TWI284746B - High heat resistant reflective coating, and laminated body using the reflective coating - Google Patents

High heat resistant reflective coating, and laminated body using the reflective coating Download PDF

Info

Publication number
TWI284746B
TWI284746B TW090107568A TW90107568A TWI284746B TW I284746 B TWI284746 B TW I284746B TW 090107568 A TW090107568 A TW 090107568A TW 90107568 A TW90107568 A TW 90107568A TW I284746 B TWI284746 B TW I284746B
Authority
TW
Taiwan
Prior art keywords
change
observed
silver
reflective layer
group
Prior art date
Application number
TW090107568A
Other languages
English (en)
Inventor
Takashi Ueno
Original Assignee
Furuya Metal Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2000373602A external-priority patent/JP4615701B2/ja
Application filed by Furuya Metal Co Ltd filed Critical Furuya Metal Co Ltd
Application granted granted Critical
Publication of TWI284746B publication Critical patent/TWI284746B/zh

Description

A7 B7 1284746 五、發明說明（ί ) 發明背景說明 發明領域 本發明係關於一種高耐熱性反射層，用以生產液晶顯 示裝置的反射體或反射性接線電極、用於建築玻璃 (building glass)、層積體（laminate)或液晶顯示裝置的 反射層。更具體而言，本發明係關於一種具有高反射率的 銀合金反射層、由此反射層所形成的層積體、以及具有此 反射層或層積層的液晶顯示裝置。 習知技術說明 許多材料被用於反射層，包括用於生產液晶顯示裝置 之反射體或反射性接線電極、以及用於建築玻璃、反射紅 外線以及熱輻射線的反射層。另外，這些反射層的層積體 被開發以提高反射率（reflection index)以及改進這些產 品的功能。這些具有改進特性之反射層的產品，已經被用 於各種領域以及各種應用。 反射層的典型材料是鋁、包含鋁作爲主要成分的鋁合 金、銀、包含銀做爲主要成分的銀合金（例如銀-鈀）、以 及金合金。由這些材料所形成的反射層於光學波長400至 4000nm範圍，包括可見以及紅外區，具有高反射率。 鋁具有高反射率，且非常便宜與實用。鋁和鋁合金通 常用於反射式液晶顯示裝置的反射體以及反射性接線電 極，這樣的液晶顯示裝置是用於可攜式的終端裝置，例如 40NDA200104TW; P1P2000284TW 1 ^紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公爱) (請先閱讀背面之注意事項寫本頁) 寫太 奸-------- 經濟部智慧財產局員工消費合作社印製 1284746 經濟部智慧財產局員工消費合作社印製 A7 B7___ 五、發明說明（工） 行動電話。當使用鋁合金時，與純鋁有關的問題，例如層 的不規則性，稱爲山丘，以及反射體與反射性接線電極表 面的惡化可以被克服。當反射體與反射性接線電極的反射 率是高的時候，送到光源的電源被降低，而且液晶顯示裝 置的亮度增加大約20%。 銀於許多金屬元素中，具有在波長400至4000nm範圍 內最高的反射率，因此，銀具有用於反射層的良好特性。 於太陽所放射的可見光、紅外線以及紫外線中，鋁、 鋁合金、銀以及銀合金傳送可見光與反射紅外線和熱射 線。可見光直接相關於照明。紅外線和熱射線的反射有用 於防止外界的光線進入房間，因此，上述材料被用於建築 玻璃，例如窗玻璃。 然而，傳統由鋁、鋁合金、銀、包括銀-鈀的銀合金、 金、金合金所形成的反射層、以及由此反射層所形成的反 射體、反射性接線電極、以及建築玻璃，具有下列問題。 鋁以及鋁合金化學上並不穩定，一由有機材料所組成 的液態抗蝕劑被施加於鋁層或鋁合金層，且於其上形成一 圖案。當圖案化的層以鹼性溶液淸洗以去除抗蝕劑時，層 的表面可能變成粗糙，而且可能降低表面對於光的反射率 或者散射。此外，當使用樹脂基底例如聚2-甲基丙烯酸甲 酯 PMMA (polymethylmethacrylate)以及政氧院聚合物 (silicone)時，鋁可能與樹脂基底所產生的氣體反應。鋁 只能被用於產生極少氣體的基底，因此限制基底可用的材 料。當包含鋁的反射層與樹脂基底於使用中接觸時，會有 40NDA200104TW; P1P2000284TW 2 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 零裝--------訂-------- (請先閱讀背面之注意事^^填寫本頁) 1284746 A7 B7 五、發明說明（4 ) 銀或銀合金的反射率於可見光區域，也就是，400至 800nm之間的光波長區域，是最高的。然而，於光波長低 於450nm的區域，銀的吸收性與吸收係數增加，而且黃色 反射光的強度增加，因此，由包含銀之反射層所形成的液 晶顯不裝置、以及包含此液晶顯不裝置的可攜式終端裝置 的外表差，而且會隨著時間而變黃。 ， 再者，銀於耐天氣性上並不好，當被置於空氣中時， 銀會吸收空氣中的濕氣（特別是水）並且變成黃色。隨著 含銀之反射層形成於玻璃基底或樹脂基底的時間變長，銀 的高反射率特性就被削弱了。 銀鈀合金，包括銀以及1-3重量百分比鈀、銀金合金， 包括銀以及1-10重量百分比金、以及銀釕合金，包括銀以 及1-10重量百分比釕’被熟知是爲具有筒抗腐触性以及高 耐熱性的二元銀合金。然而，當於高溫以及高溼度情況下 進行防水測試時，即使是於由這些銀合金所形成的合金層 中，也會發現到黑色的污點。於光學顯微鏡下，確認黑色 污點是變黑的部分，且於鈀達到有關於氫溶解的固體溶液 極限之後變成突出。當做爲建築玻璃時，上述二元合金於 濕氣區域中、或者當曝露於凝結的水滴時，缺乏長期的穩 度性。 銀金合金被熟知是爲穩定的合金，於其中銀和金被完 美地以固體狀態混合。銀金合金對於鹵素元素例如氯的耐 性並不是很好，銀金合金會與測試當中導入之空氣中的氯 或碘結合，然後產生黑色污點。 40NDA200104TW; P1P2000284TW 4 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） (請先閱讀背面之注意* —— 事項 寫本頁) 奸--------- 經濟部智慧財產局員工消費合作社印製 1284746 A7 B7 五、發明說明（S ) 除了鋁和銀，金的反射率也是高的。然而，金非常貴 並且使用於液晶顯示裝置的反射體或建築玻璃的反射層並 不實際。 發明槪述 本發明的一目的是提供一反射層，其維持高光學反射 率’迨是金的特性’以及具有改進的材料穩定度，包括耐 熱性以及抗氣候性。 本發明的另一目的是提供一層積體，包括一覆蓋層， 使得層積層維持一包含金之反射層的高光學反射率、並且 於低波長具有較低的吸收率。 本發明的另一目的是提供一層積層，包括一基膜，其 提昇包含銀之反射層與基底之間的附著性。 本發明的更一目的是提供一具有上述反射層或層積層 之液晶顯示裝置。 本發明的一反射層包含銀，作爲主要成分；一第一元 素，佔0.1至3.0重量百分比，且係選自包含金、鈀以及 釕之群組；以及一第二元素，佔〇·1至3.0重量百分比， 且係選自包含銅、鈦、鉻、鉬、鉬、鎳、鋁、鈮、金、鈀 以及釕之群組；第二元素不同於第一元素。 一層積層包含一基底以及一沉積於基底上之反射層， 反射層包含：銀，作爲主要成分；一第一元素，佔0.1至 3.0重量百分比，且係選自包含金、鈀以及釕之群組；以 40NDA200104TW; P1P2000284TW 5 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） (請先閱讀背面之注意事項寫本頁) tr>--------- 經濟部智慧財產局員工消費合作社印製 1284746 A7 B7 五、發明說明（ο ) i) 銀，作爲主要成分； ii) 一第一元素，佔0.1至3.0重量百分比，且係選自 包含金、鈀以及釕之群組；以及 iii) 一第二元素，佔〇·1至3·0重量百分比，且係選自 包含銅、鈦、鉻、鉅、鉬、鎳、鋁、鈮、金、鈀以及釕之 群組，其中第二元素不同於第一元素。 將金、鈀或釕加至銀，改善銀在高溫和高溼度條件下 的耐氣候性。主要成分銀，具有非常高的熱傳導性、容易 吸收熱、並且在原子層次很快地達到熱飽和。金、鈀及釕 降低銀的熱傳導性，並且抑制原子間的移動。金、鈀及釕 形成整個固體溶液。金、鈀及釕的含量較佳者係從0.7至 2.3重量百分比，最佳者係0.9重量百分比。 銅、鈦、鉻、鉅、鉬、鎳、鋁、或鈮，金、鈀及釕的 其中之二或更多，可以包含於反射層以提高反射層的耐熱 性及耐氣候性。 於本發明的反射層中，相較於純鋁及純銀的反射層， 表面粒子的移動不好。換句話說，本發明的反射層之中的 銀於加熱時的自擴散能量（self-diffusion energy)降低， 因此，本發明的反射層抵抗自擴散，而這改進反射層的耐 熱性。反射層於製造過程或者於一特定的氣候條件下被加 熱。於本發明的反射層中，反射率的降低被防止了。特定 而言，當反射層被加熱超過100°C，反射層中由於自擴散 所產生的視覺改變（變成模糊的白色）、以及由於表面變形 所產生的光吸收增加，被防止了。 40NDA200104TW; P1P2000284TW : ^紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） " ' ____________ (請先閱讀背面之注意事項 寫本頁)
* V •ϋ ϋ 1 §m§ IB-1 1 J,J I mmMMm —i «1 i^i I 經濟部智慧財產局員工消費合作社印制衣 1284746 A7 B7 五、發明說明（u) 如圖1所示，一可攜式終端裝置1包括一液晶顯不裝 置2。液晶顯示裝置2是由一反射體位於依序層積之下玻 璃基底、彩色濾片、極化層、液晶層、極化層、透明導電 層、以及上玻璃基底上所形成。本發明的層積體，其係作 爲此反射體，被保護不受彩色濾片製造過程所產生的鹼性 材料所破壞。此層積體比純鋁或鋁合金的反射體還具有較 高的反射率以及較低的光學吸收性，且具有此層積體的液 晶顯示裝置2遭受較少的光學損失。具有本發明層積體之 液晶顯示裝置2的亮度，比具有純鋁或鋁合金反射體之液 晶顯示裝置的亮度還要高。具有這樣液晶顯示裝置2的可 攜式終端裝置1具有改善的顯示，因此，產品的品質更佳 增進。 實施例 比較實施例 從二元銀合金產生銀合金反射層，二元表示二個元 素，也就是，銀做爲主要成分，以及金、鈀（Pd)或釕（Ru)。 金、鈀或釕的含量是0.1-4.0重量百分比。 首先，安裝一銀標靶以及鈀標靶於一磁電管濺鍍裝置 中。至銀及鈀標靶的放電控制於特定的無線電頻率交流 電。氬氣選擇性地設定在0.1至3.0帕的範圍內。這二個 金屬元素同時被濺鍍以形成二元銀合金層，其包含鈀於數 個不同的階層。同時也產生包含金或釕於數個不同階層的 40NDA200104TW; P1P2000284TW 11 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） (請先閱讀背面之注意· ----- 事項me寫本頁) --r ϋ ϋ 1 ϋ ϋ 1 I"-、 —i ϋ 1 ^1 ^1 - 經濟部智慧財產局員工消費合作社印製 1284746
五、發明說明（\ι) 銀合金層。 石英基底，大小爲100mmxl00mmxl.lt，用來做爲基 底’濺鍍過程中基底的溫度爲室溫（大約25°C )。使用蠢 氣做爲唯一的濺鍍氣體於一高度真空氣壓中，最終真空度 爲3xl〇E-6帕，銀合金層沉積於此石英基底上使得層的厚 度爲20nm。 之所以於高度真空氣壓下沉積銀合金層的原因是防止 不純的氣體停留於層中使得層變緊密。因此，可以確保所 想要的銀合金材料特性。 所產生的銀合金層保持於一熱板上大約二小時，然後 觀察層，檢查是否有視覺外觀上的改變（變成模糊(dull) 白色）以及何時發生視覺改變。熱板以每分鐘20°C的升溫 速率升高至250°C，同時檢查加熱前與加熱後銀合金層的 反射率，結果顯示於表1。 (請先閱讀背面之注意事 項寫丄 寫本頁)
--τν • ·ϋ ·ϋ ϋ ϋ ϋ ·ϋ 2rJ0 ϋ 1 a— 1 aBBl 1 mmmmm I 經濟部智慧財產局員工消費合作社印製 表1 材料組成分 (wt%) 於250°C加熱之後，層 的表面狀態 發生視 覺改變 的時間 加熱前後反射 率的變化 (波長 800 nm) Ag 模糊的白色於表面上 100°C -25 % Ag99.9Pd0.1 模糊的白色於表面上 100°C -22 % Ag99.5Pd0.5 模糊的白色於表面上 100°C -22 % Ag99.0Pdl.0 模糊的白色於表面上 120°c -21 % Ag98.5Pdl.5 模糊的白色於表面上 120°C -21 % Ag98.0Pd2.0 模糊的白色於表面上 130°C -20 % Ag97_5Pd2.5 模糊的白色在中間部份 150°C -7.4% (測量未
40NDA200104TW; P1P2000284TW 12 本紙張尺度適用中國國家標準（CNS)A4規格（210 χ 297公釐） 1284746 A7 B7 發明說明（\3 ) 經濟部智慧財產局員工消費合作社印製 改變的區域） Ag97.0Pd3.0 淡白色在中間部份周圍 150°C -6.5 % (測量未 改變的區域） Ag96.5Pd3.5 淡白色在中間部份周圍 l5〇t -6.1 % (測量未 改變的區域） Ag96.0Pd4.0 淡白色在中間部份周圍 150°C -6.1 % (測量未 改變的區域） Ag99.9AuO. 1 模糊的白色於表面上 100°C -22 % Ag99.5 AuO.5 模糊的白色於表面上 ioo°c -22 % Ag99_0Aul .0 模糊的白色於表面上 _12〇〇C -21 % Ag98.5 Aul .5 模糊的白色於表面上 ^120 °C -21 % Ag98.0Au2.0 模糊的白色於表面上 _L3〇°c -21 % Ag97.5Au2.5 模糊的白色於表面上 15(TC -7.0 % (測量未 改變的區域） Ag97.0Au3.0 淡白色在中間部份周圍 15(TC -6.5 % (測量未 改變的區域） Ag96.5 Au3.5 淡白色在中間部份周圍 150°C -6.0 % (測量未 改變的區域） Ag96.0Au4_0 淡白色在中間部份周圍 I50°c -6.0 % (測量未 改變的區域） Ag99.9RuO. 1 模糊的白色於表面上 100°C -22 % Ag99.5Ru0.5 模糊的白色於表面上 100。。 -22 % Ag99.0Rul .0 模糊的白色於表面上 I2〇〇c -21 % Ag98.5Rul .5 模糊的白色於表面上 J20°C -20 % Ag98.0Ru2.0 模糊的白色於表面上 _l3〇〇c -20% Ag97.5Ru2.5 模糊的白色於表面上 150¾ -7.4 % (測量未 改變的區域） Ag97.0Ru3.0 淡白色在中間部份周圍 I50°c -6.5 % (測量未 改變的區域） Ag96.5Ru3.5 淡白色在中間部份周圍 150。。 -6.1 % (測量未 改變的區域） Ag96.0Ru4.0 淡白色在中間部份周圍 15(TC -6.1 % (測量未 改變的區域） 如同表1所顯示的，於包含金、鈀或釕的二元銀合金 層中，如同純銀層般，層表面視覺的改變並未受到抑制， 可以假設這些二元層當暴露至戶外溫度或太陽光下時，無 40NDA200104TW; P1P2000284TW 13 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） (請先閱讀背面之注意事項 1?^寫本頁) 寫女 ^--------- 1284746 A7 B7 五、發明說明（\十） 法W熱’並且是不穩定的。相較於純銀層於加熱後，加熱 後之二元銀合金層的反射率只改善約2至3%，因此，無 法證實因爲加入金、鈀以及釕而有抗表面擴散的效果。 實施例1 從Ξ元銀合金產生本發明的銀合金反射層，三元表示 二個元素，也就是，銀作爲主要成分；一第一元素，選自 包a金把以及釕之群組；以及一第二元素，選自包含銅、 鈦、絡、钽、鉬、鎳、鋁、鈮、金、鈀以及釕之群組，其 中第二元素不同於第一元素。第一元素及第二元素的含量 爲〇·ΐ至3·ο重量百分比。 首先，安裝一銀標靶以及第一元素與第二元素的標靶 於一磁電管濺鍍裝置中。這三個金屬元素同時被濺鍍以形 成銀合金層。 如同於比較實施例中，石英基底，大小爲 100mmxl00mmxi.it，用來做爲基底，濺鍍過程中基底的 溫度保持於室溫（大約25°C )。使用氬氣做爲唯一的濺鍍 氣體於一咼度真空氣壓中，最終真空度爲3xl0E_6帕，銀 合金層沉積於此石英基底上使得層的厚度爲200nm。 所產生的銀合金層保持於一熱板上大約二小時，然後 觀察層，檢查是否有視覺外觀上的改變（變成模糊（dull) 白色）以及何時發生視覺改變。熱板以每分鐘20°C的升溫 速率升高至250°C，同時檢查加熱前與加熱後銀合金層的 反射率，結果顯示於表2。 40NDA200104TW; P1P2000284TW 14 ------------ (請先閱讀背面之注意事項 11^寫本頁) • ϋ 1 1 0 n H ϋ ϋ ϋ 1 · 經濟部智慧財產局員工消費合作社印製 本紙張尺度適用中國國家標準（CNS)A4規格（21〇 x 297公愛1 ' 1284746 A7 _B7 五、發明說明（\5) 經濟部智慧財產局員工消費合作社印製 表2 材料組成分 (wt%) 於250°C加熱之 後，層的表面狀 態 發生視 覺改變 的時間 加熱前後反射 率的變化 (波長 800 nm) Ag99.8Pd0.1Cu0.1 未觀察到改變 — -1.1 % Ag98.4PdO.lCul.5 未觀察到改變 — -1.0 % Ag96.9Pd0.1Cu3.0 未觀察到改變 — -1.0 % Ag98.4Pdl.5CuO」 未觀察到改變 — -0.9 % Ag97.0Pdl.5Cul.5 未觀察到改變 — -0.7 % Ag95.5Pdl.5Cu3.0 未觀察到改變 — -0.7 % Ag96.9Pd3.0Cu(Kl 未觀察到改變 — -1.0 % Ag95.5Pd3.0Cul.5 未觀察到改變 — -0.5 % Ag94.0Pd3.0Cu3.0 未觀察到改變 — -0.4 % Ag99.8Pd0.1Ti0.1 未觀察到改變 — -1.1 % Ag98.4PdO.lTil.5 未觀察到改變 — -1.0 % Ag96.9Pd0.1Ti3.0 未觀察到改變 — -1.0 % Ag98.4Pdl.5Ti0.1 未觀察到改變 — -0.9 % Ag97.0Pdl.5Til.5 未觀察到改變 — -0.7 % Ag95.5Pdl.5Ti3.0 未觀察到改變 — -0.7 % Ag96.9Pd3.0Ti0」 未觀察到改變 — -1.0 % Ag95.5Pd3.0Til.5 未觀察到改變 — -0.5 % Ag94.0Pd3.0Ti3.0 未觀察到改變 — -0.4 % Ag99.8Pd0.1Ti0.1 未觀察到改變 — -1.1 % Ag98.4PdO.lCrl.5 未觀察到改變 — -1.0 % Ag96.9Pd0.1Cr3.0 未觀察到改變 — -1.0 % Ag98.4Pdl.5Cr0.1 未觀察到改變 — -0.9 % Ag97.0Pdl.5Crl.5 未觀察到改變 — -0.7 % Ag95.5Pdl.5Cr3.0 未觀察到改變 — -0.7 % Ag96.9Pd3.0Cr0」 未觀察到改變 — -1.0 % Ag95.5Pd3.0Crl.5 未觀察到改變 — -0.5 % Ag94.0Pd3.0Cr3.0 未觀察到改變 — -0.4 % Ag99.8Pd0.1Cr0.1 未觀察到改變 — -1.1 % Ag98.4PdO.lTal.5 未觀察到改變 — -1.0 % Ag96.9Pd0.1Ta3.0 未觀察到改變 — -1.0 % Ag98.6Pdl.5Ta0.1 未觀察到改變 — -0.9 % Ag97.0Pdl.5Tal.5 未觀察到改變 — -0.7 % Ag95.5Pdl.5Ta3.0 未觀察到改變 — -0.7 % 40NDA200104TW; P1P2000284TW 15 I ΜΜ ΙΒ··Ι Ml· _ I MB Η·· I I Η··· ΜΗ· (請先閱讀背面之注意事項寫本頁) 項 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 _B7 五、發明說明（\U) 表2 (續） 經濟部智慧財產局員工消費合作社印製 材料組成分 (wt%) 於250°C加熱 之後，層的表 面狀態 發生視 覺改變 的時間 加熱前後反 射率的變化 (波長 800 nm) Ag98.4Pd0.1Ni0.1 未觀察到改變 — -1.1 % Ag98.4PdO.lNil.5 未觀察到改變 — -1.0 % Ag96.9Pd0.1 Ni3.0 未觀察到改變 — -1.0 % Ag98.4Pdl.5 NiO.l 未觀察到改變 — -0.9 % Ag97.0Pdl.5 Nil.5 未觀察到改變 — -0.7 % Ag95.5Pdl.5 Ni3.0 未觀察到改變 — -0.7 % Ag96.9Pd3.0Ni 0.1 未觀察到改變 — -1.0 % Ag95.5Pd3.0 Nil.5 未觀察到改變 — -0.5 % Ag94.0Pd3.0Ni 3.0 未觀察到改變 — -0.4 % Ag99.8Pd0.1A10.1 未觀察到改變 — -1.1 % Ag98.4Pd0.1 All.5 未觀察到改變 — -1.0 % Ag96.9Pd0.1 A13.0 未觀察到改變 — -1.0 % Ag98.4Pdl.5 A10.1 未觀察到改變 — -0.9 % Ag97.0Pdl.5 All.5 未觀察到改變 — -0.7 % Ag95.5Pdl.5 A13.0 未觀察到改變 — -0.7 % Ag96.9Pd3.0 A10.1 未觀察到改變 — -1.0 % Ag95.5Pd3.0 All.5 未觀察到改變 — -0.5 % Ag94.0Pd3.0 A13.0 未觀察到改變 — -0.4 % Ag99.8Pd0.1 NbO.l 未觀察到改變 — -1.1 % Ag98.4Pd0.1 Nbl.5 未觀察到改變 — -1.0 % Ag96.9Pd0.1 Nb3.0 未觀察到改變 — -1.0 % Ag98.4Pdl.5 NbO.l 未觀察到改變 — -0.9 % Ag97.0Pdl.5 Nbl.5 未觀察到改變 — -0.7 % Ag95.5Pdl.5 Nb3.0 未觀察到改變 — -0.7 % Ag96.9Pd3.0 NbO.l 未觀察到改變 — -1.0 % Ag95.5Pd3.0 Nbl.5 未觀察到改變 — -0.5 % Ag94.0Pd3.0 Nb3.0 未觀察到改變 — -0.4 % 40NDA200104TW; P1P2000284TW 16 (請先閱讀背面之注意事項寫本頁) ^---------
Ag96.9Pd3.0Ta0.1 未觀察到改變 — -1.0 % Ag95.5Pd3.OTal.5 未觀察到改變 — -0.5 % Ag94.0Pd3.0Ta3.0 未觀察到改變 — -0.4 % 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7 五、發明說明（VI) 表2 (續） 經濟部智慧財產局員工消費合作社印製 材料組成分 (wt%) 於250°C加熱 之後，層的表 面狀態 發生視 覺改變 的時間 加熱前後反 射率的變化 (波長 800 nm) Ag99.8PdO.lMoO」 未觀察到改變 — -1.1 % Ag98.4PdO.lMol.5 未觀察到改變 — -1.0 % Ag96.9Pd0.1Mo3.0 未觀察到改變 — -1.0 % Ag98.4Pdl.5Mo0.1 未觀察到改變 — -0.9 % Ag97.0Pdl.5Mol.5 未觀察到改變 — -0.7 % Ag95.5Pdl.5Mo3.0 未觀察到改變 — -0.7 % Ag96.9Pd3.0Mo0」 未觀察到改變 — -1.0 % Ag95.5Pd3.0Mol.5 未觀察到改變 — -0.5 % Ag94.0Pd3.0Mo3.0 未觀察到改變 — -0.4 % Ag99.8Pd0.1Au0.1 未觀察到改變 — -1.1 % Ag98.4Pd0.1 Aul.5 未觀察到改變 — -1.0 % Ag96.9Pd0.1 Au3.0 未觀察到改變 — -1.0 % Ag98.4Pdl.5 AuO.l 未觀察到改變 — -0.9 % Ag97.0Pdl.5 Aul.5 未觀察到改變 — -0.7 % Ag95.5Pdl.5 Au3.0 未觀察到改變 — -0.7 % Ag96.9Pd3.0 AuO.l 未觀察到改變 — -1.0 % Ag95.5Pd3.0 Aul.5 未觀察到改變 — -0.5 % Ag94.0Pd3.0 Au3.0 未觀察到改變 — -0.4 % Ag99.8Au0.1Ru0.1 未觀察到改變 — -1.0 % Ag98.4AuO. IRul .5 未觀察到改變 — -0.8 % Ag96.9Au0.1Ru3.0 未觀察到改變 — -0.5 % Ag98.4Aul.5Ru0.1 未觀察到改變 — -1.0 % Ag97.0Aul.5Rul.5 未觀察到改變 — -0.3 % Ag95.5Aul.5Ru3.0 未觀察到改變 — -0.6 % Ag96.9Au3.0Ru0.1 未觀察到改變 — -0.8 % Ag95.5Au3.0Rul .5 未觀察到改變 — -0.5 % Ag94.0Au3.0Ru3.0 未觀察到改變 — -0.8 % Ag99.8Au0.1Ru0.1 未觀察到改變 — -1.0 % Ag98.4Pd0.1 Rul.5 未觀察到改變 — -0.9 % Ag96.9Pd0.1 Ru3.0 未觀察到改變 — -1.0 % Ag98.6Pdl.5 RuO.l 未觀察到改變 — -0.9 % Ag97.0Pdl.5 Rul.5 未觀察到改變 — -0.8 % Ag95.5Pdl.5 Ru3.0 未觀察到改變 — -0.7 %
40NDA200104TW; P1P2000284TW 17 請 先 閱 讀 背 面 之 注 意 事
η 頁I
I 訂> I I •4 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7 五、發明說明（\名） 表2 (續） 經濟部智慧財產局員工消費合作社印製
AgAuXb 材料組成分 (wt%) 於250°C加熱 之後，層的表 面狀態 發生視 覺改變 的時間 加熱前後反 射率的變化 (波長 800 nm) Ag99.8Au0.1Cu0.1 未觀察到改變 — -0.9 % Ag98.4AuO.lCul.5 未觀察到改變 — -0.8 % Ag96.9Au0.1Cu3.0 未觀察到改變 — -0.8 % Ag98.4Aul.5Cu0.1 未觀察到改變 — -0.7 % Ag97.0Aul.5Cul.5 未觀察到改變 — -0.6 % Ag95.5Aul.5Cu3.0 未觀察到改變 — -0.5 % Ag96.9Au3.0Cu0」 未觀察到改變 — -0.8 % Ag95.5Au3.0Cul .5 未觀察到改變 — -0.5 % Ag94.0Au3.0Cu3.0 未觀察到改變 — -0.6 % Ag99.8Au0.1Ti0.1 未觀察到改變 — -0.9 % Ag98.4Au0.1Ti 1.5 未觀察到改變 — -0.6 % Ag96.9Au0.1Ti 3.0 未觀察到改變 — -0.3 % Ag98.4Aul.5Ti 0.1 未觀察到改變 — -0.5 % Ag97.0Aul.5Ti 1.5 未觀察到改變 — -0.8 % Ag95.5Aul.5Ti 3.0 未觀察到改變 一 -0.6 % Ag96.9Au3.0Ti 0.1 未觀察到改變. — -0.9 % Ag95.5Au3.0Ti 1.5 未觀察到改變 — -1.1 % Ag94.0Au3.0Ti 3.0 未觀察到改變 一 -1.0 % Ag99.8Au0.1Cr0.1 未觀察到改變 — -0.8 % Ag98.4Au0.1Cr 1.5 未觀察到改變 — -1.0 % Ag96.9Au0.1Cr 3.0 未觀察到改變 — -0.6 % Ag98.4Aul.5Cr 0.1 未觀察到改變 — -0.9 % Ag97.0Aul.5Cr 1.5 未觀察到改變 — -0.4 % Ag95.5Aul.5Cr 3.0 未觀察到改變 — -1.1 % Ag96.9Au3.0Cr 0.1 未觀察到改變 — -0.8 % 40NDA200104TW: P1P2000284TW 18 (請先閱讀背面之注意事項寫本頁) 寫女 ^---------
Ag96.9Pd3.0 RuO.l 未觀察到改變 — -1.0 % Ag95.5Pd3.0 Rul.5 未觀察到改變 — -0.6 % Ag94.0Pd3.0 Ru3.0 未觀察到改變 — -0.4 % 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7 五、發明說明（1¾ )
Ag95.5Au3.0Cr 1.5 未觀察到改變 — -0.9 % Ag94.0Au3.0Cr 3.0 未觀察到改變 — -0.7 % Ag99.8Au0.1Ti0.1 未觀察到改變 — -0.5% Ag98.4AuO.lTi 1.5 未觀察到改變 — -0.6 % Ag96.9AuO.lTi 3.0 未觀察到改變 — 1.1 % Ag98.6Aul.5Ti 0.1 未觀察到改變 — -0.4 % Ag97.0Aul.5Ti 1.5 未觀察到改變 — -0.9 % Ag95.5Aul.5Ti 3.0 未觀察到改變 — -0.8 % Ag96.9Au3.0Ti 0.1 未觀察到改變 — -0.5 % Ag95.5Au3.0Ti 1.5 未觀察到改變 — -1.0 % Ag94.0Au3.0Ti 3.0 未觀察到改變 — -0.6 % 表2 (續） (請先閱讀背面之注意事項寫本頁) 經濟部智慧財產局員工消費合作社印製 材料組成分 (wt%) 於250°C加熱 之後，層的表 面狀態 發生視 覺改變 的時間 加熱前後反 射率的變化 (波長 800 nm) Ag99.8Au0.1Mo0.1 未觀察到改變 — -0.7 % Ag98.4AuO.lMol.5 未觀察到改變 — -1.1 % Ag96.9AuO. 1M〇3.0 未觀察到改變 — -0.8 % Ag98.4Aul.5Mo0.1 未觀察到改變 — -0.4 % Ag97.0Aul .5Mol .5 未觀察到改變 — -0.8 % Ag95.5Aul.5Mo3.0 未觀察到改變 — -0.3 % Ag96.9Au3.0Mo0.1 未觀察到改變 — -0.9 % Ag95.5Au3.0Mol .5 未觀察到改變 — -1.1 % Ag94.0Au3.0Mo3.0 未觀察到改變 — -1.0 % Ag99.8Au0.1Na0.1 未觀察到改變 — -0.5 % Ag98.4AuO.lNal.5 未觀察到改變 — -1.1% Ag96.9Au0.1Na3.0 未觀察到改變 — -0.8 % Ag98.4Aul.5Na0.1 未觀察到改變 — -0.4 % Ag97.0Aul.5Nal.5 未觀察到改變 — -1.0% Ag95.5Aul.5Na3.0 未觀察到改變 — -0.7 % Ag96.9Au3.0Na0.1 未觀察到改變 — -0.9 % Ag95.5Au3.0Nal.5 未觀察到改變 — -0.6% Ag94.0Au3.0Na3.0 未觀察到改變 — -0.8 % Ag99.8AuO. 1A10.1 未觀察到改變 — -1.09 % 40NDA200104TW; P1P2000284TW 19 本紙張尺度適用中國國家標準（CNS)A4規格（210 χ 297公釐） t--------- 1284746 A7 B7 五、發明說明（>〇 )
Ag98.4AuO.lAl 1.5 未觀察到改變 — -1.1 % Ag96.9AuO.lAl 3.0 未觀察到改變 — -0.7 % Ag98.4Aul.5Al 0.1 未觀察到改變 — -0.9 % Ag97.0Aul.5Al 1.5 未觀察到改變 — -0.5 % Ag95.5Aul.5Al 3.0 未觀察到改變 — -0.4 % Ag96.9Au3.0Al 0.1 未觀察到改變 — -0.8 % Ag95.5Au3.0Al 1.5 未觀察到改變 — -1.0 % Ag94.0Au3.0Al 3.0 未觀察到改變 — -1.1 % Ag99.8Au0.1Nb0.1 未觀察到改變 — -1.1% Ag98.4AuO.lNbl.5 未觀察到改變 — -1.0 % Ag96.9Au0.1Nb3.0 未觀察到改變 — -0.9 % Ag98.6Aul.5Nb0.1 未觀察到改變 — -0.8 % Ag97.0Aul.5Nbl.5 未觀察到改變 — -0.7 % Ag95.5Aul.5Nb3.0 未觀察到改變 — -0.8 % Ag96.9Au3.0Nb0.1 未觀察到改變 — -1.0 % Ag95.5Au3.0Nbl.5 未觀察到改變 — -0.4 % Ag94.0Au3.0Nb3.0 未觀察到改變 — -0.4 % 表2 (續） 經濟部智慧財產局員工消費合作社印製
AgRuX 材料組成分 (wt%) 於250°C加熱 之後，層的表 面狀態 發生視 覺改變 的時間 加熱前後反 射率的變化 (波長 800 nm) Ag99.8Ru0.1Cu0.1 未觀察到改變 — -0.9 % Ag98.4RuO.lCul.5 未觀察到改變 — -0.8% Ag96.9Ru0.1Cu3.0 未觀察到改變 — -0.7 % Ag98.4Rul.5Cu0.1 未觀察到改變 — -0.7 % Ag97.0Rul.5Cul.5 未觀察到改變 — -0.6 % Ag95.5Rul .5Cu3.0 未觀察到改變 — -0.5 % Ag96.9Ru3.0Cu0.1 未觀察到改變 — -0.7 % Ag95.5Ru3.0Cul.5 未觀察到改變 — -0.5 % Ag94.0Ru3.0Cu3.0 未觀察到改變 — -0.6 % Ag99.8Ru0.1Ti0.1 未觀察到改變 — -0.9 % Ag98.4Ru0.1 Ti 1.5 未觀察到改變 — -0.6% 40NDA200104TW; P1P2000284TW 20 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） -ϋ I ϋ I I ·ϋ 一：°J ϋ 1_1 1 n ϋ ϋ I (請先閱讀背面之注意事項寫本頁) 1284746 A7 B7 五、發明說明（>υ
Ag96.9Ru0.1 Ti 3.0 未觀察到改變 — -0.4% Ag98.4Rul.5 Ti 0.1 未觀察到改變 — -0.5 % Ag97.0Rul.5 Ti 1.5 未觀察到改變 — -0.8% Ag95.5Rul.5 Ti 3.0 未觀察到改變 — -0.5 % Ag96.9Ru3.0 Ti 0.1 未觀察到改變 — -0.9 % Ag95.5Ru3.0 Ti 1.5 未觀察到改變 — -1.1% Ag94.0Ru3.0 Ti 3.0 未觀察到改變 — -1.0 % Ag99.8Ru O.lCrO.l 未觀察到改變 — -0.8 % Ag98.4 Ru0.1Crl.5 未觀察到改變 — -1.0 % Ag96.9 Ru0.1Cr3.0 未觀察到改變 — -0.6 % Ag98.4 Rul.5Cr0.1 未觀察到改變 — -0.8 % Ag97.0 Rul.5Crl.5 未觀察到改變 — -0.4 % Ag95.5 Rul.5Cr3.0 未觀察到改變 — -1.0 % Ag96.9 Ru3.0Cr0.1 未觀察到改變 — -0.8 % Ag95.5 Ru3.0Crl.5 未觀察到改變 — -0.9 % Ag94.0 Ru3.0Cr3.0 未觀察到改變 — -0.8 % Ag99.8Ru0.1Ta0.1 未觀察到改變 — -0.9 % Ag98.4Ru0.1Ta 1.5 未觀察到改變 — -0.8 % Ag96.9Ru0.1Ta 3.0 未觀察到改變 — -0.7 % Ag98.6Rul.5Ta 0.1 未觀察到改變 — -0.7 % Ag97.0Rul.5Ta 1.5 未觀察到改變 — -0.6 % Ag95.5Rul.5Ta 3.0 未觀察到改變 — -0.5 % Ag96.9Ru3.0Ta 0.1 未觀察到改變 — -0.7 % Ag95.5Ru3.0Ta 1.5 未觀察到改變 — -0.6 % Ag94.0Ru3.0Ta 3.0 未觀察到改變 — -0.6 % (請先閱讀背面之注意事項寫本頁) 寫夫 ·11111111 Φ4. 表2 (續） 材料組成分 (wt%) 於250°C加熱 之後，層的表 面狀態 發生視 覺改變 的時間 加熱前後反 射率的變化 (波長 800 nm) Ag99.8Ru0.1Mo0.1 未觀察到改變 — -0.8 % Ag98.4RuO.lMol.5 未觀察到改變 — -1.0% Ag96.9Ru0.1Mo3.0 未觀察到改變 — -0.6 % Ag98.4Rul ·5Μ〇0· 1 未觀察到改變 一 -0.7 % Ag97.0Rul.5Mol.5 未觀察到改變 — -0.4 % 經濟部智慧財產局員工消費合作社印製 40NDA200104TW; P1P2000284TW 21 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7五、發明說明（》)
Ag95.5Rul.5Mo3.0 未觀察到改變 — -1.1 % Ag96.9Ru3.0Mo0.1 未觀察到改變 — -0.8 % Ag95.5Ru3.OMol.5 未觀察到改變 — -0.7 % Ag94.0Ru3.0Mo3.0 未觀察到改變 — -0.6 % Ag99.8Ru0.1Ni0.1 未觀察到改變 — -1.0 % Ag98.4RuO.lNi 1.5 未觀察到改變 — -1.1 % Ag96.9RuO.lNi 3.0 未觀察到改變 — -0.8 % Ag98.4Rul.5Ni 0.1 未觀察到改變 — -0.8 % Ag97.0Rul.5Ni 1.5 未觀察到改變 — -0.5 % Ag95.5Rul.5Ni 3.0 未觀察到改變 — -0.5 % Ag96.9Ru3.0Ni 0.1 未觀察到改變 — -0.7 % Ag95.5Ru3.0Ni 1.5 未觀察到改變 — -1.0 % Ag94.0Ru3.0Ni 3.0 未觀察到改變 — -1.1 % Ag99.8Ru 0.1A10.1 未觀察到改變 — -1.0 % Ag98.4 Ru0.1A11.5 未觀察到改變 — -1.1 % Ag96.9 Ru0.1A13.0 未觀察到改變 — -0.7 % Ag98.4 Rul.5A10.1 未觀察到改變 — -0.9 % Ag97.0 Rul.5A11.5 未觀察到改變 — -0.5 % Ag95.5 Rul.5A13.0 未觀察到改變 — -0.5 % Ag96.9 Ru3.0A10.1 未觀察到改變 — -0.8 % Ag95.5 Ru3.0A11.5 未觀察到改變 — -1.0 % Ag94.0 Ru3.0A13.0 未觀察到改變 — -1.1 % Ag99.8Ru0.1Nb0.1 未觀察到改變 — -1.1 % Ag98.4RuO.lNbl.5 未觀察到改變 — -1.0 % Ag96.9Ru0.1Nb3.0 未觀察到改變 — -0.8 % Ag98.6Rul.5Nb0.1 未觀察到改變 — -0.8 % Ag97.0Rul.5Nbl.5 未觀察到改變 — -0.7 % Ag95.5Rul.5Nb3.0 未觀察到改變 — -0.7 % Ag96.9Ru3.0Nb0.1 未觀察到改變 — -1.0 % Ag95.5Ru3.0Nbl.5 未觀察到改變 — -0.5 % Ag94.0Ru3.0Nb3.0 未觀察到改變 — -0.4 % (請先閱讀背面之注意事項寫本頁) -------- ·#· 經濟部智慧財產局員工消費合作社印製 雖然在比較例中觀察到銀合金層表面的變化以及所伴 隨而來的反射率降低，這些現象都並未在實施例1之銀合 金層中所檢查的任何組成中觀察到，如同表2所顯示。 40NDA200104TW; P1P2000284TW 22 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 經濟部智慧財產局員工消費合作社印制衣 A7 B7 五、發明說明（工3) 再者’石英基底，於其上沉積各種銀合金層且被加熱 到250 C ’更被放置於一 400°C的熱板上歷時二小時，於任 何檢查的組成之銀合金層中，都並未觀察到表面變化以及 反射率的降低（資料並未顯示）。 生產包含銀以及0.1-3.0重量百分比銅、鈦、鉻、鉬、 鉬、鎳、鋁或鈮、但未包含金、鈀或釕的銀合金反射層， 如同所述者，銀合金藉由同時濺鍍而沉積於石英基底上， 使得層的厚度爲15nm，觀察於250°C以及400°C隨著時間 層的視覺變化，所有這些層都變白，且反射率降低（資料 未顯不）。 綜合在一起可知，包含銀做爲主要成分、第一元素以 及第二元素的銀合金層具有更改進的耐熱性以及維持高反 射率。 實施例2 於這個實施例中，硏究三元銀合金層做爲反射型液晶 顯示裝置之反射體以及反射性接線電極的效用。
執行對於化學穩定度的抗腐餓硏究，比較傳統金屬層 (純鋁、鋁合金、銀、二元銀合金）與本發明的三元銀合 金層。施加一液態抗蝕劑至反射層並且形成圖案於其上， 然後以鹼性溶液（5%氫氧化鉀水溶液）淸洗反射層以去除 抗鈾劑。觀察層的表面，結果顯示於表3中。 40NDA200104TW; P1P2000284TW 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） (請先閱讀背面之注意事項_填寫本頁) 寫太 ·11111111 1284746 Α7 Β7 五、發明說明（ 表3 經濟部智慧財產局員工消費合作社印製 材料組成分（Wt%) 鹼性溶液 A1 完全反應 A196.0 Mg 4.0 完全反應 覆蓋有丙烯酸樹脂的鋁 部分反應 Ag98.0Pd2.0 許多黑色污點 Ag97.0Pd3.0 適度的黑色污點 Ag99.8 Pd 0.1 Cu 0.1 沒變 Ag99.4 Pd 0.5 Cu 0.1 沒變 Ag98.1 Pd 0.9 Cu 1.0 沒變 Ag98.9 Pd 1.0 Cu 0.1 沒變 Ag97.9 Pd 2.0 Cu 0.1 沒變 Ag96.9 Pd 3.0 Cu 0.1 沒變 Ag96.5 Pd 3.0 Cu0.5 沒變 Ag94.0 Pd 3.0 Cu 3.0 沒變 Ag99.8 Pd 0.1 Ti 0.1 沒變 Ag99.4 Pd 0.5 Ti 0.1 沒變 Ag98.1 Pd 0.9 Ti 1.0 沒變 Ag98.9 Pd 1.0 Ti 0.1 沒變 Ag97.9 Pd 2.0 Ti 0.1 沒變 Ag96.9 Pd 3.0 Ti 0.1 沒變 Ag96.5 Pd 3.0 Ti 0.5 沒變 Ag94.0 Pd 3.0 Ti 3.0 沒變 Ag99.8 Pd 0.1 Cr 0.1 沒變 Ag99.4 Pd 0.5 Cr 0.1 沒變 Ag98.1 Pd 0.9 Cr 1.0 沒變 Ag98.9 Pd 1.0 Cr 0.1 沒變 Ag97.9 Pd 2.0 Cr 0.1 沒變 Ag96.9 Pd 3.0 Cr 0.1 沒變 Ag96.5 Pd 3.0 Cr0.5 沒變 Ag94.0 Pd 3.0 Cr 3.0 沒變 Ag99.8 Pd 0.1 Ta 0.1 沒變 Ag98.4 Pd 0.1 Ta 1.5 沒變 Ag96.9 Pd 0.1 Ta 3.0 沒變 Ag98.4 Pd 1.5 Ta 0.1 沒變 Ag97.0 Pd 1.5 Ta 1.5 沒變 Ag95.5 Pd 1.5 Ta 3.0 沒變 Ag96.9 Pd 3.0 Ta 0.1 沒變 Ag95.5 Pd 3.0 Ta 1.5 沒變 Ag94.0 Pd 3.0 Ta 3.0 沒變 40NDA200104TW; P1P2000284TW 24 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） (請先閱讀背面之注意事項寫本頁) 寫女 111111. 1284746 A7 B7 五、發明說明us) 經濟部智慧財產局員工消費合作社印製
Ag99.8 Pd 0.1 Mo 0.1 沒變 Ag98.4 Pd 0.1 Mo 1.5 沒變 Ag96.9 Pd 0.1 Mo 3.0 沒變 Ag98.4 Pd 1.5 Mo 0.1 沒變 Ag97.0 Pd 1.5 Mo 1.5 沒變 Ag95.5 Pd 1.5 Mo 3.0 沒變 Ag96.9 Pd 3.0 Mo 0.1 沒變 Ag95.5 Pd 3.0 Mo 1.5 沒變 Ag94.0 Pd 3.0 Mo 3.0 沒變 Ag99.8 Pd 0.1 Ni 0.1 沒變 Ag98.4 Pd 0.1 Ni 1.5 沒變 Ag96.9 Pd 0.1 Ni 3.0 沒變 Ag98.4 Pd 1.5 Ni 0.1 沒變 Ag97.0 Pd 1.5 Ni 1.5 沒變 Ag95.5 Pd 1.5 Ni 3.0 沒變 Ag96.9 Pd 3.0 Ni 0.1 沒變 Ag95.5 Pd 3.0 Ni 1.5 沒變 Ag94.0 Pd 3.0 Ni 3.0 沒變 Ag99.8 Pd 0.1 A1 0.1 沒變 Ag98.4 Pd 0.1 A1 1.5 沒變 Ag96.9 Pd 0.1 A1 3.0 沒變 Ag98.4 Pd 1.5 A1 0.1 沒變 Ag97.0 Pd 1.5 A1 1.5 沒變 Ag95.5 Pd 1.5 A1 3.0 沒變 Ag96.9 Pd 3.0 A1 0.1 沒變 Ag95.5 Pd 3.0 A1 1.5 沒變 Ag94.0 Pd 3.0 A1 3.0 沒變 Ag99.8 Pd 0.1 NbO.l 沒變 Ag98.4 Pd 0.1 Nb 1.5 沒變 Ag96.9 Pd 0.1 Nb 3.0 沒變 Ag98.4 Pd 1.5 Nb 0.1 沒變 Ag97.0 Pd 1.5 Nb 1.5 沒變 Ag95.5 Pd 1.5 Nb 3.0 沒變 Ag96.9 Pd 3.0 Nb 0.1 沒變 Ag95.5 Pd 3.0 Nb 1.5 沒變 Ag94.0 Pd 3.0 Nb 3.0 沒變 Ag99.8 Pd 0.1 AuO.l 沒變 Ag98.4 Pd 0.1 Au 1.5 沒變 Ag96.9 Pd 0.1 Au 3.0 沒變 Ag98.4 Pd 1.5 Au 0.1 沒變 Ag97.0 Pd 1.5 Au 1.5 沒變 40NDA200104TW; P1P2000284TW 25 本紙張尺度適用中國國家標準（CNS)A4規格（210 χ 297公釐） (請先閱讀背面之注意事項寫本頁)
，· Γ -I 1 _1 ϋ ϋ ·ϋ ϋ ϋ -ϋ ϋ I 1284746 A7 B7 五、發明說明（义) 經濟部智慧財產局員工消費合作社印製
Ag95.5 Pd 1.5 Au 3.0 沒變 Ag96.9 Pd 3.0 Au 0.1 沒變 Ag95.5 Pd 3.0 Au 1.5 沒變 Ag94.0 Pd 3.0 Au 3.0 沒變 Ag99.8 Pd 0.1 AuO.l 沒變 Ag98.4 Pd 0.1 Au 1.5 沒變 Ag96.9 Pd 0.1 Au 3.0 沒變 Ag98.4 Pd 1.5 Au 0.1 沒變 Ag97.0 Pd 1.5 Au 1.5 沒變 Ag95.5 Pd 1.5 Au 3.0 沒變 Ag96.9 Pd 3.0 Au 0.1 沒變 Ag95.5 Pd 3.0 Au 1.5 沒變 Ag94.0 Pd 3.0 Au 3.0 沒變 Ag99.8 Pd 0.1 RuO.l 沒變 Ag98.4 Pd 0.1 Ru 1.5 沒變 Ag96.9 Pd 0.1 Ru 3.0 沒變 Ag98.4 Pd 1.5 Ru 0.1 沒變 Ag97.0 Pd 1.5 Ru 1.5 沒變 Ag95.5 Pd 1.5 Ru 3.0 沒變 Ag96.9 Pd 3.0 Ru 0.1 沒變 Ag95.5 Pd 3.0 Ru 1.5 沒變 Ag94.0 Pd 3.0 Ru 3.0 沒變
AgAuX 表 3 (續） 材料組成分（wt%) 鹼性溶液 Ag98.0Au2.0 許多黑色污點 Ag97.0Au3.0 適度的黑色污點 Ag99.8AuO. 1 CuO. 1 沒變 Ag99.4Au0.5Cu0.1 沒變 Ag98.1Au0.9Cul.0 沒變 Ag98.9Aul.0Cu0.1 沒變 Ag97.9Au2.0Cu0」 沒變 Ag96.9Au3 .OCuO. 1 沒變 Ag96.5Au3.0Cu0.5 沒變 Ag94.0Au3.0Cu3.0 沒變 Ag99.8Au0.1Ti0.1 沒變 Ag99.4Au0.5Ti0.1 沒變 Ag98.1Au0.9Til.0 沒變 40NDA200104TW; P1P2000284TW 26 (請先閱讀背面之注意事項寫本頁) 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7 五、發明說明（Jl/]) 經濟部智慧財產局員工消費合作社印製
Ag98.9Aul.0Ti0.1 沒變 Ag97.9Au2.0Ti0.1 沒變 Ag96.9Au3.0Ti0.1 沒變 Ag96.5Au3.0Ti0.5 沒變 Ag94.0Au3.0Ti3.0 沒變 Ag99.8Au0.1Cr0.1 沒變 Ag98.4AuO.lCrl.5 沒變 Ag96.9Au0.1Cr3.0 沒變 Ag98.4Aul.5Cr0.1 沒變 Ag97.0Aul.5Crl.5 沒變 Ag95.5Aul .5Cr3.0 沒變 Ag96.9Au3.0Cr0.1 沒變 Ag95.5Au3.0Crl .5 沒變 Ag94.0Au3.0Cr3.0 沒變 Ag98.4AuO.lTal.5 沒變 Ag96.9Au0.1Ta3.0 沒變 Ag98.4Aul.5Ta0.1 沒變 Ag97.0Aul .5Tal .5 沒變 Ag95.5Aul.5Ta3.0 沒變 Ag96.9Au3.0Ta0.1 沒變 Ag95.5Au3.0Tal.5 沒變 Ag94.0Au3.0Ta3.0 沒變 Ag99.8Au0.1Mo0.1 沒變 Ag98.4AuO. IMol .5 沒變 Ag96.9Au0.1Mo3.0 沒變 Ag98.4Aul.5Mo0.1 沒變 Ag97.0Aul.5Mol.5 沒變 Ag95.5Aul.5Mo3.0 沒變 Ag96.9Au3.0Mo0.1 沒變 Ag95.5Au3.0Mol .5 沒變 Ag94.0Au3.0Mo3.0 沒變 Ag99.8Au0.1Ni0.1 沒變 Ag98.4AuO.lNil.5 沒變 Ag96.9Au0.1Ni3.0 沒變 Ag98.4Aul.5NiO. 1 沒變 Ag97.0Aul.5Nil.5 沒變 Ag95.5Aul.5Ni3.0 沒變 Ag96.9Au3.0Ni0.1 沒變 Ag95.5Au3.0Nil.5 沒變 Ag94.0Au3.0Ni3.0 沒變 Ag99.8Au0.1A10.1 沒變 40NDA200104TW; P1P2000284TW 27 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） (請先閱讀背面之注意事項寫本頁) 寫夫 trA--------- 1284746 A7 B7 五、發明說明（工8)
Ag98.4AuO.lAll.5 沒變 Ag96.9Au0.1A13.0 沒變 Ag98.4Aul.5A10.1 沒變 Ag97.0Aul.5All.5 沒變 Ag95.5Aul.5A13.0 沒變 Ag96.9Au3.0A10.1 沒變 Ag95.5Au3.0All.5 沒變 Ag94.0Au3.0A13.0 沒變 Ag99.8Au0.1Nb0.1 沒變 Ag98.4AuO.lNbl.5 沒變 Ag96.9Au0.1Nb3.0 沒變 Ag98.4Aul.5Nb0.1 沒變 Ag97.0Aul.5Nbl.5 沒變 Ag95.5Aul.5Nb3.0 沒變 Ag96.9Au3.0Nb0.1 沒變 Ag95.5Au3.0Nbl.5 沒變 Ag94.0Au3.0Nb3.0 沒變 (請先閱讀背面之注意事項寫本頁) 經濟部智慧財產局員工消費合作社印製
AgRuX 表 3 (續） 材料組成分(wt%) 鹼性溶液 Ag98.0Ru2.0 許多黑色污點 Ag97.0Ru3.0 適度的黑色污點 Ag99.8Ru0.1Cu0.1 沒變 Ag99.4Ru0.5Cu0.1 沒變 Ag98.1Ru0.9Cul.0 沒變 Ag98.9Rul.0Cu0.1 沒變 Ag97.9Ru2.0Cu0.1 沒變 Ag96.9Ru3.0Cu0.1 沒變 Ag96.5Ru3.0Cu0.5 沒變 Ag94.0Ru3.0Cu3.0 沒變 Ag99.8Ru0.1Ti0.1 沒變 Ag99.4Ru0.5Ti0.1 沒變 Ag98.1Ru0.9Til.0 沒變 Ag98.9Rul.0Ti0.1 沒變 Ag97.9Ru2.0Ti0」 沒變 Ag96.9Ru3.0Ti0] 沒變 Ag96.5Ru3.0Ti0.5 沒變 Ag94.0Ru3.0Ti3.0 沒變 40NDA200104TW; P1P2000284TW 28 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1111111 ·« 1284746 A7 B7 五、發明說明（>q) 經濟部智慧財產局員工消費合作社印製
Ag99.8Ru0.1Cr0.1 沒變 Ag98.4RuO.lCrl.5 沒變 Ag96.9Ru0.1Cr3.0 沒變 Ag98.4Rul.5Cr0.1 沒變 Ag97.0Rul.5Crl.5 沒變 Ag95.5Rul .5Cr3.0 沒變 Ag96.9Ru3.0Cr0.1 沒變 Ag95.5Ru3.0Crl.5 沒變 Ag94.0Ru3.0Cr3.0 沒變 Ag98.4RuO.lTal.5 沒變 Ag96.9Ru0.1Ta3.0 沒變 Ag98.4Rul.5Ta0.1 沒變 Ag97.0Rul.5Tal.5 沒變 Ag95.5Rul.5Ta3.0 沒變 Ag96.9Ru3.0Ta0.1 沒變 Ag95.5Ru3.0Tal .5 沒變 Ag94.0Ru3.0Ta3.0 沒變 Ag99.8Ru0.1Mo0.1 沒變 Ag98.4RuO.lMol.5 沒變 Ag96.9Ru0.1Mo3.0 沒變 Ag98.4Rul.5Mo0.1 沒變 Ag97.0Rul.5Mol.5 沒變 Ag95.5Rul .5M〇3.0 沒變 Ag96.9Ru3.0Mo0.1 沒變 Ag95.5Ru3.0Mol.5 沒變 Ag94.0Ru3.0Mo3.0 沒變 Ag99.8Ru0.1Ni0.1 沒變 Ag98.4RuO.lNil.5 沒變 Ag96.9Ru0.1Ni3.0 沒變 Ag98.4Rul.5Ni0.1 沒變 Ag97.0Rul.5Nil.5 沒變 Ag95.5Rul.5Ni3.0 沒變 Ag96.9Ru3.0Ni0.1 沒變 Ag95.5Ru3.0Nil.5 沒變 Ag94.0Ru3.0Ni3.0 沒變 Ag99.8Ru0.1A10.1 沒變 Ag98.4RuO.lAll.5 沒變 Ag96.9Ru0.1A13.0 沒變 Ag98.4Rul.5A10.1 沒變 Ag97.0Rul.5All.5 沒變 Ag95.5Rul.5A13.0 沒變 40NDA200104TW: P1P2000284TW 29 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） (請先閱讀背面之注意事項寫本頁) 寫太 — — — — — — — — — 1284746 A7 〜-------B7 五、發明說明（3〇)
Ag96.9Ru3.0A10.1 沒變 Ag95.5Ru3.0All.5 沒變 Ag94.0Ru3.0A13.0 沒變 Ag99.8Ru0.1Nb0.1 沒變 Ag98.4RuO.lNbl.5 沒變 Ag96.9Ru0.1Nb3.0 沒變 Ag98.4Rul.5Nb0.1 沒變 Ag97.0Rul.5Nbl.5 沒變 Ag95.5Rul.5Nb3.0 沒變 Ag96.9Ru3.0Nb0.1 沒變 Ag95.5Ru3.0Nbl.5 沒變 Ag94.0Ru3.0Nb3.0 沒變 如表3中所示，於本發明之任何組成分的銀合金層中， 並未觀察到反射率的降低，因此，三元銀合金層比傳統層 對於鹼性溶液更加穩定，並且發明層的品質比傳統層還要 優異。 接下來，量測於500nm以及800nm的反射率，從500 到800nm的範圍（ 565nm)是液晶顯示裝置的標準光學波 長範圍。如表4所示，本發明之三元銀合金層的反射率相 較於銘、銀合金、銀、二元銀合金層，改進0.5-3.0%。 (請先閱讀背面之注意事項_ ϋ ϋ I I ϋ I ϋ^OJ·1111— I _ 本頁) •線φφ_ 經濟部智慧財產局員工消費合作社印製 表4 材料組成分（wt%) 500mm波長 800mm波長 反射率（％) 反射率（％) A1 87.2 84.5 A196.0 Mg 4.0 83.1 82.3 覆蓋有丙烯酸樹脂的鋁 79.4 76.6 Ag 98.2 98.8 Ag98.0Pd2.0 91.3 94.5 Ag97.0Pd3.0 86.9 92.1 Ag99.8 Pd 0.1 Cu 0.1 98.0 ~ 98.4 Ag99.4 Pd 0.5 Cu 0.1 98.0 98.4 Ag98.1 Pd 0.9 Cu 1.0 97.8 98.0 40NDA200104TW; P1P2000284TW 30 ^紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7 經濟部智慧財產局員工消費合作社印製
Ag98.9 Pd 1.0 Cu 0.1 94.4 97.6 Ag97.9 Pd 2.0 Cu 0.1 91.4 94.6 Ag96.9 Pd 3.0 Cu 0.1 87.5 93.4 Ag96.5 Pd 3.0 Cu0.5 87.3 92.7 Ag94.0 Pd 3.0 Cu 3.0 84.7 91.1 Ag99.8 Pd 0.1 Ti 0.1 98.0 98.6 Ag99.4 Pd 0.5 Ti 0.1 98.0 98.4 Ag98.1 Pd 0.9 Ti 1.0 97.6 97.9 Ag98.9 Pd 1.0 Ti 0.1 94.4 97.6 Ag97.9 Pd 2.0 Ti 0.1 91.4 94.6 Ag96.9 Pd 3.0 Ti 0.1 87.5 93.4 Ag96.5 Pd 3.0 Ti 0.5 87.0 92.5 Ag94.0 Pd 3.0 Ti 3.0 87.0 90.7 Ag99.8 Pd 0.1 Cr 0.1 94.6 94.7 Ag98.4 Pd 0.1 Cr 1.5 91.7 91.7 Ag96.9 Pd 0.1 Cr 3.0 89.3 89.7 Ag98.4 Pd 1.5 Cr 0.1 91.5 90.7 Ag97.0 Pd 1.5 Cr 1.5 86.8 86.8 Ag95.5 Pd 1.5 Cr 3.0 84.2 84.2 Ag96.9 Pd 3.0 Cr 0.1 85.6 85.6 Ag95.5 Pd 3.0 Cr 1.5 83.5 83.5 Ag94.0 Pd 3.0 Cr 3.0 82.7 82.7 Ag99.8 Pd 0.1 Ta 0.1 94.6 94.7 Ag98.4 Pd 0.1 Ta 1.5 91.7 91.7 Ag96.9 Pd 0.1 Ta 3.0 89.3 89.7 Ag98.4 Pd 1.5 Ta 0.1 91.5 91.7 Ag97.0 Pd 1.5 Ta 1.5 86.8 86.8 Ag95.5 Pd 1.5 Ta 3.0 84.2 84.2 Ag96.9 Pd 3.0 Ta 0.1 85.6 85.6 Ag95.5 Pd 3.0 Ta 1.5 83.5 83.5 Ag94.0 Pd 3.0 Ta 3.0 82.7 82.7 Ag99.8 Pd 0.1 Mo 0.1 94.6 94.7 Ag98.4 Pd 0.1 Mo 1.5 91.7 91.7 Ag96.9 Pd 0.1 Mo 3.0 89.3 89.7 Ag98.4 Pd 1.5 Mo 0.1 91.5 91.7 Ag97.0 Pd 1.5 Mo 1.5 86.8 86.8 Ag95.5 Pd 1.5 Mo 3.0 84.2 84.2 Ag96.9 Pd 3.0 Mo 0.1 85.6 85.6 Ag95.5 Pd 3.0 Mo 1.5 83.5 83.5 Ag94.0 Pd 3.0 Mo 3.0 82.7 82.7 Ag99.8 Pd 0.1 Ni 0.1 96.1 96.1 Ag98.4 Pd 0.1 Ni 1.5 95.6 95.6 Ag96.9 Pd 0.1 Ni 3.0 94.3 94.8 40NDA200104TW; P1P2000284TW 31 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） I i_i a— 1 .^1 I ϋ 一：OJ ϋ 1 an ei ϋ (請先閱讀背面之注意事項寫本頁) 寫太 線ΦΦ· 1284746 A7 B7 五、發明說明（31) 經濟部智慧財產局員工消費合作社印製
Ag98.4 Pd 1.5 Ni 0.1 92.7 93.7 Ag97.0 Pd 1.5 Ni 1.5 91.2 92.1 Ag95.5 Pd 1.5 Ni 3.0 88.9 90.7 Ag96.9 Pd 3.0 Ni 0.1 86.1 88.9 Ag95.5 Pd 3.0 Ni 1.5 84.6 86.2 Ag94.0 Pd 3.0 Ni 3.0 82.7 84.6 Ag99.8 Pd 0.1 A1 0.1 98.1 98.7 Ag98.4 Pd 0.1 A1 1.5 98.1 98.4 Ag96.9 Pd 0.1 A1 3.0 97.6 98.1 Ag98.4 Pd 1.5 A1 0.1 96.5 97.6 Ag97.0 Pd 1.5 A1 1.5 95.3 96.8 Ag95.5 Pd 1.5 A1 3.0 93.5 95.9 Ag96.9 Pd 3.0 A1 0.1 91 94.6 Ag95.5 Pd 3.0 A1 1.5 88.6 93 Ag94.0 Pd 3.0 A1 3.0 86.1 91.7 Ag99.8 Pd 0.1 NbO.l 95 95.3 Ag98.4 Pd 0.1 Nb 1.5 94.4 94.8 Ag96.9 Pd 0.1 Nb 3.0 93.8 94.2 Ag98.4 Pd 1.5 Nb 0.1 92.4 92.7 Ag97.0 Pd 1.5 Nb 1.5 90.8 91.4 Ag95.5 Pd 1.5 Nb 3.0 89.5 90.2 Ag96.9 Pd 3.0 Nb 0.1 86.7 87.9 Ag95.5 Pd 3.0 Nb 1.5 84.6 85.9 Ag94.0 Pd 3.0 Nb 3.0 82.7 84.7 Ag99.8 Pd 0.1 AuO.l 96.7 97.0 Ag98.4 Pd 0.1 Au 1.5 95.4 96.8 Ag96.9 Pd 0.1 Au 3.0 95.8 96.1 Ag98.4 Pd 1.5 Au 0.1 92.3 94.5 Ag97.0 Pd 1.5 Au 1.5 92.1 94.3 Ag95.5 Pd 1.5 Au 3.0 92.4 95.0 Ag96.9 Pd 3.0 Au 0.1 85.1 85.3 Ag95.5 Pd 3.0 Au 1.5 83.2 83.3 Ag94.0 Pd 3.0 Au 3.0 82.0 1 82.8 Ag99.8 Pd 0.1 AuO.l 96.6 97.1 Ag98.4 Pd 0.1 Au 1.5 96.3 96.7 Ag96.9 Pd 0.1 Au 3.0 95.8 96.1 Ag98.4 Pd 1.5 Au 0.1 92.4 94.4 Ag97.0 Pd 1.5 Au 1.5 92.1 94.3 Ag95.5 Pd 1.5 Au 3.0 92.4 95.0 Ag96.9 Pd 3.0 Au 0.1 85.1 85.3 Ag95.5 Pd 3.0 Au 1.5 83.2 83.2 Ag94.0 Pd 3.0 Au 3.0 82.0 82.8 Ag99.8 Pd 0.1 RuO.l 96.7 97.1 40NDA200104TW; P1P2000284TW 32 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） (請先閱讀背面之注意事項寫本頁) ----I---訂---------
1284746 A7 B7 五、發明說明（3¾)
Ag98.4 Pd 0.1 Ru 1.5 96.4 96.6 Ag96.9 Pd 0.1 Ru 3.0 95.8 96.5 Ag98.4 Pd 1.5 Ru 0.1 82.3 93.5 Ag97.0 Pd 1.5 Ru 1.5 92.0 94.3 Ag95.5 Pd 1.5 Ru 3.0 92.3 95.0 Ag96.9 Pd 3.0 Ru 0.1 85.0 85.3 Ag95.5 Pd 3.0 Ru 1.5 83.3 83.3 Ag94.0 Pd 3.0 Ru 3.0 82.1 82.5 經濟部智慧財產局員工消費合作社印製
AgAuX 表 4 (續） 材料組成分（wt%) 500mm波長 800mm波長 反射率（％) 反射率（％) Ag98.0 Au 2.0 87.3 92.2 Ag97.0 Au 3.0 86.1 91.3 Ag99.8 Au 0.1 Cu 0.1 98.2 98.8 Ag99.4 Au 0.5 Cu 0.1 98.1 98.5 Ag98.1 Au 0.9 Cu 1.0 97.6 98.0 Ag98.9 Au 1.0 Cu 0.1 96.5 97.6 Ag97.9 Au 2.0 Cu 0.1 95.2 96.9 Ag96.9 Au 3.0 Cu 0.1 93.7 96.1 Ag96.5 Au 3.0 Cu0.5 91.1 94.7 Ag94.0 Au 3.0 Cu 3.0 85.6 91.8 Ag99.8 Au 0.1 Ti 0.1 98.0 98.5 Ag99.4 Au 0.5 Ti 0.1 97.8 98.2 Ag98.1 Au 0.9 Ti 1.0 97.3 97.9 Ag98.9 Au 1.0 Ti 0.1 96.6 97.5 Ag97.9 Au 2.0 Ti 0.1 95.5 97.1 Ag96.9 Au 3.0 Ti 0.1 93.9 96.3 Ag96.5 Au 3.0 Ti 0.5 92.3 95.2 Ag94.0 Au 3.0 Ti 3.0 86.4 90.8 Ag99.8 Au 0.1 Cr 0.1 94.6 94.7 Ag98.4 Au 0.1 Cr 1.5 93.4 93.6 Ag96.9 Au 0.1 Cr 3.0 91.9 92.4 Ag98.4 Au 1.5 Cr 0.1 90.2 90.7 Ag97.0 Au 1.5 Cr 1.5 88.5 89.3 Ag95.5 Au 1.5 Cr 3.0 86.1 86.6 Ag96.9 Au 3.0 Cr 0.1 84.9 85.2 Ag95.5 Au 3.0 Cr 1.5 83.4 83.8 Ag94.0 Au 3.0 Cr 3.0 82.6 82.6 Ag99.8 Au 0.1 Ta 0.1 95.1 95.3 Ag98.4 Au 0.1 Ta 1.5 94.6 95.0 40NDA200104TW: P1P2000284TW 33 本紙張尺度適用中國國家標準（CNS)A4規格（210 χ 297公釐） (請先閱讀背面之注意事 ϋ I ϋ ϋ ϋ n^OJI i 1 ϋ 寫本頁) 1284746 A7 B7 五、發明說明（3+) 經濟部智慧財產局員工消費合作社印製
Ag96.9 Au 0.1 Ta 3.0 93.4 94.1 Ag98.4 Au 1.5 Ta 0.1 91.8 92.5 Ag97.0 Au 1.5 Ta 1.5 90.4 91.2 Ag95.5 Au 1.5 Ta 3.0 88.7 89.9 Ag96.9 Au 3.0 Ta 0.1 85.9 87.6 Ag95.5 Au 3.0 Ta 1.5 84.5 85.9 Ag94.0 Au 3.0 Ta 3.0 82.8 84.2 Ag99.8 Au 0.1 Mo 0.1 94.8 95.1 Ag98.4 Au 0.1 Mo 1.5 94.2 94.7 Ag96.9 Au 0.1 Mo 3.0 93.5 94.0 Ag98.4 Au 1.5 Mo 0.1 92.3 92.9 Ag97.0 Au 1.5 Mo 1.5 90.6 91.5 Ag95.5 Au 1.5 Mo 3.0 89.7 90.3 Ag96.9 Au 3.0 Mo 0.1 86.8 88.6 Ag95.5 Au 3.0 Mo 1.5 84.6 86.4 Ag94.0 Au 3.0 Mo 3.0 82.7 84.5 Ag99.8 Au 0.1 Ni 0.1 95.7 95.9 Ag98.4 Au 0.1 Ni 1.5 95.2 95.4 Ag96.9 Au 0.1 Ni 3.0 93.9 94.6 Ag98.4 Au 1.5 Ni 0.1 92.3 93.5 Ag97.0 Au 1.5 Ni 1.5 90.8 91.9 Ag95.5 Au 1.5 Ni 3.0 88.7 90.6 Ag96.9 Au 3.0 Ni 0.1 85.9 88.8 Ag95.5 Au 3.0 Ni 1.5 84.4 86.1 Ag94.0 Au 3.0 Ni 3.0 82.6 84.5 Ag99.8 Au 0.1 A1 0.1 98.0 98.6 Ag98.4 Au 0.1 A1 1.5 97.9 98.3 Ag96.9 Au 0.1 A1 3.0 97.5 98.0 Ag98.4 Au 1.5 A1 0.1 96.4 97.5 Ag97.0 Au 1.5 A1 1.5 95.2 96.7 Ag95.5 Au 1.5 A1 3.0 93.4 95.8 Ag96.9 Au 3.0 A1 0.1 90.8 94.4 Ag95.5 Au 3.0 A1 1.5 88.4 92.8 Ag94.0 Au 3.0 A1 3.0 85.9 91.5 Ag99.8 Au 0.1 NbO.l 94.8 95.1 Ag98.4 Au 0.1 Nb 1.5 94.3 94.7 Ag96.9 Au 0.1 Nb 3.0 93.5 94.1 Ag98.4 Au 1.5 Nb 0.1 92.1 92.6 Ag97.0 Au 1.5 Nb 1.5 90.5 91.3 Ag95.5 Au 1.5 Nb 3.0 89.2 90.1 Ag96.9 Au 3.0 Nb 0.1 86.4 87.8 Ag95.5 Au 3.0 Nb 1.5 87.3 85.7 Ag94.0 Au 3.0 Nb 3.0 82.4 84.5 40NDA200104TW; P1P2000284TW 34 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） (請先閱讀背面之注意事項寫本頁) t---------線4
1284746 A7 B7 五、發明說明（35) 經濟部智慧財產局員工消費合作社印製
AgRuX 表 4 (續） 材料組成分(Wt%) 500mm波長 800mm波長 反射率（％) 反射率（％) Ag98.0 Ru 2.0 86.3 91.2 Ag97.0 Ru 3.0 86.0 91.3 Ag99.8 Ru 0.1 Cu 0.1 98.1 98.8 Ag99.4 Ru 0.5 Cu 0.1 98.0 98.6 Ag98.1 Ru 0.9 Cu 1.0 97.6 98.1 Ag98.9 Ru 1.0 Cu 0.1 96.5 97.5 Ag97.9 Ru 2.0 Cu 0.1 95.2 96.8 Ag96.9 Ru 3.0 Cu 0.1 93.7 96.0 Ag96.5 Ru 3.0 Cu0.5 91.1 94.7 Ag94.0 Ru 3.0 Cu 3.0 85.6 91.7 Ag99.8 Ru 0.1 Ti 0.1 98.0 98.4 Ag99.4 Ru 0.5 Ti 0.1 97.7 98.2 Ag98.1 Ru 0.9 Ti 1.0 97.2 97.9 Ag98.9 Ru 1.0 Ti 0.1 96.5 97.5 Ag97.9 Ru 2.0 Ti 0.1 95.4 97.1 Ag96.9 Ru 3.0 Ti 0.1 93.8 96.3 Ag96.5 Ru 3.0 Ti 0.5 92.1 95.2 Ag94.0 Ru 3.0 Ti 3.0 86.4 90.8 Ag99.8 Ru 0.1 Cr 0.1 94.6 94.7 Ag98.4 Ru 0.1 Cr 1.5 93.4 92.6 Ag96.9 Ru 0.1 Cr 3.0 91.9 92.4 Ag98.4 Ru 1.5 Cr 0.1 90.5 91.7 Ag97.0 Ru 1.5 Cr 1.5 88.2 88.3 Ag95.5 Ru 1.5 Cr 3.0 86.1 86.6 Ag96.9 Ru 3.0 Cr 0.1 84.8 84.2 Ag95.5 Ru 3.0 Cr 1.5 83.3 83.8 Ag94.0 Ru 3.0 Cr 3.0 82.4 82.6 Ag99.8 Ru 0.1 Ta 0.1 95.0 95.3 Ag98.4 Ru 0.1 Ta 1.5 94.6 95.0 Ag96.9 Ru 0.1 Ta 3.0 93.4 94.1 Ag98.4 Ru 1.5 Ta 0.1 91.8 92.5 Ag97.0 Ru 1.5 Ta 1.5 90.4 91.2 Ag95.5 Ru 1.5 Ta 3.0 88.7 89.9 Ag96.9 Ru 3.0 Ta 0.1 85.9 87.6 Ag95.5 Ru 3.0 Ta 1.5 84.5 85.9 Ag94.0 Ru 3.0 Ta 3.0 82.6 84.2 Ag99.8 Ru 0.1 Mo 0.1 94.7 95.1 40NDA200104TW; P1P2000284TW 35 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） --------訂---------線氣 (請先閱讀背面之注意事項寫本頁)
1284746 A7 B7 五、發明說明UL)
Ag98.4 Ru 0.1 Mo 1.5 94.1 94.7 Ag96.9 Ru 0.1 Mo 3.0 93.3 94.0 Ag98.4 Ru 1.5 Mo 0.1 92.2 92.9 Ag97.0 Ru 1.5 Mo 1.5 90.5 91.5 Ag95.5 Ru 1.5 Mo 3.0 89.9 91.3 Ag96.9 Ru 3.0 Mo 0.1 86.8 88.6 Ag95.5 Ru 3.0 Mo 1.5 84.8 86.3 Ag94.0 Ru 3.0 Mo 3.0 82.6 84.5 Ag99.8 Ru 0.1 Ni 0.1 96.7 97.2 Ag98.4 Ru 0.1 Ni 1.5 96.5 96.9 Ag96.9 Ru 0.1 Ni 3.0 96.1 96.3 Ag98.4 Ru 1.5 Ni 0.1 95.3 95.8 Ag97.0 Ru 1.5 Ni 1.5 93.7 94.7 Ag95.5 Ru 1.5 Ni 3.0 91.2 93.3 Ag96.9 Ru 3.0 Ni 0.1 88.4 91.7 Ag95.5 Ru 3.0 Ni 1.5 85.0 87.2 Ag94.0 Ru 3.0 Ni 3.0 83.5 85.6 Ag99.8 Ru 0.1 A1 0.1 98.0 98.4 Ag98.4 Ru 0.1 A1 1.5 97.9 98.2 Ag96.9 Ru 0.1 A1 3.0 97.5 98.1 Ag98.4 Ru 1.5 A1 0.1 96.4 97.5 Ag97.0 Ru 1.5 A1 1.5 95.2 96.5 Ag95.5 Ru 1.5 A1 3.0 93.4 95.8 Ag96.9 Ru 3.0 A1 0.1 90.8 94.4 Ag95.5 Ru 3.0 A1 1.5 88.4 92.7 Ag94.0 Ru 3.0 A1 3.0 85.4 91.5 Ag99.8 Ru 0.1 NbO.l 94.7 95.2 Ag98.4 Ru 0.1 Nb 1.5 94.3 94.7 Ag96.9 Ru 0.1 Nb 3.0 93.4 94.1 Ag98.4 Ru 1.5 Nb 0.1 92.1 92.5 Ag97.0 Ru 1.5 Nb 1.5 90.2 91.3 Ag95.5 Ru 1.5 Nb 3.0 88.1 90.0 Ag96.9 Ru 3.0 Nb 0.1 85.2 87.8 Ag95.5 Ru 3.0 Nb 1.5 84.1 85.7 Ag94.0 Ru 3.0 Nb 3.0 82.4 84.5 (請先閱讀背面之注意事項 寫本頁) ^---------麓
經濟部智慧財產局員工消費合作社印製 因此，可見本發明的銀合金層非常適合用於反射型液 晶顯示裝置的反射體或反射性接線電極。 40NDA200104TW; P1P2000284TW 36 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7 五、發明説明（说） 條件下對抗樹脂基底的化學穩定度。 爲了要證實本發明三元反射層的化學穩定性，藉由三 元同時濺鍍沉積15nm厚之反射層於PMMA、PET、PC、 矽氧烷樹脂以及相類似的樹脂層上。這些層於高溫與高溼 度情況下保持24小時。檢查外觀與反射特性隨著時間的變 化。 表5 材料組成分 (wt%) 高溫與高溼度測試結果 化學特性的變化 (反射率降低） 視覺變化成模糊 白色，與基底剝離 Ag98.0 Pd 2.0 許多黑色污點 發生剝離 Ag97.0 Pd 3.0 適度的黑色污點 發生剝離 Ag99.8 Pd 0.1 Cu 0.1 沒 變 些許顏色變化 Ag99.4 Pd 0.5 Cu 0.1 沒 變 沒 愛 Ag98.1 Pd 0.9 Cu 1.0 沒 變 沒 變 Ag98.9 Pd 1.0 Cu 0.1 沒 變 沒 變 Ag97.9 Pd 2.0 Cu 0.1 沒 變 沒變 Ag96.9 Pd 3.0 Cu 0.1 沒 變 沒 Ag96.5 Pd 3.0 Cu0.5 沒 變 沒 變 Ag94.0 Pd 3.0 Cu 3.0 沒 變 沒 變 Ag99.8 Pd 0.1 Ti 0.1 沒 變 沒 變 Ag99.4 Pd 0.5 Ti 0.1 沒 變 沒 變 Ag98.1 Pd 0.9 Ti 1.0 沒 變 沒 變 Ag98.9 Pd 1.0 Ti 0.1 沒 變 沒 變 Ag97.9 Pd 2.0 Ti 0.1 沒 變 沒 變 Ag96.9 Pd 3.0 Ti 0.1 沒 變 沒 變 Ag96.5 Pd 3.0 Ti 0.5 沒 變 沒 變 Ag94.0 Pd 3.0 Ti 3.0 沒 變 沒 變 Ag99.8 Pd 0.1 Au 0.1 沒 變 沒 變 Ag98.4 Pd 0.1 Au 1.5 沒 變 沒 變 Ag96.9 Pd 0.1 Au 3.0 沒 變 沒 變 Ag98.4 Pd 1.5 Au 0.1 沒 變 沒 變 Ag97.0 Pd 1.5 Au 1.5 沒變 沒 變 Ag95.5 Pd 1.5 Au 3.0 沒 變 沒 變 40NDA200104TW; P1P2000284TW 38 本紙張尺度適用中國國家標準（CNS ) A4規格（210X297公釐） (請先閱讀背面之注意事項馬本頁)
經濟部智慧財產局員工消費合作社印製 1284746 A7 _B7 五、發明說明（Μ) 經濟部智慧財產局員工消費合作社印製
Ag96.9 Pd 3.0 Au 0.1 沒 變 沒 變 Ag95.5 Pd 3.0 Au 1.5 沒 變 沒 變 Ag94.0 Pd 3.0 Au 3.0 沒 變 沒 變 Ag99.8 Pd 0.1 Cr 0.1 沒 變 沒 變 Ag98.4 Pd 0.1 Cr 1.5 沒 變 沒 變 Ag96.9 Pd 0.1 Cr 3.0 沒 變 沒 變 Ag98.4 Pd 1.5 Cr 0.1 沒 變 沒 變 Ag97.0 Pd 1.5 Cr 1.5 沒 變 沒 變 Ag95.5 Pd 1.5 Cr 3.0 沒 變 沒 變 Ag96.9 Pd 3.0 Cr 0.1 沒 變 沒 變 Ag95.5 Pd 3.0 Cr 1.5 沒 變 沒 變 Ag94.0 Pd 3.0 Cr 3.0 沒 變 沒 變 Ag99.8 Pd 0.1 Ta 0.1 沒 變 沒 變 Ag98.4 Pd 0.1 Ta 1.5 沒 變 沒 變 Ag96.9 Pd 0.1 Ta 3.0 沒 變 沒 變 Ag98.4 Pd 1.5 Ta 0.1 沒 變 沒 變 Ag97.0 Pd 1.5 Ta 1.5 沒 變 沒 變 Ag95.5 Pd 1.5 Ta 3.0 沒 變 沒 變 Ag96.9 Pd 3.0 Ta 0.1 沒 變 沒 變 Ag95.5 Pd 3.0 Ta 1.5 沒 變 沒 變 Ag94.0 Pd 3.0 Ta 3.0 沒 變 沒 變 Ag99.8 Pd 0.1 Mo 0.1 沒 變 沒 變 Ag98.4 Pd 0.1 Mo 1.5 沒 沒 變 Ag96.9 Pd 0.1 Mo 3.0 沒 變 沒 變 Ag98.4 Pd 1.5 Mo 0.1 沒 變 沒· 變 Ag97.0 Pd 1.5 Mo 1.5 沒 變 沒 變 Ag95.5 Pd 1.5 Mo 3.0 沒 變 沒 變 Ag96.9 Pd 3.0 Mo 0.1 沒 變 沒 變 Ag95.5 Pd 3.0 Mo 1.5 沒 變 沒 變 Ag94.0 Pd 3.0 Mo 3.0 沒 變 沒 變 Ag99.8 Pd 0.1 Ni 0.1 沒 變 沒 變 Ag98.4 Pd 0.1 Ni 1.5 沒 變 沒 變 Ag96.9 Pd 0.1 Ni 3.0 沒 變 沒 變 Ag98.4 Pd 1.5 Ni 0.1 沒 變 沒 變 Ag97.0 Pd 1.5 Ni 1.5 沒 變 沒 變 Ag95.5 Pd 1.5 Ni 3.0 沒 變 沒 變 Ag96.9 Pd 3.0 Ni 0.1 沒 變 沒 變 Ag95.5 Pd 3.0 Ni 1.5 沒 變 沒 變 Ag94.0 Pd 3.0 Ni 3.0 沒 變 沒 變 Ag99.8 Pd 0.1 A1 0.1 沒 變 沒 變 Ag98.4 Pd 0.1 A1 1.5 沒 變 沒 變 40NDA200104TW; P1P2000284TW 39 · 1· ·1 II ^1 I ϋ ϋ 一 0、I i^i ^1- in Hi «^1 ϋ I (請先閱讀背面之注意事項再填寫本頁)
f 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 經濟部智慧財產局員工消費合作社印製 A7 B7 五、發明說明（4〇 )
Ag96.9 Pd 0.1 A1 3.0 沒 變 沒 變 Ag98.4 Pd 1.5 A1 0.1 沒 變 沒 變 Ag97.0 Pd 1.5 A1 1.5 沒 變 沒 變 Ag95.5 Pd 1.5 A1 3.0 沒 變 沒 變 Ag96.9 Pd 3.0 A1 0.1 沒 變 沒 變 Ag95.5 Pd 3.0 A1 1.5 沒 沒 變 Ag94.0 Pd 3.0 A1 3.0 沒 變 沒 變 Ag99.8 Pd 0.1 NbO.l 沒 變 沒 變 Ag98.4 Pd 0.1 Nb 1.5 沒 變 沒 變 Ag96.9 Pd 0.1 Nb 3.0 沒 變 沒 變 Ag98.4 Pd 1.5 Nb 0.1 沒 變 沒 變 Ag97.0 Pd 1.5 Nb 1.5 沒 變 沒 變 Ag95.5 Pd 1.5 Nb 3.0 沒 變 沒 變 Ag96.9 Pd 3.0 Nb 0.1 沒 變 沒 變 Ag95.5 Pd 3.0 Nb 1.5 沒 變 沒 變 Ag94.0 Pd 3.0 Nb 3.0 沒 變 沒 變 Ag99.8 Ru 0.1 Au 0.1 沒 變 沒 變 Ag98.4 Ru 0.1 Au 1.5 沒 變 沒 變 Ag96.9 Ru 0.1 Au 3.0 沒 變 沒 變 Ag98.4 Ru 1.5 Au 0.1 沒 變 沒 變 Ag97.0 Ru 1.5 Au 1.5 沒 變 沒 變 Ag95.5 Ru 1.5 Au 3.0 沒 變 沒 變 Ag96.9 Ru 3.0 Au 0.1 沒 變 沒 變 Ag95.5 Ru 3.0 Au 1.5 沒 變 沒 變 Ag94.0 Ru 3.0 Au 3.0 沒 變 沒 變 Ag99.8 Pd 0.1 Ru 0.1 沒 變 沒 變 Ag98.4 Pd 0.1 Ru 1.5 沒 變 沒 變 Ag96.9 Pd 0.1 Ru 3.0 沒 變 沒 變 Ag98.4 Pd 1.5 Ru 0.1 沒 變 沒 變 Ag97.0 Pd 1.5 Ru 1.5 沒 變 沒 變 Ag95.5 Pd 1.5 Ru 3.0 沒 變 沒 變 Ag96.9 Pd 3.0 Ru 0.1 沒 變 沒 變 Ag95.5 Pd 3.0 Ru 1.5 沒 變 沒 變 Ag94.0 Pd 3.0 Ru 3.0 沒 變 沒 變 40NDA200104TW; P1P2000284TW 40 镳 μ·· ΜΗ xav 一·口，a n ϋ ϋ ϋ -^1 ϋ I (請先閱讀背面之注意事填寫本頁) f填 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 經濟部智慧財產局員工消費合作社印製 1284746 A7 _B7 五、發明說明（4A)
AgAuX 表 5 (續） 材料組成分 (wt%) 高溫與高溼度測試結果 化學特性的變化 (反射率降低） 化學特性的變 化（反射率降 低） Ag98.0 Au 2.0 許多黑色污點 發生剝離 Ag97.0 Au 3.0 適度的黑色污點 發生剝離 Ag99.8 Au 0.1 Cu 0.1 沒 變 沒 變 Ag99.4 Au 0.5 Cu 0.1 沒 變 沒 變 Ag98.1 Au 0.9 Cu 1.0 沒 變 沒 變 Ag98.9 Au 1.0 Cu 0.1 沒 變 沒 變 Ag97.9 Au 2.0 Cu 0.1 沒 變 沒 變 Ag96.9 Au 3.0 Cu 0.1 沒 變 沒 變 Ag96.5 Au 3.0 Cu0.5 沒 變 沒 變 Ag94.0 Au 3.0 Cu 3.0 沒 變 沒 變 Ag99.8 Au 0.1 Ti 0.1 沒 變 沒 變 Ag99.4 Au 0.5 Ti 0.1 沒 變 沒 變 Ag98.1 Au 0.9 Ti 1.0 沒 變 沒 變 Ag98.9 Au 1.0 Ti 0.1 沒 變 沒 變 Ag97.9 Au 2.0 Ti 0.1 沒 變 沒 變 Ag96.9 Au 3.0 Ti 0.1 沒 變 沒 變 Ag96.5 Au 3.0 Ti 0.5 沒 變 沒 變 Ag94.0 Au 3.0 Ti 3.0 沒 變 沒 變 Ag99.8 Au 0.1 Cr 0.1 沒 變 沒 變 Ag98.4 Au 0.1 Cr 1.5 沒 變 沒 變 Ag96.9 Au 0.1 Cr 3.0 沒 變 沒 變 Ag98.4 Au 1.5 Cr 0.1 沒 變 沒 變 Ag97.0 Au 1.5 Cr 1.5 沒 變 沒 變 Ag95.5 Au 1.5 Cr 3.0 沒 變 沒 變 Ag96.9 Au 3.0 Cr 0.1 沒 變 沒 變 Ag95.5 Au 3.0 Cr 1.5 沒 變 沒 變 Ag94.0 Au 3.0 Cr 3.0 沒 變 沒 變 Ag99.8 Au 0.1 Ta 0.1 沒 變 沒 變 Ag98.4 Au 0.1 Ta 1.5 沒 變 沒 變 Ag96.9 Au 0.1 Ta 3.0 沒 變 沒 變 Ag98.4 Au 1.5 Ta 0.1 沒 變 沒 變 Ag97.0 Au 1.5 Ta 1.5 沒 變 沒 變 Ag95.5 Au 1.5 Ta 3.0 沒 變 沒 變 Ag96.9 Au 3.0 Ta 0.1 沒 變 沒 變 Ag95.5 Au 3.0 Ta 1.5 沒 變 沒 變 40NDA200104TW; P1P2000284TW 41 I 1 1 H 1 一一口、I n 1 ϋ ϋ 1 ϋ ϋ I (請先閱讀背面之注意事項再填寫本頁)
鵠 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 經濟部智慧財產局員工消費合作社印製 A7 B7 五、發明說明（4¾
Ag94.0 Au 3.0 Ta 3.0 沒 變 沒 變 Ag99.8 Au 0.1 Mo 0.1 沒 變 沒 變 Ag98.4 Au 0.1 Mo 1.5 沒 變 沒 變 Ag96.9 Au 0.1 Mo 3.0 沒 變 沒 變 Ag98.4 Au 1.5 Mo 0.1 沒 變 沒 變 Ag97.0 Au 1.5 Mo 1.5 沒 變 沒 變 Ag95.5 Au 1.5 Mo 3.0 沒 變 沒 變 Ag96.9 Au 3.0 Mo 0.1 沒 變 沒 變 Ag95.5 Au 3.0 Mo 1.5 沒 變 沒 變 Ag94.0 Au 3.0 Mo 3.0 沒 變 沒 變 Ag99.8 Au 0.1 Ni 0.1 沒 變 沒 變 Ag98.4 Au 0.1 Ni 1.5 沒 變 沒 變 Ag96.9 Au 0.1 Ni 3.0 沒 變 沒 變 Ag98.4 Au 1.5 Ni 0.1 沒 變 沒 變 Ag97.0 Au 1.5 Ni 1.5 沒 變 沒 變 Ag95.5 Au 1.5 Ni 3.0 沒 變 沒 變 Ag96.9 Au 3.0 Ni 0.1 沒 變 沒 變 Ag95.5 Au 3.0 Ni 1.5 沒 變 沒 變 Ag94.0 Au 3.0 Ni 3.0 沒 變 沒 變 Ag99.8 Au 0.1 A1 0.1 沒 變 沒 變 Ag98.4 Au 0.1 A1 1.5 沒 變 沒 變 Ag96.9 Au 0.1 A1 3.0 沒 變 沒 變 Ag98.4 Au 1.5 A1 0.1 沒 變 沒 變 Ag97.0 Au 1.5 A1 1.5 沒 變 沒 變 Ag95.5 Au 1.5 A1 3.0 沒 變 沒 變 Ag96.9 Au 3.0 A1 0.1 沒 變 沒 變 Ag95.5 Au 3.0 A1 1.5 沒 變 沒 變 Ag94.0 Au 3.0 A1 3.0 沒 變 沒 變 Ag99.8 Au 0.1 NbO.l 沒 變 沒 變 Ag98.4 Au 0.1 Nb 1.5 沒 變 沒 變 Ag96.9 Au 0.1 Nb 3.0 沒 變 沒 變 Ag98.4 Au 1.5 Nb 0.1 沒 變 沒 變 Ag97.0 Au 1.5 Nb 1.5 沒 變 沒 變 Ag95.5 Au 1.5 Nb 3.0 沒 變 沒 變 Ag96.9 Au 3.0 Nb 0.1 沒 變 沒 變 Ag95.5 Au 3.0 Nb 1.5 沒 變 沒 變 Ag94.0 Au 3.0 Nb 3.0 沒 變 沒 變 40NDA200104TW: P1P2000284TW 42 ;- I- ϋ ϋ ϋ ϋ ϋ ϋ^OJI n ϋ I» ϋ ^1 i-i I (請先閱讀背面之注意事^:填寫本頁)
PI 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7 五、發明說明（^3)
AgRuX 表 5 (續） 經濟部智慧財產局員工消費合作社印制衣 材料組成分 (wt%) 高溫與高溼度測試結果 化學特性的變化 (反射率降低） 化學特性的變 化（反射率降 低） Ag98.0 Ru 2.0 許多黑色污點 發生剝離 Ag97.0 Ru 3.0 適度的黑色污點 發生剝離 Ag99.8 Ru 0.1 Cu 0.1 沒 變 沒 變 Ag99.4 Ru 0.5 Cu 0.1 沒 變 沒 變 Ag98.1 Ru 0.9 Cu 1.0 沒 變 沒 變 Ag98.9 Ru 1.0 Cu 0.1 沒 變 沒 變 Ag97.9 Ru 2.0 Cu 0.1 沒 變 沒 變 Ag96.9 Ru 3.0 Cu 0.1 沒 變 沒 變 Ag96.5 Ru 3.0 Cu0.5 沒 變 沒 變 Ag94.0 Ru 3.0 Cu 3.0 沒 變 沒 變 Ag99.8 Ru 0.1 Ti 0.1 沒 變 沒 Μ Ag99.4 Ru 0.5 Ti 0.1 沒 變 沒 變 Ag98.1 Ru 0.9 Ti 1.0 沒 變 沒 變 Ag98.9 Ru 1.0 Ti 0.1 沒 變 沒 變 Ag97.9 Ru 2.0 Ti 0.1 沒 變 沒 變 Ag96.9 Ru 3.0 Ti 0.1 沒 變 沒 變 Ag96.5 Ru 3.0 Ti 0.5 沒 變 沒 變 Ag94.0 Ru 3.0 Ti 3.0 沒 變 沒 變 Ag99.8 Ru 0.1 Cr 0.1 沒 變 沒 變 Ag98.4 Ru 0.1 Cr 1.5 沒 變 沒 變 Ag96.9 Ru 0.1 Cr 3.0 沒 變 沒 變 Ag98.4 Ru 1.5 Cr 0.1 沒 變 沒 變 Ag97.0 Ru 1.5 Cr 1.5 沒 變 沒 變 Ag95.5 Ru 1.5 Cr 3.0 沒 變 沒 變 Ag96.9 Ru 3.0 Cr 0.1 沒 變 沒 變 Ag95.5 Ru 3.0 Cr 1.5 沒 變 沒 變 Ag94.0 Ru 3.0 Cr 3.0 沒 變 沒 變 Ag99.8 Ru 0.1 Ta 0.1 沒 變 沒 變 Ag98.4 Ru 0.1 Ta 1.5 沒 變 沒 變 Ag96.9 Rd 0.1 Ta 3.0 沒 變 沒 變 Ag98.4 Ru 1.5 Ta 0.1 沒 變 沒 變 Ag97.0 Ru 1.5 Ta 1.5 沒 變 沒 變 Ag95.5 Ru 1.5 Ta 3.0 沒 變 沒 變 Ag96.9 Ru 3.0 Ta 0.1 沒 變 沒 變 Ag95.5 Ru 3.0 Ta 1.5 沒 變 沒 變 40NDA200104TW; P1P2000284TW 43 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） · ϋ ϋ ϋ ϋ ϋ i^i ϋ 0、I ϋ ϋ ϋ n Βϋ >ϋ ϋ I (請先閱讀背面之注意事項再填寫本頁) β 1284746 經濟部智慧財產局員工消費合作社印製 A7 B7
五、發明說明（AAO
Ag94.0 Ru 3.0 Ta 3.0 沒 變 沒 變 Ag99.8 Ru 0.1 Mo 0.1 沒 變 沒 變 Ag98.4 Ru 0.1 Mo 1.5 沒 變 沒 變 Ag96.9 Ru 0.1 Mo 3.0 沒 變 沒 變 Ag98.4 Ru 1.5 Mo 0.1 沒 變 沒 變 Ag97.0 Ru 1.5 Mo 1.5 沒 變 沒 變 Ag95.5 Ru 1.5 Mo 3.0 沒 變 沒 變 Ag96.9 Ru 3.0 Mo 0.1 沒 變 沒 變 Ag95.5 Ru 3.0 Mo 1.5 沒 變 沒 變 Ag94.0 Ru 3.0 Mo 3.0 沒 變 沒 變 Ag99.8 Ru 0.1 Ni 0.1 沒 變 沒 變 Ag98.4 Ru 0.1 Ni 1.5 沒 變 沒 變 Ag96.9 Ru 0.1 Ni 3.0 沒 變 沒 變 Ag98.4 Ru 1.5 Ni 0.1 沒 變 沒 變 Ag97.0 Ru 1.5 Ni 1.5 沒 變 沒 變 Ag95.5 Ru 1.5 Ni 3.0 沒 變 沒 變 Ag96.9 Ru 3.0 Ni 0.1 沒 變 沒 變 Ag95.5 Ru 3.0 Ni 1.5 沒 變 沒 變 Ag94.0 Ru 3.0 Ni 3.0 沒 變 沒 變 Ag99.8 Ru 0.1 A1 0.1 沒 變 沒 變 Ag98.4 Ru 0.1 A1 1.5 沒 變 沒 變 Ag96.9 Ru 0.1 A1 3.0 沒 變 沒 變 Ag98.4 Ru 1.5 A1 0.1 沒 變 沒 變 Ag97.0 Ru 1.5 A1 1.5 沒 變 沒 變 Ag95.5 Ru 1.5 A1 3.0 沒 變 沒 變 Ag96.9 Ru 3.0 A1 0.1 沒 變 沒 變 Ag95.5 Ru 3.0 A1 1.5 沒 變 沒 變 Ag94.0 Ru 3.0 A1 3.0 沒 變 沒 變 Ag99.8 Ru 0.1 NbO.l 沒 變 沒 變 Ag98.4 Ru 0.1 Nb 1.5 沒 變 沒 變 Ag96.9 Rd 0.1 Nb 3.0 沒 變 沒 變 Ag98.4 Ru 1.5 Nb 0.1 沒 變 沒 變 Ag97.0 Ru 1.5 Nb 1.5 沒 變 沒 變 Ag95.5 Ru 1.5 Nb 3.0 沒 變 沒 變 Ag96.9 Ru 3.0 Nb 0.1 沒 變 沒 變 Ag95.5 Ru 3.0 Nb 1.5 沒 變 沒 變 Ag94.0 Ru 3.0 Nb 3.0 沒 變 沒 變 40NDA200104TW: P1P2000284TW 44 t------ (請先閱讀背面之注意事W:填寫本頁) ·11111111 f 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7 五 經濟部智慧財產局員工消費合作社印製 發明說明（+5) 如表5所示，經過24小時候三元銀合金反射層未觀察 到任變化。當位於各種樹脂基底上之三元反射層的反射率 使用分光光度計予以測量時，未觀察到反射率在565nm波 長降低，對於反射型液晶顯示裝置是有用的；未觀察到反 射率在400nm至4//m之間降低，這對於建築玻璃而言是 必須的（未顯示資料）。 本發明的三元反射層證明具有高化學穩定性對抗樹 脂，並且不像傳統層，並不限定於特定的基底材料。 實施例4 檢查本發明三元反射層與各種基底之間的接著性，以 及基膜，其係置於反射層與基底之間，對於接著的效果。 首先，反射層藉由無線電頻率濺鍍直接沉積到 PMMA、PET、PC、矽氧烷樹脂、丙烯酸樹脂、非鹼性玻 璃、低鹼性玻璃、硼矽玻璃、以及石英玻璃基底上，以形 成一層積體。貼附一日本工業標準玻璃紙膠帶到反射層。 觀察當膠帶於給定的張力撕開時，反射層從基底的剝離。 另外，層積體以切刀切割成小塊並且浸於燒杯中的純水 內，施加超音波到純水，超音波的頻率爲50kHz且電功率 爲100W。當使用超音波後，於40倍的顯微鏡下觀察反射 層的剝離，並且檢查基膜的必要性。 40NDA200104TW: P1P2000284TW 45 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 裝------ (請先閱讀背面之注意事^5:填寫本頁) f填 11111111 f 經濟部智慧財產局員工消費合作社印製 1284746 Α7 Β7 五、發明說明（β) 表7 材料 波長 565.00 nm .波長^ 450.00 nm 波長 500.00 nm 波長· 550.00 nm :'波長· 565.00 nm 反射率(％) 反射率(％) 反射率(％) 反射率(％) 反射率(％) _純Ag 94.80 96.60 97.70 97.90 98.00 AgPd 92.30 94.05 95.12 95.32 95.42 AgPdCu 91.50 92.40 93.60 94.10 93.36 A^PdTi - 88.90 90.59 91.62 91.81 91.90 A^PdCr 88.40 90.08 91.11 91.29 91.38 A^PdTa 88.30 89.98 91.00 91.19 91.28 A^PdMo 88.00 89.67 90.69 90.88 90.97 A^PdNi 88.20 89.77 90.89 90.98 91.17 A^PdAl 88.90 90.49 91.61 91.70 91.79 A^PdNb 88.80 90.38 91.51 91.60 91.79 AgAu 92.80 94.56 95.64 95.83 95.93 A^AuCu 92.46 94.22 95.29 95.48 95.58 A^AuTi 88.44 ^ 90.12 91.15 91.33 91.43 A^AuCr 88.56 90.24 91.27 91.46 91.55 AgAuTa 88.30 89.98 91.00 91.19 91.28 A^AuNi 88.00 89.67 90.69 90.88 90.97 AgAuMo 88.10 89.77 90.80 90.98 91.07 A^AuPd 89.00 90.69 91.72 91.91 92.00 AgAuAl 88.70 , 90.39 91.41 91.60 91.69 A^AuNb 88.60 90.28 91.31 91.50 91.59 AgRu 89.00 90.69 91.72 91.91 92.00 AgRuCu , ,88.45 90.13 91.16 91.34 91.44 AgRuTi / 88.34 90.02 91.04 91.23 91.32 AgRuCr 88.76 90.45 91.48 91.66 91.76 AgRuTa 88.23 89.91 90.93 91.12 91.21 AgRuNi 87.80 89.47 90.49 90.67 90.76 A^RuMo 88.44 90.12 91.15 91.33 91.43 AgRuPd •87.67 89.34 90.35 90.54 f 90.63 AgRuAl 88.97 90.66 91.69 91.88 ! 91.97 AgRuNb 87.9S 89.65 90.67 90.86 90.95 40NDA200104TW; P1P2000284TW 48 裝I (請先閱讀背面之注意事填寫本頁) 11111111 f 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7 五、發明說明（4^) 特別地，二氧化鈦、五氧化二鉅、二氧化鉻、三氧化 二銦、二氧化錫、五氧化二鈮、以及氧化鎂基膜具有高反 射率以及低吸收率，如表8中的三氧化二銦-五氧化二鈮所 代表的。根據折射率的光學特性變化於這些膜中被防止了。 表8 I - . · ' Ιη203· 15wt%Nb2 ΙΠ·2〇3· 12.5\vt%Nb2 〇, I Π·2〇3· 10wt%Nb2 0, Ιϋ2〇3· 7.5wt%Nb, 0, Ιη203· 5wt%Nb205 反射率 •反射率 反射率 <反射率. 反射率 40 0 2.34 2.32 2.34 2.30 2.34 45 0 2.26 2.25 2.26 2:23 2.26 50 .0 2.22 2.21 2.21 2.18 2.20 55 0 2.19 2.18 2.18 2.16 2.17 56 0 2.19 2.18 2.17- 2.15 2.17 .^1 ϋ 1 1 Βϋ 1 一一0、 i-i ϋ n (請先閱讀背面之注音3事填寫本頁) 經濟部智慧財產局員工消費合作社印製 實施例5 I 檢查覆蓋層對於反射層之耐熱性以及反射率的效應。 於傳統銀反射層（純銀或二元銀合金）或者本發明三元反 射層上，沉積一覆蓋層，其包括三氧化二銦做爲主要成分 以及二氧化錫、五氧化二鈮、二氧化錫、氧化鎂以及五氧 化二鉅的至少其中之一，以形成一層積體。層積體於250 °C進行回火，其係液晶顯示裝置製造過程中施加到基底的 溫度。 40NDA200104TW; P1P2000284TW , 1 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7 五、發明說明（s〇) 在沒有覆蓋層的情況下，反射層的光學吸收率於回火 後增加，其導致層的劣質化，如表9所示。覆蓋層被用以 耐熱的光學吸收率實驗資料顯示於表10至12。 經濟部智慧財產局員工消費合作社印製 沒有覆蓋層 材料 回火 as-depo 波長 波長 波長 波長 波長 •波長 波長 波長 波長 波長 400.00 450.00 500.00 550.00 565.00 400.00 450.00 500.00 550.00 565.00 nm nm nm nm nm nm nm nm nm nm 吸收率 吸收率 吸收率ί吸收率 吸收率 吸收率 吸收率 口 1收率 吸收率 吸收率 (%) (%) (%) 1 (%) (%) (%) (%) (%) (%) (%) pure Ag 5.2 3.6 2.8 2.8 1.9 5 3.2 2.1 2.6 1.8 Ag?d 6.4 5.5 6.3 5.5 5.1 6.0 5.2 6.1 5.4 5.0 A^PdCu 6.6 5.7 6.5 5.8 5.5 6.5 5.6 6.2 5.7 5.1 A^PdTi 6.9 5.9 6.6 5.7 5.5 6.7 5.8 6.4 5.6 5.3 AgPdCr 6.8 5.9 6.5 5.7 5.3 6.6 5.8 6.3 5.5 5.0 AgPdTa 6.6 5.8 6.6 5.8 5.3 6.4 5.5 6.3 5.6 5.0 AgPdMo 6.8 6.9 6.4 5.5 5.5 6.6 6.7 6.3 5.5 5.2 AgPdNi 6.7 5.7 6.2 5.5 5.4 6.4 5.7 5.9 5.5 5.1 AgPdAl 6.6 6.6 6.4 5.5 5.2 6.5 6.5 6.2 5.5 5.1 AgPdNb 6.7 5.8 6.3 5.7 5.1 6.5 5.7 6.3 5.4 4.9 AgAu 6.3 5.3 6.2 5.3 5.0 6.0 5.1 6.0 5.2 5.0 AgAuCu 7.4 6.7 7.2 6.2 6.2 7.1 6.5 7.0 6.1 6.0 AgAuTi 6.6 5.8 6.4 5.7 5.3 6.4 5.2 6.3 5.6 5.2 AgAuCr 6.8 5.9 6.6 •5.8 5.5 6.7 5.8 6.4 5.6 5.3 AgAuTa 6.9 5.9 6.5 5.7 5.3 6.6 5.8 6.3 5.6 5.2 AgAuNi 6.8 5.9 6.3 5.7 5.4 6.5 5.8 6.1 5.6 5.2 AgAuMo 6.7 6.8 6.4 5.6 5.4 6.6 6.7 6.3 5.5 5.2 AgAuPd 7.5 6.3 7.5 6.3 6.2 7.1 6.1 7.0 6.2 6.0 AgAuAl 6.7 6.7 6.5 5.6 5.4 6.6 6.5 6.3 5.5 5.2 AgAuNb 6.8 5.9 6.4 5.7 5.2 6.6 5.8 6.3 5.5 5.0 AgRu 6.3 5.4 6.2 5.3 5.2 6.1 5.1 6.0 5.3 5.1 AgRuCu 6.8 5.9 6.4 5.7 5.2 6.4 5.5 6.3 5.6 5.0 AgRuTi 6.7 5.9 6.5 5.6 5.2 6.6 5.8 6.3 5.5 5.0 AgRuCr 6.7 5.9 6.6 5.7 5.3 6.5 5.7 6.3 5.5 5.0 AgRuTa 6.5 5.8 · 6.7 5.7 5.2 6.4 5.5 6.3 5.6 5.0 . AgRuNi 7.3 ,6.6 7.5 6.3 6.3 7.1 6.4 7.0 6.1 6.0 AgRuMo 7.3 6.8 7.3 6.2 6.2 7.1 6.3 7.1 6.1 6.0 AgRuPd 6.7 6.8 6.4 5.5 5.3 6.6 6.6 6.2 5.4 5.2 AgRuAl 6.8 6.9 6.4 5.6 5.3 6.6 6.7 6.3 5.5 5.2 AgRuNb 6.8 6.9 6.3 5.6 5.4 6.5 6.6 6.1 5.5 5.2 40NDA200104TW; P1P2000284TW 50 裝------- (請先閱讀背面之注意事¾再填寫本頁) — — — — — — — — — 鳟 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7
五、發明說明（sU 表10
Si〇9/Ag合金 經濟部智慧財產局員工消費合作社印製 材料 Si(X回火 SiO·； as*depo 波長 400.00 nm 波長 450.00 nm 波長 500.00 nm 波長 550.00 nm 波長 565.00 nm 波長 400.00 nm 波長 450.00 nm 波長 500.00 nm 波長 550.00 nm 波長 565.00 nm 吸收率 (%) 吸收率 (%) 吸收率 (%) 吸收率 (%) 吸收率 (%) 吸收率 (%): 吸收率 (%) 吸收率 (%) 吸收率 (%) 吸收率 (%) pure Ag 26.5 11.65 4.92 4.72 5.02 34.5 16.64 5.81 5.71 5.05 A^Pd 26.8 12.59 5.68 5.23 6.96 27.8 14.59 8.68 6.23 8.98 A^PdCu 27.09 13.06 8.94 6.77 6.28 35.8 18.64 11.91 8.74 8.Q5 A^PdTi 36.5 17.54 11.45 8.58 7.59 36.8 17.68 11.85 8.76 8.00 A^PdCr 35.5 18.45 10.59 8.58 7.96 35.9 18.65 10.69 8.75 8.04 A^PdTa 36.1 18.44 11.34 8.50 7.58 36.2 18.54 11.54 8.54 8.02 A^PdMo 36.4 18.57 11.15 8.41 7.21 36.5 18.67 11.59 8.45 7.25 A^PdNi 35.78 18.21 11.07 8.29 7.37 36.29 18.55 10.94 8.25 7.11 AgPdAl 35.89 18.15 10.8 8.33 7.64 36.58 18.41 11.39 8.42 7.76 A^PdNb 35.88 18.13 10.86 8.29 6.93 36.99 18.53 11.08 8.26 7.1 A^Au 26.2 12.31 5.50 5.10 7.99 27.7 14.45 8.52 6.12 8.85 A^AuCu 36,1 17.53 11.45 8.58 7.25 36.5 18.66 11.25 8.25 7.36 A^AuTi 35.4 18.40 10.59 8.58 7.96 36.3 17.67 11.80 8.73 8.00 A^AuCr 36.0 18.32 11.34 8.50 7.58 36.2 18.64 10.25 8.75 8.04 AgAuTa 36.3 18.44 11.15 8.41 7.21 36.5 18.53 11.55 8.54 . 8.00 A^AuNi 36.0 18.31 11.32 8.50 7.58 36.4 18.66 11.20 8.41 7.25 . AgAuMo 36.0 18.35 11.58 8.50 7.58 36.8 17.65 11.84 8.73 8.00 AgAuPd 36.3 18.58 11.14 8.41 7.21 37.0 18.61 10.21 8.74 8.02 A^AuAl 36.1 18.24 11.05 •8.45 7.85 36.7 18.51 11.52 8.56 8.00 AgAuNb 36.1 18.25 11.11 8.41 7.14 37.1 18.62 11.21 8.41 7.24 A^Ru 26.5 12.45 5.55 5.25 7.96 27.7 14.59 8.75 6.35 8.99 A^RuCu 36.0 17.52 11.45 8.58 7.25 36.4 17.66 11.81 8.73 7.56 A^RuTi 35.3 18.49 10.59 8.58 7.96 36.2 18.64 10.24 8.75 7.35 A^RuCr 35.8 18.30* 11.34 8.50 7.58 36.1 18.52 11.55 8.54 8.00 . AgRuTa 36.2 18.42 11.15 8.41 7.21 36.4 18.65 11.21 8.42 7.52 A^RuNi 36.1 18.35 11.33 8.50 7.58 36.9 17.64 11.84 8.71 8.01 A^RuMo 36.1 18.34 11.58 8.50 7.58 36.8 18.60 10.22 8.72 8.02 AgRuPd 36.2 18.59 11.28 8.41 7.21 37.1 18.50 11.51 8.51 7.96 AgRuAl 36.3 18.55 11.18 8.41 7.21 36.5 18.61 11.20 8.42 7.24 AgRuNb 36.5 18.24 11.11 8.41 7.21 37.2 18.41 10.12 8.85 8.12 40NDA200104TW; P1P2000284TW 51 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 裝——I! (請先閱讀背面之注意事填寫本頁) £ 訂-------- ·# 1284746 A7 B7 五、發明說明（5X) 表11 Ιη203-15Μ)205/Α$ 合金 經濟部智慧財產局員工消費合作社印製
Hi-R 3火_ Hi-R as-depo 材料 波長 •波長 波長 波長 波長 波長 波長 波長 波長 波長 400.00 450.00 500.00 550.00 565.00 400.00 450.00 500.00 550.00 565.00 nm nm nm nm nm nm nm nm nm nm 吸收率 吸收率 吸收率 吸收率 吸收率 吸收率 吸收率 吸收率 吸收率 吸收率 (%) (%) (%) (%) (%) (%) (%) (%) (%) (%) pure 13.27 3.48 2.57 2.35 2.25 19.84 7.03 3.21 4.28 4.24 A^Pd 15.77 5.34 3.93 3.90 3.802 22.15 8.83 4.57 5.80 5.78 AgPdCu 16.57 6.24 4.67 4.68 4.49 22.89 9.69 5.30 6.56 6.43 A^PdTi 19.1—7 9.16 7.64 7.65 7.47 25.29 12.51 8.25 9.47 9.35 A^PdCr 19.67 9.72 8.21 8.22 8.04 25.75 13.05 8.82 10.03 9.91 A^PdTa 19.77 9.84 8.33 8.34 8.15 25.85 13.16 8.93 10.14 10.02 A^PdMo 20.07 10.17 8.67 8.68 8.50 26.12 13.48 9.27 10.48 10.36 AgPdNi 19.85 10.07 8.42 8.47 8.31 26.01 13.37 9.01 10.33 10.22 AgPdAl 19.16 9.3 7.63 7.7δ 7.49 25.36 12.63 8.36 9.56 9.34 AgPdNb 19.25 9.38 7.73 7.87 7.6 25.46 12.74 8.46 9.66 9.54 A^Au 15.27 4.78 3.18 3.19 3.00 21.69 8.28 3.82 5.10 4.98 AgAuCu 15.61 5.16 3.57 3.58 3.39 22.00 8.65 4.21 5.48 5.36 A^AuTi 19.63 9.68 8.17 8.IS 7.99 25.72 13.01 8.78 9.99 9.8+7 A^AuCr 19.51 9.54 8.03 8.04 7.86 25.61 12.88 8.64 9.85 9.73 A^AuTa 19.77 9.84 8.33 8.34 8.15 25.85 13.16 8.93 10.14 10.02 A^AuNi 20.07 10.17 8.67 8.68 8.50 26.12 13.48 9.27 10.48 10.36 A^AuMo 19.97 10.06 8.56 8,56 8.38 26.03 13.37 9.16 10.37 10.25 A^AuPd 19.07 9.05 7.53 7.54 7.35 25.20 12.40 8.14 9.36 9.24 AgAuAl 19.37 9.39 7.87 7.88 7.70 25.48 12.72 8.48 9.70 9.58~ A^AuNb 19.47 9.50 7.98 7.99 7.81 25.57 12.83 8.59 9.81 9.69 A^Ru 19.07 9.05 7.53 7.54 7.35 25.20 12.40 8.14 9.36 9.24 AgRuCu 19.62 9.67 8.16 8.16 7.98 25.71 12.99 8.76 9.98 9.86 A^RuTi 19.73 9.79 8.28 8.29 8.11 25.81 13.11 8.89 10.10 9.98 AgRuCr 19.31 9.32 7.80 7.81 7.63 25.42 12.66 8.41 9.63 9.51 A^RuTa 19.84 9.92 1 8.41 8.42 8.23 25.91 13.23 9.01 10.22 10.10. A^RuNi 20.27 10.40 8.90 8.91 8.73 26.31 13.70 9.50 10.70 10.58 . A^RuMo 19.63 9.68 8.17 8.18 7.99 25.72 13.01 8.78 9.99 9.87 A^RuPd 20.40 10.55 9.05 9.06 8.88 26.43 13.84 9.65 10.85 10.73 AgRuAl 19.10 9.08 7.56 7.57 7.39 25.23 12.43 8.17 9.39 9.27 A^RuNb 20.09 10.20 8.69 8.70 8.52 26.14 13.50 9.30 10.50 10.38 40NDA200104TW; P1P2000284TW 52 --------訂---------· (請先閱讀背面之注意事項再填寫本頁) 讀
本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7 五、發明說明（S3) 表12 IT〇/Ag合金 經濟部智慧財產局員工消費合作社印製 *材料 IT〇回火 ITO as*depo 波長 400:00 nm 波長 450.00 nm 波長 500.00 nm 波長 550.00 nm 波長 565.00 nm 波長 400.00 nm 波長 450.00 nm 波長 500.00 nm 波長 550.00 nm 波長 565.00 nm 吸收率 (%) 吸收率 (%) V 吸收率 (%) 吸收率 (%)、丨 吸收率· (%) ’ 吸收率 (%) 吸收率 (%): 吸收率 (%) 1吸收率· (%) 吸收率 (%) 純Ag 15.56 4.87 3.63 4.64 1.82 19.05 4.27 1.77 1.52 5.02 AgPd 18.06 7.69 6.49 7.47 4.73 21.55 7.23 4.81 4.57 7.95 AgPdCu 18.86 8.59 7.40 8.37 5.66 22.35 8.18 5.78 5.54 8.89 AgPdTi 21.46 11.52 10.37 11.31 8.68 24.95 11.26 8.94 8.71 11.94 AgPdCr 21.96 12.09 10.94 11.87 9.27 25.45 11.85 9.54 9.31 12.53 AgPdTa 22.06 12.20 11.05 11.99 9.38 25.55 11.97 9.67 9.44 12.65 AgPdMo 22.36 12.54 11.40 12.32 9.73 25.85 12.32 10.03 9.80 13.00 AgPdNi 22.14 12.42 11.15 12.11 9.54 25.74 12.21 9.77 9.65 12.86 AgPdAl 21.45 11.66 10.37 11.4 8.64 25.04 11.4 9.07 8.83 11.96 AgPdNb 21.54 11.75 10.46 11.53 8.82 25.14 11.52 9.19 8.92 12.14 AgAu 17.56 7.13 5.92 6.90 4.15 21.05 6.64 4.20 3.96 7.36 AgAuCu 17.90 7.51 6.30 7.29 4.54 21.39 7.04 4.61 4.37 7.76 AgAuTi 21.92 12.04 10.89 11.83 9.22 25.41 11.80 9.50 9.27 12.48 AgAuCr 21.80 11.91 10.76 11.69 9.08 25.29 11.66 9.35 9.12 12.34 AgAuTa 22.06 12.20 11.05 11.99 9.38 25.55 11.97 9.67 9.44 12.65 AgAuNi 22.36 12.54 11.40 12.32 9.73 25.85 12.32 10.03 9.80 13.00 AgAuMo 22.26 1^.43 ’11.28 '12.21 9.62 25.75 12.20 9.91 9.68 12.88 AgAuPd 21.36 11.41 10.25 11.19 8.57 24.85 11.14 8.82 8.58 11.83 AgAuAl 21.66 11.75 10.60 11.53 8.92 25.15 11.49 9.18 8.95 12.18 AgAuNb 21.76 11.86 10.71 11.65 9.03 25.25 11.61 9.30 9.07 12.30 AgRu 21.36 11.41 10.25 11.19 8.57 24.85 11.14 8.82 8.58 11.83 AgRuCu 21.91 12.03 10.88 11.82 9.21 25.40 11.79 9.48 * 9.25 12.47 AgRuTi 22.02 12.15 11.01 11.94 9.34 25.51 11.92 9.62 9.39 12.60 AgRuCr 21.60 11.68 10.53 11.47 8.85 25.09 11.42 9.11 8.88 12.11 AgRuTa 22.13 12.28 11.13 12.06 9.46 25.62 12.05 9.75 9.52 12.73 AgRuNi 22.56 12.76 11.62 12.55 9.96 26.05 12.56 10.27 10.04 13.23 AgRuMo 21.92 12.04 10.89 11.83 9.22 25.41 11.80 9.50 9.27 12.48 AgRuPd 22.69 12.91 11.77 12.70 10.12 26.18 12.71 10.43 10.20 13.39 AgRuAl 21.39 11.44 10.29 11.23 8.60 24.88 11.17 8.85 8.62 11.86 AgRuNb 22.38 12.56 11.42 12.35 9.75 25.87 12.34 10.05 9.82 13.02 .yH! 40NDA200104TW; P1P2000284TW 53 裝--------訂--------- f 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7 五、發明說明（se 表11顯示反射層連同本發明之覆蓋層時，光學吸收率 於回火後，相較於沒有覆蓋層的反射層降低許多。於表11 中本發明的In2〇3-15wt% Nb205覆蓋層，相較於表10中的 二氧化矽覆蓋層以及表12中的ITO覆蓋層，具有更低的 吸收率。 表13顯示三層層積體，包括基膜、反射層以及覆蓋層， 於約250°C回火後的光學特性，類似於表9至12中所示 者，層積體的接著性也如同表6中的層積體一樣好。三層 結構層積體無論於光學特性以及接著性都較優異。 三層層積體的光學特性並未因爲使用覆蓋層而變差， 相反的，當使用覆蓋層，其包括三氧化二銦爲主要成分以 及l-30wt%Nb2O5時，反射率反而增加1-6%，而且吸收率 於約250°C的回火後，反而降低。表14顯示，即使使用較 薄的覆蓋層，也能夠得到更增進的反射率以及良好的光學 特性。 ___________%年-— !- (請先閱讀背面之注意事項再填寫本頁) « — — — — I — •il. 經濟部智慧財產局員工消費合作社印製 40NDA200104TW: P1P2000284TW 54 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） 1284746 A7 B7 五、發明說明（ss) 表13吸收率(〇/〇)· 經濟部智慧財產局員工消費合作社印製
In90.r5wt% Nb2〇^ ①未加熱_ ② 150 〇C ③ 300°C 566 10.88 10.24 15.3 564 10.67 10.04 15.06 550 9.38 8.829 13.6 500 7.104 7.071 8.297 450 13.42 14.38 7.922 400 26.96 27.49 19.93 In?O,r10wt% Nb2〇5 ①未加熱 ② 150 〇C ③300 °C 566 11.13 12.39 13.11 564 10.91 12.16 12.88 550 9.639 10.71 11.42 500 7.113 7.166 7.236 450 12.72 11.8 9.97 400 27.29 26.6 24.28 In?0.r15wt°/〇 Nb〇Os (D未加熱 ②150 〇C ③300 〇C 566 15.97 18.42 20.29 564 15.74 18.17 20.04 550 14.32 16.69 18.63 500 9.059 10.57 12.36 450 7.363 7.168 7.21 400 17.19 16.56 13.33 40NDA200104TW; P1P2000284TW 55 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐） ^------ (請先閱讀背面之注意事W：填寫本頁) 訂--------- ·# A7 五 1284746 ____B7 _____' 一 發明説明 表14 改變In20，Nb205覆蓋層厚度後反射層反射率的改變 度 5 nm 49 nm 1 70 nm 74 nm A inm] 加熱前 加熱後 加熱前 加熱後 加熱前加熱後 加熱後 1 556 92.99 91 85.61 8S.6S 83.15 91.32 95.27 554 92.91 90.85 85.62 88.69 83.18 91.29 95.28 552 92.84 90.74 85.63 88.67 83.2 91.39 95.28 ^ 550 92.92 90.74 85.69 88.72 83.35 91.5 95.33 500 90.88 87.82 85.22 88.37 83.56 91.47 95.13 450 85.71 79.83 82.88 85.02 80.93 87.77 93.56 400 74.72 70.22 80.63 84.96 79.47 85.35 83.23 85 : nm 90 : nm 100 nm λ 加熱前 加熱後 加熱前 加熱後 加熱前. 加熱後 556 86.8 93.4 S1.44 91.28 83.36 91.97 —554 86.78 93.36 81.47 91.29 83.3 91.97 552 86.81 93.37 81.5 91.39 83.31 92.04 _ 550 86.89 93.43 81.61 91.52 83.39 92.14 500 86.02 92.9S 81.96 92.18 81.36 92.04 450 81.58 88.19 78.5 88.9 71.91 87.01 400 74.11 81.17 6S 82.7 39.88 70.18 (請先閱讀背面之注意事項再填寫本頁)
裝 經濟部智慧財產局員工消費合作社印製 以上實施例以及具體實施例係用以例示而非限制，而 且本發明不被限制於其中的細節，並且可以被修改而不脫 離附加申請專利範圍的範圍以及均等性內。
40NDA200104TW; P1P2000284TW 本紙張尺度適用中國國家標準（CNS)A4規格（210 X 297公釐）

Claims (1)

1284746 .六、申請專利範圍 A8 B8 -Cl· D8 公告本 95. 1.6 替換頁2006/1/6 案號 90107568 申請專利範圍 1. 一反射層，包含： .… ' * : / 銀，作爲主要成分； • .. .. 一隹一:元素金，·佔:0:.1至3:0重量百分比.；·以及' . ••一第士元素，佔· 0 · 1至3:0重量百·分比，·且係選自包含 • 銅、:鈦乂·鎢..、鉅、.鉬:：·鎳、鈮、·以及舒之群組。·. 2, •根'據申請專利..範圍第/ 1項之反射層:，.其中該反射層係 • . · ，，· ... . ♦ * · •由播形成 ‘· ·、;··.·... · ·.·' .· ·· · · . . · 3:根據钟範圍第ί着之反射層，其中該反射層係 由濺鍍所形.成。_，·、·· . ： • . * · ... . 4· 一層镜i，.铒杳.：· ： . ·· _··. ' ' 一基底i以及·： \ • · ·:，··- .. . . · _ —沉積於該基底上之反射層，其中該反射層包含. * · · . * .銀，作爲主要成分； * 一第一元素金，佔0.1至3.0重量百分比；以及 一第二元素，佔0.1至3.0重量百分比，且係選自包含 銅、鈦、鉻、纟旦、鉬、鎳、鈮以及釕之群組。
財 產 局 員 工 消 費 合 作 社 5. 根據申請專利範圍第4項之層積體，其中該基底係一 樹脂基底。 6. 根據申請專利範圍第4項之層積體·，其中該基底係一 玻璃基底。 7. —層積體，包含： 一基底； ’ ’ 一基膜，沉積聆該基底上，其中該基膜係由矽、鉅、 * · 40NDA200104TW; P1P2000284TW 57 本紙張尺度適用中國國家標準(CMS)A4規格（210 X 297公釐） A« B8 C8 D8 1284746 .六、申請專利範圍 替換頁2006/1/6 案號 90107568 鈦、鉬、鉻、鋁、ITO、氧化鋅、二氧化矽、二氧化鈦、 五氧化二鉅、二氧化锆、三氧化二銦、二氧化錫、五 氧化二鈮、或氧化鎂的至少其中之一所製成；以及 一包含銀之反射層，洱積於該基膜上，該反射層包含： 銀，拃爲主要成分;^ ， - · · , 一第—兀素金，佔〇 · 1至3.〇重量百分比；以及 • ·:. V ·. 一第二元_，:佔Ό.Ι.至.3.0重.量百分比，且係選自包含 . ·. · ... , - . · 銅、:緣:、::络、:售:、組、.鎳、鈪、以及釕之群組。 ... ... .· ..‘ . . 8.根據申_專利範圍第'7項之層積體，m包含一覆蓋層 .... .... ... ·' . 沉積於該反射層上，:其中該覆蓋層包含三氧化二銦作 . * .. . 爲主要成分、以及二氧化錫、五氧化二鈮、.二氧化矽、 ..... .. · . . 氧化鎂以及五氧化二鉅的至少其中之一。 .9.根據申請專利範圍第7項之層積體，其中該基底係一 玻璃基底。 ’· 10. 根據申請專利範圍第7項之層積體，其中該基膜係由 矽、鉅、鈦、鉬、鉻或鋁的至少其中之一所製成。 11. 根據申請專利範圍第7項之層積體，其中該基膜係由 ITO、氧化鋅、二氧化矽、二氧化鈦、五氧化二鉅、二 氧化鍩、三氧化二銦、二氧化錫、五氧化二鈮、或氧 化鎂的至少其中之一所製成。 12. 根據申請專利範圍第11項之層積體，其中該基底係一 樹脂基底。 13. —層積體，包含： 一包含銀之反射層，包含作爲主要成分的銀；一第一 40NDA200104TW; P1P2000284TW 本紙張尺度適用中國國家標準(CNS)A4規格（210 X 297公釐〉 面 之 注 S t 頁 經 濟· 部 智 慈 財 產 局 員 工 消 費 合 作 社 印 製 58 A8B8C8D8 1284746 六、申請專利範圍 替換頁2006/1/6 案號 90107568 元素金，佔.0.1至3..0重量百分比；以及一第二元素， 佔0.Ί至3.0重量百分比，且係選自包含銅、·鈦、鉻、 組、鉬、鎳、鈮、以及釕之群組·；以及 二沆積:於該反射層上之覆_層，其中該覆蓋層包含三· ••氧·化·：=：銦作Μ全要成分·、以及二氧化鎳、五氧化二鈮·、 - ··.··- ·· · · . •二氧祀發·：氧化鎂以芨五氧化二鉅的至少其中之一。 • ·- . · · - . · · . • . ..··.· ' . . 14. 振據申請:專利..範圍第4·、·7:或13項:之層積體，其中該 • · .······. ， .·.·，·· . · · . · * •層:__振液:晶:顯吊弟置的建築坡璃或:一反射體或一反 •射性: · .. .·' ·.··· ·.. · ·· ..···:···· 15. —液晶顯示裝置，具有根擄申請專利範圍第1、2或3 · · · · . · . 項之該反射璋>。. ... .·’··：、.. • t · . * , * 16. —液晶顯示裝置，具有根據申請專利範崮第4至7、以 • . . .··.· . ' · · - 及10至Π.項其中任一項之該層積體。 ·,. 17. ·—可攜式的終端裝i，具有裉據申請專利範圍第1，5或 16項之液晶顯示裝置。 ' . 18. —反射麿，包含：. 銀，作爲主要歳分；. • * · · 經 智 慧 財 產 局 員 工 消 費 合 作 社 印 製 一第一元素鈀，佔0.1至3.0重量百分比；以及 一第5元素，佔0.1至3.0重量百分比，且係選自包含 鉅、鉬、鎳、鈮、以及釕之群組。. 19. 一層積體，包含： 一*基底；以及 一反射層，沉積於該基底上，其中該反射層包含： 銀，作爲主要成分； 59 40NDA200104TW; P1P2000284TW 本紙張尺度適用中國國家標準(CNS)A4規輅（210 X 297公釐） A8 B8 08 D8 1284746
經濟部智慧財產局員工消費合作社印製_ 申請專利範圍： 替換頁2006/1/6 案號 90107568 一第一元素鈀，佔〇·1至3·〇重量百分比；以及 一第二元素，佔0·1至3.0重量百·分比，且係選自包含 ' : - t 姐、鉬、鎳、鈮、以及釕之群組。 .20. 一®積:體，·包含· .，··’. • ； ·. 一基暖T·沉積於該基匼上，其中該基腠係由矽、钽、 $目<_絡銘_:、,ιτο、氧化鋅:V二氧化矽、·二氧化鈦、五 . · · · ·· · · · · _ · · 氧:化li嫌> :?：:氧化錐乂三氧化二銦、氧化錫·，五氧 · ·:·. · ··· ·· ·, ·· · · · · · 化:.鎂的至士其中;之一所:製成；以及·· • ·_.，.、'···".· .‘ · · ·· ···..·.__· · 一包含銀之反射層·;沉積於該基膜上，.該反射層包含： * · ·、 · * 銀，.祚爲主#成分；.·： ：_.·· 、·. •. * .·····.· . ; • -:_.··· . . . . . 、. · · . 一第一元素鈀.，佔·ύ.ι至5.0重量百分比；..以及 • .·...·· ··· · · · .. •一:第二元·素，佔0!Γ至3:0重量百分比，且係選自包含 / · .丨 _ _ .钽、鉬：鎳、齙、ά及釕之群組。. . · • 21· —朦積體，包含： .'· 一含銀之反射層，包含作爲主要成分的銀、一第一元 素鈀，佔〇·1 - 3·〇重量百分比、以及一第二元素.，佔 〇·1至3.0重量百分比，且係選自包含鉬.、鉬、鎳、鈮、 以及釕之群組:；以及 " 一沉積於該反射層上之覆蓋層，其中該覆蓋層包含三 氧化二銦作爲主要成分、以及二氧化錫、五氧化二鈮、 二氧化砂、氧化鎂以及五氧化二钽的至少其中之一。 22. —反射層，包含：· 銀，作爲主要萌分； * 40NDA200104TW； P1P2000284TW 6〇 本紙張尺度適用中國國家標準(CNS)A4規格（210 X 297公釐） A8 B8 C8 D8 1284746 六 ：·!·· .11..·' .1.·.:·. · · . · ·__ ••\ 人.·/ J ^ ^ ^ ^ ^ ^ ^ 申請專利範圍： 替換頁2006/1/6 案號 90107568 一第一元素釕，佔0.1至3.0重量百分比；以及 一第二元素，佔0.1至3.0重量百分比，且係選·.自包含 " * ： / 銅、鉻、钽、鉬、鎳、鋁、鈮、金、以及鈀之群組。 .23·二胁積:·體，·包含··: :·:: · · · ’ · ·:，· .一基唪:;取及：…... • 一反射廢沉積於該基底上，其中該反射層包含： 银.’··作爲.主要成分，/ ·. . · ·* · ·· . · · · . · · 一:第U•蠢素:虹’，佔..Q.V至3.0重量百分比；'以及 .· ···.·. ' · · ·.. 一第估:0、1'至3:0重量百分比，且係選自包含 _ ·.··.'··.··'.·· · _ .· ，.·：··. · 銅、.鉻/鉅、鉬、·鎳.、鋁:、鈮、金、以及鈀之群組。· - · · · . .. . · . 24. —層_體，.包·含：： ... ··. ： . • · * . * · .· 一基底； • ·· ···-·.· · · ·. - •一基膜，·沉·積於該基底上，其中該基膜係由矽、..鉬， ' · ·· · * •鉬、鉻：鋁、i.T〇、氧化鋅、二氧化矽、二氧化鈦.、五 氧化二鉅、二氧化锆、三氧化二銦、z:氧化錫、五氧 化二鈮、或氧化鎂的至少其中之一所製成；以及' 一包含銀之反fe層，沉積於該基膜上，該反射層包含： .β . . 銀，作爲主要成分；# . 、 一第一元素釕:，佔0.1至3.0重量百分比；以及 一第二元素，佔0.1至3.0重量百分比.，且係選自包含 銅、鉻、鉅、鉬、鎳、鋁、鈮、金、以及鈀之群組。 25. —層積體/包含： 一含銀之反射層，包含作爲主要成分的銀、一第一元 素釕，佔0.1萆3·〇重量百分比；以及 40NDA200104TW; P1P2000284TW 61 本紙張尺度適用中國國家標準XCNS)A4規格（210 X 297公釐） 1284746 880Q99 ABaD .六、申請專利範圍 替換頁2006/1/6 案號 90107568 一第二元素.，佔0.1.至3.0重量百分比，且係選自包含 銅、鉻、組、鉬、鎳、鋁、鈮.、金、以及·紀之群組； ' ： . / . 以及 U 一沆積:於該反射層上之覆葦層，其中該覆蓋層包含三. · · ·氧化亡銦作爲主要成分、以··及二载化錫、五氧化二鈮、 二氧化Ϊ:敬·.、氧化鎂以友五氧化二鉬的至少其中之一。 * · · * · · ..·：· ·.·.· ·' . · 26·· —液昂輕牟裝p，·身有f艮據.申請惠利·範_第1S或22 •墳:之該靡射:層:… .·. · . ·'； V ：.;：··· · ' ： v · · : . . ·. ... 27. —液晶Μ呆裝置具有ί據申請專利範圍第19至21、 * *. · . · * .··、·. .. · ·. · ·· ·* . 及23至:25·項中任“項之該層積體。：. 2S. —可攜式的展端裝置.，具有拫據申蕭專利範圍第26或 • t * . * ： · * 27項之液晶顯.示裝置。./ · • ' .:·.·· .. .... ·· 29. ·—反射層·，·用於建築玻璃或液晶顯示裝置的反射.體或 .反射性接線電極，毺含： . 銀，作爲主要成分； ' 一第一元素，佔0.1至3.0重量百分比，且係選自包含 金、鈀以及釕乏群組；以及 * * j 一第二元素，佔0.1至3.0重量百分比，.且係選自包含 銅、鉻、鉅、鉬、鎳、鋁、鈮、金、鈀以及釕之群組， 其中該第二元素不同於該第一元素·，且該反射 智 慧 財 產 局 員 工 消 費 合 作 社 印 層之表面在加熱250°C之後，視覺上沒有模糊（dull)白 ' . ·* ' 色的改變。 30. —層積體，用於建築玻璃或液晶顯示裝置的反射體或 反射性接線電極，包含： 62 40NDA200104TW; P1P2000284TW 本紙張尺度適用中國國家標準(CNS)A4規輅（210 X 297公釐） 1284746 .六、申請專利範圍 替換頁2006/1/6 案號 90107568 一基底；以及 一沆積於該基底上之反射層，.其中該反射層包含： • · ： · t · ·- 銀，作爲主要成分;. · · ··· . 二第一:元素，佔il·至3.0童量百分比，·且係選自包含 ，金二，鈀以及釕之群組:·；，以及 ·Λ • _ ····.- · · 一第:!!芜素，佔0,1至3·0重量百分比，·且係選自包含 • · · ·. 〈·鋒病目、鎳:、牮、:鈮.、金:、鈀取及釕之群組， •真:中:滅秦三:束素吊·同於該第一元素，且該反射·. . 層之熱:25〇π；ί後，視覺上沒有摸糊(dull)白 _ _ · .. . .· .，.*·· · 色的改變。· ·'..·*' ， . ' . . 31. —層積體，.用於建築玻璃或液晶.顯示I裝置.的反射體或 .、反射性接線電極，包含：‘ .· .. ···.·.· ··. . · · _ - • •一 基底；. . ·. . · ——基膜，沉積於該基底上，其中該基膜係由矽、鉅、 鉬、鉻、·鋁、ITO、氧化鋅、二氧化矽、二氧化鈦、五 氧化二鉅、·二氧化锆、三氧化二銦.、二氧化錫、5氧 化二鈮、或氧鎂的至少其中之一所製成；以及·· « . 經 智 慧 財 產 局 員 工 消 費 合 作 社 印 製 一包含銀之反射層，沉積於該基膜上，該反射層包含： 銀，作爲主要成分； 一第一元素，佔0.1至3.0重量百分比·，且係選自包含 金、鈀以及釕之群組；以及 ‘ 一第二元素，佔0.1:至3.0重量百分比，且係選自包含 銅、鉻、鉅、鉬、鎳、鋁、鈮、金、鈀以及釕之群組， 其中該第二元素不同於該第一元素，且該反射 • ·: · 40NDA200104TW; P1P2000284TW 63 本紙張尺度適用中國國家標準’(CNS)A4規輅（210 X 297公釐） A8B8C8D8 1284746 ./、 申請專利範圍： 替換頁2006/1/6 案號 90107568 層之表面在加熱25〇°C之後，視覺上沒有模糊（dull)白 色的改變。 .： ..：· • ： - ·· · 32· —層積體，用於建築玻璃或液晶顯示裝置的反射體或 反鼾性:·接繞電極..，包含.：’ ... · * - · · · ' 一包食男之反射層砬:含·丨乍爲主姜成分的銀·； —第—无·:#..，佔（Μ _ 3.0重量百分比:，.且係選自包含 :金?·(,亭(¾釭之群:啩；取友： 一第g靡有？ ％ 0· 1:至:3:0重量百分比V且係選.自包含 铜、銘秦':飽·'·鏡:、.ig、鈮;、金、鈀以及釕之群組， 其中該第二元素不苘於該第一元素，旦該反射 層之表面在·_♦ 25〇°C之後，視覺上·沒有模糊(dull)白 .色的改變；以及...，、 .* - * * ·.· · · * ·. 一沉積於該反射層上之覆蓋層，其中該覆蓋層包.含三 •氧化二銦作爲生要逢分、以及二氧化錫、五氧化二.鈮、 二氧化矽、氧化鎂以及五氧化二鉬的'至少其中之一。 33· —液晶顯示裝置，具有根據申請專利範圍第29項之該 反射層。 ’ 34. —液晶顯示裝置，具有根據申請專利範圍第30至32 項中任一項之該層積體。 35· —可攜式的終端裝置，具有根據申請專利範圍第33或 34項之液晶顯示裝置。 64 40NDA200104TW; P1P2000284TW 本紙張尺度適用中國國家標準(CNS)A4規輅（210 X 297公釐）
TW090107568A 2000-12-07 2001-03-29 High heat resistant reflective coating, and laminated body using the reflective coating TWI284746B (en)