TW200902645A - Ink composition for roll printing - Google Patents
Ink composition for roll printing Download PDFInfo
- Publication number
- TW200902645A TW200902645A TW97111876A TW97111876A TW200902645A TW 200902645 A TW200902645 A TW 200902645A TW 97111876 A TW97111876 A TW 97111876A TW 97111876 A TW97111876 A TW 97111876A TW 200902645 A TW200902645 A TW 200902645A
- Authority
- TW
- Taiwan
- Prior art keywords
- pig
- printing
- ink composition
- weight
- parts
- Prior art date
Description
200902645 九、發明說明: 【發明所屬之技術領域】 本發明係關於一種滾印用墨水組成物,更詳細地說, 本發明係有關於一種包括有含氟基之丙烯酸共聚物樹脂、 5具有乙烯性不飽和雙鍵之多官能基丙烯酸單體、熱聚合起 始劑、著色劑、以及溶劑之滾印用墨水組成物。 本案主張之優先權受益於韓國專利局於2〇〇7年5月14 (' 日提出之韓國專利申請書第10-2007-46318號的申請日,且 其内容完全包含於本說明書之中。 10 【先前技術】 於今日的資訊化社會中,電子顯示裝置(electronic display device)的角色變的越來越重要,各種電子顯示裝置 廣泛地應用於多種的產業領域之中。因這些電子顯示器領 15域一再發展,故適合多樣化資訊社會需求的新功能電子顯 , 示裝置已持續性地開發出來。 通常,所謂電子顯示裝置是一種將多#資訊通過視覺 傳達給人的裝置。換言之,電子裝置可定義為將各種從電 ▲子機器輸出的電子資訊訊號轉換成可以視覺辨識的光資訊 20 Λ號的裝置,也能定義成做為人與電子機器之連結媒介的 裝置。 在這些電子顯示裝置中,利用發光現象產生光資訊訊 號顯示者稱為發光型顯示裝置此㈣),而以 反射、散射、或干涉現象等調光方式顯示者稱為受光型顯 200902645 示裝置(non-emissive display)。亦可稱主能動型顯示裝置 之月il述發光型顯示裝置可舉例如··陰極射線管(cath〇de ray tube ; CRT )、電漿顯示裝置面板(piasnaa display panel ; PDP)、發光二極體(light emitting diode ; LED)、或電 5 致發光顯示裝置(electroluminescent display : ELD )等等。 又’亦可稱被動型顯示裝置之前述受光型顯示裝置可舉例 如:液晶顯示裳置(liquid crystal display ; LCD )、電化學 顯示裝置(electrochemical display : ECD )、或電泳顯示裝 置(electrophoretic image display : EPID)等等。 10 作為電視和電腦用顯示器的畫像顯示裝置之中,使用 歷史敢悠久的顯示裝置為陰極射線管(CRT ),雖然陰極 射線官因其顯示品質、以及經濟性等等方面而具有最高的 佔有率,但是仍具有重量大、容積大、以及消耗電力高等 等許多問題。 15 然而,隨著半導體技術的急速進步,因各種電子裝置 的固體化、低電壓、以及低電力化,電子機器必須跟著小 型化 '以及輕量化以成為適合新環境的電子顯示裝置。換 言之,對於具備薄、輕、低驅動電壓、以及低消耗電力特 性的平板面板(flat panel)型顯示裝置的需求急遽增大。· 20 目前所開發的各式各樣平板顯示裝置中,液晶顯示裳 置較其他顯示裝置具備薄、輕、消耗電力低、以及驅動電 壓低等特性,同時其顯示的畫面較接近陰極射線管所顧干 的畫面,故可廣泛地應用於各種電子裝置。而且, 晶顯示裝置製造容易,故其可適用範圍更加擴大。 200902645 為了使液晶顯示I置彩色化,須具備有由紅色、 綠色⑹、以及藍色(B)等三原色所構成的彩色滤光片。 使用前述紅、綠、以及藍等三原色構成的各種光阻製 造彩色遽光片之光_影法,係在由麵基板上形成之愛 色矩陣所分隔開的畫素部上’進行红色、綠色、以及藍色 的各個光阻組成物之塗佈、曝光、以及顯影等製程。由於 前述光微影法不僅浪費材料,製程複雜,而且使用之裝備 價格昂貴,因此在製造液晶顯示單元的過程中佔有相當部 分的時間以及費用。 10 最近,有各種新的製程方式取代習知的光刻微影方 式’其中具代表性者為滾印方式。 然而,從前的滾印法於進行滾印時,為了使圖案轉印 時圖案能平順地由包覆層(7、,夕Η 7卜)轉印至基板上,包 覆層採用表面張力低的PDMS ( p〇lydimethylsil〇sane )等作 15為材料,但若墨水的表面張力不比包覆層材料的表面張力 低的忐,則無法得到良好的塗佈結果。因此,為了使滚印 用墨水組成物之表面張力低於包覆層表面之表面張力,必 須添加效果佳的介面活性劑以達到降低墨水組成物内表面 張力的效果。但疋’在此情況下’前述介面活性劑成分、 2〇以及滾印用墨水組成物中包含的顏料、或分散劑和黏著劑 樹脂等等構成成分的相溶性以及消泡性會下降,因此於包 覆層上塗佈時’塗佈層表面或内部會發生孔洞(Hole ), 而導致顏料結塊的情況產生。 200902645 【發明内容】 <發明欲解決之課題> 本發明人等發現製造滾印用墨水組成物時,採用含氟 基之丙烯酸共聚物樹脂可改善包覆層上塗佈墨水時之相溶 5 性以及消泡性,並防止塗佈層表面的孔洞或顏料塊等等塗 佈不良情形發生。因此,本發明之一目的為提供一種滾印 用墨水組成物’其包括有含氟基之丙烯酸共聚物樹脂、具 有乙稀性不飽和雙鍵之多官能基丙烯酸單體、熱聚合起始 劑、著色劑、以及溶劑。另外,本發明之其他目的為提供 0 一種使用前述滾印用墨水組成物之彩色濾光片的製造方 法、一種以該方法所製造之彩色濾光片、以及一種包含該 彩色濾光片之液晶顯示單元。 <解決課題的手段> 本發明提供一種滾印用墨水組成物,其包括下記化學 5式1所不之含氟基之丙烯酸共聚物樹脂、具有乙烯性不飽和 雙鍵之多官能基丙烯酸單體、熱聚合起始劑、著色劑、、 及溶劑。 以 【化學式1】
8 200902645 其中,
Ri、R·2、R3各自獨立為氫原子或曱基, 尺4為含氟基之碳數1〜8個的烷基或芳香族基, m、η、1是整數,其莫耳比(m: n :丨)為6〇〜7〇 : 15 5 〜34 : 1〜15, 前述共聚物樹脂的數量平均分子量為5 〇〇〇〜5〇,〇〇〇。 另外,本發明提供一種彩色濾光片之製造方法,其步 驟包括: (a)於基板上形成黑色矩陣圖案; 10 (b)利用滾印法,將一含有前述化學式丨所示之含氟 基的丙烯酸共聚物樹脂、具有乙烯性不飽和雙鍵之多官能 基丙烯酸單體、熱聚合起始劑、著色劑 '以及溶劑之滚印 用墨水組成物塗佈以及轉印於前述黑色矩陣分隔之畫素 部’以進行圖案化;以及 15 ( c)乾燥前述圖案化之滾印用墨水組成物。 此外’本發明提供一種以前述製造方法製造之彩色濾 光片。 另外’本發明提供一種包含有前述彩色濾光片之液晶 顯示單元β 20 發明的效果 本發明之滾印用墨水組成物其包含有含氟基之丙烯酸 共聚物樹脂、具有乙烯性不飽和雙鍵之多官能基丙烯酸單 體、熱聚合起始劑、著色劑、以及溶劑,由於丙烯酸共聚 25物樹脂内含有氟基,故本發明之滾印用墨水組成物具有相 200902645 溶性以及消泡性。因此,本發明製造之彩色據光月因其分 散安定性以及表面改善,故能提昇液晶顯示單元的顏色特 性以及顯示品質。 5 【實施方式】 以下將詳細說明本發明。 本發明提供一種滾印用墨水組成物,其包括有下★己化 學式1所示之含氟基之丙烯酸共聚物樹脂、具有乙烯性不飽 和雙鍵之多官能基丙烯酸單體、熱聚合起始劑、著色劑、 10 以及溶劑。 本發明之滾印用墨水組成物所使用之前述含氟基之丙 烯酸共聚物樹脂可以下記化學式1表示。 【化學式1】
、R2、Rs各自獨立為氫原子或曱基, R4為含氟基之碳數1〜8個的烷基或芳香族基, m η 1疋整數,其莫耳比為〜冗:b 〜34 : 1〜15, 10 200902645 前述共聚物樹脂的數量平均分子量為5,000〜5〇,〇〇〇。 前述化學式1所示之丙烯酸共聚物樹脂含有氟基。前述 丙烯酸共聚物樹脂内之氟基能使本發明之滾印用墨水組成 物具有相溶性以及消泡性。具體而言,於已知的墨水組成 5物中使用含氟基之介面活性劑的情況下,表面張力下降效 果非常大,但因極性低造成極性相對上較大的顏料以及分 散用的分散劑之間的相溶性變差,導致顏料塊以及消泡性 低下的問題。因此,塗佈時表面會變得非常粗糙,而可能 形成内部含有氣泡的薄膜。然而,於添加含氟基之丙烯酸 10共聚物樹脂的情況下,前述丙烯酸共聚物樹脂含有能降低 表面張力的氟基,同時含有能增加顏料和分散劑、以及其 他黏著成分之間的相溶性的單體組成,因此全體墨水組成 物的相溶性與分散性能上升、塗佈時不會產生顏料塊、表 面變均一、且能減少薄膜内部的氣泡。 15 相對於全體滚印用墨水組成物100重量份,前述化學式 1所示之含氟基之丙烯酸共聚物樹脂較佳係添加丨〜扣重量 份。當前述含氟基之丙烯酸共聚物樹脂之含量未滿丨重量份 夺很難達到&升墨水組成物的相溶性以及消泡性之效 =,而超過20重量份時,含有具有乙烯性不飽和雙鍵之多 20吕月匕基丙烯酸單體的其他成分的含量相對上會減少,而使 得薄膜強度下降。 。本發明除了前述含氟基之丙烯酸共聚物樹脂之外,還 可包含有不含氟基之丙烯酸共聚物樹脂。前述不含氟基之 丙稀酸共聚物樹脂,因為可和含酸基(_ f囊之 11 200902645 單體及能與前述單體共聚合之單體進行共聚合反應,故不 同於光刻微影製程且不需使用鹼性顯影製程,所以前述不 含I基之丙烯酸共聚物樹脂亦可不含酸基。 前述含酸基之單體較佳為一種或以上選自於由(甲基) 5 丙烯酸、巴豆酸、衣康酸、馬來酸、富馬酸、單曱基馬來 酸、異戊二烯磺酸、以及苯乙烯磺酸所組成之群組。 可與前述含酸基單體共聚合之單體較佳為一種或以上 化合物選自於由下列組成之群組:苯乙烯、氣苯乙烯、α —甲基苯乙烯、乙烯基曱苯、(甲基)丙烯酸曱酯、(曱 10 基)丙烯酸乙酯、(曱基)丙烯酸丁酯、苯曱基(曱基) 丙烯酸酯、二曱氨基乙基(曱基)丙烯酸酯、異丁基(曱 基)丙烯酸酯、t一丁基(曱基)丙烯酸酯、環己基(曱基) 丙烯酸酯、異冰片烯(甲基)丙烯酸酯、2—苯氧基乙烯(曱 基)丙烯酸酯、四四氫糠基(曱基)丙烯酸酯、羥乙基(曱 15 基)丙烯酸酯、2_羥丙基(甲基)丙烯酸酯、2 —羥基一 3 —氯丙基(曱基)丙烯酸酯、4 —羥基丁基(甲基)丙烯酸 酯、醯基辛氧基_2_羥丙基(甲基)丙烯酸酯、乙基己基 丙烯酸酯、2_甲氧基乙基(曱基)丙烯酸酯、3 —曱氧基 丁基(曱基)丙烯酸酯、乙氧基二甘醇(曱基)丙烯酸酯、 20 甲氧基三甘醇(甲基)丙烯酸酯、甲氧基三丙二酵(甲基) 丙烯酸酯、甲氧基聚乙二醇(甲基)丙烯酸酯、苯氧基二 甘醇(曱基)丙烯酸酯、P—壬基笨氧基聚乙二醇(甲基) 丙烯酸酯、P —壬基苯氧基聚丙二醇(曱基)丙烯酸酯、四 氟丙基(曱基)丙烯酸酯、1,1,1,3,3,3 —六氟異丙基(曱暴) 12 200902645 丙烯酸酯、八氟戊基(甲基)丙烯酸酯、十七氟癸基(甲 基)丙烯酸酯、三溴苯基(甲基)丙烯酸酯、石一(甲基) 羥醯基(acylol)氧基乙基氫基琥珀酸酯、甲基“ 一羥基曱 基丙烯酸酯、乙基〇: 一羥基甲基丙烯酸酯、丙基α—羥基 5甲基丙烯酸酯、以及丁基α—羥基曱基丙烯酸酯。 前述不含氟基之丙烯酸共聚物樹脂可舉例如下述化學 式2或化學式3所示之共聚物,但並不限定於此。 【化學式2】
Ri、R2各自獨立為氫原子或甲基, m、n為整數,莫耳比(m : η)為70 : 30。 前述共聚物樹脂的數量平均分子量為5,000〜5〇,〇〇〇。 【化學式3】 13 200902645
10
15
Ri、R2、R3各自獨立為氫原子或曱基, m、η、1為整數’莫耳比(m: η: 1)為 70: 15: 15, 前述共聚物樹脂的數量平均分子量為5,〇〇〇〜5〇,〇〇〇。 又,於前述不含氟基之丙烯酸共聚物樹脂的酸基可與 具有縮水甘油基之單體進行加成反應,且可導入一在熱硬 化時可與具有乙烯性不飽和雙鍵之多官能基單體一起進行 加成聚合反應之乙稀性不飽和反應性基。這裡可使用之具 有縮水甘油基之單體,較佳可為一種以上之化合物選自於 由下列組成之群組··縮水甘油(甲基)丙烯酸酯、乙烯苄 基縮水甘油醚、乙烯基縮水甘油醚、烯丙基縮水甘油醚、4 —f基一4,5 —環氧基戊烯、7 —縮水甘油醚氧丙基三甲氧 基矽烷、r —縮水甘油醚氧丙基曱基二乙氧基矽烷、^ 一 縮水甘㈣氧丙基三乙氧基錢、以及降冰片烯衍生物。 本發明中,不含氟基之丙烯酸共聚物樹脂其酸價較佳 為在0〜200KOH mg/g之範圍内,且數量平均分子量較佳 為在5,〇〇〇〜50,_之範_。相對於墨水組成物1〇〇重量 14 200902645 份,前述不含氟基之樹脂黏著劑之含量範圍係為超過〇重量 份〜20重量份以下,且可單獨或混合2種以上使用。 前述具有乙烯性不飽和雙鍵之多官能基丙烯酸單體, 可使用分子中具有至少丨個以上之可加成聚合的不飽和基 5 且'弗騰點1 〇〇 c以上之化合物、或導入己内輯之多官能基丙 烯酸單體。 前述分子中具有至少1個以上之可加成聚合的不飽和 基且沸騰點loot:以上之化合物可使用聚乙二醇單(甲基) 丙烯酸醋、聚丙二醇單(曱基)丙烯酸酯、或苯氧基乙基 ίο (曱基)丙烯酸酯等單官能基單體;聚乙二醇(曱基)丙 烯酸酯、聚丙二醇(曱基)丙烯酸酯、三羥基甲基乙烧三 丙稀酸酉曰、二經基甲基丙烧三丙稀酸醋、新戊二醇(曱基) 丙烯酸酯、季戊四醇四丙烯酸酯、季戊四醇三丙烯酸酯、 二季戊四醇五丙烯酸酯、或二季戊四醇六丙浠酸酯等等之 15 多官能基單體。 又’前述導入己内酯之多官能基丙烯酸單體可使用導 入KAYARAD DPCA— 20、30、60、120之二季戊四醇、導 入KAYARAD TC_ 110S之四羥吱喃基丙稀酸酯、或導入 KAYARAD HX- 220、KAYARAD HK- 620之新戊二醇 20 經基新戊酸酯等等。其他可使用之多官能基單體可使用作 為雙紛A衍生物之環氧基丙烯酸酯、酚醛_環氧基丙烯酸 醋、U— 324A、U15HA或U—4HA等聚氨酯系之多官能基丙 烯酸酯。前述具有乙烯性不飽和雙鍵之多官能基丙烯酸單 體可單獨或混合2種以上使用。 15 200902645 相對於滾印用墨水組成物100重量份,前述具有乙烯性 不飽和雙鍵之多官能基丙烯酸單體之使用含量較佳為1〜 20重量份。前述具有乙烯性不飽和雙鍵之多官能基丙稀酸 單體之含量未滿1重量份時,塗佈膜的強度會劣化,超過20 5 重量份時,由於樹脂層的黏著性過強,反而又使薄膜強度 劣化。 本發明之滾印用墨水組成物使用熱聚合起始劑。若使 用光聚合起始劑,為了使墨水組成物的硬化而不得不使用 f 曝光製程,所以必須設置滾印裝備以外之附加裝備,如曝 10 光裝置以及為了曝光之配向裝置,因此滚印用墨水組成物 不適合使用光聚合起始劑。 本發明之墨水組成物用之熱聚合起始劑可使用偶氮系 化合物、Wako PuRe chemical IndustRis. . Ltd..之偶 氮腈系的¥_60、¥-65、¥—59、¥—70、¥—40、偶氮酯 15 系之V—60卜偶氮醯胺系之VA- 086、VA- 085、VA- 080、
Vam—110、Vam-m、VF— 096、偶氮腓系之V—50、VA —044、VA- 046B ' Aam— 027、VA— 060、VA— 057、VA —061、大分子偶氮系起始劑之VPS — 0501 ' VPS — 1001、 VPE- 0201、VPE- 0401、VPE- 0601、VPTG- 0301 等, 20 但不限定於此。 相對於全體墨水組成物100重量份,前述熱聚合起始劑 較佳之含量為0.03〜0.3重量份。前述熱聚合起始劑的含量 未滿0.03重量份時,會產生墨水熱聚合度變低的問題,超過 0.3重量份時,熱聚合起始劑的效率會減少。 16 200902645 本發明滾印用墨水組成物可使用之著色劑較佳為顏 料。刖述顏料可使用通用之顏料,只要不會對分散性有不 好的影響較佳為使用經微細加工粒子之顏料。前述顏料的 粒子大小主要在0.3#m以下為較佳,且以分佈有9〇%以上 5之〇.丨以瓜顏料粒子為較佳。當前述顏料的大小大於〇.3以 m,以單次製程製造組成物時會產生顏料分散的問題,因此 光透過變得不圓滑,使得所製造出之彩色濾光片的透過性 變得不好。 f 本發明之滾印用墨水組成物中,顏色特性為紅色之顏 10 料可使用·秦盼系紅色顏料,如Pig_ Red # 1 ( C· I. 12070 )、
Pig. Red# 2 ( C. Ι· 12310) 、pig· Red# 3 ( C. Ι· 12120)、 Pig. Red# 4( C. I. 12085)、Pig· Red# 5( c. I. 12490)、 Pig. Red# 6 ( C. I. 12090)、Pig. Red# 7 ( c. I. 12420)、 Pig. Red# 8 (C· I. 12355 )、Pig. Red# 9( C. 1.12460)、 15 Pig. Red# 10 ( c· I. 12440) ' Pig· Red# 11 ( c. I. 12430)、
Pig. Red# 12 ( C. I. 12385 ) ' Pig. Red# 13 ( C. I. 12395 ) > # Pig· Red# 14( C· I. 12380)、Pig. Red# 15( C· I. 12465 )、 V Pig. Red# 16 ( 12500) ' Pig. Red # 17 ( C. I. 12390 ) 'Pig.
Red# 18 ( C· I. 12350)、Pig· Red# 21 ( C. I_ 12300)、Pig. 20 Red# 22 ( C. I. 12315) ' Pig. Red# 23 ( C. I. 12355 ) 'Pig. Red# 31 ( 12360) ' Pig. Red# 32 ( 12320) > Pig. Red# 95 (C. I. 15897) ' Pig. Red# 112 ( C. I. 12370) 、Pig. Red # 114 (C. I. 12351 ) ' Pig. Red# 119 ( C. I. 12469) ' Pig. Red# 146 ( C. I. 12485 ) > Pig. Red# 147 ( C. I. 12433) > 17 200902645
Pig. Red# 148( C. I. 12369)、Pig. Red# 150( C. I. 12290)、 Pig. Red# 151( C. I. 15890)、Pig. Red# 184( C. I. 12487)、 Pig. Red# 187( C. I. 12486)、Pig. Red# 188( C. I. 12467)、 Pig. Red# 210( C. I_ 12474)、Pig. Red# 245( C. I. 12317)、 5 Pig. Red# 253( C. I. 12375 ) ' Pig. Red# 258( C. I. 12318) ' Pig. Red #261(C. I. 12468);蔡紛系和金屬錯合物,如pig. Red# 49( C.I· 15630)、Pig. Red#49: 1( C. I. 15630: 1 )、 Pig. Red# 49 : 2 (C. I. 15630 : 2) ' Pig. Red# 49 : 3 ( C. I. 15630:3 )、Pig. Red# 50:1 (C· I. 15500:1 )、Pig. Red 10 # 51 : 1 ( C. I. 15580 : 1 ) ' Pig. Red # 53 ( C. I. 15585 ) '
Pig. Red# 53 : 1 ( C. I. 15585 : 1 )、Pig. Red# 68 ( C. I. 15525 ) ' Pig. Red# 243 ( C. I. 15910) ' Pig. Red# 247 ( C. I· 15915);雙偶氮吡唑啉酮系,如Pig· Red# 37 (C. I. 21205 ) ' Pig. Red# 38 ( C. I. 21210) ' Pig. Red# 41 ( C. I. 15 21200);雙偶氮系縮合物,如Pig. Red# 144( C. I. 20735)、
Pig. Red# 166( C. I. 20035) ' Pig. Red# 220( C. I. 20055) ' Pig. Red# 221( C. I. 20065)、Pig. Red# 242( C. I. 20067); 2—羥基一3 —萘曱酸系金屬錯合物,如Pig. Red# 48 : 1 ( C. I. 15865 : 1 ) ' Pig. Red# 48 : 2 ( C. I. 15865 : 2) ' Pig. Red 2〇 # 48 : 3 ( C. I· 15865 : 3 )、Pig. Red# 48 : 4 ( C. I. 15865 : 4) ' Pig. Red# 48 : 5 ( C. I. 15865 : 5)、Pig. Red# 52 : 1 (C. I. 15860 : 1 )、Pig. Red# 52 : 2 ( C. I. 15860 : 2)、
Pig. Red# 57 : 1 ( C. I. 15850 : 1 ) ' Pig. Red# 58 : 2 ( C. I. 15825 : 2) ' Pig. Red# 58 : 4 ( C. I. 15825 : 4)、Pig. Red 18 200902645 # 63 : 1 ( C. I. 15880 · 1 ) ' Pig. Red# 63 : 2 ( C. I. 15880 : 2)、Pig. Red# 64 ( C. I· 15800) ' Pig. Red# 64 : 1 ( C. I. 15800:1 )、Pig. Red# 200 ( C· I. 15867);萘磺酸金屬錯 合物,如 Pig. Red #60:1 (C. I. 16105.1)、Pig. Red # 66 5 ( C. I. 18000 : 1 ) ' Pig. Red# 67 ( C. I. 18025 : 1 );三 芳基主碳系,如Pig. Red# 81 : 1 ( C· I· 45160 : 1 )、Pig_ Red # 81 : 3 ( C. I. 45160 : 3)、Pig. Red# 169 ( C. I. 45160 : 2);蒽酿系,如 Pig. Red# 89 ( C· I. 60745 ) 、Pig. Red# 177( 65300);硫靛染料系,如Pig. Red# 88( C. I. 73M2)、 10 Pig. Red# 181 ( C. I. 73360);喹吖啶酮系,如 Pig. Red# 122 ( C. I. 73915 ) ' Pig. Red# 207 ( C. I. 73900)、Pig. Red # 209( C. I. 73905 );茈系,如Pig. Red# 123( C· I. 71145)、
Pig. Red# 149( C. I. 71137)、Pig. Red# 178( C. I· 71155)、
Pig. Red# 179( C. I. 71130)、Pig. Red# 190( C· I. 71140)、 15 Pig. Red# 194( C. I. 71100) > Pig. Red# 224( C. I. 71127); 苯並咪唑酮系,如Pig. Red# 171 ( C. I. 12512) 、Pig. Red # 175 ( C. I. 12513) > Pig. Red# 176 ( C. I. 12515 ) ' Pig. Red# 185 ( C. I. 12516) ' Pig. Red# 208 ( C. I. 12514); 芘蒽酮系,如Pig· Red# 216 ( C· I. 59710);吡咯並吡咯系 20 之Pig. Red# 254 ( C. Ι· 56110);異吲哚啉系之Pig· Red# 260 ( C· I. 56295 )等等。 紫色顏料可使用三芳基正碳系,如Pig. Violet # 1 ( C. I. 45170 : 2) ' Pig. Violet# 2 ( C. I. 45175 : 1 ) ' Pig. Violet #3 (C. I. 42535:2)、Pig. Violet# 27( C. 1.42535:3)、 19 200902645
Pig. Violet# 39 ( C. I. 42555 : 2);蒽醌系,如 Pig. Violet # 5 : 1 ( C. I. 58055 : 1 );萘酚系,如 Pig. Violet # 25 ( C. I. 12321 ) 、Pig· Violet# 50 ( C. I. 12322);喹吖啶酮系, 如 Pig. Violet# 19 ( C. I. 73900);二噁嗪系,如 Pig. Violet 5 # 23 ( C. I. 51319)、Pig. Violet# 37 ( C. I. 51345);茈 系,如Pig. Violet# 29 ( C. I. 71129 );苯并咪吐酮系,如 Pig. Violet# 32 ( C· I. 12517)等等。 青色顏料可使用三芳基正碳系,如之Pig. Blue# 1 (C. Ι· 42595 : 2)、Pig. Blue#(2 ( C. I. 44045 : 2)、Pig. Blue 10 # 9 ( C. I. 42025 : 1 ) ' Pig. Blue# 10 ( C. I. 44040 : 2) '
Pig. Blue# 14( C· I. 42600: 1 )、Pig. Blue# 18( C. I. 42770 : 1) ' Pig. Blue# 19 ( C. I. 42750) ' Pig. Blue# 56 ( C. I. 42800)、Pig. Blue# 62( C· I. 44084);酞菁銅系,如Pig. Blue# 15 ( C. Ι· 74160)、Pig. Blue# 15 : 1 ( C. Ι· 74160); 15 金屬自由酞菁系,如Pig. Blue# l6 ( C_ I. 74100);陰丹士 林藍系,如Pig. Blue# 60 ( C. I. 69800)、Pig. Blue# 64 ( Ο-ΐ. 69825) ; 靛青系 ,如Pig· Blue# 66( C. I. 73000) 、 Pig. Blue# 63 ( C. I. 73015 : x )等等。 綠色顏料可使用三芳基正碳,如Pig. Green# 1 (C· I. 20 4 2 0 4 0:1 ) ' Pig. Green# 2 ( C. I. 42040 : 1 ) 、Pig. Green #4 ( C. I. 42000 : 2);酞菁銅系,如 Pig. Green # 7 ( C. I. 74260)、Pig. Green# 36 ( C. I. 74265);金屬錯合物,如 Pig. Green# 8 ( C. I. 10006) ' Pig. Green# 10 ( C. I. 12775) 等等。 20 200902645 汽顏料可使用單偶氮系,如Pig. Yellow # 1 ( c· I. 11680) ' Pig. Yellow# 2 ( C. I. 11730) ' Pig. Yellow# 3 (C. I. 11710) > pig. Yellow# 5 ( C. I. 11660) ' Pig. Yellow # 6 ( C. I. 11670 ) ' Pig. Yellow# 10 ( C. I. 12710 ) 'Pig. 5 Yellow# 49( C. I. 11765 ) ' Pig. Yellow # 65 ( C. I. 11740) ^ Pig. Yellow# 73 ( C. I. 1 1738) ' Pig. Yellow# 74 ( C. I. 11741) > Pig. Yellow# 75 ( C. I. 11770) ' Pig. Yellow# 97( C. I. 11767)、Pig. Yellow# 98( C. I· 11727)、Pig. Yell〇w #111 ( C. I. 11745 ) ' Pig. Yellow# 116 ( C. I. 11790 )、 10 Pig· Yellow# 167 ( C. I_ 11737);單偶氮系金屬錯體,如 Pig. Yellow# 61 ( C. I. 13880) ' Pig. Yellow# 62 : 1 ( C. I. 13940 : 1 )、Pig. Yell0w# i〇〇( c. I. 19140 : 1 )、Pig· Yeli〇w #168 (C. 1.13960)、Pig. Yellow# 169( C. I. 13955)、
Pig. Yellow# 1B3 ( C. I. 18792) •,乙醯基乙醯苯胺系,如 15 Pig. Yellow# 16 ( C. I. 20040 );雙芳香醯苯胺系之Pig. Yellow# 12( C. I. 21090)、Pig· Yellow# 13( C. Ι· 21100)、 Pig. Yellow# 14 ( C. I. 21095) ' Pig. Yellow# 17 ( C. I. 21105) ' Pig. Yellow# 55 ( C. I. 21096) ' Pig. Yellow# 63( C. I. 21091 )'Pig. Yellow# 81( C. I. 21127)'Pig. Yellow 20 # 83 ( C. I. 21108)、Pig. Yellow# 87 ( C. I. 21107 : 1)、
Pig. Yellow# 113 ( C. I. 21126)、Pig. Yellow# 114 ( C· I. 21092) ' Pig. Yellow# 124 ( C. I. 21107 ) ' Pig. Yellow# 126( C. I. 21101 )、Pig· Yellow# 127( 21102)、Pig· Yell〇w #152 (C_ I. 21111) 、Pig. Yellow# 170( C. I. 21104)、 21 200902645
Pig. Yellow# 171 ( C. I. 21106) ' Pig. Yellow# 172 ( C. I. 21109) 、Pig. Yellow# 174 ( C. I. 21098);黃烷士酮系, 如 Pig. Yellow# 24 ( C. Ι· 70600);二偶氮系縮合物,如 Pig. Yellow# 93( C. I. 20710) > Pig. Yellow# 94( C. I. 20038) ' 5 Pig. Yellow# 95 ( C. I. 20034) 、Pig. Yellow# 128 ( C. I. 20037)、Pig. Yellow# 166 ( C· I· 20035);蒽醌系,如Pig. Yellow# 123 ( C. I. 65049 ) 、Pig. Yellow # 147 ( C. I. 60645 );链嗓(Aldazine)系,如Pig. Yellow# 101 (C. I. 48052);萘磺酸金屬錯合物,如Pig. Yellow# 104 ( C. I. 10 15985 : 1 );蒽素嘧啶,如 Pig. Yellow# 108 ( C_ I· 68420); 異吲哚啉酮系,如Pig. Yellow# 109 ( C. I. 56284) 、Pig. Yellow# 110 ( C. I. 56280 ) ' Pig. Yellow# 139 ( C. I. 56298 ) 、Pig. Yellow# 185 ( C. I. 56290);苯並咪唑系, 如 Pig. Yellow# 123 ( C. I. 11783 ) 、Pig· Yellow# 154 ( C· 15 I· 13980)、Pig. Yellow# 175 ( C. I. 11784)、Pig. Yellow # 180 ( C. I. 21290) ' Pig. Yellow# 181 ( C. I. 11777); 喹酞酮系,如Pig. Yellow# 138 ( C. I· 56300);金屬錯合 物,如Pig. Yellow# 117 ( C· I. 48043) 、Pig. Yellow# 129 (C. I. 48042)、Pig. Yellow# 150( C. I. 12764)、Pig· Yellow 20 # 153 ( C. I. 48545) 、Pig. Yellow# 177 ( C. I. 48120)、
Pig. Yellow# 179 ( C. I. 48125 )等等。 此外,橘色顏料可使用單偶氮系,如Pig. Orange # 1 ( C. I. 11725 ) 、Pig· Orange# 6 ( C. I. 12730):萘酚系之Pig. Orange# 2 ( C. I. 12060) ' Pig. Orange # 5 ( C. I. 12075 ) > 22 200902645
Pig. Orange# 22 ( C. I. 12470) ' Pig· Orange# 24 ( C. I. 12305)、Pig. Orange# 38 (C. I. 12367);萘酚金屬錯合 物’如Pig. Orange# 17 ( C. Ι· 15510 : 1 Pig. Orange# 17 : 1(15510:2)、Pig. Orange #46 (C· I· 15602),雙偶氮 吡唑啉酮系,如Pig_ Orange# 13( C· I. 21110)、Pig. Orange # 34 ( C· I. 21115);雙芳香醯苯胺系,如Pig. Orange# 15 (C. 1.21130)、Pig. Orange# 16( C. I. 21160);萘磺酸
10 15
V 20 金屬錯合物,如Pig. Orange# 19 ( C_ I. 15990);雙偶氮系 縮合物,如Pig. Orange# 31 (C. I. 20050);苯並咪唑系, 如Pig. Orange# 36 ( C. Ι· 11780) 、Pig. Orange# 60 ( C. I. 11782);芘蒽酮系,如pig· 〇range# 4〇 (c. i_ 59700); 紫環酮系’如Pig· Orange# 43 ( C. I. 71105 );喹吖唆酮系, 如 Pig· Orange # 48( C. I. 73900 );異吲哚啉系,如 Pig. 〇range # 61 ( C, I. 11265 )、Pig· Orange# 66 ( C. I. 48210)或Pig. Orange # 69 ( C. I. 56292 )等等。 相對於全體墨水組成物1 〇〇重量份,前述滾印用墨水組 成物中為了呈現顏色特性之著色劑,依照所要求之顏色特 性,其添加量較佳為1〜20重量份,更佳為1〜15重量份。 前述墨水組成物中所使用之著色劑含量不適當時,在製造 彩色濾光片時無法製得預期畫質的產品。 乙二醇 曱醚、環己酮、2—庚酮、3 —庚酮、2_羥乙基卢 考慮到溶解性、顔料分散性、塗佈性、以及滾印之雇 案轉寫性等等時,前述溶劑可使用丙二醇單甲醚、乙二库 甲醚醋酸醋、丙二醇甲醚醋酸醋、丙二醇乙醚醋酸酿- ’ 23 200902645 酸醋、3—甲基一3 —甲氧基丁基丙酸酯、乙基3 一甲氧基丙 酸醋、甲基一3 —乙氧基丙酸酯、乙基3 —乙氧基丙酸酯、 乙酸丁 S曰、乙酸乙醋、甲酸戊醋、乙酸異戊g旨、乙酸異丁 醋、乙酸異丙酯、甲基乙基酮、丙酸丁酯、丁酸異丙酯、 5 丁酸乙、丁酸丁自旨、乙酮酸乙酯、γ — 丁内g旨、以及甲 醇、乙醇、η—丙醇、i 一丙醇等等之醇類、和苯、甲苯、 二甲苯等等之芳香族系、n一庚烷、n_己烷、n_辛烷等等 之飽和炭化風類等等。前述溶劑可單獨或混合2種以上使 用。 10 15 20 相對於全體滚印用墨水組成物丨重量份,前述溶劑較 佳為添加60〜90重量份。前述溶劑之含量未滿6〇重量份 時,墨水的固體含量變多而使黏度大幅增加,對包覆層塗 佈墨水較困難,而溶劑的含量超過90重量份時,固體的含 里變少而使黏度降低,不僅塗佈變難,且為了圖案轉寫而 造成揮發性溶劑使用量變多的缺點β 為了調節墨水的表面張力’本發明之料用墨水組成 物可更含有介面活性劑。前述添加之介面活性劑較佳為碎 系介面活性劑或氟系介面活性劑。具體而言,降低表面張 力效果較大之矽系介面活性劑可使用byk—3〇〇、Βγκ — 30卜 BYK- 302、BYK-綱、BYK_ 3G7、Βγκ— 31()、抓 -330、BYK— 333、BYK- 335、BYK— 341、BYK— 344 BYK- 345、BYK- 370等等’而i系介面活性劑可使用f_ 114、F-177、F-4H)、F_4U、F—㈣、卜 493、卜例 F— 443、F— 444、F—445、F-446、F— 470、F—471、] 24 200902645 -475、F - 482、F - 487、F - 172D、TF - 1128、TF — 1127、 TF- 1129' TF- 1126' TF - 1130' TF - Π 16SF' TF- 1131 ' TF1132、TF1027SF、TF- 144卜 TF- 1442等等,但並不限
10 15
20 於上述介面活性劑。但是,現在作為滾印用包覆層材料之 一般PDMS其表面張力約為24mN/m,故塗佈於pdmS表面之 墨水的表面張力必須低於PDMS的表面張力。然而,矽系介 面活性劑的使用量不論增加多少,墨水的表面張力降低至 24mN/m以下已是極限,若使用氟系介面活性劑則可將墨水 的表面張力降低至24mN/m以下。 為了調節前述墨水的表面張力,相對於全體墨水組成 物1〇〇重量份,所添加之介面活性劑較佳為〇〇3〜〇3重量 份。前述介面活性劑的含量未滿〇〇3重量份時,降低墨水表 面張力的效果會不充分,且會發生包覆層塗佈不良的情 况而超過0.3重置份時,則會有介面活性劑使用過量而造 成墨水相溶性以及消泡性降低等問題。 本發明之滾印用墨水組成物依需要可再使用由 劑、密著促_、以及酸化防止劑組成之群財選擇之一 種以上之添加劑。 邱心劑可按照預先表面處理顏料之形態,採用内 :分散劑可使用高分子型、非離子性、陰離子性、:陽: 基亞院基多價二醇、亞烧基二醇以及其㈣、聚氧 物、她旨:;二=氧衍生物、醇基婦化氧衍生 皿羧酸自曰、羧酸鹽、烷基醯胺基烯化 25 200902645 氧衍生物、或烷基醢胺等等。並且,其可單獨地添加也可 兩種以上混合使用。前述密著促進劑可使用乙烯基三曱氧 基矽烷、乙烯基三乙氧基矽烷、乙烯基三(2 —曱氧基乙氧 基)一石夕烧、N— (2 —氨乙基)一 3 —氨丙基甲基、曱氧基 5 石夕烧、N— (2—氨乙基)一3—氨丙基甲基三曱氧基石夕烧、 3 —氨丙基三乙氧基石夕院、3 —縮水甘油醚氡丙基三乙氧基 矽烷、3—縮水甘油醚氧丙基甲基二甲氧基矽烷、2一(3, 4—乙氧基環己基)乙基三曱氧基石夕烧、3 —氯丙基甲基二 甲氧基矽烷、3—氯丙基三曱氧基矽烷、3 —曱基丙烯醯氧 10 基丙基三甲氧基矽烷、或3—巯基丙基三甲氧基矽烷等等。 前述酸化防止劑可使用2,2—硫代雙(4—甲基一6—t— 丁苯 酚)、或2,6—g,t—丁苯酚等等。 相對於全體滾印用墨水組成物,前述添加劑之添加量 較佳為超過0重量份〜5重量份以下。 15 另外,本發明提供一種彩色濾光片之製造方法,其步 驟包括: 八 (a) 於基板上形成黑色矩陣圖案; (b) 利用滾印法,將一含有前述化學式丨所示之含氟 基的丙烯酸共聚物樹脂、具有乙烯性不餘和雙鍵之多官能 基丙烯酸單體、熱聚合起始劑、著色劑、以及溶劑之滾印 用墨水組成物,塗佈以及轉印於依據前述黑色矩陣分隔之 晝素部,以進行圖案化;以及 ⑺熱硬化前述圖案化之滾印用墨水組成物。 前述(〇係於基板上形成黑色矩陣圖案。 26 200902645 前述基板之材料無特別限定,可使用玻璃基板、塑膠 基板、或可撓曲基板等等,較佳為耐熱性強之透明玻璃基 板。 月j述於基板上形成黑色矩陣圖案之 5界已知之光職料缝印法料進❼ 據“業 月'J述黑色矩陣可使用習知常用絡黑色矩陣或樹脂黑色 矩陣製造’而前述所形成之黑色矩陣厚度較佳為〇·2〜^ m,且:前述厚度範财,光學密度介於2〜6之間為較佳。 刖述(b)為利用滾印法,將一含有前述化學Si所示 10 =氣基的丙埽酸共聚物樹脂、具有乙烯性不飽和雙鍵之 多官能基丙稀酸單體、熱聚合起始劑、著色劑、以及溶劑 2滾印用墨水組成物,塗佈以及轉印於依據前述黑色矩陣 分隔之畫素部,以進行圖案化之步驟。 ★在此,滾印法係:將前述滾印用墨水組成物塗佈於滾 b筒或平板形態之包覆層後,從使用具滚筒或平板形態之移 P版的包覆層上’將不期望的塗佈部分從具有期望圖案之 、、象圖案取出,再將殘留於包覆層上的期望圖案部分轉寫 至基板。例如,用狹縫式喷嘴(Slit Nozzle)將本發明之 泼印用墨水組成物塗佈於滾筒形態之包覆層材料(例: 20 =DMS )上後,使用形成有特定形狀的溝部(期望圖案)及 大出邛(不期望圖案)的移印版,從塗佈於包覆層上之墨 出不期望的圖案部,而殘留於前述包覆層上的期望圖 案部則與依據前述黑色矩陣分隔之畫素部接觸而進行轉 寫。或者,可依照情況,使用具有期望圖案之突出部之移 27 200902645 印版,包覆層將期望圖案從塗佈有墨水之包覆層上取出, 然後直接轉寫於基板。 前述(C)係將轉寫於前述基板上之滾印用墨水組成物 熱硬化之步驟。利用前述滾印法,將本發明之滚印用墨水 5組成物轉寫於黑色矩陣分隔之畫素部後,較佳以50〜15吖 之溫度軟烤1〜600秒,然後再以15〇〜25〇t後烤_〜3〇〇〇 秒後烤以進行熱硬化。 又,本發明提供依照本發明之前述方法製造之彩色濾 光片。 並且,本發明提供含有前述彩色濾光片之液晶顯示單 兀*。除了使用前述滾印用墨水組成物之彩色濾光片製造方 法之外本發明之液晶顯示單元之製造方法可使用現行技 術領域的技術。 15 【實施例】 以下,例示較佳實施例以幫助理解本發明。然而,下 述實施例的提供僅為了使本發明能更容易理解,因此本發 明的内容並非限定於下述實施例。 20 <第1實施例> 相對於墨水全體組成物HK)重量份,本發明使用之前述 滚印用紅色墨水係、由作為著色劑之紅色顏料# 254 4重量 份、紅色顏料# 177 0.8重量份、黃色顏料#139 12重量 &份、作為含氟基之樹脂黏著劑的(曱基)丙烯酸苯曱醋及 (甲基)丙烯酸、HFIMA以45 : 25 : 3〇之莫耳比形成之共 28 200902645 聚物(Mw= 18,800) 2重量份、(甲基)丙烯酸苯曱酯及(甲 基)丙稀酸以70 : 30形成之共聚物與烯丙基縮水甘油醚加 成反應所形成之不含氟基的聚合體(Mw=7,〇〇〇) 3 6重量 伤、作為具有乙烯性不飽和雙鍵之多官能基單體的二季戊 5四醇六丙稀酸醋9.5重量份、偶氮酿胺系熱聚合起始劑 40、Wak〇 PuRe Chemical IndustRis. LTD) 0·5 重量 份、作為添加劑之分散劑聚醚系分散劑1重量份、3_甲基 丙稀酿氧基丙基三曱氧基石夕烧〇2重量份、氟系介面活性劑 (Megaface F — 172D,大日本彳 >丰化學工業株式會社, 10日本)0.2重1份、作為溶劑之丙二醇曱醚醋酸酯5〇重量份、 甲f乙基_17重量份、乙酸乙醋1〇重量份所混合而成,並 將别述混合物攪拌5小時以製造滾印用墨水組成物。 <第2實施例> 15 相對於墨水全體組成物1 〇 〇重量份,本發明使用之前述 滾印用綠色墨水係、由作為著色劑之綠色顏料# 36 5 9重量 伤、!色顏料# 150 3.1重量份、作為含氟基之樹脂黏著劑 之(曱基)丙烯酸苯甲醋及(甲基)丙稀酸、HFIMA以: 乃:30之莫耳比所形成之共聚物(Mw= 18,800) 1.75重量 份、(甲基)丙稀酸苯甲醋及(甲基)丙稀酸以7〇 :靖 形成之共聚物與烯丙基縮水甘油醚加成反應所形成之不含 氟基聚合體(Mw=7,_) 2·32重量份、作為具有乙稀性不 飽和雙鍵之多官能基單體之二季戊四醇六丙烯酸酯6重量 份、偶氮醯胺系熱聚合起始劑(ν — 4〇、Wak〇 puRe 25 IndUStRis.LTD) 0.5重量份、作為添加劑之分散 29 200902645 7聚趟系分散劑158重量份、3 —曱基丙烯醯氧基丙基三曱 氧基石夕炫^.2重量份、氟系介面活性劑(Megaface f— 172D, 大曰本'由墨化學工業株式會社’曰本)0.2重量份、作為溶 劑之丙二醇甲峻醋酸酯54重量份、甲基乙基酮15重量份、 乙醋9.45重量份所混合而成,並將前述混合物攪拌5小 時以製造滾印用墨水組成物。 <第3實施例> fs 相對於墨水全體組成物100重量份,本發明使用之前述 滚印用藍色墨水係由作為著色劑之藍色顏料# i 5 : 6 3 76 重里伤顏料紫色#23 〇·94重量份、作為含氟基樹脂黏著 劑之(甲基)丙烯酸苯甲酯及(曱基)丙烯酸、HFIMA以 莫耳比45 . 25 . 30之莫耳比所形成之共聚物(Mw= 18,800) 2·6重量份、(甲基)丙稀酸苯甲醋及(甲基)丙稀酸以 3〇所形成之共聚物與烯丙基縮水甘油醚加成反應所形成之 不含氟基聚合體(Mw=7,_) 4 75重量份、作為具有乙烯 性^和雙鍵之多官能基單體之二季細醇六丙烯酸醋9.6 重里伤、偶氮醯胺系熱聚合起始劑(v_ 4〇、Wak〇 puRe
Chemical IndustRis· LTD) 〇·5重量份、作為添加劑之分散 2〇劑聚㈣分散劑系分散船重量份、卜甲基丙稀醯氧基丙 基三甲氧基石夕烧0.2重量份、氟素系介面活性劑⑽⑽似 F— 172D’大曰本油墨化學工.業株式會社,日本)〇2重量 份、作為溶劑之丙二醇曱_酸酿42 25重量份、曱基乙基 綱22_9重1份、乙酸乙醋iL3重量份所混合而成,並將前述 25混合物攪拌5小時以製造滾印用墨水組成物。 30 200902645 <第1比較例> 於刖述第1實施例中’除了不添加含氟基之丙烯酸共聚 物樹脂,且將(甲基)丙浠酸苯甲酯和(曱基)丙烯酸以 5 70 . 30所形成之共聚物與烯丙基縮水甘油醚加成反應所形 成之不含氟基聚合體(Mw== 7,000)添加56重量份之外, 依照與第1實施例相同之方法製造滾印用墨水組成物。 <第2比較例> 1〇 於前述第2實施例中’除了不添加含氟基之丙烯酸共聚 物樹脂’且將(甲基)丙烯酸苯甲醋和(甲基)丙稀酸以 30所形成之共聚物與烯丙基縮水甘油醚加成反應所形 成之不含氟基聚合體(Mw=7,〇〇〇)添加4们重量份之外, 依照與第2實施例相同之方法製造滾印用墨水組成物。 15 <第3比較例> 於前述第3實施例中’除了不添加含氟基之丙烯酸共聚 物樹月曰,且將(甲基)丙烯酸苯曱酯和(甲基)丙烯酸以 70 · 30所形成之共聚物與烯丙基縮水甘油醚加成反應所形 〇成之不含免基聚合體(Mw=7,〇〇〇)添加7.35重量份之外, 依照與第3實施例相同之方法製造滾印用墨水組成物。 <實驗例> 2 ,將前述第1實施例〜第3實施例以及第丨比較例〜第3比 較例所製造之滾印用墨水組成物塗佈於包覆層以及玻璃基 31 200902645 板上後,使用CCD相機觀察塗佈特性以及表面特性。前述 結果顯示於下列表1。 【表1】 滾印用彩色墨水之塗佈以及表面特性的結果 包覆層(PDMS)上 玻璃基板上 第1實施例 良好 良好 第2實施例 良好 良好 第3實施例 良好 良好 第1比較例. 喷出/掉色情形發生 表面有孔洞 第2比較例 喷出/掉色情形發生 表面有孔洞 第3比較例 噴出/掉色情形發生 顏料塊/表面有孔洞 【圖式簡單說明】 圖la為本發明第1實施例之滾印用紅色墨水塗佈於包 覆層上後之光學顯微鏡照片(X1000)。 圖lb為本發明第1比較例之滚印用紅色墨水塗佈於包 10 覆層上後之光學顯微鏡照片(X1000)。 圖2a為本發明第2實施例之滾印用綠色墨水塗佈於包 覆層上後之光學顯微鏡照片(X1000)。 圖2b為本發明第2比較例之滾印用綠色墨水塗佈於包 覆層上後之光學顯微鏡照片(X1000)。 32 200902645 圖3a為本發明第3實施例之滾印用藍色墨水塗佈於包 覆層上後之光學顯微鏡照片(X1000)。 圖扑為本發明第3比較例之滾印用藍色墨水塗 覆層上後之光學顯微鏡照片(X1000)。
無 主要元件符號說 明 33
Claims (1)
- 200902645 十、申請專利範圍: 1' 種滾印用墨水組成物,包含下記化學式1所示之 土之丙婦g文共聚物樹脂、具有乙稀性不飽和雙鍵之多 g月b基丙烯酸單體、熱聚合起始劑、著色劑、以及溶劑: 【化學式1】 L r\L rA/ r3 \其中, Ri、R2、I各自獨立為氫原子或曱基, h為含氟基之碳數1〜8個的烷基或芳香族基, 10 m、n、l是整數,其莫耳比(m:n:1)為6〇〜7〇 : 15 〜34 : 1〜15, 前述共聚物樹脂的數量平均分子量為5,000〜50,000。 2·如申請專利範圍第丨項所述之滾印用墨水組成物, f中,前述化學式1所示之含氟基之丙烯酸共聚物樹脂之含 量相對於全體滚印用墨水組成物100重量份為1〜20重量 份〇 34 200902645 3 ·如申請專利範圍第1項所述之滚印用墨水組成物, 更包含下記化學式2或化學式3所示之不含氟基之丙烯酸共 聚物樹脂: 【化學式2】、R2各自獨立為氫原子或曱基, m、η為整數,莫耳比(m : 1)為70 : 30。 且前述共聚合樹脂的數量平均分子量為5,000〜 10 50,000 ; 【化學式3】I、R2、R3各自獨立為氫原子或甲基, 35 200902645 m、η、1為整數,莫耳比(m : n : 〇為7〇 : 15 : 15, 且前述共聚合樹脂的數量平均分子量為5,〇〇〇〜 50,000。 5 10 15 20 4. 如申請專利範圍第3項所述之滾印用墨水組成物, 其中,則述化學式2以及化學式3所示之不含氟基之丙稀酸 共聚物樹脂之含量相對於全體滾印用墨水組成物1〇〇重量 份為超過〇重量份〜2〇重量份以下。 5. 如申請專利範圍第1項所述之滾印用墨水組成物, 其中,前述具有乙烯性不飽和雙鍵之多官能基丙烯酸單 體,係為分子中具有至少1個以上之可加成聚合的不飽和基 且沸點10(TC以上之化合物或導入己内酯之多官能基丙烯 酸單體。 6. 如申凊專利範圍第丨項所述之滾印用墨水組成物, 其中,則述具有乙烯性不飽和雙鍵之多官能基丙浠酸單體 之含量相對於全體印刷用墨水組成物1〇〇重量份 加重 量份。 1 \如申請專利範圍第1項所述之滾印用墨水組成物, ’則述熱聚合起始劑之含量相對於全體滾印用墨水組 成物1〇0重量份為0.03〜0.3重量份。 巾請專利範圍第〗項所述之滾印用墨水組成物, 兵τ ’則述著色劑為顏料。 9此如申請專利範圍^項所述之滾印用墨水組成物 重量份劑之含量相對於全體滾㈣墨水組成物1( 里TO為1〜20重量份。 36 200902645 10·如申請專利範圍第W所述之滾印用墨水組成物, 、令’前述溶劑係由丙二醇單甲醚、乙二醇甲醚醋酸酯、 :二醇甲醚醋酸酯、丙二醇乙醚醋酸酯、二乙二醇二甲醚、 環己_、2一庚鲷、3-庚酮、2-羥乙基丙酸酯、3一甲基 甲氧基丁基丙酸酯、乙基3 —曱氧基丙酸酯、曱基—3 -乙氧基丙酸酯、乙基3_乙氧基丙酸酯、乙酸丁醋、乙酸 乙醋、甲酸戊酉旨、乙酸異戊醋、乙酸異丁醋、乙酸異丙醋、 甲基乙基酮、丙酸丁酯、丁酸異丙酯、丁酸乙酯、丁酸丁 醋、乙酮酸乙醋…丁内醋、甲醇、乙醇、η—丙醇、i 丙醇、苯、甲苯、二甲苯、n—庚燒、n—己烧、以及n — 辛烷所組成之群組中選擇單獨或2種以上之化合物。 11·如申請專利範圍第丨項所述之滚印用墨水組成物, :中$述溶劑之含量相對於全體滾印用墨水組成物丨〇〇重 1份為60〜90重量份。 15 20 12.如申請專利範圍第丨項所述之滚印用墨水組成物, 更包含1種或以上選自由矽系介面活性劑或氟系介面活性 劑組成之群組之化合物。 13 ·如申請專利範圍第12項所述之滾印用墨水組成 物其中’前述矽系介面活性劑或氟系介面活性劑之含量 相對於全體滾印用墨水組成物100重量份為0.03〜0.3重量 份。 14·如申請專利範圍第1項所述之滾印用墨水組成物, 更包含1種或以上選自由分散劑、密著促進劑、以及酸化防 止劑組成之群組之之添加劑。 37 200902645 K如申請專利範圍第14項所述之滾印用墨 物’其中’前述添加劑之含量相 : 物雜量份為超過〇重量份〜5重量份二”用墨水組成 (b)利用滾印法,料請專利第1項〜第15項中 任一項所狀滾印心水組成物塗佈以及轉寫 、16.-種彩色濾光片之製造方法,其步驟包括 (a)於基板上形成黑色矩陣圖案; 矩陣分隔之畫素部,以進行圖案化;以及 U (c)乾燥前述圖案化之滾印用墨水組成物。 10 15 、17.如申請‘專利範圍第16項所述之彩色濾光片之製造 方法’其中’前述滾印法係將前述滚印用墨水組成物塗佈 於滾筒或平板形態之包覆層後,從使用具滾筒或平板形態 之移印版的包覆層i ’將不期望的塗佈部分從具有期望圖 案之逆像圖案取出’再將殘留於包覆層上的期望圖案部分 轉寫至基板。 18.如申請專利範圍第16項所述之彩色濾光片之製造 方法,其中,前述乾燥係a5〇〜15〇〇c軟烤1〜6〇〇秒後,再 以150〜250。(:後烤600〜3,〇〇〇秒。 19· 一種彩色濾光片’其係由申請專利範圍第16項〜第 20 18項中任一項所述之製造方法所製造之彩色渡光片。 20. —種液晶顯示單元’其包含申請專利範圍第19項所 述之彩色濾光片。 38 200902645 七、指定代表圖: (一) 本案指定代表圖為:圖la。 (二) 本代表圖之元件符號簡單說明: 益 八、本案若有化學式時,請揭示最能顯示發明特徵的化學式:其中,R!、R2、R3、R4、、η、及1如說明書中所定義。 4