TWI247731B - Gypsum compositions and related methods - Google Patents
Gypsum compositions and related methods Download PDFInfo
- Publication number
- TWI247731B TWI247731B TW090109815A TW90109815A TWI247731B TW I247731 B TWI247731 B TW I247731B TW 090109815 A TW090109815 A TW 090109815A TW 90109815 A TW90109815 A TW 90109815A TW I247731 B TWI247731 B TW I247731B
- Authority
- TW
- Taiwan
- Prior art keywords
- gypsum
- composition
- water
- mixture
- calcined
- Prior art date
Description
1247731 五、 發明說明(1) 發明之技術領域 本發明-般是關於石膏組成物和和製備石膏組成物 法。更特別’本發明是關於降低密度之石膏組成物及 其製備方法。 發明的背景 或 a固定石膏_弓二水合物)是-種已知的材料,它通 1括許多型式的產品。舉例來說,固定石膏是使用傳統 β斤產生之終端產品的主要組成份(舉例來說,石膏-内 。^面建構壁),而且也是使用在_般建築物的内部牆壁 #天化板之典型不塗泥灰的石牆中所使用的紙面石膏板。 除此之外’固定石膏是石膏/纖維素纖維合成板和產品的 2要組成份,而且也包括炸石膏板之間充填且平滑的關節 產品。許多可專門材料,諸如可以用於精密加工之模鑄 製模材料,也可以用來製備主要含有固定石膏之產品。 、、又此3有石用之產品可以藉由形成燒石膏(硫酸 料水合物及[或]無水硫_)和水(和其他的成分,視情 況而定)所製備成的。該混合物被濟轉成所需要的形狀或 祕在-表面上,然後藉由燒石膏和水反應形成形成結晶 水合石貧(硫_二水合物),另其硬化(再水合)而形成固 定石貧。燒石膏形成所需要的水合後可以形成交聯的固定 石膏晶體的基材,藉此使在含有石膏之產品中,賦予石客 結構必須的強度。利用溫和的加熱趕走剩餘的自由Ζ 反應的)以產生乾燥的產物。 目前仍有持續努力的空間,舉例來說,藉由低密度 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 4 1247731
材料(例如擴張的珍珠岩或空氣空孔)取代部份固定石膏基 材以產生更輕的含石膏產物,以增加材料的消音及[或]絕 緣丨生貝,以及處理和運輸效力率。不過,先前對含石膏產 ㈣仃實質輕量化的努力沒有完全被滿^,舉例來說,因 為在利用大1的泡棉來產生具由足夠空孔含量而達得降低 各石胃產物的密度的同時,這些產物可能仍然無法達到所 需要的消音與絕緣性質。結果,低密度含石膏產物的製備 容易受相當高含量之發泡劑影響,同時在某些情況中仍無 法達到所需的結果。最近,由纖維燒石膏形成的石膏板已 揭不於美國專利第5,〇41,333號中。纖維燒石膏的製備是 很耗時而且也很昂貴的。 在形成實質上比較低密度含石膏的產品的其他問題 包含在其製作、加工及商業化應用時的尺寸安定性。舉例 來說,在製備固定石膏產品中,在石膏固定之後,在基材 中通常會留下相當量的自由(也就是未反應的)水。固定石 膏的乾燥以趕走過量的水時,基材中交織的固定石膏結晶 會隨著水分蒸發而移的更靠近。在這個方面上,當水份在 該石膏基材中留下結晶空隙時,基材容易因由固定石膏因 抵抗水分施加在固定石膏上的毛細壓力,而產生的自然力 量造成收縮。當水溶液的燒結石膏混合物中的水含量增加 時,缺乏尺寸安定性會變成是一個問題。 即便是在最終乾燥產品上,尺寸安定也是一個需要 實際考慮的問題,特別是易影響的固定石膏溫度及濕度發 生改麦’舉例來說膨服和收縮’的情況下。舉例來說,暴 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) (請先閱讀背面之注意事項再填寫本頁) 經濟部智慧財產局員工消費合作社印製 經濟部智慧財產局員工消費合作社印製 1247731 A7 ^------E_ 五、發明說明(3 ) 在门Λ、、度下,在石貧板或磁磚的石膏基材中之結晶空隙 收勺X氣會因為該受潮的石膏板膨脹,而使下垂的問題 惡化。 如果這些尺寸不安定性能夠被避免或減到最少,將 會產生有利的結果。舉例來說,如果在乾燥期間該些板沒 有發生收縮,現行的石膏板製造方法可以有更多的產品, 而且所需要的含石膏產品可以保持精確的形狀及尺寸比例 (例如貫用鑄模或製模)將可使其有更好的功能。 口此由上述對於固定石膏組成份的技藝,其所需 要的是具有低的密度但不需要輕量的填充物和由泡沫形成 的空氣空孔。其中也發現在該技藝中需要具有尺寸更安定 、絕緣及/或消音性質的低密度固定石膏組成物。本發明 提供此一固定石膏組成物及其製備方法。本發明這些及其 匕的優點與其他特性,將藉由此處對本發明的說明而更為 清楚。 曼ϋ的概要說明 本發明提供一固定石膏組成物及其製備方法。有利 地’本發明的固定石嘗組成物是低密度,而且證實可以提 升尺寸安定性(舉例來說抗收縮)、絕緣及[或]消音性質。 一方面,本發明提供一個包括利用至少由燒石膏與 水形成混合物的方法,所製備的固定石膏組成物。其中用 於製備該混合物的水及燒石膏的比例至少大約是3 : 1是較 令人滿意的。在此實施例中,使用燒石膏形成之該固定石 貧組成物包含至少30wt%非纖維的燒石膏。該混合物是被 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 6 -----------裝--------訂?-------- (請先閱讀背面之注意事項再填寫本頁) 1247731
保持在足以使該燒石膏形成固定石膏基材的條件下。 另方面本發明提供一個包括利用至少由燒石膏 (請先閱讀背面之注意事項再填寫本頁) 與水形成混合物的方法,所製備的固定石膏組成物。其中 用於製備n合物的水及燒石膏的比例至少大約是45:工 。该混合物是被保持在足以使該燒石膏形成固定石膏基材 的條件下。 另一方面,本發明提供一個包括利用至少由燒石膏 水和由二偏磷酸鹽化合物、具有500-3000個重複磷酸鹽 早凡之聚磷酸胺鹽、多羧酸化合物、界面活性劑及其組合 物中所遥出的加強材料形成混合物的方法所製備的固定石 膏組成物。在本發明的實施例中,用於製備該混合物的水 及燒石膏的重量比例至少大約是3 : i。_合物是被保持 在足以使該燒石膏形成固定石膏基材的條件下。 經濟部智慧財產局員工消費合作社印製 再一方面,本發明提供一個含有交聯固定石膏基材 的連續相之固定石膏組成物。該基材包括石膏和水蒸發後 的空孔。依據水蒸發空孔體積” EWVV”試驗(將說明於下) ,在基材中所需要的水蒸發空孔體積至少大約69%。在本 發明的實施例中,由使用燒石膏形成的該固定石膏組成物 包含至少30 wt%非纖維的燒石膏。 再另一方面,本發明提供一個含有交聯固定石膏基 材的連續相之固定石膏組成物,其中該基材包含石膏和水 蒸發後的空孔’而且其中依據EWVV試驗,基材中水蒸發 空孔體積至少大約69%。在本發明的實施例中,是使用由 三偏磷酸鹽化合物、具有500-3000個重複磷酸鹽單元之聚 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 經濟部智慧財產局員工消費合作社印製 1247731 A7 ' _____B7__ 五、發明說明"—"" 1 嶙酸胺鹽、錢酸化合物、界面活性劑及其組合物中所選 出的加強材料形成之該固定石膏組成物。 另一方面,本發明提供一個含有交聯目定石膏基材 ”續相之固定石膏組成物,其中該基材包含石膏和水蒸 發後的空孔,而且依據EWVV試驗,基材中水蒸發空孔體 積至少大約是80%(舉例來說,從大約8〇%到大約97%)。 由實施例可知,本發明的石膏組成物可以是板材型 式。該板才可以是物件型式,舉例來說,諸如人造壁板、 門核心、結構絕緣面板系統組件、消音瓷磚或類似物。在 此方面,該物件也可以包括複合板(舉例來說,如層狀物) 。舉例來說,該物件可以包含第二個更緻密的石膏板,使 侍該第二石膏板的密度比含有依據本發明之石膏組成物的 密度更大。 參考伴卩边的圖式以及下面實施例的詳細說明可以對 本發明有更清楚的認識。 之概要說明 第1圖是依據本發明的一個概念形成之石膏板層狀複 合材的示意圖式。 第2圖是依據本發明的另一個概念形成之天花板型式 之物件的透視圖。 第3圖是依據本發明在一個概念而形成之積層複合物 的示意圖式。 明的詳細說明 本發明提供一個低密度固定石膏組成物,其包含具 (請先閱讀背面之注意事項再填寫本頁) 裝 — —訂」---- 華. 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公复) 1247731 經濟部智慧財產局員工消費合作社印製 A7 五、發明說明(6 ) 有增大水氣蒸發空孔體積之交聯固定石膏基材。該低密度 固定石膏組成物較好是由含有高之水對燒石膏比之混合物 (舉例來說,石膏漿)所製被成的。 燒石局可旎纖維的或非纖維的。非纖維的燒石膏是 指依據先前技藝一般的方法,在燃燒爐(舉例來說,轉動 爐)在大氣壓下製備成的燒石貧,舉例來說如美國專利第 2,341,426號中揭示。纖維的燒石膏,舉例來說,是揭示 於美國專利第4,029,512號和第5,041,333號中。該石膏組 成物較好是使用至少30 wt%的非纖維的燒石膏形成的。 該石膏組成物更好是由至少50 wt%是使用燒石膏形成, 在一些實施例中,被淹鑄之以本發明的固定石膏組成物製 備利用該石膏形成的該泥漿(或混合物),本質上是由非纖 維燒石膏組成。 k石·可以疋α -硫酸4弓半水合物、石_硫酸鈣半水合 物、水溶性的無水硫酸鈣或其混合物。該燒石膏較好含有 至少30〇/〇/?-硫酸鈣半水合物,而且更好是至少5〇%石_硫 酸約半水合物。在一些實施例中,燒石膏本質上是由心 硫酸鈣半水合物組成。 特別地,由於在固定石膏基材中存在增大的水氣化 空孔,而使依照本發明之固定石膏組成物具有相當鬆散且 開放的結構之特徵。舉例來說,水氣化空孔體積積能藉由 將用於製備固定石膏組成物之混合物中水和燒石膏比例提 高來形成。由各種不同大小及形狀結晶形成之固定石膏的 交聯基材,是視用於形成該固定石膏所使用之基材的i和 本紙張尺度適用中國國家標準(CNS)A4規格(21〇 297公釐) ·裝-------r 訂、— (請先閱讀背面之注意事項再填寫本頁) 9 1247731 A7 B7 經濟部智慧財產局員工消費合作社印製 五、發明說明( 燒石膏比例來決定。舉例來說,在一些實施例中,姓曰 τ 、彡口日日相 當長(舉例來說,至少在一方向上大約10微米至大約4〇微 米或更長)及[或]可以有各種不同的組態,例如真爿士、板 狀或類似物或其組合物。 很重要地,雖然增加在固定石膏基材中水氣化空孔 體積,已被證實由足夠的強度與耐機械變形(舉例來說, 抵抗下垂)且具有所需要的低密度之本發明的固定石膏組 成物是非常有用的。除此之外,本發明的固定石膏組成物 具有尺寸安定性,在該固定石膏組成物的製備期間,即便 是在該固定石膏組成物的製備期間含有相當高程度的水時 ,使它能耐收縮(例如因為乾應力)。此外,在該固定石膏 組成物中增加的水氣化空孔體積有助於賦予所需要的消音 性質,由於鬆散結構以及增加的水氣化空孔體積,在該固 定石膏組成物中可以提供較大的空間以使聲音被吸收,使 得由本發明的固定石f組成物反射的聲音#,以及透過的 聲音量被降低。 依據本發明,該固定石膏組成物包含連結固定石膏 基材的連⑽目。該基材包括石膏和增加的水氣化^孔體積 曰加的水氣化空孔體積反映在該連續相,其可以排除 除了水氣化空孔之外的不連續物,舉例來說例如在該組成 2中因為紙纖維、輕量化填充物或發泡空氣的空孔的存在 造成的不連續。在-些實施例中,依據EWW試驗,基材 的水氣化空孔體積是至少大約69%(舉例來說,從大約69% 到大約97%)。依據膽㈣式驗,該水氣化空孔體積較好是 -----------裝--------訂-W-------- (請先閱讀背面之注意事項再填寫本頁)
1247731 A7 --~--- 五、發明說明(8 ) '" 從大約74%到大約95%。舉例來說,在某些情況,依據EWVV 试驗’該水氣化空孔體積較好是從大約79%到大約89%。 (請先閱讀背面之注意事項再填寫本頁) 在-些實施例中’依照本發明在固定石膏組成物是 由包含使用燒石膏與水所形成的混合物(舉例來說,石膏 漿)’水和燒石膏的重量比至少是大約3: i的方法所製: 。該混合物是被保持在足以使該燒石膏形成固定石膏基材 的條件下。當該燒石膏含有至少3〇 wt%非纖維燒石膏時 ,用來製備固定石膏基材的水和燒石膏的重量比較好是由 大約3 · 1至大約12 : 1。用來製備固定石膏基材的水和燒 石膏的重量比更好是由大約4·5: !至大約9: i。用來製備 固定石膏基材的水和燒石膏的重量比再好是由大約5 : i至 大約8 : 1。在這些實施例中,非纖維性燒石膏較好是点_ 硫酸鈣半水合物。 經濟部智慧財產局員工消費合作社印製 在一些貫施例中,依照發明之固定石膏是利用包括 形成含有水和纖維性或非纖維性燒石膏,或不同纖維性或 非纖維性燒石膏組合或製被方法形成混合物(舉例來說, 石員水)的方法製備,其中水和燒石膏的重量比較好是由 大約4.5 : 1至大約12 : 1。用於製備該實施例中之混合物 的水和燒石膏的重量比由大約5 : 1至大約8 : 1,更好是由 大約5 : 1至大約7 : 1。 該發明的固定石膏組成物有令人滿意相當低的密度 。嚴格地由實施例來說,在一些實施例中,石膏組成物的 密度大約20磅/叹3(lb/ft3)(〜320公斤/公尺3)或更少,諸如 大約大約15磅/呎3(〜240公斤/公尺3)或更少,在一些實施 11 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 1247731
1247731 經濟部智慧財產局員工消費合作社印製 Α7 Β7 五、發明說明(10) 會強化其強度,包括該固定石膏的耐機械變形(例如垂流) 。關於攻方面,因為在該固定石膏的交聯基材中密度降低 與水八化空孔體積增加,特別需要使用三偏磷酸鹽使強度 增加。舉例來說,三偏磷酸鹽化合物可以是一種如三偏磷 酉文鈉一偏Q酸每、二偏磷酸鈉、三偏碟酸卸、三偏磷酸 銨、二偏磷酸鋰或類似物之鹽類。也可以使用這些鹽類的 組合物。在一些實施例中,三偏磷酸鹽化合物是三偏磷酸 鈉。 如果包括在内,三偏磷酸鹽化合物可以單獨使用或 與至少一種之具有500-3000個重複磷酸鹽單元之聚磷酸胺 _〇〇_至夕種夕羧酸化合物及[或]一個界面活性劑結合使 用。如果包括在内,用來製備固定石膏組成物之添加的或 包含於水/燒石膏混合物水溶液中之三偏磷酸鹽化合物量 較好大約是燒石膏重量的01%至大約2%,所添加的或包 含於水/燒石t混合物水溶液中之三偏磷酸鹽化合物量更 好大約是燒石膏重量的0.5%至大約1%。 聚磷酸銨鹽(例如鹽類或其陰離子部份)較好是有500_ 3000個重複單元。如果包括在内,用來製備固定石膏組成 物之"』、、加的或包含於水/燒石貧混合物水溶液中之聚碌酸 銨的量較好大約是燒石膏重量的〇1%至大約2%,所添加 的或包含於水/燒石貧混合物水溶液中之三偏磷酸鹽化合 物量更好大約是燒石膏重量的〇·5%至大約。 聚磷酸鍈鹽(例如鹽類或其陰離子部份)較好是有 1000-3000個重複單元。如果包括在内,用來製 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) —-——1 (請先閱讀背面之注意事項再填寫本頁) 裳--------訂---------· 13 經濟部智慧財產局員工消費合作社印製 1247731 A7 ^~^______ 五、發明說明(11 ) 膏組成物之添加的或包含於水/燒石膏混合物水溶液中之 聚磷酸銨的量較好大約是燒石膏重量的01%至大約2%, 所添加的或包含於水/燒石膏混合物水溶液中之三偏磷酸 鹽化合物量更好大約是燒石膏重量的0 5%至大約1%。 多羧酸化合物(舉例來說,酸、鹽或其陰離子部份)包 括至少二個羧酸鹽或離子基團,至少二個羧酸基,或至少 一個羧酸鹽或離子基和至少一個羧酸基。該多羧酸的化合 物較好是可以溶於水中。該多羧酸化合物是有利的,因為 一般相信他們有助於結晶的結合而形成該固定石膏交聯基 材結構。結果,該多羧酸化合物適合增加強度,藉此減少 固定石膏組成物在處理及加工期間的損害,而且它們可增 加固定石膏組成物的尺寸安定性。本發明的多羧酸化合物 分子量從大約100,000道耳吞至大約i百萬道耳呑。較高分 子量之該多羧酸化合物不是所需要的,因為黏度太高,同 時較低分子量之多羧酸化合物(持續地降低至i 00000道耳 吞以下)效果較小。 在一些實施例中,多羧酸化合物的分子量是從大約 200000道耳吞至大約700000道耳吞,分子量較好是從大約 400000道耳吞至大約600000道耳吞(例如大約5〇〇〇〇〇道耳 吞)。舉例來說,不是作為限制,多羧酸化合物可以由聚 丙烯酸酯、聚甲基丙烯酸酯、聚乙基丙稀酸酯及類似物或 其組合物中選出。在一些實施例中,多羧酸化合物是聚丙 稀酸酯,在此情況中聚丙烯酸酯分子量較好是由大約 200, 〇〇〇道耳吞至大約700, 〇〇〇道耳吞,更好是從大約 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) (請先閱讀背面之注意事項再填寫本頁) 裝 — —訂·—— ¢. 14 1247731 A7 B7 五、發明說明(12 ) 4_00道耳吞至大約__道耳吞。在實施例中,一個合 適的聚丙烯酸醋是ACRYS〇p 644, &賓夕凡尼亞州費城 (請先閱讀背面之注意事項再填寫本頁) 之羅姆&哈斯(Rohm & Haas)可以獲得的商業化產品。 如果包括在内,用來製備固定石膏組成物之添加的 或包含於水/燒石膏混合物水溶液中之多魏酸化合物的量 較好大約是用來製備該混合物所用之燒石膏重量的〇 〇5% 至大約2%,所添加的或包含於水/燒石膏混合物水溶液中 之多羧酸化合物的量更好大約是燒石膏重量的〇ι%至大 約 0.4% 〇 值知一提的是可以單獨使用該多羧酸化合物或與其 它的加強材料一起組合使用。舉例來說,該多羧酸化合物 T以和一偏y酸鹽化合物、具有⑼個重複填酸鹽單 兀之聚磷酸胺鹽(例如1〇〇〇_3〇〇個重複磷酸單元)及[或]一 個界面活性劑結合使用。 經濟部智慧財產局員工消費合作社印製 在依據本發明之石膏組成物的製備期間,在水/燒石 貧混合物中一種或多種界面活性劑的介在物,有助於降低 該混合物的表面張力,而且依次減少乾燥應力,使得固定 石膏的收縮可以降到最低。就這方面而言,一般相信藉由 減少燒石f的水混合物之表面張力,液體施加在石膏結晶 上而在晶體中產生用以抵抗該水溶液的力量的毛細壓力可 以被降低’藉此減少未反應之水溶液由基材蒸發時該交聯 結晶基材結構收縮的傾向。因此,在本發明之實施例中特 別有用的界面活性劑,其特徵是具有可以使水的表面張力 將低至大約40達因/公分或更低的能力。該界面活性劑更 15 本紙張尺度適用中國國家標準(CNS)A4規格(21〇 x 297公釐) 1247731
五、 經濟部智慧財產局員工消費合作社印製 發明說明(13) 好是具有將水的表面張力將低至大約35達因/公分或更低 的能力。合適的界面活性劑例如包括,但不是限制,炔二 醇基界面活性劑、含氟界面活性劑。一種或多種界面活性 劑被包含在用來幵》成該固定石膏組成物之混合物中,而且 也可以使用不同類型之界面活性劑的各種不同組合。 一個炔二醇基界面活性劑的例子是DYn〇l® 604,可 以由賓夕凡尼亞州里海谷氣體產品(Air Pr〇ducts 〇f Lehigh Valley)獲得。含氟界面活性劑的例子可以是烷基磺酸鈉之 陰離子形式氟化界面活性劑(例如LQDYNE® S-103 A)、烷 基叙氯化物的1%離子氟化I界面活性劑(例如LqdyneS® S-106 A),或烷基胺基酸形式的兩性氟化界面活性劑(例 如LODYNE® S-100)。適合用於本發明的界面活性劑的例 子也包括含氟/含矽界面活性劑摻合物,其商品名為 LODYNES⑧S_228M。LODYNES®系列的界面活性劑可以 由瑞士巴塞爾的西巴(Ciba)獲得。界面活性劑的使用可以 是任一有效合適的量。所添加的或包含於水/燒石膏混合 物水溶液中之界面活性劑的量較好大約是〇〇1%至大約i %,所添加的或包含於水/燒石膏混合物水溶液中之界面 活性劑的量更好大約是燒石膏重量的〇 〇5 %至大約〇·2 % 。特別地,界面活性劑可以作為該石膏組成物中唯一的強 化材料,或者與其它的強化材料,舉例來說如三偏磷酸鹽 化合物、具有500-3000個重複磷酸鹽單元之聚磷酸胺鹽( 例如1000-300個重複磷酸單元)及[或]多綾酸化合物或^ 混合物結合使用。 (請先閱讀背面之注意事項再填寫本頁) ·裝 訂—— 奉· 16 經濟部智慧財產局員工消費合作社印製 1247731 五、發明說明(14) 石用組成物也能包括選擇的添加劑 限制,強化添加劑、黏人抝“丨l _ 仁疋不 沴珠山、由w 膠乳之聚合物),膨脹的 贩石…〜發泡體形成的空氣空孔、澱粉,諸如預 明== 二t纖維網(舉例來說,在石膏板上含有本發 明的石貧組成物)。這此 二了選擇的添加劑的各種不同的組 s可以包含於該固定石膏組成物中。如果需要,這些可包 含於該固定石膏組成物中的添加劑,也包含—種或錄的 強化材料。 如果需要’該可選擇的強化添加劑可包含於本發明 的石貧組成物中,以提高在加工期間的強度及過減效率, 其將詳細討論於下。舉例來說,該強化添加劑可包含纖維 素(如紙)、無機的纖維、其他合成纖維或類似物或其組合 物。該加強添加劑,諸如紙張纖維,可以是任一適當的量 。舉例來說,在一些實施例中,該加強添加劑存在的量是 從該固定石膏的中量之大約2%至大約15%。 為了進一步降低密度,本發明的石膏組成物可以選 擇性地包含由水溶性發泡體形成的空氣空孔(其是與水氣 化空孔相反的)。特別地,在製備如目前的板材期間,水 溶性發泡體可以被添加在水溶性燒石膏混合物中。任一種 適合的發泡劑都可以用於本發明的實施例中,舉例來說諸 如PFM 33,可由賓夕凡尼亞州Ambler GEO特用化學品公 司獲得。 除此之外,石膏組成物可選擇地含有澱粉,諸如預 膠化的澱粉或酸改質的澱粉。預膠化澱粉之介在物可增加 本紙張尺度適用中國國家標準(CNS)A4規格mo X 297公釐) 17 ------------_ 裝· II (請先閱讀背面之注意事項再填寫本頁) ϋ n ·ϋ ϋ tr. 1247731 經濟部智慧財產局員工消費合作社印製 A7 五、發明說明(15 ) 該固定且乾燥的石膏澆鑄物之強度,而且可以將在增加濕 氣(例如,較南之水對燒石膏比)的條件下,避免紙張脫層 的危險或將其降至最低。在技藝中有助於預膠化澱粉原料 的技術,舉例來說諸如在至少丨85卞(与85)的溫度下加 熱澱粉原料或其它的方法。合適的預膠化澱粉包括,但不 是限制,可由Lauhoff穀物公司獲得之pcF1〇〇〇澱粉,和可 以由Archer丹尼爾Midland公司獲得之amerik〇r 318 和HQM PREGEL澱粉。如果包含其中,該預膠化澱粉 可以以任一適當的量存在。舉例來說,如果包含其中,可 以被添加至被用來形成固定石膏組成物的混合物中,使得 它存在的量是該故並石膏組成物重量的大約〇·5%至大約 10%。 石霄組成物也能包括一纖維性網。該纖維性往可以 是針織的或不織布的。該纖維網墊較好是由在水合時候, 可以承受該石膏組成物的膨脹之材料所組成。舉例來說, 纖維性網墊可以是紙墊、玻璃纖維墊或其他合成纖維墊的 型式。在一些實施例中,該纖維墊是不織布的,而且可以 包括玻璃纖維。纖維性墊較好是在成形期間,可以塗佈在 該石膏澆鑄物的表面,以形成一個平坦的表面,同時在生 產、處理和塗佈期間,改善整體性、外觀和該乾燥的石膏 澆鑄物的處理性。除此之外,纖維性墊能被用做最後產物 的暴露表面(舉例來說,天花板磚瓦),同樣地,其可以提 供所想要的平坦而令人喜愛外觀。如果需要,纖維性墊可 以有任一適合的厚度。舉例來說,在一些實施例中,纖維 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公f ) ' *----- (請先閱讀背面之注意事項再填寫本頁) --------訂----- #1. 1247731 A7 B7 五、發明說明(16 ) 性墊厚度由大約0.003吋(与0.0076公分)至大約〇·ΐ5吋(与 0.381 公分)。 在一些實施例中,是需要消音性質的(舉例來說,降 低噪音)舉例來說,諸如當本發明的石膏組成物存在於如 消音瓷磚之某些材料時。本發明之該石膏組成物的噪音減 低係數,依據ASTM E 1042-92,較好至少是大約〇 4,更 好是噪音減低係數是在丨.0附近。舉例來說,在一些實施 例中,本發明的石膏組成物證實噪音減低係數大約是〇.5 ,噪音減低係數較好至少大約是〇·6,更好至少大約是〇.7 ,再好至少大約是0.8,而且最好至少大約是〇·9。依據本 發明,該消音值(例如,其噪音減低係數測量所得)隨該固 定石膏交聯基材中的水氣化空孔體積,以及在被用來製備 該固定石膏組成物之混合物中水對燒石膏的比例增加而增 加0 依據本發明的另一概念,所提供的物件含有本發明 的石膏組成物。舉例來說,該些物件可以是壁板、門核心 、結構絕緣面㈣統組件、、;肖音£磚絕緣面板或類似物等 型式。 除了本發明的固定石膏組成物,該物件能包括第二 口疋石㈢、'且成物,其比本發明的固定石膏組成物更緻密 。舉例來說,本發明的固定石膏組成物和第二個更緻密的 固定=膏組成物可以包含分層的個別石膏板,以形成物件 中胃板複β物。5玄第二個固定石膏組成物的密度較好是 至少大約2〇妙尺3(与320公斤/公尺3),更好是至少大約30 (請先閱讀背面之注意事項再填寫本頁) 裳--------訂----- ¢. 經濟部智慧財產局員工消費合作社印製
19 1247731
經濟部智慧財產局員工消費合作社印製 磅/呎3(与479公斤/公尺3),而且再好是至少大約4〇磅/呎% 与639公斤/公尺3)。該第二個固定石膏組成物的密度可以 更高(舉例來說,至少大約50磅/呎3(与799公斤/公尺q,至 少大約60磅/呎3(与959公斤/公尺3)或更高)。相對的,本發 明的固定石嘗組成物的密度較好是低於2〇磅/呎%与32〇公 斤/公尺3),諸如此一密度是低於15磅/呎3(与24〇公斤/公尺 3),或低於大約12磅/呎3(与192公斤/公尺3)。 忒緻始、的石貧板的存在是需要的,舉例來說,因為 它提供一個用以形成本發明之較低密度的固定石膏組成物 的外殼。除此之外,該緻密的石膏板提供在處理時候的濕 強度,以及在形成複合物的乾強度。緻密石膏板的介在物 也可以提高耐火性及耐下垂性,同時也反射聲音(同時本 發明較低密度的石膏板吸收聲音),以助於將聲音通過含 有石膏板複合物的物件的量降到最低。 參考第1圖,複合物1〇是示意說明的。該複合物1〇包 括第一石貧板12,其包括本發明的固定石膏組成物,以及 包括第二固定石膏組成物的第二石膏板14,使得它比第一 石貧板12更緻岔。加強網襯(例如多孔網襯)可以選擇性地 夾在板12和14之間,以利於低密度板12的生產並且提高該 複合材ίο的整體強度。在複合材10中,板12和14可以是任 一個合適的厚度。舉例來說,第一板12的厚度是由大約〇 5 吋(与1.27公分)至大約2吋(与5.〇8公分),同時第二板14的 厚度是由大約0.625吋(与0.159公分)至大約〇 25吋(与〇 635 公分)。 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公爱) 裝--------訂--------- (請先閱讀背面之注意事項再填寫本頁) 20 1247731 A7 ^E____ 五、發明說明(18 ) 第一石貧板12包括第一表面16和第二表面18,而且 第二石貧板14包括第一表面2〇和第二表面22。石膏板12的 表面16是與石膏板14的表面20接觸。纖維性網襯24被塗佈 在石貧板12的表面18上。複合材1〇也包括在石膏板14的表 面22上之壁板紙26。 第2圖說明顯示在一實施例物件,即天花板磚28,中 之複合材。如第1圖,本發明之緻密的、低密度固定石膏 板以及纖維性網襯分別標示為14、12和24。天花板碑28包 括一個岩架30以利使用中附屬配件固定。 第3圖說明兩個接合在一起而形成積層複合物32(舉例 來說’含有一個以上的複合物)的兩個複合物1〇A*1〇B。 積層複合物32含有第一石膏板12A和12B,以及更緻密的 第二石膏板14A和14B。壁板紙26A和26B是分別負載在石 用板14A和14B的外表面22A和22B 〇二複合物10A和10B可 以用任一型式結合在一起。舉例來說,複合物1 〇 A和1 〇B 可以用膠黏劑34結合在一起。雖然膠黏劑34顯示於第3圖 中’在該技藝中任一種普通的技術都適宜經由任一種合適 的材料,諸如石膏、黏合劑、膠、膠乳、黏合劑或相似物 ’但是不限制使複合物1 〇A和1 〇B結合在一起。可以暸解 的是’在一些實施例(舉例來說,使用多步驟的程序)中, 如果需要,單一個第一石膏板12可以夾在兩個緻密的第二 石膏板14A和14B之間。 現在回到依據本發明之固定石膏組成物的製備,石 貧和水的混合物(例如泥漿或懸浮液)被形成。本發明之固 本紙張尺度適用中國國家標準(CNS)A4規格(21〇 X 297公釐) (請先閱讀背面之注意事項再填寫本頁) 裝--------訂---- Φ. 經濟部智慧財產局員工消費合作社印製 21 1247731 五、 濟 部 智 慧 財 產 消 費 合 作 社 印 製 發明說明(I9 ) =膏組成物的水氣化空孔體,積是隨用於製備洗鑄成該 口疋石线成物之燒石膏水純混合物之水與石膏的比例 正比。因此’較高比例之水對燒石膏比被用來製備該混 力在韻疋石貧交聯基材中水氣化空孔體積會更大。 水對料製備該混合物且至少含有3G wt%非纖維性 k石貧的重量比較好是至少大約3:卜更好是由大約3:1 至大約12:卜在一些實施例中’水對用來製備該混合物 且至少含有30 Wt%非纖維性燒石膏的重量比由大約4.5: Ϊ 至大約9 : 1 ’或水對用來製備該混合物且至少含有游。 非纖維性燒石膏的重量比由大約5: !。各種不 同比例之纖維的與非纖維的燒石膏混合物可以被用於本發 吕丁 明的實施例中。當固定石膏組成物是由7〇⑽纖維性燒 石膏所形成時’被用來製備該混合物的水與燒石膏比例至 少是大約4.5:1到大約12••卜較好是,在實施例中之水與燒 石貧重量比是由大約4.5:1到大約9:1,更好^^大約5:1到 大約8:1。 澆鑄該混合物之前,一種或多種強化的材料,舉例 來說如三偏磷酸鹽化合物、具有5〇〇_3〇〇〇個重複磷酸鹽單 凡之聚磷酸胺鹽多羧酸化合物、界面活性劑或其組合物可 以被引進燒石膏的水性混合物中。被引進水性燒石膏混合 物較好是以所加入用以形成該混合物的燒石膏的重量為基 礎。 洗鑄之前,水性燒石膏混合物也可以具有選擇性的 添加劑諸如,但不是限制,強化的添加劑(諸如纖維)、黏 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 1247731
五、發明說明(2〇) 合齊K例如膠乳聚合物)、形成輯在_定基材組成物引 入空孔的水性泡沫、澱粉(諸如預膠化澱粉)、促進劑、抑 (請先閱讀背面之注意事項再填寫本頁) ,、殺蟲劑、殺g劑、殺細_、耐水劑或其他用在先 剞技藝中之任一種添加劑及其組合物。 。亥水|±燒石貧混合物,現在含有強化材料或其他可 選擇的添加劑’’可以㈣拌料濕潤然錢鑄(舉例來 說,成為板材的型式)。在澆鑄形成期間,此處說明的纖 維性網墊可以被塗佈在該混合物的表面上。為了降低乾燥 的成本,如果需要,在燒石膏完全水和之後,濕的石膏澆 鑄物可以被過濾(舉例來說,在大約20到大約50毫米汞 柱)以排掉過多的水分。然後該些過濾或未過濾的石膏澆 鑄物被乾燥(舉例來說,在烘箱或窯中)以形成所需要的固 定石t組成物。 經濟部智慧財產局員工消費合作社印製 重要地,依據本發明的石膏組成物具有尺寸安定性 ,特別疋在加工期間是可以财收縮的。在這方面,在其製 備期間’該固定石膏組成物的收縮大約2%或更低,更好 是大約1%或更低的收縮,再好是大約〇1%或更低的收縮 。相當令人驚訝的,此一低密度的固定石膏組成物可以達 到此一低程度的收縮。 在乾無之後’可以進行先前技藝所熟悉的處理。舉 例來說,该固定石言組成物可以利用表面塗料、樹脂及[ 或]石夕酸鹽浸潰處理以強化石膏組成並且改善物理、化學 的和機械性質。 藉由實施例來說明,一個用以舉例說明低密度固定 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 23 I247731 五、 A7 B7 發明說明(21 ) 石貧板的訪法之流程將被#兒明於下· 塗以灰泥、加速劑和其他乾的添加劑 所需要的水分、紙纖維聚+ Aery sol 644
I 發泡(界面活性劑溶液) 混合/攪拌(濕的)
I 石膏澆鑄/最後固定 乾燥(強度形成) 為了要形成複合材(例如用於物件中),所用之壁板紙 在接近每一個邊緣處有雙重的摺痕。摺痕的邊緣向上而形 成一個盤子狀。由石膏板混合器將緻密的石膏漿層鋪放在 紙上’可以利用一般熟悉的技藝中的技術,適當地監測該 層的厚度與位置。剩餘的燒石膏水溶液混合物被送發至一 額外的混合程序中,以添加更多的水分(以及,如果需要 ’添加強化材料及[或]選擇性的添加劑),以製備用以形 成本發明較低密度固定石膏組成物之混合物。然後如先前 技藝中適當之技術,以軋輥、清潔設備及類似物將低密度 泥漿層鋪放在緻密層上。如果需要,可以使用針織或不織 布纖維網襯。 (請先閱讀背面之注意事項再填寫本頁) 裝--------訂---------. 經濟部智慧財產局員工消費合作社印製
24 1247731 A7 五、發明說明(22) --- ------------φ裝—— {:請先閱讀背面之注意事項再填寫本頁) "此複合物形成可以在—般傳統的石膏板製造線上 订,以進仃固定程序。當該複合材幾乎被水合時 度板的頂端部份可以選擇性的被穿孔,以改善乾燥性質= 時提升其降低。桑音的性質。然後以如板刀或高壓”= 謂该複合材被切成所需要的長度。然後利用如紙邊向下 且無紙或纖維網襯側向上,而使該板可以被乾燥。 可以依據所需要之物件而改變額外的整理方式。舉 例來祝,對於天花板磚而言,該整理包括將其据成所需的 大小、整理、塗裝與包裝。 用於其他應用之整理程序包括,舉例來說,面貼合( 紙面向外)、被貼合(紙面向内)、尺寸整理(末端切割)以及 如果需要’之塗佈程序。 依據本發明之固定石膏組成物的水氣化空孔體積可 以利用下面說明之水氣化空孔體積(EWVV)試驗方法測量 。該試驗使用掃瞄式電子顯微鏡和影像顯微分析,決定該 固定石膏交聯基材的水空孔體積。該試驗可以區分因為發 泡劑或其他類似物,而在該固定石膏組成物中所形成的空 子L 。 經濟部智慧財產局員工消費合作社印製 在EWVV測試準備中,固定石膏組成物首先被製成 。然後以下述方法製備用於用於SEM分析之固定石膏組成 物的樣品:環氧基樹脂(Buhle環氧樹脂被使用),以及環 氧化合物硬化劑首先被放置在個別的杯子中在高真空下抽 氣。在除氣之後,環氧基樹脂和硬化劑在大氣慶之旋轉的 杯子中,以6 ·· 1的比例混合5分鐘進行混合以將空氣的添 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 25 1247731 A7 " -------- -- 五、發明說明(23 ) (請先閱讀背面之注意事項再填寫本頁) 加量減到最低。含這個混合物和這個樣品的杯子,被放置 在-個橡膠的杯架中’然後將其放置在高真空中。然後使 ^遙控電動馬達將環氧樹脂的杯子調整至定纟,將該環氧 樹脂混合物倒在該石膏樣品上。使空氣慢慢地進入該搶室 中同&利用该加壓的壓力使環氧基樹脂進入所有的空間 而形成6亥固定石賞。樣品標籤在熟成前被插入環氧基樹脂 中’以避免任一樣品辨識的困擾。 在熟成之後,以120微米、接著是75微米、45微米 和15微米覆蓋鑽石的金屬輪輕拍該樣品來進行研磨。足 夠的樣品被研磨,已提供石膏的戴面圖式。研磨後使用每 分鐘120轉,在TEXMET(也可以由Buhler獲得)上之9微米 (30分鐘)、1微米(30分鐘)METAm鑽石漿(可由伊利諾州 Bluff湖Buhler獲得商業化產品)拋光。 經濟部智慧財產局員工消費合作社印製 然後使用配備碳附件之Denton真空臺n(Dent〇n Vacuum Desk II)濺鍍系統,使該樣品被塗上一薄碳層。需 要小心的在該拋光的截面上塗佈一均勻的碳塗層,以避免 在影像擷取時產生亮度與對比的跳動。然後每個樣品被塗 上在SEM放大300倍取影像時接地所需的銀。所有的樣品 都是在配備固態後散射電子偵測器之泰普康(T〇pc〇n) SM300 SEM來取像。選擇僅含有水氣化空孔之固定石膏 的連續相,而不包括巨大的不連續點,例如不是交聯固定 石膏基材的一部份之空氣泡沫空孔、紙纖維或類似物的區 域進行影像分析。該SEM分析可以利用金(King)等在K〇na 粉體和粒子(Kona Powder and Particle)第u卷中之,,定旦石芒 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 26 1247731 經濟部智慧財產局員工消費合作社印製 A7 B7 五、發明說明(24 ) 物學用有效SEM影像分析系統,,說明的方法,在此處併入 多考資料中使用其中說明的電腦軟體進行。該影像分析 提供用於該固定石膏組成物之交聯基材的水氣化空孔。 下面的實施例進一步說明本方法,當然不應該被認 為是用來限制它的範圍。 實施例1 用於實驗石膏澆鑄物的製備與各種試驗的步驟 依據本發明製備的含固定石膏組成物的樣品,被用 來比較它們的乾密度、噪音降低值(NRC)和乾收縮。 利用乾摻混製備石膏澆鑄物:300克/3硫酸鈣半水合 物,2.0克含有以糖塗佈之硫酸鈣二水合物細研磨顆粒之 固定加速劑以維持其效率,並且以美國申請專利第3573947 號中說明的方式加熱,其中所揭示的在此處併入參考資料 中;各種不同比例的水和灰泥(也就是燒石膏)。在5公升 的混合器中,以浸泡5秒鐘低速攪拌25秒的方式,然後該 樣品與各種不同量之自來水在7〇T(〜21t)下混合。水和 灰泥(也就是燒石膏)的量是可以變化的,以提供使水和灰 泥的比例是在大約1:1至大約9:1。如此形成的泥漿被澆 鑄至所需要的模型中,以製備石膏澆鑄物(直徑六-吋,厚 度半吋的環)。在硫酸鈣半水合物固定形成石膏澆鑄物(硫 酸鈣二水合物)之後,該還由模子中移出,並且在丨12卞( 〜44°C)通風的烤箱中乾燥至少24小時,或直到它的重量 停止變化為止。然後該乾燥的石膏澆鑄物被用來進行 EWVV試驗,測量密度、噪音降低值和乾收縮。 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 裝--------訂---------— (請先閱讀背面之注意事項再填寫本頁) 27 1247731 A7 經濟部智慧財產局員工消費合作社印製 五、發明說明(25 ) 石膏澆鑄物的密度可從它的體積和重量測量獲得。 石膏澆鑄物的收縮可從他們乾燥前後大小的差異計算而得 石月π鑄物的。呆音降低值可以由標準阻抗管試驗(美國 材料忒驗牟會Ε 1042-92的每一美國材料試驗學會步驟)獲 传。該石t洗鑄物的水氣化空孔體積可以由上面說明之水 氣化空孔體積試驗而得。 EWVV結果,樣品的三次測試平均值,記錄於下面的 表1中。該些結果反映出大約87%純石膏樣品(具有大約13 %雜質)。EWVV直接隨用於製備該該固定石膏交聯基材 的燒石嘗的純度而改變。因此,可預期的越高純度之燒石 局,其EWVV值越高,具有高百分比之雜質的燒石膏可以 預期的EWVV值會更低。每個樣品的十個3〇〇大影像被分 析’而且以這十個影像進行上述EWVV試驗的影像分析。 十個影像被分析的平均值作為測量值,且該EWXX試驗本 身具有大約+/_5%的試驗誤差。 在表中: TMP是指三偏磷酸鈉; APP是指聚磷酸銨; PC是指分子量大約500000之聚丙稀酸;和 S是指可以降低水、燒石膏表面張力的界面活性劑, 其中被澆鑄的固定石膏的表面張力大約是40達因/公分 (dynes/cm) ° 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) 28 ----------—裝--------訂--------- (請先閱讀背面之注意事項再填寫本頁) 1247731 經濟部智慧財產局員工消費合作社印製 A7 五、發明說明(28) 在表II中的數據進一步說明依據本發明可以製備低密 度固定石膏組成物。這些數據也顯示形成該固定石膏組成 物之燒石膏水溶液中水和燒石膏比例增加時,該固定石膏 組成物的密度會降低。由於使用較高之水和燒石膏比例製 成之固定石膏組成物中,具有較大的水氣化空孔體積,而 使密度被降低。 該由測量之NRC值的數據也可以說明,依據本發明而 使用較高之水和燒石膏比例,可以改善消音性質。當沒有 其它的吸音添加劑,諸如紙纖維或類似物時,記錄於表π 中之該固定石膏組成物本身的NRC值是肇因於其消音性質 。具較高NRC值之固定石膏交聯基材可以用來製備具有高 NRC值之低密度石膏基消音碑,而且藉由添加劑的選擇及 其他用來改善消新性能之技術,其可以進一步強化它們的 消音行為。另一方面,藉由使用依據本發明之高nrc值的 組成物,其可以使用較少的紙或其他已知的消音強化材, 而且仍可以達到消音磚的要求或超過工業標準。 再者,一舉本發明使用強化材料製成的低密度固定 石膏組成物比沒有強化材之低密度固定石膏組成物更不會 收縮。因此,任一大小或形狀之固定石膏組成物包括,舉 例來說,板、消音碑、嵌板、門核心或類似物可以被製備 成才示準的大小與間隙,而不會有明顯的收縮以及其伴隨物 的損失,例如碎片。 所有此處提及的參考資料,包括專利、專利申請案 和出版物,特此它們全部被併入參考資料中。 本紙張尺度適用中國國家標準(CNS)A4規格(210 X 297公釐) -----------裝 *-------訂------ (請先閱讀背面之注意事項再填寫本頁) 31 1247731 A7 B7 五、發明說明(29) 雖然本發明已經藉由較佳的實施例而被說明,报明 顯的那些在技藝中熟悉的技術,可以被用來對較佳實施例 進行非此處特別說明的改變。因此,本發明包括在下述申 請專利範圍所界定之本發明的精神與範圍中的所有修正。 元件標號對照 1〇,1〇Α,10Β···複合材 12,12A,12B...第一石膏板 14,14A,14B···第二石膏板 16…第一石膏板的第一表面 18··.第一石膏板的第二表面 20..·第二石膏板的第一表面 22…第一石貧板的第二表面 24.. .纖維的網襯 26、26A、26B···壁板紙 28.. .天花板磚 30···天花板磚突出物 3 2 · · ·貼合的複合材 34.. .黏合劑 -----------裝--------訂--------- (請先閱讀背面之注意事項再填寫本頁) 經濟部智慧財產局員工消費合作社印製 32 本紙張尺度細巾目目家鮮(CNS)A4規格(210 X 297公釐)
Claims (1)
1247731 六、申讀
A8 B8 C8 D8 第9 010 9 8 15號申請案申請專利範圍修正本 修正日期:94年1月 1 ·種口疋石τ組成物,其係藉由一包含下列步驟之方法 所製備: 衣備以燒石T、水和由三偏磷酸化合物、具有 5〇(M_重複魏„元之聚磷㈣、多_化合物、 "面活f生劑及其組合物中選出的強化材料所形成的混 合物,其中存在於混合物中的水與燒石膏的重量比例至 少是3 : 1 ;和 將該混合物保持在足以使該燒石膏形成交聯的基 材固定石膏的條件下。 2. ^申請專利範圍第1項之石膏組成物,其中該強化材料 是三偏磷酸鈉或三偏磷酸鈉與至少一種具有ι〇〇〇_3⑼〇 重複單元之聚磷酸銨。 3. :申請專利範圍第!項之石f組成物,其中該多叛酸化 合物是分子量由200000道耳吞至700000道耳吞的聚丙 婦酸酯。 經 濟 部 智 慧 財 產 局 員 工 消 費 合 4. 如申請專利範圍第丨項之石膏組成物,其中該界面活性 劑疋由炔二醇基界面活性劑、含氟界面活性劑、含矽界 面活性劑及其組合物中選出。 5. 如申請專利範圍第丨項之石膏組成物,其中該界面活性 劑的特性是,具有將水的表面張力降低至40達因/公分 或更低的能力。 如申請專利範圍第}項之石膏組成物,其中該組成物具 ;‘ 規接χ ^ -______ — J J - 1247731 A8 B8 C8 D8 申請專利範圍 有σ呆音減低係數至少約0.4,依據ASTM E 1042-92。 7.如申凊專利範圍第丨項之石膏組成物,其中該組成物係 進乂由以下之至少一者形成··纖維性網襯、黏合劑、 擴張的珍珠岩、澱粉、強化添加劑以及由水性泡沫形成 的空氣空孔。 8·如申請專利範圍第w之石膏組成物,其中用來製備該 混合物之水比燒石膏的重量比率係約4·5: 1至約9:; 的 9.如申請專利範圍第旧之石膏組成物,其中該燒石膏 至少50%重量係-硫酸鈣半水合物。 10· —種含有一石膏板的物件,其中該石膏板包括如申請專 利範圍第1項之石膏組成物。 11.如申請專利範圍第10項之物#,其進一丨包含一第二石 貧板’且該第二石膏板的密度係大於該石膏組成物。 12_如申請專利範圍第"項之物件,其中該第二石膏板具有 -密度至少約20驗3,以及其中該石膏組成物具有一 密度少於約20 lb/ft3。 經濟部智慧財產局員工消費合作社印裂 13·如申請專利範圍第n項之物件’其進一步包含壁板紙, 其中該壁板紙係被擔負在該第二石膏板上。 14·如申請專利範圍第"項之物件,其進一步包含一第三石 膏板,且'該第三石膏板的密度係大於該石膏組成物·; 15.如申請專利範圍第14項之物件,其進—步包含1二石 θ組成物,且該第二石言組成物的密度係小於該第二石 貧板與該第三石膏板之密度。 +紙張尺度過用中固固家標準(2j〇 1247731 A8 B8 C8 D8 六、申請專利範圍
經濟部智慧財產局員工消費合作社印裂 申。月專利耗圍弟1項之石貧組成物 混合物的強化杖料夕曰总ώ 中用末沿成该 強化材科之置係自約0.01%至約5%重量之声 石貧。 几 17·如申請專利範圍第丨項之石膏 r 一 月、、且成物,其中該強化材料 心㈣酸化合物與多《化合物,或-具有.3_ 重複碟酸鹽單元之《酸録與Μ酸化合物。 18 ·如申请專利範圍第1項 春 β組成物,其中用來製備該 混合物之水比燒石膏的重量比率係約3:(至約A卜 19. 如申請專利範圍第& 、I石月、、且成物,其中用來製備該 混合物之水比燒石膏的重量比率係'約5: i至約8:卜 20. 如申凊專利圍第j項之石膏組成物,其中該固定石 組成物最多約收縮2〇/〇。 21· 一種用製備一固定石膏組成物之方法,其包含: 製備至少以燒石膏、水和由三偏磷酸化合物、具有 5 00 3QOG重複鱗鹽單元之聚罐酸銨、多叛酸化合物、 界面活性劑及其組合物中選出的強化材料所形成的 合物,其中存在於混合物中的水與燒石膏的重量比例 少是大約3 : 1 ;以及 將該混合物保持在足以使該燒石膏形成交聯的 材固定石膏的條件下。 膏 混 至 基 (靖先Mti背面之注音心事項本頁) »!裝 . 本‘.%尺度過用中舀舀家標準(CNS)A4 現格(2]G X 29了公g ) 35