TWI621736B - 化學鍍鎳或鎳合金用鎳膠體催化劑液及化學鍍鎳或鎳合金方法 - Google Patents
化學鍍鎳或鎳合金用鎳膠體催化劑液及化學鍍鎳或鎳合金方法 Download PDFInfo
- Publication number
- TWI621736B TWI621736B TW104125364A TW104125364A TWI621736B TW I621736 B TWI621736 B TW I621736B TW 104125364 A TW104125364 A TW 104125364A TW 104125364 A TW104125364 A TW 104125364A TW I621736 B TWI621736 B TW I621736B
- Authority
- TW
- Taiwan
- Prior art keywords
- acid
- nickel
- electroless
- colloidal
- liquid
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
- C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
- C23C18/18—Pretreatment of the material to be coated
- C23C18/20—Pretreatment of the material to be coated of organic surfaces, e.g. resins
- C23C18/28—Sensitising or activating
- C23C18/30—Activating or accelerating or sensitising with palladium or other noble metal
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
- C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
- C23C18/31—Coating with metals
- C23C18/32—Coating with nickel, cobalt or mixtures thereof with phosphorus or boron
- C23C18/34—Coating with nickel, cobalt or mixtures thereof with phosphorus or boron using reducing agents
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
- C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
- C23C18/1601—Process or apparatus
- C23C18/1633—Process of electroless plating
- C23C18/1635—Composition of the substrate
- C23C18/1639—Substrates other than metallic, e.g. inorganic or organic or non-conductive
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
- C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
- C23C18/31—Coating with metals
- C23C18/32—Coating with nickel, cobalt or mixtures thereof with phosphorus or boron
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
- C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
- C23C18/31—Coating with metals
- C23C18/32—Coating with nickel, cobalt or mixtures thereof with phosphorus or boron
- C23C18/34—Coating with nickel, cobalt or mixtures thereof with phosphorus or boron using reducing agents
- C23C18/36—Coating with nickel, cobalt or mixtures thereof with phosphorus or boron using reducing agents using hypophosphites
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
- C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
- C23C18/48—Coating with alloys
- C23C18/50—Coating with alloys with alloys based on iron, cobalt or nickel
Landscapes
- Chemical & Material Sciences (AREA)
- General Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Inorganic Chemistry (AREA)
- Chemically Coating (AREA)
- Catalysts (AREA)
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2014184889A JP6201153B2 (ja) | 2014-09-11 | 2014-09-11 | 無電解ニッケル又はニッケル合金メッキ用のニッケルコロイド触媒液並びに無電解ニッケル又はニッケル合金メッキ方法 |
JP2014-184889 | 2014-09-11 |
Publications (2)
Publication Number | Publication Date |
---|---|
TW201610228A TW201610228A (zh) | 2016-03-16 |
TWI621736B true TWI621736B (zh) | 2018-04-21 |
Family
ID=55458777
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
TW104125364A TWI621736B (zh) | 2014-09-11 | 2015-08-05 | 化學鍍鎳或鎳合金用鎳膠體催化劑液及化學鍍鎳或鎳合金方法 |
Country Status (5)
Country | Link |
---|---|
JP (1) | JP6201153B2 (fr) |
KR (1) | KR101831099B1 (fr) |
CN (1) | CN106460179B (fr) |
TW (1) | TWI621736B (fr) |
WO (1) | WO2016039016A1 (fr) |
Families Citing this family (16)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP6268379B2 (ja) * | 2016-07-08 | 2018-01-31 | 石原ケミカル株式会社 | 無電解ニッケル又はニッケル合金メッキ用のニッケルコロイド触媒液並びに無電解ニッケル又はニッケル合金メッキ方法 |
CN108866517B (zh) * | 2018-07-03 | 2020-04-17 | 广东工业大学 | 一种无光化学镀镍制备方法 |
CN109576686A (zh) * | 2019-01-11 | 2019-04-05 | 江门市德商科佐科技实业有限公司 | 一种增强化学镀镍溶液稳定性的添加剂 |
CN110548527B (zh) * | 2019-07-26 | 2022-08-09 | 青岛科技大学 | 一种化学镀制备负载型Ni-Fe-P-MnFeO3电催化剂的方法 |
CN110306174A (zh) * | 2019-07-29 | 2019-10-08 | 深圳市飞荣达科技股份有限公司 | 胶体镍组合物及其应用 |
JP6843455B1 (ja) * | 2020-04-27 | 2021-03-17 | 石原ケミカル株式会社 | 無電解ニッケル又はニッケル合金メッキ用のニッケルコロイド触媒液並びに無電解ニッケル又はニッケル合金メッキ方法 |
JP6858425B1 (ja) * | 2020-06-24 | 2021-04-14 | 石原ケミカル株式会社 | 無電解ニッケル又はニッケル合金メッキ用のニッケルコロイド触媒液並びに無電解ニッケル又はニッケル合金メッキ方法 |
JP6950051B1 (ja) * | 2020-07-22 | 2021-10-13 | 上村工業株式会社 | 無電解Ni−Pめっき用触媒液、および該触媒液を用いた無電解Ni−Pめっき皮膜の形成方法 |
CN112680761B (zh) * | 2020-12-16 | 2023-12-26 | 江西瑞顺超细铜线科技协同创新有限公司 | 一种镀镍铈合金软铜线生产工艺 |
RU2762733C1 (ru) * | 2021-02-18 | 2021-12-22 | Федеральное государственное бюджетное образовательное учреждение высшего образования "Российский химико-технологический университет имени Д.И. Менделеева" (РХТУ им. Д.И. Менделеева) | Раствор для химического никелирования металлических изделий |
CN113122846B (zh) * | 2021-04-03 | 2023-04-28 | 昆山陆新新材料科技有限公司 | 一种铝合金金属镀件 |
KR20230077067A (ko) | 2021-11-25 | 2023-06-01 | 삼우금속공업 주식회사 | 티타늄 소재의 무전해 니켈 도금방법 |
CN114411127B (zh) * | 2022-01-26 | 2023-08-08 | 深圳市溢诚电子科技有限公司 | 基于钌-钯体系的化学镀镍前处理活化液及其制备方法 |
JP7220494B1 (ja) | 2022-08-26 | 2023-02-10 | 石原ケミカル株式会社 | 金含有メッキ液中の金濃度測定装置並びに測定方法 |
CN115522186B (zh) * | 2022-10-09 | 2023-04-11 | 深圳创智芯联科技股份有限公司 | 一种玻璃基板的化学镀镍液及其化学镀镍工艺 |
CN116770282B (zh) * | 2023-07-04 | 2024-03-19 | 江苏贺鸿电子有限公司 | 一种线路板用化学镀镍工艺 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH0293076A (ja) * | 1988-09-29 | 1990-04-03 | Sanko Tokushu Kinzoku Kogyo Kk | 無電解メッキに利用される微細な金属体の製造方法 |
JPH03180476A (ja) * | 1989-12-08 | 1991-08-06 | Sony Corp | 光ディスクの原盤作成方法 |
JPH11209878A (ja) * | 1998-01-22 | 1999-08-03 | Dipsol Chem Co Ltd | 金属コロイド安定化剤、該安定化剤を含有する金属コロイド液状組成物、その調製方法及びその使用 |
JP2007270344A (ja) * | 2006-03-09 | 2007-10-18 | Okuno Chem Ind Co Ltd | 無電解ニッケルめっき液 |
JP2013028866A (ja) * | 2006-03-09 | 2013-02-07 | Okuno Chemical Industries Co Ltd | 無電解ニッケルめっき液 |
Family Cites Families (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP3826544B2 (ja) | 1998-02-27 | 2006-09-27 | 奥野製薬工業株式会社 | 無電解めっき用触媒組成物 |
GB0025989D0 (en) * | 2000-10-24 | 2000-12-13 | Shipley Co Llc | Plating catalysts |
JP4679716B2 (ja) | 2000-12-08 | 2011-04-27 | 日揮触媒化成株式会社 | 金属コロイド溶液の製造方法 |
JP4069248B2 (ja) * | 2002-12-09 | 2008-04-02 | 大阪市 | 無電解めっき用触媒組成物 |
JP4081576B2 (ja) | 2003-06-18 | 2008-04-30 | 上村工業株式会社 | 無電解めっき皮膜の形成方法、それに用いる置換触媒溶液、並びにプリント配線基板及び放熱めっき部材 |
CN101684554B (zh) * | 2008-09-23 | 2012-03-07 | 比亚迪股份有限公司 | 一种聚酰亚胺薄膜的化学镀铜液及其表面化学镀铜方法 |
JP5570285B2 (ja) * | 2010-04-19 | 2014-08-13 | 株式会社日本表面処理研究所 | 無電解めっき法で用いる触媒水溶液、その触媒水溶液の調製方法及びその触媒水溶液を用いた無電解めっき法並びにその無電解めっき法を用いて形成した金属皮膜を備える金属層付被めっき物 |
US8591637B2 (en) | 2010-12-14 | 2013-11-26 | Rohm And Haas Electronic Materials Llc | Plating catalyst and method |
US8591636B2 (en) | 2010-12-14 | 2013-11-26 | Rohm And Haas Electronics Materials Llc | Plating catalyst and method |
CN102877046A (zh) * | 2011-07-13 | 2013-01-16 | 比亚迪股份有限公司 | 一种化学镀铜液及化学镀铜方法 |
JP6013753B2 (ja) * | 2012-03-30 | 2016-10-25 | タキロン株式会社 | 軒樋曲り継手 |
-
2014
- 2014-09-11 JP JP2014184889A patent/JP6201153B2/ja active Active
-
2015
- 2015-07-17 KR KR1020167035470A patent/KR101831099B1/ko active IP Right Grant
- 2015-07-17 CN CN201580029055.8A patent/CN106460179B/zh active Active
- 2015-07-17 WO PCT/JP2015/070619 patent/WO2016039016A1/fr active Application Filing
- 2015-08-05 TW TW104125364A patent/TWI621736B/zh active
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH0293076A (ja) * | 1988-09-29 | 1990-04-03 | Sanko Tokushu Kinzoku Kogyo Kk | 無電解メッキに利用される微細な金属体の製造方法 |
JPH03180476A (ja) * | 1989-12-08 | 1991-08-06 | Sony Corp | 光ディスクの原盤作成方法 |
JPH11209878A (ja) * | 1998-01-22 | 1999-08-03 | Dipsol Chem Co Ltd | 金属コロイド安定化剤、該安定化剤を含有する金属コロイド液状組成物、その調製方法及びその使用 |
JP2007270344A (ja) * | 2006-03-09 | 2007-10-18 | Okuno Chem Ind Co Ltd | 無電解ニッケルめっき液 |
JP2013028866A (ja) * | 2006-03-09 | 2013-02-07 | Okuno Chemical Industries Co Ltd | 無電解ニッケルめっき液 |
Also Published As
Publication number | Publication date |
---|---|
TW201610228A (zh) | 2016-03-16 |
KR20170008287A (ko) | 2017-01-23 |
CN106460179A (zh) | 2017-02-22 |
JP2016056421A (ja) | 2016-04-21 |
CN106460179B (zh) | 2019-05-10 |
WO2016039016A1 (fr) | 2016-03-17 |
KR101831099B1 (ko) | 2018-04-04 |
JP6201153B2 (ja) | 2017-09-27 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
TWI621736B (zh) | 化學鍍鎳或鎳合金用鎳膠體催化劑液及化學鍍鎳或鎳合金方法 | |
TWI613321B (zh) | 化學鍍銅用之水系銅膠體催化劑溶液及化學鍍銅方法 | |
TWI684673B (zh) | 化學鍍銅用之銅膠體催化溶液及化學鍍銅方法 | |
TWI749234B (zh) | 化學鍍銅用銅膠體催化劑液、化學鍍銅方法、以及鍍銅基板的製造方法 | |
TWI597384B (zh) | Electroless nickel or electroless nickel alloy pretreatment solution and plating method | |
WO2021220788A1 (fr) | Solution catalytique colloïdale au nickel destinée au dépôt autocatalytique de nickel ou d'alliage de nickel, procédé de dépôt autocatalytique de nickel ou d'alliage de nickel et procédé de fabrication de substrat plaqué de nickel ou d'alliage de nickel | |
CN115803476A (zh) | 化学镀镍或镍合金用镍胶体催化液、化学镀镍或镍合金方法、以及镀镍或镍合金基板的制造方法 | |
TWI734804B (zh) | 用於化學鍍鎳或鎳合金的鎳膠體催化劑液以及化學鍍鎳或鎳合金方法 | |
JP6735981B2 (ja) | 無電解銅メッキ方法及び当該方法を用いたプリント配線板の製造方法 | |
JP2023008598A (ja) | 無電解ニッケル又はニッケル合金メッキ方法 |