resin sheets 101 configuring the resin molded product 100 of the present embodying mode contain fibrous filler. And when molding the resin molded product 100 , while melting, as shown in FIGS. 6 and 8 , the surfaces of the core member 102 by the heat of the resin sheets P in the melted state, the core member 102 and the resin sheets P are welded onto each other. And as shown in FIG. 8 , the core member 102 and the resin sheets P are clamped by the split molds 32 , to mold the resin molded product 100 .
  • the resin sheets P in the melted state contain fibrous filler, it is possible to suppress draw-down. This makes it possible that the molding is conducted by extruding the resin sheets P at high temperature and the surfaces of the core member 102 are more securely melted, to weld the core member 102 and the resin sheets P onto each other. As a result, the welding strength between the core member 102 and the resin sheets P can be improved. Also, by making the resin sheets P contain fibrous filler, it is possible to enhance rigidity of the resin molded product 100 .
  • the core member 102 and the resin sheets P configuring the resin molded product 100 of the present embodying mode include styrene-based resin as the primary component, it is possible to further enhance the welding strength between the core member 102 and the resin sheets P and the rigidity of the resin molded product 100 .
  • the embodying modes described above are favorable embodying modes of the present invention, and the scope of the present invention is not limited only to these embodying modes, but various changes may be made therein without departing from the gist of the present invention.
  • the sheets of resin P are brought into contact with the pinch-off sections 118 of the split molds 32 , to form a sealed space 117 by the sheets of resin P, the pinch-off sections 118 , and the cavities 116 , and then the core member 102 is inserted between the split molds 32 .
  • the core member 102 is beforehand inserted between the split molds 32 . This makes it possible to warm up the surfaces of the core member 102 by the heat of the sheets of resin P extruded from the T dies 28 .
  • the core member 102 is sequentially welded onto the two resin sheets P.
  • the core member 102 is sequentially welded onto the two resin sheets P. Specifically, first, one of the resin sheets P is arranged in the split molds 32 , to form the resin sheet P in a contour along the cavity of the split mold 32 , and then the core member 102 is welded onto the resin sheet P.
  • the other one of the resin sheets P is arranged in the split molds 32 , to form the resin sheet P in a contour along the cavity of the split mold 32 , and then the core member 102 is welded onto the resin sheet P.
  • the core member 102 is welded onto the resin sheets P extruded from the T dies 28 ; hence, the surfaces of the core member 102 can be easily melted by the heat of the resin sheets P.
  • the core member 102 is welded onto the resin sheets P while melting the surfaces of the core member 102 by the heat of the resin sheets P.
  • the surfaces of the core member 102 are warmed up in advance by warming means before the core member 102 is pushed onto the one resin sheet P adsorbed onto the cavity 116 of the split mold 32 on the right side and the core member 102 is welded onto the one resin sheet P.
  • the surfaces of the core member 102 are warmed up by warming means before the core member 102 is pushed onto the other one resin sheet P adsorbed onto the cavity 116 of the split mold 32 on the left side and the core member 102 is welded onto the other one resin sheet P.
  • timing to warm up the surfaces of the core member 102 by warming means is not particularly restricted; only if the timing is before the resin sheets P and the core member 102 are welded onto each other, it is possible to warm up the surfaces of the core member 102 at any timing.
  • a decorative sheet is arranged between the split molds 32 such that the decorative sheet is welded onto the resin sheets P by clamping the split molds 32 .
  • a decorative sheet is supplied together with the resin sheets P to a space between a pair of rollers 30 such that by adjusting the rotation speed of the pair of rollers 30 , thickness of the resin sheets P is adjusted and the decorative sheet is pushed to be tightly fixed onto the resin sheets P.
  • the resin molded product 100 of the embodying mode described above is molded by interposing the core member 102 between two resin sheets P.
  • the resin molded product 100 of the embodying mode is molded by interposing the core member 102 between at least two resin sheets P; for example, it is also possible to mold the product by interposing the core member 102 by four resin sheets P.
  • the layer configuration of the resin molded product 100 in this situation is as resin sheet/resin sheet/core member/resin sheet/resin sheet.

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Blow-Moulding Or Thermoforming Of Plastics Or The Like (AREA)
  • Laminated Bodies (AREA)
  • Casting Or Compression Moulding Of Plastics Or The Like (AREA)
  • Extrusion Moulding Of Plastics Or The Like (AREA)
US14/130,003 2011-07-14 2012-06-28 Molding method of resin molded product and resin molded product Abandoned US20150174799A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2011-156086 2011-07-14
JP2011156086A JP6173657B2 (ja) 2011-07-14 2011-07-14 樹脂成形品の成形方法
PCT/JP2012/066489 WO2013008633A1 (ja) 2011-07-14 2012-06-28 樹脂成形品の成形方法及び樹脂成形品

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2012/066489 A-371-Of-International WO2013008633A1 (ja) 2011-07-14 2012-06-28 樹脂成形品の成形方法及び樹脂成形品

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US15/221,667 Division US10668652B2 (en) 2011-07-14 2016-07-28 Molding method of resin molded product and resin molded product

Publications (1)

Publication Number Publication Date
US20150174799A1 true US20150174799A1 (en) 2015-06-25

Family

ID=47505930

Family Applications (2)

Application Number Title Priority Date Filing Date
US14/130,003 Abandoned US20150174799A1 (en) 2011-07-14 2012-06-28 Molding method of resin molded product and resin molded product
US15/221,667 Active 2033-02-07 US10668652B2 (en) 2011-07-14 2016-07-28 Molding method of resin molded product and resin molded product

Family Applications After (1)

Application Number Title Priority Date Filing Date
US15/221,667 Active 2033-02-07 US10668652B2 (en) 2011-07-14 2016-07-28 Molding method of resin molded product and resin molded product

Country Status (6)

Country Link
US (2) US20150174799A1 (ja)
EP (1) EP2732953B1 (ja)
JP (1) JP6173657B2 (ja)
KR (1) KR101578593B1 (ja)
CN (1) CN103635302B (ja)
WO (1) WO2013008633A1 (ja)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140291880A1 (en) * 2013-03-29 2014-10-02 Toyota Boshoku Kabushiki Kaisha Manufacturing method for conveyance seat
US20160243751A1 (en) * 2013-11-01 2016-08-25 Toyota Jidosha Kabushiki Kaisha Method of manufacturing resin molded product and manufacturing device thereof
US20180147754A1 (en) * 2016-11-28 2018-05-31 Tzu-Chi LIN Uniform temperature roll-extrusion forming system and uniform temperature roller structure thereof
US11110500B2 (en) 2016-11-28 2021-09-07 Tzu-Chi LIN Uniform temperature roller system having uniform heat exchange by supercritical fluid
US11529754B2 (en) 2017-03-31 2022-12-20 Jsp Corporation Skin material-coated foamed particle molded body
WO2023006536A1 (fr) * 2021-07-30 2023-02-02 Safran Seats Procédé de fabrication d'une pièce de siège d'avion
US12128602B2 (en) 2021-07-30 2024-10-29 Safran Seats Method for manufacturing an aircraft seat part

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105531097A (zh) * 2013-09-11 2016-04-27 凯孚尔有限公司 借助于热成型设备或接合设备制造产品的方法，以及热成型设备或接合设备
JP6464670B2 (ja) * 2014-10-30 2019-02-06 キョーラク株式会社 サイドレール及びサイドレールの製造方法
JP6551966B2 (ja) * 2014-12-26 2019-07-31 キョーラク株式会社 サンドイッチパネルおよびサンドイッチパネルの成形方法
JP6614432B2 (ja) * 2015-06-10 2019-12-04 キョーラク株式会社 成形品の製造方法
BR112018003668A2 (pt) * 2015-09-17 2018-09-25 Honda Motor Co Ltd método de moldagem de resina e dispositivo de moldagem de resina
JP6152214B1 (ja) * 2016-03-31 2017-06-21 株式会社精工技研 加飾樹脂成形品
JP6933806B2 (ja) * 2017-09-29 2021-09-08 キョーラク株式会社 樹脂成形体の製造方法
CN111512255B (zh) 2017-07-20 2023-08-29 X趋势人工智能公司 多设备机器人控制
CN110497634A (zh) * 2018-05-17 2019-11-26 沛恩集团(控股)股份有限公司 冰桶制备方法
JP7397284B2 (ja) * 2019-09-20 2023-12-13 キョーラク株式会社 パレット及び製造方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5725940A (en) * 1992-10-27 1998-03-10 Mitsui Toatsu Chemicals, Inc. Composite molded article and method for making same
US6358599B1 (en) * 1999-04-30 2002-03-19 The Dow Chemical Company Alkenyl aromatic polymer foam laminates
US20060141260A1 (en) * 2004-12-29 2006-06-29 Enamul Haque Sandwich composite material using an air-laid process and wet glass
US20070256379A1 (en) * 2006-05-08 2007-11-08 Edwards Christopher M Composite panels

Family Cites Families (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4920881A (en) * 1988-05-02 1990-05-01 Webquip Corporation Method of cooling hot webs
US4980382A (en) * 1989-12-29 1990-12-25 Arco Chemical Technology, Inc. Process for the preparation of expandable vinyl aromatic polymer particles containing hexabromocyclododecane
AU668470B2 (en) * 1993-07-12 1996-05-02 Seaward International, Inc. Elongated structural member and method and apparatus for making same
JPH09225990A (ja) * 1996-02-27 1997-09-02 Mitsubishi Heavy Ind Ltd 押出成形用ダイ
JP4440426B2 (ja) * 2000-05-11 2010-03-24 しげる工業株式会社 成形品及びその製造方法
US6705853B1 (en) * 2000-10-20 2004-03-16 Durakon Industries, Inc. Six station rotary thermoforming machine
JP2004306459A (ja) * 2003-04-08 2004-11-04 Kyowa Sangyo Kk 車両用サンバイザのバイザ本体の製造方法
JP2005125736A (ja) * 2003-09-30 2005-05-19 Kanto Auto Works Ltd 発泡層付き内装品
US7442332B2 (en) * 2004-05-04 2008-10-28 Clopay Plastic Products Company, Inc. Method and apparatus for uniformly stretching thermoplastic film and products produced thereby
WO2006033449A1 (en) * 2004-09-22 2006-03-30 Sekisui Plastics Co., Ltd. Expanded molded article having voids
JP4764072B2 (ja) * 2005-05-31 2011-08-31 キョーラク株式会社 樹脂製パネルの製造方法
JP4809952B2 (ja) * 2005-07-29 2011-11-09 キョーラク株式会社 コンテナおよびその製造方法
JP5252942B2 (ja) * 2007-02-13 2013-07-31 株式会社タケヒロ 自動車用耐荷重ボードおよびその製造方法
JP5603534B2 (ja) 2007-03-30 2014-10-08 盟和産業株式会社 積層板の製造方法
WO2009016725A1 (ja) * 2007-07-31 2009-02-05 Toyota Shatai Kabushiki Kaisha 自動車のインストルメントパネル及びその製造方法
JP5004371B2 (ja) * 2008-04-30 2012-08-22 キョーラク株式会社 サンドイッチパネル用芯材およびサンドイッチパネル用芯材の成形方法、ならびにサンドイッチパネルおよびサンドイッチパネルの成形方法
CN103331898B (zh) 2008-06-25 2017-12-01 京洛株式会社 树脂成型品的成型加工方法、成型加工装置和热塑性树脂薄板的厚度调整装置
EP2343185B1 (en) * 2008-10-31 2016-03-02 Kyoraku CO., LTD Sandwich panel and method of forming the sandwich panel
JP5403246B2 (ja) * 2009-09-01 2014-01-29 キョーラク株式会社 樹脂成形品の成形方法および成形装置、並びに熱可塑性樹脂製シートの厚みの調整装置
JP5345026B2 (ja) 2009-09-01 2013-11-20 キョーラク株式会社 樹脂成形品の成形方法および成形装置、並びに熱可塑性樹脂製シートの厚みの調整装置
US9102093B2 (en) 2010-09-14 2015-08-11 Kyoraku Co., Ltd. Molding apparatus and molding method
JP5730043B2 (ja) * 2011-01-31 2015-06-03 キョーラク株式会社 樹脂成形体およびその製造方法

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5725940A (en) * 1992-10-27 1998-03-10 Mitsui Toatsu Chemicals, Inc. Composite molded article and method for making same
US6358599B1 (en) * 1999-04-30 2002-03-19 The Dow Chemical Company Alkenyl aromatic polymer foam laminates
US20060141260A1 (en) * 2004-12-29 2006-06-29 Enamul Haque Sandwich composite material using an air-laid process and wet glass
US20070256379A1 (en) * 2006-05-08 2007-11-08 Edwards Christopher M Composite panels

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140291880A1 (en) * 2013-03-29 2014-10-02 Toyota Boshoku Kabushiki Kaisha Manufacturing method for conveyance seat
US10611065B2 (en) * 2013-03-29 2020-04-07 Toyota Boshoku Kabushiki Kaisha Manufacturing method for conveyance seat
US20160243751A1 (en) * 2013-11-01 2016-08-25 Toyota Jidosha Kabushiki Kaisha Method of manufacturing resin molded product and manufacturing device thereof
US20180147754A1 (en) * 2016-11-28 2018-05-31 Tzu-Chi LIN Uniform temperature roll-extrusion forming system and uniform temperature roller structure thereof
US11110500B2 (en) 2016-11-28 2021-09-07 Tzu-Chi LIN Uniform temperature roller system having uniform heat exchange by supercritical fluid
US11529754B2 (en) 2017-03-31 2022-12-20 Jsp Corporation Skin material-coated foamed particle molded body
WO2023006536A1 (fr) * 2021-07-30 2023-02-02 Safran Seats Procédé de fabrication d'une pièce de siège d'avion
FR3125736A1 (fr) * 2021-07-30 2023-02-03 Safran Seats Procédé de fabrication d'une pièce de siège d'avion
US12128602B2 (en) 2021-07-30 2024-10-29 Safran Seats Method for manufacturing an aircraft seat part

Also Published As

Publication number Publication date
JP6173657B2 (ja) 2017-08-02
JP2013022734A (ja) 2013-02-04
EP2732953A4 (en) 2015-06-17
KR101578593B1 (ko) 2015-12-17
US10668652B2 (en) 2020-06-02
CN103635302A (zh) 2014-03-12
EP2732953A1 (en) 2014-05-21
US20160332343A1 (en) 2016-11-17
KR20140015569A (ko) 2014-02-06
EP2732953B1 (en) 2017-04-05
WO2013008633A1 (ja) 2013-01-17
CN103635302B (zh) 2016-08-17

Similar Documents

Publication Publication Date Title
US10668652B2 (en) Molding method of resin molded product and resin molded product
JP5556805B2 (ja) 樹脂成形品の成形方法および成形装置、並びに熱可塑性樹脂製シートの厚みの調整装置
JP5613442B2 (ja) 表皮付きパネルの成形方法、表皮付きパネル
US8562898B2 (en) Method for forming resin molded articles
JP6543791B2 (ja) 樹脂成形体の製造方法及びプレス成形装置
EP3287255B1 (en) Molten resin extrusion device and extrusion method as well as molten resin molding apparatus and molding method
US9746107B2 (en) Duct
WO2018179633A1 (ja) プレス成形金型および樹脂成形品
JP5769078B2 (ja) 樹脂製熱伝達ユニットの製造方法
JP7093073B2 (ja) 熱可塑性樹脂複合材料の製造方法及び製造装置
EP2208598B1 (en) Method and apparatus for molding resin foam product
JP2006281698A (ja) 発泡成形品の成形方法及び発泡成形品の成形装置
JP5760753B2 (ja) ダクトの成形方法及びダクト
EP0755762A1 (en) Molded article of fiber-reinforced resins and process and equipment for the molding thereof
JP2013011368A (ja) ダクト
JP2012179752A (ja) 成形装置及び成形方法
JP5768440B2 (ja) インパネダクト及び成形方法
JP7041834B2 (ja) 成形方法
JP2004322517A (ja) 長尺状成形品の製造方法及び製造装置
JPH079468A (ja) 熱可塑性樹脂成型体の製造方法
JP2013126746A (ja) 入れ駒を用いた成形体の製造方法
JPH10100175A (ja) 繊維強化熱可塑性樹脂成形体の製造法
JP2013028157A (ja) 電動プレス成形機の制御方法及び樹脂成形体の製造方法
JP2002355846A (ja) フォーム層付表皮一体発泡成形方法及び表皮一体発泡成形装置

Legal Events

Date Code Title Description
AS Assignment

Owner name: KYORAKU CO., LTD., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:SUMI, TAKEHIKO;REEL/FRAME:031856/0766

Effective date: 20131125

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION