RU2018131948A - Композиция, содержащая модифицированный красный шлам с низким содержанием хроматов, и способ ее получения - Google Patents
Композиция, содержащая модифицированный красный шлам с низким содержанием хроматов, и способ ее получения Download PDFInfo
- Publication number
- RU2018131948A RU2018131948A RU2018131948A RU2018131948A RU2018131948A RU 2018131948 A RU2018131948 A RU 2018131948A RU 2018131948 A RU2018131948 A RU 2018131948A RU 2018131948 A RU2018131948 A RU 2018131948A RU 2018131948 A RU2018131948 A RU 2018131948A
- Authority
- RU
- Russia
- Prior art keywords
- composition according
- paragraphs
- red mud
- compounds
- modified
- Prior art date
Links
- 239000000203 mixture Substances 0.000 title claims 40
- 238000000034 method Methods 0.000 title claims 25
- ZCDOYSPFYFSLEW-UHFFFAOYSA-N chromate(2-) Chemical compound [O-][Cr]([O-])(=O)=O ZCDOYSPFYFSLEW-UHFFFAOYSA-N 0.000 title claims 17
- 239000011651 chromium Substances 0.000 claims 17
- 239000003638 chemical reducing agent Substances 0.000 claims 14
- 150000001845 chromium compounds Chemical class 0.000 claims 14
- XEEYBQQBJWHFJM-UHFFFAOYSA-N iron Substances [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims 10
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 claims 6
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims 6
- 150000001875 compounds Chemical class 0.000 claims 5
- RAQDACVRFCEPDA-UHFFFAOYSA-L ferrous carbonate Chemical compound [Fe+2].[O-]C([O-])=O RAQDACVRFCEPDA-UHFFFAOYSA-L 0.000 claims 5
- 238000010438 heat treatment Methods 0.000 claims 4
- 229910001385 heavy metal Inorganic materials 0.000 claims 4
- 150000002506 iron compounds Chemical class 0.000 claims 4
- 150000002823 nitrates Chemical class 0.000 claims 4
- 150000002826 nitrites Chemical class 0.000 claims 4
- 239000002002 slurry Substances 0.000 claims 4
- BVKZGUZCCUSVTD-UHFFFAOYSA-L Carbonate Chemical compound [O-]C([O-])=O BVKZGUZCCUSVTD-UHFFFAOYSA-L 0.000 claims 3
- UCKMPCXJQFINFW-UHFFFAOYSA-N Sulphide Chemical compound [S-2] UCKMPCXJQFINFW-UHFFFAOYSA-N 0.000 claims 3
- XSQUKJJJFZCRTK-UHFFFAOYSA-N Urea Chemical compound NC(N)=O XSQUKJJJFZCRTK-UHFFFAOYSA-N 0.000 claims 3
- 230000015572 biosynthetic process Effects 0.000 claims 3
- 239000004202 carbamide Substances 0.000 claims 3
- 239000003795 chemical substances by application Substances 0.000 claims 3
- JOPOVCBBYLSVDA-UHFFFAOYSA-N chromium(6+) Chemical class [Cr+6] JOPOVCBBYLSVDA-UHFFFAOYSA-N 0.000 claims 3
- 239000000356 contaminant Substances 0.000 claims 3
- 235000013980 iron oxide Nutrition 0.000 claims 3
- UQSXHKLRYXJYBZ-UHFFFAOYSA-N iron oxide Inorganic materials [Fe]=O UQSXHKLRYXJYBZ-UHFFFAOYSA-N 0.000 claims 3
- VBMVTYDPPZVILR-UHFFFAOYSA-N iron(2+);oxygen(2-) Chemical class [O-2].[Fe+2] VBMVTYDPPZVILR-UHFFFAOYSA-N 0.000 claims 3
- 239000005416 organic matter Substances 0.000 claims 3
- 150000003839 salts Chemical class 0.000 claims 3
- 239000010802 sludge Substances 0.000 claims 3
- IIACRCGMVDHOTQ-UHFFFAOYSA-N sulfamic acid Chemical compound NS(O)(=O)=O IIACRCGMVDHOTQ-UHFFFAOYSA-N 0.000 claims 3
- GWEVSGVZZGPLCZ-UHFFFAOYSA-N Titan oxide Chemical compound O=[Ti]=O GWEVSGVZZGPLCZ-UHFFFAOYSA-N 0.000 claims 2
- 239000003463 adsorbent Substances 0.000 claims 2
- 239000011248 coating agent Substances 0.000 claims 2
- 238000000576 coating method Methods 0.000 claims 2
- 229920000876 geopolymer Polymers 0.000 claims 2
- 239000012535 impurity Substances 0.000 claims 2
- 238000009413 insulation Methods 0.000 claims 2
- 230000001590 oxidative effect Effects 0.000 claims 2
- 239000006174 pH buffer Substances 0.000 claims 2
- 125000005575 polycyclic aromatic hydrocarbon group Chemical group 0.000 claims 2
- 238000002360 preparation method Methods 0.000 claims 2
- 238000000746 purification Methods 0.000 claims 2
- 239000002689 soil Substances 0.000 claims 2
- 239000000126 substance Substances 0.000 claims 2
- 238000004438 BET method Methods 0.000 claims 1
- 229910019142 PO4 Inorganic materials 0.000 claims 1
- ZLMJMSJWJFRBEC-UHFFFAOYSA-N Potassium Chemical compound [K] ZLMJMSJWJFRBEC-UHFFFAOYSA-N 0.000 claims 1
- 239000002253 acid Substances 0.000 claims 1
- 238000004887 air purification Methods 0.000 claims 1
- AZDRQVAHHNSJOQ-UHFFFAOYSA-N alumane Chemical class [AlH3] AZDRQVAHHNSJOQ-UHFFFAOYSA-N 0.000 claims 1
- 238000000137 annealing Methods 0.000 claims 1
- 239000007864 aqueous solution Substances 0.000 claims 1
- 239000004566 building material Substances 0.000 claims 1
- 229940043430 calcium compound Drugs 0.000 claims 1
- 150000001674 calcium compounds Chemical class 0.000 claims 1
- -1 carbonate compound Chemical class 0.000 claims 1
- 238000005553 drilling Methods 0.000 claims 1
- 239000002359 drug metabolite Substances 0.000 claims 1
- 238000001035 drying Methods 0.000 claims 1
- 230000005670 electromagnetic radiation Effects 0.000 claims 1
- 239000003344 environmental pollutant Substances 0.000 claims 1
- 239000003063 flame retardant Substances 0.000 claims 1
- 239000012530 fluid Substances 0.000 claims 1
- 239000011521 glass Substances 0.000 claims 1
- 239000008187 granular material Substances 0.000 claims 1
- 230000005484 gravity Effects 0.000 claims 1
- 238000005338 heat storage Methods 0.000 claims 1
- XLYOFNOQVPJJNP-UHFFFAOYSA-M hydroxide Chemical compound [OH-] XLYOFNOQVPJJNP-UHFFFAOYSA-M 0.000 claims 1
- 239000011261 inert gas Substances 0.000 claims 1
- 229910052500 inorganic mineral Inorganic materials 0.000 claims 1
- 235000014413 iron hydroxide Nutrition 0.000 claims 1
- NCNCGGDMXMBVIA-UHFFFAOYSA-L iron(ii) hydroxide Chemical compound [OH-].[OH-].[Fe+2] NCNCGGDMXMBVIA-UHFFFAOYSA-L 0.000 claims 1
- 239000007788 liquid Substances 0.000 claims 1
- 238000004519 manufacturing process Methods 0.000 claims 1
- 244000000010 microbial pathogen Species 0.000 claims 1
- 239000011707 mineral Substances 0.000 claims 1
- 238000002156 mixing Methods 0.000 claims 1
- 230000004048 modification Effects 0.000 claims 1
- 238000012986 modification Methods 0.000 claims 1
- NDLPOXTZKUMGOV-UHFFFAOYSA-N oxo(oxoferriooxy)iron hydrate Chemical compound O.O=[Fe]O[Fe]=O NDLPOXTZKUMGOV-UHFFFAOYSA-N 0.000 claims 1
- 239000003415 peat Substances 0.000 claims 1
- 235000021317 phosphate Nutrition 0.000 claims 1
- 150000003013 phosphoric acid derivatives Chemical class 0.000 claims 1
- 231100000719 pollutant Toxicity 0.000 claims 1
- 239000011591 potassium Substances 0.000 claims 1
- 229910052700 potassium Inorganic materials 0.000 claims 1
- 230000002285 radioactive effect Effects 0.000 claims 1
- 150000003377 silicon compounds Chemical class 0.000 claims 1
- 239000000243 solution Substances 0.000 claims 1
- 238000004381 surface treatment Methods 0.000 claims 1
- 239000004408 titanium dioxide Substances 0.000 claims 1
- DXZMANYCMVCPIM-UHFFFAOYSA-L zinc;diethylphosphinate Chemical compound [Zn+2].CCP([O-])(=O)CC.CCP([O-])(=O)CC DXZMANYCMVCPIM-UHFFFAOYSA-L 0.000 claims 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B18/00—Use of agglomerated or waste materials or refuse as fillers for mortars, concrete or artificial stone; Treatment of agglomerated or waste materials or refuse, specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B18/04—Waste materials; Refuse
- C04B18/0409—Waste from the purification of bauxite, e.g. red mud
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
- C09K5/00—Heat-transfer, heat-exchange or heat-storage materials, e.g. refrigerants; Materials for the production of heat or cold by chemical reactions other than by combustion
- C09K5/08—Materials not undergoing a change of physical state when used
- C09K5/14—Solid materials, e.g. powdery or granular
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B14/02—Granular materials, e.g. microballoons
- C04B14/04—Silica-rich materials; Silicates
- C04B14/041—Aluminium silicates other than clay
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B14/02—Granular materials, e.g. microballoons
- C04B14/04—Silica-rich materials; Silicates
- C04B14/06—Quartz; Sand
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B14/02—Granular materials, e.g. microballoons
- C04B14/30—Oxides other than silica
- C04B14/303—Alumina
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B14/02—Granular materials, e.g. microballoons
- C04B14/30—Oxides other than silica
- C04B14/308—Iron oxide
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B18/00—Use of agglomerated or waste materials or refuse as fillers for mortars, concrete or artificial stone; Treatment of agglomerated or waste materials or refuse, specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B18/02—Agglomerated materials, e.g. artificial aggregates
- C04B18/023—Fired or melted materials
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B18/00—Use of agglomerated or waste materials or refuse as fillers for mortars, concrete or artificial stone; Treatment of agglomerated or waste materials or refuse, specially adapted to enhance their filling properties in mortars, concrete or artificial stone
- C04B18/04—Waste materials; Refuse
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B20/00—Use of materials as fillers for mortars, concrete or artificial stone according to more than one of groups C04B14/00 - C04B18/00 and characterised by shape or grain distribution; Treatment of materials according to more than one of the groups C04B14/00 - C04B18/00 specially adapted to enhance their filling properties in mortars, concrete or artificial stone; Expanding or defibrillating materials
- C04B20/10—Coating or impregnating
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B20/00—Use of materials as fillers for mortars, concrete or artificial stone according to more than one of groups C04B14/00 - C04B18/00 and characterised by shape or grain distribution; Treatment of materials according to more than one of the groups C04B14/00 - C04B18/00 specially adapted to enhance their filling properties in mortars, concrete or artificial stone; Expanding or defibrillating materials
- C04B20/10—Coating or impregnating
- C04B20/1018—Coating or impregnating with organic materials
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B20/00—Use of materials as fillers for mortars, concrete or artificial stone according to more than one of groups C04B14/00 - C04B18/00 and characterised by shape or grain distribution; Treatment of materials according to more than one of the groups C04B14/00 - C04B18/00 specially adapted to enhance their filling properties in mortars, concrete or artificial stone; Expanding or defibrillating materials
- C04B20/10—Coating or impregnating
- C04B20/1055—Coating or impregnating with inorganic materials
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B20/00—Use of materials as fillers for mortars, concrete or artificial stone according to more than one of groups C04B14/00 - C04B18/00 and characterised by shape or grain distribution; Treatment of materials according to more than one of the groups C04B14/00 - C04B18/00 specially adapted to enhance their filling properties in mortars, concrete or artificial stone; Expanding or defibrillating materials
- C04B20/10—Coating or impregnating
- C04B20/1055—Coating or impregnating with inorganic materials
- C04B20/1066—Oxides, Hydroxides
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
- C04B28/006—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing mineral polymers, e.g. geopolymers of the Davidovits type
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
- C04B28/02—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing hydraulic cements other than calcium sulfates
- C04B28/06—Aluminous cements
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
- C04B28/24—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing alkyl, ammonium or metal silicates; containing silica sols
- C04B28/26—Silicates of the alkali metals
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B40/00—Processes, in general, for influencing or modifying the properties of mortars, concrete or artificial stone compositions, e.g. their setting or hardening ability
- C04B40/0028—Aspects relating to the mixing step of the mortar preparation
- C04B40/0039—Premixtures of ingredients
- C04B40/0042—Powdery mixtures
-
- C—CHEMISTRY; METALLURGY
- C05—FERTILISERS; MANUFACTURE THEREOF
- C05F—ORGANIC FERTILISERS NOT COVERED BY SUBCLASSES C05B, C05C, e.g. FERTILISERS FROM WASTE OR REFUSE
- C05F7/00—Fertilisers from waste water, sewage sludge, sea slime, ooze or similar masses
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
- C09K8/00—Compositions for drilling of boreholes or wells; Compositions for treating boreholes or wells, e.g. for completion or for remedial operations
- C09K8/02—Well-drilling compositions
- C09K8/03—Specific additives for general use in well-drilling compositions
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
- C09K8/00—Compositions for drilling of boreholes or wells; Compositions for treating boreholes or wells, e.g. for completion or for remedial operations
- C09K8/02—Well-drilling compositions
- C09K8/03—Specific additives for general use in well-drilling compositions
- C09K8/032—Inorganic additives
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F24—HEATING; RANGES; VENTILATING
- F24H—FLUID HEATERS, e.g. WATER OR AIR HEATERS, HAVING HEAT-GENERATING MEANS, e.g. HEAT PUMPS, IN GENERAL
- F24H7/00—Storage heaters, i.e. heaters in which the energy is stored as heat in masses for subsequent release
-
- H—ELECTRICITY
- H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
- H05B—ELECTRIC HEATING; ELECTRIC LIGHT SOURCES NOT OTHERWISE PROVIDED FOR; CIRCUIT ARRANGEMENTS FOR ELECTRIC LIGHT SOURCES, IN GENERAL
- H05B3/00—Ohmic-resistance heating
- H05B3/10—Heating elements characterised by the composition or nature of the materials or by the arrangement of the conductor
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2103/00—Function or property of ingredients for mortars, concrete or artificial stone
- C04B2103/0068—Ingredients with a function or property not provided for elsewhere in C04B2103/00
- C04B2103/0094—Agents for altering or buffering the pH; Ingredients characterised by their pH
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2103/00—Function or property of ingredients for mortars, concrete or artificial stone
- C04B2103/0068—Ingredients with a function or property not provided for elsewhere in C04B2103/00
- C04B2103/0096—Reducing agents
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/00241—Physical properties of the materials not provided for elsewhere in C04B2111/00
- C04B2111/00258—Electromagnetic wave absorbing or shielding materials
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
- C04B2111/00758—Uses not provided for elsewhere in C04B2111/00 for agri-, sylvi- or piscicultural or cattle-breeding applications
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
- C04B2111/00862—Uses not provided for elsewhere in C04B2111/00 for nuclear applications, e.g. ray-absorbing concrete
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/10—Compositions or ingredients thereof characterised by the absence or the very low content of a specific material
- C04B2111/1075—Chromium-free or very low chromium-content materials
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/20—Resistance against chemical, physical or biological attack
- C04B2111/28—Fire resistance, i.e. materials resistant to accidental fires or high temperatures
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/52—Sound-insulating materials
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/54—Substitutes for natural stone, artistic materials or the like
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
- Y02E20/00—Combustion technologies with mitigation potential
- Y02E20/14—Combined heat and power generation [CHP]
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
- Y02P40/00—Technologies relating to the processing of minerals
- Y02P40/10—Production of cement, e.g. improving or optimising the production methods; Cement grinding
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02W—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO WASTEWATER TREATMENT OR WASTE MANAGEMENT
- Y02W30/00—Technologies for solid waste management
- Y02W30/50—Reuse, recycling or recovery technologies
- Y02W30/91—Use of waste materials as fillers for mortars or concrete
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Ceramic Engineering (AREA)
- Organic Chemistry (AREA)
- Materials Engineering (AREA)
- Structural Engineering (AREA)
- Inorganic Chemistry (AREA)
- Civil Engineering (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Environmental & Geological Engineering (AREA)
- Life Sciences & Earth Sciences (AREA)
- General Life Sciences & Earth Sciences (AREA)
- Geochemistry & Mineralogy (AREA)
- Geology (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Combustion & Propulsion (AREA)
- Mechanical Engineering (AREA)
- General Engineering & Computer Science (AREA)
- Solid-Sorbent Or Filter-Aiding Compositions (AREA)
- Treatment Of Sludge (AREA)
- Water Treatment By Sorption (AREA)
- Battery Electrode And Active Subsutance (AREA)
- Compounds Of Alkaline-Earth Elements, Aluminum Or Rare-Earth Metals (AREA)
- Compounds Of Iron (AREA)
- Silicates, Zeolites, And Molecular Sieves (AREA)
- General Chemical & Material Sciences (AREA)
- Treating Waste Gases (AREA)
- Soil Sciences (AREA)
- Disinfection, Sterilisation Or Deodorisation Of Air (AREA)
- Fire-Extinguishing Compositions (AREA)
- Building Environments (AREA)
- Business, Economics & Management (AREA)
- Emergency Management (AREA)
- Curing Cements, Concrete, And Artificial Stone (AREA)
- Hydrology & Water Resources (AREA)
- Water Supply & Treatment (AREA)
- Analytical Chemistry (AREA)
- Compositions Of Oxide Ceramics (AREA)
- Silicon Compounds (AREA)
Claims (63)
1. Композиция, содержащая модифицированный красный шлам с низким содержанием хроматов со следующим минеральным составом:
- от 10 до 50% по массе соединений железа;
- от 12 до 35% по массе соединений алюминия;
- от 5 до 17% по массе соединений кремния;
- от 2 до 10% по массе диоксида титана;
- от 0,5 до 6% по массе соединений кальция;
- от 0 до 1 ppm соединений хрома (VI); и
- в некоторые случаях другие неизбежные примеси,
при этом состав композиции, в частности, модифицированный красный шлам с низким содержанием хроматов, содержит труднорастворимый восстановитель для Cr (VI), при этом композиция содержит еще буферную систему рН, сконфигурированную для стабилизации диапазона рН, в котором труднорастворимый восстановитель для Cr (VI) и полученный из него Cr (lll) обладают низкой растворимостью, в частности, растворимостью в воде при 25°C менее 1 г/л.
2. Композиция по п. 1, в которой труднорастворимый восстановитель для Cr (VI) обладает растворимостью в воде при рН 7 и 25°C менее 1 г/л, в частности, менее 0,1 г/л.
3. Композиция по п. 1 или 2, в которой труднорастворимый восстановитель для Cr (VI) содержит труднорастворимое соединение Fe (ll).
4. Композиция по любому из предыдущих пунктов, в которой труднорастворимый восстановитель для Cr (VI) содержит карбонат железа (ll) (Fe2CО3).
5. Композиция по любому из предыдущих пунктов, в которой она содержит комбинацию легкорастворимых и труднорастворимых соединений Fe (II).
6. Композиция по любому из предыдущих пунктов, в которой модифицированный красный шлам с низким содержанием хроматов содержит модифицированный карбонизированный красный шлам с низким содержанием хроматов, в котором массовое отношение карбоната Fe (ll) к оксидам железа составляет по меньшей мере 1.
7. Композиция по любому из предыдущих пунктов, в которой модифицированный красный шлам с низким содержанием хроматов содержит модифицированный карбонизированный и регидратированный красный шлам с низким содержанием хроматов, в котором массовое отношение карбоната Fe (ll) к оксидам железа составляет по меньшей мере 1, а массовое отношение суммы гидроксида железа и гидрата оксида железа к оксидам железа составляет по меньшей мере 1.
8. Композиция по любому из предыдущих пунктов, в которой композиция далее содержит по меньшей мере одно из следующих средств:
- еще один восстановитель Cr (VI), который, в частности, выбран из группы, состоящей из Fe, AI и Zn;
- средство для удаления нитратов и нитритов, которое, в частности, выбрано из группы, состоящей из мочевины и/или амидосульфоновой кислоты;
- средство, которое сконфигурировано для удаления загрязнителей, в частности, тяжелых металлов, посредством образования труднорастворимых солей, и, в частности, содержит сульфид;
- органическое вещество, на поверхности которого при термообработке образуется активированный уголь.
9. Композиция по любому из предыдущих пунктов, в которой модифицированный красный шлам с низким содержанием хроматов имеет удельную площадь поверхности в диапазоне 2-250 м²/г (измеренную по способу БЭТ), в частности, 10-200 м²/г (измеренную по способу БЭТ).
10. Композиция по любому из предыдущих пунктов, в которой модифицированный красный шлам с низким содержанием хроматов имеет удельный вес по меньшей мере 4,5 г/см³, в частности, по меньшей мере 5 г/см³, в частности, по меньшей мере 5,3 г/см³.
11. Композиция по любому из предыдущих пунктов, в которой композиция, в частности, модифицированный красный шлам с низким содержанием хроматов, находится по существу в форме гранул.
12. Композиция по любому из предыдущих пунктов, в которой композиция, в частности, модифицированный красный шлам с низким содержанием хроматов, содержит по меньшей мере частичную модификацию поверхности, в частности, содержит по меньшей мере частичное покрытие поверхности.
13. Композиция по любому из предыдущих пунктов, в которой композиция далее содержит восстановитель для Cr (VI), в частности, выбранный из группы, состоящей из Fe, AI и Zn, и предпочтительно находится в тонкодисперсной форме.
14. Композиция по любому из предыдущих пунктов, в которой смесь содержит еще средство для удаления нитратов и нитритов, которое, в частности, выбрано из группы, состоящей из мочевины и амидосульфоновой кислоты.
15. Композиция по любому из предыдущих пунктов, в которой смесь содержит еще средство, сконфигурированное для удаления загрязнителей, в частности, тяжелых металлов, посредством образования труднорастворимых солей, и, в частности, содержит сульфид.
16. Композиция по любому из предыдущих пунктов, в которой смесь содержит еще средство, в частности, органическое вещество, на поверхности которого при термообработке образуется активированный уголь.
17. Способ получения композиции по любому из пп. 1-16, в котором способ содержит следующие этапы:
a) подготовка нейтрализованного красного шлама;
b) добавление труднорастворимого восстановителя для Cr (VI) к красному шламу и смешивание труднорастворимого восстановителя для Cr (VI) с красным шламом;
c) восстановление содержащихся в красном шламе соединений хрома (VI) посредством труднорастворимого восстановителя для Cr (VI) в соединения хрома (lll) в водных системах для получения модифицированного красного шлама с низким содержанием хроматов, при этом способ далее содержит добавление буферной системы рН, сконфигурированной для стабилизации диапазона рН, в котором труднорастворимый восстановитель для Cr (VI) и полученный из него Cr (lll) обладают низкой растворимостью, в частности, растворимостью в воде при 25°C менее 1 г/л.
18. Способ по п. 17, в котором на этапе b) добавляется труднорастворимое соединение Fe (ll), в частности, карбонат Fe (ll), в качестве восстановителя для Cr (VI), при этом выполняется пошаговое восстановление соединений хрома (VI) в соединения хрома (lll), вследствие чего дополнительно итерационно образуется гидроксид Fe (lll).
19. Способ получения композиции по любому из пп. 4-16, в котором способ содержит следующие этапы:
a) подготовка нейтрализованного красного шлама;
b) восстановление содержащихся в красном шламе соединений железа (lll) в соединения железа (ll) и содержащихся в красном шламе соединений хрома (VI) в соединения хрома (lll) в водных системах;
c) добавление карбонатного соединения к полученному на этапе b) раствору, содержащему соединения железа (ll), для получения карбоната железа (ll), при этом способ далее содержит добавление буферной системы рН, сконфигурированной для стабилизации диапазона рН, в котором труднорастворимый восстановитель для Cr (VI) и полученный из него Cr (lll) обладают низкой растворимостью, в частности, растворимостью в воде при 25°C менее 1 г/л.
20. Способ по пп. 17-19, в котором способ далее содержит регидратацию посредством окисления соединений Fe (ll) в соединения Fe (lll) в водном растворе.
21. Способ по пп. 17-20, в котором способ далее содержит отжиг модифицированного красного шлама с низким содержанием хроматов при температуре в диапазоне от 450°C до 700°C.
22. Способ по любому из пп. 17-21, в котором способ далее содержит обработку модифицированного красного шлама с низким содержанием хроматов кислотой.
23. Способ по любому из пп. 17-22, в котором способ далее содержит термообработку модифицированного красного шлама с низким содержанием хроматов при температуре в диапазоне от 150°C до 350°C.
24. Способ по любому из пп. 17-23, в котором способ далее содержит грануляцию смеси, в частности, модифицированного красного шлама с низким содержанием хроматов.
25. Способ по любому из пп. 17-24, в котором способ далее содержит обработку поверхности смеси, в частности, модифицированного красного шлама с низким содержанием хроматов, в частности, нанесение покрытия на поверхность.
26. Способ по любому из пп. 17-25, в котором способ далее содержит добавление по меньшей мере одного из следующих средств:
- еще один восстановитель Cr (VI), который, в частности, выбран из группы, состоящей из Fe, AI и Zn;
- средство для удаления нитратов и нитритов, которое, в частности, выбрано из группы, состоящей из мочевины и/или амидосульфоновой кислоты;
- средство, которое сконфигурировано для удаления загрязнителей, в частности, тяжелых металлов, посредством образования труднорастворимых солей, и, в частности, содержит сульфид;
- органическое вещество, на поверхности которого при термообработке образуется активированный уголь.
27. Способ по любому из пп. 17-26, в котором способ далее содержит этап сушки, в частности, в по существу неокислительной атмосфере, например, в среде инертного газа.
28. Использование композиции по любому из пп. 1-16 в качестве адсорбента, в частности, итерационно действующего адсорбента длительного действия.
29. Использование композиции по любому из пп. 1-16 для очистки жидких и/или газообразных сред, в частности, для очистки воды или водоподготовки и/или очистки воздуха.
30. Использование композиции по любому из пп. 1-16 для удаления по меньшей мере одного из группы, состоящей из нитратов, нитритов, фосфатов, тяжелых металлов, полиароматических углеводородов (ПАУ), метаболитов лекарственных средств и патогенных микроорганизмов, из водных систем.
31. Использование композиции по любому из пп. 1-16 для удаления по меньшей мере одного вещества из группы, состоящей из механических включений, загрязнителей и пахучих веществ из газообразных систем.
32. Использование композиции по любому из пп. 1-16 в сельском хозяйстве, в частности, для стимуляции роста и/или в качестве средства для улучшения почвы или детоксикации почвы.
33. Использование композиции по любому из пп. 1-16 в качестве не содержащего галогенов огнезащитного средства и/или огнетушащего средства, в частности, для пожаров на обширной территории, таких как лесные или торфяные пожары.
34. Использование композиции по любому из пп. 1-16 в составе строительных материалов, в частности, по меньшей мере для одной из следующих целей:
- для огнезащиты;
- для термоизоляции;
- для аккумуляции тепла;
- для звукоизоляции;
- для защиты от радиоактивного и/или электромагнитного излучения или его ослабления.
35. Использование композиции по любому из пп. 1-16 в качестве утяжелителя для буровых растворов.
36. Использование композиции по любому из пп. 1-16 в качестве геополимера или производства геополимеров, в частности, с применением растворимого калиевого стекла.