TW201240203A - Method for producing polymer/carbon nanotube mixtures in powder form - Google Patents
Method for producing polymer/carbon nanotube mixtures in powder form Download PDFInfo
- Publication number
- TW201240203A TW201240203A TW100147337A TW100147337A TW201240203A TW 201240203 A TW201240203 A TW 201240203A TW 100147337 A TW100147337 A TW 100147337A TW 100147337 A TW100147337 A TW 100147337A TW 201240203 A TW201240203 A TW 201240203A
- Authority
- TW
- Taiwan
- Prior art keywords
- polymer
- mixture
- grinding
- carbon nanotube
- carbon
- Prior art date
Description
201240203 六、發明說明: 【發明所屬之技術領域】 本發明係為一種於製造及/或加工呈粉末型式之 聚合物/奈米碳管混合物之方法,其包含研磨由奈米碳 管以及聚合物粒子組成之混合物的步驟。 本發明更進-步關於可藉由本發明的方法得到之 呈粉末型式之聚合物/奈米碳管混合物,並且使用此呈 粉末型式之聚合物/奈米碳管;^合物生產製備電極。 【先前技術】 奈米碳管(CNTs)的優異性質是眾所周知的。舉例 來說’其強度大於鋼約10(M吾,其熱傳導率約與鑽石 一樣優異,其熱穩定性在真空狀態下可高達誦义以 及其導電度疋銅之導電度的數倍。然而,通常當可以 均勻为散奈米碳官以及建立碳管與媒介之間的最大接 觸時,這些結構相關的特徵才可在分子層級出現,亦 即使其等與媒介可相容,以及可穩定的分散。 以導電度來看,在理想的情況下,進一步必要形 成管網絡,其中其等只在兩端處能夠接觸或者足夠靠 近。在這情況下,奈米碳管應盡可能的使其進行個體 化(individualisation,即無黏聚物)’非對準以及在一 個恰可形成網絡的濃度下存在,其藉由呈奈米碳管濃 度(展透限制)的函數之導電度的突升反應。 為達到此複合材料更優異的性質,像反應型樹脂 201240203 如環氧化物,其優異的分散性質以及奈米碳管的個體 化是必要的,因為龐大的黏聚物會導致破損部位(Zhou, eXPRESS Polym. Lett. 2008, 2, 1,40-48)以及接著該組 成物之機械性質的退化反而可被觀察到。 於鋰離子電池中使用奈米碳管已是習知技術。舉 例來說,WO 95/07551 A1提到链離子電池,其特徵於 其陽極是以碳纖維材料所構成,其包含了具有平均粒 徑為0.1到100微米之纖維凝聚體或非凝聚體纖維團 塊。在此情況下,具直徑從3.5到7〇 nm的薄線型碳 纖維相互交織並且此纖維與鋰離子相互嵌入。陰極同 樣也包含了碳纖維。 二w,bP2 081 244 A1揭露具有電流收 =、電極以及排列於其上之活性物質層。活性物質 二::結構網絡以及活性材料組成物。結構網絡包 網絡。活性材料組成物包 藉由流體床方法製造奈米碳管的 :程形成的巨觀之凝聚盤,有時尺寸會在毫= 奈米碳管使用於鐘離子電池時,4= 廢U不未碳管的均勻分布。通常藉由例如球磨機、 降2、、輥機制或喷射分散機於此材料施以外觀尺寸 了 電 201240203 極材料。此黏聚物藉由在纖維之間有接觸點的汽相-生 長碳纖維的糾結而形成。至少部分接觸點是化學鍵結 方式接觸點。纖維黏聚物係藉由墨缩以及粉碎自氣相 中生長之分支的碳纖維而產生。 WO 2009/1 〇5863揭露複合電極的材料,其由碳塗 佈的複合氧化物、碳纖維以及點結劑組成。此材料是 藉由活性電極材料以及共同接觸面(Μ娜d)的纖 維化碳以及添加黏結劑到共同合物Μ 低其混合物的黏性。較佳的纖維化碳是氣相_ 更進-步的敘述是經共研磨後,在合 適的溶劑裡此黏結劑以溶液型態添加。 在這些降低外觀尺寸的方法中,°均可觀察到不欲 產生之精細分佈的塵埃,其於工作時對健康及安全是 有害的。更進一步觀察到,碳奈米材料會顯著地沉降 在研磨管柱以及研磨物體的表面,因此在研磨製程後 必須小心的移除。再者,經常產生極不均勻的粉末, 其包含了巨觀尺寸的石墨板塊。最後’發現在幾天期 間後’研磨後所得到相當小的奈米碳管凝聚體容易重 新聚集。 另一重點為降低尺寸的方法需要較大量的能源以 達到預期尺寸降低的結果。 【發明内容】 因此本發明的目的之一在於至少部分克服先前技 6 201240203 術的缺點。特別的是,本發明的目的之一在於提供一 種方法,其可以較不耗費能源的方式量產較小尺寸的 奈米碳管凝聚體,以及所得到之產物可以玎靠的處理 以及能夠被用來製造鋰離子蓄電池或者其他不需改變 現有方法之電化學應用。 ' 奈米碳管組成物在一合適的溶劑經吸收後可更進 一步得到穩定的分散體。 根據本發明用於製造及/或加工呈粉末梨式之聚 合物/奈米碳官混合物的方法,包含研磨由奈米碳管以 及平均粒徑H〇oimm M $1〇mm之聚合物粒子 組成之混合物的步驟可達到本發明之目的。 本方法的特點,在於研磨係於wt%到$15 wt·% (以混合物_重量表示)不溶解聚合物粒子的 液相物詩在下以及在溫度低於粉末齡的熔點下進 行。 令人驚S牙的是,依據本發明的方法,發現可使用 簡單低迠量研磨方法,而不影響其研磨結果。此所得 到的呈粉末型式之聚合物/奈米碳管混合物明顯的減 >、灰塵敏感性,可流動性以及不會貼附到研磨管柱的 管壁或研磨機制的其他部分。 最後,發現藉由本發明提供之方法所得到的呈粉 末型式之聚合物/奈米碳管混合物,在適當的溶劑中經 分散後,其可穩定的分散且無沉澱或只有技術上微不 足道的沉澱發生。 201240203 低能量研磨和混合粉末之間的區別是不明確的。 因此,因此根據本發明,混合個別的粉末混合物也包 括在“研磨”一詞若發生可能存在的奈米碳管凝聚體之 尺寸的降低。研磨也可使用混合器,其可引發研磨的 效果。 根據本發明的方法’研磨可在wt %到<15 wt·% (以混合物的總重量表示)的液相物質存在下進 行,其不溶解聚合物粒子。當然,不存在會溶解聚合 物粒子之其他液相。 因此無法得到聚合物溶液,但相對的固態聚合物 粒子以及固態奈米碳管以及/或奈米碳管凝g體會一 起分散在此液相中。相對少量的液相可確保在研磨過 程前防止粉塵的產生,例如藉由此液相提供的奈米碳 :。:PVDF製備的聚合物粒子中之非溶解液相為酒 精即為-例。也可以完全避免液相並進行乾式研磨。 再者’研磨是在溫度低於聚合物粒 進行。這也確保在研磨過程中,固態奈米碳管Hi CNT凝聚物以及固1¾合錄子可機械式接觸另1 者。在聚合物粒子具有一炫點範圍而非單 況下只==:__最低點以下進二 要聚口物不融化’原則上是可以在 於室溫或在高溫下操作。例如, =- 以致,脆性’從而影響其在研磨過程;=, 在溫度較〶時,將有較強的奈米碳管和/或奈米碳管的 201240203 聚合物的黏附而聚集在聚合物粒子上是所欲的。 原則上材料溫度隨著研磨過程而變動是可行的。 例如’其最初在第一個溫度下研磨,然後在第二個溫 度繼續是可行的,其中第一個溫度低於第二個溫度。 在研磨過程中也可設定溫度梯度。 依據本發明的方法,原則上可使用所有的研磨設 備。一個優點是即使最簡單的設備亦可使用,因為所 得到的粉末混合物仍然可流動。 流動性指的是自由流動的程度或整體材料的流動 行為。特別來說,在研磨後所得到的粉末形式混合物 展現良好的流動性。這些混合物的流動指數可>10 ml/s ’較佳的是〉15 ml/s,更佳的是> 2〇 mi/s以及 特別較佳的是>25 ml/s (根據ISO標準6186量測其 "IL動性質’使用流動性測試儀Karg-Industrietechnik (Code No 1012.000) Model PM,以及 15mm 喷嘴進行 I測)。可流動的混合物為它們的劑量和加工提供了顯 著的優勢。 原則上聚合物粒子可以用任何聚合物製備,其中 可能包括提供添加劑如填料或其類似者。其有利於聚 合物材料牽涉進一步所預期奈米碳管的加工。例如, 聚合物可以是黏結劑。 根據本發明,聚合物粒子其平均粒徑為2 〇.〇〇1 mm到$1〇 mn^此數值一般可以使用雷射繞射光譜 儀方法里測(例示之儀器為具有Hydro S分散單元之 201240203
Mastersizer MS 2000,Malvern 公司.u , x A』,水相卜較佳的 尺寸範圍在2 0.02 mm到$ 6 mm。更佳的是 , 徑在2 0.05 mm到52 mm以及特別較佳的是 mm 到 $ 1 mm。 一 根據本發明的方法’所得到的奈米碳管為凝聚體 (黏聚物)型式以及/或非凝聚體型式。 本發明中的奈米碳管全為單管壁或多管壁的圓柱 型態(舉例來說’在專利Iijima US 5,747,161; Tennant WO 86/03455所提到的)、螺旋型態、多螺旋型態、杯 狀堆疊型態(其由一邊封閉的錐形杯或兩邊開放的錐 形杯組成(舉例來說,在專利Geus EP 198558以及 Endo US 7,018,601中)),或具有洋蔥型結構。較佳使 用圓柱型態、螺旋型態、多螺旋型態以及杯狀堆疊型 態或其混合物的多管壁奈米碳管。奈米碳管有利的長 度對於外部直徑比為25,較佳的是2100。 相對於前述所提到的習知螺旋型態的奈米碳管, 其僅具有一連續或者中斷的石墨稀層,在其中也有奈 米碳管的結構,其由數個石墨烯層組成,其可結合形 成堆疊、或捲起。這也可以是多螺旋狀型態。這些奈 米碳管如DE 10 2007 044031 A1中提及的,其全部範 圍做為參考。這結構之行為與單螺旋型態的奈米碳管 相比較,就像多管壁的圓柱型態奈米碳管(圓柱 MWNTs)之行為與單管壁的圓柱型態奈米碳管(圓柱 SWNTs)之相比。 201240203 不像在洋蔥型結構的情況下,獨立的石墨稀層或 石墨層於奈米碳管中,就像在截面上所看到的,明確 地從奈米碳管的中心連續地延伸至外緣而不中斷。舉 例來扰,這可以允許改良的以及較快速的讓其他材料 插入至碳管網絡中,因為更開放的邊緣是可以當作插 入點的入口區域,其是相對於單螺旋結構的奈米碳管 (Carbon 1996,34,1301-3)或具洋蔥型結構的 CNTs(Science 1994, 263, 1744-7)。 【實施方式】 根據本發明中之方法的實施方式會在下文進行解 釋,實施方式也可與其他任何想像的方法來結合,除 非文意明確意味相反的意思。 根據本發明中之方法的實施方式中,具有平均黏 聚物尺寸在20.001 mm到$ 1 〇 mm之間之奈米碳管 黏聚物的型態提供奈米碳管。 黏聚物型態是以奈米碳管型態存在,其中一般而 言是指已經在市面上可取得的。幾種黏聚物之間的結 構類型是可以區別的(可參考例如Moy US 6,294,144): 鳥巢結構(BN)、精梳紗結構(CY)以及開放性網絡結構 (ON)。更進一步的黏聚物結構是已知的,舉例來說, 奈米碳管能以蓬鬆紗方式來排列(WO PCT/EP2010/004845)。更進一步的敘述是,平行表面 排列的奈米碳管是以地毯或森林型態,也就是所謂的 201240203 森林結構(例如於專利Dai US 6,232,706以及Lemaire US 7,744,793)。在此情況下,鄰近的碳管主要是相互 平行排列。上述提到的黏聚物型態也能以其他合適的 方法與它者混合或者以混合混成物來使用,也就是說 不同的結構可存在於一個黏聚體内。 黏聚體較佳的平均黏聚體尺寸為2 〇.〇2 mm。此數 值一般可以使用雷射繞射光譜儀方法量測(儀器為具 有 Hydro S 分散單元之 Mastersizer MS 2000,Malvern 公司;於水相)。黏聚物尺寸其上限較佳的尺寸範圍在 5 10 mm以及更佳的是$ 6 mm。更佳的是,平均黏聚 物尺寸在2 0.05 mm到$2 mm以及特別較佳的是2 0.1 mm 到 £ 1 麵。 依據本發明方法之另外一個實施方式為研磨於> Owt·%到Slwt.%的液相(以混合物的總重表示)存 在下進行。液相的比例較佳的是從2 〇 Wt·%到£ 0.1 wt.%以及較佳的是從2 〇 wt.%到$ 0.01 wt.%。總體 而言,雖然技術上無法避免的水分痕跡也包括在内, 但也可使用乾式研磨製程。 根據本發明’在研磨過程中的能源輸入應該需要 夠低,因此CNTs本身的所不欲之縮短,特別是在CNT 凝聚體、奈米碳管,尤其是在凝聚體部分,其不會發 生或只發生至不明顯的程度。能源輸入可以藉由使用 於研磨設備之馬達的瓦數消耗來計算而得。依據本發 明方法之部分的實施方式,其研磨製程可將能源輸入 12 201240203 控制衫o.lkWh/kg(以由奈米碳管以及聚合物粒子組 成的混合物表示),其他的實施方式中可以控制在〈 0.05 kWh/kg 或 $ 0.01 kWh/kg。 依據本發明方法之部分的實施方式,進行研磨製 程的溫度是從2 -196 Y到S ! 8〇 %。當然, 中’不會超過聚合物粒子的炫點。較佳的溫度為落於^ -4〇°C到$1〇〇〇C之範圍。舉例來說,以此方式可 在較佳使用的聚合物如聚二氟亞乙烯(依照其精確材 料,從-40。(:到-30。〇之玻璃轉移溫度之上或之下 進行操作。 依據本發明方法之部分的實施方式(如果奈米碳 管係以奈米碳管黏聚物的型態提供),研磨可以此方法 進行,以致研磨後之奈米碳管黏聚體的平均尺寸為> 〇·〇1μιη到$20μιη。如上所解釋,黏聚體的尺寸可使 用雷射繞射光譜儀方法量測。經研磨後較佳的黏聚體 尺寸,特別是可用以製備電極材料的,為從2 〇.丨 到$1〇μηι以及更佳的是21μιη到$7μιη。 依據本發明方法之另一個實施方式(如果CNTs係 以CNT黏聚物的型態提供研磨可以此方法進行, 以致其中經研磨後奈米碳管黏聚物的BET表面為> 25 m2/g 到 < 50 m2/、& 5〇 m2/g 到 < 15〇 m2/g 或者> 150m2/g到<400 m2/g。此等BET表面可以是奈米碳 管纖維縮短的良好指示(縮短係不欲出現在電極材= 的應用)’其不會發生或者是僅有不明顯程度的發生。 13 201240203 較佳的是,BET表面是介於2 80m2/g到S120m2/g, 以及更為較佳的是,^:90m2/g到$110以及更佳的是 2 120 m2/g到S 400 m2/g。根據在—196 °C下的多點 BET方法(相似於Din ISO 9277),BET表面可以藉由 氮氣吸附法來量測。 依據本發明方法之另一個實施方式,奈米碳管以 及聚合物物體係以重量比例為2 〇〇5:1到S 20:1提 供。較佳的比例是2 0.05:1到$20:1以及特別較佳的是 ^0·9:1到^^:丨。在這些重量比例中,所得之奈米碳 管/聚合物混合物可不經修飾而使用於製備電極材 料,其聚合物滿足所使用之黏著劑的功用。 依據本發明方法之另一個實施方式,奈米碳管可 以是多管壁奈米碳管,其具有平均外徑為23nm到$ 00 m較佳的疋>5nm到$25賊以及長度對直徑 比例為2 5,較佳的是$ 1〇〇。 本發明方法之另-個實施方式,聚合物粒子 ::勿組成’该聚合物係選自由以下所組成之群 1*夂$« ^"乙稀&、聚乙烯醇、聚環氧乙烯、聚乙稀 ==化聚環氧乙稀、交聯聚環氧乙稀、聚 丙制聚值甲基丙埽酸曱醋、聚偏二氟乙稀、聚六氟 乙缚之共聚物、聚丙稀酸乙醋、聚四 稀、聚丙歸腈、聚乙叫聚乙烯、 : L乙稀:丁二烯共聚物及/或聚笨乙稀及/或其 八入 佳的疋聚偏二氟乙烯(PVDF)。 201240203 依據本發明方法之另-財施方式,成粉末形式 之聚合物/奈米碳管混合物或含有高達15 wt% (相對 於混合物的總重则目之聚合物/奈米碳管混合物,其均 為研磨後所制的,在額外的步馳分散於溶劑卜 所得之混合物或分餘可直接t作含有可用以生產電 極材料之黏著劑配方。聚合物較佳的是溶解在溶劑中。 ^較佳的是,溶劑係選自由内醯胺、酮類、腈、醇、 環醚及/或水所組成之群組。溶劑更佳的是N—甲基吡咯 啶酮,其對於PVDF是合適的溶劑。分散在pvDF中 減少尺寸之奈米碳管及/或奈米碳管凝聚體的穩定分 散液可以此方式加工,直接進一步生產電極材料。相 較於無聚合物之研磨、溶解聚合物黏著劑以及分散奈 米碳管凝聚體的市售途徑,發現根據本發明之方法可 達到節省能源。 本發明更進一步提供呈粉末型式之聚合物/奈米 碳管混合物或含有高達15 wt.%液相(相對於混合物的 總重)之聚合物/奈米碳管混合物’其均可藉由本發明中 的方法而得到。極為較佳的混合物為乾燥的混合物, 其傾向使混合物產生具有一比例為2 0 wt.%到$ i wt.%之液相(以相對於混合物的總重表示)。 關於細節和較佳的實施方式’參考了上述意見以 避免重覆。 依據本發明用於生產電極,其更進一步提供呈粉 末形式之聚合物/奈米碳管混合物的用途。如先前已解 15 201240203 釋的,用於聚合物的溶劑可能添加到前述所得到,較 佳的是乾燥混合物中,以便於舉例來說生產導電膠, 選擇性的連同生產其他電化學活性化合物。 在混合物的較佳用途中,電極可以是用於光伏打 電池的電極,較佳的是光-電化學太陽能電池、燃料電 池、電解槽、熱-電化學電池、蓄電池以及/或電池。較 佳的例子為鋰離子二次電池。 本發明係更進一步關於藉由使用根據本發明呈粉 末形式之聚合物/奈米碳管混合物或含有高達15 wt.% 液相(相對於混合物的總重)之聚合物/奈米碳管混合物 來製備電極。 本發明現在藉助下列例子及圖片更詳細解釋,但 並不加以侷限於其。 使用含有PVDF之研磨CNTs的應用實施例: 定義: 奈米碳管:從Bayer MaterialScience公司取得 Baytubes® C150HP。此為多管壁奈米碳管,其具有平 均外徑為13nm到16nm以及長度超過Ιμπι。其更 進一步以具平均粒徑為0.1 mm到1 mm的黏聚物形 式提供。 PVDF :從solvay Solexes公司取得聚偏二氟乙 稀。材料具有熔點範圍(ASTMD 3418)為155 - 172 0C 以及平均粒徑為< 180 μιη。 201240203 在每一個案例中,2g的奈米碳管以及2g的PVDF 添加到分析研磨機(型號:A10 Janke and Kunkel (IKA)) 中°轉子是由一個槳與具有直徑55mm的兩個葉片所 組成。轉子的轉速為20000/分鐘,其最大圓周速度為 58 m/s。在研磨過程中,研磨機藉由水循環進行冷卻, 因此溫度不會超過所使用的聚合物之熔點。 每一個新的測試,研磨時間會變化以系統性地研 九研磨時間對於被研磨之表面材料的效應。被言膜之 表面材料之重要參數為光學印象(均勻性、流動行 為)、奈米碳管凝聚體的粒徑分佈、BET表面以及微觀 外表。 即使經過一段短研磨時間,得到高度可流動、光 予上均勻、可容易從研磨管腔内移除的粉末亦可能成 立。在不添加PVDF的比較例中,觀察到類似於石墨 之平板成形於容器内管壁上,其僅能以強烈機械力移 除。更進一步觀察到在研磨過程中含有PVDF,其所 形成的粉塵少於研磨奈米碳管不添加pvDF時。 即使在研磨5分鐘後,進行量測^^曱基吼咯啶酮 (NMP)的粒從分佈,可顯示其最小的粒徑(以雷射繞射 進行量測;邀#茗#部分達到5_6 μπι,經過更長 的研磨時間並不會明顯減少。此數值是在將粉末不額 外使用其他處理(舉例來說像是超音波)麟至ΝΜΡ 中所測得。 光學檢驗揭露奈米碳管凝聚體在這些樣品中沒有 17 201240203 可見的沉澱。 在這些奈米碳管的性質中,有利的是單一奈米石炭 管在研磨過程中,其對應的應用性質不會產生降解。 未受損傷(無缺陷)和最長奈米碳管具有優異的電氣 和機械性質。為了研究以及確保這一點,在不同的研 磨時間後測定樣品的BET表面。 在此狀況中,BET表面顯著增加為清楚顯示奈米 碳管的損傷。這是基於假設BET表面的增加是由奈米 碳管碎片所造成以及形態學上的改變(缺陷)。 在一系列比較例測試中,於行星式球磨機不添加 PVDF ’經高能量機械處理短時間後,可顯示其BEt 表面從186m2/g至較高於兩倍之427 m2/g。 圖1顯示根據本發明中,呈研磨時間的函數、在 根據本發明之研磨後奈米碳管凝聚物與PVDF之現合 物的BET表面之態勢圖。〇分鐘量測值是在奈米碳管 /PVDF樣品上所量測,其樣品是簡單地手動攪拌而不 使用機械處理所製備。量測係在氮氣吸附下進行,其 根據在-196 0C下多點BET的方法(相似於DIN ISO 9277) 〇 如可見於圖1,數值分布在約1〇6 m2/g附近,幾 乎與研磨時間是無關的’在3G分鐘後具有朝更高之數 值的趙勢。然;@,此顯著的相反於在比較例中所觀察 到的上升。 在研磨奈米碳管凝聚物期間,聚合物的正面效應 201240203 ^要指標可藉由電子式脚錢微鏡影像圖2至4所 =。上述所有在實施财_的樣品均可以相應方 巧加以夹傲。 依此方法的實施例,樣品經研磨7分鐘後,最初 =個圖面在不同倍率下所呈現。圖2倍率為1〇〇:1, 才目辦大的聚合物粒子,其粒徑在5〇㈣到動叫範 、人<間’可在除了甚小的奈米碳管凝聚體而被識別。 足可以類似地在圖3中清楚的看見,其倍率為995:1。 根據圖4 (倍率為4973:1 ),粒子可被明確地辨識 ^奈米碳管凝聚體。已可在表面上看管 纖維。 、不侷限在單一理論中,將假設CNT凝聚體的附著 代表於本發财法中可實現減少粉塵形成、減少在奈 米後管凝聚體與PVDF於研磨期間再凝聚的發生以及 促進粉體樣品的流動行為之論證。 製備電池之電極的應用實施例如下: 6 g如上述應用例所述製造之呈粉末型式的聚合 物/奈米碳管之混合物分散在使用溶解板(直徑為 40mm)的N-甲基吼咯啶_溶劑中。高能量混合器的轉 速為2000 rpm,時間為1.5小時。在最後一個步驟中, 45 g 的活 性 材 料 NM3100 (LiNiOO,33CoO,33MNO,33〇2) (Toda Kogyo 公司所提 供)被摻混到分散液中以及混合物在700ipm下進行分 201240203 散1.5。分散液在雙壁的容器中以維持溫度,因此其溫 度可維持在23°C。鋁箔以所獲得之膠塗布,其濕塗佈 膜的厚度為250 μιη。此膜在60°C以循環氣體氣候機 櫃下乾燥隔夜。用於製備電池的陰極可藉由沖壓乾膜 而製備。此類電極的放電性質當包含在半電池中可被 表徵。結果例證於圖5。 【圖式簡單說明】 圖1 根據本發明中的方法,顯示BET表面在研 磨時間上的相依關係 圖2-4 根據本發明中的方法,顯示所得之混合 物 圖5 根據本發明中的方法,顯示在半電池測試 中之電極的放電容量 【主要元件符號說明】 無
Claims (1)
- 201240203 七 申請專利範圍: 1· 一種用以製備及/或加工呈粉末形式之聚合物/奈米 碳管混合物之方法,其包含研磨混合物之步驟,該 混合物由呈凝聚體蜇態及/或非凝聚體型態之奈米 碳管,以及具有平均粒徑在2 0.001 mm到$ 10 mm 的t合物粒子所組成, 其特徵在於 該研磨係在2 〇 wt.%到$15 wt.% (以混合物的總 重量表示)不溶解聚合物粒子的液相物質的存在 下’以及在溫度低於該粉末粒子的熔點以下進行。 2. 根據申請專利範圍第1項之方法,其中該呈凝聚體 型態之奈米碳管係以具有尺寸為2 0.001 mm到$ 10 mm之奈米碳管黏聚物形式提供。 3. 根據申請專利範圍第1或第2項之方法,其中該研 磨可在溫度> -196 °c至$ 180 °C進行。 4·根據申請專利範圍第2項之方法,其中該研磨係於 不米碳官黏聚物之平均黏聚物於該研磨後尺寸在> Ο.ΟΙμιη至$20μιητ之方式進行。 5.根據申請專利範圍第2項之方法,其中該研磨係於 奈2米碳管黏聚物的BET表面於該研磨後為仝25 m2/g 至 <50m2/g’ >50m2/g 至 Sl50m2/g4> 15〇m2/g至y00m2/g之方式進行。 6·根據申請專利範圍第1項之方法,其中該奈米碳管 以及该聚合物粒子係以重量比例為2 〇 〇5:1至$ 21 201240203 20:1提供。 7. 根據申請專利範圍第1項之方法,其中該奈米碳管 為多管壁奈米碳管,其具有平均外徑為^】 £ 100 nm以及長度相對於直徑比例為>5。 8. 根射請專利㈣第丨項之方法,其中該聚合物粒 子由聚合物組成,該聚合物係選自由以下所組成之 群組:聚乙酸乙烯酯、聚乙烯醇、聚環氧乙烯、聚 乙烯吡咯啶酮、烷基化聚環氧乙烯、交聯聚氧化^ 烯、聚乙烯醚、聚甲基丙烯酸甲酯、聚偏二氟乙烯、 聚六氟丙烯和聚偏二氟乙烯之共聚物、聚丙烯酸乙 酯、聚四氟乙烯、聚氣乙烯、聚丙烯腈、聚乙烯〇比 咬、聚乙稀、聚丙稀、苯乙烯·丁二稀共聚物及/ 或聚苯乙烯及/或其共聚物。 9. 一種呈粉末形式之聚合物/奈米碳管混合物或含有 高達S 15 wt.%之液相(以混合物的總重量表示)之 聚合物/奈米碳管混合物,其可根據申請專利範圍 第1項至第8項之方法獲得。 10. 根據申請專利範圍第1項之方法,其中在研磨後獲 得之呈粉末形式之聚合物/奈米碳管混合物或含有 高達S 15 wt.%之液相(以混合物的總重量表示)之 聚合物/奈米碳管混合物,係在額外步驟裡分散至 溶劑中。 根據申請專利範圍第1〇項之方法,其中該溶劑係 選自由内醯胺、_類、腈、醇、環醚及/或水所組 22 201240203 成之群組。 12. 根據申請專利範圍第11項之方法,其中該溶劑是 N·曱基吼洛唆酮。 13. —種可藉由根據申請專利範圍第10項至第12項中 一項之方法獲得之分散液。 14. 一種將根據申請專利範圍第9項之呈粉末形式之 聚合物/奈米碳管混合物或含有高達S 15 wt.°/〇之液 相(以混合物的總重量表示)聚合物/奈米碳管混 合物用於製備電極之用途。 15. —種電極,其可自根據申請專利範圍第9項之呈粉 末形式之聚合物/奈米碳管混合物或含有高達S 15 wt.%之液相(以混合物的總重量表示)聚合物/奈 米碳管混合物或第13項之分散體獲得。 16. 根據申請專利範圍第14項之用途,其中該電極可 以為用於光-電化學太陽能電池、燃料電池、電解 槽、熱-電化學電池、蓄電池以及/或電池之電極。 23