MX359051B - Proceso para producir un artículo moldeado por estampación en caliente, y artículo moldeado por estampación en caliente. - Google Patents

Proceso para producir un artículo moldeado por estampación en caliente, y artículo moldeado por estampación en caliente.

Info

Publication number
MX359051B
MX359051B MX2013004355A MX2013004355A MX359051B MX 359051 B MX359051 B MX 359051B MX 2013004355 A MX2013004355 A MX 2013004355A MX 2013004355 A MX2013004355 A MX 2013004355A MX 359051 B MX359051 B MX 359051B
Authority
MX
Mexico
Prior art keywords
molded article
hot stamp
stamp molded
cold
steel sheet
Prior art date
Application number
MX2013004355A
Other languages
English (en)
Other versions
MX2013004355A (es
Inventor
Hayashi Kunio
Tomokiyo Toshimasa
Aso Toshimitsu
Tanino Hitoshi
Wada Ryozo
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2010289527A external-priority patent/JP5752409B2/ja
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of MX2013004355A publication Critical patent/MX2013004355A/es
Publication of MX359051B publication Critical patent/MX359051B/es

Abstract

La presente invención proporciona un proceso para producir un artículo moldeado estampado en caliente, que comprende una etapa de laminación en caliente, una etapa de devanado, una etapa de laminación en frío, una etapa de recocido continuo y una etapa de estampación en caliente, en donde la etapa de recocido continuo comprende una etapa de calentamiento para calentar una placa de acero laminada en frío a una temperatura de no menos de Ac1°C y menos de Ac3°C, una etapa de enfriamiento para enfriar la placa de acero laminada en frío a partir de la temperatura de calentamiento más alta a 660°C en una tasa de enfriamiento de 10°C/s o menos, y una etapa de retención para retener la placa de acero laminada en frío a una temperatura que varía de 550°C a 660°C durante 1 a 10 minutos.
MX2013004355A 2010-10-22 2011-10-21 Proceso para producir un artículo moldeado por estampación en caliente, y artículo moldeado por estampación en caliente. MX359051B (es)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2010237249 2010-10-22
JP2010289527A JP5752409B2 (ja) 2010-12-27 2010-12-27 硬度バラつきの小さいホットスタンプ成形体の製造方法およびその成形体
PCT/JP2011/074297 WO2012053636A1 (ja) 2010-10-22 2011-10-21 ホットスタンプ成形体の製造方法及びホットスタンプ成形体

Publications (2)

Publication Number Publication Date
MX2013004355A MX2013004355A (es) 2013-06-28
MX359051B true MX359051B (es) 2018-09-13

Family

ID=45975344

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2013004355A MX359051B (es) 2010-10-22 2011-10-21 Proceso para producir un artículo moldeado por estampación en caliente, y artículo moldeado por estampación en caliente.

Country Status (9)

Country Link
US (2) US9598745B2 (es)
EP (1) EP2631306B1 (es)
JP (1) JP5547287B2 (es)
KR (1) KR101533164B1 (es)
CN (1) CN103314120B (es)
BR (1) BR112013009520B1 (es)
CA (1) CA2814630C (es)
MX (1) MX359051B (es)
WO (1) WO2012053636A1 (es)

Families Citing this family (46)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9896736B2 (en) 2010-10-22 2018-02-20 Nippon Steel & Sumitomo Metal Corporation Method for manufacturing hot stamped body having vertical wall and hot stamped body having vertical wall
US9512499B2 (en) 2010-10-22 2016-12-06 Nippon Steel & Sumitomo Metal Corporation Method for manufacturing hot stamped body having vertical wall and hot stamped body having vertical wall
BR112013009520B1 (pt) 2010-10-22 2019-05-07 Nippon Steel & Sumitomo Metal Corporation Métodos para produção de chassi estampado a quente e chassi estampado a quente
KR101417260B1 (ko) * 2012-04-10 2014-07-08 주식회사 포스코 재질 균일성이 우수한 고탄소 열연강판 및 이의 제조방법
JP5821794B2 (ja) * 2012-07-18 2015-11-24 新日鐵住金株式会社 焼入れ鋼材およびその製造方法ならびに焼入れ用鋼材
CA2879540C (en) * 2012-08-06 2018-06-12 Nippon Steel & Sumitomo Metal Corporation Cold-rolled steel sheet and method for manufacturing same, and hot-stamp formed body
CN109023051A (zh) * 2012-08-15 2018-12-18 新日铁住金株式会社 热压用钢板、其制造方法以及热压钢板构件
ES2707893T3 (es) * 2012-08-28 2019-04-05 Nippon Steel & Sumitomo Metal Corp Chapa de acero
FI124825B (fi) * 2013-02-22 2015-02-13 Rautaruukki Oyj Menetelmä metallipinnoitetun ja kuumamuokatun teräskomponentin valmistamiseksi ja metallipinnoitettu teräsnauhatuote
JP6470266B2 (ja) * 2013-05-17 2019-02-13 エーケー スティール プロパティ−ズ、インク． プレス焼入れ用亜鉛めっき鋼材およびその製造方法
CN103331390B (zh) * 2013-07-10 2015-03-11 鞍钢股份有限公司 一种汽车u形梁的生产方法
EP2851440A1 (en) * 2013-09-19 2015-03-25 Tata Steel IJmuiden BV Steel for hot forming
US20160289809A1 (en) * 2013-09-19 2016-10-06 Tata Steel Ijmuiden B.V. Steel for hot forming
JP6211908B2 (ja) * 2013-12-02 2017-10-11 トヨタ自動車株式会社 ホットスタンプ成形品の製造方法
KR101568549B1 (ko) 2013-12-25 2015-11-11 주식회사 포스코 우수한 굽힘성 및 초고강도를 갖는 열간 프레스 성형품용 강판, 이를 이용한 열간 프레스 성형품 및 이들의 제조방법
WO2015144318A1 (en) * 2014-03-28 2015-10-01 Tata Steel Ijmuiden B.V. Method for hot forming a coated steel blank
EP2998410A1 (en) * 2014-09-22 2016-03-23 Autotech Engineering A.I.E. Method for laser beam heat treatment of press hardened components and press hardened components
DE102014017274A1 (de) * 2014-11-18 2016-05-19 Salzgitter Flachstahl Gmbh Höchstfester lufthärtender Mehrphasenstahl mit hervorragenden Verarbeitungseigenschaften und Verfahren zur Herstellung eines Bandes aus diesem Stahl
US20180100214A1 (en) * 2015-03-16 2018-04-12 Tata Steel Ijmuiden B.V. Steel for hot forming
MX2017012377A (es) * 2015-03-31 2017-12-14 Nippon Steel & Sumitomo Metal Corp Lamina de acero para estampado en caliente, metodo para producir lamina de acero para estampado en caliente, y articulo moldeado por estampado en caliente.
RU2605034C1 (ru) * 2015-11-20 2016-12-20 Федеральное Государственное Унитарное Предприятие "Центральный научно-исследовательский институт черной металлургии им. И.П. Бардина" (ФГУП "ЦНИИчермет им. И.П. Бардина") Горячекатаная сталь для горячей штамповки
DE102016100648B4 (de) * 2015-12-23 2018-04-12 Benteler Automobiltechnik Gmbh Wärmebehandlungsofen sowie Verfahren zur Wärmebehandlung einer vorbeschichteten Stahlblechplatine und Verfahren zur Herstellung eines Kraftfahrzeugbauteils
JP2017155329A (ja) * 2016-02-29 2017-09-07 株式会社神戸製鋼所 焼入れ用鋼板及びその製造方法
CN105755353A (zh) * 2016-03-31 2016-07-13 苏州睿昕汽车配件有限公司 一种耐腐蚀汽车配件合金钢材料及其制备方法
CN105755382A (zh) * 2016-03-31 2016-07-13 苏州睿昕汽车配件有限公司 一种耐腐蚀汽车配件合金钢材料及其制备方法
US10385415B2 (en) 2016-04-28 2019-08-20 GM Global Technology Operations LLC Zinc-coated hot formed high strength steel part with through-thickness gradient microstructure
US10619223B2 (en) 2016-04-28 2020-04-14 GM Global Technology Operations LLC Zinc-coated hot formed steel component with tailored property
US10288159B2 (en) 2016-05-13 2019-05-14 GM Global Technology Operations LLC Integrated clutch systems for torque converters of vehicle powertrains
US10240224B2 (en) 2016-08-12 2019-03-26 GM Global Technology Operations LLC Steel alloy with tailored hardenability
JP6424195B2 (ja) * 2016-11-14 2018-11-14 株式会社豊田中央研究所 熱間プレス成形方法
WO2018098485A1 (en) * 2016-11-28 2018-05-31 Ak Steel Properties, Inc. Method for production for press hardened steel with increased toughness
US10260121B2 (en) 2017-02-07 2019-04-16 GM Global Technology Operations LLC Increasing steel impact toughness
KR102228292B1 (ko) * 2017-02-20 2021-03-16 닛폰세이테츠 가부시키가이샤 강판
MX2020000928A (es) * 2017-07-25 2020-07-22 Tata Steel Ijmuiden Bv Tira, chapa o pieza de acero para producir una parte formada en caliente, parte y metodo de formacion de una pieza en una parte.
US11180824B2 (en) * 2018-03-29 2021-11-23 Nippon Steel Corporation Hot stamped article
EP3778951A4 (en) * 2018-03-29 2021-10-27 Nippon Steel Corporation HOT PUNCHED SHAPED PRODUCT
MX2020010540A (es) * 2018-04-09 2020-11-06 Nippon Steel Corp Material de acero adecuado para su uso en un ambiente acido.
WO2019222950A1 (en) 2018-05-24 2019-11-28 GM Global Technology Operations LLC A method for improving both strength and ductility of a press-hardening steel
WO2019241902A1 (en) 2018-06-19 2019-12-26 GM Global Technology Operations LLC Low density press-hardening steel having enhanced mechanical properties
CN111197145B (zh) 2018-11-16 2021-12-28 通用汽车环球科技运作有限责任公司 钢合金工件和用于制造压制硬化钢合金部件的方法
US11530469B2 (en) 2019-07-02 2022-12-20 GM Global Technology Operations LLC Press hardened steel with surface layered homogenous oxide after hot forming
CN110438314B (zh) * 2019-09-05 2021-05-25 首钢集团有限公司 一种含b钢的生产方法
CN113528973A (zh) * 2021-06-16 2021-10-22 首钢集团有限公司 一种高塑性热成形钢的生产方法
KR20230088117A (ko) * 2021-12-10 2023-06-19 현대제철 주식회사 핫스탬핑용 소재
CN114369758A (zh) * 2021-12-10 2022-04-19 首钢集团有限公司 一种高强高韧性热冲压钢基体及其制备方法和应用
CN115161441A (zh) * 2022-07-28 2022-10-11 鞍钢股份有限公司 热冲压成形用铝合金预涂镀钢板的生产方法及连续退火炉

Family Cites Families (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3846206B2 (ja) 2000-02-29 2006-11-15 Ｊｆｅスチール株式会社 歪時効硬化特性に優れた高張力冷延鋼板およびその製造方法
US8084143B2 (en) * 2003-09-30 2011-12-27 Nippon Steel Corporation High-yield-ratio and high-strength thin steel sheet superior in weldability and ductility, high-yield-ratio high-strength hot-dip galvanized thin steel sheet, high-yield ratio high-strength hot-dip galvannealed thin steel sheet, and methods of production of same
JP4448456B2 (ja) 2004-01-29 2010-04-07 新日本製鐵株式会社 浸炭時の粗大粒防止特性と疲労特性に優れた肌焼鋼とその製造方法
JP4506476B2 (ja) 2005-01-17 2010-07-21 Ｊｆｅスチール株式会社 温間成形に適した冷延鋼板およびその製造方法
JP4427462B2 (ja) * 2005-01-21 2010-03-10 新日本製鐵株式会社 車両用鋼部材及びその製造方法
JP4449795B2 (ja) 2005-03-22 2010-04-14 住友金属工業株式会社 熱間プレス用熱延鋼板およびその製造方法ならびに熱間プレス成形部材の製造方法
CN102242306B (zh) 2005-08-03 2013-03-27 住友金属工业株式会社 热轧钢板及冷轧钢板及它们的制造方法
DE102005051052A1 (de) 2005-10-25 2007-04-26 Sms Demag Ag Verfahren zur Herstellung von Warmband mit Mehrphasengefüge
KR100711358B1 (ko) 2005-12-09 2007-04-27 주식회사 포스코 성형성, 소부경화성 및 도금특성이 우수한 고강도 냉연강판및 용융아연도금강판, 그리고 이들의 제조방법
JP4714574B2 (ja) * 2005-12-14 2011-06-29 新日本製鐵株式会社 高強度鋼板及びその製造方法
KR100742820B1 (ko) 2005-12-27 2007-07-25 주식회사 포스코 냉간가공성과 소입성이 우수한 강선재 및 그 제조방법
JP4725415B2 (ja) 2006-05-23 2011-07-13 住友金属工業株式会社 熱間プレス用鋼板および熱間プレス鋼板部材ならびにそれらの製造方法
CN100543155C (zh) 2006-09-27 2009-09-23 马鞍山钢铁股份有限公司 一种中碳钢在线球化轧制工艺
CN101583486B (zh) * 2006-10-30 2014-08-27 安赛乐米塔尔法国公司 涂覆的钢带材、其制备方法、其使用方法、由其制备的冲压坯料、由其制备的冲压产品和含有这样的冲压产品的制品
JP5070947B2 (ja) 2007-06-14 2012-11-14 住友金属工業株式会社 焼入れ鋼板部材および焼入れ用鋼板とそれらの製造方法
JP4995109B2 (ja) * 2008-02-07 2012-08-08 新日本製鐵株式会社 加工性及び耐衝突特性に優れた高強度冷延鋼板及びその製造方法
AU2009229885B2 (en) 2008-03-27 2011-11-10 Nippon Steel Corporation High-strength cold-rolled steel sheet, high-strength galvanized steel sheet, and high-strength alloyed hot-dip galvanized steel sheet which have excellent formability and weldability, and methods for manufacturing the same
JP5391572B2 (ja) * 2008-04-08 2014-01-15 新日鐵住金株式会社 冷延鋼板および溶融めっき鋼板ならびに該鋼板の製造方法
JP4563469B2 (ja) 2008-05-16 2010-10-13 トヨタ自動車株式会社 プレス加工方法及びプレス加工品
JP5178348B2 (ja) * 2008-06-26 2013-04-10 双葉電子工業株式会社 模型用ラジオコントロール装置
CA2729942C (en) * 2008-07-11 2013-08-06 Nippon Steel Corporation Aluminum plated steel sheet for rapid heating hot-stamping, production method of the same and rapid heating hot-stamping method by using this steel sheet
JP5709151B2 (ja) * 2009-03-10 2015-04-30 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5387073B2 (ja) 2009-03-16 2014-01-15 新日鐵住金株式会社 熱間プレス用鋼板およびその製造方法ならびに熱間プレス用鋼板部材の製造方法
WO2011016518A1 (ja) 2009-08-06 2011-02-10 新日本製鐵株式会社 輻射伝熱加熱用金属板及びその製造方法、並びに異強度部分を持つ金属加工品及びその製造方法
US20130095347A1 (en) * 2010-06-14 2013-04-18 Kaoru Kawasaki Hot-stamped steel, method of producing of steel sheet for hot stamping, and method of producing hot-stamped steel
JP5752409B2 (ja) 2010-12-27 2015-07-22 新日鐵住金株式会社 硬度バラつきの小さいホットスタンプ成形体の製造方法およびその成形体
US9512499B2 (en) 2010-10-22 2016-12-06 Nippon Steel & Sumitomo Metal Corporation Method for manufacturing hot stamped body having vertical wall and hot stamped body having vertical wall
BR112013009520B1 (pt) 2010-10-22 2019-05-07 Nippon Steel & Sumitomo Metal Corporation Métodos para produção de chassi estampado a quente e chassi estampado a quente

Also Published As

Publication number Publication date
MX2013004355A (es) 2013-06-28
US20130292009A1 (en) 2013-11-07
JP5547287B2 (ja) 2014-07-09
JPWO2012053636A1 (ja) 2014-02-24
CN103314120A (zh) 2013-09-18
BR112013009520A2 (pt) 2017-07-25
EP2631306A4 (en) 2016-09-07
KR20130069809A (ko) 2013-06-26
WO2012053636A1 (ja) 2012-04-26
CN103314120B (zh) 2014-11-05
BR112013009520B1 (pt) 2019-05-07
US9598745B2 (en) 2017-03-21
US20170145531A1 (en) 2017-05-25
US9840751B2 (en) 2017-12-12
EP2631306A1 (en) 2013-08-28
CA2814630A1 (en) 2012-04-26
EP2631306B1 (en) 2019-12-11
CA2814630C (en) 2016-04-26
KR101533164B1 (ko) 2015-07-01

Similar Documents

Publication Publication Date Title
MX359051B (es) Proceso para producir un artículo moldeado por estampación en caliente, y artículo moldeado por estampación en caliente.
MX348196B (es) Metodo para fabricar cuerpo estampado en caliente que tiene pared vertical y cuerpo estampado en caliente que tiene pared vertical.
IN2014MN00193A (es)
IN2014KN01251A (es)
UA106201C2 (ru) СПОСОБ ИЗГОТОВЛЕНИЯ горячештампованных ИЗДЕЛИЙ И горячештампованные ИЗДЕЛИЯ, ИЗГОТОВЛЕННЫЕ ЭТИМ СПОСОБОМ
MX368319B (es) Método de fabricación y método para miembro conformado por prensado en caliente.
GB2437955B (en) Method of manufacturing hot-formed steel product
PL2581465T3 (pl) Wyrób formowany przez wytłaczanie na gorąco, sposób wytwarzania blachy stalowej cienkiej do wytłaczania na gorąco i sposób wytwarzania wyrobu formowanego przez wytłaczanie na gorąco
MY148425A (en) Process for hot rolling and for heat treatment of a steel strip
MX360240B (es) Lámina de acero para miembro estampado en caliente y método para producirla.
LU91466B1 (en) Steel sheet for hot press forming having low-temperature heat treatment property, method of manufacturing the same, method of manufacturing parts using the same, and parts manufactured by the same
EP4254440A3 (en) Method of production of tin containing non grain-oriented silicon steel sheet
WO2012085247A3 (de) Verfahren zum erzeugen gehärteter bauteile
WO2013188668A3 (en) Improved aluminum alloys and methods for producing the same
WO2012048841A8 (en) Method of hot forming a steel blank and the hot formed part
ZA201307339B (en) Steel sheets for hot stamping,use, method of production of same, and method of production of high-strength parts.
EP2832887A4 (en) CUSTOMIZED COATING FOR HOT COATING, HOT-PUTTED ELEMENT AND METHOD FOR THE PRODUCTION THEREOF
MX347081B (es) Método para fabricar una lámina de acero eléctrico de grano orientado..
MY176515A (en) A method of forming parts from sheet metal alloy
MX2017001024A (es) Metodo para calentar laminas de acero y dispositivo para llevar a cabo el metodo.
MX2014002935A (es) Metodo para producir una cinta electrica superiormente resistente de grano no orientado y su uso.
MX2019007946A (es) Parte estampada en caliente y metodo de fabricacion de la misma.
EP2719787A4 (en) HOT-PRESSED FORMING, MANUFACTURING METHOD AND THIN STEEL PLATE FOR HOT PRESSING
WO2011095417A3 (de) Metallband mit einer konstanten metallbandicke und unterschiedlichen mechanischen eigenschaften
MX2013002063A (es) Metodo para conformar en caliente una parte de metal revestida y parte conformada.

Legal Events

Date Code Title Description
FG Grant or registration